Open Access Nano Express

Maskless and low-destructive nanofabrication on quartz by friction-induced selective etching

Chenfei Song1, Xiaoying Li2, Shuxun Cui1, Hanshan Dong2, Bingjun Yu1 and Linmao Qian1*

Author affiliations

1 Tribology Research Institute, National Traction Power Laboratory, Southwest Jiaotong University, Chengdu, Sichuan Province, 610031, People’s Republic of China

2 School of Metallurgy and Materials, The University of Birmingham, Birmingham, B15 2TT, UK

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2013, 8:140  doi:10.1186/1556-276X-8-140


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/140


Received:25 February 2013
Accepted:12 March 2013
Published:27 March 2013

© 2013 Song et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

A low-destructive friction-induced nanofabrication method is proposed to produce three-dimensional nanostructures on a quartz surface. Without any template, nanofabrication can be achieved by low-destructive scanning on a target area and post-etching in a KOH solution. Various nanostructures, such as slopes, hierarchical stages and chessboard-like patterns, can be fabricated on the quartz surface. Although the rise of etching temperature can improve fabrication efficiency, fabrication depth is dependent only upon contact pressure and scanning cycles. With the increase of contact pressure during scanning, selective etching thickness of the scanned area increases from 0 to 2.9 nm before the yield of the quartz surface and then tends to stabilise after the appearance of a wear. Refabrication on existing nanostructures can be realised to produce deeper structures on the quartz surface. Based on Arrhenius fitting of the etching rate and transmission electron microscopy characterization of the nanostructure, fabrication mechanism could be attributed to the selective etching of the friction-induced amorphous layer on the quartz surface. As a maskless and low-destructive technique, the proposed friction-induced method will open up new possibilities for further nanofabrication.

Keywords:
Maskless; Nanofabrication; Friction-induced selective etching; Quartz; 81.16.Rf; 68.37.Ps

Background

By virtue of its excellent chemical and physical properties, quartz has been widely used in micro/nanoelectromechanical systems (MEMS/NEMS), such as piezoelectric sensors [1], biochips [2], optical sensors [3], etc. Traditional lithographic fabrication on a quartz surface includes a complex process of mask deposition, exposure, etching and mask removal [4,5]. As device dimension has been down to nanoscale, traditional lithography hardly provides feasible nanofabrication on the quartz surface because of its involute process and limited resolution [6].

Although electron beam lithography has a better resolution in nanofabrication [7], high-energy beam can cause undesirable amorphization on quartz [8]. By virtue of their high precision, proximal probe methods based on scanning tunnel microscopy and atomic force microscopy (AFM) have been employed to fabricate nanostructures [9-13]. For example, AFM was used to fabricate a series of nanoscale grooves on polymers, metals and semiconductors by mechanical cutting [9]. However, it is inappropriate for quartz surface because of crack generation during the cutting process on such hard, brittle materials [10]. Although nanostructures can be fabricated on conductive surfaces by an anodic oxidation process at a given voltage, it is invalid for an insulator surface of quartz [11]. Recently, hillock-like nanostructures can be fabricated on silicon and quartz surfaces by sliding a diamond tip with repeated scratching cycles under suitable low loads [12,13]. However, since such hillocks are mainly generated from mechanical deformation of substrates, possible lattice damages may form on the surface of the hillocks and reduce their mechanical properties [14]. Because the lattice damages are detrimental to the applications of quartz devices [15,16], it is imperative to develop a straightforward and low-destructive nanofabrication method for the quartz surface.

In the present study, a novel nanofabrication method to produce three-dimensional nanostructures on the quartz surface has been developed by low-destructive scanning on a target area and post-etching in a KOH solution. The capability of this nanofabrication method was demonstrated by various nanostructures including slopes, hierarchical stages and chessboard-like patterns. The etching rate of the scanned area was tested at various temperatures. To produce deeper structures, refabrication was attempted on the existing nanostructures. The fabrication mechanism was discussed based on Arrhenius fitting of the etching rate and transmission electron microscopy (TEM) characterization of the nanostructure. In brief, the low-destructive friction-induced nanofabrication method may shed new light on nanotechnology.

Methods

Monocrystalline quartz wafers (X-cut) with a thickness of 0.5 mm were purchased from Semiconductor Wafer, Inc. (Hsinchu, Taiwan). By AFM (SPI3800N, Seiko, Tokyo, Japan), the root-mean-square (RMS) roughness of the quartz wafers was measured as 0.15 nm over a 2 × 2 μm2 area. The whole fabrication process consists of two steps: low-destructive scanning on the target area and selective etching in the KOH solution, as shown in Figure 1. Low-destructive scanning was performed by AFM mounted with a diamond tip (Micro Star Technologies, Huntsville, TX, USA). The nominal curvature radius of the tip was 350 nm, and the spring constant of the cantilever was calibrated as 200 N/m [17]. To avoid the wear of surface, the applied normal load Fn was lower than 15 μN, under which the corresponding maximum Hertzian contact pressure was below 5.1 GPa [18,19]. After scanning, the demanded nanostructures were produced at the scanned area of the quartz surface by etching the samples in 20-wt.% KOH solution for appropriate periods at 293 K if not specially mentioned. A variety of nanostructures can be fabricated through the control of scanning load and tip traces. To improve the fabrication efficiency, quartz samples were etched at various temperatures ranging from 273 to 328 K after scanning under constant loads of 5, 8 and 12 μN. To get a deeper fabrication depth, refabrication was realised on an existing 5 × 5 μm2 area with a depth of 1.2 nm. All the AFM images of the nanostructures were scanned by Si3N4 tips with a nominal spring constant of 0.1 N/m (MLCT, Bruker Corp., Billerica, MA, USA).

thumbnailFigure 1. Sketch map of the fabrication process. Nanofabrication of quartz can be achieved by low-destructive scanning on a target area and post-etching in a KOH solution.

To understand the mechanism of the low-destructive friction-induced nanofabrication, the microscopic structure of the scanned area of the quartz sample was detected by cross-sectional TEM (XTEM, JEOL JEM-2100 LaB6, JEOL Ltd., Tokyo, Japan) before and after KOH etching. The XTEM samples were prepared using a Quanta 3D FEG focused ion beam (FIB, FEI Company, Hillsboro, OR, USA) miller from the scanned area on quartz. In order to facilitate the FIB cutting across the scanned area, linescratch areas in the length of 200 μm were produced on the quartz samples by a nanoscratch tester (CSM Instruments, Peseux, Switzerland) with a spheral diamond tip having a radius of 20 μm. The low-destructive area was scratched under the normal load of 45 mN (the corresponding Hertzian contact pressure is 4.9 GPa), and the groove in a depth of 23 nm was scratched under the normal load of 95 mN.

Results and discussion

Results

Typical nanostructures produced on quartz by friction-induced selective etching

Figure 2 shows the AFM images of a wearless surface and typical nanostructures produced by friction-induced selective etching. The 1.5 × 3 μm2 marked area in Figure 2a was scanned under progressive loads from 0 to 15 μN. Since no deformation or removal of material was observed on the scanned area, the scanning can be considered as a wearless process [20]. Unlike the mechanical cutting, this wearless scanning can avoid severe mechanical deformation or the generation of crack on the fabrication area. After etching for 3 h in KOH solution at 293 K, the material in the scanned area was selectively removed to form a slope, where the fabrication depth D increased from 0 to 2.9 nm with the increase of normal load Fn from 0 to 15 μN, as shown in Figure 2b. Since the superficial layer on the fabrication area was selectively etched, possible mechanical destruction on the fabrication area could be further reduced.

thumbnailFigure 2. Maskless and low-destructive nanofabrication on quartz. (a) Low-destructive fabrication after scanning in 1.5× 3 μm2 area (line-marked) under progressive loads that ranged from 0 to 15 μN. (b) A slope produced by etching the area (a) in KOH solution for 3 h. (c) Five-step hierarchical structure produced by low-destructive scanning under Fn = 5 μN and etching for 3 h, where the scan size of each cycle was successively set as 7, 5.6, 4.2, 2.8 and 1.4 μm. (d) Chessboard-like patterns produced by low-destructive scanning on the selected area under Fn = 12 μN and etching for 3 h, where the scan size was 1 μm and the interval between adjoining scan centres was 2 μm.

When the scan size was adjusted during repeated scanning, the hierarchical structure (as shown in Figure 2c) with five stages can be fabricated. Here, under a constant load of 5 μN and with a fixed centre point, the scanned area was successively set as 7 × 7, 5.6 × 5.6, 4.2 × 4.2, 2.8 × 2.8 and 1.4 × 1.4 μm2. Consequently, the overlapped areas were scratched by repeated scans. After selective etching for 3 h, the hierarchical structure was created, where the fabrication depth D of the stages increased from 1.2 to 3.5 nm with the increase of the number of repeated scanning cycles from 1 to 5. By programming the tip trace, the demanded patterns can also be produced at a target area. The chessboard-like patterns in Figure 2d were produced by Fn = 12 μN and N = 1. The scan size was 1 μm, and the interval between adjoining scan centres was 2 μm. After etching for 3 h, the separated convexity with 2.1 nm in height was formed.

Effect of etching temperature on fabrication efficiency

Since all the mentioned fabrications were conducted at room temperature (293 K), it took about 3 h to finish selective etching of the scanned areas. To improve the efficiency of fabrication, selective etching of the scanned area was tested at various temperatures. As shown in Figure 3, the fabrication depth D versus etching time t curves showed a similar trend at different temperatures T, that is, keeping quasi-linear at the beginning and slowing down after a turning point. Such variation can be described by the following equation:

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/140/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/140/mathml/M1">View MathML</a>

(1)

thumbnailFigure 3. Effect of etching temperature on fabrication efficiency. The etching temperatures were set as 273, 293, 308 and 328 K. The quartz samples were scanned under the same normal load of 8 μN. Dashed lines were fitted by Equation 1.

It was found that Equation 1 can fit D ~ t curves well when T is above 293 K. Even for T = 273 K, the fitting curve by Equation 1 shows a similar variation trend as the measured one.

The results in Figure 3 also suggested that different from the continuous etching in traditional lithography, the selective etching of the scanned area mainly occurred before the turning point. After the turning point in each curve, the etching rate was very low and the etching depth was quite close to the final fabrication depth. Therefore, a linear fit was used for estimating the average etching rate η before the turning point in each curve. Clearly, the rise of etching temperature can significantly improve the etching rate. With the increase of temperature from 273 to 328 K, the etching rate rose from 0.17 to 7.0 nm/h under the scan load of 8 μN. However, since etching pits appeared on the original surface at the etching temperature of 328 K in this experiment, the highest etching temperature for efficiency improvement of fabrication should be limited to 328 K. It was also noted that even though the etching rate η varied dramatically with temperature, the final fabrication depth Df only relied on the scan load or the contact pressure. For instance, Df was always about 1.6 nm for Fn = 8 μN regardless of the etching temperatures. The results have implied that the fabrication is indeed friction-controlled.

Refabrication on the existing nanostructures

Results showed that there was a critical fabrication depth after single low-destructive scanning and post-etching (Figure 4). To produce deeper structures in a low-destructive way, refabrication was attempted at target areas on existing nanostructures. Firstly, a 5 × 5 μm2 nanostructure with a depth of 1.2 nm was produced by wearless scanning under Fn = 5 μN and selective etching (Figure 5a). The first refabrication was carried out by wearless scanning under 8 μN in the central 3.5 × 3.5 μm2 area, and the additional fabrication depth was 1.6 nm after etching (Figure 5b). The second refabrication was finished by wearless scanning under 5 μN in the central 2 × 2 μm2 area, and the added depth was 1.1 nm (Figure 5c). Lastly, the final fabrication depth in the central 2 × 2 μm2 area was about 3.9 nm. Therefore, refabrication can provide a feasible way for producing a deeper structure on quartz surface in nanoscale.

thumbnailFigure 4. Effect of contact pressure on the height of the fabrication area. The height h of the fabrication area after scanning under progressive contact pressure Pc. Dashed line, before KOH etching; solid line, after KOH etching.

thumbnailFigure 5. Refabrication on an existing structure of quartz surface. (a) Initial fabrication by low-destructive scanning under 5 μN on a 5 × 5 μm2 area and etching for 3 h at 293 K. (b) First refabrication by low-destructive scanning under 8 μN in the central 3.5 × 3.5 μm2 area and etching for 3 h at 293 K. (c) Second refabrication by low-destructive scanning under 5 μN in the central 2 × 2 μm2 area and etching for 3 h at 293 K.

Discussion

Effect of contact pressure on low-destructive nanofabrication

From Figure 2b, it was noted that the fabrication depth increased with the increase of the scanning load or the contact pressure on the wearless scanned area. To analyse the effect of contact pressure on nanofabrication in a more detailed manner, a scratch consisting of a wearless area and groove was performed on the quartz surface under progressive loads from 0 to 40 μN by AFM. As shown in Figure 4, the cross-sectional profile of the scanned area (dashed line) revealed that the surface was wearless below Fn = 15 μN, where the corresponding contact pressure Pc was below 5.1 GPa. With the further increase of the normal load from 15 to 40 μN, the groove was formed on the surface and the wear depth increased from 0 to 1.7 nm (dashed line). After etching for 6 h at 293 K, the etched thickness increased from 0 to 2.9 nm on the wearless scanned area and then tended to stabilise on the groove. Therefore, the upper limit of the contact pressure for low-destructive scanning was 5.1 GPa, and the critical fabrication depth was 2.9 nm after single low-destructive scanning and post-etching. The fabrication of deeper nanostructure can be realised through repeated scanning or refabrication process (Figures 2c and 5).

From the results in Figure 3, it seemed that the eventual fabrication depth was only dependent on the contact pressure during the wearless scanning process, regardless of the etching temperature. To verify it, the fabrication depths under various contact pressures and etching temperatures were tested, and the results were summarised in Table 1. It was found that under the same contact pressure, the fabrication depths were almost the same for various etching temperatures. With the increase of normal load from 5 to 12 μN (the corresponding Pc from 3.5 to 4.7 GPa), the fabrication depth increased from 1.2 to 2.1 nm. Clearly, the contact pressure Pc was the decisive factor for the eventual fabrication depth at various etching temperatures.

Table 1. Fabrication depths under various scanning loads and etching temperatures (nm)

In brief, the contact pressure played a significant role in the low-destructive friction-induced nanofabrication. With the increase of contact pressure, the fabrication depth increased from 0 to 2.9 nm before the yield of quartz surface. Since the superficial layer of the scanned area can be etched selectively, it was reasonable to speculate that such layer may reveal a unique etching behaviour and microstructure. To understand the fabrication mechanism of the proposed method, it is essential to analyse the reaction kinetics of selective etching and detect the microstructures of the scanned area.

The mechanism of the low-destructive nanofabrication

As shown in Figures 2 and 3, the proposed fabrication method was mainly based on the friction-induced selective etching on the scanned area. The etching reaction of quartz in KOH solution can be expressed as follows:

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/140/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/140/mathml/M2">View MathML</a>

(2)

which is a nucleophilic reaction. Based on chemical kinetics [21,22], the etching rate η can be described as follows:

<a onClick="popup('http://www.nanoscalereslett.com/content/8/1/140/mathml/M3','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/8/1/140/mathml/M3">View MathML</a>

(3)

where A is the frequency factor, c is the concentration of reactants, α is the reaction order, R is the gas constant, T is the etching temperature and Ea is the activation energy. Under a given etching temperature, the etching rate η was dependent only on A(c)α and Ea. To understand the role of contact pressure Pc in the friction-induced selective etching, the values of Ea and A(c)α under various Pc were estimated through fitting the experimental η ~ T curves in Figure 6 by Equation 3 (dashed line).

thumbnailFigure 6. Effect of normal loads on the etching rates at different etching temperatures. Etching rates η of scanned area produced under various normal loads of 5, 8 and 12 μN at different etching temperatures. The corresponding contact pressure was 3.5, 4.4 and 4.7 GPa, respectively. Dashed line is Arrhenius fitting of the etching rates.

As shown in Table 2, it was found that the contact pressure Pc had limited effect on the activation energy Ea but induced a large variation on the value of A(c)α. Since α is a constant in this erosion reaction, the dependence of the etching rate η on the contact pressure Pc should be mainly attributed to the variation of frequency factor A and the concentration of reactants c. As a stable oxide, there should be no further componential changes during the scanning process on the quartz surface. It was reported that the microscopic structure of solid had a significant effect on the chemical kinetics of fluid–solid reactions [23]. Therefore, it is logical to assume that the selective etching behaviours may be attributed to the structural changes of the scanned area on the quartz surface.

Table 2. Fitting results in Figure6

To further understand the fabrication mechanism of the proposed method, an XTEM observation was conducted on scratched quartz samples to detect the microscopic structures of the scanned area. Before KOH etching, the TEM observation revealed no visible deformation under the wearless scanned area (Figure 7a), while severe lattice distortion was observed under the groove (Figure 7b). After etching for 3 h at 293 K, there was still no visible damage on the wearless scanned area (Figure 7c), which further confirmed that the proposed method provided a low-destructive way for nanofabrication on quartz. At the same time, the distortion zone below the groove cannot be etched by KOH solution (Figure 7d). Combined with the results in Figure 4, because the formation of lattice distortion under groove did not help to increase the etching thickness, the selective etching of quartz might be related to other structural changes in the scanned area.

thumbnailFigure 7. XTEM observation of quartz samples produced by a nanoscratch tester. TEM images of (a) low-destructive scanned area and (b) groove before KOH etching. TEM images of (c) low-destructive scanned area and (d) groove after KOH etching. The centre of each scanned area was marked with a white arrow. The inset pictures are the AFM images of the low-destructive scanned area and groove, respectively.

Since amorphization usually occurs on the quartz surface during scratching and indentation [24,25], it is reasonable to speculate that amorphization during scanning/scratching at the superficial layer might have contributed to the selective etching of the quartz surface. To verify it, the etching rates of bulk amorphous SiO2 and crystal quartz were tested at 293 K. Before the tests, a gold film about 300 nm in thickness was deposited on half of each sample surface as a mask layer. After etching for 4 h in KOH solution and removal of the gold layers, there was no etching difference between the covered and exposed surfaces on the crystal quartz surface (Figure 8a). In contrast, a distinct step of 24 nm in height was formed on the amorphous SiO2 surface (Figure 8b). This has clearly demonstrated that amorphization can increase the etching rate of SiO2 in KOH. However, as the etching rate of the scanned area (about 1.65 nm/h at 4.7 GPa or 12 μN) was much lower than that of the bulk amorphous SiO2 (about 6 nm/h), it is most probably that the amorphization of the quartz surface after scanning under 4.7 GPa would be incomplete. Nevertheless, the friction-induced amorphization could be an acceptable explanation to the selective etching of the quartz surface although it is difficult, if not impossible, to clearly show the extremely thin (0 to approximately 3 nm), superficial and incompletely amorphized layer using the current XTEM technique and equipment.

thumbnailFigure 8. Comparison of etching results on monocrystalline quartz and amorphous SiO2. (a) No difference between covered surface and exposed surface on monocrystalline quartz after etching for 4 h at 293 K. (b) Exposed surface of amorphous SiO2 was etched evidently at 293 K.

Based on the mentioned discussions, the possible fabrication mechanism can be proposed as follows. In the KOH solution, the defective Si-O nets of friction-induced amorphous SiO2 can help the KOH solutes to preferentially diffuse into the scanned area and induce both higher concentrations of reactants c and a large number of colliding between reactants A in the scanned area [21,26]. According to the collide theory, the KOH etching of the scanned area depends on the total collision number between the KOH solutes and Si-O microscopic structure. Compared to the original surface, the scanned area has a faster etching rate and will be etched selectively. The etched depth may be decided by the thickness of the amorphous layer, and the etching rate is determined by the extent of amorphization. Higher contact pressure and repeated scanning can provide more gross energy W for the interaction between the tip and the quartz surface and consequently lead to faster etching rates and deeper structures. For example, under the conditions of N = 1 and Fn = 5 μN, the fabrication depth D was 1.2 nm and the etching rate η was 0.68 nm/h. The gross energy W dissipated during the scanning was calculated as 2.0 × 10−9 J [27]. To produce a deeper structure in depth of 1.6 nm, it needed 3.2 × 10−9 J by increasing Fn to 8 μN or 4.0 × 10−9 J by scanning one more cycle. At the same time, the etching rate η increased to 1.05 nm/h by increasing Fn to 8 μN, which meant that the increment of η was 0.31 nm/h per 10−9 J. As a comparison, the etching rate η increased to 1.21 nm/h by scanning one more cycle and the corresponding increment of η was 0.27 nm/h per 10−9 J. Therefore, compared to the number of scanning cycles, it seems that the scan load reveals a relatively stronger effect on the etching depth and etching rate. Nevertheless, the competitive relation between the load and scanning cycles should be investigated more thoroughly in the future.

In summary, a novel nanofabrication method based on friction-induced selective etching is proposed, by which three-dimensional nanostructures on demand can be created on a target quartz surface. This method enables nanofabrication more easily than photolithography with etching masks. This proximal probe technique makes it possible to fabricate at specified locations and to measure the dimensions of nanostructures with high precision. To overcome the critical etching thickness in a single fabrication flow, refabrication can be conducted on the existing structures. The friction-induced process under low contact pressure facilitates nanoscale material removal in a low-destructive way. Considering such advantages and potential applications, this method can open up new opportunities for future nanofabrication.

Conclusions

In conclusion, we have presented a maskless and low-destructive method for nanofabrication on quartz based on AFM. Various nanostructures including slopes, hierarchical stages and chessboard-like patterns can be fabricated by changing the loading mode and programming the scan traces. Under the given experimental conditions, the surface of the scanned area is wearless below the critical contact pressure 5.1 GPa and the etched thickness of the scanned area goes up from 0 to 2.9 nm with the increase of contact pressure. Even though the rise of etching temperature can improve the efficiency of fabrication, the fabrication depth is controlled by the contact pressure and scanning cycles. Refabrication can be realised to overcome the critical etching thickness in a single fabrication flow. TEM observation shows that the formation of distortion does not contribute to the etching thickness. Analysis suggests that the fabrication mechanism could be attributed to the selective etching of friction-induced amorphous layer on the quartz surface. The proposed method based on friction-induced selective etching will provide new opportunities for nanofabrication on quartz surface.

Abbreviations

AFM: Atomic force microscopy; FIB: Focused ion beam; TEM: Transmission electron microscopy; XTEM: Cross-sectional TEM.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

CS and BY realised the fabrication experiments and acquired the original data in this paper. XL and HD did the TEM observation and analysis. LQ and SC have made substantial contributions to the concept and design of this paper. All authors read and approved the manuscript.

Acknowledgments

The authors are grateful for the financial support from the National Basic Research Program (2011CB707604), Natural Science Foundation of China (90923017 and 51175441) and from the Royal Society under the China-UK Science Networks Scheme. Chengfei Song wants to thank the 2011 Doctoral Innovation Funds of Southwest Jiaotong University and the Fundamental Research Funds for the Central Universities.

References

  1. Castellanos-Gomez A, Agrait N, Rubio-Bollinger G: Carbon fibre tips for scanning probe microscopy based on quartz tuning fork force sensors.

    Nanotechnology 2010, 21:145702. PubMed Abstract | Publisher Full Text OpenURL

  2. Oh J, Chang YW, Kim HJ, Yoo S, Kim DJ, Im S, Park YJ, Kim D, Yoo KH: Carbon nanotube-based dual-mode biosensor for electrical and surface plasmon resonance measurements.

    Nano Lett 2010, 10:2755-2760. PubMed Abstract | Publisher Full Text OpenURL

  3. Ilchenko VS, Savchenkov AA, Byrd J, Solomatine I, Matsko AB, Seidel D, Maleki L: Crystal quartz optical whispering-gallery resonators.

    Opt Lett 2008, 33:1569-1571. PubMed Abstract | Publisher Full Text OpenURL

  4. Jackson MJ: Microfabrication and Nanomanufacturing. Florida: CRC Press; 2006. OpenURL

  5. Srinivasan C, Hohman JN, Anderson ME, Weiss PS, Horn MW: Sub-30-nm patterning on quartz for imprint lithography templates.

    Appl Phys Lett 2008, 93:083123-083125. Publisher Full Text OpenURL

  6. Zhang X, Liu ZW: Superlenses to overcome the diffraction limit.

    Nat Mater 2008, 7:435-441. PubMed Abstract | Publisher Full Text OpenURL

  7. Grigorescu AE, Hagen CW: Resists for sub-20-nm electron beam lithography with a focus on HSQ: state of the art.

    Nanotechnology 2009, 20:292001. PubMed Abstract | Publisher Full Text OpenURL

  8. Zheng K, Wang C, Cheng YQ, Yue Y, Han X, Zhang Z, Shan Z, Mao SX, Ye M, Yin Y, Ma E: Electron-beam-assisted superplastic shaping of nanoscale amorphous silica.

    Nat Commun 2010, 1:24. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  9. Xie XN, Chung HJ, Sow CH, Wee ATS: Nanoscale materials patterning and engineering by atomic force microscopy nanolithography.

    Mat Sci Eng R 2006, 54:1-48. Publisher Full Text OpenURL

  10. Yoshino M, Ogawa Y, Aravindan S: Machining of hard-brittle materials by a single point tool under external hydrostatic pressure.

    J Manuf Sci Eng 2005, 127:837-845. Publisher Full Text OpenURL

  11. Baumgärtel T, Borczyskowski CV, Graaf H: Detection and stability of nanoscale space charges in local oxidation nanolithography.

    Nanotechnology 2012, 23:095707. PubMed Abstract | Publisher Full Text OpenURL

  12. Yu BJ, Dong HS, Qian LM, Chen YF, Yu JX, Zhou ZR: Friction-induced nanofabrication on monocrystalline silicon.

    Nanotechnology 2009, 20:303. OpenURL

  13. Song CF, Li XY, Yu BJ, Dong HS, Qian LM, Zhou ZR: Friction-induced nanofabrication method to produce protrusive nanostructures on quartz.

    Nanoscale Res Lett 2011, 6:310. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  14. Yu BJ, Li XY, Dong HS, Qian LM: Mechanical performance of friction-induced protrusive nanostructures on monocrystalline silicon and quartz.

    Micro & Nano Lett 2012, 7:1270-1273. PubMed Abstract | Publisher Full Text OpenURL

  15. Seydel E, Berger H, Hildebrandt G, Bradaczek H: Lattice damages in quartz crystal blanks influence on the resonator properties and on the X-ray measurement. In Frequency Control Symposium and Exposition, 2004:Proceedings of the 2004 IEEE International:23–27 August 2004; Montreal. New York: IEEE Conference Publications; 2004:109-115. OpenURL

  16. Guo LJ: Nanoimprint lithography: methods and material requirements.

    Adv Mater 2007, 19:495-513. OpenURL

  17. Torii A, Sasaki M, Hane K, Okuma S: A method for determining the spring constant of cantilevers for atomic force microscopy.

    Meas Sci Technol 1996, 7:179-184. Publisher Full Text OpenURL

  18. Guzzo PL, Raslan AA, De Mello JDB: Ultrasonic abrasion of quartz crystals.

    Wear 2003, 255:67-77. Publisher Full Text OpenURL

  19. Johnson KL: Contact Mechanics. Cambridge: Cambridge University Press; 1985. OpenURL

  20. Bhushan B: Nano- to microscale wear and mechanical characterization studies using scanning probe microscopy.

    Wear 2001, 251:1105-1123. Publisher Full Text OpenURL

  21. Upadhyay SK: Chemical Kinetics and Reaction Dynamics. New York: Springer; 2006. OpenURL

  22. Deleuze M, Goiffon A, Ibanez A, Philippot E: Solvent influence on kinetics and dissolution mechanism of quartz in concentrated basic media (NaOH, KOH, LiOH).

    J Sol St Chem 1995, 118:254-260. Publisher Full Text OpenURL

  23. Bhatia SK, Perlmutter DD: The effect of pore structure on fluid–solid reactions: application to the SO2-lime reaction.

    AICHE J 1981, 27:226-234. Publisher Full Text OpenURL

  24. Kailer A, Nickel KG, Gogotsi YG: Raman microspectroscopy of nanocrystalline and amorphous phases in hardness indentation.

    J Raman Spectrosc 1999, 30:939-946. Publisher Full Text OpenURL

  25. Ekwinska MA, Rymuza Z: New approach to estimate nanowear test results through nanoindentation test.

    Microelectron Eng 2010, 87:1404-1409. Publisher Full Text OpenURL

  26. Mehrer H: Diffusion in Solids: Fundamentals, Methods, Materials, Diffusion-Controlled Processes: Springer Series in Solid-State Sciences 155. New York: Springer; 2007. OpenURL

  27. Yu BJ, Qian LM, Dong HS, Yu JX, Zhou ZR: Friction-induced hillocks on monocrystalline silicon in atmosphere and in vacuum.

    Wear 2010, 268:1095-1102. Publisher Full Text OpenURL