Open Access Nano Express

Graphene oxide-based SPR biosensor chip for immunoassay applications

Nan-Fu Chiu1*, Teng-Yi Huang1, Hsin-Chih Lai2 and Kou-Chen Liu3

Author Affiliations

1 Institute of Electro-Optical Science and Technology, National Taiwan Normal University, No. 88, Sec. 4, Ting-Chou Road, Taipei 11677, Taiwan

2 Department of Medical Biotechnology and Laboratory Science, Chang Gung University, No. 259 Wenhwa 1st Road, Gueishan Shiang, Taoyuan 33302, Taiwan

3 Department of Electronic Engineering, Chang Gung University, No. 259 Wenhwa 1st Road, Gueishan Shiang, Taoyuan 33302, Taiwan

For all author emails, please log on.

Nanoscale Research Letters 2014, 9:445  doi:10.1186/1556-276X-9-445

The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/9/1/445


Received:30 June 2014
Accepted:15 August 2014
Published:28 August 2014

© 2014 Chiu et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly credited.

Abstract

This work develops a highly sensitive immunoassay sensor for use in graphene oxide sheet (GOS)-based surface plasmon resonance (SPR) chips. This sensing film, which is formed by chemically modifying a GOS surface, has covalent bonds that strongly interact with the bovine serum albumin (BSA), explaining why it has a higher sensitivity. This GOS film-based SPR chip has a BSA concentration detection limit that is 100 times higher than that of the conventional Au-film-based sensor. The affinity constants (KA) on the GOS film-based SPR chip and the conventional SPR chip for 100 μg/ml BSA are 80.82 × 106 M-1 and 15.67 × 106 M-1, respectively. Therefore, the affinity constant of the GOS film-based SPR chip is 5.2 times higher than that of the conventional chip. With respect to the protein-protein interaction, the SPR sensor capability to detect angle changes at a low concentration anti-BSA of 75.75 nM on the GOS film-based SPR chip and the conventional SPR chip is 36.1867 and 26.1759 mdeg, respectively. At a high concentration, anti-BSA of 378.78 nM on the GOS film-based SPR chip and the conventional SPR chip reveals two times increases in the SPR angle shift. Above results demonstrate that the GOS film is promising for highly sensitive clinical diagnostic applications.

Keywords:
Graphene oxide sheet (GOS); Surface plasmon resonance (SPR); Protein; Bovine albumin serum (BSA)

Background

As a novel class of two-dimensional carbon nanostructures, graphene oxide sheets (GOSs) have received considerable attention in recent years in the fields of plasmonics [1-3] and surface plasmon resonance (SPR) biosensors [4-11], following both experimental and theoretical scientific discoveries. GOSs have remarkable optical [12-19] and biosensing [20-28] properties and are expected to have a wide range of applications. A GOS has a high surface area and sp2 within an sp3 matrix that can confine π-electrons [12-14,29]. GOSs contain oxygen at their surfaces in the form of epoxy (-O), hydroxyl (-OH), carboxyl (-COOH), and ether functional groups on a carbon framework [30-35]. The direct bandgap behavior of a GOS can be controlled by modification by oxidation that generates photoluminescence (PL) [16-19] and makes available chemically functionalized GOS with biological applications. Surface chemical modifications significantly influence the performance of surface chemistry-derived devices such as optoelectronic devices, luminescent devices, biosensors, and biomaterials. This work develops a novel method for detecting immunological diseases, in which terminal groups (-COOH) are modified and carboxyl groups on GOS surfaces are activated. The carboxyl groups of a GOS film can be converted into amine-reactive groups to increase its surface area sensing. Furthermore, modifying the oxygen-containing functional groups on the surface of GOS can increase its bandgap and its dielectric constant, thereby improving its surface plasmon resonance (SPR) properties.

Methods

Figure 1a,b shows the design of two sensing chips, i.e., a conventional SPR chip and a GOS film-based SPR chip. Standard SPR thin films were deposited with thin film for gold (Au) thickness of 47 nm and chromium (Cr) thickness of 2 nm on BK7 glass substrate to a thickness of 0.17 mm. SPR experiments were conducted using a BI-3000G SPR system with Kretschmann prism coupling (Biosensing Instrument, Tempe, AZ, USA). The test injection sample volume was 200 μl and the flow rate was 60 μl/s. All experiments were performed at 25°C and repeated in triplicate.

thumbnailFigure 1. SPR biosensor chip using an immunoassay method for detecting a protein using a gold binding. (a) Conventional SPR chip and (b) GOS film-based SPR chip. Intensity of an evanescent field with a depth of approximately 100 ~ 500 nm decays exponentially with increasing distance from the metal. Bimolecular binding, observed within approximately 10 nm of the metal surface, gives rise to a higher signal shift response than that of the interactive process at a distance of 300 nm therefrom. For typical SPR Kretschmann prism coupling that uses a red light to induce the evanescent field, its field intensity is no more than 600 nm in practice.

Designed configuration for sensing

Figure 1a presents a conventional SPR sensing chip and a biomolecule binding mechanism. 8-Mercaptooctanoic acid (MOA; Sigma-Aldrich Co. LLC., St. Louis, MO, USA) is activation of carboxylic acid-terminated thiol self-assembled monolayers (SAMs) on a modified Au surface. MOA binds to the Au surface through their thiol linker (-SH end) resulting monolayers, which are terminated with carboxylic acid (-COOH). The MOA can be further functionalized to immobilize a bovine serum albumin (BSA; Sigma, Chemical Company, St. Louis, MO, USA) protein. Anti-BSA protein interactions are performed as well.

Figure 1b shows a GOS film-based SPR chip with its biomolecule binding mechanism. Two binding mechanisms are functionalized SAMs on amino-modified Au surfaces by solutions of cystamine (Cys; Alfa Aesar Co., Ward Hill, MA, USA) with a concentration of 5 mM and octadecanthiols (ODT, C18H37SH; Sigma-Aldrich Co. LLC.) with a concentration of 10 mM formation of Au-S bonds that immobilize a GOS. Concentration of the GOS diluted in water was 2 mg/ml. The GOS film sensing surface detects BSA protein concentrations in a range of 100 pg/ml to 100 μg/ml and their interaction with anti-BSA. Moreover, analysis is performed of the kinetics of protein-protein interactions at physical contacts that are established between two proteins, owing to biochemical events, protein affinity adsorption forces, and protein binding forces.

Preparation of modified GOS films

The GOS (Graphene Laboratories Inc., Calverton, NY, USA) was manufactured by Hummer’s method and diluted in water to a concentration of 2 mg/ml. In general, the oxide of a graphene material contains an epoxy group, a hydroxyl group, and a carboxyl group. Therefore, more efficient chemical modification methods and means of activating the carboxyl groups on the GOS surface are sought. The GOS immobilization was chemically modified by a reaction with a 4:1 ratio of N-hydroxysulfosuccinimide (NHS)/N-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC). Carboxylic acid groups of GOS were converted to reactive NHS esters using EDC and NHS, and GOS were subsequently immobilized by reacting its NHS-activated carboxylic acid groups. This method can convert carboxyl groups to amine-reactive NHS esters that immobilize hydrocarbon chains, as shown in Figure 2b. The activated surfaces of the GOS reacted with the amine groups of the BSA protein, subsequently forming a strongly covalent bond, as shown in Figure 2c. Analytical results suggest that in addition to improving the protein compatibility of this GOS material, GOS immobilization to EDC/NHS-crosslinks can be used to prepare a chemically modified GOS film-based SPR chip specifically for analysis in a protein sample solution [10,36,37].

thumbnailFigure 2. GOS, terminal groups, and carboxyl groups. (a) Molecular structure of GOS. (b) Modification of terminal groups (-COOH) of monolayers of GOS film by surface-confined ester reactions. (c) Carboxyl groups ending in -COOH cause GOS surface to exhibit affinity for NH2 end of protein.

Kinetic analysis of bimolecular interactions at surface

SPR sensorgrams include real-time information on the changes in mass that are caused by binding in a bimolecular interaction, such as that between probe [P] and target [T], as follows [38,39].

<a onClick="popup('http://www.nanoscalereslett.com/content/9/1/445/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/9/1/445/mathml/M1">View MathML</a>

(1)

In a bimolecular competition experiment with a probe for the target that is present both on the sensor surface and in solution, the complex [PT] is formed, and under the two binding equilibria, the dissociation constant KA and dissociation constant KD are given by Equation 2.

<a onClick="popup('http://www.nanoscalereslett.com/content/9/1/445/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/9/1/445/mathml/M2">View MathML</a>

(2)

where ka and kd are the association and dissociation rate constants for the formation and dissociation of the complex [PT].

Figure 3 shows an analysis of the cyclic sensorgram of the change in the refractive index of the liquid phase close to the sensor chip surface in the SPR experiments. The amount of complex [PT] is proportional to the shift in SPR angle (mdeg). The observed shift in the SPR angle is the sum of the shift that is caused by the association of [T] with [P] and that is caused by the difference between the refractive indices of the solution and the baseline buffer. The shift in the SPR angle is recorded as a function of time in the sensorgram. At equilibrium, the fraction of the surface that is covered reaches a steady state and this equilibrium surface coverage (θeq)SP is given by the Langmuir absorption isotherm, [40]

thumbnailFigure 3. Time course for value of SPR sensorgrams in analysis of interaction that involves bimolecular association and dissociation.

<a onClick="popup('http://www.nanoscalereslett.com/content/9/1/445/mathml/M3','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/9/1/445/mathml/M3">View MathML</a>

(3)

where the Langmuir absorption coefficient (Kabs) is defined as Kabs= ka/kd.

Based on Fresnel’s equations, given the reflection coefficient, the SP wave vectors for the Au-GOS-BSA boundary, and the coupler matching condition of the SPR are as given by Equation 4.

<a onClick="popup('http://www.nanoscalereslett.com/content/9/1/445/mathml/M4','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/9/1/445/mathml/M4">View MathML</a>

(4)

where Kx is the wave-vector parallel to the surface form which light is reflected, K0 is the wave-vector in a vacuum, and Ksp is the SP wave-vector that is parallel to the interfaces between the metal and the dielectric. θeq is the SPR angle at equilibrium, εp is the refractive index of the prism, and εm and εd are the metal and dielectric constants of the sample, respectively.

Results and discussion

Analysis of sensitivity of interaction between GOS and BSA

Two-dimensional GOS surfaces can detect a large area, in which the evanescent field decays exponentially with the distance beyond 600 nm from the metal. Figure 4 shows the interaction of a GOS with BSA. GOS performs a spacing function BSA and GOS, which increases the accessibility of the immobilized GOS.

thumbnailFigure 4. GOS-BSA interaction. GOS is immobilized on a planar immobilization film, which is a few tens of nanometers thick, and is readily accessible by analytic BSA protein with which it undergoes specific interactions.

Kinetic analysis of interaction between GOS and BSA

Molecular kinetics of the interactions of the three sensor films and the protein are analyzed. Figure 5 presents the SPR sensorgrams (BI-3000G SPR system) of a Au-MOA film (conventional SPR chip) (Figure 5a), a Au-Cys-GOS film (GOS film-based SPR chip) (Figure 5b), and a Au-ODT-GOS film (ODT-based GOS film-based SPR chip) (Figure 5c), in response to solutions of BSA with a concentration of 100 μg/ml in phosphate buffered saline (PBS) buffer. The affinity constants (KA) of 100 μg/ml BSA on the ODT-based GOS film-based SPR chip, the conventional SPR chip, and the GOS film-based SPR chip were 2.6 × 106 M-1, 15.67 × 106 M-1, and 80.82 × 106 M-1, respectively. The ratio of the affinities of the ODT-based GOS film-based SPR chip, conventional chip, and GOS film SPR chip was 1:6:31 times. The results demonstrate that this Cys-modified Au surface excellently immobilized a GOS film in an SPR chip.

thumbnailFigure 5. SPR sensorgrams obtained in response to BSA, at concentration of 100 μg/ml, flowing over surfaces of films. (a) Interaction with conventional SPR chip based on Au-MOA film, (b) interaction with the Cys-based GOS film-based SPR chip, and (c) interaction with ODT-based GOS film-based SPR chip. Association rate (ka), dissociation rate (kd), affinity constant (KA), and dissociation constant (KD) were obtained from fitted curves.

Figure 6 shows SPR response curves of conventional SPR chip and GOS film-based SPR chip, which exhibits higher sensitivity. In the detection of BSA protein, the limit of detection (LOD) of the conventional SPR chip was 10 ng/ml; that of the GOS film-based SPR chip was as low as 100 pg/ml. This GOS film-based SPR chip had a limit of detection (LOD) for BSA that was 1/100 that of the conventional Au-film-based sensor. These results were consistent with the calibration curves. The calibration curves were fitted by y = -6.43 + 2.77 e0.54x (correlation coefficient, R2 = 0.976) for the GOS film-based SPR chip, and y = -1.9 + 0.12 e0.87x (correlation coefficient, R2 = 0.966) for the conventional SPR chip, where x is the concentration of BSA and y is the SPR angle (θ).

thumbnailFigure 6. Response of sensor film to various concentrations of BSA. Calibration curves for detection of BSA by GOS film-based SPR chip and conventional SPR chip.

Biomolecular interaction analysis using BSA and anti-BSA

To evaluate the sensitivity and specificity of the developed immunoassay film in the on-site detection of anti-bovine serum albumin (Anti-BSA; Sigma, Chemical Company, St. Louis, MO, USA), an anti-BSA antibody sample was diluted to 378.78, 151.51, and 75.75 nM by adding PBS buffer. Figure 7 schematically depicts the Au-Cys-GOS-BSA-enhanced SPR sensor for anti-BSA.Figure 8 plots the SPR response in the adsorption of anti-BSA proteins on the GOS film-based SPR chip. Real-time SPR angle signals are obtained for 75.75, 151.51, and 378.78 nM anti-BSA antibodies on the conventional SPR film chip at 26.1759, 39.4802, and 63.8839 mdeg (millimeter degree), as shown in Figure 8a. Real-time SPR angle signals are obtained for 75.75, 151.51, and 378.78 nM anti-BSA proteins on the immunoassay film chip at 36.1867, 69.1671, and 127.7401 mdeg, as shown in Figure 8b.

thumbnailFigure 7. GOS-BSA-anti-BSA interaction. GOS-BSA is immobilized on a planar immobilization film that is a few hundreds of nanometers thick and is readily accessible to analytic anti-BSA protein with which it undergoes particular interactions.

thumbnailFigure 8. Sensorgram of immobilization of BSA 100 μg/ml on sensor chip in real time. Various detected concentrations of anti-BSA on (a) conventional SPR chip and (b) GOS film-based SPR chip.

Binding affinity was determined using anti-BSA protein concentrations of 75 to 378.78 nM. Since the immunoassay analyses were carried out using the same protein, BSA, with the anti-BSA interaction, the results are similar to those of the kinetic analysis, as shown in Figure 8a,b. The responses were measured against the concentration for the protein-protein interactions. Comparing the immunoassay sensitivity of the GOS film-based SPR chip and the conventional SPR chip reveals that the former exhibits an SPR angle shift that is 1.4 times higher than that of the latter at the low concentration of 75.75 nM and twice that of the latter at the high concentration of 378.78 nM, as shown in Figure 9. The anti-BSA concentration was exponentially fitted in the range of 75.75 to 378.78 nM. Additionally, the exponential regression equations of the slope of each fitted curve were as follows: 178.745 to 184.34 e-0.034x for the GOS film-based SPR chip and 92.312 to 82.146 e-0.0035x for the conventional SPR chip.

thumbnailFigure 9. Equilibrium analysis of binding of anti-BSA protein to a high-affinity BSA protein.

Conclusions

In summary, a GOS film was developed for binding with proteins based on SPR analysis for the purpose of immunoassay sensing. The GOS film-based SPR chip herein had a BSA concentration detection limit of as low as 100 pg/ml, which was 1/100th that of the conventional SPR chip. Additionally, in immunoassay detection, the GOS film-based SPR chip was highly sensitive at a low concentration of 75.75 nM, exhibiting an SPR angle shift of 1.4 times that of the conventional chip, and exhibited an SPR angle shift of two times that of the conventional chip at a high concentration of 378.78 nM. Finally, we believe that the fact that the GOS can be chemically modified to increase its SPR sensitivity can be exploited in clinical diagnostic protein-protein interaction applications, especially in cases in which tumor molecular detection is feasible.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

N-FC participated in the design of the study and performed the statistical analysis and drafted the manuscript. T-YH carried out the immunoassays and performed the statistical analysis. H-CL and K-CL conceived the study and participated in its design and coordination. All authors read and approved the final manuscript.

Acknowledgements

The authors would like to thank the Ministry of Science and Technology of the Republic of China, Taiwan, for financially supporting this research under Contract No. MOST 103-2221-E-003 -008, NSC 102-2221-E-003-021, NSC 100-2325-B-182-007, and NSC 99-2218-E-003-002-MY3.

References

  1. Yan H, Low T, Zhu W, Wu Y, Freitag M, Li X, Guinea F, Avouris P, Xia F: Damping pathways of mid-infrared plasmons in graphene nanostructures.

    Nat Photon 2013, 7:394-399. Publisher Full Text OpenURL

  2. Bao Q, Loh KP: Graphene photonics, plasmonics, and broadband optoelectronic devices.

    ACS Nano 2012, 6:3677-3694. PubMed Abstract | Publisher Full Text OpenURL

  3. Jablan M, Soljacic M, Buljan H: Plasmons in graphene: fundamental properties and potential applications.

    Proc IEEE 2013, 101:1689. OpenURL

  4. Zhang H, Sun Y, Gao S, Zhang J, Zhang H, Song D: A novel graphene oxide-based surface plasmon resonance biosensor for immunoassay.

    Small 2013, 9:2537. PubMed Abstract | Publisher Full Text OpenURL

  5. Wu T, Liu S, Luo Y, Lu W, Wang L, Sun X: Surface plasmon resonance-induced visible light photocatalytic reduction of graphene oxide: using Ag nanoparticles as a plasmonic photocatalyst.

    Nanoscale 2011, 3:2142. PubMed Abstract | Publisher Full Text OpenURL

  6. Ryu Y, Moon S, Oh T, Kim Y, Lee T, Kim DH, Kim D: Effect of coupled graphene oxide on the sensitivity of surface plasmon resonance detection.

    Appl Opt 2014, 53:1419. PubMed Abstract | Publisher Full Text OpenURL

  7. Choi SH, Kim YL, Byun KM: Graphene-on-silver substrates for sensitive surface plasmon resonance imaging biosensors.

    Opt Express 2011, 19:458-466. PubMed Abstract | Publisher Full Text OpenURL

  8. Wu L, Chu HS, Koh WS, Li EP: Highly sensitive graphene biosensors based on surface plasmon resonance.

    Opt Express 2010, 18:14395-14400. PubMed Abstract | Publisher Full Text OpenURL

  9. Zhang J, Sun Y, Xu B, Zhang H, Gao Y, Zhang H, Song D: A novel surface plasmon resonance biosensor based on graphene oxide decorated with gold nanorod–antibody conjugates for determination of transferrin.

    Biosens Bioelectron 2013, 45:230-236. PubMed Abstract | Publisher Full Text OpenURL

  10. Chiu N-F, Huang T-Y: Sensitivity and kinetic analysis of graphene oxide-based surface plasmon resonance biosensors.

    Sens Actuators B Chem 2014, 197:35. OpenURL

  11. Aliofkhazraei M: Advances in Graphene Science. Volume 8. InTech—Open Access Company; 2013.

    Graphene oxide based surface plasmon resonance biosensors, Croatia

    OpenURL

  12. Johari P, Shenoy VB: Modulating optical properties of graphene oxide: role of prominent functional groups.

    ACS Nano 2011, 5:7640-7647. PubMed Abstract | Publisher Full Text OpenURL

  13. Loh KP, Bao Q, Eda G, Chhowalla M: Graphene oxide as a chemically tunable platform for optical applications.

    Nat Chem 2010, 2:1015. PubMed Abstract | Publisher Full Text OpenURL

  14. Lim G-K, Chen Z-L, Clark J, Goh RGS, Ng W-H, Tan H-W, Friend RH, Ho PK, Chua L-K: Giant broadband nonlinear optical absorption response in dispersed graphene single sheets.

    Nat Photon 2011, 5:554-560. Publisher Full Text OpenURL

  15. Eda G, Chhowalla M: Chemically derived graphene oxide: towards large-area thin-film electronics and optoelectronics.

    Adv Mater 2010, 22:2392-2415. PubMed Abstract | Publisher Full Text OpenURL

  16. Shukla S, Saxena S: Spectroscopic investigation of confinement effects on optical properties of graphene oxide.

    Appl Phys Lett 2011, 98:073104. Publisher Full Text OpenURL

  17. Luo Z, Vora PM, Mele EJ, Johnson ATC, Kikkawa JM: Photoluminescence and band gap modulation in graphene oxide.

    Appl Phys Lett 2009, 94:111909. Publisher Full Text OpenURL

  18. Chien C-T, Li S-S, Lai W-J, Yeh Y-C, Chen H-A, Chen I-S, Chen L-C, Chen K-H, Nemoto T, Isoda S, Chen M, Fujita T, Eda G, Yamaguchi H, Chhowalla M, Chen C-W: Tunable photoluminescence from graphene oxide.

    Angew Chem Int Ed 2012, 54:6662. OpenURL

  19. Shang J, Ma L, Li J, Ai W, Yu T, Gurzadyan GG: The origin of fluorescence from graphene oxide.

    Sci Rep 2012, 2:1. OpenURL

  20. Lee W-C, Kuo C-C, Chiu N-F: Simple fabrication of glucose biosensor based on Graphene-Nafion composite by amperometric detections.

    Proc IEEE Sensors 2012.

    doi: 10.1109/ICSENS.2012.6411155

    OpenURL

  21. Liu F, Choi JY, Seo TS: Graphene oxide arrays for detecting specific DNA hybridization by fluorescence resonance energy transfer.

    Biosens Bioelectron 2010, 25:2361-2365. PubMed Abstract | Publisher Full Text OpenURL

  22. Hu Y, Li F, Bai X, Li D, Hua S, Wang K, Niu L: Label-free electrochemical impedance sensing of DNA hybridization based on functionalized graphene sheets.

    Chem Commun 2011, 47:1743-1745. Publisher Full Text OpenURL

  23. Wang Z, Zhou X, Zhang J, Boey F, Zhang H: Direct electrochemical reduction of single-layer graphene oxide and subsequent functionalization with glucose oxidase.

    J Phys Chem C 2009, 113:14071-14075. Publisher Full Text OpenURL

  24. Salihoglu O, Balci S, Kocabas C: Plasmon-polaritons on graphene-metal surface and their use in biosensors.

    Appl Phys Lett 2012, 100:213110. Publisher Full Text OpenURL

  25. Jung JH, Cheon DS, Liu F, Lee KB, Seo TS: A graphene oxide based immuno-biosensor for pathogen detection.

    Angew Chem Int Ed 2010, 49:5708-5711. Publisher Full Text OpenURL

  26. Liu J, Fu S, Yuan B, Li Y, Deng Z: Toward a universal “adhesive nanosheet” for the assembly of multiple nanoparticles based on a protein-induced reduction/decoration of graphene oxide.

    J Am Chem Soc 2010, 132:7279-7281. PubMed Abstract | Publisher Full Text OpenURL

  27. Guo S, Dong S: Graphene and its derivative-based sensing materials for analytical devices.

    J Mater Chem 2011, 21:18503-18516. Publisher Full Text OpenURL

  28. Mohanty N, Berry V: Graphene-based single-bacterium resolution biodevice and DNA transistor: interfacing graphene derivatives with nanoscale and microscale biocomponents.

    Nano Lett 2008, 8:4469-4476. PubMed Abstract | Publisher Full Text OpenURL

  29. Shin SY, Kim ND, Kim JG, Kim KS, Noh DY, Kim KS, Chung JW: Control of the π plasmon in a single layer graphene by charge doping.

    Appl Phys Lett 2011, 99:082110-082111. Publisher Full Text OpenURL

  30. Dreyer DR, Park S, Bielawski CW, Ruoff RS: The chemistry of graphene oxide.

    Chem Soc Rev 2010, 39:228-240. PubMed Abstract | Publisher Full Text OpenURL

  31. Cao Y, Lai Z, Feng J, Wu P: Graphene oxide sheets covalently functionalized with block copolymers via click chemistry as reinforcing fillers.

    J Mater Chem 2011, 21:9271-9278. Publisher Full Text OpenURL

  32. Liu X-W, Yao Z-J, Wang Y-F, Wei X-W: Graphene oxide sheet-prussian blue nanocomposites: green synthesis and their extraordinary electrochemical properties.

    Colloids Surf B: Biointerfaces 2010, 81:508-512. PubMed Abstract | Publisher Full Text OpenURL

  33. Georgakilas V, Otyepka M, Bourlinos AB, Chandra V, Kim N, Kemp KC, Hobza P, Zboril R, Kim KS: Functionalization of graphene: covalent and non-covalent approaches, derivatives and applications.

    Chem Rev 2012, 112:6156-6214. PubMed Abstract | Publisher Full Text OpenURL

  34. Chen D, Feng H, Li J: Graphene oxide: preparation, functionalization, and electrochemical applications.

    Chem Rev 2012, 112:6027-6053. PubMed Abstract | Publisher Full Text OpenURL

  35. Bai H, Li C, Shi G: Functional composite materials based on chemically converted graphene.

    Adv Mater 2011, 23:1089-1115. PubMed Abstract | Publisher Full Text OpenURL

  36. Tu Q, Pang L, Chen Y, Zhang Y, Zhang R, Lu B, Wang J: Effects of surface charges of graphene oxide on neuronal outgrowth and branching.

    Analyst 2014, 139:105-115. PubMed Abstract | Publisher Full Text OpenURL

  37. Katz EY: A chemically modified electrode capable of a spontaneous immobilization of amino compounds due to its functionalization with succinimidyl groups.

    J Electroanal Chem 1990, 291:257-260. Publisher Full Text OpenURL

  38. Lin S, Lee AS-Y, Lin C-C, Lee C-K: Determination of binding constant and stoichiometry for antibody-antigen interaction with surface plasmon resonance.

    Curr Proteomics 2006, 3:271-282. Publisher Full Text OpenURL

  39. Myszka DG: Kinetic analysis of macromolecular interactions using surface plasmon resonance biosensors.

    Curr Opin Biotechnol 1997, 8:50-57. PubMed Abstract | Publisher Full Text OpenURL

  40. Oshannessy DJ, Brighamburke M, Soneson KK, Hensley P, Brooks I: Determination of rate and equilibrium binding constants for macromolecular interactions using surface plasmon resonance: use of nonlinear least squares analysis methods.

    Anal Biochem 1993, 212:457-468. PubMed Abstract | Publisher Full Text OpenURL