Abstract
Stable amorphous calcium carbonate supported by mesoporous silica gel was successfully synthesized. The silica gel support is prepared through the hydrolytic polycondensation of ethyl silicate under suitable conditions. Laser scanning confocal microscopy (LSCM) observations reveal that the morphology of the products is branched with cruciform-like and flower-like structure. Raman spectroscopic analysis and scanning electron microscopy (SEM) observation of the products confirm the combination of stable amorphous calcium carbonate (ACC) nanoparticles and mesoporous silica gel. A possible growth mechanism for the branched structure has been proposed. Results indicate potential application of this work to ACC storage, crystal engineering, biomimetic synthesis, etc.
Background
Amorphous calcium carbonate (ACC) has attracted increasing interest as a result of its potential use in biomimetic and industrial applications. However, it is a transient precursor phase to crystalline modification [1–4], so it is difficult to obtain in vitro. Stabilizing amorphous precusors is one of the major issues in biomineralization studies [5]. Moreover, people had been trying to add process-directing agents during the nucleation stage. Additives such as phosphorproteins [6], aspartic acid [7], and ployacrylic acid (PAA) [5] have been proved to act as stabilizers for ACC. In addition, researchers have also tried other inorganic substances, with the result that spherical ACC accompanied by vaterite or calcite was obtained [8].
The reason ACC is unstable under ambient conditions is because of its large interfacial energy. Accordingly, it would be interesting to develop a highly porous support material which would make it possible to lower the interfacial energy of ACC during the reaction [9]. With this in mind, silica gel was chosen as the material because of its tunable porosity via hydrolytic polycondensation of liquid precursors such as the silicon alkoxides under controlled conditions [10]. The first synthesis of porous silica was described by Kistler in 1931 [11]. Since that time, silica gels have been used as functional materials with an impressive range of applications [12]. The use of silica gel for CaCO3 single crystal growth has been employed as a means to control the purity and morphology [13, 14]. However, a silica gel-based system for controlling the formation of amorphous CaCO3 has not been studied.
In this work, we used a porous silica gel support to form ACC for the first time. Silica gel is obtained through the hydrolytic polycondensation of ethyl silicate as an additive to a solution of CaCl2 and (NH2)2CO. The morphology of silica gel can be tailored to form a 3D-matrix during hydrolytic polycondensation under suitable conditions [9], so that support is afforded that lowers the interfacial energy of the ACC. The structure and morphology of the product were characterized by laser scanning confocal microscopy (LSCM), micro-Raman spectroscopy, and scanning electron microscopy (SEM).
Methods
The ethyl silicate (ES), calcium chloride dihydrate (CaCl2··2H2O), urea, ethyl alcohol (C2H5OH), and sodium hydroxide (NaOH) used as precursors were of analytical grade and used without further purification. All chemicals were purchased from Sinopharm Chemical Reagent Co., Ltd (Shanghai, China). Deionized water with an electrical conductivity of less than 106 S m-1 was taken from a Mili-Q system.
Four separate silica solutions were prepared by mixing 0.2 mL ethyl silicate, 0.2 mL alcohol, 6.5 mL NaOH (0.1 M), and deionized water in 100-mL plastic beakers and stirring for 1 h. A 0.5 M calcium chloride solution and 2.5 M urea solution were prepared in 30-mL quantities. Subsequently, different amounts (0.5, 1, 1.5, and 2 mL) of the 0.5 M calcium chloride solution and 1.5 mL of the 2.5 M urea solution were added to the plastic beakers. As a result, the concentration of CaCl2 is, respectively, 2.5, 5, 7.5, and 15 mM, in these four mixing solutions. Deionized water was added until the total amount of mixture was 100 mL. After that, 5 mL each of the solutions was transferred to separate Petri dishes, each with a 5 cm × 5 cm slide substrate. Each Petri dish was sealed by parafilm with seven pinholes and then incubated at 60°C until bakeout. The sample on the slide substrate was then subjected to analysis.
Laser scanning confocal microscopy (LSCM) and scanning electron microscopy (Hitachi S-4800 SEM, Hitachi, Ltd., Chiyoda-ku, Japan) were used to observe the morphology of the sample. SEM images were obtained without gold coating in order to avoid spurious results. The Raman scattering spectrum was obtained using the 532-nm line of a Nd, YAG laser as the excitation source. For all measurements with visible excitation, the slits were set at 100 μm and a × 100 objective was used.
Results and discussion
Figure 1 shows the recorded LSCM images of the samples grown in the mixing solutions with CaCl2 concentrations of 7.5 mM (Figure 1a,b,c) and 5 mM (Figure 1d,e,f). The branched samples, including cruciform-like and flower-like structures are formed by varying the CaCl2 concentration from 5 to 7.5 mM. However, no such branched products are formed with a CaCl2 concentration that is less than 5 mM or greater than 7.5 mM (see Additional file 1: Figure S1). That is to say, the suitable CaCl2 concentration for the formation of branched products ranges from 5 to 7.5 mM. Note that the shape of the branched samples obtained with 7.5 mM CaCl2 (Figure 1a) is more pronounced than that obtained with 5 mM CaCl2 (Figure 1d). The magnified 3D contour maps shown in Figure 1b,c and Figure 1e,f further confirm the foregoing evidence that the aspect ratio of the branched product obtained with 7.5 mM CaCl2 (0.10 ~ 0.21) is lower than that obtained with 5 mM CaCl2 (0.05 ~ 0.15). One can conclude that the nature of the final products tends to be related to the CaCl2 concentration, where 7.5 mM appears optimal for forming the branched form.
Figure 2 shows the Raman scattering spectra of the branched samples. Scattering bands centered at 1,008 and 1,085 cm-1 are seen for both the cruciform-like and flower-like samples. So, the branched samples, either cruciform-like or flower-like, are made of the same material. The peak at 1,085 cm-1 corresponds to the ν1 symmetric vibrational mode of the carbonate ion (CO32-) in CaCO3[15–17]. The Raman spectrum of the branched sample shows characteristics of the family of ACC phases, which contain only the ν1 symmetric (1,085 cm-1) CO32- peak [15, 18]. Note that there is an additional intense band at around 1,008 cm-1, which corresponds to the Si-(OH) stretching vibration of silica gel [19, 20]. As a result, we can draw the conclusion that the branched sample is composed of silica gel and the ACC phase.
To investigate the nanostructure of the branched products, SEM was performed on a well-chosen flower-like product of sufficiently small size (Figure 3a). Figure 3b and Figure 3c are the magnified images, respectively, obtained from areas 1 and 2 of the flower-like product shown in Figure 3a. A fibrous matrix overspreads the field of view, and the flower-like crystallite is composed of a fibrous matrix and nanoparticles with a diameter of about 50 nm. The composition of the flower-like product was confirmed by EDS spectrum measurements (Figure 3d) to contain Si, O, and Ca, which reveals the existence of SiO2 and CaCO3. As C is a light element, it cannot be detected by EDS. Considering both the Raman results (Figure 2) and the SEM images (Figure 3), the branched samples were shown to consist of ACC nanoparticles and mesoporous silica gel. Namely, the structure of the resulting silica gel was successfully tailored to be mesoporous, which allows the existence of a stable ACC phase.
The ACC phase is usually the transient precursor of calcite [1], vaterite [2], or aragonite [4]. It is difficult to obtain stable ACC in the laboratory because of the large interfacial energy.
According to the LSCM and SEM observations, a possible self-assembly process for the branched products is proposed, as illustrated in Figure 4. First, the hydrolysis and polycondensation reactions of ethyl silicate in an alkaline medium result in silica alcogel after stirring for 1 h. Second, by adding CaCl2 and urea solutions, ion pairs of Ca2+ and CO3-, which are prenucleation clusters for ACC aggregation [21–23], are formed in the solution. Third, when the mixed solution of CaCl2, urea, and, the silica alcogel is dried under a mild thermal treatment, namely, baking at 60°C, a mesoporous gel is obtained [9] and at the same time, ACC aggregates are entrapped in the silica gel voids, which has been demonstrated by SEM observation of the composites of fibrous silica gel and ACC (Figure 3). The mesoporous silica supports lower the ACC interfacial energy so that a composite of mesoporous silica gel and stable ACC is formed. Moreover, it can be seen that the ACC nanoparticles are aggregated in an oriented fashion so the branched morphology of the composites appears, as shown in Figure 1.
Conclusions
In this work, the possibility of synthesizing stable ACC supported by mesoporous silica gel has been described. These composites are obtained using the reaction of CaCl2 and (NH2)2CO in a silica gel medium that is prepared through the hydrolytic polycondensation of ethyl silicate. LSCM, Raman, and SEM observations show that the morphology of the composites, which are composed of ACC nanoparticles and mesoporous silica gel takes on a branched form with cruciform-like and flower-like structures. The growth mechanism is discussed and a possible self-assembly process for the branched products is proposed. Silica gel with 3D-matrix morphology was successfully fabricated as a support for ACC. As a result, chemical agents with 3D-matrix morphology, such as silica gel, have the potential to significantly improve the utility and integrity of underground reservoirs for ACC storage. Moreover, the results suggest potential applications of the work with important implications in crystal engineering, biomimetic synthesis, etc.
References
Zhou GT, Guan YB, Yao QZ, Fu SQ: Biominetic mineralization of prismatic calcite mesocrystals: relevance to biomineralization. Chem Geol 2010, 279: 63–72. 10.1016/j.chemgeo.2010.08.020
Dong WY, Cheng HX, Yao Y, Zhou YF, Tong GS, Yan DY, Lai YJ, Li W: Bioinspired synthesis of calcium carbonate hollow spheres with a nacre-type laminated microstructure. Langmuir 2011, 27(1):366–370. 10.1021/la1034799
Faatz M, Gröhn F, Wegner G: Amorphous calcium carbonate synthesis and potential intermediate in biominerlization. Adv Mater 2004, 16: 996–1000. 10.1002/adma.200306565
Weiss IM, Tuross N, Addadi L, Weiner S: Mollusc larval shell formation: amorphous calcium carbonate is a precursor phase for aragonite. J Exp Zool 2002, 293: 478–491. 10.1002/jez.90004
Kaempfe P, Lauth VR, Halfer T, Treccani L, Maas M, Rezwan K: Micromolding of calcium carbonate using a bio-inspired, coacervation-mediated process. J Am Ceram Soc 2013, 96(3):736–742. 10.1111/jace.12194
Bentov S, Weil S, Glazer L, Sagi A, Berman A: Stabilization of amorphous calcium carbonate by phosphate rich organic matrix proteins and by single phosphoamino acids. J Struct Biol 2010, 171: 207–215. 10.1016/j.jsb.2010.04.007
Maruyama K, Yoshino T, Kagi H: Synthesizing a composite material of amorphous calcium carbonate and aspartic acid. Mater Lett 2011, 65: 179–181. 10.1016/j.matlet.2010.09.039
Gorna K, Hund M, Vučak M, Gröhn F, Wegner G: Amorphous calcium carbonate in form of spherical nanosized particles and its application as fillers for polymers. Mat Sci Eng A 2008, 477: 217–225. 10.1016/j.msea.2007.05.045
Ciriminna R, Fidalgo A, Pandarus V, Béland F, Ilharco LM, Pagliaro M: The sol-gel route to advanced silica-based materials and recent applications. Chem Rev 2013, 113(8):6592–6620. 10.1021/cr300399c
Iler RK: The Chemistry of Silica. New York: Wiley-Intersicence; 1979.
Kistler SS: Coherent expanded aerogels and jellies. Nature 1931, 127: 741.
Pagliaro M: Silica-Based Materials for Advanced Chemical Applications. UK: RSC publishing; 2009.
Voinescu AE, Kellermeier M, Bartel B, Carnerup AM, Larsson AK, Touraud D, Kunz W, Kienle L, Pfitzner A, Hyde ST: Inorganic self-organized silica aragonite biomorphic composites. Cryst Growth Des 2008, 8(5):1515–1521. 10.1021/cg700692t
Asenath-Smith E, Li HY, Keene EC, She ZW, Estroff LA: Crystal growth of calcium carbonate in hydrogels as a model of biomineralization. Adv Funct Mater 2012, 22: 2891–2914. 10.1002/adfm.201200300
Blue CR, Rimstidt JD, Dove PM: A mixed flow reactor method to synthesize amorphous calcium carbonate under controlled chemical conditions. Method Enzymol 2013, 532: 557–568.
Karampelas S, Fitsch E, Mevellec JY, Gauthier JP, Sklavounos S, Soldatos T: Determination by Raman scattering of the nature of pigments in cultured freshwater pearls from the mollusk Hyriopsis cumingi. J Raman Spectrosc 2007, 38: 217–230. 10.1002/jrs.1626
Soldati AL, Jacob DE, Wehrmeister U, Hager T, Hofmeister W: Micro-Raman spectroscopy of pigments contained in different calcium carbonate polymorphs from freshwater cultured pearls. J Raman Spectrosc 2008, 39: 525–536. 10.1002/jrs.1873
Jacob DE, Wirth R, Soldati AL, Wehrmeister U, Schreiber U: Amorphous calcium carbonate in the shell of adult Unionoida. J Struct Biol 2011, 173: 241–249. 10.1016/j.jsb.2010.09.011
Robbe OC, Raulin K, Dubart F, Bernard R, Kinowski C, Damene N, Yazidi IEI, Boed A, Turrell S: Porous silica supports for micro-Raman spectroscopic studies of individual living cells. J Mol Struct 2013, 1050: 232–237.
Silva SW, Pedroza RC, Sartoratto PPC, Rezende DR, Neto AVS, Soler MAG, Morais PC: Raman spectroscopy of cobalt ferrite nanocomposite in silica matrix prepared by sol-gel method. J Non-Cryst Solids 2006, 352: 1602–1606. 10.1016/j.jnoncrysol.2006.01.054
Gebauer D, Völkel A, Cölfen H: Stable prenucleation calcium carbonate clusters. Science 2008, 322: 1819–1822. 10.1126/science.1164271
Pouget EM, Bomans PHH, Goos JACM, Frederik PM, de With G, Sommerdijk NAJM: The initial stages of template-controlled CaCO3 formation revealed by cryo-TEM. Science 2009, 323: 1455–1458. 10.1126/science.1169434
Wallace A, Hedges LO, Fernandez-Martinez A, Raiteri P, Gale JD, Waychunas GA, Whitelam S, Banfield JF, Yoreo JJD: Microscopic evidence for liquid-liquid separation in supersaturated CaCO3 solutions. Science 2013, 341: 885–889. 10.1126/science.1230915
Acknowledgements
This study was financially supported by Natural Science Foundation of China under grant No. 11134006 and 51321091.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
FF carried out the synthesis process of the composites, performed the statistical analysis, and drafted the manuscript. LGT and SX participated in the design of the study. XGX conceived of the study and participated in its design and coordination. XBH helped to draft the manuscript. All authors read and approved the final manuscript.
Electronic supplementary material
11671_2014_2207_MOESM1_ESM.jpeg
Additional file 1: Figure S1 LSCM images: (a) the products obtained from 2.5 mM CaCl2. (b) the products obtained from 10 mM CaCl2. Figure S1 shows the LSCM images of products grown in the mixing solutions with CaCl2 concentrations of 2.5 mM (Figure S1a) and 10 mM (Figure S1b) respectively. The regular branched products could not be found in Figure S1, which means no such branched products are formed with CaCl2 concentration which is lower than 5 mM or higher than 7.5 mM. (JPEG 321 KB)
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Fu, F., Tian, L.G., Xu, S. et al. Synthesis of stable ACC using mesoporous silica gel as a support. Nanoscale Res Lett 9, 450 (2014). https://doi.org/10.1186/1556-276X-9-450
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-450