Large-area high-performance SERS substrates with deep controllable sub-10-nm gap structure fabricated by depositing Au film on the cicada wing

Qi Jiwei, Li Yudong, Yang Ming, Wu Qiang, Chen Zongqiang, Wang Wudeng, Lu Wenqiang, Yu Xuanyi, Xu Jingjun* and Sun Qian*

Author affiliations

The MOE Key Laboratory of Weak-Light Nonlinear Photonics, Tianjin Key Laboratory of Photonics and Technology, TEDA Applied Physics School and School of Physics, Nankai University, Tianjin 300457, China

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2013, 8:437  doi:10.1186/1556-276X-8-437


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/437


Received:21 July 2013
Accepted:19 September 2013
Published:22 October 2013

© 2013 Jiwei et al.; licensee Springer.

This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Noble metal nanogap structure supports strong surface-enhanced Raman scattering (SERS) which can be used to detect single molecules. However, the lack of reproducible fabrication techniques with nanometer-level control over the gap size has limited practical applications. In this letter, by depositing the Au film onto the cicada wing, we engineer the ordered array of nanopillar structures on the wing to form large-area high-performance SERS substrates. Through the control of the thickness of the Au film deposited onto the cicada wing, the gap sizes between neighboring nanopillars are fine defined. SERS substrates with sub-10-nm gap sizes are obtained, which have the highest average Raman enhancement factor (EF) larger than 2 × 108, about 40 times as large as that of commercial Klarite® substrates. The cicada wings used as templates are natural and environment-friendly. The depositing method is low cost and high throughput so that our large-area high-performance SERS substrates have great advantage for chemical/biological sensing applications.

Keywords:
Surface-enhanced Raman scattering; Controllable gap size; Cicada wing; Nanogap

Background

Surface-enhanced Raman scattering (SERS), as a powerful spectroscopy technique that can provide non-destructive and ultra-sensitive characterization down to a single molecular level [1,2], is currently receiving a great deal of attention from researchers. Lots of works focus on the SERS mechanism and the fabrication of high-performance SERS-active substrates for application [3-44]. High-performance SERS substrates mean that the substrates should be uniform, reproducible, and ultra-sensitive.

Recently, the nanogap structure becomes attractive to researchers because it can provide enormous Raman enhancement due to the existence of enormous electromagnetic enhancement in the gap of metal nanostructure, which is called 'hot spot’ [3-16]. And the surface plasmonic coupling between neighboring nanounits is believed to be the main reason for the enormous electromagnetic enhancement. Many investigations on the mechanism of the surface plasmonic coupling and the fabrication of the nanogap-structured SERS substrates for practical application have been presented [3-17]. Compared to the nanoparticle substrates, the ordered nanopillar/nanorod array substrates are more uniform and reproducible, which make them more beneficial to practical application and theoretical analysis. But the uniform ordered nanopillar/nanorod array substrates with tunable gap size are usually fabricated by electron-beam lithography (EBL) and focused ion-beam lithography (FIBL), which require a very high fabrication cost [18-20]. To circumvent this difficulty, many low-cost methods and techniques have been proposed, like self-assembly [21,22], indentation lithography [14,20,23-27], corroding ultra-thin layer [7], femto-second laser fabrication [28-31], and so on. But to date, for the existence of many limits of these low-cost techniques, the fabrication of the large-area low-cost high-performance SERS substrate, with tunable gap size, is still critical not only for practical applications of SERS in the chemical/biological sensor, but also in understanding surface plasmonic coupling existing inside the nanogaps.

In this letter, we provide a simple method to fabricate large-area low-cost high-performance SERS substrates with tunable gap size through depositing the Au film onto the ordered nanopillars array structure on the cicada wings. The fine control of the gap size is achieved by controlling the Au film deposition thickness. The dependence of the average enhancement factor (EF) on the gap size is investigated. The highest average EF, 2 × 108, is obtained when the gap size is <10 nm. This highest average EF is about 40 times as large as that of commercial Klarite® substrates. The large-area low-cost high-performance SERS substrates with tunable gap size, obtained in our work, not only are useful for improving the fundamental understanding of SERS phenomena, but also facilitate the use of SERS for chemical/biological sensing applications with extremely high sensitivity. In addition, because the cicada wings used as the templates in our work are from nature, our SERS substrates are environment-friendly.

Methods

Sample and substrate preparation

Many nanostructures existing in biology are evolutionary results for the needs of adaptation and survival, which can produce astonishing optical effects and can be used directly. An ordered array of nanopillar structures on the cicada wing, with a perfect anti-reflection efficiency, has been investigated widely [45-48] and was used as the template in this letter. The cicadas (Cryptympana atrata Fabricius) were captured locally. Before the depositing process, the cicada wings are cleaned to get rid of the stains and restored the sticking nanopillars. Figure 1 shows the scanning electron microscope (SEM) image of the cicada wing and schematic illustrations of the fabrication of the SERS substrates. A hexagonally quasi-two-dimensional (q2D) ordered assembly of nanopillars exists on the surface of the cicada wing. The nearest-neighbor nanopillar distance (Λ) is an approximate 190 nm; the average height (h) of each nanopillar is about 400 nm, and the average diameter at the pillar top and base are about 65 and 150 nm, respectively. The main component of the cicada wing is chitin - a high molecular weight crystalline polymer [47]. And due to the existing of the ordered array of nanopillars, the cicada wing shows an excellent anti-reflection [46-48]. Here, the cicada wing, with a large-area uniform nanostructure on the surface, was used as the template. As shown in Figure 1, the Au film was deposited onto the surface of the cicada wing with an ion beam sputter evaporator to engineer the nanostructure. The Au film thicknesses (d) were controlled to be 50, 100, 150, 200, 250, 300, 350, and 400 nm, respectively, and these SERS substrates were signed with CW50, CW100, and so on in the following discussion. The deposition process was kept with target substrate at room temperature with a depositing rate of 0.03 nm/s.

thumbnailFigure 1. Schematic illustration of the fabrication program of the SERS substrates. The ordered array of nanopillar structures on the cicada wing was used directly as the template. The SEM image and schematic illustration of the nanopillar structures are shown. The Au films were deposited on the cicada wings to engineer the nanostructures and define the gap size.

Figure 2a,b,c,d and Figure 2e,f,g,h show the top view and side view SEM images of CW50, CW200, CW300, and CW400, respectively. As shown in Figure 2, with the increase in the deposited Au film thickness d, when d ≤ 300 nm, the gap size (g) between the nearest-neighbor nanopillars decreases, and the nanopillars tend to become hexagonal nanorods. The average g of CW50 to CW300 were measured with commercial software and shown in Figure 3b. According to the measured results, the average g even decreases to sub-10 nm when d is 300 nm. The average heights of the nanopillars (h) of CW50 to CW300 were also measured, and the measurement results show that the average height of the nanopillars (h) decreases from about 400 nm to about 200 nm with the increase in d. This is reasonable because with the decrease of g, the gold atoms are easier to fall into the bottom which leads to a faster rise of the bottom. Additionally, the surfaces of the nanopillar structures of CW50, CW100, and CW150 are relatively smooth; contrarily, the surfaces of the nanopillar structures of CW200, CW250, and CW300 are relatively rough. When d > 350 nm, i.e., the cases of CW350 and CW400, relatively continuous layers formed on the top of the nanopillars. The relatively continuous layers are rugged and the nanopillars were covered up so the gs of CW350 and CW400 cannot be measured and shown in Figure 3b.

thumbnailFigure 2. Top-(a,b,c,d) and side-view (e,f,g,h) SEM images of SERS substrates CW50, CW200, CW300, and CW400, respectively.

thumbnailFigure 3. Comparison of substrates and neat benzene thiol, average EFs and gap sizes, spatial mapping, and COMSOL simulations. (a) Comparison of the SERS of substrates CW300 (red), Klarite® (green), and neat Raman spectra (black) of benzene thiol collected at 785-nm incident. The number of molecules of benzene thiol that each measurement is probing is denoted in the figure. Inset: zoomed-in region of the spectra showing the three primary modes located near 1,000/cm, with the 998/cm used for calculation of the SERS enhancement factor. Note that the SERS of the Klarite® substrate and the neat spectra have been multiplied by a factor of 100 for easier direct comparison. (b) Average EFs (black open squares) and gap sizes between neighboring nanopillars (red open rhombuses) as function of gold film thickness deposited on the cicada wing. (c) Spatial mapping of the SERS intensity at 998/cm of SERS substrate CW300 over an area larger than 20 μm × 20 μm. The background is the optical reflection image of substrate CW300 photographed through a microscope with a × 50 objective. (d) COMSOL simulations of SERS enhancement (black dash) and the mean of experimental average EFs (red squares) as function of gap size between neighboring nanopillars. All date points are normalized to the corresponding value of SERS enhancement of CW50.

SERS spectra measurement and EFs calculation

To characterize the SERS performance of our substrates, benzene thiol was used as the probe molecule. And commercial Klarite® substrates were used as reference samples. The Klarite® SERS substrate consists of a gold-coated textured silicon (regular arrays of inverted pyramids of 1.5-μm wide and 0.7-μm deep) mounted on a glass microscope slide. All of the substrates (including Klarite® substrates) were immersed in a 1 × 10-3 M solution of benzene thiol in ethanol for approximately 18 h and were subsequently rinsed with ethanol and dried with nitrogen to ensure that a complete self-assembled monolayer (SAM) was formed on the substrate surface. All the Raman spectra were recorded with a confocal Raman spectroscopic system (model inVia, Renishaw Hong Kong Ltd., Kowloon Bay, Hong Kong, China). The spectrograph uses 1,200 g/mm gratings, a 785-nm laser, and a SynchroScan type camera. The incident laser power for different SERS substrates were not the same because of the huge difference of the Raman sensitivity among the substrates. The incident laser power was set to be 0.5 mW for CW350 to CW400 and 0.1 mW for CW50 to CW100 and Klarite® substrates 0.05 mW for CW150 to CW200 and 0.005 mW for CW250 to CW300. All the SERS spectra were collected using a × 50, NA = 0.5, long working distance objective. The laser spot size is about 2 μm. SERS spectra were recorded with an accumulation time of 10 s and a single scan was performed after SAM of benzene thiol formed on the substrate surface. To get an accurate approximation of the enhancement factors, the neat Raman spectrum of benzene thiol was measured. For these measurements, the power of the 785 nm laser was 1 mW, the accumulation time was 10 s, the spot size was 20 μm, and the depth of focus was 18 μm. Figure 3a shows the Raman spectra of the benzene thiol SAM on the optimal substrate (CW300; red), Klarite® substrate (green), and neat thiophenol (black), with everything being normalized to account for the accumulation time and laser power. The number of molecules contributing to the Raman signal was quoted in Figure 3a and was used for calculating EFs. The average EFs were calculated from the equation

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/437/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/437/mathml/M1">View MathML</a>

where ISERS and IRaman represent the normalized Raman intensity of SERS spectra and neat Raman spectrum of benzene thiol, respectively, which can be measured directly from the Raman spectra. NSERS and NRaman represent the numbers of molecules contributing to SERS signals and neat Raman signals of benzene thiol, respectively. NRaman is defined as follows:

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/437/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/437/mathml/M2">View MathML</a>

where ρ = 1.073 g/mL and MW = 110.18 g/mol are the density and molecular weight of benzene thiol and V is the collection volume of the liquid sample monitor. NA = Avogadro’s number. NSERS is defined as follows:

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/437/mathml/M3','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/437/mathml/M3">View MathML</a>

where ρsurf is the surface coverage of benzene thiol on which has been reported as approximately 0.544 nmol/cm2, and Ssurf is the surface area irradiated by exciting the laser.

To get an accurate and comparable estimation of the average enhancement factor, the Raman mode used for the calculation of the average EF must be selected carefully because the average EFs calculated from different Raman modes have a great deviation. For comparison, the three Raman modes associated with vibrations about the aromatic ring are presented in the inset of Figure 3a, and the average EFs of optimal substrate (CW300) which are calculated based on the intensities of the modes at 998/cm (C-H wag), 1,021/cm (C-C symmetric stretch), and 1,071/cm (C-C asymmetric stretch) are 2 × 108, 5 × 108, and 2 × 109, respectively. However, while the average EFs calculated were based on the neat benzene thiol dependent on the choice of Raman mode strongly, the relative Raman enhancement between our SERS substrates (including the Klarite® substrate) were found to be relatively independent on the choice of Raman mode used for comparison, as shown in Figure 3a. Here, the intensities of the peak found at 998/cm, with the carbon-hydrogen wagging mode which is the furthest mode removed from the gold surface, were used to compute the average EFs. And the average EF of the Klarite® substrate was calculated to be 5.2 × 106, which is reasonable because the enhancement factor for the inverted pyramid structure of Klarite® substrates relative to a non-enhancing surface is rated to have a lower bound of approximately 106.

Results and discussion

The average EFs for our SERS substrates were calculated and are presented in Figure 3b as a function of d (black open squares). For each substrate, more than 80 spectra were collected at various positions to ensure that a reproducible SERS response was attained. Spatial mapping with an area larger than 20 μm × 20 μm of the SERS intensity of CW300 was shown in Figure 3c as an example. It was certified that the relative standard deviation (RSD) in the SERS intensities were limited to approximately 30% within a given substrate, which is similar with the result of other groups [17]. The SERS response at a given point on the substrate was found to be highly reproducible, with variations in the detected response being limited to about 7%.

According to the results shown in Figure 3b, with the increase in d, when d ≤ 300 nm, the gap size g decreases, and the average EF increases. The highest average EF, 2 × 108, is obtained when d = 300 nm. But when d ≥ 350 nm, the average EF decreases abruptly to about 5 × 105. This is because a relatively continuous and rugged layer has formed on the top of the nanopillars and, consequently, the high density and deep nanogaps were covered up when d ≥ 350 nm.

Additionally, as shown in Figure 3a,b, the Raman intensity of the peak at 998/cm of our optimal SERS substrate (CW300) is about 200 times as large as that of the Klarite® substrate. But the calculated highest average EF of CW300, 2 × 108, is only about 40 times as large as the average EF of the Klarite® substrate, 5.2 × 106. This is because the surface area (Ssurf) of CW300 is about four times as large as the Ssurf of the Klarite® substrate. The large surface area of our substrate is induced by the high density and large depth of the nanogap structure. In other words, the high density and large depth of the nanogap structure of our substrate provide dense strong 'hot spots’ and an enormous Raman intensity but yields a relative small average EF. As shown in Figure 3a, an obvious background signal is found in the Raman spectrum of the Klarite® substrate, which almost cannot be found in the Raman spectrum of our substrate. Manifestly, our high density and deep nanogap structure substrates have an advantage for application.

To gain a better understanding on the role of plasmonic coupling in the SERS effect, COMSOL calculations of the predicted SERS enhancement with the parameters estimated according to the SEM images were carried out and presented as a function of gap size in Figure 3d. All of the simulation values presented in Figure 3d are normalized to the calculated SERS enhancement (E4) for the structure of CW50. And the measured average EFs shown in Figure 3d are also normalized to the measured average EFs of the SERS substrate CW50. Our experimental results agree with the simulations, both showing a dramatic increase in the average EFs with the decrease in the gap size, which is believed to be caused by the plasmonic coupling from the neighboring nanopillars. As shown, the experimental average EFs are larger than the simulations, which is because of the neglect of the roughness of the nanopillar surface in the simulating.

Conclusions

In conclusion, through a simple low-cost and high-output method-depositing Au film, we engineer the ordered array of nanopillars structure on the wing to form large-area high-performance SERS substrate. By this method, the gap size between the nanopillars is fine defined and SERS substrates with sub-10-nm gap size are obtained, which have the highest average EF of about 2 × 108. The dramatic increase in the average EFs with the decrease in the gap size induced by the plasmonic coupling from the neighboring nanopillars is certified. In this work, the natural and low-cost cicada wings were used as the templates directly; so, our SERS substrates are environment-friendly. Our low-cost environment-friendly large-area uniform reproducible and ultra-sensitive SERS substrates have huge advantages for applications and theoretical studies.

Abbreviations

SERS: Surface-enhanced Raman scattering; EF: Raman enhancement factor; EBL: Electron-beam lithography; FIBL: Focused ion-beam lithography; SAM: Self-assembled monolayer; SEM: Scanning electron microscope; RSD: Relative standard deviation.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

QJ conceived of the study, carried out the fabrication of the SERS substrates, measurement, analysis, and simulation and drafted the manuscript. LY participated in the SERS spectra analysis and discussion. YM and WQ participated in the SEM measurements and SERS spectra measurements. CZ, WW, LW, and YX participated in the simulation. XJ and SQ are the PIs of the project and participated in the design of the study, revised the manuscript, and conducted the coordination. All authors read and approved the final manuscript.

Acknowledgements

This study is supported by the National Natural Science Foundation of China under Grant No 61178004, the Tianjin Natural Science Foundation under Grant No 12JCQNJC01100, 06TXTJJC13500, the Doctoral Program of Higher Education of China under Grant No 20110031120005, the Program for Changjiang Scholars and Innovative Research Team in Nankai University, 111 Project under Grant No B07013, and the Fundamental Research Funds for the Central Universities. We are also very grateful to Professor Zhou Q. L., Professor Xie J. H., and their group for providing the solution of benzene thiol in ethanol.

References

  1. Nie S, Remory S: Probing single molecules and single nanoparticles by surface-enhanced Raman scattering.

    Science 1997, 275:1102-1106. PubMed Abstract | Publisher Full Text OpenURL

  2. Kneipp K, Wang Y, Kneipp H, Perelman LT, Itzkan I, Dasari RR, Field MS: Field single molecule detection using surface- enhanced Raman scattering.

    Phys Rev Lett 1997, 78:1667-1670. Publisher Full Text OpenURL

  3. Liang HY, Li ZP, Wang WZ, Wu YS, Xu HX: Highly surface-roughened “Flower-like” silver nanoparticles for extremely sensitive substrates of surface-enhanced Raman scattering.

    Adv Mater 2009, 21:4614-4618. Publisher Full Text OpenURL

  4. Wu HY, Cunningham BT: Plasmonic coupling of SiO2-Ag “post-cap” nanostructures and silver film for surface enhanced Raman scattering.

    Appl Phys Lett 2011, 98:153103. Publisher Full Text OpenURL

  5. Zhang L, Lang X, Hirata A, Chen M: Wrinkled nanoporous gold films with ultrahigh surface-enhanced Raman scattering enhancement.

    ACS nano 2011, 5:4407-4413. PubMed Abstract | Publisher Full Text OpenURL

  6. Duan H, Hu H, Kumar K, Shen Z, Yang JKW: Direct and reliable patterning of plasmonic nanostructures with sub-10-nm gaps.

    ACS nano 2011, 5:7593-7600. PubMed Abstract | Publisher Full Text OpenURL

  7. Im H, Bantz KC, Lindquist NC, Haynes CL, Oh SH: Vertically oriented sub-10-nm plasmonic nanogap arrays.

    Nano Lett 2010, 10:2231-2236. PubMed Abstract | Publisher Full Text OpenURL

  8. Wang HH, Liu CY, Wu SB, Liu NW, Peng CY, Chan TH, Hsu CF, Wang JK, Wang YL: Highly Raman-enhancing substrates based on silver nanoparticle arrays with tunable sub-10 nm gaps.

    Adv Mater 2006, 18:491. Publisher Full Text OpenURL

  9. Siegfried T, Ekinci Y, Solak HH, Martin OJF, Sigg H: Fabrication of sub-10 nm gap arrays over large areas for plasmonic sensors.

    Appl Phys Lett 2011, 99:263302. Publisher Full Text OpenURL

  10. Cho WJ, Kim Y, Kim JK: Ultrahigh-density array of silver nanoclusters for SERS substrate with high sensitivity and excellent reproducibility.

    ACS nano 2012, 6:249-255. PubMed Abstract | Publisher Full Text OpenURL

  11. Gupta MK, Chang S, Singamaneni S, Drummy LF, Gunawidjaja R, Naik RR, Tsukruk VV: pH-triggered SERS via modulated plasmonic coupling in individual bimetallic nanocobs.

    Small 2011, 7:1192-1198. PubMed Abstract | Publisher Full Text OpenURL

  12. Hu X, Meng G, Huang Q, Xu W, Han F, Sun K, Xu Q, Wang Z: Large-scale homogeneously distributed Ag-NPs with sub-10 nm gaps assembled on a two-layered honeycomb-like TiO2 film as sensitive and reproducible SERS substrates.

    Nanotechnology 2012, 23:385705. PubMed Abstract | Publisher Full Text OpenURL

  13. Jin M, Van Wolferen H, Wormeester H, van den Berg A, Carlen ET: Large-area nanogap plasmon resonator arrays for plasmonics applications.

    Nanoscale 2012, 4:4712-4718. PubMed Abstract | Publisher Full Text OpenURL

  14. Kostovski G, Chinnasamy U, Jayawardhana S, Stoddart PR, Mitchell A: Sub-15nm optical fiber nanoimprint lithography: a parallel self-aligned and portable approach.

    Adv Mater 2011, 23:531. PubMed Abstract | Publisher Full Text OpenURL

  15. Li JF, Huang YF, Ding Y, Yang ZL, Li SB, Zhou XS, Fan FR, Zhang W, Zhou ZY, Wu DY, Ren B, Wang ZL, Tian ZQ: Shell-isolated nanoparticle-enhanced Raman spectroscopy.

    Nature 2010, 464:392-395. PubMed Abstract | Publisher Full Text OpenURL

  16. Alexander KD, Skinner K, Zhang S, Wei H, Lopez R: Tunable SERS in gold nanorod dimers through strain control on an elastomeric substrate.

    Nano Lett 2010, 10:4488-4493. PubMed Abstract | Publisher Full Text OpenURL

  17. Caldwell JD, Glembocki O, Bezares FJ, Bassim ND, Rendell RW, Feygelson M, Ukaegbu M, Kasica R, Shirey L, Hosten C: Plasmonic nanopillar arrays for large-area, high-enhancement surface-enhanced Raman scattering sensors.

    ACS nano 2011, 5:4046-4055. PubMed Abstract | Publisher Full Text OpenURL

  18. Brolo AG, Arctander E, Gordon R, Leathem B, Kavanagh KL: Nanohole-enhanced Raman scattering.

    Nano Lett 2004, 4:2015-2018. Publisher Full Text OpenURL

  19. Chu Y, Wang D, Zhu W, Crozier KB: Double resonance surface enhanced Raman scattering substrates: an intuitive coupled oscillator model.

    Opt Express 2011, 19:14919-14928. PubMed Abstract | Publisher Full Text OpenURL

  20. Gong J, Lipomi DJ, Deng J, Nie Z, Chen X, Randall NX, Nair R, Whitesides GM: Micro- and nanopatterning of inorganic and polymeric substrates by indentation lithography.

    Nano Lett 2010, 10:2702-2708. PubMed Abstract | Publisher Full Text OpenURL

  21. Zhang XY, Hu A, Zhang T, Lei W, Xue XJ, Zhou Y, Duley WW: Self-assembly of large-scale and ultrathin silver nanoplate films with tunable plasmon resonance properties.

    ACS nano 2011, 5:9082-9092. PubMed Abstract | Publisher Full Text OpenURL

  22. He HX, Zhang H, Li QG, Zhu T, Li SFY, Liu ZF: Fabrication of designed architectures of Au nanoparticles on solid substrate with printed self-assembled monolayers as templates.

    Langmuir 2000, 16:3846-3851. Publisher Full Text OpenURL

  23. Liu GL, Lee LP: Nanowell surface enhanced Raman scattering arrays fabricated by soft-lithography for label-free biomolecular detections in integrated microfluidics.

    Appl Phys Lett 2005, 87:074101. Publisher Full Text OpenURL

  24. Xu M, Lu N, Xu H, Qi D, Wang Y, Chi L: Fabrication of functional silver nanobowl arrays via sphere lithography.

    Langmuir 2009, 25:11216-11220. PubMed Abstract | Publisher Full Text OpenURL

  25. Xue M, Zhang Z, Zhu N, Wang F, Zhao XS, Cao T: Transfer printing of metal nanoparticles with controllable dimensions, placement, and reproducible surface-enhanced Raman scattering effects.

    Langmuir 2009, 25:4347-4351. PubMed Abstract | Publisher Full Text OpenURL

  26. Ryckman JD, Liscidini M, Sipe JE, Weiss SM: Direct imprinting of porous substrates: a rapid and low-cost approach for patterning porous nanomaterials.

    Nano Lett 2011, 11:1857-1862. PubMed Abstract | Publisher Full Text OpenURL

  27. Wu W, Hu M, Ou FS, Li Z, Williams RS: Cones fabricated by 3D nanoimprint lithography for highly sensitive surface enhanced Raman spectroscopy.

    Nanotechnology 2010, 21:255502. PubMed Abstract | Publisher Full Text OpenURL

  28. Diebold ED, Mack NH, Doom SK, Mazur E: Femtosecond laser-nanostructured substrates for surface-enhanced Raman scattering.

    Langmuir 2009, 25:1790-1794. PubMed Abstract | Publisher Full Text OpenURL

  29. Lin CH, Jiang L, Chai YH, Xiao H, Chen SJ, Tsai HL: One-step fabrication of nanostructures by femtosecond laser for surface-enhanced Raman scattering.

    Opt Express 2009, 17:21581-21589. PubMed Abstract | Publisher Full Text OpenURL

  30. Wang C, Chang YC, Yao J, Luo C, Yin S, Ruffin P, Brantley C, Edwards E: Surface enhanced Raman spectroscopy by interfered femtosecond laser created nanostructures.

    Appl Phys Lett 2012, 100:023107. Publisher Full Text OpenURL

  31. Jiang L, Ying D, Li X, Lu Y: Two-step femtosecond laser pulse train fabrication of nanostructured substrates for highly surface-enhanced Raman scattering.

    Opt Lett 2012, 37:3648-3650. PubMed Abstract | Publisher Full Text OpenURL

  32. Ruan C, Eres G, Wang W, Zhang Z, Gu B: Controlled fabrication of nanopillar arrays as active substrates for surface-enhanced Raman spectroscopy.

    Langmuir 2007, 23:5757-5760. PubMed Abstract | Publisher Full Text OpenURL

  33. Cui B, Clime L, Li K, Veres T: Fabrication of large area nanoprism arrays and their application for surface enhanced Raman spectroscopy.

    Nanotechnology 2008, 19:145302. PubMed Abstract | Publisher Full Text OpenURL

  34. Oh YJ, Jeong KH: Glass nanopillar arrays with nanogap-rich silver nanoislands for highly intense surface enhanced Raman scattering.

    Adv Mater 2012, 24:2234-2237. PubMed Abstract | Publisher Full Text OpenURL

  35. Chung AJ, Huh YS, Erickson D: Large area flexible SERS active substrates using engineered nanostructures.

    Nanoscale 2011, 3:2903-2908. PubMed Abstract | Publisher Full Text OpenURL

  36. Kim SM, Zhang W, Cunningham BT: Photonic crystals with SiO2-Ag “post-cap” nanostructure coatings for surface enhanced Raman spectroscopy.

    Appl Phys Lett 2008, 93:143112. Publisher Full Text OpenURL

  37. Theiss J, Pavaskar P, Echternach PM, Muller RE, Cronin SB: Plasmonic nanoparticle arrays with nanometer separation for high-performance SERS substrates.

    Nano Lett 2010, 10:2749-2754. PubMed Abstract | Publisher Full Text OpenURL

  38. Deng X, Braun GB, Liu S, Sciortino PF Jr, Koefer B, Tombler T, Moskovits M: Single-order, subwavelength resonant nanograting as a uniformly hot substrate for surface-enhanced Raman spectroscopy.

    Nano Lett 2010, 10:1780-1786. PubMed Abstract | Publisher Full Text OpenURL

  39. Dou X, Chung PY, Jiang P, Dai J: Surface plasmon resonance and surface-enhanced Raman scattering sensing enabled by digital versatile discs.

    Appl Phys Lett 2012, 100:041116. Publisher Full Text OpenURL

  40. Choi CJ, Xu Z, Wu HY, Liu GL, Cunningham BT: Surface-enhanced Raman nanodomes.

    Nanotechnology 2010, 21:415301. PubMed Abstract | Publisher Full Text OpenURL

  41. Hao J, Han MJ, Xu Z, Li J, Meng X: Fabrication and evolution of multilayer silver nanofilms for surface-enhanced Raman scattering sensing of arsenate.

    Nanoscale Res Lett 2011, 6:263. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  42. Gao T, Xu Z, Fang F, Gao W, Zhang Q, Xu X: High performance surface-enhanced Raman scattering substrates of Si-based Au film developed by focused ion beam nanofabrication.

    Nanoscale Res Lett 2012, 7:399. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  43. Zhu SQ, Zhang T, Guo XL, Wang QL, Liu X, Zhang XY: Gold nanoparticle thin films fabricated by electrophoretic deposition method for highly sensitive SERS application.

    Nanoscale Res Lett 2012, 7:613. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  44. Tsvetkov MY, Khlebtsov BN, Khanadeev VA, Bagratashvili VN, Timashev PS, Samoylovich MI, Khlebtsov NG: SERS substrates formed by gold nanorods deposited on colloidal silica films.

    Nanoscale Res Lett 2013, 8:250. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  45. Parker AR, Townley HE: Biomimetics of photonic nanostructures.

    Nat Nanotechnol 2007, 2:347-353. PubMed Abstract OpenURL

  46. Zhang G, Zhang J, Xie G, Liu Z, Shao H: Cicada wings: a stamp from nature for nanoimprint lithography.

    Small 2006, 2:1440-1443. PubMed Abstract | Publisher Full Text OpenURL

  47. Xie G, Zhang G, Lin F, Zhang J, Liu Z, Mu S: The fabrication of subwavelength anti-reflective nanostructures using a bio-template.

    Nanotechnology 2008, 19:095605. PubMed Abstract | Publisher Full Text OpenURL

  48. Stoddart PR, Cadusch PJ, Boyce TM, Erasmus RM, Comins JD: Optical properties of chitin: surface-enhanced Raman scattering substrates based on antireflection structures on cicada wings.

    Nanotechnology 2006, 17:680-686. Publisher Full Text OpenURL