Open Access Highly Accessed Nano Express

Unique mechanical properties of nanostructured transparent MgAl2O4 ceramics

Jie Zhang1*, Tiecheng Lu23*, Xianghui Chang4, Nian Wei2 and Jianqi Qi2

Author Affiliations

1 School of Physics and Optoelectronic Engineering, Ludong University, Yantai 264025, People’s Republic of China

2 Department of Physics and Key Laboratory for Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, People’s Republic of China

3 International Center for Material Physics, Chinese Academy of Sciences, Shenyang 110015, People’s Republic of China

4 College of Physical Science and Technology, Southwest Jiaotong University, Chengdu 610031, People’s Republic of China

For all author emails, please log on.

Nanoscale Research Letters 2013, 8:261  doi:10.1186/1556-276X-8-261


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/261


Received:27 March 2013
Accepted:21 May 2013
Published:1 June 2013

© 2013 Zhang et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Nanoindentation tests were performed on nanostructured transparent magnesium aluminate (MgAl2O4) ceramics to determine their mechanical properties. These tests were carried out on samples at different applied loads ranging from 300 to 9,000 μN. The elastic recovery for nanostructured transparent MgAl2O4 ceramics at different applied loads was derived from the force-depth data. The results reveal a remarkable enhancement in plastic deformation as the applied load increases from 300 to 9,000 μN. After the nanoindetation tests, scanning probe microscope images show no cracking in nanostructured transparent MgAl2O4 ceramics, which confirms the absence of any cracks and fractures around the indentation. Interestingly, the flow of the material along the edges of indent impressions is clearly presented, which is attributed to the dislocation introduced. High-resolution transmission electron microscopy observation indicates the presence of dislocations along the grain boundary, suggesting that the generation and interaction of dislocations play an important role in the plastic deformation of nanostructured transparent ceramics. Finally, the experimentally measured hardness and Young’s modulus, as derived from the load–displacement data, are as high as 31.7 and 314 GPa, respectively.

Keywords:
Nanostructured transparent ceramic; Nanoindentation; Hardness; Elastic modulus

Background

Magnesium aluminate (MgAl2O4) spinel transparent ceramic has been considered as an important optical material due to its good mechanical properties and excellent transparency from visible light to infrared wavelength range [1]. However, it is well known that their intrinsic fracture toughness (premature failure due to brittle fracture) [2-4] limits their wide applications in severe environments. Therefore, there has been great interest in the investigation of ceramic materials with improved toughness [5-8]. In particular, it has been believed that nanostructured ceramics may have greatly improved mechanical properties when compared with their conventional large-grained counterparts [9].

In our previous work [10,11], we employed a novel technique to study the fabrication of nanostructured transparent ceramics. Moreover, we analyzed the transparency mechanism in these ceramics. Nanoindentation is a powerful technique widely employed to determine the mechanical properties of nanostructured materials [12,13]. However, during the past decades, nanoindentation test has been widely utilized to measure the mechanical properties of numerous materials including polycrystalline ceramics [14-16] rather than those of nanostructured transparent ceramics. In this paper, we use the nanoindentation technique to probe the mechanical properties of nanostructured transparent MgAl2O4 ceramics.

Methods

High-purity nanostructured transparent MgAl2O4 ceramics with a grain size of approximately 40 nm, fabricated by high pressure-temperature sintering [10], were selected as the test material for the present study. The mechanical properties of ceramic samples were characterized using a nanoindentation technique (Hysitron Inc., Minneapolis, MN, USA). Nanoindentation experiments were carried out on the samples with a diamond Berkovich (three-sided pyramid) indenter. In all loading-unloading cycles, loading and unloading lasted 2 s, respectively, and with a pause at a maximum load (Pmax) of 5 s. More than 20 indentations were performed at each load. The employed load ranges from 300 to 9,000 μN. Hardness (H) and Young’s modulus (Er) were calculated based on the model of Oliver and Pharr approach [17]. The nanostructure of the samples was investigated by means of high-resolution transmission electron microscopy (HRTEM). The residual nanoindentation imprints were observed using a scanning probe microsope (SPM).

Results and discussion

Figure 1 shows a typical load-depth curve obtained through nanoindentation in the present study. The inset shows the difference between the total indentation depth at a maximum indented load (hmax) and depth of residual impression upon unloading (hf), i.e., the elasticity recovery hmaxhf. Following the nanoindentation load-depth data, the H and Er were determined [17]; these quantities can be derived using the following relations:

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/261/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/261/mathml/M1">View MathML</a>

(1)

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/261/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/261/mathml/M2">View MathML</a>

(2)

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/261/mathml/M3','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/261/mathml/M3">View MathML</a>

(3)

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/261/mathml/M4','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/261/mathml/M4">View MathML</a>

(4)

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/261/mathml/M5','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/261/mathml/M5">View MathML</a>

(5)

where S is the elastic constant stiffness defined as the slope of the upper portion of the unloading curve, as shown in Figure 1, hc is the contact depth, ϵ is the strain (0.75 for the Berkovich indenter), Pmax is the maximum applied load, A is the projected contact area at that load, Er is the Young’s modulus, and β is the correction factor that depends on the geometry of the indenter (for the Berkovich tip, β is 1.034).

thumbnailFigure 1. Typical load-depth curve obtained from nanoindentation,Pmax = 3,250 μN. Inset shows the elastic recovery (hmaxhf) as a function of applied load.

Also, we determined the elastic recovery (hmaxhf) for nanostructured transparent MgAl2O4 ceramics indented at different applied loads. The results showed that there was a higher degree of plastic deformation at a higher applied load, as shown in the inset of Figure 1.

The load-depth curve (Figure 1) is characterized by a substantial continuity, i.e., there are no large steps (pop-ins or pop-outs) observed in both loading and unloading. Figure 1 shows high elastic recovery (70.58%) and low plastic deformation (29.42%). However, when different loads were applied from 300 to 9,000 μN, it was observed that there was an appreciable increase in plastic deformation. In fact, from the present calculation of the depth before and after removal of the applied load, it was found that 57.72% of the total work done during the indentation is attributed to elastic deformation.

Images of the nanoindentation were captured by the SPM mode, as shown in Figure 2A, which confirms the absence of any cracks and fractures around the indented zone. Instead, the flow of the material along the edges of indent impressions can be clearly seen. This flow is substantiated via a line trace of SPM images along the diagonal section of the selected indent (bluish grey line in Figure 2A). The corresponding cross-sectional profiles are displayed in Figure 2B. Similar pile-ups around the indentation were observed in the nanocrystallization during the nanoindentation of a bulk amorphous metal alloy at room temperature, indicating the severity of plastic flow around this region during indentation [18]. Moreover, polycrystalline hydroxyapatite is reported to exhibit plasticity at higher temperature [19,20], but no plasticity has been reported at room temperature for nanostructured transparent ceramics. Furthermore, for ceramic materials, the plasticity is limited at low loads, and the influence of dislocation can be important [21,22]. Thus, the faceted pile-up region suggests that dislocations generated during the indentation are attributed to the residual strain of nanostructured transparent ceramics.

thumbnailFigure 2. SPM image and corresponding cross-sectional profile. SPM image of an indented area (A) and the corresponding cross-sectional profile (B) along the bluish grey line in (A).

In order to further investigate the mechanical properties of nanostructured transparent ceramics, we used HRTEM to examine the microstructures of the sample indented at 9,000 μN. The HRTEM image is shown in Figure 3. The inset in this figure is a selected area electron diffraction pattern of the indented sample, indicative of a magnesia-alumina spinel crystal structure. The left part of the HRTEM image reveals well-ordered atomic structures. However, there are dislocations close to the triangular grain boundary, suggesting that the generation, movement, and interaction of dislocations during the indentation play an important role in the plastic deformation as well as the resulting mechanical properties.

thumbnailFigure 3. HRTEM image of the nanostructured transparent MgAl2O4 ceramic. Inset shows the selected area diffraction pattern.

Hardness and Young’s modulus of the nanostructured transparent MgAl2O4 ceramics are shown in Figure 4 as a function of the applied load. Both hardness and Young’s modulus decrease with increasing loads. Furthermore, it also indicates that there appears to be a larger decrease in the hardness than in the Young’s modulus with increasing load. These phenomena have been attributed to the well-known indentation size effect. Gong et al. [14] studied an alumina ceramic by nanoindentation testing and found that more cracks were generated at higher loads. However, the absence of cracks in the vicinity of the indented zone (Figure 2) suggests that it should not be reasonable to explain the load-dependent mechanical properties of our nanostructured transparent ceramics only by the indentation size effect. Dislocation activity, as evidenced in Figure 3, compared to HRTEM images of the sample at atmospheric pressure [11] should be considered as an important factor that can influence the mechanical properties of nanostructured transparent ceramics. A more detailed study is clearly needed to understand how the dislocation activity influences the mechanical properties.

thumbnailFigure 4. Hardness (A) and Young’s modulus (B) as a function of applied load. Inset shows TEM image of the sample.

It has been observed that the hardness and modulus of ceramic materials with a smaller grain size have stronger load dependence than those with a larger grain size [23]. However, Young’s modulus is independent of the applied load when the load is above 10 mN [21]. Moreover, the contact depths in nanostructured samples indented at the lowest peak loads are already equal to or larger than the average grain size, and thus, Young’s modulus does not show any variation with increasing applied load [24]. In order to compare the hardness and modulus of our nanostructured transparent ceramics with those of conventional large-grained ceramics, we averaged the hardness and modulus data shown in Figure 4. The average hardness and modulus are 31.7 and 314 GPa, respectively. Our average hardness is approximately twice that of large-grained (100 to 200 μm) MgAl2O4[25]. This is understandable since the well-known Hall–Petch relationship predicts that a material with a smaller grain size should be harder than the same material with a larger grain size. Both the average modulus (314 GPa) and the modulus (265 GPa) measured at the maximum load (9,000 μN) are comparable to the Young’s modulus (277 GPa) of large-grained (100 to 200 μm) MgAl2O4[25]. This is also reasonable since it has been predicted that [26] the difference in Young’s modulus between porosity-free nanostructured materials with a grain size larger than 10 nm and conventional large-grained materials should be within approximately 5%.

Conclusion

In summary, the deformation behavior and the mechanical properties (hardness and Young’s modulus) of the nanostructured transparent MgAl2O4 ceramics have been determined by nanoindentation tests. The degree of plastic deformation increases with increasing applied loads. After the indentation test, scanning probe microscope image shows no cracking, whereas high-resolution TEM image shows the evidence of dislocation activity in nanostructured transparent MgAl2O4 ceramics. The measured hardness is much higher than that of conventional large-grained MgAl2O4 ceramics, which should be of considerable interest to the fields of materials science and condensed matter.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

JZ carried out the sample preparation, analyzed SPM, and participated on the nanoindentation analysis and paper corrections. TL analyzed the microstructures, evaluated the hardness and modulus, and designed the study. XC analyzed the TEM and HRTEM. NW and JQ participated in the study coordination and paper correction. All authors read and approved the final manuscript.

Acknowledgments

This work was supported by the National Natural Science Foundation (NSFC) of the People’s Republic of China under grant no. 50272040, Fok Ying Tong Education Foundation under grant no. 91046, Youth Foundation of Science and Technology of Sichuan Province under grant no. 03ZQ026-03, NSFC of the People’s Republic of China under grant no. 50742046, NSFC of the People’s Republic of China under grant no. 50872083, and Doctor Foundation of Ludong University under grant no. LY2012019. We thank T.D. Shen for his technical assistance in preparing our manuscript.

References

  1. Wang C, Zhao Z: Transparent MgAl2O4 ceramic produced by spark plasma sintering.

    Scripta Mater 2009, 61:193-196. Publisher Full Text OpenURL

  2. Zhang X, Wang Z, Hu P, Han WB, Hong C: Mechanical properties and thermal shock resistance of ZrB2–SiC ceramic toughened with graphite flake and SiC whiskers.

    Scripta Mater 2009, 61:809-812. Publisher Full Text OpenURL

  3. Zhao Z, Zhang L, Zheng J, Bai H, Zhang S, Xu B: Microstructures and mechanical properties of Al2O3/ZrO2 composite produced by combustion synthesis.

    Scripta Mater 2005, 53:995-1000. Publisher Full Text OpenURL

  4. Han XD, Zhang YF, Zheng K, Zhang XN, Zhang Z, Hao YJ, Guo XY, Yuan J, Wang ZL: Low-temperature in situ large strain plasticity of ceramic SiC nanowires and its atomic-scale mechanism.

    Nano Lett 2007, 7:452-467. PubMed Abstract | Publisher Full Text OpenURL

  5. Tredway WK: Materials science - toughened ceramics.

    Science 1998, 282:1275-1275. OpenURL

  6. Koziol K, Vilatela J, Moisala A, Motta M, Cunniff P, Sennett M, Windle A: High-performance carbon nanotube fiber.

    Science 2007, 318:1892-1895. PubMed Abstract | Publisher Full Text OpenURL

  7. Lawn BR, Padture NP, Cait H, Guiberteau F: Making ceramics ductile.

    Science 1994, 263:1114-1116. PubMed Abstract | Publisher Full Text OpenURL

  8. Rao MP, Sanchez-Herencia AJ, Beltz GE, McMeeking RM, Lange FF: Laminar ceramics that exhibit a threshold strength.

    Science 1999, 286:102-105. PubMed Abstract | Publisher Full Text OpenURL

  9. Szlufarska I, Nakano A, Vashishta P: A crossover in the mechanical response of nanocrystalline ceramics.

    Science 2005, 309:911-914. PubMed Abstract | Publisher Full Text OpenURL

  10. Lu T, Chang X, Qi J, Luo X: Low-temperature high-pressure preparation of transparent nanocrystalline MgAl2O4 ceramics.

    Appl Phys Lett 2006, 88:213120. Publisher Full Text OpenURL

  11. Zhang J, Lu T, Chang X, Wei N, Xu W: Related mechanism of transparency in MgAl2O4 nano-ceramics prepared by sintering under high pressure and low temperature.

    J Phys D: Appl Phys 2009, 42:052002(5pp). OpenURL

  12. Gouldstone A, Van Vliet KJ, Suresh S: Nanoindentation simulation of defect nucleation in a crystal.

    Nature 2001, 411:656. PubMed Abstract | Publisher Full Text OpenURL

  13. Lucas M, Leach AM, McDowell MT, Hunyadi SE, Gall K, Murphy CJ, Riedo E: Plastic deformation of pentagonal silver nanowires: comparison between AFM nanoindentation and atomistic simulations.

    Phys Rev B 2008, 77:245420-245424. OpenURL

  14. Gong J, Peng Z, Miao H: Analysis of the nanoindentation load–displacement curves measured on high-purity fine-grained alumina.

    J Eur Ceram Soc 2005, 25:649-654. Publisher Full Text OpenURL

  15. Lee D, Jia S, Banerjee S, Bevk J, Herman IP, Kysar JW: Viscoplastic and granular behavior in films of colloidal nanocrystals.

    Phys Rev Lett 2007, 98:026103-026104. PubMed Abstract | Publisher Full Text OpenURL

  16. Ca´ceres D, Vergara I, Gonza´lez R: Effect of neutron irradiation on hardening in MgO crystals.

    Phys Rev B 2002, 66:024111-024116. OpenURL

  17. Oliver WC, Pharr GM: An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments.

    J Mater Res 1992, 7:1564-1583. Publisher Full Text OpenURL

  18. Kim J-J, Choi Y, Suresh S, Argon AS: Nanocrystallization during nanoindentation of a bulk amorphous metal alloy at room temperature.

    Science 2002, 295:654-657. PubMed Abstract | Publisher Full Text OpenURL

  19. Viswanath B, Raghavan R, Ramamurty U, Ravishankar N: Mechanical properties and anisotropy in hydroxyapatite single crystals.

    Scripta Mater 2007, 57:361-364. Publisher Full Text OpenURL

  20. Singh D, de la Cinta L-MM, Routbort JL, Gutierrez-Mora F, Case ED: Plastic deformation of hydroxyapatites and its application to joining.

    Int J Appl Ceram Tech 2005, 2:247-255. Publisher Full Text OpenURL

  21. Roa JJ, Capdevila XG, Martinez M, Espiell F, Segarra M: Nanohardness and Young’s modulus of YBCO samples textured by the Bridgman technique.

    Nanotech 2007, 18:385701. Publisher Full Text OpenURL

  22. Kooi BJ, Poppen RJ, Carvalho NJM, De Hosson JTM, Barsoum MW: Ti3SiC2: a damage tolerant ceramic studied with nanoindentations and transmission electron microscopy.

    Acta Mater 2003, 51:2859-2872. Publisher Full Text OpenURL

  23. Tang CY, Uskokovic PS, Tsui CP, Veljovic DJ, Petrovic R, Janackovic DJ: Influence of microstructure and phase composition on the nanoindentation characterization of bioceramic materials based on hydroxyapatite.

    Ceram Inter 2009, 35:2171-2178. Publisher Full Text OpenURL

  24. Guicciardi S, Sciti D, Melandri C, Bellosi A: Nanoindentation characterization of submicro- and nano-sized liquid-phase-sintered SiC ceramics.

    J Am Ceram Soc 2004, 87:2101-2107. OpenURL

  25. Technology Assessment & Transfer, Inc:

    Transparent spinel ceramics for armor and electro-optical applications.

    http://www.techassess.com/doc/spinel_technical_data.pdf webcite

    OpenURL

  26. Shen TD, Koch CC, Tsui TY, Pharr GM: On the elastic moduli of nanocrystalline Fe, Cu, Ni, and Cu-Ni alloys prepared by mechanical milling/alloying.

    J Mater Res 1995, 10:2892-2896. Publisher Full Text OpenURL