Open Access Highly Accessed Nano Express

Catechin-capped gold nanoparticles: green synthesis, characterization, and catalytic activity toward 4-nitrophenol reduction

Yoonho Choi1, Myung-Jin Choi2, Song-Hyun Cha2, Yeong Shik Kim3, Seonho Cho2 and Youmie Park12*

Author Affiliations

1 College of Pharmacy, Inje University, 197 Inje-ro, Gimhae, Gyeongnam 621-749, Republic of Korea

2 National Creative Research Initiatives (NCRI) Center for Isogeometric Optimal Design, Seoul National University, 1 Gwanak-ro, Gwanak-gu, Seoul 151-744, Republic of Korea

3 College of Pharmacy and Natural Products Research Institute, Seoul National University, 1 Gwanak-ro, Gwanak-gu, Seoul 151-742, Republic of Korea

For all author emails, please log on.

Nanoscale Research Letters 2014, 9:103  doi:10.1186/1556-276X-9-103


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/9/1/103


Received:10 February 2014
Accepted:24 February 2014
Published:3 March 2014

© 2014 Choi et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly credited.

Abstract

An eco-friendly approach is described for the green synthesis of gold nanoparticles using catechin as a reducing and capping agent. The reaction occurred at room temperature within 1 h without the use of any external energy and an excellent yield (99%) was obtained, as determined by inductively coupled plasma mass spectrometry. Various shapes of gold nanoparticles with an estimated diameter of 16.6 nm were green-synthesized. Notably, the capping of freshly synthesized gold nanoparticles by catechin was clearly visualized with the aid of microscopic techniques, including high-resolution transmission electron microscopy, atomic force microscopy, and field emission scanning electron microscopy. Strong peaks in the X-ray diffraction pattern of the as-prepared gold nanoparticles confirmed their crystalline nature. The catalytic activity of the as-prepared gold nanoparticles was observed in the reduction of 4-nitrophenol to 4-aminophenol in the presence of NaBH4. The results suggest that the newly prepared gold nanoparticles have potential uses in catalysis.

Keywords:
Green synthesis; Catechin; Gold nanoparticles; Catalysis; 4-Nitrophenol reduction

Background

Recent advances in nanotechnology have resulted in diverse applications of gold nanoparticles (AuNPs) in various research fields. AuNPs are the most stable NPs and are used in novel applications, including as vehicles for drug/gene delivery, catalysts, optical sensors, and imaging and visualization agents [1-3]. In addition, the catalytic properties of AuNPs have been explored, and the AuNPs have been found to exhibit improved catalytic performance compared with that of their bulk counterpart. The catalytic activity of AuNPs has been commonly evaluated using a well-known reaction: the reduction of 4-nitrophenol (4-NP) to 4-aminophenol (4-AP) in the presence of NaBH4. 4-NP is an industrial waste and environmental hazard with a long degradation time. Thus, the removal of this component from water is important for public health. The product, 4-AP, is a useful intermediate in the manufacture of antipyretics and analgesics.

Recently, the green synthesis of AuNPs using biological entities as reducing agents has been rapidly replacing chemical methods in which toxic chemicals are utilized. This approach provides numerous benefits, including the high biocompatibility and good water solubility of the resultant AuNPs. Furthermore, the process is eco-friendly and time and cost effective. Plant extracts and pure compounds from plant sources have been demonstrated to be highly effective reducing agents for the synthesis of AuNPs [4].

Catechins are flavanol compounds that are abundant in tea. The biological activities of tea catechins have been extensively reviewed elsewhere [5-8]. Among tea catechins, catechin and epigallocatechin gallate have been used for the synthesis or modification of NPs [9-12]. Ointment of a combination of AuNPs with the antioxidant epigallocatechin gallate and α-lipoic acid accelerated cutaneous wound healing through anti-inflammatory and antioxidant effects [9]. In particular, the topical application of this combined ointment promoted the proliferation and migration of dermal keratinocytes and fibroblasts, which enhanced the restoration of normal skin structures. The same research group has reported that the topical application of the ointment of AuNPs (3 to 5 nm in size) with epigallocatechin gallate and α-lipoic acid effectively promoted wound healing in diabetic mice [10]. The attractive biological activity of epigallocatechin gallate-modified AuNPs is their anticancer activity, which includes efficacy in the treatment of prostate and bladder cancers [11,12]. As an analytical application, catechin-modified TiO2-NPs were used as matrices for the analysis of steroid hormones using surface-assisted laser desorption/ionization mass spectrometry [13]. When catechin was bound to the TiO2-NP surface, the absorption wavelength increased at 337 nm when compared with that of the unmodified TiO2-NPs, which led to an increase in the N2 laser absorption efficiencies [13]. As another analytical application, catechin-synthesized AuNPs were used as a nanosensor for the fluorescent detection of lead in water and urine samples [14].

Herein, catechin was used as a reducing agent for the green synthesis of AuNPs at room temperature for 1 h, and the use of other toxic chemicals as reducing agents was avoided (referred to hereafter as catechin-AuNPs). The catechin-AuNPs were characterized using UV-visible spectrophotometry, high-resolution transmission electron microscopy (HR-TEM), atomic force microscopy (AFM), field emission scanning electron microscopy (FE-SEM), and high-resolution X-ray diffraction (HR-XRD). The reaction yield of the synthesis was measured using inductively coupled plasma mass spectrometry (ICP-MS). Furthermore, the catalytic activity of catechin-AuNPs was evaluated on the basis of the reduction of 4-NP to 4-AP in the presence of NaBH4.

Methods

4-Nitrophenol, hydrochloroauric acid trihydrate (HAuCl4 · 3H2O), sodium borohydride, and (+)-catechin hydrate were purchased from Sigma-Aldrich (St. Louis, MO, USA). Carbon-coated copper grids (carbon type-B, 300 mesh) were purchased from Ted Pella (Redding, CA, USA). The RTESP AFM probe (MPP-11100-10, premium high-resolution tapping mode silicon probe) was obtained from Bruker Nano (Santa Barbara, CA, USA). Mica (grade V-1, 25 mm × 25 mm length, 0.15 mm thick) was purchased from SPI Supplies Division of Structure Probe (West Chester, PA, USA). All the other reagents were of analytical grade. The UV-visible spectra were recorded using a Shimadzu UV-2600 with a quartz cuvette (Shimadzu Corporation, Kyoto, Japan). The HR-TEM images were acquired with a JEM-3010 (JEOL, Tokyo, Japan) operated at 300 kV. The AFM images were obtained using a Dimension® Icon® (Bruker Nano, Santa Barbara, CA, USA) operated under tapping mode. The sample-loaded mica and copper grids were dried in a 60°C oven overnight before the analyses. The FE-SEM images were collected in a JSM-7100 F SEM using an accelerating voltage of 15 kV (JEOL). ICP-MS analysis was performed in an ELAN 6100 (Perkin-Elmer SCIEX, Waltham, MA, USA). The ICP-MS samples were prepared using centrifugation. The centrifugation of catechin-AuNPs was performed at 12,300 × g for 40 min, and the supernatant containing the unreacted Au3+ was used for ICP-MS analysis. The total concentration of Au3+ of the catechin-AuNPs solution was also measured using ICP-MS. The average value of the three measurements was used to determine the yield. For HR-XRD analyses, the catechin-AuNP solution was centrifuged at 12,300 × g for 40 min to remove the supernatant. The pellet was pooled and freeze-dried. The freeze-dried samples were prepared with a FD5505 freeze dryer (Il Shin Bio, Seoul, Korea). A Bruker D8 Discover high-resolution X-ray diffractometer (Bruker, Karlsruhe, Germany) equipped with a CuKα radiation source (λ = 0.1541 nm) was used in the range of 20° to 90° (2θ scale).

The stock solutions of HAuCl4 · 3H2O (0.5 mM) and catechin (0.5 mM) were prepared using deionized water. Then, 600 μL of HAuCl4 · 3H2O (0.5 mM) was placed in a 5-mL glass vial with 200 μL of deionized water, and catechin (0.5 mM, 200 μL) was subsequently added to this solution. The reaction mixture was then further incubated under ambient temperature (26°C) for 1 h. The synthesis of gold nanoparticles was monitored through the acquisition of UV-visible spectra.

To evaluate the catalytic activity of the catechin-AuNPs, the reduction of 4-NP to 4-AP in the presence of NaBH4 was performed. The catalytic reduction of 4-NP was conducted in aqueous solution under ambient temperature (26°C), and UV-visible spectra were measured in a quartz cuvette. The 4-NP solution (899.9 μL, 0.15 mM) was mixed with deionized water (450.1 μL). Then, freshly prepared NaBH4 (1.65 mL, 5.5 mM) was added. To this reaction mixture, 1 mL of freshly synthesized catechin-AuNPs was added. UV-visible spectra were recorded at a time interval of 5 min in the range of 200 to 700 nm.

Results and discussion

Green synthesis and the yield of catechin-AuNPs

The color of the solution changed to purple upon reduction of Au3+ to Au0 by catechin (Figure 1). The characteristic surface plasmon resonance (SPR) band was observed at 553 nm, which indicated the successful synthesis of AuNPs. The reaction proceeded under ambient temperature (26°C) for 1 h, which means the reaction was fast and required minimal energy as well as being eco-friendly. The reaction proceeded very rapidly, as indicated by the color becoming purple (which indicates the reduction of Au3+) within 1 min.

thumbnailFigure 1. UV-visible spectra of catechin-AuNPs before and after the reaction at room temperature for 1 h.

In general, the stability of tea catechins is affected by temperature and pH [15,16]. The thermal degradation of catechins is noticeable upon with an increase in temperature. Furthermore, tea catechins are very stable at pH levels less than 4, whereas the stability of catechins decreases in alkaline solutions. In terms of the stability point, the reaction conditions that were used in the present research minimized the thermal and pH degradation of catechin, which may have facilitated the reaction. The pH of the HAuCl4 solution was less than 4, and no other reagents were added to adjust the pH. In addition, the reaction was performed under ambient temperature (26°C) without the input of any external energy.

We determined the yield of the reaction by measuring the concentration of unreacted Au3+ using ICP-MS. After the sample was subjected to centrifugation, the purple color disappeared in the supernatant, which indicated that the AuNPs were effectively separated from the unreacted Au3+. The yield was 99.1% indicating that the reaction occurred very efficient.

HR-TEM images

HR-TEM images generally provide information regarding the size, shape, and dispersion state of NPs. As illustrated in Figure 2, various shapes of AuNPs were synthesized, including spherical, triangular, pentagonal, hexagonal with nonequilateral edges, irregular, and urchin-like shapes. A high-magnification image of several AuNPs is presented in Figure 2B. All the AuNPs were surrounded by shells, which were also observed in the AFM and FE-SEM images. The width of the shells was measured to be 5.41 ± 0.21 nm from ten measurements taken from Figure 2B. A lattice fringe is clearly observed in Figure 2C, which indicates the crystalline nature of the synthesized AuNPs. In addition, the shell is also clearly observed in Figure 2C. Another interesting shape is the urchin-like shape observed in Figures 2D,E,F. The high-magnification image in Figure 2F clearly reveals the lattice fringes in the urchin-like shapes, which also confirms the crystalline nature of the AuNPs. The crystalline structure of the catechin-AuNPs will be further discussed in the HR-XRD section. Lu and co-workers reported the synthesis of biocompatible and urchin-like-shaped AuNPs with excellent surface-enhanced Raman scattering (SERS) activity [17]. Notably, Wang and co-workers observed that Au urchin-like shapes exhibit much greater SERS activity compared to that of Au microspheres [18].

thumbnailFigure 2. HR-TEM images of freshly green-synthesized AuNPs. The scale bar represents (A) 100 nm, (B) 20 nm, (C) 5 nm, (D) 100 nm, (E) 20 nm, and (F) 5 nm.

We hypothesized that the shells that surrounded the AuNPs in Figure 2 might be catechin playing a role as a capping and stabilizing agent. To test this hypothesis, catechin-AuNPs were stored at room temperature for 6 days. As illustrated in Figure 3, the shells all disappeared, and mostly amorphous-shaped AuNPs were observed; these AuNPs exhibited a tendency to aggregate. Thus, we concluded that the shells are catechins playing an essential role in stabilizing the colloidal AuNPs.

thumbnailFigure 3. HR-TEM images of 6-day-old AuNPs. The scale bar represents (A) 100 nm and (B) 20 nm.

AFM and FE-SEM images

The AFM and FE-SEM images provide further information regarding the 3-D structures and topography of the nanostructures. The 3-D height AFM image in Figure 4A clearly shows that the AuNPs were successfully green-synthesized using catechin as a reducing agent. In the height image, the brighter color NPs possess greater heights. As mentioned previously in the HR-TEM section, the shells were also observed in the AFM images. In the 2-D and 3-D amplitude error images, the shells were clearly discernible from the AuNPs (Figures 4B,C). In the 3-D phase images shown in Figure 4D, the light-yellow-colored AuNPs are surrounded by dark-purple-colored shells. The section analysis of lines a-b and c-d in Figure 4E is depicted in Figure 4F. The heights of randomly selected NPs were measured to be 8.26 to 10.33 nm. In addition, the average value of shell height was determined to be 2.99 nm. The FE-SEM images in which all of the AuNPs possessed shells were consistent with the HR-TEM and AFM image analyses (Figure 5).

thumbnailFigure 4. AFM images. (A) 3-D height (10 μm × 10 μm), (B) 2-D amplitude error (500 nm × 500 nm), (C) 3-D amplitude error (500 nm × 500 nm), (D) 3-D phase (500 nm × 500 nm), (E) 2-D height (500 nm × 500 nm), and (F) section analysis of lines a-b and c-d in image (E).

thumbnailFigure 5. FE-SEM images. The magnifications of the images are (A) × 33,000, (B) × 150,000, and (C) × 160,000.

XRD analysis

The crystalline structure of metallic Au was confirmed by HR-XRD analysis (Figure 6). Intense diffraction peaks were observed at 38.2°, 44.3°, 64.5°, 77.7°, and 81.7°, corresponding to the (111), (200), (220), (311), and (222) planes, respectively, of face-centered cubic (fcc) Au. The predominant orientation was the (111) plane because the most intense peak appeared at 38.2°. The (200)/(111) intensity ratio was 0.32. When compared with the conventional bulk intensity ratio of 0.52, the observed value was low, indicating that the (111) plane was the primary one [19].

thumbnailFigure 6. HR-XRD analysis.

The Debye-Scherrer equation (D = 0.89λ/Wcosθ) was employed to estimate the particle diameter from the (111) peak, and the estimated diameter was approximately 16.6 nm. The definition of each term in the equation is as follows: λ is the wavelength of CuKα radiation (0.1541 nm), W is the full-width at half-maximum of the (111) peak, θ is the diffraction angle, and D is the particle diameter.

Catalytic activity toward 4-nitrophenol reduction

The catalytic activity of green-synthesized AuNPs has been evaluated by other researchers [19-24]. The biological entities used in these studies were cyclodextrins and plant extracts (a glucan of an edible mushroom (Pleurotus florida), Trigonella foenum-graecum, ayurvedic arishtams, Anacardium occidentale, and Gnidia glauca). The merit of our method over these reports lies in its energy-saving process, in which no input of external energy is used for the green synthesis of the catechin-AuNPs; in contrast, the other methods used elevated temperatures for the reactions. To evaluate the catalytic activity of the catechin-AuNPs, the reduction reaction of 4-NP to 4-AP in the presence of NaBH4 was studied. When NaBH4 was added to 4-NP, the color of the solution became yellow, which resulted in a peak at 400 nm in the UV-visible spectrum because of the formation of the 4-nitrophenolate anion. The reaction did not proceed any further in the absence of the catechin-AuNP catalyst. Upon the addition of catechin-AuNPs, the appearance of 4-AP was monitored by the emergence of a peak at 300 nm with a concomitant decrease in the intensity of the peak at 400 nm (Figure 7A). The decreased intensity of the peak at 400 nm and the appearance of the peak at 300 nm were quantitatively monitored by UV-visible spectrophotometry. The approximate time required for the completion of the reaction was 30 min.

thumbnailFigure 7. 4-NP reduction by NaBH4 in the presence of catechin-AuNPs catalyst. (A) UV-visible spectra and (B) a plot of ln(Ct/C0) as a function of time (min).

The relationship between ln(Ct/C0) and time (min) revealed a linear correlation (y = −0.091x + 0.071, r2 = 0.981), where C0 and Ct are the 4-NP concentration at time 0 and time t, respectively (Figure 7B) [21]. The ratio of absorbance, At/A0, could be substituted for the ratio of concentration, Ct/C0 (i.e., Ct/C0 = At/A0) because the concentration of 4-NP is proportional to its absorbance [21]. On the basis of these results, we determined that the shell did not affect the catalytic activity of the catechin-AuNPs.

Conclusions

Catechin, which is a potent antioxidant, has been successfully utilized as a green reducing agent for the synthesis of AuNPs. No external energy was necessary during the 1 h reaction, which was simple, fast, energy-saving, and eco-friendly. Together with spherically shaped AuNPs, anisotropic AuNPs with diverse shapes were also observed. The crystalline nature of the AuNPs was confirmed by the resulting HR-XRD peaks and the lattice fringes in the HR-TEM images. Most notably, the capping of AuNPs with catechins was clearly visualized in the microscopic images. The width and height information of the shells was obtained from the HR-TEM and AFM images, respectively. The catechin shells were observed to disappear after the catechin-AuNPs were stored at ambient temperature, during which the aggregation of the AuNPs increased. Thus, catechin plays a role as a reducing agent and is also responsible for the capping of AuNPs. The catalytic activity of catechin-AuNPs for the reduction of 4-NP demonstrated that the newly-prepared AuNPs can be used as a catalyst that is prepared via a green synthesis route.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

YC performed the green synthesis of the catechin-AuNPs. MJC, SHC, and YP characterized the catechin-AuNPs. YSK, SC, and YP supervised the entire process and drafted the manuscript. All authors read and approved the final manuscript.

Acknowledgements

This work was supported by a National Research Foundation of Korea (NRF) grant funded by the Korean government: the Ministry of Education (NRF-2012R1A1A2042224) and the Ministry of Science, ICT & Future Planning (NRF-2010-18282). This financial support is gratefully acknowledged. The authors would like to thank Ms. Sang Hui Jun for assisting in the preparation of this manuscript.

References

  1. Mieszawska AJ, Mulder WJ, Fayad ZA, Cormode DP: Multifunctional gold nanoparticles for diagnosis and therapy of disease.

    Mol Pharm 2013, 10:831-847. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  2. Dreaden EC, Austin LA, Mackey MA, El-Sayed MA: Size matters: gold nanoparticles in targeted cancer drug delivery.

    Ther Deliv 2012, 3:457-478. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  3. Vigderman L, Zubarev ER: Therapeutic platforms based on gold nanoparticles and their covalent conjugates with drug molecules.

    Adv Drug Deliv Rev 2013, 65:663-676. PubMed Abstract | Publisher Full Text OpenURL

  4. Park Y, Hong YN, Weyers A, Kim YS, Linhardt RJ: Polysaccharides and phytochemicals: a natural reservoir for the green synthesis of gold and silver nanoparticles.

    IET Nanobiotechnol 2011, 5:69-78. PubMed Abstract | Publisher Full Text OpenURL

  5. Mak JC: Potential role of green tea catechins in various disease therapies: progress and promise.

    Clin Exp Pharmacol Physiol 2012, 39:265-273. PubMed Abstract | Publisher Full Text OpenURL

  6. Yang CS, Wang X: Green tea and cancer prevention.

    Nutr Cancer 2010, 62:931-937. PubMed Abstract | Publisher Full Text OpenURL

  7. Lambert JD, Elias RJ: The antioxidant and pro-oxidant activities of green tea polyphenols: a role in cancer prevention.

    Arch Biochem Biophys 2010, 501:65-72. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  8. Friedman M: Overview of antibacterial, antitoxin, antiviral, and antifungal activities of tea flavonoids and teas.

    Mol Nutr Food Res 2007, 51:116-134. PubMed Abstract | Publisher Full Text OpenURL

  9. Leu JG, Chen SA, Chen HM, Wu WM, Hung CF, Yao YD, Tu CS, Liang YJ: The effects of gold nanoparticles in wound healing with antioxidant epigallocatechin gallate and alpha-lipoic acid.

    Nanomedicine 2012, 8:767-775. PubMed Abstract | Publisher Full Text OpenURL

  10. Chen SA, Chen HM, Yao YD, Hung CF, Tu CS, Liang YJ: Topical treatment with anti-oxidants and Au nanoparticles promote healing of diabetic wound through receptor for advance glycation end-products.

    Eur J Pharm Sci 2012, 47:875-883. PubMed Abstract | Publisher Full Text OpenURL

  11. Hsieh DS, Wang H, Tan SW, Huang YH, Tsai CY, Yeh MK, Wu CJ: The treatment of bladder cancer in a mouse model by epigallocatechin-3-gallate-gold nanoparticles.

    Biomaterials 2011, 32:7633-7640. PubMed Abstract | Publisher Full Text OpenURL

  12. Shukla R, Chanda N, Zambre A, Upendran A, Katti K, Kulkarni RR, Nune SK, Casteel SW, Smith CJ, Vimal J, Boote E, Robertson JD, Kan P, Engelbrecht H, Watkinson LD, Carmack TL, Lever JR, Cutler CS, Caldwell C, Kannan R, Katti KV: Laminin receptor specific therapeutic gold nanoparticles (198AuNP-EGCg) show efficacy in treating prostate cancer.

    Proc Natl Acad Sci USA 2012, 109:12426-12431. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  13. Chiu TC: Steroid hormones analysis with surface-assisted laser desorption/ionization mass spectrometry using catechin-modified titanium dioxide nanoparticles.

    Talanta 2011, 86:415-420. PubMed Abstract | Publisher Full Text OpenURL

  14. Wu YS, Huang FF, Lin YW: Fluorescent detection of lead in environmental water and urine samples using enzyme mimics of catechin-synthesized Au nanoparticles.

    ACS Appl Mater Interfaces 2013, 5:1503-1509. PubMed Abstract | Publisher Full Text OpenURL

  15. Su YL, Leung LK, Huang Y, Chen ZY: Stability of tea theaflavins and catechins.

    Food Chem 2003, 83:189-195. Publisher Full Text OpenURL

  16. Wang R, Zhou W, Wen RA: Kinetic study of the thermal stability of tea catechins in aqueous systems using a microwave reactor.

    J Agric Food Chem 2006, 54:5924-5932. PubMed Abstract | Publisher Full Text OpenURL

  17. Lu L, Ai K, Ozaki Y: Environmentally friendly synthesis of highly monodisperse biocompatible gold nanoparticles with urchin-like shape.

    Langmuir 2008, 24:1058-1063. PubMed Abstract | Publisher Full Text OpenURL

  18. Wang X, Yang DP, Huang P, Li M, Li C, Chen D, Cui D: Hierarchically assembled Au microspheres and sea urchin-like architectures: formation mechanism and SERS study.

    Nanoscale 2012, 4:7766-7772. PubMed Abstract | Publisher Full Text OpenURL

  19. Sen IK, Maity K, Islam SS: Green synthesis of gold nanoparticles using a glucan of an edible mushroom and study of catalytic activity.

    Carbohydr Polym 2013, 91:518-528. PubMed Abstract | Publisher Full Text OpenURL

  20. Aswathy Aromal S, Philip D: Green synthesis of gold nanoparticles using Trigonella foenum-graecum and its size-dependent catalytic activity.

    Spectrochim Acta A Mol Biomol Spectrosc 2012, 97:1-5. PubMed Abstract | Publisher Full Text OpenURL

  21. Huang T, Meng F, Qi L: Facile synthesis and one-dimensional assembly of cyclodextrin-capped gold nanoparticles and their applications in catalysis and surface-enhanced Raman scattering.

    J Phys Chem C 2009, 113:13636-13642. Publisher Full Text OpenURL

  22. Aromal SA, Babu KV, Philip D: Characterization and catalytic activity of gold nanoparticles synthesized using ayurvedic arishtams.

    Spectrochim Acta A Mol Biomol Spectrosc 2012, 96:1025-1030. PubMed Abstract | Publisher Full Text OpenURL

  23. Sheny DS, Mathew J, Philip D: Synthesis characterization and catalytic action of hexagonal gold nanoparticles using essential oils extracted from Anacardium occidentale.

    Spectrochim Acta A Mol Biomol Spectrosc 2012, 97:306-310. PubMed Abstract | Publisher Full Text OpenURL

  24. Ghosh S, Patil S, Ahire M, Kitture R, Gurav DD, Jabgunde AM, Kale S, Pardesi K, Shinde V, Bellare J, Dhavale DD, Chopade BA: Gnidia glauca flower extract mediated synthesis of gold nanoparticles and evaluation of its chemocatalytic potential.

    J Nanobiotechnology 2012, 10:17. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL