SpringerOpen Newsletter

Receive periodic news and updates relating to SpringerOpen.

Open Access Nano Express

a-Si:H/SiNW shell/core for SiNW solar cell applications

Eman Sad Ashour12*, Mohamad Yusof Bin Sulaiman2, Mohd Hafidz Ruslan2 and Kamaruzzaman Sopian2

Author Affiliations

1 Department of Physics, Faculty of Science and Technology, Universiti Kebangsaan Malaysia (UKM), Bangi 43600, Malaysia

2 Solar Energy Research Institute (SERI), Universiti Kebangsaan Malaysia (UKM), Bangi 43600, Malaysia

For all author emails, please log on.

Nanoscale Research Letters 2013, 8:466  doi:10.1186/1556-276X-8-466


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/466


Received:16 June 2013
Accepted:29 September 2013
Published:6 November 2013

© 2013 Ashour et al.; licensee Springer.

This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Vertically aligned silicon nanowires have been synthesized by the chemical etching of silicon wafers. The influence of a hydrogenated amorphous silicon (a-Si:H) layer (shell) on top of a silicon nanowire (SiNW) solar cell has been investigated. The optical properties of a-Si:H/SiNWs and SiNWs are examined in terms of optical reflection and absorption properties. In the presence of the a-Si:H shell, 5.2% reflection ratio in the spectral range (250 to 1,000 nm) is achieved with a superior absorption property with an average over 87% of the incident light. In addition, the characteristics of the solar cell have been significantly improved, which exhibits higher open-circuit voltage, short-circuit current, and efficiency by more than 15%, 12%, and 37%, respectively, compared with planar SiNW solar cells. Based on the current–voltage measurements and morphology results, we show that the a-Si:H shell can passivate the defects generated by wet etching processes.

Keywords:
Silicon nanowire; Solar cells; a-Si:H; Antireflection coating; Metal-assisted wet chemical etching; PECVD

Background

Silicon nanowires (SiNWs) attract significant attention because of their potential applications in many fields like sensors, transistors, lithium batteries, diodes, and photovoltaics [1-5]. Particularly, they can be applied on silicon solar cells as an antireflection coating, due to low average reflectance values [6,7]. Several synthesis methods have been used to fabricate SiNWs including chemical vapor deposition [8], laser ablation [9], thermal evaporation, and solution methods [10-12]. Among these synthesis methods, wet chemical etching has been frequently used to prepare SiNWs. Metal-assisted wet chemical etching is advantageous for achieving SiNWs with controlled diameter, length, spacing, and density, avoiding expensive and low-throughput usual lithographic processes [13].

Recently, it has been shown that a silicon nanowire antireflection coating (ARC) prepared by metal-assisted wet chemical etching is a near-perfect antireflection coating [14]. The superior antireflection property of the nanowire surface is attributed to three reasons: huge surface area of SiNWs, rough surface morphology which leads to strong light scattering as well as absorption, and graded refractive index profile between air and SiNWs that closely implies a multilayer antireflection coating [6,14,15]. Some other properties of SiNWs, for example, crystal ordination, good doping level, and excellent uniformity, imply appropriate utilization of SiNWs in silicon solar cells.

Despite all these features, the maximum efficiency of planar solar cells using SiNW ARC does not exceed 10%. This low efficiency is attributed to many factors. One of the most important is the surface recombination velocity which strongly increases when using SiNW ARC, due to the large surface area [16,17]. It is necessary, therefore, to passivate the SiNW surface, minimizing the surface states [18].

Among all materials used to passivate planar silicon solar cells, hydrogenated amorphous silicon (a-Si:H) has attracted much attention since Sanyo's first declaration of the heterojunction with intrinsic thin layer (HIT) solar cell design [19]. From that time, HIT solar cell efficiency exceeds 22%, and the surface passivation capability of a-Si:H was intensively studied [19,20]. Finding that interstitial a-Si:H is the main cause of reduction of the surface state density results in high-quality passivation of the silicon surface [21,22]. Additionally, a thin layer of a-Si:H was proved to passivate all types of silicon substrates with the entire doping levels. Being deposited at temperatures below 250°C was a merit that leads to a decrease in the thermal budget of solar cell production processes. In this respect, a-Si:H is expected to be a good passivation choice for Si nanostructure solar cells. Crozier et al. [16] demonstrated that in situ amorphous Si/SiNW surface recombination decayed just about 2 orders of magnitude compared with SiNWs alone. The surface passivation capability of amorphous silicon was proved by the increase of lifetime and carrier diffusion length. However, this passivation effect was not investigated on the SiNW solar cell performance. In a previous study [16], SiNWs were synthesized using the VLS process which was a bottom-up synthesis approach. Indeed, those SiNWs differ from SiNWs synthesized by metal-assisted wet chemical etching (top-down approach), especially in the defect type and quantity, SiNW density, as well as doping mechanism [23].

In this work, for the first time, the fabrication of an a-Si:H/vertically aligned SiNW (shell/core) solar cell was proposed. The SiNW arrays were fabricated by metal-assisted wet chemical etching of silicon substrates, whereas the a-Si:H shell was deposited by plasma-enhanced chemical vapor deposition (PECVD). The structural, optical, and electrical properties of the a-Si:H/SiNW solar cell were all analyzed.

Methods

The growth of aligned SiNW arrays was carried out on p-type (100) silicon (0 to 1 Ω cm) wafers. The etching was carried out in a Teflon beaker containing a HF/AgNO3 solution, varying etching parameters like concentration, temperature as well as etching time. Prior to the etching, the samples were sequentially cleaned with acetone, ethanol, and de-ionized water for 5 min each followed by cleaning with a boiling piranha solution (H2SO4/H2O2 = 3:1 by volume, for 60 min) to remove any organic containment. The samples were then rinsed thoroughly with de-ionized water followed by dipping in 10% HF solution to remove any surface oxides. The cleaned silicon wafers were then immersed in the etching solution HF/AgNO3 (5.25:0.02 M). After the etching processes, the tree-like silver pattern wrapping the silicon samples was detached using a NH3OH/H2O2 (3:1) solution. Finally, the samples were rinsed with de-ionized water and air-dried.

A conventional diffusion procedure was carried out to fabricate the SiNW solar cell. The n + emitter was formed by phosphorus diffusion using a POCl3 liquid source at 850°C for 20 min. The phosphosilicate glass (PSG) that formed during diffusion was removed by dipping the samples in 5% HF for 2 min.

Hydrogenated amorphous silicon was deposited on the surface of SiNWs by PECVD. The deposition occurred under the following conditions: a power of 100 W, a temperature of 150°C, a pressure of 1 Torr, and a SiH4 gas flow of 26 sccm.

The Al back contact with 2,000-nm thickness was formed using an electron beam evaporator (Edwards Auto 306 Turbo, Sanborn, NY, USA). In order to form the back surface field (BSF), alloying of Al and Si was carried out at 900°C. The front metal contacts were made by Ag deposition (180 nm) through a metal mask using the same e-beam evaporator followed by contact sintering in forming gas at 450°C. Finally, 1 × 1 cm2 solar cells were diced for electrical characterization.

The morphology of the samples was examined using a field emission scanning electron microscope (FESEM; Carl Zeiss Supra 55VP, Oberkochen, Germany). The structure and chemical composition of the samples were investigated by Fourier transform infrared spectroscopy (FTIR). Reflection (R) spectra were obtained using a Shimadzu UV-3600 spectrophotometer (Kyoto, Japan). The J-V characteristics of the devices were measured with Keithley 237 SMU (Cleveland, OH, USA) under illumination at 100 mW/cm2 from a solar simulator with an AM 1.5G filter.

Results and discussion

The cross-sectional views of the SiNWs and a-Si:H/SiNWs were investigated using FESEM as shown in Figure 1. Vertically aligned SiNWs were uniformly distributed over the whole area of the silicon surface with 3-μm length. While comparing SiNW and a-Si:H/SiNW structures, it was observed that the deposited a-Si:H filled the SiNW surface with a thin shell. The transmission electron microscopy (TEM) image in Figure 1c indicates that the thickness of the deposited a-Si:H is around 30 nm. Additionally, the TEM image presents the homogenous and uniform a-Si:H shell over the SiNWs.

thumbnailFigure 1. FESEM and TEM images of the SiNWs and a-Si:H/SiNWs. (a, b) FESEM images of SiNWs and a-Si:H/SiNWs, respectively. (c) TEM image of the a-Si:H shell over the SiNWs.

Figure 2 highlights the FTIR transmittance spectra of both planar SiNWs and thin a-Si:H shell deposited on the SiNW core by PECVD for 3 min. While investigating the planar SiNW FTIR spectrum, the main peak appeared at 1,105 cm-1; it is mostly the signature of the asymmetrical stretching of the Si-O-Si bond, and relying on previous works, it is mainly related to the silicon substrate [24]. For a-Si:H/SiNWs, a broad band around 2,000.22 cm-1 emerged normally owing to the stretching mode of the Si-H bond [25]. The full width at half maximum (FWHM) of the Si-H peak was in the same range as that of the reference a-Si:H deposited by PECVD under the same conditions. Since the a-Si:H shell was not annealed after deposition, no narrowing of the stretch peak was observed [26]. The high FWHM of the Si-H peak is mostly related to the high content of hydrogen of the deposited a-Si:H [24]. The high hydrogen content of the a-Si:H shell is suggested to have a good-quality passivation effect [27]. In summary, the FTIR spectrum confirms the deposition of the a-Si:H over SiNWs with appropriate features.

thumbnailFigure 2. Transmittance spectra of planar SiNWs and thin a-Si:H shell.

Figure 3 presents the reflection spectrum of a-Si:H/SiNWs and SiNWs. a-Si:H/SiNWs had suppressed the reflection to low values at incident light wavelength ranges from 250 to 1,000 nm. As noted, the combination of a-Si:H shell over SiNW core reduces the average reflectance as low as 5.2%. Relying on previous studies, the low reflection of a-Si:H/SiNWs is mainly caused by the graded refractive index of the SiNW core [28]. Moreover, the filling ratio between the SiNWs and substrate surface plays a vital role in reducing the reflection of the core/shell structures. While studying the a-Si:H thickness effect on the filling ratio, 30 nm was found to be the optimum thickness with respect to both the filling ratio and hence the light reflection [29].

thumbnailFigure 3. Reflection spectrum of a-Si:H/SiNWs and SiNWs (a) and absorption spectrum from reflection and transmission results (b).

Going back to earlier works, a-Si:H thin films reflect more than 45% of the incident light [30]. Thus, it is expected that the a-Si:H/SiNW structure will be a sufficient antireflection coating combining amorphous and crystalline silicon features.

The absorption spectrum that was extracted from the measured reflection and transmission results is shown in Figure 3. It is noticeable that a-Si:H/SiNWs show a superior absorption property with an average over 87% of the incident light. Note here that the recent simulated results predicted the absorption to be around 60% to 75% [29] for 1-μm thickness. Using SiNWs with 3-μm lengths in this work could be the cause of such increment. As well known, SiNWs reflect less light while increasing their thickness [18].

Another inspiring feature of the a-Si:H/SiNW absorption spectrum is the shifting of the absorbed edge to near-infrared wavelengths. This shifting confirms the dual absorption function of both a-Si:H and SiNWs. Basically, each of them absorbed the wavelengths of the light which match to their energies. Comparing the absorption edges of our a-Si:H/SiNWs with those of amorphous silicon nanowires, it was found that the absorption edge located on the wavelength corresponds to the a-Si bandgap [31].

Lastly, broadband optical absorption combined with a low reflection value is a significant advantage of a-Si:H/SiNWs compared with a-Si thin films and silicon surfaces. This suggests that a-Si:H/SiNWs can be used as effective antireflection coating for silicon solar cells.

Figure 4 and Table 1 present the electrical performance of a-Si:H/SiNW and SiNW solar cells. The values show that the a-Si:H shell highly improves surface passivation, leading to an increase of open-circuit voltage (Voc), from 481 to 553 mV, with around 15% enhancement. This passivation enhancement is related to the high content of hydrogen in the a-Si:H shell, as shown earlier in the FTIR results. Hydrogen atoms diffuse inside the SiNW core and passivate the recombination centers. Consequently, elimination of the recombination centers caused enhanced collection of electron–hole pairs leading to increased Voc that reveals a relatively low surface recombination velocity between the SiNWs and front electrode as well good bulk properties of the SiNWs. A relative explanation for the highly increased Voc is the assumption of Smith et al. [32] that the majority of generated carriers in the amorphous Si shell spread into the SiNW core, and then carriers are transported to the front electrode as photocurrent. The high mobility of the SiNW core leads to enhanced transportation of the carriers and finally enhanced surface passivation of the SiNW surface.

thumbnailFigure 4. Electrical performance of a-Si:H/SiNW and SiNW solar cells.

Table 1. Performances of the SiNW solar cells with and without a-Si:H shell

Referring to Figure 4 and Table 1, there is also clear improvement in the short-circuit current density (Jsc). This increasing trend could not be mainly related to the trapping effect of the a-Si:H/SiNW core/shell structure. As mentioned previously, the reflection of the a-Si:H/SiNWs is slightly higher than that of the SiNWs alone. Subsequently, the main factor that leads to such increment in electrical performance is the low recombination velocity which becomes less due to the passivation effect of the a-Si:H shell as described earlier.

The calculated fill factor (FF) of the a-Si:H-passivated SiNW solar cell improved by 8%, reaching 55%. This improvement can be attributed to the decreasing contact area between the electrode and SiNWs. However, the original FF of the nonpassivated SiNW solar cell is still low. This low magnitude is more related to the main problem facing SiNW solar cells, i.e. electrode contact resistance. Hopefully, by solving the metal contact problem, the fill factor can be improved.

Our a-Si:H-passivated SiNW solar cell exhibits an improved efficiency by 37%, an open-circuit voltage by 15%, a short-circuit current by 12%, and a fill factor by 8%, as compared to the SiNW solar cell without a-Si:H. It is anticipated that the recombination rate and surface state density are decreased when the a-Si:H shell was used. However, more optimization of the a-Si:H shell thickness is needed. Moreover, more theoretical and experimental perceptions of the a-Si:H/SiNW interface is needed to maximize the a-Si:H passivation effect on the SiNW surface.

Conclusions

In summary, vertically aligned Si nanowires have been synthesized and implemented to a Si nanowire/a-Si:H core/shell solar cell for photovoltaic devices. Optical studies reveal that the a-Si:H/SiNWs have low reflectivity (around 5.2%) in the entire spectral range (250 to 1,000 nm) of interest for solar cells with a superior absorption property with an average over 87% of the incident light. In investigating the passivation effect of the a-Si:H shell, we find that the combination of the a-Si:H shell and SiNW solar cell leads to enhanced power conversion efficiency, open-circuit voltage, and short-circuit current by more than 37%, 15%, and 12%, respectively, compared to the SiNW cells. This is mainly due to the suppression of the surface recombination of the large surface area of SiNWs. We expect that the a-Si:H will have a significant role in passivation of the SiNW surface with more optimization of its thickness and more theoretical understanding of its interface with SiNWs.

Abbreviations

AgNO3: Silver nitrate; AM: Air mass; ARC: Antireflection coating; a-Si:H: Hydrogenated amorphous silicon; FESEM: Field emission scanning electron microscopy; FF: Fill factor; FTIR: Fourier transform infrared spectroscopy; H2O2: Hydrogen peroxide; H2SO4: Sulfuric acid; HF: Hydrofluoric; HIT: Heterojunction with intrinsic thin layer; Jsc: Short-circuit current; PCE: Power conversion efficiency; PECVD: Plasma-enhanced chemical vapor deposition; PSG: Phosphosilicate glass; SiNW: Si nanowire; TEM: Transmission electron microscopy; VLS: Vapor–liquid-solid; Voc: Open-circuit voltage.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

ESA conceived of the study and participated in its design and coordination as well carried out the fabrication and characterization of the a-Si:H/SiNW solar cell. Moreover, ESA interpreted the results and prepared the manuscript. MYS was involved in drafting and revising the manuscript. MHR, KS, ESA, and MYS have given final approval of the manuscript to be published.

Acknowledgements

This work has been funded by the Ministry of Science, Technology and Innovation, Malaysia, and Solar Energy Research Institute (SERI), UKM.

References

  1. Huia S, Zhang J, Chena X, Xua H, Maa D, Liua Y, Taoa B: Study of an amperometric glucose sensor based on Pd–Ni/SiNW electrode.

    Sensor Actuator B Chem 2011, 155:592-597. Publisher Full Text OpenURL

  2. Zaremba-Tymieniecki M, Li C, Fobelets K, Durrani ZAK: Field-effect transistors using silicon nanowires prepared by electroless chemical etching.

    IEEE Electron Device Lett 2010, 31:860-862. OpenURL

  3. Huang Z, Zhang X, Reiche M, Liu L, Lee W, Shimizu T, Senz S, Gösele U: Extended arrays of vertically aligned sub-10 nm diameter [100] Si nanowires by metal-assisted chemical etching.

    Nano Lett 2011, 8:3046-3051. OpenURL

  4. Jung JY, Guo Z, Jee SW, Um HD, Park KT, Hyun MS: A waferscale Si wire solar cell using radial and bulk p–n junctions.

    Nanotechnology 2010, 21:5303-5306. OpenURL

  5. Kumar D, Srivastava SK, Singh PK, Husain M, Kumar V: Fabrication of silicon nanowire arrays based solar cell with improved performance.

    Sol Energy Mater Sol Cells 2011, 95:215-218. Publisher Full Text OpenURL

  6. Peng K, Xu Y, Wu Y, Yan Y, Lee ST, Zu J: Aligned single crystalline silicon nanowire arrays for photovoltaic applications.

    Small 2005, 1:1062-1067. PubMed Abstract | Publisher Full Text OpenURL

  7. Kodambaka S, Tersoff J, Reuter CM, Ross MF: Diameter-independent kinetics in the vapor–liquid-solid growth of Si nanowires.

    Phys Rev Lett 2006, 96:6105-6108. OpenURL

  8. Zhang YF, Tang YF, Wang N, Lee CS, Bello I, Lee ST: Silicon nanowires prepared by laser ablation at high temperature.

    Appl Phys Lett 1998, 72:1835-1837. Publisher Full Text OpenURL

  9. Niu J, Sha J, Yang D: Silicon nanowires fabricated by thermal evaporation of silicon monoxide.

    Phys E 2004, 23:131-134. Publisher Full Text OpenURL

  10. Holmes DJ, Johnston PK, Doty CR, Korgel AB: Control of thickness and orientation of solution-grown silicon nanowires.

    Science 2000, 287:1471-1473. PubMed Abstract | Publisher Full Text OpenURL

  11. Huang Z, Fang H, Zhu J: Fabrication of silicon nanowire arrays with controlled diameter, length, and density.

    J Adv Mater 2007, 19:744-19748. Publisher Full Text OpenURL

  12. Dai AH, Chang CH, Lai YC, Lin AC, Chung JR, Lin RG, He HJ: Subwavelength Si nanowire arrays for self-cleaning antireflection coatings.

    J Mater Chem 2010, 20:10924-10930. Publisher Full Text OpenURL

  13. Li X, Li J, Chen T, Tay KB, Wang J, Yu H: Periodically aligned Si nanopillar arrays as efficient antireflection layers for solar cell applications.

    Nanoscale Res Lett 2010, 5:1721-1762. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  14. Yue H, Jia R, Chen A, Ding W, Meng Y, Wu D, Wu D, Chen W, Liu X, Jin Z, Wang W, Ye T: Antireflection properties and solar cell application of silicon nanostructures.

    J Vac Sci Technol B 2011, 29:1208-1212. OpenURL

  15. Fang H, Li X, Song S, Xu Y, Zhu J: Fabrication of slantingly-aligned silicon nanowire arrays for solar cell applications.

    Nanotechnology 2008, 19:5703-5708. OpenURL

  16. Dan Y, Seo K, Takei K, Meza JH, Javey A, Crozier KB: Dramatic reduction of surface recombination by in situ surface passivation of silicon nanowires.

    Nano Lett 2011, 11:2527-2532. PubMed Abstract | Publisher Full Text OpenURL

  17. Lipiski M, Ziba P, Panek P, Jonas S, Kluska S, Czternastek H, Szyszka A, Paszkiewicz B: Silicon nitride for silicon solar cells. In Proceedings of the 29th International Conference of IMAPS 2005: September 19–21 2005; Darłówko. Washington, D.C.: International Microelectronics and Packaging Society; 2005:203-206. OpenURL

  18. Li H, Jia R, Chen C, Xing Z, Ding W, Meng Y, Wu D, Liu X, Ye T: Influence of nanowires length on performance of crystalline silicon solar cell.

    Appl Phys Lett 2011, 98:116-118. OpenURL

  19. Tanaka M, Taguchi M, Matsuyama T, Sawada T, Tsuda S, Nakano S, Hanafusa H, Yukinori Kuwano Y: Development of new a-Si/c-Si heterojunction solar cells: ACJ-HIT (artificially constructed junction-heterojunction with intrinsic thin-layer).

    Jap J Appl Phys 1992, 31:3518-3522. Publisher Full Text OpenURL

  20. Rath JK, Rubinelli FA, Van der Werf CHM, Schropp REI, Van der Weg FW: Performance of heterojunction p + microcrystalline silicon n crystalline silicon solar cells.

    J Appl Phys 1997, 82:6089-6095. Publisher Full Text OpenURL

  21. Terada N, Tsuge S, Toshiaki B, Takahama T, Wakisaka K, Tsuda S, Nakano S: High-efficiency a-Si/c-Si heterojunction solar cell photovoltaic energy conversion. In Proceedings of the 24th IEEE Photovoltaic Specialists Conference: December 5–9 1994; Waikoloa. Piscataway: IEEE; 1994:1219-1226. OpenURL

  22. Knights CJ, Lujan AR: Microstructure of plasma-deposited a-Si : H films.

    Appl Phys Lett 1979, 35:244-246. Publisher Full Text OpenURL

  23. Bandaru RP, Pichanusakorn P: An outline of the synthesis and properties of silicon nanowires.

    Semicond Sci Technol 2010, 25:1-16. OpenURL

  24. Mahan HA, Molenbroek CE, Gallagher CA, Nelson PB, Iwaniczko E, Xu Y: Deposition of device quality, low hydrogen content, hydrogenated amorphous silicon at high deposition rates. US Patent 6,468,885 B1, 9 Oct 2002

  25. Xie ML, Qi WM, Chen MJ: The nature of several intense Si-H infrared stretching peaks in the neutron-transmutation-doped Si-H system.

    J Phys Condens Matter 1991, 3:8519-8523. Publisher Full Text OpenURL

  26. Tsai CC, Fritzsche H: Effect of annealing on the optical properties of plasma deposited amorphous hydrogenated silicon.

    Sol En Mater 1979, 1:29-42. Publisher Full Text OpenURL

  27. Descoeudres A, Barraud L, De Wolf S, Strahm B, Lachenal D, Guérin C, Holman CZ, Zicarelli F, Demaurex B, Seif J, Holovsky J, Ballif C: Improved amorphous/crystalline silicon interface passivation by hydrogen plasma treatment.

    Appl Phys Lett 2011, 99:3506-3508. OpenURL

  28. Garnett E, Yang P: Light trapping in silicon nanowire solar cells.

    Nano Lett 2010, 91:3317-3319. OpenURL

  29. Xie QW, Liu FW, Oh IJ, Shen ZW: Optical absorption in c-Si/a-Si:H core/shell nanowire arrays for photovoltaic applications.

    Appl Phys Lett 2011, 99:3107-3109. OpenURL

  30. Pankove IJ, Carlson ED: Electrical and optical properties of hydrogenated amorphous silicon.

    Annu Rev Mater Sci 1980, 10:43-63. Publisher Full Text OpenURL

  31. Zhu J, Yu Z, Burkhard FG, Hsu MC, Connor TS, Xu Y, Wang Q, McGehee M, Fan S, Cui Y: Optical absorption enhancement in amorphous silicon nanowire and nanocone arrays.

    Nano Lett 2009, 9:279-282. PubMed Abstract | Publisher Full Text OpenURL

  32. Smith EZ, Chu V, Shepard K, Aljishi S, Slobodin D, Kolodzey J, Wagner S, Chu LT: Photothermal and photoconductive determination of surface and bulk defect densities in amorphous silicon films.

    Appl Phys Lett 1987, 50:1521-1523. Publisher Full Text OpenURL