Open Access Nano Express

Lu3+/Yb3+ and Lu3+/Er3+ co-doped antimony selenide nanomaterials: synthesis, characterization, and electrical, thermoelectrical, and optical properties

Younes Hanifehpour12*, Sang Woo Joo1* and Bong-Ki Min3

Author Affiliations

1 School of Mechanical Engineering, Yeungnam University, Gyongsan 712-749, South Korea

2 Department of Applied Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran

3 Center for Research Facilities, Yeungnam University, Gyongsan 712-749, South Korea

For all author emails, please log on.

Nanoscale Research Letters 2013, 8:141  doi:10.1186/1556-276X-8-141

The electronic version of this article is the complete one and can be found online at:

Received:18 February 2013
Accepted:11 March 2013
Published:27 March 2013

© 2013 Hanifehpour et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.


Lu3+/Yb3+ and Lu3+/Er3+ co-doped Sb2Se3 nanomaterials were synthesized by co-reduction method in hydrothermal condition. Powder X-ray diffraction patterns indicate that the LnxLnxSb2−2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x = 0.00 − 0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). Scanning electron microscopy and transmission electron microscopy images show that co-doping of Lu3+/Yb3+ ions in the lattice of Sb2Se3 produces nanorods, while that in Lu3+/Er3+ produces nanoparticles, respectively. The electrical conductivity of co-doped Sb2Se3 is higher than that of the pure Sb2Se3 and increases with temperature. By increasing the concentration of Ln3+ions, the absorption spectrum of Sb2Se3 shows red shifts and some intensity changes. In addition to the characteristic red emission peaks of Sb2Se3, emission spectra of co-doped materials show other emission bands originating from f-f transitions of the Yb3+ ions.

Co-doped; Nanomaterial; Luminescent; Electrical conductivity; Hydrothermal


Nanosized semiconductor materials have drawn much research attention because their physical and chemical properties, due to size quantization effect, dramatically change and, in most case, are improved as compared with their bulk counterparts [1-3]. Rare earth-substituted compounds with various compositions have become an increasingly important research topic in diverse areas, such as luminescent device, light-emitting displays, biological labeling, and imaging [4-6], due to the introduction of dopant levels within the bandgap and modification of the band structure. In addition, significant efforts have been devoted to enhance the activity of wide bandgap photocatalysts by doping for environmental remediation [7,8]. Semiconductor selenides find applications as laser materials, optical filters, sensors, and solar cells. Antimony selenide, an important member of these V2VI3 compounds, is a layer-structured semiconductor of orthorhombic crystal structure and exhibits good photovoltaic properties and high thermoelectric power, which allows possible applications for optical and thermoelectronic cooling devices [9-11]. The research of impurity effects or doping agents on the physical properties of Sb2Se3 is interesting both for basic and applied research. Doping of some transition metal and lanthanide to the lattice of metal chalcogenides has been investigated [12-20]. The incorporation of large electropositive ions such as lanthanides into metal chalcogenide frameworks is expected to affect the electronic properties of that framework. In this work, we report the preparation, structural, electrical, and optical properties of Lu3+/Yb3+ and Lu3+/Er3+ co-doped antimony selenide via co-reduction method at hydrothermal condition.


All chemicals were of analytical grade and were used without further purification. Gray selenium (1 mmol) and NaOH (5 mmol) were added to distilled water (60 mL) and stirred well for 10 min at room temperature. Afterwards, hydrazinium hydroxide (2 mL, 40 mmol), SbCl3 (1.98, 1.96, 1.94, and 1.92 mmol) and Ln2O3 (0.00, 0.01, 0.02, and 0.04 mmol) (Ln: Lu3+, Yb3+, Er3+) based on the molecular formula LnxLnxSb2−2xSe3 (0 ≤ x ≤ 0.04) were added, and the mixture was transferred to a 100-mL Teflon-lined autoclave. The autoclave was sealed, maintained at 180°C for 48 h, and then cooled to room temperature. The optimum conditions for this reaction are pH = 12, temperature = 180°C, and reaction time = 48 h. The black precipitate obtained was filtered and washed with ethanol and water. It was dried at room temperature. Yields for the products were 75% to 85%. Phase identification was performed by powder X-ray diffraction (XRD, D5000 Siemens AG, Munich, Germany) with Cu Kα radiation. Cell parameters were calculated using the Celref program (CCP14, London, UK) from powder XRD patterns, and reflections have been determined and fitted using a profile fitting procedure with the WinXPOW program (STOE & CIE GmbH, Darmstadt, Germany). The reflections observed in 2θ = 4° to 70° were used for the lattice parameter determination. The morphology of materials was examined by scanning electron microscopy (SEM, Hitachi S-4200, Hitachi High-Tech, Minato-ku, Tokyo, Japan). A linked ISIS-300 Oxford EDS detector (Oxford Instruments plc, Oxfordshire, UK) was used for elemental analyses. The high-resolution transmission electron microscopy (HRTEM) image and selected area electron diffraction (SAED) pattern were recorded by a Cs-corrected HRTEM (JEM-2200FS, JEOL Ltd., Akishima, Tokyo, Japan) operated at 200 kV. Photoluminescence measurements were carried out using a Spex FluoroMax3 spectrometer (HORIBA Jobin Yvon Inc., Edison, NJ, USA) after dispersing a trace amount of sample via ultrasound in distilled water. Four-point probe method was used for the measurement of electrical and thermoelectrical resistivity of samples. A small oven was needed for the variation of temperature of the samples from the room temperature to about 200°C (maximum). A small chip with 1-mm thickness and 7-mm length was used for this analysis.

Results and discussion

The powder XRD patterns (Figure 1) of LuxYbxSb2−2xSe3 samples indicate that the Lu3+/Yb3+ co-doped antimony selenide has the same orthorhombic structure as Sb2Se3 and that single-phase Sb2Se3 is retained at lower doping concentrations of Lu3+/Yb3+. All the peaks in Figure 1 can be attributed to the orthorhombic phase of Sb2Se3 with Pbnm space group and lattice parameters a = 11.62 Å, b = 11.76 Å, and c = 3.95 Å (JCPDS card file 72–1184). For doping levels higher than x = 0.04 for Lu3+ and Yb3+, additional unknown phases were observed (curve c of Figure 1). In the case of Lu3+/Er3+ co-doped compounds, the intensity of some peaks has been changed, and for doping levels higher than of x = 0.04 for Lu3+ and Er3+, additional unknown phases were also observed (see Additional file 1).

thumbnailFigure 1. Powder XRD pattern of LuxYbxSb2xSe3. Curve a: x = 0.0, curve b: x = 0.04, and curve c = impurity phase.

Additional file 1. XRD patterns of LuxErxSb2−2xSe3, TEM, HRTEM images, SAED pattern of Sb2Se3 nanorods, absorption spectra of Lu0.02Yb0.02Sb1.96Se3, Lu0.01Yb0.01Sb1.98Se3, and Lu0.02Er0.02Sb1.96Se3 are provided. Figure S1. Powder X-ray diffraction pattern of LuxErxSb2−xSe3 (x = 0.02). Figure S2. Powder X-ray diffraction pattern of LuxErxSb2−xSe3 (x = 0.04). Figure S3. Powder X-ray diffraction pattern of unknown LuxErxSb2−xSe3 phase. Figure S4. TEM image of Sb2Se3 nanorods. Figure S5. HRTEM image of the Sb2Se3 nanorods. Figure S6. SAED Pattern of the Sb2Se3 nanorods. The SAED zone axis is [1]. Figure S7. Absorption spectra of Lu0.02Yb0.02Sb1.96Se3 nanorods at room temperature. Figure S8. Absorption spectra of Lu0.01Yb0.01Sb1.98Se3 nanorods at room temperature. Figure S9. Absorption spectra of Lu0.02Er0.02Sb1.96Se3 nanoparticles at room temperature. (DOC 3322 kb)

Format: DOC Size: 3.2MB Download file

This file can be viewed with: Microsoft Word ViewerOpen Data

In addition, a little shift toward the low angle was seen in the diffraction peaks of the co-doped Sb2Se3 compared with those of the undoped Sb2Se3 nanocrystals. This suggests that the larger lanthanide ions substitute the antimony ions, resulting in increased lattice constants. As expected, the EDX and ICP analyses of the product confirm the ratio of Sb/Se/Ln/Ln (see Figure 2).

thumbnailFigure 2. EDX patterns of LnxLnxSb22xSe3 compounds.

The cell parameters of the synthesized materials were calculated from the XRD patterns. With increasing dopant content (x), the lattice parameters were increased for these materials, as shown in Figure 3. This trend is similar to the previous reported Ln-doped Sb2Se3 compounds [16-20].

thumbnailFigure 3. The lattice constants of co-doped Sb2Se3 dependent upon Ln3 +doping on Sb3 +sites.

Figure 4a shows SEM images of Lu0.04Yb0.04Sb1.92Se3 nanorods with 3-μm lengths and thicknesses of 70 to 200 nm. Co-doping of Lu3+ and Yb3+ into the structure of Sb2Se3 does not change the morphology of the Sb2Se3 nanorods, but doping of Lu3+ and Er3+ into the structure of Sb2Se3 changes the morphology from rods to particles. The diameter of Lu0.04Er0.04Sb1.92Se3 particles is around 25 nm (Figure 4b).

thumbnailFigure 4. SEM images of co-doped antimony selenide. (a) Lu0.04Yb0.04Sb1.92Se3 nanorods (b) Lu0.04Er0.04Sb1.92Se3 nanoparticles.

Figure 5a shows TEM image of as-prepared Lu0.04Yb0.04Sb1.92Se3 nanorods. The SAED pattern and typical HRTEM image recorded from the same nanorods of Lu0.04Yb0.04Sb1.92Se3 is shown in Figure 5b,c. The crystal lattice fringes are clearly observed, and the average distance between the neighboring fringes is 0.82 nm, corresponding to the [1-10] plane lattice distance of the orthorhombic-structured Sb2Se3, which suggests that Lu0.04Yb0.04Sb1.92Se3 nanorods grow along the [1] direction. The HRTEM image and SAED pattern are the same for Sb2Se3 and show similar growth direction (see the Additional file 1).

thumbnailFigure 5. TEM (a), SAED pattern (b), and HRTEM image (c) of Lu0.04Yb0.04Sb1.92Se3 nanorods.

Figure 6a,b shows the TEM image and SAED patterns of Lu0.04Er0.04Sb1.92Se3 nanoparticles obtained in ethanol/water media that confirms the result through SEM images and shows high crystallinity of the sample.

thumbnailFigure 6. TEM (a) and SAED pattern (b) of Lu0.04Er0.04Sb1.92Se3 nanoparticle.

In doped semiconductors, two types of emissions are responsible for dopant (impurity) luminescence. One can be observed only upon direct excitation of the dopant. The other type is obtained if energy transfer from host to dopant occurs. Binary compounds such as Sb2Se3 and its alloys are thermoelectric materials with layered crystalline structures. These materials have been investigated for the direct conversion of thermal energy to electric energy, and they are specially used for electronic refrigeration [9]. The four-point probe method was used for the measurement of electrical and thermoelectrical resistivity of samples (Figure 7).

thumbnailFigure 7. Schematic of four-point probe.

At room temperature, the electrical resistivity of pure Sb2Se3 was of the order of 0.2 Ω·m; in the case of Lu0.04Yb0.04Sb1.92Se3, the minimum value of electrical resistivity is 0.009 Ω·m, and for Lu0.04Er0.04Sb1.92Se3, it is 0.032 Ω·m. With the increase in lanthanide concentration, the electrical resistivity of synthesized nanomaterials decreased obviously (Figure 8a).

thumbnailFigure 8. Electrical (a) and thermoelectrical (b) resistivity of co-doped Sb2Se3 compounds.

The temperature dependence of the electrical resistivity for co-doped Sb2Se3 nanomaterials between 290 and 350 K is shown in Figure 8b. Electrical resistivity decreases linearly with temperature, and the minimum value for Lu0.04Yb0.04Sb1.92Se3 was measured as 0.0006 Ω·m and for Lu0.04Er0.04Sb1.92Se3 as 0.005 Ω·m. Two factors that include the overlapping of wave functions of electrons in doped Sb2Se3 and that acting as a charge carrier due to lanthanide atomic structure (having empty f orbitals) are important reasons for decreasing electrical resistivity. The obtained data shows higher electrical resistivity for co-doped samples in comparison with doped samples in the case of Lu3+, Yb3+ and Er3+ doped Sb2Se3[16,17]. The measurements indicate that the co-doping materials have higher electrical and thermoelectrical conductivity than the doped compounds in spite of lower lanthanide content [16-20]. Comparing both doped and co-doped data, the combining energy levels of the two lanthanides and the overlapping of wave functions of electrons in two different lanthanides are responsible for the difference between the obtained results. Among the co-doped compounds, Lu3+/Yb3+-doped Sb2Se3 has the higher electrical conductivity.

UV–vis spectra of Lu0.04Yb0.04Sb1.92Se3 are shown in Figure 9a. The absorption spectra reveal the existence of Sb2Se3 and Lu3+ ions (in the visible domain) and Yb3+ ions in the near-IR domain. By increasing the concentration of Ln3+ ions, the absorption spectrum of Sb2Se3 shows red shifts and some intensity changes (see Additional file 1). The Lu3+ ion has no excited 4f levels; therefore, the peaks between 500 and 600 nm can be assigned to the ionization of Lu 5d orbitals and lattice of Sb2Se3.[21,22], and the peak at 830 nm can be assigned to the 2F7/22F5/2 transition (f-f transitions) of the Yb3+ ions [23].

thumbnailFigure 9. Absorption spectra of co-doped antimony selenide at room temperature. (a) Lu0.04Yb0.04Sb1.92Se3 (b) Lu0.04Er0.04Sb1.92Se3.

For Lu0.04Er0.04Sb1.92Se3, the transition of the Er3+ ions is not observed because of instrument limitation. The peaks between 500 and 620 nm can then be assigned to the lattice of Sb2Se3 (Figure 9b). The difference between absorption patterns of compounds is related to various defects created in the lattice. There is a red shift in the doped materials in comparison with pure Sb2Se3 because of the smaller nanoparticles of Sb2Se3, in which the bandgap is higher than the doped nanomaterials [24,25]. It is well known that the fundamental absorption can be used to determine the nature and value of the optical bandgap of the nanoparticles. The bandgap energies of samples were estimated from the absorption limit. The calculated bandgap is 2.43 eV for Lu0.04Yb0.04Sb1.92Se3 and 2.36 eV for Lu0.04Er0.04Sb1.92Se3.

Figure 10a exhibited the room-temperature photoluminescence emission spectra of Lu0.04Yb0.04Sb1.92Se3. The Lu3+ 5d-4f luminescence is almost completely quenched at temperatures T > 200 K. The Lu3+ ion has no excited 4f levels, and therefore, thermal quenching of Lu3+ 5d-4f luminescence cannot have been caused by nonradiative transitions to 4f levels and should be attributed to the thermally activated ionization of 5d electrons to the conduction band [21,22]. The peaks at 500 to 700 nm can then be assigned to the crystal structure of Sb2Se3, and its defects and the band at 880 nm is related to 2F5/22F7/2 transition of Yb3+ions.

thumbnailFigure 10. Emission spectra for co-doped antimony selenide at room temperature (λexc =470 nm). (a) Lu0.04Yb0.04Sb1.92Se3 (b) Lu0.04Er0.04Sb1.92Se3.

In case the of Lu0.04Er0.04Sb1.92Se3, intra-4f Er3+ transitions of the 4I11/2 and 4I13/2 levels to the ground state (4I15/2) are expected around 1.54 μm. These could, however, not be determined due to equipment limitations [24]. Therefore, emission bands at 550 to 700 nm are related to the crystal structure of Sb2Se3 (Figure 10b). The optical properties of co-doped compounds considering absorbance and photoluminescence spectra show similar f-f transitions in the case of Yb-doped materials and similar results for Lu- and Er-doped materials as obtained for Ln-doped Sb2Se3. We expect that these materials can be good candidates as novel photocatalysts due to their modified bandgaps by doping with lanthanides. Indeed, doping is the best way for the modification of semiconductors for special uses such as photocatalysts in order for the degradation of azo dye and organic pollutant to take place.


New thermoelectric Ln2xSb2−2xSe3 (Ln: Lu3+/Yb3+ and Lu3+/Er3+)-based nanomaterials were synthesized by a simple hydrothermal method. The cell parameters were increased for compounds upon increasing the dopant content (x). According to the SEM and TEM images, different morphologies were seen in co-doped Sb2Se3. The HRTEM image and SAED pattern show similar growth [1] directions for Lu3+/Yb3+ co-doped like Sb2Se3 nanorods. Lanthanide doping promotes the electrical conductivity of Sb2Se3 as well as thermoelectrical conductivity. UV–vis absorption and emission spectroscopy reveals mainly the electronic transitions of the Ln3+ ions in the case of Yb3+-doped nanomaterials.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

YH carried out the experiments and drafted the manuscript. SWJ directed the study and provided the analyses. BM carried out the experimental analysis. All authors read and approved the final manuscript.


This work is funded by the World Class University grant R32-2008-000-20082-0 of the National Research Foundation of Korea.


  1. Calvert P: Rough guide to the nanoworld.

    Nature 1996, 383:300-301. Publisher Full Text OpenURL

  2. Weller H: Quantized semiconductor particles: a novel state of matter for materials science.

    Adv Mater 1993, 5:88-95. Publisher Full Text OpenURL

  3. Alivisatos AP: Semiconductor clusters, nanocrystals, and quantum dots.

    Science 1996, 271:933-937. Publisher Full Text OpenURL

  4. Wang F, Han Y, Lim CS, Lu YH, Wang J, Xu J, Chen HY: Simultaneous phase and size control of upconversion nanocrystals through lanthanide doping.

    Nature 2010, 463:1061-1065. PubMed Abstract | Publisher Full Text OpenURL

  5. Tachikawa T, Ishigaki T, Li J, Fujitsuka M: Defect mediated photoluminescence dynamics of Eu+3-doped TiO2 nanocrystals revealed at the single particle or single aggregate level.

    Angew Chem Int Ed 2008, 47:5348-5352. Publisher Full Text OpenURL

  6. Sun Y, Chen Y, Tian LJ, Yu Y, Kong XG: Morphology-dependent upconversion luminescence of ZnO:Er3+ nanocrystals.

    J Lumin 2008, 128:15-21. Publisher Full Text OpenURL

  7. Batzill M, Morales EH, Diebold U: Influence of nitrogen doping on the defect formation and surface properties of TiO2 rutile and anatase.

    Phys Rev Lett 2006, 96:026103-4. PubMed Abstract | Publisher Full Text OpenURL

  8. Asahi R, Morikawa T, Ohwaki T, Aoki K, Taga Y: Visible-light photocatalysis in nitrogen- doped titanium oxides.

    Science 2001, 293:269-271. PubMed Abstract | Publisher Full Text OpenURL

  9. Chim T, Chun B: Microstructure and thermoelectric properties of n- and p-type Bi2Te3 alloys by rapid solidification processes.

    J Alloys Compd 2007, 437:225-230. Publisher Full Text OpenURL

  10. Qiu X, Burda C, Fu R, Pu L, Chen H, Zhu J: Heterostructured Bi2Se3 nanowires with periodic phase boundaries.

    J Am Chem Soc 2004, 126:16276-16277. PubMed Abstract | Publisher Full Text OpenURL

  11. Mastrovito C, Lekse JW, Aitken JA: Rapid solid-state synthesis of binary group 15 chalcogenides using microwave irradiation.

    J Solid State Chem 2007, 180:3262-3270. Publisher Full Text OpenURL

  12. Larson P, Lambrecht RL: Electronic structure and magnetism in Bi2Te3, Bi2Se3, and Sb2Te3 doped with transition metals (Ti–Zn).

    Phys Rev B 2008, 78:195-207. OpenURL

  13. Janícek P, Drasar C, Losták P, Vejpravová J: Transport, magnetic, optical and thermodynamic properties of Bi2−xMnxSe3 single crystals.

    Physica B 2008, 403:3553-3558. Publisher Full Text OpenURL

  14. Lostak P, Drasar C, Klichova I, Cernohorsky T: Properties of Bi2Se3 single crystals doped with Fe atom.

    Phys Status Solidi B 1997, 200:289-296. Publisher Full Text OpenURL

  15. Alemi A, Klein A, Meyer G, Dolatyari M, Babalou A: Synthesis of new LnxBi2−xSe3 (Ln: Sm3+, Eu3+, Gd3+, Tb3+) nanomaterials and investigation of their optical properties.

    Z Anorg Allg Chem 2011, 637:87-93. Publisher Full Text OpenURL

  16. Alemi A, Hanifehpour Y, Joo SW, Min B: Synthesis of novel LnxSb2−xSe3 (Ln: Lu3+, Ho3+, Nd3+) nanomaterials via co-reduction method and investigation of their physical properties.

    Colloids and Surfaces A: Physicochem. Eng. Aspects 2011, 390:142-148. Publisher Full Text OpenURL

  17. Alemi A, Hanifehpour Y, Joo SW, Khandar A, Morsali A, Min B: Co-reduction synthesis of new LnxSb2−xS3 (Ln: Nd3+, Lu3+, Ho3+) nanomaterials and investigation of their physical properties.

    Physica B 2011, 406:2801-2806. Publisher Full Text OpenURL

  18. Alemi A, Hanifehpour Y, Joo SW, Khandar A, Morsali A, Min B: Synthesis and characterization of new LnxSb2−xSe3 (Ln: Yb3+, Er3+) nanoflowers and their physical properties.

    Physica B 2012, 407:38-43. Publisher Full Text OpenURL

  19. Alemi A, Hanifehpour Y, Joo SW, Min B: Structural studies and physical properties of novel Sm3+-doped Sb2Se3 nanorods.

    Physica B 2011, 406:3831-3835. Publisher Full Text OpenURL

  20. Alemi A, Hanifehpour Y, Joo SW, Min B: Co-reduction synthesis, spectroscopic and structural studies of novel Gd3+-doped Sb2Se3 nanorods.

    J Nanomater 2012. Publisher Full Text OpenURL

  21. Makhov VN, Batygov SK, Dmitruk LN, Kirm M, Vielhauer S: VUV 5d−4f luminescence of Gd3+ and Lu3+ ions in the CaF2 host.

    Phys Solid State 2008, 50:1625-1630. Publisher Full Text OpenURL

  22. Zych E, Hreniak D, Strek W: Spectroscopic properties of Lu2O3:Eu3+ nano-crystalline powders and sintered ceramics.

    J Phys Chem B 2002, 106:3805-3812. Publisher Full Text OpenURL

  23. Loh E: 4fn→4fn−15d Spectra of rare-earth ions in crystals.

    Phys Rev 1968, 175:533-536. Publisher Full Text OpenURL

  24. Strohheofer C, Polman A: Absorption and emission spectroscopy in Er3+-Yb3+ doped aluminum oxide waveguides.

    Opt Mater 2003, 21:705-712. Publisher Full Text OpenURL

  25. Hoven GN, Elsken JA, Polman A, Dam C, Uffelen K, Smit MK: Absorption and emission cross sections of Er3+ in Al2O3 waveguides.

    Appl Opt 1997, 36:3338-3341. PubMed Abstract | Publisher Full Text OpenURL