Charge storage characteristics of Au nanocrystal memory improved by the oxygen vacancy-reduced HfO2 blocking layer

Ruifan Tang, Kai Huang*, Hongkai Lai*, Cheng Li, Zhiming Wu and Junyong Kang

Author affiliations

Semiconductor Photonics Research Center, Department of Physics, Xiamen University, Xiamen 361005, China

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2013, 8:368  doi:10.1186/1556-276X-8-368


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/368


Received:2 May 2013
Accepted:21 August 2013
Published:28 August 2013

© 2013 Tang et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

This study characterizes the charge storage characteristics of metal/HfO2/Au nanocrystals (NCs)/SiO2/Si and significantly improves memory performance and retention time by annealing the HfO2 blocking layer in O2 ambient at 400°C. Experimental evidence shows that the underlying mechanism can be effectively applied to reduce oxygen vacancy and suppress unwanted electron trap-assisted tunneling. A memory window of 1 V at an applied sweeping voltage of ±2 V is also shown. The low program/erase voltage (±2 V) and the promising retention performances indicate the potential application of NCs in low-voltage, non-volatile memory devices.

Keywords:
Memory performance; Oxygen deficiency; Annealing; Non-volatile memory; 85.35.-p; 61.72.Cc

Background

Nanocrystal (NC) floating gate memory devices have recently attracted much attention as a strong candidate for non-volatile memories given their scalability, fast write/erase speeds, low operating voltages, and long retention times [1-4]. Numerous attempts have been made to develop non-volatile memory devices using metal NCs, such as Ni [5], Au [6], Ir [7], and Pt [8], because metal NCs have a higher density of states around the Fermi level, a wider range of available work functions, and smaller energy perturbation compared with their semiconductor counterparts [9]. Further improvement in memory performance can be achieved through the integration of metal NCs with high-κ dielectric materials, such as HfO2[10] and Al2O3[11]. The use of high-κ dielectric materials as blocking layers decreases the electric field at the top dielectric and program/erase (P/E) voltages, which also supports the demand for small effective oxide thickness [12]. Au NCs with high work functions (5.1 eV) enable the creation of a deep potential well to trap charge carriers, such as HfO2, with high dielectric constants (20 to 25) and relatively high barrier heights (−5.7 eV). The structure of metal/HfO2/Au NCs/SiO2/Si shows a strong potential for application in non-volatile memory devices [13,14].

Metal/HfO2/Au NCs/SiO2/Si is fabricated in this study. The capacitance-voltage (C-V) characteristics show that the main storage consists of holes. However, electron trapping is seldom achieved because of the HfO2 blocking layer. X-ray photoelectron spectroscopy (XPS) confirms that the oxygen deficiency within the HfO2 layer is caused by the presence of Hf-Hf bonding. The energy band diagram shows that electrons trapped in the NCs tend to leak into the gate electrode through trap-assisted tunneling, which is supported by the oxygen vacancy-related levels during programming. However, Hf-Hf bonding disappears after HfO2 is annealed at 400°C for 10 min in O2 ambient. The structure of metal/HfO2 (as-annealed)/Au NCs/SiO2/Si shows that both electrons and holes are stored. Given their memory window of 1 V at an applied sweeping voltage of ±2 V, low P/E voltage (±2 V), and promising retention performances, low-voltage NC memories have a strong potential for application in non-volatile memory devices.

Methods

A metal/HfO2/Au NCs/SiO2/Si (A1) structure was fabricated. P-type Si with a doping level of 8.33 × 1017 cm−3 was used as a substrate. A 3-nm-thick thermal SiO2 oxide was fabricated using a rapid thermal annealing (RTA) device after pre-gate cleaning. An Au film with a thickness of approximately 1 nm was sputtered using SCD005 (Balzers Union, Balzers, Liechtenstein) with a sputtering time of 2 s. The sample was then annealed in N2 ambient using the RTA device. Annealing was performed at 600°C for 10 s to form Au NCs. A 30-nm HfO2 film deposited by the electron beam (E-beam) evaporation system with a base pressure of 3.6 × 10−6 Torr served as the blocking layer. After depositing the TaN/Al metal gate electrode with thicknesses of 50/300 nm and the Cr/Au bottom electrode with thicknesses of 20/200 nm through magnetron sputtering, the capacitive structure of the NC memory device was finally completed. Metal/HfO2/SiO2/Si (A2), metal/SiO2/Au NCs/SiO2/Si (A3), and metal/HfO2 (PDA)/Au NCs/SiO2/Si (A4) were fabricated using the same process, with the exception of a 20-nm SiO2 film deposition using the E-beam for sample A3 and the annealing of HfO2 after deposition at 400°C for 10 min in the O2 ambient for sample A4. XPS with a 1,486.6-eV Al Kα source was used to obtain composition information about the as-deposited and annealed HfO2 film. The electrical characteristics of the NC memory devices were measured in the parallel mode using a Keithley 4200 semiconductor characterization system (Cleveland, OH, USA) and a Keithley 590 C-V analyzer at room temperature.

Results and discussion

Figure 1 shows the cross-sectional high-resolution transmission electron microscopy (HRTEM) micrograph of the A1 device. The Au NCs formed on the 3-nm thermal SiO2 are covered with a 30-nm HfO2 layer. The NC density is approximately 8 × 1011 cm−2, wherein the size is mainly distributed from 6 to 8 nm. The charging properties are described from the C-V measurements at 1 MHz with a step of 0.1 V/s for A1 (Figure 2a). Double C-V sweeps are performed with voltage sweeps from inversion to accumulation, i.e., from positive to negative bias and back to inversion to give prominence to the charge trapping in the Au NCs. Electron and hole trapping in the NCs are enabled by the positive and negative biases, respectively. The positive flat band voltage shifts (ΔV) correspond to an increase in electron trapping, whereas the negative ΔV corresponds to the increase in hole trapping given the increasing sweep voltage range. Figure 2a shows that the negative ΔV is about 1.05 V, whereas the positive ΔV is close to 0, which indicates that no additional electrons can be trapped with the increase in the sweep range. The inset plot in Figure 2a shows the C-V curves of sample A2. Sample A2 showed no apparent hysteresis loop both at the ±2 and ±4 V bias sweep, indicating that a charging effect only occurs with Au NCs. The electron’s energy barrier of 3.2 eV between Si and SiO2 is known to be much less than that of the hole (4.7 eV). Electron tunneling is expected to be easier than hole tunneling. However, the C-V characteristic shown here indicates that electron trapping is more difficult than hole trapping. One possible reason is because the electrons trapped in the Au NCs leak back to the substrate and result in lessened electron trapping, which is similar to previous reports [15]. In previous reports, a band offset exists at the valence band between Ge and Si. Holes can be trapped in Ge1 − xSix/Si heteronanocrystals, whereas electrons tunnel back to the substrate directly through the ultrathin tunnel oxide. However, these reports are inconsistent with our experiments because no additional barrier layer for holes exists in our experiments; thus, lessened electron trapping cannot be attributed to electron loss in thin tunnel oxide.

thumbnailFigure 1. Cross-sectional HRTEM micrograph of sample A1.

thumbnailFigure 2. C-V hysteresis of sample A1 (a) and sample A3 (b). The inset plot in (a) shows the C-V curves of sample A2.

Another possible mechanism leading to electron injection from the inverted substrate into the Au NCs during programming is the positive gate bias. Electrons are emitted from the NCs, which cross the HfO2 blocking layer to the gate electrode [16]. Sample A3 is fabricated with SiO2 as the blocking layer to investigate the effect of HfO2 and the possible mechanism. The control oxide thickness of SiO2 in sample A3 is noted to be about 20 nm; to lessen the electric field differences between samples A1 and A3 during the sweep process, the sweeps are performed from −8 to 0 V and −10 to 2 V. Figure 2b shows the C-V hysteresis curves for A3 with sweep ranges of −8 to 0 V and −10 to 2 V. The positive ΔV is approximately 1 V and is greater than the negative ΔV (0.38 V) with the increase in sweep range. A high positive ΔV value indicates that both electrons and holes can be stored in NCs. Electron trapping is also easier than hole trapping, which is consistent with previously reported theories and results [17,18]. Therefore, the asymmetric C-V hysteresis curve of A1 is reasonably caused by the HfO2 blocking layer. The HfO2 films prepared using different growth methods have different microstructures and properties [19]. XPS measurements are performed using our E-beam device to investigate the composition information of the as-deposited HfO2 film. About 2 nm of the sample top layer was removed using Ar ion bombardment to remove surface contaminants. Figure 3a shows the two peaks at 17.1 and 18.6 eV, which correspond to the Hf 4f and Hf 4f peaks from HfO2. Small but noticeable shoulders at the lower binding energy side of the main peak were also observed, which can be attributed to Hf-Hf bonding and indicate the existence of oxygen vacancy within the HfO2 film [20]. Oxygen vacancy reportedly results in oxygen vacancy-related levels within the bandgap [21]. Takeuchi et al. used spectroscopic ellipsometry to demonstrate the existence of shallow oxygen vacancy-related defects 1.2 eV below the HfO2 conduction band [22]. Given the existence of an oxygen vacancy-related level below the conduction band and the rise of electron potential because of electron trapping in the NCs [23], electrons trapped in Au NCs could possibly leak into the gate electrode through the trap-assisted tunneling method during the programming operation (Figure 3b). This method is similar to the multi-phonon-assisted tunneling model described in previous reports [24]. The trap-assisted tunneling effect may be responsible for the minimal electron storage.

thumbnailFigure 3. XPS spectra and energy band diagram. (a) Hf 4f core-level XPS spectra of as-deposited HfO2 film and (b) energy band diagram of sample A1 during programming.

HfO2 was annealed after deposition at 400°C in O2 ambient to verify this assumption. XPS analysis was performed on the O2-annealed HfO2 film after 2 nm of the HfO2 top layer was removed by Ar ion bombardment to remove the surface contaminants. Figure 4a shows that no evidence of Hf-Hf bonding was observed, with the exception of the characteristic peak attributed to Hf-O bonds. This lack of evidence suggests that the annealing process can effectively reduce the oxygen vacancy of HfO2 films. Sample A4 was fabricated using the O2-annealed HfO2 as blocking layer. Figure 4b shows the C-V characteristics of A4. The positive ΔV is almost similar to the negative ΔV with the increase in the sweep voltage range, thereby indicating that both electrons and holes can be easily stored in the Au NCs. The ease of electron and hole storage is caused by the reduced oxygen vacancy levels and the suppressed unwanted electron trap-assisted tunneling performed during programming, which leads to electron storage (Figure 5). Electron storage can be confirmed further through a comparison of A1 and A4’s gate current characteristics. Figure 6a shows that sample A4, with an O2-annealed HfO2, shows lower leakage current density at all regimes of the gate voltage compared with sample A1, with an as-deposited HfO2. The lower leakage current indicates that the reduced oxygen vacancy-related levels suppress electron injection from both the substrate and gate given that the positive gate voltage corresponds to substrate injection and the negative gate voltage corresponds to gate injection. Figure 6b,c shows the retention properties of A1 and A4. The initial memory windows are 0.92 and 1.02 V for A1 and A4, respectively. The windows are followed using a suitable reading condition. The decayed charges for sample A4 with O2-annealed HfO2 were only 35% within a 104-s span, which is much better than that of A1 (approximately 71% loss). The difference between the observed retention behavior of A1 and A4 could be explained by the energy band diagram, which is based on the existence of oxygen vacancy-related levels. Figure 7a shows that the electrons trapped in the Au NCs leak into the gate electrode through the HfO2 layer via electron tunneling to the oxygen vacancy-related level, as proposed in [24]; therefore, discharging easily occurs. However, the reduced oxygen-related levels in sample A4 HfO2 layer suppress the unwanted trap-assisted tunneling (Figure 7b); thus, electron loss rate is reduced.

thumbnailFigure 4. XPS spectra and C-V hysteresis. (a) Hf 4f core-level XPS spectra of as-annealed HfO2 film and (b)C-V hysteresis of sample A4.

thumbnailFigure 5. Energy band diagram of sample A1 during programming.

thumbnailFigure 6. Leakage currents and charge retention property. (a) Comparison of the gate stack leakage currents of samples A1 and A4, and charge retention property of samples (b) A1 and (c) A4.

thumbnailFigure 7. Energy band diagram of samples (a) A1 and (b) A4 during retention.

A 1-V memory window was observed for A4 at the ±2-V sweep (Figure 8), which shows the potential to prepare a low-voltage NC memory. The P/E operation was also performed by applying ±2-V pulses to the gate electrode. Figure 8 shows that a 1-V memory window can be obtained at P/E times of 10/10 ms, which shows a sufficient memory window even at a ±2-V applied pulse voltage. Given the improvements in the retention performances (Figure 6c), sample A4 shows promise for application in low-voltage NC memory.

thumbnailFigure 8. P/E characteristics of sample A4 with as-annealed HfO2 for P/E voltage levels of +2/−2 V.

Conclusions

Electrons trapped in Au NCs tend to tunnel into the gate electrode through the oxygen vacancy-related levels of the HfO2 blocking layer and tend to degrade memory performance because of the existence of oxygen vacancy. Annealing the HfO2 blocking layer at 400°C in O2 ambient decreases oxygen vacancy and suppresses unwanted electron trap-assisted tunneling. Given their memory window of 1 V at an applied sweeping voltage of ±2 V, low P/E voltage of ±2 V, and improved retention performances, low-voltage NC memories show promise for application in non-volatile memory devices.

Abbreviations

E-beam: Electron beam; HRTEM: High-resolution transmission electron microscopy; NCs: Nanocrystals; P/E: Programming/erasing; RTA: Rapid thermal annealing; XPS: X-ray photoelectron spectroscopy.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

RT carried out the experiments studied on the device fabrication and drafted the manuscript. KH designed the research programs and guided the experiment’s progress. HL, CL, ZW, and JK participated in the mechanism development. All authors read and approved the final manuscript.

Acknowledgements

This work was supported by the National Basic Research Program of China under grant numbers 2011CB301905 and 2012CB933503; National Natural Science Foundation of China under grant numbers 61108064, 61036003, and 61176092; the Fundamental Research Funds for the Central Universities (2011120143); and Ph.D. Programs Foundation of Ministry of Education of China (20110121110025).

References

  1. Yang FM, Liu PT, Chang TC: Using double layer CoSi nanocrystals to improve the memory effects of nonvolatile memory devices.

    Appl Phys Lett 2007, 90:212108. Publisher Full Text OpenURL

  2. Yang HG, Shi Y, Bu HM, Wu J, Zhao B, Yuan XL, Zheng YD: Simulation of electron storage in Ge/Si hetero-nanocrystal memory.

    Solid-State Electron 2001, 45:767. Publisher Full Text OpenURL

  3. Lee C, Kwon JH, Sohn BH: Nonvolatile nanocrystal charge trap flash memory devices using a micellar route to ordered arrays of cobalt nanocrystals.

    Appl Phys Lett 2007, 91:153506. Publisher Full Text OpenURL

  4. Lee JS, Yang JY, Hong JP: Charge trap memory characteristics of AlOx shell-Al core nanoparticles embedded in HfO2 gate oxide matrix.

    Appl Phys Lett 2009, 95:052109. Publisher Full Text OpenURL

  5. Tan Z, Samanta SK, Yoo WJ, Lee S: Self-assembly of Ni nanocrystals on HfO2 and N-assisted Ni confinement for nonvolatile memory application.

    Appl Phys Lett 2005, 86:013107. Publisher Full Text OpenURL

  6. Mikhelashvili V, Meyler B, Yoffis S, Garbrecht M: A nonvolatile memory capacitor based on Au nanocrystals with HfO2 tunneling and blocking layers.

    Appl Phys Lett 2011, 98:212902. Publisher Full Text OpenURL

  7. Wang TT-J, Chu CL, Hsieh IJ, Tseng WS: Formation of iridium nanocrystals with highly thermal stability for the applications of nonvolatile memory device with excellent trapping ability.

    Appl Phys Lett 2010, 97:143507. Publisher Full Text OpenURL

  8. Jeff RC Jr, Yun M, Ramalingam B, Triplett G, Gangopadhyay S: Charge storage characteristics of ultra-small Pt nanoparticle embedded GaAs based non-volatile memory.

    Appl Phys Lett 2011, 99:212902. Publisher Full Text OpenURL

  9. Liu ZT, Lee C, Narayanan V, Pei G, Kan EC: Metal nanocrystal memories—part I: device design and fabrication.

    IEEE Trans Electron Devices 2002, 49:9. OpenURL

  10. Kim JH, Yang JY, Lee JS, Hong JP: Memory characteristics of cobalt-silicide nanocrystals embedded in HfO2 gate oxide for nonvolatile nanocrystal flash devices.

    Appl Phys Lett 2008, 92:013512. Publisher Full Text OpenURL

  11. Wang C-C, Chiou Y-K, Chang C-H, Tseng J-Y, Wu L-J, Chen C-Y, Wu T-B: Memory characteristics of Au nanocrystals embedded in metal-oxide-semiconductor structure by using atomic-layer-depositioned Al2O3 as control oxide.

    J Phys D: Appl Phys 2007, 40:1673. Publisher Full Text OpenURL

  12. Lee C-H, Hur S-H, Shin Y-C, Choi J-H, Park D-G, Kim K: Charge-trapping device structure of SiO2/SiN/high-k dielectric Al2O3 for high-density flash memory.

    Appl Phys Lett 2005, 86:152908. Publisher Full Text OpenURL

  13. Mikhelashvili V, Meyler B, Yofis S, Shneider Y, Salzman J, Eisenstein G: Nonvolatile low-voltage memory transistor based on SiO2 tunneling and HfO2 blocking layers with charge storage in Au nanocrystals.

    Appl Phys Lett 2011, 98:212902. Publisher Full Text OpenURL

  14. Mikhelashvili V, Meyler B, Yofis S, Shneider Y, Salzman J, Eisenstein G: Optical properties of nonvolatile memory capacitors based on gold nanoparticles and SiO2-HfO2 sublayers.

    Appl Phys Lett 2011, 98:022905. Publisher Full Text OpenURL

  15. Lu J, Zuo Z, Chen YB, Shi Y: Charge storage characteristics in metal-oxide-semiconductor memory structure based on gradual Ge1-xSix/Si heteronanocrystals.

    Appl Phys Lett 2008, 90:013105. OpenURL

  16. Compagnoni C-M, Iemini D, Spinelli A, Lacaita A-L: Modeling of tunneling P/E for nanocrystal memories.

    IEEE Trans Electron Devices 2005, 52:569. Publisher Full Text OpenURL

  17. Dufourcq J, Bodnar S, Gay G, Lafond D, Vandroux L: High density platinum nanocrystals for non-volatile memory applications.

    Appl Phys Lett 2008, 92:073102. Publisher Full Text OpenURL

  18. Lee JJ, Kwong DL: Metal nanocrystal memory with high-k tunneling barrier for improved data retention.

    IEEE Trans Electron Devices 2005, 52:507. Publisher Full Text OpenURL

  19. Filatova EO, Sokolov AA, Kozhevnikov IV, Taracheva EY, Braun W: Investigation of the structure of thin HfO2 films by soft x-ray reflectometry techniques.

    J Phys Condens Matter 2009, 21:180512. OpenURL

  20. Chen B, Jha R, Misra V: Work function tuning via interface dipole by ultrathin reaction layers using AlTa and AlTaN alloys.

    IEEE Trans Electron Devices 2006, 27:731. OpenURL

  21. Ramo D-M, Gavartin J-L, Shluger A-L: Spectroscopic properties of oxygen vacancies in monoclinic HfO2 calculated with periodic and embedded cluster density functional theory.

    Phys Revi B 2007, 75:205336. OpenURL

  22. Takeuchi H, Ha D, King T-J: Observation of bulk HfO2 defects by spectroscopic ellipsometry.

    J Vac Sci Technol A 2004, 22:1337. Publisher Full Text OpenURL

  23. She M, King T-J: Impact of crystal size and tunnel dielectric on semiconductor nanocrystal memory performance.

    IEEE Trans Electron Devices 1934, 2003:50. OpenURL

  24. Lwin ZZ, Pey KL, Zhang Q, Bosman M, Liu Q, Gan CL, Singh PK, Mahapatra S: Study of charge distribution and charge loss in dual-layer metal-nanocrystal-embedded high-κ/SiO2 gate stack.

    Appl Phys Lett 2012, 100:193109. Publisher Full Text OpenURL