Open Access Nano Express

InSb-added TiO2 nanocomposite films by RF sputtering

Seishi Abe

Author affiliations

Research Institute for Electromagnetic Materials, Sendai 982-0807, Japan

Citation and License

Nanoscale Research Letters 2013, 8:269  doi:10.1186/1556-276X-8-269

The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/269


Received:19 April 2013
Accepted:30 May 2013
Published:7 June 2013

© 2013 Abe; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

This study investigates the preparation of InSb-added TiO2 nanocomposite films by RF sputtering. The optical absorption spectra are obviously shifted to visible and near-infrared regions. High-resolution transmission electron microscopy indicates that sphere-shaped InSb nanocrystals with a size of about 15 nm are dispersed in a matrix. The X-ray diffraction result reveals that the matrix forms a phase mixture of TiO2 and In2O3, which is also produced by decomposing the InSb during postannealing at 723 K. Therefore, the absorption shift is clearly due to quantum size effects of the InSb nanocrystals embedded in the wide-gap oxides TiO2 and In2O3.

Keywords:
TiO2 nanocomposite; Band gap; RF sputtering

Background

Quantum dot solar cells have attracted much attention because of their potential to increase conversion efficiency [1]. Specifically, the optical absorption edge of a semiconductor nanocrystal is often shifted due to quantum size effects. The optical band gap can then be tuned to an effective energy region for absorbing the maximum intensity of the solar radiation spectrum. Furthermore, quantum dots produce multiple electron–hole pairs per photon through impact ionization, whereas bulk semiconductor produces one electron–hole pair per photon.

A wide-gap semiconductor sensitized by semiconductor nanocrystals is a candidate material for such use. Wide-gap materials such as TiO2 and ZnO can only absorb the ultraviolet (UV) part of the solar radiation spectrum. The semiconductor nanocrystal supports the absorption of visible (vis) and near-infrared (NIR) light. Up to now, various nanocrystalline materials (InP [2], CdSe [3], CdS [4,5], PbS [6], and Ge [7,8]) have been investigated as sensitizers for TiO2. Wide-gap semiconductor ZnO was also investigated, since the band gap and the energetic position of the valence band maximum and conduction band minimum of ZnO are very close to those of TiO2[9]. Most of these composite materials were synthesized through chemical techniques, although physical deposition, such as sputtering, is also useful. In addition, one-step synthesis of a composite thin film is favorable for low-cost production of solar cells. Package synthesis requires a specific material design for each deposition technique, for example, radio frequency (RF) sputtering [10,11] and hot-wall deposition [12]. The present study proposes a new composite thin film with InSb-added TiO2 produced by RF sputtering. InSb nanocrystals may exhibit relatively high absorption efficiency due to a direct band structure with 0.17eV [13] and an exciton Bohr radius of 65.5 nm [14]. According to the material design, based on differences in the heat of formation [10,11], InSb nanocrystals are thermodynamically stable in an TiO2, since Ti is oxidized more than InSb because the free energy of oxidation in InSbO4, which is a typical oxide of InSb, exceeds that of the TiO2[15,16]. In addition, nanocrystalline InSb dispersed in the oxide matrix may exhibit quantum size effects, due to the wide band-gap of 3.2 eV in TiO2 with anatase structure [17]. However, it is difficult to forecast how the composite will be formed in the one-step synthesis, since the compound semiconductor, InSb, may have decomposed during the preparation process. In the current study, the composition of InSb-added TiO2 nanocomposite film is varied widely to find a composite with vis-NIR absorption due to the presence of InSb nanocrystals embedded in the wide-gap oxide matrix.

Methods

An InSb-added TiO2 nanocomposite film was prepared by RF sputtering from a composite target. Specifically, 5 × 5 mm2 InSb chips, which were cleaved from a 2-in diameter InSb (100) wafer, were set on a 4-in diameter ceramic TiO2 target. The chamber was first evacuated to a vacuum of 1.5 × 10−7 Torr. InSb-added TiO2 nanocomposite films were deposited on a Corning #7059 glass substrate (Norcross, GA, USA) cooled by water. The distance between the target and the substrate was kept constant at 73 mm. The total gas pressure of argon or argon with diluted oxygen was fixed at 2.0 × 10−3 Torr. RF power and deposition time were kept constant at 200 W and 60 min, and no RF bias was applied to the substrate. The InSb-added TiO2 nanocomposite films thus deposited were successively annealed at temperatures from 623 to 923 K in 50 K steps for 60 min in a vacuum to crystallize both InSb and TiO2. The film was structurally characterized using X-ray diffraction (XRD, Rigaku RAD-X, Rigaku Corporation, Tokyo, Japan). The optical-absorption spectrum of the film was measured using UV–vis-NIR spectroscopy (Shimadzu UV3150, Nakagyo-ku, Kyoto, Japan), and the composition of the film was analyzed using energy-dispersion spectroscopy (EDAX Phoenix, NJ, USA), operating at 10 kV with standard samples of MnTiO3 to calibrate the analyzed results for elements Ti and O and with InSb for elements In and Sb. The nanoscale structure was observed using high-resolution transmission electron microscopy (HRTEM, Hitachi H-9000NAR, Hitachi, Ltd., Tokyo, Japan) operating at 300 kV. Ion milling was performed during sample preparation.

Results and discussion

Figure 1 depicts the transmittance spectra of as-deposited InSb-added TiO2 thin films prepared in a pure argon atmosphere. The composition of InSb can be varied by employing different InSb chip numbers while keeping almost stoichiometric InSb at concentrations exceeding 5 at.% (In + Sb). At 0 at.% (In + Sb), the optical absorption edge of TiO2 is observed at approximately 400 nm, with relatively less optical transparency in a wide range from UV to NIR. This weak transparency is due to the oxygen deficit in TiO2 with a composition ratio O/Ti of 1.94. A slight addition of 1 at.% also exhibits similar behavior, but further concentrations exceeding 5 at.% abruptly improve the transparency due to the excess oxygen in TiO2 with ratios O/Ti exceeding 2. This result suggests that the oxygen deficit in TiO2 is improved by adding InSb. In addition, the optical absorption edge shifts towards the longer wavelength region as the In + Sb content increases.

thumbnailFigure 1. Optical transmittance spectra of as-deposited InSb-added TiO2 thin films. Inset indicates EDS analysis results of In + Sb, Sb/In, and O/Ti.

Figure 2 presents a typical XRD pattern of InSb-added TiO2 thin films annealed at different temperatures. In this case, the film was prepared in pure argon with an InSb chip number of 8 (15 at.% (In + Sb) in as-deposited film). The as-deposited film forms an amorphous structure, with XRD peaks of InSb, In2O3, and TiO2 (anatase and rutile) at a temperature of 723 K. The XRD peak of InSb tends to disappear at temperatures exceeding 823 K, beyond the melting point of 803 K, in InSb [18]. Thus, an annealing temperature of 723 K seems to be better to ensure the InSb phase stability.

thumbnailFigure 2. XRD pattern for InSb-added TiO2 thin films with different annealing temperatures. Red squares indicate InSb, black squares indicate In2O3, dots indicate TiO2 with anatase structure, and circles indicate TiO2 with rutile structure.

Figure 3 presents the XRD patterns of InSb-added TiO2 thin films with different In + Sb concentrations. In this case, the film was deposited in a pure argon atmosphere and subsequently annealed at 723 K. Postannealing reduces the composition of In + Sb in most of the samples, typically from 25 at.% (as-deposited) to 18 at.% (annealed). There are no ternary or quaternary compounds in the patterns. At 0 and 1 at.% (In + Sb), only a rutile structure can be observed, with anatase structure and Sb peaks at 5 at.%, and with InSb and In2O3 peaks at 8 at.%. Further addition of 12 at.% induces the disappearance of the Sb peak. In the experiment setup, two compounds, InSb and TiO2, are employed as the targets (i.e., metal Sb and In2O3 compound are not used). In addition, the high transparency (Figure 1) strongly suggests that residual metal elements In and Sb are negligible in the as-deposited films with concentrations exceeding 5 at.%. Both Sb and In2O3 are thus produced by decomposing the added InSb during postannealing.

thumbnailFigure 3. XRD pattern for InSb-added TiO2 thin films with different In + Sb concentrations. Red squares indicate InSb, black squares indicate In2O3, blue squares indicate Sb, dots indicate TiO2 with anatase structure, and circles indicate TiO2 with rutile structure.

The two phases, Sb and In2O3, are thus produced, due to decomposition of the added InSb during postannealing. These InSb-originating phases (InSb, Sb, and In2O3) are summarized in Figure 4 with respect to the InSb chip numbers and the annealing temperatures. The InSb phase crystallizes first at 623 K with an InSb chip number of 12 (25 at.% (In + Sb) in the as-deposited film). The Sb phase tends to appear with relatively small InSb chip numbers, less than four chips (12 at.% (In + Sb)), in contrast to the In2O3 phase with its higher chip numbers and relatively high temperatures. The dominant phase changes from Sb to In2O3 with respect to the InSb contents and annealing temperatures, although added InSb is almost stoichiometric, 2.7 at.% In + 2.6 at.% Sb with two InSb chips and 7.5 at.% In + 7.5 at.% Sb with eight chips, for example. Next, the composition is varied widely, with Ar and additional oxygen atmosphere, regardless of whether the TiO2 phase, which is also contained in the composite, affects the difference in phase appearance (Sb and In2O3). Figure 5 depicts the compositional plane of the phase appearance in InSb-added TiO2 thin films annealed at 723 K. The stoichiometric composition of TiO2 with InSb is indicated by a dotted line. Single-phase TiO2 appears in relatively low InSb concentrations. In particular, pure TiO2 (In + Sb = 0) has an oxygen deficit from stoichiometry in TiO2. This deficit causes low optical transparency over a wide wavelength range (Figure 1) at 0 at.% (In + Sb). In contrast, addition of InSb tends to provide excess oxygen from stoichiometric TiO2, in accordance with improving the transparency (Figure 1). InSb phase appears at 8 at.% (In + Sb), especially with In2O3 exceeding 12 at.%. Further addition of oxygen provides an amorphous structure. Although the as-deposited films contain almost stoichiometric InSb, with the Sb/In ratio ranging from 0.9 to 1.2, postannealing induces sublimation of Sb with the ratio less than 0.9 as indicated by green, yellow, and red colors. Such an Sb deficit is seen not only in the In2O3 with InSb and TiO2 (circle), but also in the Sb with InSb and TiO2 (square). Hence, the difference in phase appearance (Sb and In2O3) (Figure 4) seems to be independent of the compositional deviation from stoichiometry in a binary In-Sb system. According to the phase diagram of the In-Sb-O ternary system [19], the binary In-Sb system is in equilibrium with In2O3. A tie-line between the two phases (In2O3 and In-Sb system) indicates that the oxygen concentration dominates the phase appearance in the binary system. Specifically, relatively high oxygen content provides Sb with an InSb phase, even with a nominal Sb deficit from stoichiometric InSb. This suggestion is consistent with the present result. Sb with an InSb phase appears at relatively high oxygen concentrations exceeding 61 at.%, and less oxygen is needed to provide In2O3 with an InSb phase. It is therefore found that the difference in phase appearance (Sb and In2O3) (Figure 4) is due to the different inclusions of oxygen. In these results, the composite containing Sb does not achieve the present objective, since the residual Sb reduces the transparency. To avoid the inclusion of Sb, the sputtering target needs a different setup, such as excess In or less oxygen in the composite target, made of ceramic TiO2 with InSb chips. A composite with InSb and single-phase TiO2 cannot be obtained in the current study. However, the carrier mobility of the phase mixture of TiO2 and In2O3 exceeds that of the pure TiO2[20]. Thus, the inclusion of In2O3 is considered to be useful for the current interest.

thumbnailFigure 4. Relation between InSb-originating phases (InSb, Sb, and In2O3), annealing temperature, and InSb chip number. Black squares indicate single-phase In2O3; triangles indicate a phase mixture of InSb and In2O3; the red square indicates single-phase InSb; dots indicate a phase mixture of InSb and Sb, and circles indicate no relating peaks or amorphous. The dotted line indicates dominant phase change from Sb to In2O3.

thumbnailFigure 5. Compositional plane of phase appearance in InSb-added TiO2 thin films. Dots indicate a phase mixture of InSb, TiO2, and In2O3; squares indicate a phase mixture of InSb, TiO2, and Sb; triangles indicate a phase mixture of TiO2 and Sb; rhombuses indicate single-phase TiO2; and pentagons indicate amorphous. Violet indicates an Sb/In ratio of 1.00 to 1.10; blue indicates 0.90 to 0.99; green indicates 0.60 to 0.89; yellow indicates 0.40 to 0.59; and red indicates less than 0.40.

Figure 6 depicts a typical optical absorption spectrum for composite film with InSb, TiO2, and In2O3. For comparison, the absorption spectra of TiO2 and In2O3 are also presented in the figure. The absorption edge in both TiO2 and In2O3 appears in the UV range, while the composite film containing 18 at.% (In + Sb) exhibits an obvious shift to the vis-NIR range, thus absorb a desirable energy region for high conversion efficiency [21]. The composite film contains Sb deficit in InSb with a ratio Sb/In of 0.7. Hence, the actual concentration of InSb compound is estimated to be 15 at.%, assuming an Sb reacts fully to form InSb compound. The film also contains excess oxygen in TiO2 with a ratio O/Ti of 2.23. The excess oxygen and the decomposed In may react to form In2O3. The analyzed oxygen content is enough just to form stoichiometric TiO2 with an estimated concentration of 76 at.% and In2O3 with 8 at.%. An HRTEM image of the composite film is presented in Figure 7a. The slightly dark sphere-like nanocrystals are clearly dispersed, with a size of approximately 15 nm. The selected area (dotted line) is enlarged in Figure 7b for easier viewing. Fast Fourier transform (FFT) analysis of the region (circle in Figure 7b) reveals the details of the local structure in the nanocrystal. Figure 7c presents the corresponding FFT diffraction pattern, which can be indexed to cubic InSb. The spots labeled A, B, and C correspond to crystal faces of (110), (1-10), and (200) in the cubic InSb, with plane widths of 0.452, 0.466, and 0.330 nm, respectively. The angles labeled A-X-B, A-X-C, and B-X-C are 89°, 46°, and 43°. The standard data (JCPDS 6–208) indicates a plane width of 0.458 nm at both (110) and (1-10), and 0.324 nm at (200), with an angle of 90° for A-X-B and 45° for both A-X-C and B-X-C. The analysis results are close to the standard data. The observed grain is thus found to be cubic InSb nanocrystal. Therefore, InSb-added TiO2 nanocomposite film produces a composite with InSb nanocrystals dispersed in a multiphase matrix composing TiO2 and In2O3. The mean grain size of the InSb nanocrystals is estimated to be 18 nm using Scherrer's formula [22] in XRD peak fitting. This size is nearly the same as that of the observed InSb nanocrystals. This is small enough to exhibit the quantum size effects because of the exciton Bohr radius of 65.5 nm in InSb [14]. Furthermore, the ground state transition of electron–hole pairs in the semiconductor nanocrystal is calculated by the following formula [23,24]: E = Eg + (ħπ)2/2μR2 − 1.8e2/4π ∈ ∈ 0R, where Eg is the bulk band gap, ħ is the reduced Planck constant, μ is the reduced mass of an electron–hole pair, R is the effective Bohr radius, e is the electron charge, and ∈ is the background dielectric constant of InSb. Hence, the ground state transition of the InSb nanocrystals is calculated to be 0.78 eV, which corresponds well to the onset absorption containing 18 at.% (In and Sb) (Figure 6). Therefore, the optical absorption shift is obviously due to quantum size effects of the InSb nanocrystals embedded in the multiphase matrix, TiO2 and In2O3.

thumbnailFigure 6. Typical optical absorption spectra of InSb-added TiO2 composite film. With a phase mixture of InSb, TiO2, and In2O3, containing 18 at.% (In + Sb).

thumbnailFigure 7. Direct observation of InSb-added TiO2 nanocomposite film. With a phase mixture of InSb, TiO2, and In2O3, containing 18 at.% (In + Sb). (a) HRTEM image. (b) Enlarged image for easier viewing. (c) FFT diffraction pattern of the selected area, indicated by the circle in (b).

InSb-added Al-oxide thin film, which is a similar composite containing InSb nanocrystals, produces a mean grain size of 8 nm during postannealing at 723 K, with similar concentrations of 9.5 at.% In and 13.5 at.% Sb [25]. The present result provides InSb nanocrystals of nearly twice this size. In addition, no inclusion of In2O3 is seen in the InSb-added Al-oxide thin films, while this does appear in the present study (Figures 2 and 3). These different results are probably due to the difference in the free energy of reaction between the two oxides, TiO2 and Al2O3[16]. Specifically, Al2O3 with its smaller free energy of reaction is thermodynamically more stable than TiO2. InSb-added Al-oxide thin films also exhibit a narrower size distribution in the InSb nanocrystals compared with that of the SiO2 matrix [26], whose free energy of reaction is close to that of the TiO2. The thermodynamic stability of the matrix may affect the aggregation of the InSb nanocrystals during postannealing, although the size distribution of the InSb nanocrystals dispersed in the multiphase matrix, TiO2 and In2O3, is not estimated here, due to a difficulty of finding InSb nanocrystals in the HRTEM image containing three kinds of crystals, InSb, TiO2, and In2O3.

The present results indicate that InSb-added TiO2 nanocomposite films provide a composite with InSb nanocrystals embedded in a multioxide matrix composing TiO2 and In2O3 and exhibiting vis-NIR absorption due to quantum size effects of the InSb nanocrystals. One-step synthesis of a composite thin film therefore has potential for low-cost production of next-generation solar cells.

Conclusions

InSb-added TiO2 nanocomposite films have been proposed as candidate materials for quantum dot solar cells. It should be pointed out that composite thin films with InSb nanocrystals dispersed in a multiphase composing TiO2 and In2O3 appear in a restricted composition range from 12 to 18 at.% (In + Sb), because of compositional variation. The optical absorption edge shifts toward the vis-NIR range, favorably absorbing a desirable energy region for high conversion efficiency. A HRTEM image indicates that the composite thin film contains spherical InSb nanocrystals with a size of approximately 15 nm. This size is sufficiently small to exhibit quantum size effects. InSb-added TiO2 nanocomposite films also produce In2O3, due to decomposition of the added InSb during postannealing. The electrical properties are not studied at all in the present study. However, the photocurrent of the composite may be enhanced by including In2O3, since the carrier mobility of the phase mixture of TiO2 and In2O3 is higher than that of the pure TiO2. Therefore, a multioxide matrix of TiO2 and In2O3 with InSb nanocrystals should be useful for next-generation solar cells.

Competing interests

The author declares that there are no competing interests.

Author information

SA is a group leader of the Research Institute for Electromagnetic Materials.

Acknowledgments

The present work was supported by a Grant-in-Aid for Scientific Research from the Japan Society for the Promotion of Science (No. 24360295). The author gratefully acknowledges the valuable comments of President T. Masumoto (Research Institute for Electromagnetic Materials (DENJIKEN), Sendai, Japan). The author is also grateful to Mr. N. Hoshi (DENJIKEN) for assisting in the experiments.

References

  1. Nozik AJ: Quantum dot solar cells.

    Phys E 2002, 14:115-120. Publisher Full Text OpenURL

  2. Zaban A, Micic OI, Gregg BA, Nozik AJ: Photosensitization of nanoporus TiO2 electrodes with InP quantum dots.

    Langmuir 1998, 14:3153-3156. Publisher Full Text OpenURL

  3. Liu D, Kamat PV: Photoelectrochemical behavior of thin CdSe and coupled TiO2/CdSe semi-conductor films.

    J Phys Chem 1993, 97:10769-10773. Publisher Full Text OpenURL

  4. Weller H: Quantum sized semiconductor particles in solution in modified layers.

    Ber Bunsen-Ges Phys Chem 1991, 95:1361-1365. Publisher Full Text OpenURL

  5. Zhu G, Su F, Lv T, Pan L, Sun Z: Au nanoparticles as interfacial layer for CdS quantum dot-sensitized solar cells.

    Nanoscale Res Lett 2010, 5:1749-1754. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  6. Hoyer P, Könenkamp R: Photoconduction in porus TiO2 sensitized by PbS quantum dots.

    Appl Phys Lett 1995, 66:349-351. Publisher Full Text OpenURL

  7. Chatterjee S, Goyal A, Shah I: Inorganic nanocomposites for next generation photovoltaics.

    Mater Lett 2006, 60:3541-3543. Publisher Full Text OpenURL

  8. Abe S, Ohnuma M, Ping DH, Ohnuma S: Anatase-dominant matrix in Ge/TiO2 thin films prepared by RF sputtering method.

    Appl Phys Exp 2008, 1:095001. OpenURL

  9. Yang W, Wan F, Chen S, Jiang C: Hydrothermal growth and application of ZnO nanowire films with ZnO and TiO2 buffer layers in dye-sensitized solar cells.

    Nanoscale Res Lett 2009, 4:1486-1492. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  10. Ohnuma S, Fujimori H, Mitani S, Masumoto T: High-frequency magnetic properties in metal-nonmetal granular films.

    J Appl Phys 1996, 79:5130-5135. Publisher Full Text OpenURL

  11. Abe S: Formation of Nb2O5 matrix and vis-NIR absorption in Nb-Ge-O thin film.

    Nanoscale Res Lett 2012, 7:341. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  12. Abe S: One-step synthesis of PbSe-ZnSe composite thin film.

    Nanoscale Res Lett 2011, 6:324. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  13. Littler CL, Seller DG: Temperature dependence of the energy band gap of InSb using nonlinear optical techniques.

    Appl Phys Lett 1985, 46:986-988. Publisher Full Text OpenURL

  14. Lin MC, Chen PY, Su IW: Electrodeposition of zinc telluride from a zinc chloride-1-ethyl-methylimidazolium chloride molten salt.

    J Electro Soc 2001, 10:c653. OpenURL

  15. Band AJ, Oarsons R, Jordan J: Standard potentials in aqueous solution. New York: Taylor & Francis; 1985:70-83. OpenURL

  16. Kubachevski O, Alcock CB: Metallurgical Thermochemistry. Oxford: Pergamon; 1979. OpenURL

  17. Tang H, Prasad K, Sanjine`s R, Schmid PE, Levy F: Electrical and optical properties of TiO2 anatase thin films.

    J Appl Phys 1994, 75:2042. Publisher Full Text OpenURL

  18. Sharma X, Ngai N, Chang A: The In-Sb system.

    J Phase Equilibria 1989, 10:657-664. OpenURL

  19. Kobayashi J, Itoh S: Thermodynamic study on indium-antimony-oxygen system with respect to recycling of rare metals from compound semiconductors.

    J Japan Inst Metals 2008, 72:763-768. Publisher Full Text OpenURL

  20. Chen Y, Zhou X, Zhao X, He X, Gu X: Crystallite structure, surface morphology and optical properties of In2O3-TiO2 composite thin films by sol–gel method.

    Materials Science and Engeering B 2008, 151:179-186. Publisher Full Text OpenURL

  21. Loferski JJ: Theoretical considerations covering the choice of the optimum semiconductor for photovoltaic solar energy conversion.

    J Appl Phys 1956, 27:777-784. Publisher Full Text OpenURL

  22. Scherrer P: Bestimmung der Größe und der inneren Struktur von Kolloidteilchen mittels Röntgenstrahlen.

    Göttinger Nachrichten 1918, 2:98-100. PubMed Abstract | PubMed Central Full Text OpenURL

  23. Brus LE: A simple model for the ionization potential, electron affinity, and aqueous redox potentials of small semiconductor crystallites.

    J Chem Phys 1983, 79:5566-5571. Publisher Full Text OpenURL

  24. Giessen H, Flugel B, Mohs G, Peyghambarian Nsprague JR, Micic OI, Nozik AJ: Observation of the quantm confined ground state in InP quantum dots at 300K.

    Appl Phys Ltt 1996, 68:304-306. Publisher Full Text OpenURL

  25. Usui H, Abe S, Ohnuma S: InSb/Al-O nanogranular films prepared by RF Sputtering.

    J Phys Chem C 2009, 113:20589-20593. Publisher Full Text OpenURL

  26. Zhu K, Shi J, Zhang L: Preparation and optical absorption of InSb microcrystallites embedded in SiO2 thin films.

    Solid State Commun 1998, 107:79-84. Publisher Full Text OpenURL