Open Access Nano Express

Passivation mechanism of thermal atomic layer-deposited Al2O3 films on silicon at different annealing temperatures

Yan Zhao1, Chunlan Zhou1*, Xiang Zhang2, Peng Zhang3, Yanan Dou4, Wenjing Wang1, Xingzhong Cao3, Baoyi Wang3, Yehua Tang1 and Su Zhou1

Author Affiliations

1 Key Laboratory of Solar Thermal Energy and Photovoltaic System, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190, China

2 Institute of Microelectronics, Chinese Academy of Sciences, Beijing, 100029, China

3 Key Laboratory of Nuclear Analysis Techniques, Institute of High Energy Physics, Chinese Academy of Sciences, Beijing, 100049, China

4 Shanghai Institute of Technical Physics, Chinese Academy of Sciences, Shanghai, 200083, China

For all author emails, please log on.

Nanoscale Research Letters 2013, 8:114  doi:10.1186/1556-276X-8-114

The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/8/1/114


Received:14 November 2012
Accepted:20 February 2013
Published:2 March 2013

© 2013 Zhao et al; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Thermal atomic layer-deposited (ALD) aluminum oxide (Al2O3) acquires high negative fixed charge density (Qf) and sufficiently low interface trap density after annealing, which enables excellent surface passivation for crystalline silicon. Qf can be controlled by varying the annealing temperatures. In this study, the effect of the annealing temperature of thermal ALD Al2O3 films on p-type Czochralski silicon wafers was investigated. Corona charging measurements revealed that the Qf obtained at 300°C did not significantly affect passivation. The interface-trapping density markedly increased at high annealing temperature (>600°C) and degraded the surface passivation even at a high Qf. Negatively charged or neutral vacancies were found in the samples annealed at 300°C, 500°C, and 750°C using positron annihilation techniques. The Al defect density in the bulk film and the vacancy density near the SiOx/Si interface region decreased with increased temperature. Measurement results of Qf proved that the Al vacancy of the bulk film may not be related to Qf. The defect density in the SiOx region affected the chemical passivation, but other factors may dominantly influence chemical passivation at 750°C.

Keywords:
Thermal ALD; Al2O3 film; Passivation; Annealing.

Background

Excellent surface passivation is required to realize the next-generation industrial silicon solar cells with high efficiencies (>20%). Silicon oxide films thermally grown at very high temperatures (>900°C) are generally used to suppress the surface recombination velocities (SRVs) to as low as 10 cm/s and applied in front- and rear-passivated solar cells. In recent years, atomic layer-deposited (ALD) aluminum oxide (Al2O3) thin films have been investigated as candidate surface passivation materials [1-3]. ALD Al2O3 thin films enable perfect passivation similar to high-quality thermally grown silicon oxide and can be prepared at low temperatures (<300°C). Given that the silicon bulk lifetime is sensitive to high temperatures, ALD Al2O3 has a natural advantage over thermal SiO2 in terms of integration into industrial cell processes. Extensive experiments on Al2O3 film applications in photovoltaics have demonstrated that Al2O3 can passivate both low-doped n- and p-type silicons. ALD Al2O3 also exerts a better passivation effect on p+-type emitters than other dielectric layers. Very recently, Hoex et al. [4] found that Al2O3 can also enable high-surface passivation for n+-type emitters within the range of 10 to 100 Ω/sq.

Low SRVs for dielectric passivation are attributed to two passivation mechanisms: chemical passivation and field-effect passivation [5,6]. Chemical passivation (e.g., thermal SiO2 films) decreases the interface defect density (Dit). In dielectric layers such as SiNx and Al2O3, a high fixed charge density (Qf) near the silicon surface generates an electric field, repelling electrons or holes to reduce carrier recombination on the surface. Thermal ALD Al2O3 reportedly acquires a negative Qf as high as 1013 cm-2 with sufficiently low Dit (about 1011 eV-1 cm-2) after annealing [7,8]. Experiments have shown that the fixed charge located near the Al2O3/Si interface is related to some types of defect proposed as Al vacancies, interstitial O, and interstitial H in Al2O3 film or at the interface [5]. Positron annihilation is a useful technique for vacancy-type defect investigation. Edwardson et al. [9] performed Doppler broadening of annihilation radiation (DBAR) studies and found an interface that traps positrons in an ALD Al2O3 sample, which significantly differed from the S-W result of DBAR in the current work. The discrepancy can be attributed to the different annealing conditions.

In the present study, the effect of annealing temperature on the surface passivation characteristics of Al2O3 films was investigated. Corona charging experiments were performed to distinguish between chemical and field-effect passivation mechanisms. Slow positron beam DBAR measurements were performed to probe the defects in Al2O3 films annealed at 300°C, 500°C, and 750°C.

Methods

Experimental

Aluminum oxide films were deposited onto a 1 to 10 Ωcm p-type Czochralski Si (100) substrate using the thermal ALD method. The 420-μm-thick double-sided polished wafers were cleaned using the RCA standard method and dipped in 1% hydrofluoric acid for 1 min before deposition to remove the native oxide layer on the surface. Thermal ALD Al2O3 films about 23 nm thick were prepared with Al(CH3)3 and H2O as reactants at 250°C. The optimum deposition temperature that led to the highest as-deposited effective lifetime was determined to be 250°C. Double faces were deposited to prepare symmetrical Al2O3/Si/Al2O3. After deposition, the samples were annealed at different temperatures (300°C to 750°C) for 10 min in air. Annealing in air was performed because it closely resembles the firing condition in the manufacturing process of solar cells. The effective lifetimes of these samples were measured before and after annealing, and a negative Qf of the Al2O3 films was obtained using corona charging measurements using Semilab WT2000 (Semilab Semiconductor Physics Laboratory Co. Ltd., Budapest, Hungary). DBAR measurements of the three annealed samples (300°C, 500°C, and 750°C) were performed to investigate the defects in the films. A slow beam of positrons that had variable energies (<10 keV) was used to obtain information from the thin films.

Corona charging measurement

The effective lifetime of the annealed samples was measured using the microwave photoconductive decay method. Corona charging experiments were performed to determine Qf[10]. As a positive charge was added stepwise to the film surface using a corona, the effective lifetime decreased until the positive charge was totally balanced with the negative fixed charge and then increased because the positive charge also enabled field-effect passivation. Thus, the negative Qf was equal to the amount of added corona charge density (Qc) at the minimum point of the τeff-Qc curve. The surface passivation mechanism comprises chemical passivation and field-effect passivation. Thus, the minimum effective lifetime was also obtained to determine the role of chemical passivation because the effective lifetime is mainly controlled by chemical passivation when the negative charge is neutralized. Figure 1 shows the typical corona charging measurement for the as-deposited Al2O3/Si sample. Qf before annealing was determined as -3.5 × 1011 cm-2 from the curve, and the lowest lifetime was recorded as 42.8 μs to characterize the chemical passivation of the sample.

thumbnailFigure 1. Typical corona charging measurement for the as-deposited Al2O3/Si sample.

DBAR measurement

Positron annihilation is used to analyze defects in oxides and semiconductors [11-13]. When a positron is implanted into a matter, it annihilates an electron and emits two γ rays. The energy of γ rays varies around 511 keV because of the energy and momentum conservation of the positron-electron system given by the relation Eγ = 511 ± ΔEγ keV, where ΔEγ is the Doppler shift. Even a slight change in momentum can lead to a large shift of energy. The S and W parameters were calculated to characterize Doppler broadening. The S parameter is defined as the ratio of the mid-portion area to the entire spectrum area. The W parameter is the ratio of the wing portion to the entire area. With increased concentration of vacancy in solid, the positron is mostly trapped and annihilates low-momentum electrons, leading to a narrow Doppler peak with a high S parameter. W parameters are higher and S parameters are lower when annihilation of the core electrons of atoms occurs. Given that the momentum distribution of electrons varies in different types of defect, changes in S-W plots can also characterize the types and distributions of defects in the films [14].

Results and discussion

Influence of annealing temperature on surface passivation

The effective lifetimes of the samples annealed at different temperatures in air are shown in Figure 2. The effective lifetime change is the ratio of the effective lifetime after annealing to that of the effective lifetime before annealing. The ratio was used instead of the actual value because the effective lifetimes of the six as-deposited samples (before annealing) were not strictly identical, which rendered meaningless the observation of the absolute value of the effective lifetime after annealing. The effective lifetime change initially increased with increased annealing temperature and then rapidly decreased below unity. This result indicated that passivation collapsed at annealing temperatures higher than 700°C. The optimum annealing temperature was around 500°C in air, which was higher than the reported 400°C to 450°C when annealed in N2[15].

thumbnailFigure 2. Influence of annealing temperature on Al2O3 passivation.

Corona charging measurement was performed to observe the field-effect and chemical passivation mechanisms. Qf and the lowest lifetime can be extracted from the resulting measurement curve, as described in the section ‘Corona charging measurement.’ Figure 3a shows the measured data, and Figure 3b shows the Qf and the minimum effective lifetime change (lowest lifetime after annealing vs. as-deposited value) as a function of the annealing temperature. Qf significantly increased to 1012 cm-2 after annealing at 400°C compared with Qf of about 1011 cm-2 before annealing (Figure 1). Qf increases from 2.5 × 1011 cm-2 at 300°C, reaches the highest point of about 2.5 × 1012 cm-2 at 500°C, and thereafter decreases to 8 × 1011 cm-2. Qf did not significantly change when the annealing temperature was higher than 600°C. Meanwhile, the effective lifetime of the sample annealed at 300°C was slightly enhanced (Figure 2), i.e., 1.2 times greater than that of the as-deposited sample. This result indicated that Qf of 2.5 × 1011 cm-2 did not significantly affect surface passivation. The chemical passivation variation at 300°C to 500°C was similar to Qf based on the minimum lifetime in the corona charging measurement. The chemical passivation effect increased with increased annealing temperature before 500°C and quickly decreased thereafter. This variation was related to the hydrogen release from the film found by Dingemans [16].

thumbnailFigure 3. Corona charging measurement of samples. (a) Before and after annealing. (b) Fixed charge density and minimum effective lifetime change after annealing at different temperatures.

Notably, Qf reached 1012 cm-2 after annealing at 750°C, and this value was almost one magnitude higher than that of the as-deposited sample. However, the effective lifetime was low (Figure 2) because of the poor chemical passivation at 750°C in Figure 3b of the minimum lifetime change value. Therefore, chemical passivation was a prerequisite in achieving excellent surface passivation.

The approximate effective lifetime τeff of a symmetrically passivated silicon wafer can be expressed as 1/τeff = 1/τb + 2Seff/W, where τb is the bulk lifetime, W is the crystalline silicon (c-Si) wafer thickness, and Seff is the effective SRV. The bulk lifetime was estimated at about 1 ms using the I2 passivation method to determine Seff. Figure 4 shows that Seff was linear with 1/Qf2 for negative Qf values >6.8 × 1011 cm-2, except for the sample annealed at 750°C. The linear relationship of samples annealed between 400°C and 700°C indicated that passivation was dominated by field-effect passivation (Qf). Thus, the sample annealed at 300°C (dislocated line) indicated that Qf of 2.5 × 1011 cm-2 was too low to dominate surface passivation, which confirmed the conclusion drawn from Figure 3. This result also agreed with the simulation of Hoex et al. for p-type c-Si [5]. Based on the dislocation of the sample annealed at 750°C, a high interface trap density was inferred to destroy the field-effect passivation and increase Seff.

thumbnailFigure 4. Plot of Seff and 1/Qf2 with the linear fit for annealing temperatures. The annealing temperatures are between 400°C to 700°C (Qf> 6.8 × 1011cm-2). The slightly bent linear fit line was due to the logarithmic X- and Y-axes.

DBAR analysis at different annealing temperatures

DBAR analysis was performed at the Beijing Slow Positron Beam (Institute of High Energy Physics, Chinese Academy of Sciences, Beijing, China). A positron beam generated from a Na22 radioactive source was used, and the energy of the positrons was modulated between 0 and 10 keV to obtain the incident energy profile of positron annihilation. The energy region of the S parameter ranged from 510.24 to 511.76 keV, whereas the W parameter ranged from 504.2 to 508.4 and from 513.6 to 517.8 keV. Thus, the total energy region of the peak ranged from 504.2 to 517.8 keV.

The vacancy defects in the alumina films were mainly Al vacancies, O vacancies, and clusters of vacancies (voids) [13,17,18]. O vacancies with a positive charge (F+- and F2+-type defects) have difficulty trapping positrons because of their identical charge. Nobuaki Takahashi et al. [19] calculated the defect energetics using first-principle calculations and found that the oxygen vacancy has a much higher formation energy than the aluminum vacancy [19], further supporting the view that few positrons are trapped in charged O vacancies. Therefore, Al and neutral O vacancies (F center) are crucial to the annihilation results in the present study. Figure 5a,b shows the measured S and W parameters as a function of the incident positron energy for samples annealed at different temperatures for 10 min. In Figure 5a, the shapes of the three curves are similar because the deposition conditions of the three films were identical, and the substrates on which these films grew were also the same. The first one or two points were recorded at low positron incident energy (<0.5 eV), which can be ascribed to the trap states near the film surface. The S parameter of the injection energy was approximately between 0.5 and 2 keV, which mainly represented the annihilation events occurring in the aluminum oxide film. Figure 5a shows that the S parameter initially increased rapidly, which indicated a higher vacancy defect density of the inner oxide film than that of the surface. A decrease was observed beyond 1 keV, demonstrating that the S parameter of the Al2O3/Si interface was lower than that of the Al2O3 films. The lower S parameter can be attributed to the positron annihilation with high-momentum electrons of oxygen at the interface. This result was probably due to the SiOx layer grown between the aluminum oxide and Si substrate, which reportedly has an important function in excellent surface passivation [6,20,21]. The S parameter continued to increase after 2 keV with increased incident energy because larger portions of positrons were injected into the silicon substrate. The S parameter in the substrate was much higher than that in the oxide film because of the different chemical environments of annihilation. The S parameter did not reach a constant value before 10 keV, which implied that positrons with 10 keV energy cannot completely penetrate the Si substrate far from the oxide layer. The S-E plot in Figure 5a also shows that the S parameter in Al2O3 films (about 1 keV) evidently decreased with increased annealing temperature because of the decreased density of trap vacancies in the Al2O3 films. The W parameter was more sensitive to the chemical environment of the annihilation site. The larger W and smaller S parameters indicated more positrons annihilating core electrons. Thus, the smallest S and largest W parameters of the sample annealed at 750°C (Figure 5a,b) implied that the Al2O3 films had been compressed at this temperature with the lowest vacancy defect density and that the film structure probably did not change.

thumbnailFigure 5. Doppler broadening spectroscopy of S-W parameters vs. positron incident energy. (a)S and (b)W parameters vs. positron incident energy for samples annealed at different temperatures for 10 min. (c)S-W plot for samples annealed at different temperatures for 10 min.

The S and W parameters of the same incident energy were plotted in one graph, as shown in Figure 5c. The S vs. W diagrams of monolithic materials present clusters of points because all S or W parameters are almost the same [14]. For example, in one type of defect, the S and W parameters may vary with the positron incident energy, and the S-W plot extends to the line passing the data point of the bulk region without defect [13,14]. The slope of the line changes with the layers of different compositions and defect types. Thus, the annealed sample consisted of a three-layered structure in which each curve consisted of three extended line segments (Figure 5c). This finding corresponded with the S-E curve analysis result, which also suggested that the film contained a layer different from Al2O3 and Si near the interface. No significant interface response in the S-W result has been previously observed [9], and the discrepancy may be a result of the different annealing environments (air vs. N2). Annealing in air may lead to a thicker interface oxide (SiOx) resulting in more evident responses in the DBRA result.

The different slopes of the Al2O3 segment of the three samples indicated that the defect types or chemical environments of these samples were different. The three lines crossed one another to avoid passing through a single point of bulk sample without defects, indicating that each of the samples had more than two types of defect. As mentioned in the section ‘DBAR analysis at different annealing temperatures,’ the S parameter was mainly influenced by Al and neutral O vacancies. Thus, residual C during deposition and O-H bond content also possibly influenced the S-W line slope. Residual C varied with the annealing temperature and may have thus influenced the environment of Al vacancies, although further investigations are needed.

A thinner sample was prepared to understand the microstructure of the Al2O3/Si samples, which showed a three-layered structure in DBAR analysis. The 6-nm-thick sample was obtained using thermal ALD and observed by transmission electron microscopy (TEM). The result in Figure 6 shows three layers, namely Si, Al2O3, and Si-Al2O3 interface layers, which have been reported for nonstoichiometric silica (SiOx) [6,20,21].

thumbnailFigure 6. TEM image of aluminum oxide films prepared using thermal ALD.

The fitted S parameter can be clearly analyzed in different parts of a film to gain accurate information from DBAR spectroscopy. In this study, the energy of injected positrons had a different distribution at the positron incident energy of the X-axis in the S-E plot. The positrons also reached different layers of the film. Thus, the S parameter of each point in the S-E plot contained integrated information on multiple layers. The S parameter was separated in different layers, and the density/type of vacancies was analyzed at different positions in the film. The S-E plot was fitted using the VEPFIT program to calculate the S parameter from different layers using a four-layered mode, which corresponded to the surface/Al2O3/SiOx/Si structure observed by TEM. The obtained S parameter is shown in Figure 7. The S parameter in the Al2O3 films decreased with increased temperature, indicating that the vacancy density in the Al2O3 film decreased with increased annealing temperature. The S parameter was much lower in the SiOx layer than that in Al2O3 and the Si substrate. The S parameter also decreased with increased annealing temperature, which probably corresponded with the dominant Pb defect that decreased with increased annealing temperature [22].

thumbnailFigure 7. Fitted S parameters for different positions in Al2O3 films using the VEPFIT program.

Al vacancies, O interstitials, and H interstitials are proposed as the reasons for the negative Qf of Al2O3[23,24]. The measured Qf in Figure 3 and information on Al vacancies in Figure 7 were considered in analyzing the effect of Al vacancy density on the negative fixed charge Qf. With increased annealing temperature from 300°C to 500°C, the increase in Qf was opposite to the decrease in Al vacancy in the bulk film. Thus, Qf may not be related with Al vacancies in the Al2O3 films. The measured minimum effective lifetime in Figure 3 and S parameters of SiOx interface in Figure 7 were correlated, and the decrease in vacancy of SiOx was coincident with the enhanced chemical passivation at annealing temperatures lower than 500°C. However, the chemical passivation breakdown at 750°C cannot be explained: among the samples annealed at 300°C and 750°C, the chemical passivation at 750°C was the poorest, but the defect density at the interface region still decreased. The functions of interstitial atoms (O or H) near the interface require further investigation.

Conclusions

Qf did not significantly affect the passivation at a low annealing temperature (300°C). The interface trap density markedly increased at a high annealing temperature (750°C) and failed at surface passivation even at a high Qf. Positron annihilation techniques were used to probe the vacancy-type defects. A three-layered microstructure of thermal ALD Al2O3 films on Si substrate was found. The Al defect density in the bulk film and the vacancy density near the interface decreased with increased temperature based on the fitted S parameter at different positions in the Al2O3 films. The Al vacancy of the bulk film was not related to Qf based on the Qf measurement results. The effects of interstitial atoms on Qf need further investigation. The defect density in the SiOx region may affect chemical passivation, but other factors may also influence chemical passivation particularly beyond 500°C.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

YZ participated in the design of the study, carried out the fabrication of Al2O3 films, performed the statistical analysis, as well as drafted the manuscript. CLZ designed the study to find the relation between negative-charged Al vacancy and Qf. XZ carried out the TEM analysis and participated in the Qf test. YND performed the film deposition. PZ, XZC, and BYW provided the Beijing Slow Positron Beam and performed the positron BDAR analysis. WJW, YHT, and SZ co-wrote the paper. All authors read and approved the final manuscript.

Acknowledgments

This study was supported by the National High Technology Research and Development Program of China (grant no. 2011AA050515) and the National Basic Research Program of China (grant no. 2012CB934204). The authors are grateful to Dr. Cao for the DBAR measurements at the Beijing Slow Positron Beam, Institute of High Energy Physics, Chinese Academy of Sciences.

References

  1. Schmidt J, Werner F, Veith B, Zielke D, Bock D, Brendel R, Tiba V, Poodt P, Roozeboom F, Li A, Cuevas A: Surface passivation of silicon solar cells using industrially relevant Al2O3 deposition techniques.

    Photovoltaics Int 2010, 10:42-48. OpenURL

  2. Rothschild A, Vermang B, Goverde H: Atomic layer deposition of Al2O3for industrial local Al back-surface field (BSF) solar cells.

    Photovoltaics Int 2011, 13:92-101. OpenURL

  3. Schmidt J, Merkle A, Brendel R, Hoex B, van de Sanden MCM, Kessels WMM: Surface passivation of high-efficiency silicon solar cells by atomic-layer-deposited Al2O3.

    Progr Photovoltaics Res Appl 2008, 16(6):461-466. Publisher Full Text OpenURL

  4. Hoex B, van de Sanden MCM, Schmidt J, Brendel R, Kessels WMM: Surface passivation of phosphorus-diffused n+-type emitters by plasma-assisted atomic-layer deposited Al2O3.

    Phys Status Solidi 2012, 6(1):4-6. Publisher Full Text OpenURL

  5. Hoex B, Gielis JJH, van de Sanden MCM, Kessels WMM: On the c-Si surface passivation mechanism by the negative-charge-dielectric Al2O3.

    J Appl Phys 2008, 104(11):113703. Publisher Full Text OpenURL

  6. Terlinden NM, Dingemans G, van de Sanden MCM, Kessels WMM: Role of field-effect on c-Si surface passivation by ultrathin (2–20 nm) atomic layer deposited Al2O3.

    Appl Phys Lett 2010, 96(11):112101. Publisher Full Text OpenURL

  7. Manchanda L, Morris MD, Green ML, van Dover RB, Klemens F, Sorsch TW, Silverman PJ, Wilk G, Busch B, Aravamudhan S: Multi-component high-K gate dielectrics for the silicon industry.

    Microelectron Eng 2001, 59(1):351-359. OpenURL

  8. Jeon IS, Park J, Eom D, Hwang CS, Kim HJ, Park CJ, Cho HY, Lee JH, Lee NI, Kang HK: Post-annealing effects on fixed charge and slow/fast interface states of TiN/Al2O3/p-Si metal-oxide-semiconductor capacitor.

    Jpn J Appl Phys 2003, 42(3):1222-1226. OpenURL

  9. Edwardson CJ, Coleman PG, Li TTA, Cuevas A, Ruffell S: Positron annihilation studies of the AlOx/SiO2/Si interface in solar cell structures.

    J Appl Phys 2012, 111(5):053515. Publisher Full Text OpenURL

  10. Hoex B, Schmidt J, van de Sanden MCM, Kessels WMM: Crystalline silicon surface passivation by the negative-charge-dielectric Al2O3. In Photovoltaic Specialists Conference, May 11–16 2008. PVSC'08. 33rd IEEE. San Diego, CA. Piscataway: IEEE; 2008:1-4. OpenURL

  11. Xu J, Somieski B, Hulett LD, Pint BA, Tortorelli PF, Suzuki R, Ohdaira T: Microdefects in Al2O3 films and interfaces revealed by positron lifetime spectroscopy.

    Appl Phys Lett 1997, 71(21):3165-3167. Publisher Full Text OpenURL

  12. Uedono A, Kiyohara M, Yasui N, Yamabe K: Suppression of oxygen diffusion by thin Al2O3films grown on SrTiO3 studied using a monoenergetic positron beam.

    J Appl Phys 2005, 97(3):033508. Publisher Full Text OpenURL

  13. Muthe KP, Sudarshan K, Pujari PK, Kulkarni MS, Rawat NS, Bhatt BC, Gupta SK: Positron annihilation and thermoluminescence studies of thermally induced defects in α-Al2O3 single crystals.

    J Phys D Appl Phys 2009, 42:105405. Publisher Full Text OpenURL

  14. Somieski B, Hulett LD, Xu J, Pint BA, Tortorelli PF, Nielsen B, Asoka-Kumar P, Suzuki R, Ohdaira T: Microstructure of thermally grown and deposited alumina films probed with positrons.

    Phys Rev B 1999, 59(10):6675. Publisher Full Text OpenURL

  15. Vermang B, Goverde H, Lorenz A, Uruena A, Vereecke G, Meersschaut J, Cornagliotti E, Rothschild A, John J, Poortmans J, Mertens R: On the blistering of atomic layer deposited Al2O3 as Si surface passivation. In Photovoltaic Specialists Conference (PVSC), June 19–24 2011 37th IEEE. Seattle: IEEE; 2011:003562-003567. OpenURL

  16. Dingemans G, Einsele F, Beyer W, van de Sanden MCM, Kessels WMM: Influence of annealing and Al2O3 properties on the hydrogen-induced passivation of the Si/SiO2interface.

    J Appl Phys 2012, 111(9):093713. Publisher Full Text OpenURL

  17. Chang H, Choi Y, Kong K, Ryu BH: Atomic and electronic structures of amorphous Al2O3.

    Chem Phys Lett 2004, 391(4–6):293-296. OpenURL

  18. Perevalov TV, Tereshenko OE, Gritsenko VA, Pustovarov VA, Yelisseyev AP, Park C, Han JH, Lee C: Oxygen deficiency defects in amorphous Al2O3.

    J Appl Phys 2010, 108(1):013501. Publisher Full Text OpenURL

  19. Takahashi N, Mizoguchi T, Tohei T, Nakamura K, Nakagawa T, Shibata N, Yamamoto T, Ikuhara Y: First principles calculations of vacancy formation energies in Σ13 pyramidal twin grain boundary of α-Al2O3.

    Mater Trans 2009, 50(5):1019-1022. Publisher Full Text OpenURL

  20. Li TTA, Ruffell S, Tucci M, Mansoulié Y, Samundsett C, De Iullis S, Serenelli L, Cuevas A: Influence of oxygen on the sputtering of aluminum oxide for the surface passivation of crystalline silicon.

    Sol Energ Mater Sol Cell 2011, 95(1):69-72. Publisher Full Text OpenURL

  21. Dou YN, He Y, Huang CY, Zhou CL, Ma XG, Chen R, Chu JH: Role of surface fixed charge in the surface passivation of thermal atomic layer deposited Al2O3 on crystalline-Si.

    Appl Phys A Mater Sci Process 2012, 109(3):673-677. Publisher Full Text OpenURL

  22. Yu RS, Ito K, Hirata K, Sato K, Zheng W, Kobayashi Y: Positron annihilation study of defects and Si nanoprecipitation in sputter-deposited silicon oxide films.

    Chem Phys Lett 2003, 379(3):359-363. OpenURL

  23. Matsunaga K, Tanaka T, Yamamoto T, Ikuhara Y: First-principles calculations of intrinsic defects in Al2O3.

    Phys Rev B 2003, 68(8):085110. OpenURL

  24. Peacock P, Robertson J: Behavior of hydrogen in high dielectric constant oxide gate insulators.

    Appl Phys Lett 2003, 83(10):2025-2027. Publisher Full Text OpenURL