Open Access Nano Express

Fabrication of self-assembled Au droplets by the systematic variation of the deposition amount on various type-B GaAs surfaces

Mao Sui1*, Ming-Yu Li1, Eun-Soo Kim1 and Jihoon Lee12*

Author Affiliations

1 College of Electronics and Information, Kwangwoon University, Nowon-gu Seoul 139-701, South Korea

2 Institute of Nanoscale Science and Engineering, University of Arkansas, Fayetteville, AR 72701, USA

For all author emails, please log on.

Nanoscale Research Letters 2014, 9:436  doi:10.1186/1556-276X-9-436

The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/9/1/436


Received:15 July 2014
Accepted:18 August 2014
Published:27 August 2014

© 2014 Sui et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly credited.

Abstract

The fabrication of self-assembled Au droplets is successfully demonstrated on various GaAs (n11)B, where n is 2, 4, 5, 7, 8, and 9, by the systematic variation of the Au deposition amount (DA) from 2 to 12 nm with subsequent annealing at 550°C. Under an identical growth condition, the self-assembled Au droplets of mini to supersizes are successfully synthesized via the Volmer-Weber growth mode. Depending on the DA, an apparent evolution is clearly observed in terms of the average height (AH), lateral diameter (LD), and average density (AD). For example, compared with the mini Au droplets with a DA of 2 nm, AH of 22.5 nm, and LD of 86.5 nm, the super Au droplets with 12-nm DA show significantly increased AH of 316% and LD of 320%, reaching an AH of 71.1 nm and LD of 276.8 nm on GaAs (211)B. In addition, accompanied with the dimensional expansion, the AD of Au droplets drastically swings on 2 orders of magnitudes from 3.2 × 1010 to 4.2 × 108 cm-2. The results are systematically analyzed with respect to the atomic force microscopy (AFM) and scanning electron microscopy (SEM) images, energy-dispersive X-ray spectrometry (EDS) spectra, cross-sectional line profiles, Fourier filter transform (FFT) power spectra, and root-mean-square (RMS) roughness as well as the droplet dimension and density summary, respectively.

Keywords:
Self-assembled Au droplets; Deposition amount; GaAs type-B; Nucleation; Diffusion

Background

Interests on semiconductor nanowires (NWs) are derived from their unique physical properties compared with the bulk materials such as the quantum confinement and increased cross sections [1,2] as well as their potentials to be adapted in numerous electronic, optoelectronic, and nanomechanic applications [3-5]. For instance, a single GaAs NW photovoltaic device has demonstrated 40% conversion efficiency over the 'Shockley-Queisser limit’ [5]. The fabrication of NWs is usually achieved via the metallic droplet-assisted vapor-liquid-solid (VLS) mechanism [6-8]. In the VLS, crystallization can occur at the liquid-solid interface due to the higher sticking coefficient and the Au droplets as a common catalyst exert an excellent capability of transferring the vapor phase precursors through the supersaturation regardless of the materials and substrates utilized. Naturally, NWs can only be grown at droplet sites, and thus, the fabrication of NWs including the size, density, and shape strongly depends on the fabrication of Au droplets. For example, ZnO NWs showed a larger diameter as well as lower density with the increased size of droplets [9]. To date, various NWs such as Si, Ge, ZnO, GaN, GaAs, InP, and InAs have been fabricated by the Au droplet-assisted VLS approach [9-16]. In the meantime, due to their unique properties and applications, such as localized surface plasmonic resonance, catalysis, quantum size effect, and bio-sensing, Au droplets have drawn a lot of research attention and have been demonstrated on diverse surfaces including Si, sapphire, SiO2, GaN SiC, and polymeric substrates [17-25]. As a common semiconductor with a direct band gap, GaAs is widely used in light-absorbing and light-emitting devices, and also various GaAs surfaces of different indices are often used in controlled fabrication of nanostructures. For example, the cross-sectional shape of NWs can be determined by substrate indices such as a triangular shape on GaAs (111)A, trapezoid shape on GaAs (110), and hexagonal shape on GaAs (111)B [26-28]. In addition, the resulting NWs on GaAs (111)B often showed stacking faults (SFs), and SF-free NWs can be successfully fabricated on GaAs (311)B and others [29-31]. This naturally puts the investigation on the Au droplets synthesized on a diverse GaAs index, which is an essential research topic in the fabrication of desired NWs. However, to date, systematic studies on Au droplets on type-B GaAs are still deficient.

In this paper, we thus demonstrate the fabrication of self-assembled Au droplets on various GaAs (n11)B, where n is 2, 4, 5, 7, 8, and 9 via the systematic variation of the Au deposition amount (DA). As an example, the simplified fabrication process of the self-assembled Au droplets on GaAs (211)B via the Volmer-Weber growth mode [32-34] is illustrated in Figure 1. Staring from the bare GaAs (211)B in Figure 1a, the surface still showed a quite smooth surface topography even after the 6-nm Au deposition as shown in Figure 1b,b-1. After a systematic annealing process, the resulting Au droplets are shown with the 3-nm deposition in Figure 1c and 6-nm DA in Figure 1d. Under an identical growth condition, the self-assembled Au droplets show drastically different sizes and densities, and as a function of the DA, a gradual dimensional expansion including the average height and the average diameter was clearly observed while the average density swings over 2 orders of magnitude. On the various substrates utilized, a similar trend of the evolution process was clearly observed while showing minor index dependency.

thumbnailFigure 1. Illustration of self-assembled Au droplet evolution on GaAs (211)B as a function of deposition amount (DA). (a) Bare GaAs surface. (b) After 3-nm Au deposition. (c) Au droplets with 3-nm DA. (d) Au droplets with 6-nm DA. (a-1) - (d-1) Line profiles of the cross sections marked with the white lines on AFM top views.

Methods

In this work, the fabrication of the self-assembled Au droplets was investigated on various GaAs type-B (n11) substrates, where n is 9, 8, 7, 5, 4, and 2 in a pulsed laser deposition (PLD) system. The GaAs wafers utilized in this work were semi-insulating or undoped with an off-axis of ±0.1° from the Wafer Technology Ltd. (Milton Keynes, UK). To start with, a batch of samples including the various type-B GaAs substrates was indium soldered on an Inconel sample holder side by side to maintain the uniformity among the samples and then was treated with a 30-min degas process at 350°C under 1 × 10-4 Torr to remove the contaminants. Subsequently, Au deposition was equally performed on the various type-B GaAs substrates at a growth rate of 0.05 nm/s with an ionization current of 3 mA under 1 × 10-1 Torr in a plasma ion-coater chamber. Au deposition of 2, 3, 4, 6, 9, and 12 nm was systematically performed, and regardless of the deposition amount, the surface showed a quite smooth morphology as shown in Figure 1b,b-1. As an example, Table 1 shows the root-mean-square (RMS) roughness (Rq) of the various GaAs surfaces after the 3-nm Au deposition as compared to the Figure 1b. Next, annealing process was implemented by a programmed recipe, and the substrate temperature (Tsub) was gradually increased to 550°C from the ambient temperature (approximately 25°C) at a fixed rate of 1.83°C/s under a chamber pressure of 1 × 10-4 Torr. After reaching the target Tsub (550°C) [35], the samples were dwelt for 150 s to ensure the maturation of the droplets. Immediately after the dwell process, the samples were quenched down to the ambient temperature to minimize the ripening effect [36,37]. An atomic force microscope (AFM) under atmospheric pressure was employed to characterize the surface morphology with non-contact tapping mode. The tips used in this work were NSC16/AIBS (μmasch, Lady's Island, SC, USA) with a curvature radius less than 10 nm. The spring constant was approximately 40 N/m, and the resonation frequency was approximately 170 kHz. A scanning electron microscope (SEM) under vacuum was utilized for the characterizations of the resulting samples, and energy-dispersive X-ray spectrometry (EDS) was utilized (Thermo Fisher Noran System 7, Thermo Fisher Scientific, Waltham, MA, USA) for the elemental analysis.

Table 1. Root-mean-square (RMS) roughness (Rq) of various GaAs surfaces after 3-nm Au deposition

Results and discussion

Figure 2 shows the self-assembled Au droplets on GaAs (211)B by the systematic variation of the Au DA from 2 to 12 nm with subsequent annealing at 550°C. Figure labels indicate the related DAs. AFM top views (3 × 3 μm2) of the corresponding samples are shown in Figure 2a,b,c,d,e,f along with enlarged 1 × 1 μm2 images below. The line profiles in Figure 3a-1,b-1,c-1,d-1,e-1,f-1 show the cross sections indicated by the white lines in the 1 × 1 μm2 images of Figure 2. The Fourier filter transform (FFT) power spectra shown in Figure 3a-1,b-1,c-1,d-1,e-1,f-1 are transformed from each AFM image. Figure 4a,b summarizes the average height (AH) and the lateral diameter (LD) of the self-assembled Au droplets, and Figure 4c,d shows the average density (AD) of the corresponding samples as well as the RMS surface roughness (Rq) as a function of the DA. The self-assembled Au droplets were fabricated based on the Volmer-Weber growth mode, thus resulting in the initial appearance of round dome-shaped droplets at 2 nm as in Figure 2a [32-34,38]. Once sufficient thermal energy for the surface diffusion is supplied, Au adatoms can be driven to diffuse. As a result of the binding energy between Au adatoms (Ea) being greater than the binding energy between Au adatoms and surface atoms (Ei), the Au droplets can be nucleated from the thin Au film during surface diffusion [39,40]. After the nucleation, nuclei can grow by absorbing nearby adatoms inward as well as merging with other smaller nuclei and thus can form into gradually larger round dome-shaped droplets. After systematic annealing with 2-nm deposition as shown in Figure 2a, dense Au droplets of round dome shapes were synthesized with an AH of 22.5 nm and LD of 86.5 nm, and the AD was 3.2 × 1010 cm-2 as plotted in Figure 4. When the DA was increased to 3 nm as shown in Figure 2b, the size of droplets was increased by × 1.38 to 31.1 nm for the AH and by × 1.23 to 106.5 nm for the LD as plotted in Figure 4a,b. Meanwhile, the corresponding AD was shapely decreased by × 3.08 from 3.2 × 1010 cm-2 to 1.04 × 1010 cm-2 as plotted in Figure 4c. Then at the 4-nm DA, the size of Au droplets was increased by × 1.44 to 44.9 nm for the AH and × 1.33 to 142.4 nm for the LD, and the AD was 3.9 × 109 cm-2 which was decreased by × 2.66. Then the trend, namely increased size along with the decreased density, was continuously maintained with the increased DA for 6 to 12 nm, and notably, at 6-nm DA as seen in Figure 2d, droplets began to show slightly irregular shapes without any preferential direction as evidenced by the round FFT power spectrum in Figure 3d-1. The LD measurements were performed along the shorter diameter. When the DA increased from 6 to 12 nm, the AH was further increased from 52.5 to 71.1 nm, the LD was increased from 186.2 to 276.8 nm, and the corresponding AD was dropped to 4.2 × 108 cm-2. Overall, with the DA variation from 2 to 12 nm, the AH of the self-assembled Au droplets was increased by × 3.16 from 22.5 to 71.1 nm and the LD was increased by × 3.20 from 86.5 to 276.8 nm as shown in Figure 4a,b. Meanwhile, the corresponding AD was decreased by nearly 2 orders from 3.2 × 1010 to 4.2 × 108 cm-2. The size of droplets can be increased with decreased density when more amount of material is provided. This evolution of size and density can be a conventional behavior, and it also can be observed with other self-assembled nanostructures [41-44]. The diffusion length (lD) can be defined as <a onClick="popup('http://www.nanoscalereslett.com/content/9/1/436/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/9/1/436/mathml/M1">View MathML</a> (where D is the surface diffusion coefficient and τ is the residence time), and the D has a strong proportional dependency on the substrate temperature (D ∝ Tsub). Then, driven by a high Tsub, the lD can be significantly increased. In a thermodynamic equilibrium system, nanostructures tend to increase their dimensions by absorbing nearby adatoms to lower the surface energy until reaching the equilibrium in order to keep the energy of the whole system in the lowest state. Therefore, when more adatoms exist within the lD, the increased dimensions of droplets can be expected. In terms of the uniformity, the color pattern of the FFT power spectrum represents the frequency of the height with a directionality. The FFT spectrum with the 2-nm DA in Figure 3a-1 showed a round shape due to the round shape of the droplets. With the 3-nm DA, a smaller core of the FFT pattern was observed due to the reduced height frequency associated with the reduced density in Figure 3b-1 as well as the AFM image in Figure 2b. Then, the FFT patterns in Figure 3c-1,d-1,e-1,f-1 with the increased DAs became smaller and smaller as the frequency of the height became narrower and uniform. In addition, flat tops of droplets were observed with the line profiles of the DAs of 9 and 12 nm in Figures 3e,f and 5e,f. This is in strong contrast with the round dome-shaped droplets at lower DAs. In the case of Si with the increased Au deposition amount, lateral growth of Au nanostructures occurred even with as low as approximately 5-nm DA and finally resulted in the formation of a merged Au layer at approximately 20-nm DA [45]. However, in this experiment, the droplets were still maintained even above 12-nm DA (not shown here). Although it is not very logical to compare GaAs and Si directly due to the different growth conditions such as temperature, from this result, it can be expected that the binding energy between Au adatoms and surface atoms (Ei) is weaker on GaAs surfaces than on Si (111). In other words, with increased DAs, droplets with lateral dimension expansion (coalescence) would require much higher DAs. In terms of the surface roughness (Rq) during the DA variation from 2 to 3 nm, the Rq was increased from 6.22 to 11.63 nm along with the expansion of the droplet dimensions as shown in Figure 4d. With the gradually increased DAs, the Rq in Figure 4d showed an increasing trend accompanied with increased droplet dimensions, 6.22 nm for the 2-nm DA and 11.63 for the 3-nm DA, and gradually increased to 24.37 nm at the 9-nm DA. Then, the Rq was saturated and showed a decreasing trend from there, likely due to the dominance of density decrease over the dimensional increase. Figure 6 shows the EDS spectra of the surface elemental characterization and the related SEM images of 4- and 12-nm samples. Generally, the resulting EDS spectra showed similar spectra for Ga and As with 4- and 12-nm DA as expected. The Kα1 peaks of Ga and As at 9.243 and 10.532 keV and Lα1 peaks of Ga and As at 1.096 and 1.282 keV were observed in Figure 6a,b. However, likely caused by the variation of the DA and the interaction volume of Au with the X-ray, the Au peaks show obvious difference in peak counts as seen in Figure 6a,b. For example, the Mα1 peak at 2.123 keV of the 12-nm sample showed a peak count value of approximately 22,000 while only approximately 5,000 for 4 nm. Also, the Lα1 peak at 9.711 keV showed a clear difference between 4 and 12 nm as shown in Figure 6a-2,b-2.

thumbnailFigure 2. Au droplet evolution on GaAs (211)B induced by the systematic variation of the Au DA. (a) 2 nm, (b) 3 nm, (c) 4 nm, (d) 6 nm, (e) 9 nm, and (f) 12 nm. Au droplets are presented with AFM top views of 3 × 3 μm2 and 1 × 1 μm2.

thumbnailFigure 3. Line profiles and corresponding FFT power spectra. (a-f) Line profiles of the cross sections indicated with the white lines in Figure 2a,b,c,d,e,f of 1 × 1 μm2 AFM top views. (a-1) - (f-1) The corresponding Fourier filter transform power spectra.

thumbnailFigure 4. Summary plots of self-assembled Au droplets on GaAs (211)B as a function of DA. (a) Average height (AH), (b) average lateral diameter (LD), (c) average density (AD), and (d) root-mean-square (RMS) roughness (Rq).

thumbnailFigure 5. Surface line profiles and corresponding FFT power spectra. (a-f) Surface line profiles of the cross sections indicated with the white lines in Figure 7a,b,c,d,e,f of 1 × 1 μm2 AFM top views. (a-1) - (f-1) The corresponding Fourier filter transform power spectra.

thumbnailFigure 6. EDS spectra and SEM images. Energy-dispersive X-ray spectroscopy (EDS) power spectra of samples with (a) 4-nm and (b) 12-nm DAs. (a-1), (b-1) The corresponding scanning electron microscope (SEM) images. (a-2), (b-2) The enlarged spectra between 9 to 11 keV.

Figure 7 shows the self-assembled Au droplets fabricated on GaAs (511)B, and the results are summarized with the AFM images in Figure 7a,b,c,d,e,f, the line profiles in Figure 5a,b,c,d,e,f, the FFT power spectra in Figure 5a-1,b-1,c-1,d-1,e-1,f-1, the summary plots of the size and density as well as the Rq in Figure 8a,b,c,d, and finally the SEM images in Figure 8e,f,g,h. Overall, the self-assembled Au droplets on GaAs (511)B showed a similar evolution tendency to that of the GaAs (211)B in terms of the AH, LD, AD, and Rq as plotted in Figure 8. Namely, the dimensions of the Au droplets including the AH and LD were gradually increased, while the AD was continuously decreased as a function of the DA. For example, while the DA was varied from 2 to 12 nm, the AH of droplets was increased by × 3.45 from 22.2 to 76.7 nm and the LD by × 3.79 from 85.1 to 323.2 nm as clearly shown in Figure 8a,b. The corresponding AD was dropped by × 103.2 from 3.2 × 1010 to 3.1 × 108 cm-2 as shown in Figure 8c. The FFT pattern started with a relatively larger round shape with 2-nm DA in Figure 5a-1 and gradually became smaller in size with the increased DA for the same reason discussed above as shown in Figure 5b-1,c-1,d-1,e-1,f-1. The Rq began with 5.88 nm for 2-nm DA and reached 21.71 nm for 9-nm DA, and then the Rq was decreased to 21.14 nm with 12-nm DA likely due to the dominance of the density decrease.

thumbnailFigure 7. Evolution of self-assembled Au droplets. This was induced by the systematic variation of the Au deposition amount from 2 to 12 nm on GaAs (511)B. (a) 2 nm, (b) 3 nm, (c) 4 nm, (d) 6 nm, (e) 9 nm, and (f) 12 nm. Au droplets are presented with AFM top views of 3 × 3 μm2 and 1 × 1 μm2.

thumbnailFigure 8. Summary plots and SEM images. Summary plots of (a) AH, (b) LD, (c) AD, and (d)Rq of the self-assembled Au droplets on GaAs (511)B as a function of DA. (e-h) SEM images of the resulting Au droplets with the DAs as labeled.

Figure 9 shows the Au droplet evolution as a function of the DA along with the systematic annealing at 550°C on GaAs (411)B, (711)B, (811)B, and (911)B, respectively. As summarized in Table 2, the results in terms of the size and density evolution are quite analogous to the previous two surfaces. For instance, the size of Au droplets on GaAs (411)B was gradually increased (by × 3.16 for AH and × 3.20 for LD), while the AD was progressively decreased by nearly 2 orders during the variation of the DAs from 2 to 12 nm as clearly shown in Table 2. Similar trends of Au droplet evolution on the other three surfaces can be clearly seen in Figure 9 with the comparable magnitude of changes. In general, various GaAs (n11)B show distinction in terms of the atom density, dangling bonds, and step density [29-31], and as a result, the resulting self-assembled nanostructures can show different behaviors in terms of size and density and even configurations. However, in this experiment, the difference in the result appeared to be minor. Perhaps, it is because the diffusion length of adatoms has a much stronger dependency on the activation energy and substrate temperature. As mentioned, the diffusion length increases by the square root of the product of the diffusion coefficient and residual time of adatoms (<a onClick="popup('http://www.nanoscalereslett.com/content/9/1/436/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/9/1/436/mathml/M2">View MathML</a>), and the diffusion coefficient is strongly proportional to the substrate temperature (D ∝ Tsub). In this experiment, the substrate temperature was fixed at 550°C, and thus the size of the Au droplets can be increased by absorbing Au adatoms within the diffusion length as discussed. Likewise, the diffusion length can also be affected by the variation of atom density, dangling bonds, and step density. However, the difference or the effect induced by the variation of the index to the surface diffusion seems to be relatively smaller as compared to that induced by the substrate temperature [35].

thumbnailFigure 9. Au droplet evolution as a function of the DA. (a-x) Self-assembled Au droplets fabricated by the variation of the Au deposition amount on GaAs (411)B, (711)B, (811)B, and (911)B. The resulting droplets are presented with AFM top views of 1 × 1 μm2.

Table 2. Summary of the self-assembled droplets on GaAs (211)B, (411)B, (511)B, (711)B, (811)B, and (911)B

Conclusions

In this study, the evolution of the self-assembled Au droplets was successfully demonstrated on various GaAs (n11)B, where n is 2, 4, 5, 7, 8, and 9. With the systematic variation of the DAs from 2 to 12 nm at a fixed annealing temperature of 550°C, the Au droplet growth progressed based on the Volmer-Weber growth mode and the results were methodically investigated with the AFM and SEM images, line profiles, and Fourier filter transform power spectra. In general, along with the gradually increased DAs, the self-assembled Au droplets showed the increased size of the AH and LD, while the AD showed a gradual decreasing tendency. More specifically, both the AH and LD were increased approximately three times while the density was varied around 2 orders of magnitude during the variation of the DAs from 2 to 12 nm. The size and density behavior of the self-assembled Au droplets was discussed based on the theories of kinetics and thermal dynamics. Au droplets exhibited minor index dependency, and this can be likely due to the strong dependency of adatom diffusion on the substrate temperate.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

MS, ML, and JL participated in the experiment design and carried out the experiments. MS, ML, EK, and JL participated in the analysis of data. MS, ML, and JL designed the experiments and testing methods. MS and JL carried out the writing of the manuscript. All authors helped in the drafting and read and approved the final manuscript.

Acknowledgements

This work was supported by the National Research Foundation (NRF) of Korea (nos. 2011-0030821 and 2013R1A1A1007118). This research was in part supported by a research grant of Kwangwoon University in 2014.

References

  1. Balandin AA: Nanophononics: phonon engineering in nanostructures and nanodevices.

    J Nanosci Nanotechnol 2005, 5:1015. PubMed Abstract | Publisher Full Text OpenURL

  2. Barbagiovanni EG, Lockwood DJ, Simpson PJ, Goncharova LV: Quantum confinement in Si and Ge nanostructures.

    Appl Phys Lett 2012, 111:034307. OpenURL

  3. Cao L, White JS, Park J-S, Schuller JA, Clemen BM, Brongersma ML: Engineering light absorption in semiconductor nanowire devices.

    Nat Mater 2009, 8:643. PubMed Abstract | Publisher Full Text OpenURL

  4. Huang Y, Duan X, Cui Y, Lieber CM: Gallium nitride nanowire nanodevices.

    Nano Lett 2002, 2:101. Publisher Full Text OpenURL

  5. Krogstrup P, Henrik Ingerslev J, Martin H, Olivier D, Holm JV, Martin A, Jesper N, Morral AF: Single-nanowire solar cells beyond the Shockley–Queisser limit.

    Nat Photonics 2013, 7:306. Publisher Full Text OpenURL

  6. Kolasinski KW: Catalytic growth of nanowires: vapor–liquid–solid, vapor–solid–solid, solution–liquid–solid and solid–liquid–solid growth.

    Curr Opin Solid State Mater Sci 2006, 10:182. Publisher Full Text OpenURL

  7. Wang H, Zepeda-Ruiz LA, Gilmer GH, Upmanyu M: Atomistics of vapour–liquid–solid nanowire growth.

    Nat Comm 2013, 4:1. OpenURL

  8. Yiying W, Yang P: Direct observation of vapor-liquid-solid nanowire growth.

    J Am Chem Soc 2001, 123:3165. Publisher Full Text OpenURL

  9. Dong Lai G, Xiao H, Guo Zhong X, Zhou Z, Gong Ping L, Mi H, Hua Z, Hongyu C, Tom W: Metal-layer-assisted coalescence of Au nanoparticles and its effect on diameter control in vapor-liquid-solid growth of oxide nanowires.

    Phys Rev B 2011, 83:045403. OpenURL

  10. Hannon JB, Kodambaka S, Ross FM, Tromp RM: The influence of the surface migration of gold on the growth of silicon nanowires.

    Nature 2006, 440:69. PubMed Abstract | Publisher Full Text OpenURL

  11. Chan CK, Xiao Feng Z, Yi C: High capacity Li ion battery anodes using Ge nanowires.

    Nano Lett 2008, 8:307. PubMed Abstract | Publisher Full Text OpenURL

  12. Duan X, Lieber CM: Laser-assisted catalytic growth of single crystal GaN nanowires.

    J Am Chem Soc 2000, 122:188. Publisher Full Text OpenURL

  13. Gudiksen MS, Lauhon LJ, Wang J, Smith DC, Lieber CM: Growth of nanowire superlattice structures for nanoscale photonics and electronics.

    Nature 2002, 415:617. PubMed Abstract | Publisher Full Text OpenURL

  14. Hong-yi X, Ya-nan G, Wen S, Zhi-ming L, Timothy B, Hao-feng L, Qiang G, Hark Hoe T, Chennupati J, Jin Z: Quantitative study of GaAs nanowires catalyzed by Au film of different thicknesses.

    Nanoscale Res Lett 2012, 7:589. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  15. Naji K, Saint-Girons G, Penuelas J, Patriarche G, Largeau L, Dumont H, Rojo-Romeo P, Gendry M: Influence of catalyst droplet diameter on the growth direction of InP nanowires grown on Si(001) substrate.

    Appl Phys Lett 2013, 102:243113. Publisher Full Text OpenURL

  16. Duan X, Lieber CM: General synthesis of compound semiconductor nanowires.

    Adv Mater 2000, 12:298. Publisher Full Text OpenURL

  17. Ruffino F, Torrisi V, Marletta G, Grimaldi MG: Growth morphology of nanoscale sputter-deposited Au films on amorphous soft polymeric substrates.

    Appl Phys A 2011, 103:939-949. Publisher Full Text OpenURL

  18. Cheng-Yen C, Jyh-Yang W, Fu-Ji T, Yen-Cheng L, Yean-Woei K, Yang CC: Fabrication of sphere-like Au nanoparticles on substrate with laser irradiation and their polarized localized surface plasmon behaviors.

    Optic Express 2009, 17:14186-14198. Publisher Full Text OpenURL

  19. Ressel B, Prince KC, Heun S, Homma Y: Wetting of Si surfaces by Au–Si liquid alloys.

    J Appl Phys 2003, 93:3886. Publisher Full Text OpenURL

  20. Liu J, Lee T, Janes DB, Walsh BL, Melloch MR, Woodall JM, Reifenberger R, Andres RP: Guided self-assembly of Au nanocluster arrays electronically coupled to semiconductor device layers.

    Appl Phys Lett 2000, 77:373. OpenURL

  21. Marie-Christine D, Didier A: Gold nanoparticles: assembly, supramolecular chemistry, quantum-size-related properties, and applications toward biology, catalysis, and nanotechnology.

    Chemical Reviews 2004, 104:293-346. PubMed Abstract | Publisher Full Text OpenURL

  22. Schaadt DM, Feng B, Yu ET: Enhanced semiconductor optical absorption via surface plasmon excitation in metal nanoparticles.

    Appl Phys Lett 2005, 86:063106. Publisher Full Text OpenURL

  23. Bing W, Haiqian W, Huixiang L, Changgan Z, Hou JG, Xudong X: Tunable single-electron tunneling behavior of ligand-stabilized gold particles on self-assembled monolayers.

    Physical Review B 2000, 63:035403. OpenURL

  24. Donnelly T, Krishnamurthy S, Carney K, McEvoy N, Lunney JG: Pulsed laser deposition of nanoparticle films of Au.

    Appl Surf Sci 2007, 254:1303. Publisher Full Text OpenURL

  25. Ruffino F, Grimaldi MG: Formation of patterned arrays of Au nanoparticles on SiC surface by template confined dewetting of normal and oblique deposited nanoscale films.

    Thin Solid Film 2013, 536:99. OpenURL

  26. Fortuna SA, Xiuling L: Metal-catalyzed semiconductor nanowires: a review on the control of growth directions.

    Semicond Sci Tech 2010, 25:024005. Publisher Full Text OpenURL

  27. Wacasera BA, Depperta K, Karlssonb LS, Samuelsona L, Seifert W: Growth and characterization of defect free GaAs nanowires.

    J Cryst Growth 2006, 287:504. Publisher Full Text OpenURL

  28. Fortuna SA, Jianguo W, Ik Su C, Xiuling L: Planar GaAs nanowires on GaAs (100) substrates: self-aligned, nearly twin-defect free, and transfer-printable.

    Nano Lett 2008, 8:4421. PubMed Abstract | Publisher Full Text OpenURL

  29. Yuan Z, Nomura KI, Nakano A: A core/shell mechanism for stacking-fault generation in GaAs nanowires.

    Appl Phys Lett 2012, 100:163103. Publisher Full Text OpenURL

  30. Shtrikman H, Popovitz-Biro R, Kretinin A, Heiblum M: Stacking-faults-free zinc blende GaAs nanowires.

    Nano Lett 2009, 9:1506. PubMed Abstract | Publisher Full Text OpenURL

  31. Ghosh SC, Kruse P, LaPierre RR: The effect of GaAs(100) surface preparation on the growth of nanowires.

    Nanotechnology 2009, 20:115602. PubMed Abstract | Publisher Full Text OpenURL

  32. Zhenyu Z, Lagally MG: Atomistic processes in the early stages of thin-film growth.

    Science 1997, 276:377-383. PubMed Abstract | Publisher Full Text OpenURL

  33. Ruffino F, Torrisi V, Marletta G, Grimaldi MG: Effects of the embedding kinetics on the surface nano-morphology of nano-grained Au and Ag films on PS and PMMA layers annealed above the glass transition temperature.

    Appl Phys A 2012, 107:669-683. OpenURL

  34. Schwartzkopf M, Buffet A, Korstgens V, Metwalli E, Schlage K, Benecke G, Perlich J, Rawolle M, Rothkirch A, Heidmann B, Herzog G, Muller-Buschbaum P, Rohlsberger R, Gehrke R, Norbert S, Roth SV: From atoms to layers: in situ gold cluster growth kinetics during sputter deposition.

    Nanoscale 2013, 5:5053-5062. PubMed Abstract | Publisher Full Text OpenURL

  35. Sui M, Li M-Y, Kim E-S, Lee J: Effect of annealing temperature on the fabrication of self-assembled gold droplets on various type-B GaAs surfaces.

    CrystEngComm 2014, 16:4390. Publisher Full Text OpenURL

  36. Voorhees PW: The theory of Ostwald ripening.

    J Stat Phys 1985, 38:231. Publisher Full Text OpenURL

  37. Bartelt NC: Ostwald ripening of two-dimensional islands on Si(001).

    Phys Rev B 1996, 54:11741. Publisher Full Text OpenURL

  38. Ruffino F, Canino A, Grimaldi MG, Giannazzo F, Bongiorno C, Roccaforte F, Raineri V: Self-organization of gold nanoclusters on hexagonal SiC and SiO2 surfaces.

    J Appl Phys 2007, 101:064306. Publisher Full Text OpenURL

  39. Venables JA, Spiller GDT, Hanbucken M: Nucleation and growth of thin films.

    Rep Progr Phys 1984, 47:399. Publisher Full Text OpenURL

  40. Abraham DB, Newman CM: Equilibrium Stranski-Krastanow and Volmer-Weber models.

    Lett J Exploring Front Phys 2009, 86:16002. OpenURL

  41. Lee J, Wang Z, Hirono Y, Kim E-S, Kim N, Park S, Cong W, Salamo GJ: Various configurations of In nanostructures on GaAs (100) by droplet epitaxy.

    CrystEngComm 2010, 12:3404-3408. Publisher Full Text OpenURL

  42. Ziad Y, Abu W, Wang ZM, Lee JH, Salamo GJ: Observation of Ga droplet formation on (311)A and (511)A GaAs surfaces.

    Nanotechnology 2006, 17:4037. PubMed Abstract | Publisher Full Text OpenURL

  43. Lee JH, Wang ZM, Salamo GJ: Observation of change in critical thickness of In droplet formation on GaAs(100).

    J Phys Condens Matter 2010, 19:176223. OpenURL

  44. Ruffino F, Canino A, Grimaldi MG, Giannazzo F, Roccaforte F, Raineri V: Electrical properties of self-assembled nano-Schottky diodes.

    J Nanomater 2008, 2008:243792. OpenURL

  45. Li M-Y, Sui M, Eun-Soo K, Jihoon L: Droplets to merged nanostructures: evolution of gold nanostructures by the variation of deposition amount on Si(111).

    Crystal Growth Des 2014, 14:1128-1134. Publisher Full Text OpenURL