CdSe, CdSe-TiO2, and CdSe-C60/TiO2 composites were prepared using sol–gel method, and their photocatalytic activity was evaluated by measuring the degradation of rhodamine B solutions under visible light. The surface area, surface structure, crystal phase, and elemental identification of these composites were characterized by nitrogen adsorption isotherms, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDX), and UV-visible (vis) absorption spectrophotometry. XRD showed that the CdSe-C60/TiO2 composite contained a typical single and clear anatase phase. SEM of the CdSe-C60/TiO2 composites revealed a homogenous composition in the particles. EDX revealed the presence of C and Ti with strong Cd and Se peaks in the CdSe-C60/TiO2 composite. The degradation of dye was determined by UV–vis spectrophotometry. An increase in photocatalytic activity was observed and attributed to an increase in the photoabsorption effect by fullerene and the cooperative effect of the CdSe. The repeatability of photocatalytic activity was also tested in order to investigate the stability of C60 and CdS-C60/TiO2 composites.
Keywords:Fullerene; CdSe; Visible light; UV–vis; TEM
TiO2 is the most widely used photocatalyst for effective decomposition of organic compounds in air and water under irradiation of UV light with a shorter wavelength, corresponding to its bandgap energy, due to its relatively high photocatalytic activity, biological and chemical stability, low cost, nontoxic nature, and long-term stability. However, the photocatalytic activity of TiO2 (the bandgap of anatase TiO2 is 3.2 eV which can be excited by photons with wavelengths below 387 nm) is limited to irradiation wavelengths in the UV region [1,2]. However, only about 3% to 5% of the solar spectrum falls in this UV range. This limits the efficient utilization of solar energy for TiO2. Some problems still remain to be solved in its application, such as the fast recombination of photogenerated electron–hole pairs. Therefore, improving the photocatalytic activity by modification has become a hot topic among researchers in recent years [3,4].
Photosensitization of stable, large bandgap semiconductors such as SnO2, TiO2, and ZnO in visible light using semiconducting photosensitizers such as CdS, CdSe, and CdTe  has been a long-sought, continuing goal in the area of photoelectrochemical solar energy conversion. Cadmium selenide is a kind of semiconductor with a forbidden zone of 1.7 eV, and its valence electrons can be easily evoked to conduction band when the light wavelength of evoking light is ≤730 nm [6-9]. However, in practical applications, the photoelectrical properties and photocatalytic efficiency of CdSe require improvement.
Conjugated material is proposed to be a good candidate for improving the transportation of photocarriers in the photocatalysis process by forming an electronic interaction with TiO2 due to its unique properties in electron or hole transporting . Among them, fullerene has a variety of special chemical and physical properties due to its delocalized conjugated structure and has been studied quite extensively . Fullerene can efficiently promote a rapid photo-induced charge separation and slow down charge recombination in the dark. Therefore, fullerene has been used to raise the performances of solar cell and medicinal chemistry [12,13]. Kamat et al. have demonstrated the charge transfer between fullerene clusters and titanium dioxide under visible light; fullerene can be reduced by one-electron function in colloidal TiO2 suspensions and form C60. Besides, many works focused on improving the efficiency of dye sensitization-based photochemical solar cells by adding C60. Those researches were mostly focused on the electron transfer between TiO2 particle and C60 cluster. Photon conversion efficiency can be improved by C60 cluster due to high separation efficiency for the photo-induced electrons and holes. Although the use of fullerene for scavenging photogenerated electrons from titanium dioxide particles has been demonstrated, a few efforts are made to utilize the unique properties of fullerenes to increase the efficiency of photocatalysis; however, the interior mechanism is yet not very clear. A systematical study on a purpose of understanding the interaction between C60 molecules and TiO2 and further effect on the photocatalytic activity is still necessary and important [15-17].
In this work, CdSe-TiO2 and C60-hybridized CdSe-TiO2 photocatalysts showed significantly enhanced photocatalytic activity for the degradation of salicylic acid and formaldehyde under visible-light irradiation. The enhancement of photoactivity was attributed the photosensitization of CdSe and the enhanced interfacial charge separation between C60 layers and TiO2 particles.
Crystalline fullerene (C60) powder of 99.9% purity from TCI (Tokyo Kasei Kogyo Co. Ltd., Tokyo, Japan) was used as the carbon matrix. For the oxidization of C60, m-chloroperbenzoic acid (MCPBA) was chosen as the oxidizing agent and was purchased from Acros Organics (Fair Lawn, NJ, USA). Benzene (99.5%) was used as the organic solvent and was purchased from Samchun Pure Chemical Co., Ltd. (Seoul, Korea). Cadmium acetate dihydrate (Cd(CH3COO)2, 98%), selenium metal powder, and ammonium hydroxide (NH4OH, 28%) were purchased from Dae Jung Chemicals & Metal Co., Ltd. (Siheung-si, Gyonggi-do, Korea). Anhydrous purified sodium sulfite (Na2SO3, 95%) was purchased from Duksan Pharmaceutical Co., Ltd. (Ansan-si, Gyeonggi-do, Korea). Titanium(IV) n-butoxide (TNB, C16H36O4Ti) as the titanium source for the preparation of the CdSe-C60/TiO2 composites was purchased as reagent-grade from Acros Organics (USA). Rhodamine B (Rh.B, C28H31ClN2O3) was purchased from Samchun Pure Chemical Co., Ltd. (Korea). All chemicals were used without further purification, and all experiments were carried out using distilled water.
Synthesis of CdSe
For the synthesis of CdSe, sodium selenosulfite (Na2SeSO3) solution and Cd(NH3)42+ solution were first prepared. Na2SO3 (4 g) and selenium metal powder (0.2 g) were dissolved in 20 of mL distilled water and refluxed for 1 h to form Na2SeSO3 solution. Meanwhile, Cd(CH3COO)2 (0.675 g) was dissolved in 7 mL of distilled water. NH4OH (2 mL) was added, and the mixture was stirred until it dissolved completely to form Cd(NH3)42+ solution. Finally, the Cd(NH3)42+ and Na2SeSO3 solutions were mixed together, and the mixture was stirred and refluxed for at least 5 h. After the mixture had been brought down to room temperature, the mixture was filtered through a Whatman filter paper. The solids obtained were collected and washed five times with distilled water. After being dried in vacuum at 353 K for 8 h, the CdSe compound was obtained.
Synthesis of CdSe-C60 composite
For the preparation of the CdSe-C60 composite, C60 had to be functionalized by MCPBA at first. MCPBA (ca. 1 g) was suspended in 50 mL of benzene, followed by the addition of fullerene (ca. 30 mg). The mixture was heated under reflux in air and stirred for 6 h. The solvent was then dried at the boiling point of benzene (353.13 K). After completion, the dark-brown precipitates were washed with ethyl alcohol and dried at 323 K, resulting in the formation of oxidized fullerene.
The functionalized C60 with the Cd(NH3)42+ and Na2SeSO3 solutions prepared as previously described were mixed together, and the mixture was stirred and refluxed for at least 5 h. After the mixture had been brought down to room temperature, the mixture was filtered through a Whatman filter paper. The solids obtained were collected and washed five times with distilled water. After being dried in a vacuum at 353 K for 8 h, a CdSe-C60 composite with chemical band was obtained. Figure 1 shows the schematic presentation of the functionalization of C60 and the coupling of CdSe nanoparticles with C60. Figure 1 shows the schematic presentation of the functionalization of MWCNTs and the coupling of CdSe nanoparticles with MWCNTs.
Figure 1. Schematic presentation of the functionalization of fullerenes and the coupling of CdSe nanoparticles with fullerenes.
Synthesis of CdSe-C60/TiO2 composites
CdSe-C60 was prepared using pristine concentrations of TNB for the preparation of CdSe-C60/TiO2 composites. CdSe-C60 powder was mixed with 3 mL TNB. The solutions were homogenized under reflux at 343 K for 5 h while being stirred in a vial. After stirring, the solution transformed to CdSe-C60/TiO2 gels and was heat-treated at 873 K to produce the CdSe-C60/TiO2 composites.
X-ray diffraction (XRD; Shimadzu XD-D1, Uki, Kumamoto, Japan) was used to identify the crystallinity of the composite with monochromatic high-intensity Cu Ka radiation (l = 1.5406 Å). Scanning electron microscopy (SEM; JSM-5600, JEOL Ltd., Tokyo, Japan) was used to observe the surface state and structure of the prepared composite using an electron microscope. Transmission electron microscopy (TEM; JEM-2010, JEOL Ltd.) was used to determine the state and particle size of the prepared composite. TEM at an acceleration voltage of 200 kV was used to investigate the number and the stacking state of graphene layers on the various samples. TEM specimens were prepared by placing a few drops of sample solution on a carbon grid. The elemental mapping over the desired region of the prepared composite was determined by an energy dispersive X-ray spectroscopy (EDX) analyzer attached to the SEM. UV-visible (vis) diffuse reflectance spectra were obtained using a UV–vis spectrophotometer (Neosys-2000, Scinco Co. Ltd., Seoul, Korea) using BaSO4 as a reference at room temperature and were converted from reflection to absorbance spectra by the Kubelka-Munk method.
Photocatalytic degradation of dyes
Photocatalytic activity was evaluated by dye degradation in aqueous media under visible-light irradiation. For visible-light irradiation, the reaction beaker was located axially and held in a visible lamp box (8 W, halogen lamp, KLD-08 L/P/N, Korea). The luminous efficacy of the lamp was 80 lm/W, and the wavelength was 400 to 790 nm. The lamp was located at a distance of 100 mm from the aqueous solution in a dark box. The initial concentration of the dyes was set at 1 × 10−5 mol/L in all experiments. The amount of photocatalytic composite used was 0.05 g/50-mL solution. The reactor was placed for 2 h in the dark box to make the photocatalytic composite particles adsorb as many dye molecules as possible. After the adsorption phase, visible-light irradiation was restarted to make the degradation reaction proceed. To perform dye degradation, a glass reactor (diameter = 4 cm, height = 6 cm) was used, and the reactor was placed on the magnetic churn dasher. The suspension was then irradiated with visible light for a set irradiation time. Visible-light irradiation of the reactor was performed for 120 min. Samples were withdrawn regularly from the reactor, and dispersed powders were removed in a centrifuge. The clean transparent solution was analyzed by a UV–vis spectrophotometer (Optizen POP, Mecasys Co., Ltd., Daejeon, Korea). The dye concentration in the solution was determined as a function of the irradiation time.
Results and discussion
The result is agreement with XRD results for titanium and CdSe. After the examinations of wounds conducted by the coated implements with SEM/EDX, special particles were found; they are kinds of elements such as Cd, Se, Ti, O and C. Table 1 lists the numerical results of EDX quantitative microanalysis of the samples. Figure 2 shows that strong Kα and Kβ peaks from the Ti element appear at 4.51 and 4.92 keV, respectively, whereas a moderate Kα peak for O was observed at 0.52 keV . There were some small impurities, which were attributed to the use of fullerene without purification.
Table 1. EDX elemental microanalysis and BET surface area values
Figure 2. EDX elemental microanalysis of CdSe (a), CdSe-TiO2 (b), and CdSe-C60/TiO2 (c), they are kinds of elements such as Cd, Se, Ti, O and C.
Figure 3 shows the characterized results of the microsurface structures and morphology of the CdSe, CdSe-TiO2, and C60 modified CdSe-TiO2 compounds. As shown in Figure 3, C60 and CdSe are coated uniformly on the TiO2 surface, which leads to an increase in nanoparticle size. Zhang et al. reported that a good dispersion of small particles could provide more reactive sites for the reactants than aggregated particles . The surface roughness appears to be more with little grain aggregation. Figure 3a,b,c is CdSe, CdSe-TiO2, and CdSe-C60/TiO2, respectively. The aggregation phenomenon becomes increasingly serious, and the CdSe addition can make the aggregation worse. Figure 3c shows spherical C60 particles.
Figure 3. SEM images of CdSe (a), CdSe-TiO2 (b), and CdSe-C60/TiO2 (c), different samples with different magnification.
Table 1 lists Brunauer-Emmett-Teller (BET) surface areas of the raw CdSe, CdSe-TiO2, and CdSe-C60/TiO2 photocatalysts. The BET value decreased from 85.00 m2/g of pure fullerene to 47.27 m2/g of CdSe-C60/TiO2. The TiO2 and CdSe particles were introduced into the pores of fullerene, and the value of CdS-C60/TiO2 decreased . Added C60 can increase the surface area because C60 has a relatively larger surface area. The BET values of CdSe and CdSe-TiO2 compounds were 26.71 and 30.47 m2/g, respectively. The BET surface area of the CdS-TiO2 photocatalyst was increased by 55.13 % when the CdSe-TiO2 particles were modified by C60. The pore size and pore volume increased significantly when the particles were modified by C60 because C60 particles have larger surface area and pores.
Figure 4 shows the XRD pattern of CdSe, CdSe-TiO2, and C60-modified CdSe-TiO2 particles. It can be seen that the TiO2 modificator is of the anatase structure. It can also be seen from Figure 4 that the crystallization of the annealed TiO2 is worse than that of the pure TiO2 implanted. XRD analysis used to determine the phase purity of the samples. Figure 4 shows the XRD patterns of the component results of CdSe and CdSe-TiO2 photocatalysts. Figure 4 shows all of the peaks around 2θ of 25.4°, 42°, and 49.6°, which could be indexed to the characteristic peaks (111), (220), and (311) plane reflections of cubic crystal structure CdSe with a lattice constant of 6.05 Å (JCPDS 65–2891) [21,22]. Moreover, with the CdSe-TiO2 photocatalyst, some peaks were also found at 37.9°, 47.8°, 55°, and 62.7°, which could be indexed to the characteristic peaks (004), (200), (201), and (204) of anatase TiO2 (JCPDS 21–1272) [23,24]. No peaks for impurities were detected.
Figure 4. XRD patterns of CdSe, CdSe-TiO2, and CdSe-C60/TiO2.
Figure 5 shows TEM images of CdSe-C60/TiO2. The representative TEM images in Figure 5 show that the prepared powders are uniform with some aggregations between particles. The mean diameter of C60 was estimated to be approximately 20 to 30 nm. From Figure 5, the image of CdSe-C60/TiO2 compounds showed that all particles had agglomerated. This suggests that the presence of CdSe and C60 can efficiently enhance the agglomeration of TiO2 and impede the dispersion of nanoparticles.
Figure 5. TEM image of the CdSe-C60/TiO2 compounds.
UV–vis reflectance analysis was carried out on various systems of interest, and the measurements were then converted to absorbance spectra using Kubelka-Munk method. Figure 6 shows the UV–vis diffuse reflectance spectra of the CdSe, CdSe-TiO2, TiO2, and CdSe-C60/TiO2. As expected, the spectrum obtained from the bare TiO2 shows that TiO2 absorbs mainly the UV light with absorption wavelength below 400 nm. After the introduction of CdSe, the absorption edge is shifted toward the visible region. The CdSe exhibits the fundamental absorption edge at about 812 nm. For CdSe-TiO2, the absorbance spectrum has two absorbance onsets at approximately 738 nm and 400 nm, corresponding to the presence of CdSe and TiO2 particles, respectively. It is interesting to note that the onset for TiO2 absorption was almost unchanged (at a wavelength of about 400 nm) while the CdSe absorbance onset at 812 nm was a blueshift to the wavelength of 738 nm. This indicated an increase in the bandgap of CdSe due to the introduced TiO2. CdSe-C60/TiO2 exhibits the good adsorption effect at visible region because of the synergistic reaction of CdSe, C60, and TiO2.
Figure 6. UV–vis diffuse reflectance spectra of CdSe, CdSe-TiO2, TiO2, and CdSe-C60/TiO2.
The diffuse reflectance spectra of the CdSe, CdSe-TiO2, TiO2, and CdSe-C60/TiO2 were transformed by performing the Kubelka-Munk transformation of the measured reflectance according to the following equation:
where K is the reflectance transformed according to the Kubelka-Munk function, R is the reflectance (%), and F(R) is the so-called remission or Kubelka-Munk function .
It is well known that the bandgap Eg and the absorption coefficient α are related as in the following equation:
where α, v, Eg, and A are the absorption coefficient, light frequency, bandgap, and a constant, respectively. If the compound scatters in a perfectly diffuse manner, K becomes equal to 2α. In this case, we can use the following expression:
Therefore, the bandgap energy (Eg) of the resulting samples can be estimated from a plot of [F(R)hν]2 versus photon energy (hν). The [F(R)hν]2 versus hν graph of CdSe, CdSe-TiO2, TiO2, and CdSe-C60/TiO2 are presented in Figure 7. The intercept of the tangent to the x-axis would give a good approximation of the bandgap energy of the samples. The bandgap of CdSe is evaluated to be 1.81 eV, which is fairly close to the literature value of 1.74 eV [26,27]. It is also found that the bandgap of CdSe-TiO2 is 1.95 eV, which is greater than the standard bandgap (1.78 eV for CdSe), showing a blueshift of 0.14 eV. The bandgap of CdSe-C60/TiO2 is about 1.77 eV, showing a blueshift of 0.05 eV.
Figure 7. Variation of (αhν)2 versus photon energy (hν) for CdSe, CdSe-TiO2, TiO2, and CdSe-C60/TiO2.
Figure 8 shows the time series of dye degradation using CdSe, CdSe-TiO2, and CdSe-C60/TiO2 under visible-light irradiation. The spectra for the dye solution after visible-light irradiation show the relative degradation yields at different irradiation times. The decrease in dye concentration continued with an oppositely gentle slope, which was due to visible-light irradiation. The concentration of dyes was 1.0 × 10−5 mol/L, and the absorbance for dye decreased with the visible-light irradiation time. Moreover, the dye solution increasingly lost its color, and the dye concentration decreased. Two steps are involved in the photocatalytic decomposition of dyes: the adsorption of dye molecules and degradation. After adsorption in the dark for 30 min, the samples reached adsorption-desorption equilibrium. In the adsorptive step, CdSe, CdSe-TiO2, and CdSe-C60/TiO2 composites showed different adsorptive effects with CdSe-C60/TiO2 having the best adsorptive effect. The adsorptive effect of pure CdSe was the lowest. The adsorptive effect of CdSe-C60/TiO2 was better than that of CdSe-TiO2 because the added C60 can enhance the BET surface area which can increase the adsorption effect. CdSe-C60/TiO2 has the largest BET surface area, which can enhance the adsorptive effect. In the degradation step, the CdSe, CdSe-TiO2, and CdSe-C60/TiO2 composites showed a good degradation effect, as shown in the UV–vis absorption spectra. The CdSe-C60/TiO2 composites showed good adsorption and degradation effects. A comparison of the decoloration effect of the catalysts showed that the degradation effect can be increased by an increase in the adsorption capacity.
Figure 8. UV–vis spectra of the Rh.B concentration against CdSe, CdSe-TiO2, and CdSe-C60/TiO2 composites.
The enhanced activity is probably attributed to the improved optical absorption and the heterostructure which favors the separation of photo-introduced electron–hole pairs in CdSe-TiO2 photocatalyst . Figure 9a shows the scheme of excitation and charge transfer process between CdSe and TiO2 under visible-light irradiation. Under irradiation by UV or visible lamp, both CdSe and TiO2 can be excited; the generated electrons in CdSe and holes in TiO2 are then immigrated to the conduction band (CB) of TiO2 and the valence band (VB) of CdSe, respectively. This transfer process is thermodynamically favorable due to the bandgap (both the CB and VB) of CdSe that lie at the upper position than that of TiO2. The lifetime of the excited electrons (e−) and holes (h+) is prolonged in the transfer process, inducing higher quantum efficiency. Meanwhile, the generated electrons probably react with dissolved oxygen molecules and produce oxygen peroxide radical O2·−, the positively charged hole (h+) may react with the OH− derived from H2O to form the hydroxyl radical OH·. The Rh.B molecule then can be photocatalytically degraded by the oxygen peroxide radical O2·− and hydroxyl radical OH · [29,30].
Figure 9. Schematic diagram of the separation of generated electrons and holes on the interface of compounds. (a) CdSe-TiO2 and (b) CdSe-C60/TiO2 compounds under visible-light irradiation.
CdSe-C60/TiO2 composites have the best discoloration effect, which is due to the following reasons: (1) C60 is an energy sensitizer that improves the quantum efficiency and increases charge transfer, (2) C60 can enhance the adsorption effect during the discoloration processes, and (3) CdSe can provide excited electrons for TiO2 and engender hydroxyl radicals (·OH) and superoxide radical anions (·O2−) with the presence of H2O and oxygen. Figure 9b shows a schematic diagram of the separation of photogenerated electrons and holes on the CdSe-C60/TiO2 interface [31,32].
Photocatalysts were synthesized successfully using a simple sol–gel method. From the XRD patterns, the cubic crystal structure of CdSe was observed. TEM showed that the surface of TiO2 has been coated uniformly with C60 and CdSe layers with a C60 particle size of approximately 20 nm. The diffuse reflectance spectra indicated that the composites showed strong photoabsorption in the UV–vis range, and the presence of C60 enhanced the level of photoabsorption in the visible range. The nitrogen adsorption isotherms show that the added C60 can enhance the adsorption effect significantly. The photocatalytic activity of the CdSe-C60/TiO2 composite was examined by the degradation of MB in aqueous solutions under visible-light irradiation. The CdSe-C60/TiO2 composites showed good adsorption and degradation effects. Overall, within the limits of the degradation ability, the degradation effect can be enhanced by an increase in adsorption capacity. CdSe-C60/TiO2 composites also have good photocatalytic activity in cycle experiment which emphasizes the excellent stability of C60 and photochemical stability of C60-modified photocatalyst.
The authors declare that they have no competing interests.
ZDM wrote the paper and prepared the samples. LZ, SY, QS, and KU analyzed the sample. KYC performed the TEM. WCO coordinated the study as the corresponding author. All authors read and approved the final manuscript.
Thanks very much for all of the Authors, and the professor Oh. They did the job of analyzed and prepared work, and contribution of materials.
Appl. Catal. B: Environ 2003, 46:287-292. Publisher Full Text
Jing LQ, Li SD, Song S, Xue LP, Fu HG: Investigation on the electron transfer between anatase and rutile in nano-sized TiO2 by means of surface photovoltage technique and its effects on the photocatalytic activity.
Sol. Energy Mater. Sol. Cells 2008, 92:1030-1036. Publisher Full Text
Sol. Energy Mater. Sol. Cells 2008, 92:402-409. Publisher Full Text
J. Molecular Catal. A: Chemical 2006, 247:268-274. Publisher Full Text
J Mater Chem 2011, 21:7596. Publisher Full Text
Korean J. Mater. Res 2010, 20:228-234. Publisher Full Text
Ultras Sonochem 2011, 18:757. Publisher Full Text
Nature 1991, 350:320-322. Publisher Full Text
Carbon 2004, 42:1137-1141. Publisher Full Text
Carbon 2005, 43:1700-1708. Publisher Full Text
J. Photochem. Photobiol. A: Chem 2009, 203:145-150. Publisher Full Text
Chem. Phys. Lett 1997, 270:145-151. Publisher Full Text
Chem Rev 1993, 93:267-300. Publisher Full Text
Appl. Catal. B: Environ 2006, 68:1-11. Publisher Full Text
J Am Chem Soc 1999, 121:10047-10052. Publisher Full Text
Int J Hydrogen Energy 2013, 38:1267-1277. Publisher Full Text
Sol Energy Mater Sol Cells 2004, 81:113-118. Publisher Full Text
Mater Lett 2000, 46:81-85. Publisher Full Text
Thin Solid. Film 1995, 257:166-184. Publisher Full Text