Open Access Highly Accessed Nano Express

A self-powered UV photodetector based on TiO2 nanorod arrays

Yanru Xie1, Lin Wei2, Guodong Wei1, Qinghao Li1, Dong Wang1, Yanxue Chen1*, Shishen Yan1, Guolei Liu1, Liangmo Mei1 and Jun Jiao34

Author Affiliations

1 School of Physics and State Key Laboratory of Crystal Materials, Shandong University, Jinan 250100, People's Republic of China

2 School of Information Science and Engineering, Shandong University, Jinan, 250100, People's Republic of China

3 Department of Mechanical and Materials Engineering, Portland State University, P.O. Box 751, Portland, OR, 97207-0751, USA

4 Department of Physics, Portland State University, P.O. Box 751, Portland, OR, 97207-0751, USA

For all author emails, please log on.

Nanoscale Research Letters 2013, 8:188  doi:10.1186/1556-276X-8-188


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/188


Received:11 March 2013
Accepted:7 April 2013
Published:23 April 2013

© 2013 Xie et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Large-area vertical rutile TiO2 nanorod arrays (TNAs) were grown on F/SnO2 conductive glass using a hydrothermal method at low temperature. A self-powered ultraviolet (UV) photodetector based on TiO2 nanorod/water solid–liquid heterojunction is designed and fabricated. These nanorods offer an enlarged TiO2/water contact area and a direct pathway for electron transport simultaneously. By connecting this UV photodetector to an ammeter, the intensity of UV light can be quantified using the output short-circuit photocurrent without a power source. A photosensitivity of 0.025 A/W and a quick response time were observed. At the same time, a high photosensitivity in a wide range of wavelength was also demonstrated. This TNA/water UV detector can be a particularly suitable candidate for practical applications for its high photosensitivity, fast response, excellent spectral selectivity, uncomplicated low-cost fabrication process, and environment-friendly feature.

Keywords:
TiO2; Nanorod; Ultraviolet photodetector; Solid–liquid heterojunction

Background

Ultraviolet (UV) photodetector has been a popular research issue for its potential applications in a wide range of fields, such as remote control, chemical analysis, water purification, flame detection, early missile plume detection, and secure space-to-space communications [1]. To avoid the use of filters and achieve visible-blind operation, wide bandgap semiconductors, such as GaN, SiC, ZnO, and TiO2[2-8], have been studied during the last decade for wide-spreading usage in photodetection, especially in the ultraviolet region. Among conventional available UV photodetectors, quite many kinds of structures have been fabricated, which in most cases are based on epitaxial growth process and various solid-state junction structures. Typical examples are photodetectors based on p-n junction, p-i-n photodiodes, Schottky barrier (SB), metal–semiconductor-metal, and metal-insulator-semiconductor structures [9-15]. These photodetectors typically require an external bias as the driving force to prevent the recombination of photogenerated electron–hole pairs. For large-area two-dimensional arrays that contain huge amounts of small UV sensors, energy supply will be one of the main challenges for such sensor systems.

Recently, self-powered nanodevices and nanosystems have attracted lots of attention due to their various advantages. Xu et al. fabricated a nanowire pH sensor and a nanowire UV sensor powered by a piezoelectric nanogenerator equipped with a capacitor, demonstrating a self-powered system composed entirely of nanowires [16]. Yang et al. reported a self-powered ultraviolet photodetector based on a single Sb-doped ZnO nanobelt bridging an ohmic contact and a Schottky contact, in which high photoresponse sensitivity and short response time were observed [17]. Bai et al. reported a ZnO nanowire array ultraviolet photodetector with self-powered properties, in which a high sensitivity of 475 without external bias is found [18]. Although n-type semiconducting ZnO is a significant material for optoelectronic applications, it is unstable under both acidic and alkaline conditions. Also, the photoresponse of ZnO-based UV detector is sensitive to the surrounding atmosphere and can be easily affected by oxygen as well as water molecules. On the other hand, TiO2 nanostructures have also emerged as very promising materials for optoelectronic devices due to their excellent physical and chemical properties, such as high melting point, chemical inertness, physical stability, direct bandgap (rutile 3.0 eV), high photoconversion efficiency, and photostability. Self-powered UV photodetectors based on a photochemical cell have been fabricated using a liquid I-/I3- redox couple electrolyte and a nanocrystalline TiO2 film [19] or a multilayer TiO2 nanorod-assembled cloth/nanorod array-based electrode [20]. Impressive performances were observed in these UV detectors. However, liquid I-/I3- redox couple electrolyte is not ideal for long-term operation: it is highly corrosive, volatile, and photoreactive, interacting with common metallic components and sealing materials. From this point, water-based electrolytes may be the safest, most stable, and most environment-friendly electrolyte. Lee et al. reported a UV detector based on TiO2/water solid–liquid heterojunction [21]. This self-powered UV photodetector behaves similar to a Schottky diode and works in photovoltaic mode. Moreover, TiO2/water solid–liquid heterojunction UV detector exhibits high photosensitivity, excellent spectral selectivity, linear variations in photocurrent, and fast response. Cao et al. reported the photocurrent response of TiO2 nanorod arrays under UV illumination using a 0.5 M Na2SO4 aqueous electrolyte [22], in which TiO2 nanostructures can harvest more incident light photons compared to a flat thin-film active layer because of the markedly enlarged TiO2/electrolyte contact area. However, they did not report its photosensitivity and spectral response. All of these reported results indicate that self-powered UV detectors based on TiO2 nanostructures show great potential as excellent candidates for commercial UV photodetectors. Further advancements for TiO2-based self-powered UV detectors demand a deeper understanding of the main parameters determining the photoelectric behavior, which also requires additional research and insight into the electrical transporting process in these nanostructured devices.

In this paper, self-powered UV detectors were fabricated based on single-crystalline rutile TiO2 nanorod arrays (TNAs), which were grown directly on fluorine-doped tin oxide (FTO) glass by a low-temperature hydrothermal method. This UV photodetector establishes a built-in potential due to its Schottky barrier-like behavior. The built-in potential separates the electron–hole pairs generated by UV light and makes the photodetector generate photocurrent without any external bias. A considerable photocurrent response was observed under UV light illumination. Also, this self-powered photodetector demonstrates fast photoresponse speed, high photosensitivity, excellent spectral selectivity, uncomplicated low-cost fabrication process, and environment-friendly feature.

Methods

Growth of TiO2 nanorod arrays by hydrothermal process

The single-crystalline rutile TNAs used for this study were grown vertically on FTO glass using the following hydrothermal methods: a diluted hydrochloric solution was prepared by mixing 50 mL of deionized water with 40 mL of concentrated hydrochloric acid and was stirred at ambient temperature for 5 min, and then 400 μL of titanium tetrachloride was added to the mixture. After being stirred for another 10 min, the mixture was injected into a stainless steel autoclave with a Teflon container cartridge. The FTO substrates were ultrasonically cleaned and were placed at an angle against the Teflon container wall with the conducting side facing down. Hydrothermal synthesis was conducted at 180°C for 2 h. After synthesis, the autoclave was cooled to room temperature under flowing water, and the FTO substrates were taken out, rinsed thoroughly with deionized water, and annealed at 500°C for 1 h to improve the crystalline structure.

Assemble of TNA/water solid–liquid heterojunction

The schematic structure of the TNA/water solid–liquid heterojunction UV photodetector is shown in Figure 1. For device fabrication, the TNA layer grown on FTO glass was used as the active photoanode. Pt counter electrodes were prepared by depositing a 20-nm Pt film on FTO glass using magnetron sputtering. A 60-μm-thick sealing material (SX-1170-60, Solaronix SA, Aubonne, Switzerland) was pasted onto the Pt counter electrodes. Afterward, the Pt counter electrode and a nanostructure TNA photoanode were sandwiched and sealed with the conductive sides facing inward. Finally, some high-quality deionized water was injected into the space between TNA/FTO glass and Pt/FTO glass electrodes as an electrolyte. A solid–liquid heterojunction UV photodetector was then fabricated, and the active area of the TNA/water device for UV light detection was about 0.126 cm2.

thumbnailFigure 1. Schematic device structure of the TNA/water heterojunction ultraviolet photodetector.

Characterization of the TNA samples and the UV photodetector

The crystal structure of the TNA samples were examined by X-ray diffraction (XRD; XD-3, PG Instruments Ltd., Beijing, China) with Cu Kα radiation (λ = 0.154 nm) at a scan rate of 2°/min. The surface morphology was characterized using a scanning electron microscope (SEM; Hitachi S-4800, Hitachi, Ltd., Chiyoda, Tokyo, Japan). The optical transmittance was measured using a UV-visible dual-beam spectrophotometer (TU-1900, PG Instruments, Ltd.). The photoresponse characteristics of the self-powered UV detector in the dark and under illumination were recorded with a programmable voltage–current source (2400, Keithley Instruments Inc., Cleveland, OH, USA). A 500-W xenon lamp (7ILX500, 7Star Optical Instruments Co., Beijing, China) equipped with a monochromator (7ISW30, 7Star Optical Instruments Co.) was used as light source for spectral response characterization. For the photoresponse switching behavior measurement, a UV LED (NCSU033B(T), Nichia Co., Japan) with a wavelength of 365 nm was used as light source, and the photocurrent was obtained by an electrochemical workstation (RST5200, Zhengzhou Shirusi Instrument Technology Co. Ltd, Zhengzhou, China).

Results and discussion

The well-aligned TNAs with pure rutile phase are verified by the XRD pattern in Figure 2a. The θ-2θ scan pattern shows that the TiO2 nanorods grown on FTO-coated glass substrates have a tetragonal rutile structure (JCPDS 02–0494). The SnO2 peaks are due to the pattern of FTO glass substrate. The reason that the hydrothermal growth method delivers rutile phase instead of other phases, such as anatase and brookite, could be attributed to the small lattice mismatch between FTO and rutile. Both rutile and SnO2 have near-identical lattice parameters with a = 4.594, c = 2.958 Å and a = 4.737, c = 3.185 Å for TiO2 and SnO2, respectively, making the epitaxial growth of rutile TiO2 on FTO film possible. On the other hand, anatase and brookite have lattice parameters of a = 3.784, c = 9.514 Å and a = 5.455, c = 5.142 Å, respectively. The production of these phases is unfavorable due to a very high activation energy barrier which cannot be overcome at the low temperatures used in this hydrothermal reaction. Figure 2b,c shows the micrographs of an as-grown TiO2 nanorod array taken by a field emission scanning electron microscope at tilted and top views. The images at different magnifications and at different locations reveal that the entire surface of the FTO-coated glass substrate is uniformly covered with ordered TiO2 nanorods. Further analysis indicates that the nanorods are typically 100 to 150 nm in diameter and are tetragonal in shape with square top facets consisting of many small grids. The density of nanorods is typically 20 nanorods/μm2. No significant changes in nanorod array morphology were observed after annealing at 500°C.

thumbnailFigure 2. XRD pattern and SEM images of TiO2 nanorod arrays. (a) X-ray diffraction pattern of the TiO2 nanorod array grown on FTO glass. (b) SEM image (40° tilted) of the TiO2 nanorod array grown on FTO glass by hydrothermal method. (c) A high-magnification top-view SEM image of TiO2 nanorod array.

The optical property of the TNA was investigated using UV-visible transmittance spectrum. Figure 3 shows the optical transmittance spectra of the TNA sample and the FTO glass substrate. An obvious sharp absorption edge can be observed at 420 nm, which can be attributed to the energy bandgap of rutile TiO2 nanorods. As the size of the TiO2 nanorod is well above the TiO2 Bohr exciton diameter, no obvious blueshift caused by quantum confinement is observed. The low transmittance (20% to 30%) in the wavelength ranges of 400 to 550 nm is caused by the strong light scattering from TNAs. An absorption edge for the FTO glass substrate is about 310 nm, as shown in the inset of Figure 3. From these two transmittance spectra, we can conclude that only light with the wavelength between 310 and 420 nm can reach the TNAs and contribute to the UV photoresponsivity, which is confirmed in the following spectral response characterization.

thumbnailFigure 3. The UV-visible absorption spectra of TiO2 nanorod array and an FTO glass substrate (inset).

Typical current–voltage (I-V) characteristics of the UV detector are shown in Figure 4. An SB-like behavior of the UV detector is demonstrated from the dark I-V curve, which shows a forward turn-on voltage of about 0.4 V and a rectification ratio of about 44 at ± 0.6 V. Under the illumination of 1.25 mW/cm2 of UV light (λ = 365 nm), the UV detector shows an excellent photovoltaic performance, yielding a short-circuit current of 4.67 μA and an open-circuit voltage of 0.408 V. This inherent built-in potential arises from the SB-like TiO2-water interface, acts as a driving force to separate the photogenerated electron–hole pairs, and produces the photocurrent. Therefore, this device can operate not only at photodiode mode but also at photovoltaic mode without any external bias. The real-time photocurrent response of the self-powered UV detector was measured at 0-V bias under a 365-nm UV LED on/off switching irritation with an on/off internal of 5 s. Five repeat cycles under an on/off light intensity of 1.25 mW/cm2 are displayed in Figure 5a, in which the photocurrent was observed to be consistent and repeatable. A fast photoresponse can be clearly seen. From enlarged rising and decaying edges of the photocurrent response shown in Figure 5b,c, the rise time and the decay time of the UV detector are approximately 0.15 and 0.05 s, indicating a rapid photoresponse characteristic. On the contrary, TiO2 one-dimensional UV photodetectors based on photoconductivity exhibit a much longer recovery time due to the presence of a carrier depletion layer at the nanomaterial surface caused by surface trap states [23]. The photosensitivity of the TNA self-powered UV detector to 365 nm light was also tested using a range of intensities from 12.5 μW/cm2 to 1.25 mW/cm2. A steadily increasing photocurrent response was observed in relation to increasing incident light intensity (not included here). This UV detector exhibits an excellent capacity to detect very weak optical signals. Even under a weak incident light intensity of 12.5 μW/cm2, the magnitude of photosensitivity has already approached two orders.

thumbnailFigure 4. Current–voltage (I-V) characteristics of the UV detector. Typical I-V curves for the self-powered TNA/water UV detector measured at applied bias from -0.6 to 0.6 V under dark (red line) and 365-nm UV light illumination (black line).

thumbnailFigure 5. Time response of the TNA/water UV detector. (a) Photocurrent response under on/off radiation of 1.25 mW/cm2 of UV light illumination. (b) Enlarged rising and (c) decaying edges of the photocurrent response.

The wavelength selective ability of the TNA/water UV detector was measured in the range of 260 to 550 nm at 0-V bias, and the result is shown in Figure 6. It is clearly seen that excellent UV light detection selectivity in a spectral range between 310 and 420 nm is observed, which indicates that the device can be used as photodetector for UV-A range (320 ~ 400 nm) application. The maximum responsivity of the spectrum is about 0.025 A/W, located at the wavelength of 350 nm. The spectral response edge of 310 nm is limited by the transmittance of the FTO glass substrate. The edge of 420 nm is attributed to the absorption edge of the TNA layer.

thumbnailFigure 6. Spectral responsivity characteristic of TNA/water UV photodetector from 260 to 550 nm under 0-V bias.

The working principle of the device is discussed simply in the following. When UV light (310 ~ 420 nm) shines on the TNA/water UV detector, the incident photons that pass through the FTO glass into the TNAs and electrons in TiO2 are excited from the valence band to the conduction band and then generate electron–hole pairs in the TNAs. The built-in potential produced by solid–liquid heterojunction separates the UV light-generated electron–hole pairs. The separated holes move from the valence band of the TNAs into the interface of TNA/water, subsequently seizing the electrons from the water OH- anions (h+ + OH- → HO·). Considering the quite large TNA/water surface area, the small diameter of the nanorods, and the built-in interface potential, a fast removal of holes from the surface can be expected. On other hand, the separated electrons transport into the TNA conduction band and are collected easily by the FTO contact as the work function of FTO matches the conduction band of TiO2. These electrons move into the external circuit and then come back to the Pt layer of the detector, thereupon returning the electrons to HO· radicals (e- + HO· → OH-) at the interface of water/Pt. In this way, the built-in potential makes the UV detector generate photocurrent without any external bias. Even though zero bias is applied, the UV detector exhibits high photosensitivity [21,24].

Conclusions

In conclusion, a photoelectrochemical cell-structured self-powered UV photodetector was developed using water as the electrolyte and a rutile TiO2 nanorod array as the active photoelectrode. This device exhibits a prominent performance for UV light detection. Under ambient environment, the photocurrent responses rapidly with UV light on/off switching irradiation. Also, this self-powered TNA/water UV detector demonstrates high photosensitivity and excellent spectral selectivity. All of these results indicate that this novel UV detector can be a promising candidate as a low-cost UV photodetector for commercially integrated photoelectronic applications.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

The work presented here was performed through the collaboration of all authors. YX carried out the measurements of the TNA/water UV detector and drafted the manuscript. LW conducted the transmittance spectra measurements. GW grew the TNA photoanode. QL carried out the XRD and the SEM characterizations. DW deposited the Pt film and helped fabricate the device. YC supervised the work and finalized the manuscript. SY and GL analyzed the results and participated in the revision of the manuscript. LM and JJ proofread the manuscript and corrected the English. All authors read and approved the final manuscript.

Acknowledgments

This work was supported by the National Key Basic Research Program of China (2013CB922303, 2010CB833103), the National Natural Science Foundation of China (60976073, 11274201, 51231007), the 111 Project (B13029), and the Foundation for Outstanding Young Scientist in Shandong Province (BS2010CL036).

References

  1. Munoz E, Monroy E, Pau JL, Calle F, Omnes F, Gibart P: III Nitrides and UV detection.

    J Phys-Condens Mater 2001, 13:7115. Publisher Full Text OpenURL

  2. Razeghi M, Rogalski A: Semiconductor ultraviolet detectors.

    J Appl Phys 1996, 79:7433. Publisher Full Text OpenURL

  3. Li DB, Sun XJ, Song H, Li ZM, Jiang H, Chen YR, Miao GQ, Shen B: Effect of asymmetric Schottky barrier on GaN-based metal–semiconductor-metal ultraviolet detector.

    Appl Phys Lett 2011, 99:261102. Publisher Full Text OpenURL

  4. Fu XW, Liao ZM, Zhou YB, Wu HC, Bie YQ, Xu J, Yu DP: Graphene/ZnO nanowire/graphene vertical structure based fast-response ultraviolet photodetector.

    Appl Phys Lett 2012, 100:223114. Publisher Full Text OpenURL

  5. Hassan JJ, Mahdi MA, Kasim SJ, Ahmed NM, Hassan HA, Hassan Z: High sensitivity and fast response and recovery times in a ZnO nanorod array/p-Si self-powered ultraviolet detector.

    Appl Phys Lett 2012, 101:261108. Publisher Full Text OpenURL

  6. Sciuto A, Roccaforte F, Raineri V: Electro-optical response of ion-irradiated 4H-SiC Schottky ultraviolet photodetectors.

    Appl Phys Lett 2008, 92:093505. Publisher Full Text OpenURL

  7. Zhang F, Yang WF, Huang HL, Chen XP, Wu ZY, Zhu HL, Qi HJ, Yao JK, Fan ZX, Shao JD: High-performance 4H-SiC based metal–semiconductor-metal ultraviolet photodetectors with Al2O3/SiO2 films.

    Appl Phys Lett 2008, 92:251102. Publisher Full Text OpenURL

  8. Kong XZ, Liu CX, Dong W, Zhang XD, Tao C, Shen L, Zhou JR, Fei YF, Ruan SP: Metal–semiconductor-metal TiO2 ultraviolet detectors with Ni electrodes.

    Appl Phys Lett 2009, 94:123502. Publisher Full Text OpenURL

  9. Alivov YI, Ozgur U, Dogan S, Johnstone D, Avrutin V, Onojima N, Liu C, Xie J, Fan Q, Morkoc H: Photoresponse of n-ZnO/p-SiC heterojunction diodes grown by plasma-assisted molecular-beam epitaxy.

    Appl Phys Lett 2005, 86:241108. Publisher Full Text OpenURL

  10. Chang KH, Sheu JK, Lee ML, Tu SJ, Yang CC, Kuo HS, Yang JH, Lai WC: Inverted Al0.25Ga0.75N/GaN ultraviolet p-i-n photodiodes formed on p-GaN template layer grown by metalorganic vapor phase epitaxy.

    Appl Phys Lett 2010, 97:013502. Publisher Full Text OpenURL

  11. Liang S, Sheng H, Liu Y, Huo Z, Lu Y, Shen H: ZnO Schottky ultraviolet photodetectors.

    J Cryst Growth 2001, 225:110. Publisher Full Text OpenURL

  12. Cheng G, Wu XH, Liu B, Li B, Zhang XT: ZnO nanowire Schottky barrier ultraviolet photodetector with high sensitivity and fast recovery speed.

    Appl Phys Lett 2011, 99:203105. Publisher Full Text OpenURL

  13. Endo H, Sugibuchi M, Takahashi K, Goto S, Sugimura S, Hane K, Kashiwaba Y: Schottky ultraviolet photodiode using a ZnO hydrothermally grown single crystal substrate.

    Appl Phys Lett 2007, 90:121906. Publisher Full Text OpenURL

  14. Xue HL, Kong XZ, Liu ZR, Liu CX, Zhou JR, Chen WY: TiO2 based metal–semiconductor-metal ultraviolet photodetectors.

    Appl Phys Lett 2007, 90:201118. Publisher Full Text OpenURL

  15. Chen CH, Tsai CM, Cheng CF, Yen SF, Su PY, Tsai YH, Tsai CN: GaN-based metal-insulator-semiconductor ultraviolet photodetectors with CsF current-suppressing layer.

    Jpn J Appl Phys 2012, 51:04DG15. OpenURL

  16. Xu S, Qin Y, Xu C, Wei YG, Yang RS, Wang ZL: Self-powered nanowire devices.

    Nat Nanotechnol 2010, 5:366. PubMed Abstract | Publisher Full Text OpenURL

  17. Yang Y, Guo W, Qi JJ, Zhao J, Zhang Y: Self-powered ultraviolet photodetector based on a single Sb-doped ZnO nanobelt.

    Appl Phys Lett 2010, 97:223113. Publisher Full Text OpenURL

  18. Bai ZM, Yan XQ, Chen X, Liu HS, Shen YW, Zhang Y: ZnO nanowire array ultraviolet photodetectors with self-powered properties.

    Current Applied Physics 2013, 13:165. Publisher Full Text OpenURL

  19. Li XD, Gao CT, Duan HG, Lu BG, Pan XJ, Xie EQ: Nanocrystalline TiO2 film based photoelectrochemical cell as self-powered UV-photodetector.

    Nano Energy 2012, 1:640. Publisher Full Text OpenURL

  20. Wang ZR, Ran SH, Liu B, Chen D, Shen GZ: Multilayer TiO2 nanorod cloth/nanorod array electrode for dye-sensitized solar cells and self-powered UV detectors.

    Nanoscale 2012, 4:3350. PubMed Abstract | Publisher Full Text OpenURL

  21. Lee WJ, Hon MH: An ultraviolet photo-detector based on TiO2/water solid–liquid heterojunction.

    Appl Phys Lett 2011, 99:251102. Publisher Full Text OpenURL

  22. Cao CL, Hu CG, Wang X, Wang SX, Tian YS, Zhang HL: UV sensor based on TiO2 nanorod arrays on FTO thin film.

    Sensor Actuat B-Chem 2011, 156:114-119. Publisher Full Text OpenURL

  23. Chen RS, Chen CA, Tsai HY, Wang WC, Huang YS: Ultrahigh efficient single-crystalline TiO2 nanorod photoconductors.

    Appl Phys Lett 2012, 100:123108. Publisher Full Text OpenURL

  24. Gratzel M: Photoelectrochemical cells.

    Nature 2001, 414:338. PubMed Abstract | Publisher Full Text OpenURL