Microstructure and dielectric properties of biocarbon nanofiber composites

Bo Dai1*, Yong Ren1, Gaihua Wang1, Yongjun Ma2, Pei Zhu1 and Shirong Li1

Author affiliations

1 State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010, People’s Republic of China

2 Analytical and Testing Center, Southwest University of Science and Technology, Mianyang 621010, People’s Republic of China

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2013, 8:293  doi:10.1186/1556-276X-8-293


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/293


Received:19 April 2013
Accepted:7 June 2013
Published:22 June 2013

© 2013 Dai et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

A kind of web-like carbon with interconnected nanoribbons was fabricated using bacterial cellulose pyrolyzed at various temperatures, and the microwave dielectric properties were investigated. Bacterial cellulose was converted into carbonized bacterial cellulose (CBC) with a novel three-dimensional web built of entangled and interconnected cellulose ribbons when the carbonization temperature was below 1,200°C; the web-like structure was destroyed at a temperature of 1,400°C. Composites of CBC impregnated with paraffin wax exhibited high complex permittivity over a frequency range of 2 to 18 GHz, depending on the carbonization temperature. Both real and imaginary parts were the highest for CBC pyrolyzed at 1,200°C. The complex permittivity also strongly depended on CBC loadings. For 7.5 wt.% loading, the real and imaginary permittivities were about 12 and 4.3, respectively, and the minimum reflection loss was -39 dB at 10.9 GHz. For 30 wt.% loading, the real and imaginary permittivities were about 45 and 80, respectively, and the shielding efficiency was more than 24 dB in the measured frequency range and could be up to 39 dB at 18 GHz. The electromagnetic properties were assumed to correlate with both the dielectric relaxation and the novel web-like structure.

Keywords:
Carbon fibers; Heat treatment; Electrical properties; Transmission electron microscopy (TEM)

Background

The rapid proliferation of advanced electronic devices for many commercial and military applications, such as data transmission, telecommunications, wireless network systems, and satellite broadcasting as well as radar and diagnostic and detection systems, has led to numerous electromagnetic compatibility and electromagnetic interference (EMI) problems. The interaction of electromagnetic waves originating from different sources can lead to a decrease in quality and a misinterpretation of transferred data, and it has thus become vital to avoid such interference and electromagnetic wave pollution through the use of appropriate absorbing and shielding materials. Carbonaceous materials - such as graphite and/or carbon black - are often used as dielectric electromagnetic absorbers, generating dielectric loss by improving the electrical conductivity of the mixture. In particular, nanostructured materials and carbon fiber composites have been the subjects of growing interest as microwave radiation absorbing and shielding materials in the high-frequency range due to their fascinating properties [1-5]. It is reported that carbon nanofiber-polymer composites presented EMI shielding effectiveness (SE) of approximately 19 dB with 15 wt.% carbon nanofiber loading [3]. Graphite-coated FeNi nanoparticles exhibited reflection loss (RL) of approximately -23 dB with the thickness 2.5 mm and the absorption peak at 14 GHz [5]. Carbon nanocoils coated with Fe3O4 exhibited remarkably improved microwave absorption (RL approximately -20 dB) compared to the pristine carbon nanocoils (RL approximately -2 dB) [6]. Another allotrope of carbon, viz., single-layered two-dimensional graphene, graphene oxide, or reduced graphene oxide, has attracted a great deal of attention for its application in many diverse areas due to its unique electrical, mechanical, and thermal properties in addition to its light weight, high surface area, and layered morphology. The graphene/epoxy composites exhibited SE of approximately 21 dB in the X-band for a 15 wt.% loading [7]. The reduced graphene oxide exhibits -7 dB RL while graphite only exhibits approximately -1 dB in the frequency range of 2 approximately 18 GHz [8]. Further to the considerable interest in adding small concentrations of nanocarbons into the matrix, what unquestionably matters is the ability to disperse them [9]. The cost and limited supply also hinders the application of nanocarbons as fillers for EMI shielding and microwave absorption. Recently, researchers have tried low-cost natural materials (rice husks) as carbonaceous sources to fabricate carbon-matrix composites with self-assembly interconnected carbon nanoribbon networks [10]. These composites have higher electric conductivities and EMI shielding effectiveness values than those without. In this paper, the example of microwave composites is reported using bacterial cellulose as the carbonaceous source, which had self-assembled interconnected nanoribbon networks. These composites exhibited high permittivity in the frequency range of 2 to 18 GHz and thus could be excellent high-loss materials, for example, as an EMI material or high-performance microwave absorbing material. The interesting electromagnetic characteristics are due to the novel three-dimensional web-like networks which establish additional electrical conduction pathways throughout the whole system.

Methods

Sample preparation

Carbonized bacterial cellulose (CBC) was obtained by heat-treated bacterial cellulose (BC), which was pyrolyzed for 4 h under a nitrogen atmosphere at 800°C, 1,000°C, 1,200°C, or 1,400°C. CBC was cleaned using diluted hydrochloric acid with volume fraction of 10% and then soaked in concentrated nitric acid at room temperature for 4 h. Afterwards, the black solution was diluted with distilled water and rinsed for several times until the pH value reaches 7. The resulting CBC were separated from the solution by filtration and dried using a vacuum at 60°C for further use. Dried CBC fibers were mechanically milled into powder for the measurement of electromagnetic parameters. The CBC/paraffin wax samples were prepared by uniformly mixing the powders in a paraffin wax matrix. A series of CBC/paraffin wax composites were prepared with CBC loading of up to 30 wt.%. The absorbers were dispersed in ethanol with paraffin wax by stirring and sonication at 90°C for 1 h. The mixtures were then pressed into cylindrical dies with 7.0 mm outer diameter, 3.0 mm inner diameter, and about 2.0 mm height.

Characterization

The morphology of CBC was observed by transmission electron microscopy (TEM, Tecnai F20, FEI, Hillsboro, OR, USA) and scanning electron microscopy (SEM, FEI NOVA600i). The sheet resistance (Rs) of the composites was measured by the four-probe method using a Keithley 2400 multimeter (Cleveland, OH, USA), and the direct current (DC) conductivity σ was obtained using the measured Rs and the sheet thickness t according to σ = 1/(Rst). Complex permittivity and permeability measurements were performed on an Agilent E8363B vector network analyzer in the 2 to 18 GHz frequency range. Three samples were tested for each electromagnetic parameter measurement, and the reported results are the averages.

Results and discussion

Phase and microstructure of CBC

Raman scattering is a well-accepted characterization method for evaluating the degree of structural order of carbonaceous materials, using the ratio of the integrated intensity of the D band (ID) to that of the G band (IG) [11]. The typical Raman spectra (in a shift regime) of the CBC samples treated at various temperatures are shown in Figure 1a. It displays a prominent G-peak at approximately 1,585 cm-1 along with a D-peak at approximately 1,340 cm-1 corresponding to the first order scattering of the E2g mode and A1g mode, respectively. There are changes in the ratio of the area for the peaks assigned to the D and G bands, i.e., from 1.96 at 800°C to 1.68 at 1,400°C. The decrease in the ratio of the D/G bands may be explained in terms of an increase in the crystallite domains or a reduction in the quantity of amorphous carbon. Figure 1b shows the X-ray diffraction patterns of samples. It presents diffraction patterns typical of a predominantly amorphous carbon. The increased temperature led to an increase in their crystallinity, which corresponds to the result of Raman measurements.

thumbnailFigure 1. Raman spectra (a) and XRD patterns (b) for CBC pyrolyzed at various temperatures.

BC fiber is an extracellular product excreted in the form of pellicles. It is structured in a web-like network by self-assembly of continuous nanofibers about 10 nm thick and 50 nm wide [12]. Each nanofiber is a bundle of cellulose microfibrils, each of which is about 4 nm thick and 4 nm wide. The web-like network leads BC to be homogenously dispersed in the matrices [13], and its composites have significant mechanical strength and extremely low thermal-expansion coefficients [14,15]. After carbonization under a nitrogen atmosphere, BC was converted into a kind of carbon nanoribbon and the corresponding TEM images are presented in Figure 2. As shown in Figure 2a, the carbonization at temperature of 800°C did not break the pristine structure, and the web-like networks were very well preserved. The carbonized bacterial cellulose networks can be described as a three-dimensional web built of entangled and interconnected cellulose ribbons. The width and thickness of the nanoribbons are in the order of tens of nanometers and a few nanometers, respectively. A higher magnification shows that each ribbon assembly is composed of a number of extended chains of bacterial fibrils (Figure 2b). These fibrils are seen to be in close contact with one another and to twist as a whole. The structure of BC carbonization at 1,200°C is almost the same as that of carbonization at 800°C, which formed branched nanoribbon networks. However, after carbonization at 1,400°C, branches of the nanoribbon seemed to be broken and the three-dimensional structure degraded to two dimensions. The width of the nanoribbon was narrower than those shown in Figure 2a,c.

thumbnailFigure 2. TEM images of CBC pyrolyzed. At (a,b) 800°C, (c) 1,200°C, and (d) 1,400°C, respectively.

Microwave electromagnetic properties of CBC

The relative complex permittivity (ϵr= ϵ′ - jϵ″) was measured in the frequency range of 2 to 18 GHz. The real (ϵ′) and imaginary (ϵ″) parts of permittivity for the composites with 20 wt.% CBC loadings pyrolyzed at different temperatures are presented as a function of the frequency in Figure 3a,b. Both the real and the imaginary permittivities presented high values. The complex permittivity spectra reveal the behaviors of electrical conduction and dielectric relaxation of the composites. Upon increasing the temperature, the permittivity plots for the specimen displayed a firstly increasing and then diminishing response. At 1,200°C, the values of both ϵ′ and ϵ″ were the highest. The two mechanisms responsible for the dielectric properties were analyzed. First, there are many mobile charge carriers (electrons or holes) with great mobility in CBC that interact with electromagnetic fields by oscillating when irradiated, just like those in carbon nanotubes (CNTs). Second, it is proposed that the web-like networks in CBC also established bridges for mobile charge carriers along which they can move freely. These additional channels interact with the electromagnetic field over a short range, resulting in high permittivity. With an increase in the pyrolysis temperature, the degree of graphite order increased as discussed above; and thus, there were more mobile charge carriers. However, the web-like networks of carbon nanofiber was somehow destroyed when the pyrolysis temperature increased beyond 1,200°C (as shown in Figure 2d). Therefore, it is understandable that the CBC pyrolyzed at 1,200°C exhibited the highest permittivity. In addition, it is noteworthy that the magnitudes of the loss tangent (tan δe = ϵ″/ϵ′) approached 1, even exceeded 1, especially for that sample pyrolyzed at 1,200°C. The loss tangent is directly related to the attenuation factor α that determines the attenuating property of the material: the higher the loss tangent, the larger the attenuation factor [16]. Therefore, the high loss tangent for the CBC composites signifies that they have good attenuating properties.

thumbnailFigure 3. Real (a) and imaginary (b) parts of permittivity for the composites with 20 wt.% CBC loadings.

Figure 4 shows the dielectric permittivities of the CBC paraffin wax composites with 5 to 30 wt.% CBC pyrolyzed at 1,200°C. It is evident that both the real and imaginary permittivities increased rapidly with CBC concentration. The complex permittivity spectra reveal the behavior of electrical conduction and dielectric relaxation of the composites. The rapid increase in the permittivities with concentration is attributed to the onset of percolation, similar to that of the CNTs [17,18]. Figure 5 is a plot of DC conductivity of the CBC/paraffin wax composites versus the amount of the CBC loading pyrolyzed at 1200°C. One can see a sharp increase of conductivity when CBC loading was increased from 1 to 7.5 wt.%. The conductivity of the CBC was of 2 × 10-9 S/cm for 1 wt.% and 0.02 S/cm for 7.5 wt.% and reached a relatively high value of 0.5 S/cm for 15 wt.%. This implies that such a composite has a percolation threshold of about 7.5 wt.%.

thumbnailFigure 4. Frequency dependencies of (a) real and (b) imaginary permittivities.

thumbnailFigure 5. DC conductivity of CBC/paraffin wax composites versus CBC loading pyrolyzed at 1,200°C.

For microwave absorption, the elelctromagnetic parameters should be appropriate, and the optimal filler concentration is always around the percolation threshold. Theoretical RL values in the sample with 7.5 wt.% CBC loading were calculated according to the transmission line theory [19].

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/293/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/293/mathml/M1">View MathML</a>

(1)

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/293/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/293/mathml/M2">View MathML</a>

(2)

where Zin is the normalized impedance at the absorber surface. Figure 6a shows the frequency dependences of the RL at various sample thickness (t = 1.8, 1.9, 2.0, and 2.1 mm). An optimal RL of -40.9 dB was observed at 10.9 GHz with the -20 dB bandwidth over the frequency range of 10.4 to 11.4 GHz for t = 2.0 mm. The minimum RL obviously shifts to lower frequency range with increased thickness, which can be understood according to the geometrical effect matching condition in which the thickness of the layer is a quarter wavelength thickness of the material. It is interesting that microwave absorption properties do not change dramatically for the thicknesses of 1.8 to 2.1mm.

thumbnailFigure 6. Frequency dependences of the RL at various sample thickness (a) and the EMI shielding efficiency (b).

For EMI shielding, the total shielding effectiveness SET is always expressed by SET = 10 lg(Pin/Pout) = SEA + SER + SEI, where Pin and Pout are the power incident on and transmitted through a shielding material, respectively. The SEA and SER are the absorption and reflection shielding efficiencies, respectively, and can be described as SEA = 8.686 αt and SER = 20 lg |1 + n|2/4|n| [20]. For the composite with 30 wt.% CBC pyrolyzed at 1,200°C, using the measured electromagnetic parameters, we calculated the SEA (with the thickness t assumed to be 2.0 mm) and the SER, which together with SEA + SER are shown in Figure 6b. It can be seen that the SET increased from 24 dB in the low frequencies to 39 dB at 18 GHz. The contribution to the SET was mainly from the reflection in the low frequency range and from the absorption in the high range. The EMI shielding efficiency is attributed to the formation of conducting interconnected nanofiber networks in an insulating paraffin wax matrix that will interact with the incident radiation and lead to the high shielding effectiveness.

Conclusions

The pyrolysis of bacterial cellulose led to the formation of a unique interconnected web-like network of carbon nanoribbons, and this was used to fabricate carbon-matrix composites. These composites had remarkable imaginary permittivities and huge loss tangents and thus good attenuating properties. The web-like networks were very helpful for increasing the dielectric loss. The electromagnetic properties could be optimized by manipulating the bacterial nanoribbons by doping or surface modification; and thus, the RL and SET could be further improved. Based on these properties, and taking into account its other advantages, such as its light weight, easy processability, high mechanical strength, and good dispersion in the matrices, such CBC has the potential to be as an effective EMI shielding material and microwave absorber.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

BD participated in the data analysis and wrote the manuscript. YR and YM participated in the detection of the SEM and TEM. GW, PZ, and SL participated in the design of the experiment and performed the data analysis. All authors read and approved the final manuscript.

Acknowledgements

We thank Prof. C. H. Pei for the helpful discussions and Dr. J. S. Liu for the technical assistance. This work was supported by the National Basic Research Program of China (no. 2011CB612212), the Program for New Century Excellent Talents in University (no. MCET-11-1061), and the Open Project of State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials (no. 11zxfk26) of China.

References

  1. Baughman RH, Zakhidov AA, Heer WA: Carbon nanotubes–the route toward applications.

    Science 2002, 297(5582):787-792. PubMed Abstract | Publisher Full Text OpenURL

  2. Watts PCP, Hsu WK, Barnes A, Chambers B: High permittivity from defective multiwalled carbon nanotubes in the X-band.

    Adv Mater 2003, 15(7–8):600-603. OpenURL

  3. Yang YL, Gupta MC, Dudley KL, Lawrence RW: Conductive carbon nanofiber-polymer foam structures.

    Adv Mater 2005, 17(16):1999-2003. Publisher Full Text OpenURL

  4. Tang N, Zhong W, Au C, Yang Y, Han M, Lin K: Synthesis, microwave electromagnetic and microwave absorption properties of twin carbon nanocoils.

    J Phys Chem C 2008, 112(49):19316-19323. Publisher Full Text OpenURL

  5. Liu XG, Ou ZQ, Geng DY, Han Z, Jiang JJ, Liu W: Influence of a graphite shell on the thermal and electromagnetic characteristics of FeNi nanoparticles.

    Carbon 2010, 48(3):891-897. Publisher Full Text OpenURL

  6. Wang G, Gao Z, Tang S, Chen C, Duan F, Zhao S, Lin S, Feng Y, Zhou L, Qin Y: Microwave absorption properties of carbon nanocoils coated with highly controlled magnetic materials by atomic layer deposition.

    ACS Nano 2012, 6(12):11009-11017. PubMed Abstract | Publisher Full Text OpenURL

  7. Liang JJ, Wang Y, Huang Y, Ma YF, Liu ZF, Cai JM: Electromagnetic interference shielding of graphene/epoxy composites.

    Carbon 2009, 47(3):922-925. Publisher Full Text OpenURL

  8. Wang C, Han XJ, Xu P, Zhang XL, Du YC, Hu SR: The electromagnetic property of chemically reduced graphene oxide and its application as microwave absorbing material.

    Appl Phys Lett 2011, 98(7):072906–3. OpenURL

  9. Qin F, Brosseau C: A review and analysis of microwave absorption in polymer composites filled with carbonaceous particles.

    J Appl Phys 2012, 111(6):061301-061324. Publisher Full Text OpenURL

  10. Liu Q, Zhang D, Fan T, Gu J, Miyamoto Y, Chen Z: Amorphous carbon-matrix composites with interconnected carbon nano-ribbon networks for electromagnetic interference shielding.

    Carbon 2008, 46(3):461-465. Publisher Full Text OpenURL

  11. Lin W, Moon KS, Zhang S, Ding Y, Shang J, Chen M, Wong C: Microwave makes carbon nanotubes less defective.

    ACS Nano 2010, 4(3):1716-1722. PubMed Abstract | Publisher Full Text OpenURL

  12. Haigler CH, Benziman M: Cellulose and Other Natural Polymer Systems: Biogenesis, Structure, and Degradation. Edited by Brown RMJr. New York: Plenum; 1982. OpenURL

  13. Fernandes SCM, Freire CSR, Silvestre AJD, Neto CP, Gandini A, Berglund LA: Transparent chitosan films reinforced with a high content of nanofibrillated cellulose.

    Carbohydr Polym 2010, 81(2):394-401. Publisher Full Text OpenURL

  14. Nishno T, Takano K, Nakamae K: Elastic modulus of the crystalline regions of cellulose polymorphs.

    J Polym Sci, Part B: Polym Phys 1995, 33(11):1647-1651. Publisher Full Text OpenURL

  15. Yano H, Sugiyama J, Nakagaito AN, Nogi M, Matsuura T, Higita M: Optically transparent composites reinforced with networks of bacterial nanofibers.

    Adv Mater 2005, 17(2):153-155. Publisher Full Text OpenURL

  16. Von Hippel AR: Dielectrics and Waves. Boston: Artech House; 1995. OpenURL

  17. Grimes CA, Mungle C, Kouzoudis D, Fang S, Eklund PC: The 500 MHz to 5.50 GHz complex permittivity spectra of single-wall carbon nanotube-loaded polymer composites.

    Chem Phys Lett 2000, 319(5–6):460-464. OpenURL

  18. Wu JH, Kong LB: High microwave permittivity of multiwalled carbon nanotube composites.

    Appl Phys Lett 2004, 84(24):4956-4958. Publisher Full Text OpenURL

  19. Natio Y, Suetake K: Application of ferrite to electromagnetic wave and its characteristics.

    IEEE Trans Microwave Theory Tech 1971, 19(1):65-73. Publisher Full Text OpenURL

  20. Joo J, Epstein AJ: Electromagnetic radiation shielding by intrinsically conducting polymers.

    Appl Phys Lett 1994, 65(18):2278-2280. Publisher Full Text OpenURL