Open Access Nano Express

Diameter-sensitive biocompatibility of anodic TiO2 nanotubes treated with supercritical CO2 fluid

Ming-Ying Lan12, Chia-Pei Liu3, Her-Hsiung Huang4, Jeng-Kuei Chang3 and Sheng-Wei Lee3*

Author Affiliations

1 Department of Otolaryngology, Taipei Veterans General Hospital, Taipei, 11217, Taiwan

2 Institute of Clinical Medicine, National Yang-Ming University, Taipei, 11221, Taiwan

3 Institute of Materials Science and Engineering, National Central University, No. 300, Jhongda Road, Jhong-Li, Taoyuan, 32001, Taiwan

4 Department of Dentistry, National Yang-Ming University, Taipei, 11221, Taiwan

For all author emails, please log on.

Nanoscale Research Letters 2013, 8:150  doi:10.1186/1556-276X-8-150


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/150


Received:13 February 2013
Accepted:21 March 2013
Published:2 April 2013

© 2013 Lan et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

This work reports on the diameter-sensitive biocompatibility of anodic TiO2 nanotubes with different nanotube diameters grown by a self-ordering process and subsequently treated with supercritical CO2 (ScCO2) fluid. We find that highly hydrophilic as-grown TiO2 nanotubes become hydrophobic after the ScCO2 treatment but can effectively recover their surface wettability under UV light irradiation as a result of photo-oxidation of C-H functional groups formed on the nanotube surface. It is demonstrated that human fibroblast cells show more obvious diameter-specific behavior on the ScCO2-treated TiO2 nanotubes than on the as-grown ones in the range of diameters of 15 to 100 nm. This result can be attributed to the removal of disordered Ti(OH)4 precipitates from the nanotube surface by the ScCO2 fluid, thus resulting in purer nanotube topography and stronger diameter dependence of cell activity. Furthermore, for the smallest diameter of 15 nm, ScCO2-treated TiO2 nanotubes reveal higher biocompatibility than the as-grown sample.

Background

Titanium (Ti) and its alloys have been widely used for dental and orthopedic implants because of their favorable mechanical properties, superior corrosion resistance, and good biocompatibility [1-3]. When exposed to the atmosphere, the Ti metal spontaneously forms a thin, dense, and protective oxide layer (mainly TiO2, approximately 10 nm thick) on its surface, which acts like a ceramic with superior biocompatibility. When the Ti implant is inserted into the human body, the surrounding tissues directly contact the TiO2 layer on the implant surface. Therefore, the surface characteristics of the TiO2 layer determine the biocompatibility of Ti-based implants. Earlier studies primarily investigated the influence of surface topography of implants on cell behaviors at the micrometer scale [4-6]. Recently, the interaction of nanometric scale surface topography, especially in the sub-100-nm region, with cells has been recognized as an increasingly important factor for tissue acceptance and cell survival [7-9]. Various nanotopography modifications have been proposed to enhance the cell responses to the Ti-based implants. For example, TiO2 nanowire scaffolds fabricated by hydrothermal reaction of alkali with the Ti metal, mimicking the natural extracellular matrix in structure, can promote the adhesion and proliferation of mesenchymal stem cells (MSCs) on Ti implants [10]. Chiang et al. also proposed that a TiO2 multilayer nanonetwork causes better MSC adhesion and spreading, as well as faster cell proliferation and initial differentiation [11].

In the recent years, self-organized TiO2 nanotubes fabricated by electrochemical anodization of pure Ti foils have attracted considerable interest owing to their broad applications in photocatalysis [12], dye-sensitized solar cells [13], and biomedical field [14,15]. A major advantage of anodic oxidation is the feasibility to well control the diameter and shape of the nanotubular arrays to the desired length scale, meeting the demands of a specific application by precisely controlling the anodization parameters. In a number of studies on the cell response to TiO2 nanotubes, nanosize effects have been demonstrated for a variety of cells [16-18]. Park et al. reported that vitality, proliferation, migration, and differentiation of MSCs and hematopoietic stem cells, as well as the behavior of osteoblasts and osteoclasts, are strongly influenced by the nanoscale TiO2 surface topography with a specific response to nanotube diameters between 15 and 100 nm [19]. Furthermore, even if the surface chemistry of the nanotubes is completely modified with a dense alloy coating onto the original nanotube layers, the nanosize effects still prevail [20]. In other words, the cell vitality has an extremely close relationship with the geometric factors of nanotube openings.

On the other hand, using supercritical CO2 (ScCO2) as a solvent has shown many advantages when chemically cleaning or modifying the surface of materials. The high diffusivity and low surface tension of ScCO2 enable reagents to access the interparticle regions of powders, buried interfaces, or even nanoporous structures that cannot be reached using conventional solution or gaseous treatment methods [21,22]. Recent studies have shown that ScCO2 is an effective alternative for terminal sterilization of medical devices [23]. It was also reported that the contact of ScCO2 with P25 TiO2 (70% anatase and 30% rutile), which contains both anatase and rutile phases, leads to the formation of a variety of functional groups and substantially modifies the surface chemistry [24]. Moreover, the ScCO2 drying technique has been proven to effectively reduce intertube contacts and to produce bundle-free and crack-free TiO2 nanotube films [25]. The aim of this study is to gain an understanding of the influence of ScCO2 on surface topography and chemistry of anodic TiO2 nanotubes and also to study the diameter-specific biocompatibility of these ScCO2-treated TiO2 nanotubes with human fibroblast cells. The human fibroblast cell behavior, including cell adhesion, proliferation, and survival, in response to the diameter of TiO2 nanotubes is investigated.

Methods

Preparation of ScCO2-treated TiO2 nanotubes

Self-organized TiO2 nanotubes were prepared by electrochemical anodization of Ti foils (thickness of 0.127 mm, 99.7% purity, ECHO Chemical Co. Ltd., Miaoli, Taiwan). A two-electrode electrochemical cell with Ti anode and Pt as counter electrode was used. All anodization experiments were carried out in ethylene glycol electrolytes containing 0.5 wt.% NH4F at 20°C for 90 min. All electrolytes were prepared from reagent-grade chemicals and deionized water. Anodization voltages applied were between 10 and 40 V, and resulted in nanotube diameters ranging from 15 up to 100 nm. The TiO2 nanotubes with the diameter of 100 nm annealed at 400°C for 2 h were also prepared as the reference sample. After the electrochemical process, the nanotube samples were cleaned ultrasonically with deionized water for 1 h to remove the residual by-products on the surface. Subsequently, ScCO2 fluid (99.9% purity) was utilized to treat the nanotubes at the temperature of 53°C and in the pressure of 100 bar for 2 h. For the in vitro experiments, low-intensity UV light irradiation (<2 mW/cm2) was performed on all nanotube samples using fluorescent black-light bulbs for 8 h.

Material characterization

Field emission scanning electron microscopy (FE-SEM; FEI Quanta 200 F, FEI, Hillsboro, OR, USA) was employed for the morphological characterization of the TiO2 nanotube samples. X-ray diffraction (XRD) was utilized to determine the phase of the TiO2 nanotubes. The surface wettability of materials was evaluated by measuring the contact angle between the TiO2 nanotubes and water droplets in the dark. Contact angle measurements were performed at room temperature by the extension method, using a horizontal microscope with a protractor eyepiece. In addition, in order to investigate the functional groups possibly formed during the ScCO2 process, X-ray photoelectron spectroscopy (XPS) was employed to analyze the carbon spectra (in terms of C 1s) on the nanotube surfaces.

Cell culture

MRC-5 human fibroblasts were received from the Bioresource Collection and Research Center, Taiwan. Cells were plated in a 10-cm tissue culture plate and cultured with Eagle's minimum essential medium (Gibco, Life Technologies Corporation, Grand Island, NY, USA) containing 10% fetal bovine serum, 2 mM L-glutamine, 1.5 g/L sodium bicarbonate, 0.1 mM non-essential amino acids, and 1.0 mM sodium pyruvate. Cultures were maintained at 37°C in a humidified atmosphere of 5% CO2. Cells were then seeded onto the autoclaved titanium samples placed in a 12-well culture plate (Falcon, BD Biosciences, San Jose, CA, USA) at a density of 5 × 103 cells/cm2 for 3 days for cell adhesion assay and 1 × 104 cells/cm2 for 1 week for cell proliferation assay, respectively.

Cell adhesion

For cell adhesion experiments, 3 days after cell plating, non-adherent cells were washed with phosphate-buffered saline (PBS). The adherent cells were fixed in 4% paraformaldehyde (USB Corp., Cleveland, OH, USA) for 1 h at room temperature and washed with PBS. After fixation, the cells were permeabilized with 0.1% Triton X-100 (Sigma-Aldrich Corporation, St. Louis, MO, USA) in PBS for 15 min at 4°C. Cells were then washed with PBS and incubated with rhodamine phalloidin (Life Technologies Corporation, Grand Island, NY, USA) for 15 min for actin filament stain and with diamidino-2-phenylindole (DAPI; Thermo Fisher Scientific Inc., Waltham, MA, USA) for 5 min for nuclei stain. The images of the stained fibroblasts were taken using a fluorescent microscope to examine the cell adhesion morphology and cytoskeletal arrangement. For SEM observation, cells were fixed with 2.5% glutaraldehyde solution (Merck & Co., Inc., Whitehouse Station, NJ, USA) for 1 h at room temperature. Samples were rinsed in PBS solution twice, dehydrated in a series of ethanol (40%, 50%, 60%, 70%, 80%, 90%, and 100%) and critical point dried with a critical point dryer (CPD 030, Leica Microsystems, Wetzlar, Germany).

Cell proliferation

Additional cell proliferation was quantified 1 week after cell plating at a density of 1 × 104 cells/cm2 using cell proliferation reagent WST-1 (Roche, Woerden, Netherlands) according to the manufacturer's instructions. On the 7th day, cells on the nanotubes were washed with PBS twice. The cells were incubated with a medium containing 10% WST-1 cell proliferation reagent at 37°C in a humidified atmosphere of 5% CO2 for 2 h. The solution was then retrieved from each well to a 96-well plate, and optical densities were measured using a spectrophotometer (Tecan Group Ltd., Männedorf, Switzerland) at 450 nm. All experiments were carried out in triplicate, and at least three independent experiments were performed. Data were presented as mean ± standard deviation and analyzed by analysis of variances using SPSS 12.0 software (SPSS Inc., Chicago, IL, USA). A p value of <0.05 was considered statistically significant.

Results and discussion

Figure 1a,b,c,d shows the SEM micrographs of as-anodized TiO2 nanotubes with the diameters of 10, 25, 50, and 100 nm produced by electrochemical anodization at the applied voltages of 5, 10, 20, and 40 V, respectively. The diameters of as-grown nanotubes are nearly proportional to the applied voltages. As shown in the XRD spectra of Figure 2a, only peaks related to the Ti foil are observed, indicating that all as-anodized TiO2 nanotubes are mainly amorphous phase, likely to be TiO2·xH2O [26]. Figure 2b shows a representative TEM image taken from an as-grown nanotube with the diameter of 100 nm. The corresponding diffraction pattern reconfirms that the nanotubes are non-crystalline. We also find that even after being cleaned ultrasonically in water for 1 h, the nanotube surface is partially covered by irregularly shaped and disordered structures, as indicated by white arrows. These disordered structures should be Ti(OH)4 precipitates formed via the instantaneous hydrolysis reaction, which leads to the generation and accumulation of Ti(OH)4 precipitates at the entrance of the nanotubes [27,28]. We also find that the ScCO2 fluid can effectively remove these Ti(OH)4 precipitates from the nanotube surface, ultimately resulting in purer nanotube topography for these nanotubes (see Figure 1e,f,g,h). This result shows that the ScCO2 treatment can be an effective approach for surface cleaning for Ti-based nanostructured implants.

thumbnailFigure 1. SEM images of self-organized TiO2 nanotubes with different diameters. The nanotubes are in the range of 15 to 100 nm before (a to d) and after (e to h) the ScCO2 treatment. Disordered Ti(OH)4 precipitates are indicated by white arrows.

thumbnailFigure 2. XRD spectra and TEM image of as-grown TiO2 nanotubes. (a) XRD spectra of as-grown TiO2 nanotubes with different diameters and (b) TEM image taken from an as-grown nanotube with the diameter of 100 nm. The inset also shows the corresponding diffraction pattern.

An earlier work has shown that cell attachment, spreading, and cytoskeletal organization are significantly greater on hydrophilic surfaces relative to hydrophobic surfaces [29]. Das et al. further indicated that a low contact angle leads to high surface energy, which is also an important factor that contributes to better cell attachment [30]. As mentioned previously, the ScCO2 treatment may substantially modify the surface chemistry of TiO2 and possibly change the surface wettability accordingly. It is thus essential to understand the influence of the ScCO2 treatment on the nanotube wettability. As shown in Figure 3, all as-grown TiO2 nanotubes are highly hydrophilic since their contact angles are quite small. Nevertheless, after the ScCO2 treatment, these nanotube samples become hydrophobic. Once these ScCO2-treated TiO2 nanotubes were irradiated with UV light, their surface hydrophobicity transforms to high hydrophilicity again. These UV-irradiated TiO2 nanotubes could preserve their high hydrophilicity for at least 1 month. It should be noted that even with different nanotube diameters, all nanotube samples show similar behavior in the transition of surface wettability. There are two equations in the literature that describe the water contact angle on rough surfaces. One is Wenzel's law, which describes the small contact angle on hydrophilic materials [31]. The other one is formulated by Cassie and Baxter [32], which is generally valid for heterogeneous surfaces composed of air and a solid with hydrophobicity. Both models discuss the surface wettability based on the surface roughness and geometry of materials. Our results indicate that in these TiO2 nanotubes of different diameters (i.e., with different geometric factors), surface chemistry effects prevail in their surface wettability behavior.

thumbnailFigure 3. Optical images showing water droplets. On the as-grown (upper column), ScCO2-treated (middle column), and ScCO2-treated TiO2 nanotubes with UV light irradiation (lower column), respectively. Contact angles are denoted in the images.

We attempt to elaborate the possible mechanism for the observed transitions in wettability in this study. First, we can almost exclude the possibility that the absorption of non-polar CO2 molecules on the nanotube surface leads to the hydrophobicity by the fact that the ScCO2-treated nanotubes still remain hydrophobic when kept in the atmosphere for more than 1 month. Another possibility is that newly forming functional groups on the nanotube surface during the ScCO2 process change the surface chemistry and wettability. Figure 4 shows the XPS surface analysis results, in terms of the C 1s spectra, of the as-grown, ScCO2-treated, and ScCO2-treated TiO2 nanotubes of 100 nm in diameter with UV light irradiation, respectively. We find that the C-H signal in the as-grown sample becomes much stronger (more significantly than other signals) after the ScCO2 treatment. It suggests that numerous C-H functional groups form on the TiO2 nanotube surface, possibly resulting from the reaction between the ScCO2 and TiO2·xH2O or Ti(OH)4. It has been reported that the C-H functional groups are non-polar with a hydrophobic nature [33]. This can explain why the TiO2 nanotubes become hydrophobic after the ScCO2 treatment. In addition, it is well known that TiO2 can act as a photocatalyst under UV light irradiation [34]. The C-H functional groups can be effectively photo-oxidized on the TiO2 nanotubes under UV light irradiation [35]. Therefore, the ScCO2-treated nanotubes recover their surface wettability after being irradiated with the UV light. This also agrees with the XPS result that C-H signal diminishes in the UV light-irradiated sample. The Raman spectra in Figure 5 show a similar trend. The carbon-related Raman vibrations in the as-grown sample, including C-H bending, C-H stretching, and H-C-H bending modes [36,37], become significantly stronger after the ScCO2 treatment and then diminish under UV light irradiation, indicating that the C-H functional groups indeed form on the nanotube surface and then are being photo-oxidized under UV light exposure. In addition, we find that almost no carbon-related Raman signals can be seen for the annealed TiO2 nanotubes before and after the ScCO2 treatment. This observation also supports our inference that the forming C-H functional groups may result from the reaction between ScCO2 and TiO2·xH2O or Ti(OH)4 nanotube surface. Since the annealed nanotubes have been dehydrated and transformed into a pure anatase phase, the reaction between ScCO2 and TiO2·xH2O or Ti(OH)4 to generate the C-H functional groups does not occur during the process.

thumbnailFigure 4. XPS surface analysis results, in terms of spectra for C 1 s . Of the as-grown, ScCO2-treated, and ScCO2-treated TiO2 nanotubes of 100 nm in diameter with UV light irradiation.

thumbnailFigure 5. Raman spectra of as-grown 100-nm-diameter TiO2 nanotubes treated with ScCO2 fluid and subsequent UV light irradiation.

The human fibroblast cell behavior in response to the as-grown and ScCO2-treated TiO2 nanotubes is studied. To evaluate the fibroblast cell attachment on the TiO2 nanotubes, cytoskeleton actin was stained with rhodamine phalloidin that expressed red fluorescence and nuclei were stained with DAPI that expressed blue fluorescence. The actin immunostaining shows very different cell-material contact morphology for the TiO2 nanotubes of different diameters (see Figure 6). For both as-grown and ScCO2-treated samples, there are much longer and well-defined actin fibers noted on fibroblasts cultured on 25-nm- and smaller diameter nanotubes with respect to the larger ones. It is well known that cells have to adhere on a material surface first and then spread for further cell division. Better cell adhesion can cause more activation of intracellular signaling cascades through integrin coupled to actin cytoskeleton [38,39]. Therefore, the smaller diameter nanotubes give more focal points for fibroblasts to get attached, thus help in the cell adhesion. FE-SEM was used for the detailed observation of cell adhesion (see Figure 7). The fibroblasts on the smaller diameter TiO2 nanotubes reveal good cell adhesion with an elongated flatten morphology, while those on the 50-nm- and larger diameter nanotubes show rounded morphology and lack of cell spreading. It is known that cells recognize surface features when a suitable site for adhesion has been detected. Cells then stabilize the contact by forming focal adhesions and mature actin fibers, followed by recruiting tubulin microtubules [38]. The actin cytoskeleton is linked to integrins which are located within the adhesions. Our findings suggest that the cytoskeleton on the smaller diameter nanotubes should be formed better than that on the larger diameter ones for both as-grown and ScCO2-treated nanotubes. These observations also indicate that with UV light irradiation to recover the surface wettability, ScCO2-treated TiO2 nanotube surface is suitable for the cell adhesion.

thumbnailFigure 6. Fluorescent images of the fibroblast cell attachment. On the as-grown (upper column) and ScCO2-treated (lower column) TiO2 nanotubes of different diameters. The red fluorescence indicates cytoskeletal protein actin filament, and the blue fluorescence indicates nuclei.

thumbnailFigure 7. SEM images showing the cell adhesion and proliferation of human fibroblast cells. On the as-grown (upper column) and ScCO2-treated (lower column) TiO2 nanotubes of different diameters.

The WST-1 assay was employed for further evaluating the fibroblast cell proliferation on the as-grown and ScCO2-treated TiO2 nanotubes of different diameters. Figure 8 shows the comparison of optical densities measured from the WST-1 assay results. We find that cell proliferation is lowest for the largest diameter of 100 nm in both as-grown and ScCO2-treated TiO2 nanotube samples. In addition, the ScCO2-treated TiO2 nanotubes appear to exhibit a monotonically increasing trend in cell proliferation with decreasing nanotube diameter. This trend is not so obvious in the as-grown samples. It indicates that human fibroblast cells show more obvious diameter-specific behavior on the ScCO2-treated TiO2 nanotubes than on the as-grown ones. As discussed previously, the ScCO2 fluid can effectively remove the disordered Ti(OH)4 precipitates from the nanotube surface. This may result in purer nanotube topography and thus more sensitive cell response to the diameter of the ScCO2-treated nanotubes. Eventually, for the smallest diameter of 15 nm, ScCO2-treated TiO2 nanotubes reveal higher biocompatibility than the as-grown sample.

thumbnailFigure 8. Optical densities (QD) measured after the culture of human fibroblast cells. On the as-grown and ScCO2-treated TiO2 nanotubes of different diameters.

Conclusions

In conclusion, this study investigates the diameter-sensitive biocompatibility of ScCO2-treated TiO2 nanotubes of different diameters prepared by electrochemical anodization. We find that ScCO2-treated TiO2 nanotubes can effectively recover their surface wettability under UV light irradiation as a result of photo-oxidation of C-H functional groups formed on the surface. It is demonstrated that human fibroblast cells show more obvious diameter-specific behavior on the ScCO2-treated nanotubes than on the as-grown ones, which can be attributed to the removal of disordered Ti(OH)4 precipitates from the nanotube surface by the ScCO2 fluid. This results in purer nanotube topography, stronger diameter dependence of cell activity, and thus higher biocompatibility for the 15-nm-diameter ScCO2-treated TiO2 nanotubes than the as-grown sample. This study demonstrates that the use of ScCO2 fluid can be an effective, appropriate, and promising approach for surface treatments or modifications of bio-implants.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

MYL conducted the in vitro experiments and drafted that part of the manuscript. CPL prepared all nanotube samples and analyzed their surface wettability. HHH revised the manuscript. JKC conducted the ScCO2 experiments and XPS analysis. SWL designed the study and wrote the manuscript. All authors read and approved the final manuscript.

Authors’ information

MYL is currently a visiting staff of the Department of Otolaryngology at Taipei Veterans General Hospital and also a Ph.D. candidate of National Yang-Ming University (Taiwan). CPL is currently a Master's degree student of National Central University (Taiwan). HHH is a professor of the Department of Dentistry at National Yang-Ming University (Taiwan). JKC is an assistant professor of the Institute of Materials Science and Engineering at National Central University (Taiwan). SWL is an associate professor of the Institute of Materials Science and Engineering at National Central University (Taiwan).

Acknowledgments

The research is supported by the Veterans General Hospitals University System of Taiwan Joint Research Program under contract nos. VGHUST101-G4-3-1 and VGHUST101-G4-3-2 and by the National Science Council of Taiwan under contract no. NSC-100-2221-E-008-016-MY3. The authors also thank the Center for Nano Science and Technology at National Central University and Clinical Research Core Laboratory at Taipei Veterans General Hospital for the facility support.

References

  1. Johansson CB, Albrektsson T: A removal torque and histomorphometric study of commercially pure niobium and titanium implants in rabbit bone.

    Clin Oral Implan Res 1991, 2:24-29. Publisher Full Text OpenURL

  2. Abrahamsson I, Zitzmann NU, Berglundh T, Wennerberg A, Lindhe J: Bone and soft tissue integration to titanium implants with different surface topography: an experimental study in the dog.

    Int J Oral Maxillofac Implants 2001, 16:323-332. PubMed Abstract OpenURL

  3. Olmedo D, Fernández MM, Guglielmotti MB, Cabrini RL: Macrophages related to dental implant failure.

    Implant Dent 2003, 12:75-80. PubMed Abstract | Publisher Full Text OpenURL

  4. Buser D, Schenk RK, Steinemann S, Fiorellini J, Fox C, Stich H: Influence of surface characteristics on bone integration of titanium implants. A histomorphometric study in miniature pigs.

    J Biomed Mater Res 1991, 25:889-902. PubMed Abstract | Publisher Full Text OpenURL

  5. Hansson S, Norton M: The relation between surface roughness and interfacial shear strength for bone-anchored implants. A mathematical model.

    J Biomech 1999, 32:829-836. PubMed Abstract | Publisher Full Text OpenURL

  6. Davies JE: Understanding peri-implant endosseous healing.

    J Dent Educ 2003, 67:932-949. PubMed Abstract | Publisher Full Text OpenURL

  7. Oliveira PT, Nanci A: Nanotexturing of titanium-based surfaces upregulates expression of bone sialoprotein and osteopontin by cultured osteogenic cells.

    Biomaterials 2004, 25:403-413. PubMed Abstract | Publisher Full Text OpenURL

  8. Mendonça G, Mendonça DBS, Aragão FJL, Cooper LF: Advancing dental implant surface technology–from micron- to nanotopography.

    Biomaterials 2008, 29:3822-3835. PubMed Abstract | Publisher Full Text OpenURL

  9. Yang WE, Hsu ML, Lin MC, Chen ZH, Chen LK, Huang HH: Nano/submicron-scale TiO2 network on titanium surface for dental implant application.

    J Alloy Compd 2009, 479:642-647. Publisher Full Text OpenURL

  10. Dong W, Zhang T, Epstein J, Cooney L, Wang H, Li Y, Jiang YB, Cogbill A, Varadan V, Tian ZR: Multifunctional nanowire bioscaffolds on titanium.

    Chem Mater 2007, 19:4454-4459. Publisher Full Text OpenURL

  11. Chiang CY, Chiou SH, Yang WE, Hsu ML, Yung MC, Tsai ML, Chen LK, Huang HH: Formation of TiO2 nano-network on titanium surface increases the human cell growth.

    Dent Mater 2009, 25:1022-1029. PubMed Abstract | Publisher Full Text OpenURL

  12. Su Z, Zhou W: Formation, morphology control and applications of anodic TiO2 nanotube arrays.

    J Mater Chem 2011, 21:8955-8970. Publisher Full Text OpenURL

  13. Chen JG, Chen CY, Wu CG, Lin CY, Lai YH, Wang CC, Chen HW, Vittal R, Ho KC: An efficient flexible dye-sensitized solar cell with a photoanode consisting of TiO2 nanoparticle-filled and SrO-coated TiO2 nanotube arrays.

    J Mater Chem 2010, 20:7201-7207. Publisher Full Text OpenURL

  14. Popat KC, Eltgroth M, LaTempa TJ, Grimes CA, Desai TA: Titania nanotubes: a novel platform for drug-eluting coatings for medical implants.

    Small 2007, 3:1878-1881. PubMed Abstract | Publisher Full Text OpenURL

  15. Das K, Bose S, Bandyopadhyay A, Karandikar B, Gibbins BL: Surface coatings for improvement of bone cell materials and antimicrobial activities of Ti implants.

    J Biomed Mater Res B 2008, 87:455-460. OpenURL

  16. Chun AL, Moralez JG, Webster TJ, Fenniri H: Helical rosette nanotubes: a biomimetic coating for orthopedics.

    Biomaterials 2005, 26:7304-7309. PubMed Abstract | Publisher Full Text OpenURL

  17. Popat KC, Leoni L, Grimes CA, Desai TA: Influence of engineered titania nanotubular surfaces on bone cells.

    Biomaterials 2007, 28:3188-3197. PubMed Abstract | Publisher Full Text OpenURL

  18. Bauer S, Park J, von der Mark K, Schmuki P: Improved attachment of mesenchymal stem cells on super-hydrophobic TiO2 nanotubes.

    Acta Biomater 2008, 4:1576-1582. PubMed Abstract | Publisher Full Text OpenURL

  19. Park J, Bauer S, von der Mark K, Schmuki P: Nanosize and vitality: TiO2 nanotube diameter directs cell fate.

    Nano Lett 2007, 7:1686-1691. PubMed Abstract | Publisher Full Text OpenURL

  20. Bauer S, Park J, Faltenbacher J, Berger S, von der Mark K, Schmuki P: Size selective behavior of mesenchymal stem cells on ZrO2 and TiO2 nanotube array.

    Integr Biol 2009, 1:525-532. Publisher Full Text OpenURL

  21. McCool B, Tripp CP: Inaccessible hydroxyl groups on silica are accessible in supercritical CO2.

    J Phys Chem B 2005, 109:8914-8919. PubMed Abstract | Publisher Full Text OpenURL

  22. Tsai PJ, Yang CH, Hsu WC, Tsai WT, Chang JK: Enhancing hydrogen storage on carbon nanotubes via hybrid chemical etching and Pt decoration employing supercritical carbon dioxide fluid.

    Int J Hydrogen Energ 2012, 37:6714-6720. Publisher Full Text OpenURL

  23. Reverchon E, Porta GD, Adami R: Medical device sterilization using supercritical CO2 based mixtures.

    Recent Pat Chem Eng 2010, 3:000-000. OpenURL

  24. Gu W, Tripp CP: Reaction of silanes in supercritical CO2 with TiO2 and Al2O3.

    Langmuir 2006, 22:5748-5752. PubMed Abstract | Publisher Full Text OpenURL

  25. Zhu K, Vinzant TB, Neale NR, Frank AJ: Removing structural disorder from oriented TiO2 nanotube arrays: reducing the dimensionality of transport and recombination in dye-sensitized solar cells.

    Nano Lett 2007, 7:3739-3746. PubMed Abstract | Publisher Full Text OpenURL

  26. Su Z, Zhou W: Formation mechanism of porous anodic aluminium and titanium oxides.

    Adv Mater 2008, 20:1-5. OpenURL

  27. Wang D, Liu Y, Yu B, Zhou F, Liu W: TiO2 nanotubes with tunable morphology, diameter, and length: synthesis and photo-electrical/catalytic performance.

    Chem Mater 2009, 21:1198-1206. Publisher Full Text OpenURL

  28. Lai CW, Sreekantan S: Photoelectrochemical performance of smooth TiO2 nanotube arrays: effect of anodization temperature and cleaning methods.

    Int J Photoenergy 2012, 2012:356943-1-356943-11. OpenURL

  29. Webb K, Hlady V, Tresco PA: Relative importance of surface wettability and charged functional groups on NIH 3 T3 fibroblast attachment, spreading, and cytoskeletal organization.

    J Biomed Mater Res 1998, 41:422-430. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  30. Das K, Bose S, Bandyopadhyay A: Surface modifications and cell-materials interactions with anodized Ti.

    Acta Biomater 2007, 3:573-585. PubMed Abstract | Publisher Full Text OpenURL

  31. Wenzel RN: Resistance of solid surfaces to wetting by water.

    Ind Eng Chem 1936, 28:988-994. Publisher Full Text OpenURL

  32. Cassie ABD, Baxter S: Wettability of porous surfaces.

    Trans Faraday Soc 1944, 40:546-551. OpenURL

  33. Petters MD, Prenni AJ, Kreidenweis SM, DeMott PJ, Matsunaga A, Lim YB, Ziemann PJ: Chemical aging and the hydrophobic-to-hydrophilic conversion of carbonaceous aerosol.

    Geophys Res Lett 2006, 33:L24806-1-L24806-5. OpenURL

  34. Hashimoto K, Irie H, Fujishima A: TiO2 photocatalysis: a historical overview and future prospects.

    Jpn J Appl Phys 2005, 44:8269-8285. Publisher Full Text OpenURL

  35. Collins-Martínez V, Ortiz AL, Elguézabal AA: Influence of the anatase/rutile ratio on the TiO2 photocatalytic activity for the photodegradation of light hydrocarbons.

    Iny J Chem React Eng 2007, 5:A92-1-A92-11. OpenURL

  36. Lauchlan L, Chen SP, Etemad S, Kletter M, Heeger AJ, MacDiarmid AG: Absolute Raman scattering cross sections of trans-(CH)x.

    Phys Rev B 1983, 27:2301-2307. Publisher Full Text OpenURL

  37. Kalyanasundaram K, Thomas JK: The conformational state of surfactants in the solid state and in micellar form. A laser-excited Raman scattering study.

    J Phys Chem 1976, 80:1462-1473. Publisher Full Text OpenURL

  38. Dalby MJ, Childs S, Riehle MO, Johnstone HJH, Affrossman S, Curtis ASG: Fibroblast reaction to island topography: changes in cytoskeleton and morphology with time.

    Biomaterials 2003, 24:927-935. PubMed Abstract | Publisher Full Text OpenURL

  39. Schlaepfer DD, Hauck CR, Sieg DJ: Signaling through focal adhesion kinase.

    Prog Biophys Mol Biol 1999, 71:435-478. PubMed Abstract | Publisher Full Text OpenURL