Large-scale and controllable synthesis of metal-free nitrogen-doped carbon nanofibers and nanocoils over water-soluble Na2CO3

Qian Ding12, Xueyin Song12, Xiujuan Yao12, Xiaosi Qi123, Chak-Tong Au4, Wei Zhong12* and Youwei Du12

Author Affiliations

1 Nanjing National Laboratory of Microstructures, Nanjing University, Nanjing 210093, People’s Republic of China

2 Jiangsu Provincial Laboratory for Nanotechnology, Nanjing University, Nanjing 210093, People’s Republic of China

3 College of Science, Guizhou University, Guiyang, 550025, People’s Republic of China

4 Chemistry Department, Hong Kong Baptist University, Hong Kong 852, People’s Republic of China

For all author emails, please log on.

Nanoscale Research Letters 2013, 8:545  doi:10.1186/1556-276X-8-545

The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/545


Received:11 July 2013
Accepted:17 December 2013
Published:27 December 2013

© 2013 Ding et al.; licensee Springer.

This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Using acetylene as carbon source, ammonia as nitrogen source, and Na2CO3 powder as catalyst, we synthesized nitrogen-doped carbon nanofibers (N-CNFs) and carbon nanocoils (N-CNCs) selectively at 450°C and 500°C, respectively. The water-soluble Na2CO3 is removed through simple washing with water and the nitrogen-doped carbon nanomaterials can be collected in high purity. The approach is simple, inexpensive, and environment-benign; it can be used for controlled production of N-CNFs or N-CNCs. We report the role of catalyst, the effect of pyrolysis temperature, and the photoluminescence properties of the as-harvested N-CNFs and N-CNCs.

Keywords:
Carbon materials; Chemical vapor deposition; Water-soluble; Nitrogen-doped

Background

Since Iijima’s paper on helical carbon nanotubes, carbon nanomaterials (CNM) such as carbon nanotubes (CNT) and carbon nanofibers (CNF) have attracted great attention for their unique and outstanding electrical and mechanical properties [1-4]. The helical CNT are composed of five-membered or seven-membered rings, having carbon atoms of sp2 and sp3 hybridization [5,6]. It is envisaged that helical CNT exhibit novel and peculiar properties that are different from those of linear CNT. It has been suggested that CNM can be utilized in hydrogen storage [7,8], microwave absorption [9], and field emission [10,11]. Using CNM, scientists tried to fabricate nanosized electromagnetism devices [12-14] such as solenoid switch [15,16], miniature antenna [17,18], energy converter [19,20], and sensor [21,22].

For CNM generation, methods such as arc discharge, laser ablation, hydrothermal carbonization, solvothermal reduction, and chemical vapor deposition (CVD) are used [23-28]. Nonetheless, it is common to have metal impurities in the products, and the intrinsic properties of the as-obtained CNM are uncertain. The problem of metal impurities hinders further researches on CNM especially those related to electromagnetism features [29,30]. It is tedious and costly to remove metal impurities such as those of iron-group elements or their alloys [31]. Furthermore, unexpected defects or contaminants could be introduced into the CNM during purification procedures.

As a traditional method, CVD has its advantages [32,33]. By regulating parameters such as catalyst amount, reaction temperature, source flow rate, one can obtain different kinds of CNM. It is possible to control the CVD process for a designated outcome by adopting a particular set of reaction conditions [34,35]. Using acetylene as carbon precursor, Amelinckx et al. [36], Nitze et al. [37], and Tang et al. [38] obtained CNM with high purity and selectivity. Nevertheless, there are disadvantages such as high reaction temperature and outgrowth of desired product [28,39]. As for the growth mechanism of CNT in CVD processes, there are still controversies [40,41].

By doping foreign elements such as nitrogen and boron into the graphite lattices of CNM, Wang et al. [42], Ayala et al. [43], and Koós et al. [44] induced crystal and electronic changes to the structures of CNM [42-44]. It is noted that as support for palladium nanoparticles, helical CNM show excellent properties in electro-catalytic applications [45,46]. According to Franceschini et al. [47] and Mandumpal et al. [48], the introduction of nitrogen restrains the aggregation of vacancies, resulting in defects and dislocations, as well as amplified curvature of graphite planes. The results of both experimental and theoretical studies demonstrate that compared to pure CNT, nitrogen-doped CNT show enhanced field emission properties and there is a shift of the dominant emission towards lower energies [49-51]. Through theoretical studies of heteroatom-substituted graphite systems, Hagiri et al. suggested that different heteroatom arrangements cause different spin-stable singlet and triplet states and that the substituted nitrogen atom as a spin cap induces the π electron excess [52]. When it comes to CNT utilization, high incorporation of nitrogen is desirable in promoting porosity and electrochemical reactivity of CNT. On the other hand, if CNT are supposed to be applied in semiconductor technology, low nitrogen-doping density is necessary.

Recently, we reported the large-scale synthesis of various kinds of non-doped CNM that are metal-free [53-55]. Herein, we report the use of Na2CO3 as catalyst for the selective formation of nitrogen-doped CNF (N-CNF) and nitrogen-doped CNC (N-CNC). We used Na2CO3 because it is water-soluble and can be removed from N-CNM through steps of water washing. We found that the Na2CO3 catalyst prepared by us is active and selective for mass formation of N-CNF and N-CNC. By means of CVD using Na2CO3 as catalyst, high-purity N-CNM can be obtained after washing the products with deionized water and ethanol. The approach is simple, inexpensive, and environment-benign, and can be used for mass production of high-purity N-CNF and N-CNC.

Methods

All materials used were commercially available and analytically pure. In the present study, we employed Na2CO3 as catalyst. First, we mixed 10 g of Na2CO3 (in powder form) in 200 ml of deionized water at room temperature (RT) with continuous stirring. Once a transparent solution was obtained, the solution was kept at 80°C for several hours and allowed to cool down to RT for the precipitation of a white powder. The powder was filtered out, dried, and ground into tiny particles.

We placed 0.5 g of catalyst at the center of a ceramic boat with two open ends. The boat was then put inside a quartz tube with a thermocouple attached to its center. For the CVD reaction, we used acetylene as carbon source and ammonia as nitrogen source. After the reaction chamber was purged with argon for the elimination of oxygen, the sources were introduced into the system at either 450°C or 500°C at a C2H2/NH3 flow rate ratio of 1:1 for 6 h. To study the effect of changing the flow rate ratio, we also introduced acetylene and ammonia at a C2H2/NH3 flow rate ratio of 5:1 at 450°C for 6 h. After the reaction, argon was again introduced to protect the product from oxidation until the system was cooled down to RT. To remove the catalyst and to avoid organic outgrowth, the as-obtained products were repeatedly washed with deionized water and ethanol. Compared to the methods commonly used for CNM purification, the one used in the present study causes no damage to the desired product.

The morphologies of samples were examined using a transmission electron microscope (TEM) operated at an accelerating voltage of 200 kV and a field emission scanning electron microscope (FE-SEM) operated at an accelerating voltage of 5 kV. Fourier transform infrared (FTIR) spectroscopic studies of samples (in KBr pellets) were conducted over a Nocolet 510P spectrometer (Thermo Nocolet, Stanford, CT, USA). The surface analysis of products was carried out by means of X-ray photoelectron spectroscopy (XPS, PHI 5000 VersaProbe, UIVAC-PHI Inc., Chigasaki, Kanagawa, Japan). The products were examined on an X-ray powder diffractometer (XRD) at RT for phase identification using CuKα radiation (model D/Max-RA, Rigaku Corporation, Tokyo, Japan). Raman spectroscopic investigations were performed over a Jobin-Yvon Labram HR800 instrument (Horiba, Ann Arbor, MI, USA) with 514.5-nm Ar laser excitation. The photoluminescence (PL) spectra were collected at RT over a spectrofluorophotometer (Shimadzu RF-5301 PC; Shimadzu Co. Ltd., Beijing, China) using a Xe lamp as light source. For PL investigation, about 0.1 mg of sample was ultrasonically dispersed in 5 ml of deionized water. Thermoanalysis was carried out using a thermal analysis system (NETZSCH STA 449C; NETZSCH Company, Shanghai, China) with the sample heated in air at a rate of 20°C/min.

Results and discussion

We observed that when reaction temperature is higher than 500°C or lower than 400°C, the yield of CNM is small (TEM observation). Above 500°C, there is heavy decomposition of Na2CO3 into sodium oxide and CO2, a situation unfavorable for CNM formation. Below 400°C, the decomposition of acetylene becomes unfavorable. Since there could be Na2CO3 decomposition at certain reaction temperatures, we do not choose weight change as a means to measure product yields. Shown in Table 1 are the conditions used for the generation of CNM.

Table 1. Preparation summary of samples

Figure 1 shows the XRD patterns of the as-obtained and purified samples. The peaks of Na2CO3 can be indexed to the monoclinic phase of Na2CO3 (JCPDS 37–0451) with a = 8.906 Å, b = 5.238 Å, and c = 6.045 Å. Figure 1a,b is the patterns of C450 and C450N before and after purification, respectively. It is apparent that there are graphite carbon and Na2CO3 in CNM and N-CNM before purification. After repeated washing with water and ethanol, there is complete elimination of Na2CO3 as well as ethanol-soluble organic outgrowth. With the incorporation of nitrogen, there is decline of graphite signal intensity.

thumbnailFigure 1. XRD patterns of (a) as-obtained and (b) purified samples.

Figure 2 shows the FE-SEM and TEM images of the purified samples. The selectivity to carbon species was determined statistically according to the number of counts of CNM at different regions of the TEM and FE-SEM images. The images of C5N1 are not given here for they are similar to those of C450 and C450N. As shown in Figure 2a,d, the major constitution of C450 is long and composed of linear carbon nanofibers (LCNF). The rest is irregular carbon complexes, and there is no detection of helical carbon nanofibers (HCNF). According to the TEM images, the average diameter of LCNF is ca. 20 nm. In other words, LCNF can be synthesized in large scale with high selectivity using this method. As shown in Figure 2b,e, the major product of C450N is still LCNF, but there is sighting of helical structures. As shown in the inset of Figure 2b, there are sightings of long HCNF. The TEM images indicate that the obtained LCNF and HCNF have average diameter of ca. 30 nm. The results show that with the doping of nitrogen into graphitic lattices, there is change in CNM morphology: the generation of helical structures. When the reaction temperature is 500°C, the major product of C500N is the long spiny carbon nanofibers (SCNF) (Figure 2c,f), having average diameter of ca. 100 nm. It is known that reaction temperature is a parameter that affects the synthesis of nanomaterials in terms of morphology, structure, and component. Through the control of morphology, structure, and/or component, it is possible to obtain CNM of particular properties. In the case of long SCNF, the material is enriched with multi-pillar structures and is relatively large in specific surface area. With such physical properties, the material can be used as support for better dispersion of nanoparticles.

thumbnailFigure 2. FE-SEM and TEM images of C450, C450N, and C500N. FE-SEM images of (a) C450, (b) C450N, and (c) C500N, and the TEM images of (d) C450, (e) C450N, and (f) C500N (insets are the corresponding high-magnification images).

XPS O1s, C1s, and N1s spectra were obtained for the determination of surface composition and bonding environment of C and N atoms of the purified samples. The nitrogen content of a particular product is defined as 100 N/(C + N + O) at.%. As depicted in Table 2, the amounts of nitrogen in C450, C5N1, C450N, and C500N are 0%, 1.77%, 2.86%, and 2.10%, respectively. It is noted that the oxygen contents of the four samples are about 4%. Based on the results, we deduce that a rise of nitrogen source at reaction temperature of 450°C results in products higher in nitrogen content. However, with a rise of reaction temperature from 450°C to 500°C, there is a slight decline of nitrogen content. It is plausible that NH3 decomposition is enhanced with temperature rise, but the concurrent decomposition of catalyst goes against the formation of nitrogen-doped CNT. That C500N is lower than C450N in nitrogen content is a net consequence of the two actions.

Table 2. Nitrogen content of samples

According to some researches, the electronic properties of CNM can be tuned by doping nitrogen atoms into the carbon lattices and be regulated by controlling the type, concentration, and content of dopants [56,57]. We observe that C450, C5N1, C450N, and C500N show C1s, N1s, and O1s peaks at around 284, 400, and 532 eV, respectively (Figure 3a). As shown in Figure 3b, the C1s peak can be deconvoluted into two components at 284.1 and 285.8 eV. The stronger one at 284.1 eV is ascribed to the carbon of sp2-hybridized C-C bonds whereas that at 285.8 eV to carbon of C-N bonds. There are three primary statuses of nitrogen configuration in nitrogen-doped CNMs: graphitic (substitutional nitrogen), pyridine-like, and pyrrole-like. In order to analyze the electronic state of nitrogen atoms in CNMs, we focused our attention especially to the N1s spectra, as revealed in Figure 3c. The peak around 398.3 eV is attributed to sp3-hybridized nitrogen of the tetrahedral phase; the nitrogen is pyridine-type and is connected with the defective graphite sheets. The peak at 399.8 eV is ascribable to nitrogen with a local structure alike that of pyrrole, and the nitrogen is hence considered as pyrrole-type. The peak at 401.0 eV corresponds to sp2-hybridized nitrogen of trigonal phase, and the nitrogen is graphite-type or substitutional type. The composition of the three types of nitrogen is reflected by the area ratio of the corresponding N1s peaks. With rise of reaction temperature from 400°C to 500°C, there is a significant increase of graphitic nitrogen relative to that of pyridine-type nitrogen. It is deduced that the formation of graphitic configuration becomes more favorable with the rise of temperature.

thumbnailFigure 3. XPS spectra of the purified samples. (a) Survey scan, (b) C1s spectra, (c) N1s spectra, and (d) illustration of nitrogen configuration.

Figure 4 shows the Raman spectra of C450, C5N1, C450N, and C500N. Each of the samples exhibits two peaks. The one at about 1,340 cm-1 (called D band) is associated with amorphous carbon relating to the vibration of carbon atoms with dangling bonds of disordered graphite. The peak at about 1,600 cm-1 (called G band) is related to the double-degenerate E2g mode of graphite, corresponding to the vibration of triple-degenerate sp2 hybrid bond. The intensity ratio of G band and D band (IG/ID) is generally used to identify the crystallinity of graphite. Lower IG/ID means more defect or vacancy. The intensity ratios of C450, C5N1, C450N, and C500N are listed in Table 3.

thumbnailFigure 4. Raman spectra of C450, C5N1, C450N, and C500N.

Table 3. The IG/ID intensity ratios of all samples

Compared with C5N1, C450N is lower in IG/ID value. The C2H2/NH3 flow rate ratio for the formation of C5N1 is 5:1 whereas that of C450N is 1:1. In other words, with a source flow richer in nitrogen, there is rise of nitrogen content, and with more defects or vacancies in N-CNM, there is decline of IG/ID value. With the rise of reaction temperature from 450°C to 500°C, there is slight decrease of nitrogen content but enhanced formation of amorphous carbon, and the net result is the further decline of IG/ID value.

The PL spectra of C450, C5N1, and C450N obtained with an excitation source of 220 nm wavelength are showed in Figure 5a. It is known that pristine CNM exhibits strong UV PL at 368 nm at RT. In the present study, we find that by doping of nitrogen into CNM, there is enhancement of UV PL, and PL signal intensifies with the rise of nitrogen content. The peak at 468 nm is a sideband peak, and its intensity is usually weaker than that of 368 nm. The super peak at about 440 nm is the double wavelength of 220 nm attributable to the excitation wavelength. In Figure 5b, with the excitation wavelength increasing from 220 to 280 nm, the intensity of the PL peak at 368 nm decreases. When the excitation wavelength reaches 300 nm, there is the detection of a peak at about 410 nm over the C450N sample as shown in Figure 5c. The peak is a purple band. There is no detection of such a peak at about 410 nm over the C450 and C5N1 samples. We ascribe the phenomenon to the impurity transition level induced by doping nitrogen of a certain concentration into the graphite lattice. It is hence possible to modulate the luminescence peak in a controllable manner from visible light to the UV band by doping CNT with different concentrations of nitrogen.

thumbnailFigure 5. PL spectra of C450, C5N1, and C450. (a) C450, C5N1, and C450 with an excitation wavelength of 220 nm. (b) C450N with different excitation wavelengths ranging from 220 to 280 nm. (c) C450, C5N1, and C450 with an excitation wavelength of 300 nm.

Figure 6 is the FTIR spectrum of C450N. The peak at 3,455.8 cm-1 can be ascribed to the stretching vibration of unsaturated –CH = CH–. The peaks at 1,610.3 and 1,441.9 cm-1 are ascribed to –C-H stretching vibration while that at 879.4 cm-1 to –C-H deformation vibration. Compared to the FTIR result of our previous study [53], the nitrogen-doped CNM shows weaker peak intensity and poorer transmittance plausibly due to the presence of defects or vacancies.

thumbnailFigure 6. FTIR spectrum of C450N. Inset is the FTIR spectrum of C450, after [53].

We tested the oxidation resistance of C450 and C450N. As shown in Figure 7, both samples are sharply oxidized at about 460°C, at a temperature lower than that for the oxidation of CNM generated in CVD processes using iron-group metals or their alloys as catalysts [58,59]. Furthermore, the oxidation of C450N starts at about 460°C, and it is not so with C450. The results suggest that there are more active defects and amorphous carbon in C450N in comparison with C450.

thumbnailFigure 7. TGA curve of C450 and C450N.

Conclusions

By controlling the acetylene decomposition temperature, N-CNF and N-CNC can be selectively synthesized in large scale over Na2CO3. Due to the water-soluble property of NaCO3, the products can be obtained in high purity through steps of water and ethanol washing. The CVD process using Na2CO3 as catalyst is simple, inexpensive, and environment-benign. We detect graphitic, pyridine-like as well as pyrrole-like N species in the nitrogen-doped CNM. Compared to the non-doped pristine CNM, the nitrogen-doped ones show enhanced UV PL intensity.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

WZ and QD designed the study and guided this work. XYS, XJY, and XSQ participated in the design of the study. QD carried out the experiments, analyzed the data, and drafted the manuscript. WZ and CTA checked and revised the manuscript. CTA and YWD gave precious suggestions to this work. All authors read and approved the final manuscript.

Acknowledgements

This work was supported by the National Natural Science Foundation of China (grant no. 11174132), the National Key Project for Basic Research (grant nos. 2010CB923402 and 2011CB922102), and PAPD, People’s Republic of China.

References

  1. Iijima S: Helical microtubules of graphitic carbon.

    Nature 1991, 354:56-58. Publisher Full Text OpenURL

  2. Iijima S, Ichihashi T: Single-shell carbon nanotubes of 1-nm diameter.

    Nature 1993, 363:603-605. Publisher Full Text OpenURL

  3. Bethune DS, Johnson RD, Salem JR, Devries MS, Yannoni CS: Atoms in carbon cages - the structure and properties of endohedral fullerenes.

    Nature 1993, 366:123-128. Publisher Full Text OpenURL

  4. Rodriguez NM, Chambers A, Baker RTK: Catalytic engineering of carbon nanostructures.

    Langmuir 1995, 11:3862-3866. Publisher Full Text OpenURL

  5. Tamura R, Tsukada M: Electronic states of the cap structure in the carbon nanotube.

    Phys Rev B 1995, 52:6015-6026. Publisher Full Text OpenURL

  6. Terrones H, Terrones M, Hernandez E, Grobert N, Charlier JC, Ajayan PM: New metallic allotropes of planar and tubular carbon.

    Phys Rev Lett 2000, 84:1716-1719. PubMed Abstract | Publisher Full Text OpenURL

  7. Tans SJ, Verschueren ARM, Dekker C: Room-temperature transistor based on a single carbon nanotube.

    Nature 1998, 393:49-52. Publisher Full Text OpenURL

  8. Bai XD, Zhong DY, Zhang GY, Ma XC, Liu S, Wang EG, Chen Y, Shaw DT: Hydrogen storage in carbon nitride nanobells.

    Appl Phys Lett 2001, 79:1552-1554. Publisher Full Text OpenURL

  9. Wadhawan A, Garrett D, Perez JM: Nanoparticle-assisted microwave absorption by single-wall carbon nanotubes.

    Appl Phys Lett 2003, 83:2683-2685. Publisher Full Text OpenURL

  10. Adessi C, Devel M: Theoretical study of field emission by single-wall carbon nanotubes.

    Phys Rev B 2000, 62:13314-13317. Publisher Full Text OpenURL

  11. Shim M, Javey A, Kam NWS, Dai HJ: Polymer functionalization for air-stable n-type carbon nanotube field-effect transistors.

    J Am Chem Soc 2001, 123:11512-11513. PubMed Abstract | Publisher Full Text OpenURL

  12. Dai HJ, Hafner JH, Rinzler AG, Colbert DT, Smalley RE: Nanotubes as nanoprobes in scanning probe microscopy.

    Nature 1996, 384:147-150. Publisher Full Text OpenURL

  13. Tsukagoshi K, Alphenaar BW, Ago H: Coherent transport of electron spin in a ferromagnetically contacted carbon nanotube.

    Nature 1999, 401:572-574. Publisher Full Text OpenURL

  14. Yang CK, Zhao J, Lu JP: Magnetism of transition-metal/carbon-nanotube hybrid structures.

    Phys Rev Lett 2003, 90:257203. PubMed Abstract | Publisher Full Text OpenURL

  15. Liu L, Jayanthi CS, Tang MJ, Wu SY, Tombler TW, Zhou CW, Alexseyev L, Kong J, Dai H: Controllable reversibility of an sp(2) to sp(3) transition of a single wall nanotube under the manipulation of an AFM tip: a nanoscale electromechanical switch?

    Phys Rev Lett 2000, 84:4950-4953. PubMed Abstract | Publisher Full Text OpenURL

  16. Banerjee P, Wolny F, Pelekhov DV, Herman MR, Fong KC, Weissker U, Muhl T, Obukhov Y, Leonhardt A, Buchner B, Hammel PC: Magnetization reversal in an individual 25 nm iron-filled carbon nanotube.

    Appl Phys Lett 2010, 96:252505-252505.

    -3

    Publisher Full Text OpenURL

  17. Dresselhaus MS: Applied physics - nanotube antennas.

    Nature 2004, 432:959-960. PubMed Abstract | Publisher Full Text OpenURL

  18. Kempa K, Rybczynski J, Huang ZP, Gregorczyk K, Vidan A, Kimball B, Carlson J, Benham G, Wang Y, Herczynski A, Ren ZF: Carbon nanotubes as optical antennae.

    Adv Mater 2007, 19:421. Publisher Full Text OpenURL

  19. Zhang J, Hu YS, Tessonnier JP, Weinberg G, Maier J, Schlogl R, Sheng DS: CNFs@CNTs: superior carbon for electrochemical energy storage.

    Adv Mater 2008, 20:1450. Publisher Full Text OpenURL

  20. Guldi DM, Sgobba V: Carbon nanostructures for solar energy conversion schemes.

    Chem Commun 2011, 47:606-610. Publisher Full Text OpenURL

  21. Baughman RH, Zakhidov AA, de Heer WA: Carbon nanotubes - the route toward applications.

    Science 2002, 297:787-792. PubMed Abstract | Publisher Full Text OpenURL

  22. Kong J, Franklin NR, Zhou CW, Chapline MG, Peng S, Cho KJ, Dai H: Nanotube molecular wires as chemical sensors.

    Science 2000, 287:622-625. PubMed Abstract | Publisher Full Text OpenURL

  23. Loiseau A, Willaime F, Demoncy N, Hug G, Pascard H: Boron nitride nanotubes with reduced numbers of layers synthesized by arc discharge.

    Phys Rev Lett 1996, 76:4737-4740. PubMed Abstract | Publisher Full Text OpenURL

  24. Journet C, Maser WK, Bernier P, Loiseau A, delaChapelle ML, Lefrant S, Deniard P, Lee R, Fischer JE: Large-scale production of single-walled carbon nanotubes by the electric-arc technique.

    Nature 1997, 388:756-758. Publisher Full Text OpenURL

  25. Liu ZP, Zhou XF, Qian YT: Synthetic methodologies for carbon nanomaterials.

    Adv Mater 2010, 22:1963-1966. PubMed Abstract | Publisher Full Text OpenURL

  26. Sawant SY, Somani RS, Bajaj HC: A solvothermal-reduction method for the production of horn shaped multi-wall carbon nanotubes.

    Carbon 2010, 48:668-672. Publisher Full Text OpenURL

  27. Ebbesen TW, Ajayan PM: Large-scale synthesis of carbon nanotubes.

    Nature 1992, 358:220-222. Publisher Full Text OpenURL

  28. Cassell AM, Raymakers JA, Kong J, Dai HJ: Large scale CVD synthesis of single-walled carbon nanotubes.

    J Phys Chem B 1999, 103:6484-6492. Publisher Full Text OpenURL

  29. Banks CE, Crossley A, Salter C, Wilkins SJ, Compton RG: Carbon nanotubes contain metal impurities which are responsible for the “electrocatalysis” seen at some nanotube-modified electrodes.

    Angew Chemie-Int Ed 2006, 45:2533-2537. Publisher Full Text OpenURL

  30. Jones CP, Jurkschat K, Crossley A, Compton RG, Riehl BL, Banks CE: Use of high-purity metal-catalyst-free multiwalled carbon nanotubes to avoid potential experimental misinterpretations.

    Langmuir 2007, 23:9501-9504. PubMed Abstract | Publisher Full Text OpenURL

  31. Park TJ, Banerjee S, Hemraj-Benny T, Wong SS: Purification strategies and purity visualization techniques for single-walled carbon nanotubes.

    J Mater Chem 2006, 16:141-154. Publisher Full Text OpenURL

  32. Leal MCA, Horna CD: CVD and the new technologies.

    An Quim 1991, 87:445-456. OpenURL

  33. Li QW, Yan H, Cheng Y, Zhang J, Liu ZF: A scalable CVD synthesis of high-purity single-walled carbon nanotubes with porous MgO as support material.

    J Mater Chem 2002, 12:1179-1183. Publisher Full Text OpenURL

  34. Kong J, Zhou C, Morpurgo A, Soh HT, Quate CF, Marcus C, Dai H: Synthesis, integration, and electrical properties of individual single-walled carbon nanotubes.

    Appl Phys A Mater Sci Process 1999, 69:305-308. Publisher Full Text OpenURL

  35. Su M, Zheng B, Liu J: A scalable CVD method for the synthesis of single-walled carbon nanotubes with high catalyst productivity.

    Chem Phys Lett 2000, 322:321-326. Publisher Full Text OpenURL

  36. Amelinckx S, Zhang XB, Bernaerts D, Zhang XF, Ivanov V, Nagy JB: A formation mechanism for catalytically grown helix-shaped graphite nanotubes.

    Science 1994, 265:635-639. PubMed Abstract | Publisher Full Text OpenURL

  37. Nitze F, Abou-Hamad E, Wagberg T: Carbon nanotubes and helical carbon nanofibers grown by chemical vapour deposition on C60 fullerene supported Pd nanoparticles.

    Carbon 2010, 49:1101-1109. OpenURL

  38. Tang NJ, Wen JF, Zhang Y, Liu FX, Lin KJ, Du YW: Helical carbon nanotubes: catalytic particle size-dependent growth and magnetic properties.

    ACS NANO 2010, 4:241-250. PubMed Abstract | Publisher Full Text OpenURL

  39. Li YY, Sakoda A: Growth of carbon nanotubes and vapor-grown carbon fibers using chemical vapor deposition of methane.

    J Chin Inst Chem Eng 2002, 33:483-489. OpenURL

  40. Lee CJ, Lyu SC, Cho YR, Lee JH, Cho KI: Diameter-controlled growth of carbon nanotubes using thermal chemical vapor deposition.

    Chem Phys Lett 2001, 341:245-249. Publisher Full Text OpenURL

  41. Emmenegger C, Bonard JM, Mauron P, Sudan P, Lepora A, Grobety B, Züttela A, Schlapbach L: Synthesis of carbon nanotubes over Fe catalyst on aluminium and suggested growth mechanism.

    Carbon 2003, 41:539-547. Publisher Full Text OpenURL

  42. Wang B, Ma YF, Wu YP, Li N, Huang Y, Chen YS: Direct and large scale electric arc discharge synthesis of boron and nitrogen doped single-walled carbon nanotubes and their electronic properties.

    Carbon 2009, 47:2112-2115. Publisher Full Text OpenURL

  43. Ayala P, Arenal R, Rummeli M, Rubio A, Pichler T: The doping of carbon nanotubes with nitrogen and their potential applications.

    Carbon 2010, 48:575-586. Publisher Full Text OpenURL

  44. Koós AA, Dillon F, Obraztsova EA, Crossley A, Grobert N: Comparison of structural changes in nitrogen and boron-doped multi-walled carbon nanotubes.

    Carbon 2010, 48:3033-3041. Publisher Full Text OpenURL

  45. Hu GZ, Nitze F, Sharifi T, Barzegar HR, Wagberg T: Self-assembled palladium nanocrystals on helical carbon nanofibers as enhanced electrocatalysts for electro-oxidation of small molecules.

    J Mater Chem 2012, 22:8541-8548. Publisher Full Text OpenURL

  46. Hu GZ, Nitze F, Barzegar HR, Sharifi T, Mikolajczuk A, Tai CW, Borodzinski A, Wågberg T: Palladium nanocrystals supported on helical carbon nanofibers for highly efficient electro-oxidation of formic acid, methanol and ethanol in alkaline electrolytes.

    J Power Sources 2012, 209:236-242. OpenURL

  47. Franceschini DF, Achete CA, Freire FL: Internal-stress reduction by nitrogen incorporation in hard amorphous-carbon thin-films.

    Appl Phys Lett 1992, 60:3229-3231. Publisher Full Text OpenURL

  48. Mandumpal J, Gemming S, Seifert G: Curvature effects of nitrogen on graphitic sheets: structures and energetics.

    Chem Phys Lett 2007, 447:115-120. Publisher Full Text OpenURL

  49. Wang XB, Liu LQ, Zhu DB, Zhang L, Ma HZ, Yao N, Zhang B: Controllable growth, structure, and low field emission of well-aligned CNx nanotubes.

    J Phys Chem B 2002, 106:2186-2190. Publisher Full Text OpenURL

  50. Wang C, Qiao L, Qu CQ, Zheng WT, Jiang Q: First-principles calculations on the emission properties of pristine and N-doped carbon nanotubes.

    J Phys Chem C 2009, 113:812-818. Publisher Full Text OpenURL

  51. Li LJ, Glerup M, Khlobystov AN, Wiltshire JG, Sauvajol JL, Tavlor RA, Nicholas RJ: The effects of nitrogen and boron doping on the optical emission and diameters of single-walled carbon nanotubes.

    Carbon 2006, 44:2752-2757. Publisher Full Text OpenURL

  52. Hagiri I, Takahashi N, Takeda K: Theoretical possibility of the variety of ground-state spin arrangements created by the spin hole and spin cap in a pi-conjugated system.

    J Phys Chem A 2004, 108:2290-2304. Publisher Full Text OpenURL

  53. Qi XS, Ding Q, Zhang H, Zhong W, Au C, Du YW: Large-scale and controllable synthesis of metal-free carbon nanofibers and carbon nanotubes over water-soluble Na2CO3.

    Mater Lett 2012, 81:135-137. OpenURL

  54. Qi XS, Zhong W, Yao XJ, Zhang H, Ding Q, Wu Q, Deng Y, Au C, Du Y: Controllable and large-scale synthesis of metal-free carbon nanofibers and carbon nanocoils over water-soluble NaxKy, catalysts.

    Carbon 2012, 50:646-658. Publisher Full Text OpenURL

  55. Qi X, Ding Q, Zhong W, Au C-T, Du Y: Controllable synthesis and purification of carbon nanofibers and nanocoils over water-soluble NaNO3.

    Carbon 2013, 56:383-385. OpenURL

  56. Glerup M, Castignolles M, Holzinger M, Hug G, Loiseau A, Bernier P: Synthesis of highly nitrogen-doped multi-walled carbon nanotubes.

    Chem Commun 2003, 2003:2542-2543. OpenURL

  57. He MS, Zhou S, Zhang J, Liu ZF, Robinson C: CVD growth of N-doped carbon nanotubes on silicon substrates and its mechanism.

    J Phys Chem B 2005, 109:9275-9279. PubMed Abstract | Publisher Full Text OpenURL

  58. Murakami Y, Miyauchi Y, Chiashi S, Maruyama S: Characterization of single-walled carbon nanotubes catalytically synthesized from alcohol.

    Chem Phys Lett 2003, 374:53-58. Publisher Full Text OpenURL

  59. Chen CM, Dai YM, Huang JG, Jehng JM: Intermetallic catalyst for carbon nanotubes (CNTs) growth by thermal chemical vapor deposition method.

    Carbon 2006, 44:1808-1820. Publisher Full Text OpenURL