Open Access Nano Review

Improvement in dielectric and mechanical performance of CaCu3.1Ti4O12.1 by addition of Al2O3 nanoparticles

Chompoonuch Warangkanagool1 and Gobwute Rujijanagul2*

Author Affiliations

1 Department of Physics, Faculty of Science, Naresuan University, Phitsanulok, 65000, Thailand

2 Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai, 50200, Thailand

For all author emails, please log on.

Nanoscale Research Letters 2012, 7:68  doi:10.1186/1556-276X-7-68

The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/7/1/68


Received:19 September 2011
Accepted:5 January 2012
Published:5 January 2012

© 2012 Warangkanagool and Rujijanagul; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

The properties of CaCu3.1Ti4O12.1 [CC3.1TO] ceramics with the addition of Al2O3 nanoparticles, prepared via a solid-state reaction technique, were investigated. The nanoparticle additive was found to inhibit grain growth with the average grain size decreasing from approximately 7.5 μm for CC3.1TO to approximately 2.0 μm for the unmodified samples, while the Knoop hardness value was found to improve with a maximum value of 9.8 GPa for the 1 vol.% Al2O3 sample. A very high dielectric constant > 60,000 with a low loss tangent (approximately 0.09) was observed for the 0.5 vol.% Al2O3 sample at 1 kHz and at room temperature. These data suggest that nanocomposites have a great potential for dielectric applications.

Keywords:
nanocomposites; dielectric properties; microstructure; mechanical property

Background

CaCu3Ti4O12 [CCTO] is an interesting dielectric material which exhibits a high dielectric constant over 10,000 at room temperature and shows temperature independence over the temperature range from approximately 100 to 400 K [1-3]. Since the discovery of this material by Subramanian et al. [1], CCTO has been widely studied to further understand and improve its properties. The CCTO crystal has a cubic symmetry with an Im3 space group. In the CCTO lattice, the TiO6 octahedra are tilted which results in a doubling of the perovskite-like structure, involved in the planar square arrangement of the oxygen around the copper ions [4]. The CCTO ceramics exhibit an electrically heterogeneous structure involving mobile-charged species in terms of the Maxwell-Wagner relaxation [5]. Internal interfaces in the polycrystalline CCTO give rise to the polarization in the insulating grain boundary and at the semiconducting grains which is well explained by the internal barrier layer capacitor [IBLC] model [6,7]. To improve the dielectric properties further, many cations have been introduced into CCTO, including Co, Zr, Fe, Sc, and Nb on the B site and substitution of La and Eu at the A site [4,8-12]. Although some of these additives resulted in a reduction of the loss tangent, most additives also reduced the dielectric constant. Fang et al. proposed that Cu stoichiometry can affect the electrical properties of the CCTO ceramics, [13] while Kwon et al. reported that both Cu- and Ti-deficient CCTO presented a higher dielectric constant than undoped CCTO [14]. Recently, many authors have reported on the properties of composites between CCTO and other materials such as BaTiO3, SrTiO3, ZnNb2O6, and polystyrene [15-17]. However, the properties of composites formed by adding nanocomposites to CCTO have still not been widely investigated. In the present work, a new nanocomposite system between CCTO (with non-stoichiometric composition) and Al2O3 nanoparticles was fabricated. We demonstrate that the dielectric behavior of the composites can be significantly improved by the addition of these nanoparticles. Some other properties of the nanocomposites were also investigated and reported.

Experimental procedure

It has been proposed that Cu stoichiometry is related to the dielectric response [13,14]. Fang et al. [13] reported that Cu-excessive CCTO samples showed improved densification and dielectric behaviors. In the present work, Cu-excessive CCTO ceramics in a composition of CaCu3.1Ti4O12.1 [CC3.1TO] were fabricated. Our studies indicate that this composition exhibited a good densification and dielectric response (data not shown). The samples were fabricated using the solid-state mixed oxide method. Reagent grade CaCO3, CuO, and TiO2 powders were used as starting materials. The mixture of these powders was ground for 24 h in ethanol using zirconia grinding media. The suspension was then dried and subsequently calcined at 900°C for 8 h with a heating rate of 5°C/min. The calcined CC3.1TO powders were mixed with (0.5, 1, and 2 vol.%) Al2O3 nanoparticles (40 nm average particle size) and 1% polyvinyl alcohol [PVA] binder and were ball-milled in ethanol for 12 h using the same method as mentioned earlier. The slurry was then dried and sieved to a fine powder. The mixed powders were uniaxially pressed into pellets at a pressure of 60 MPa. The PVA binder was burnt out at 550°C with a heating rate of 1°C/min. Finally, the pellets were sintered at 1,025°C for 6 h with a heating rate of 5°C/min. The sintered pellets were investigated for phase formation by X-ray diffraction [XRD]. Density of the sintered samples was measured using the Archimedes method with distilled water as the fluid medium. The microstructures of the sintered samples were characterized using a scanning electron microscope [SEM], and the average grain size was determined using the linear intercept method. For the electrical measurement, silver paste was applied to both sides of the circular faces of the ceramics, then dried at 600°C for 15 min, and cooled naturally to room temperature. The dielectric constant and dielectric loss were then measured using a LCZ meter. The mechanical properties (hardness) of various sintered samples were studied using a Knoop microhardness tester. Indentations were applied to the polished surfaces with 0.3- and 0.5-kg loads and with an indentation period of 15 s.

Results and discussion

Phase formation

The XRD results for the sintered ceramics containing up to 2 vol.% Al2O3 are illustrated in Figure 1. All of the patterns were similar to the unmodified CCTO diffraction peaks and were consistent with the results reported previously [18]. The peaks of the second phases such as Cu2O and CuO could not be observed in the XRD patterns [14]. Further, no peak was observed for the Al2O3 phase in any of the XRD patterns. This may be due to the amount of Al2O3 additive which was too little to be detected at the sensitivity level of the XRD instrument.

thumbnailFigure 1. XRD patterns of the surfaces of the CC3.1TO and CC3.1TO-Al2O3 pellets.

Densification, microstructure, and hardness behavior

The plot of density as a function of Al2O3 volume fraction is shown in Figure 2. The density slightly increased with the increasing amounts of Al2O3 up to 0.5 vol.% and then decreased for the 2 vol.% sample. The reduction in density for the higher Al2O3 samples suggests that the sintering mechanism of the samples was not complete. To obtain the best densification for compositions > 0.5 vol.% Al2O3, higher sintering temperatures or longer soaking times would be required.

thumbnailFigure 2. Density and average grain size as Al2O3 volume fraction function for CC3.1TO and CC3.1TO-Al2O3 nanocomposites. Inset shows Knoop hardness value as a function of Al2O3 content of the samples.

Figure 3 displays the SEM micrographs of the as-sintered surfaces of CC3.1TO-Al2O3 nanocomposites. An agglomeration of Al2O3 nanoparticles was not explicitly observed, implying that the processing method produced a reasonably uniform distribution of the nanoparticles in the matrix of the composites. The surfaces of the CC3.1TO samples showed a duplex microstructure consisting of coarse grains (average grain size of approximately 20 μm) and fine grains (average grain size of approximately 1 μm) located around the coarse grains. This characteristic indicates an abnormal grain growth in the microstructure of the samples. The formation of a copper oxide liquid phase (in Cu-excessive CCTO), as suggested by Kim et al. [19], may be the main reason for the formation of abnormal grain growth since the present samples have a Cu-excessive CCTO composition. The liquid phase enhanced nucleation of abnormal grains and the abnormal grains were then formed after sintering. Similar results have been reported previously for Cu-excessive CCTO ceramics [14,20]. The average grain sizes of the coarse grains were found to decrease with the additive (e.g., average grain size of the coarse grains was approximately 3 μm for the 2 vol.% sample; Figure 3b). However, the average grain size of the fine grains remained unchanged for higher Al2O3 content samples. Overall, the average grain size, calculated from coarse and fine grains, decreased from approximately 7.5 μm for the unmodified sample to approximately 2.0 μm for the 2 vol.% sample (Figure 2). The decrease in the average grain size is most likely caused by the mismatch of the different components. Further, Al2O3 might segregate to the grain boundaries which could prevent grain boundary movement during the sintering process and, as a result, inhibit grain growth.

thumbnailFigure 3. SEM micrographs of as-sintered surfaces of the CC3.1TO-Al2O3 nanocomposites. (a) CC3.1TO and (b) CC3.1TO and 2 vol.% Al2O3.

The Knoop hardness values of the samples as a function of Al2O3 content are illustrated in the inset of Figure 2. The Knoop hardness data reveal that the additive improved the hardness values. The maximum hardness value in this work was 9.8 GPa (for the 1 vol.% sample) which is comparable to the value reported by Puchmark et al. for the PZT-Al2O3 nanocomposites. The improvement in the mechanical properties is most likely due to the nanoparticles reinforcing the grain boundaries and acting as effective pins against microcrack propagation [21]. Moreover, the enhancement of hardness can be related to the reduction in grain size, i.e., small grain size samples gave a higher measured hardness.

Dielectric properties

Figure 4 shows the dielectric constants versus the frequency at room temperature for the CC3.1TO and CC3.1TO-Al2O3 pellets. Compared with the CC3.1TO sample, a significant improvement in the dielectric constant of the CC3.1TO-Al2O3 samples was observed. For the CC3.1TO sample, the dielectric constant was 11,000 (measured at 1 kHz and at room temperature) which is close to the values reported previously [1,2]. The CC3.1TO sample also exhibited nearly dielectric-frequency independence over the frequency range of 0.1 to 500 kHz. Further, the dielectric constant increased reaching a value > 60,000 at 1 kHz for the 0.5 vol.% sample then decreased for further increases in the Al2O3 content. For the 2 vol.% sample, however, the dielectric-frequency curve showed a weak frequency dispersion of the dielectric constant. The reduction in the dielectric constant for the samples which were doped with more than 0.5 vol.% Al2O3 may be due to the fact that composites with higher additive amounts (Al2O3 > 0.5 vol.%) also had higher structural heterogeneity. Moreover, the formation of an impurity phase may have caused a reaction between Al2O3 and CC3.1TO which could not be detected using the XRD technique [22], but it might also have contributed to the reduction in the dielectric constant. Plots of the loss tangent versus the frequency of the CC3.1TO and CC3.1TO-Al2O3 pellets at room temperature are presented in the inset of Figure 4. The loss tangent-frequency curve of the CC3.1TO ceramic exhibited a weak frequency dispersion for a narrow frequency range (1 to 50 kHz). However, after adding the additive, the loss tangent significantly decreased at low frequencies (< 1 kHz) which resulted in a wider range of frequency stability (10 Hz to 10 kHz). Further, the loss tangent decreased from 0.21 for the CC3.1TO ceramics to 0.09 for the 0.5 vol.% sample (at 1 kHz). A further slight decrease in the loss tangent was observed for additional additive amounts. The decrease in loss tangent shows a reduced conductivity of the CC3.1TO-Al2O3 samples. This result could be related to changes in the transport behavior due to an increase in resistivity at the grain boundaries where the additive nanoparticles predominantly segregated.

thumbnailFigure 4. Dielectric constants versus frequency at room temperature for the CC3.1TO and CC3.1TO-Al2O3 pellets. The inset shows the loss tangent versus the frequency of the ceramic pellets at room temperature.

Figure 5 shows the dielectric constant values as a function of temperature at various frequencies for the CC3.1TO and CC3.1TO-Al2O3 pellets. The CC3.1TO sample showed a high dielectric constant (εr approximately 10,000) with temperature and frequency stability from room temperature to 60°C. After adding the additive, however, a significant improvement in the dielectric behavior was observed. The 0.5 vol.% sample showed a very high dielectric constant > 60,000 (at 1 kHz) which was nearly temperature-independent for the temperature range of approximately 35°C to 110°C. Compared to the CC3.1TO sample, this sample also displayed a pronounced frequency dependence of the dielectric constant especially for temperatures < 125°C. Moreover, the dielectric-temperature curve of the 0.5 vol.% presented a broad flat curve at high frequencies (> 10 kHz). For higher additive amounts (Al2O3 > 0.5 vol.%), the dielectric constant decreased with the increasing additives. Further, the dielectric frequency dispersion for the Al2O3 nanoparticle sample with 2 vol.% was not as strong for temperatures < 112°C. The loss tangent values as a function of temperature at various frequencies for the samples are illustrated in the insets of Figure 5. For the CC3.1TO sample, the loss tangent value was 0.21 and was stable with temperature as well as frequency from room temperature to approximately 41°C. The 0.5 vol.% sample had a loss tangent value lower than 0.10 for room temperature to approximately 50°C. From the (IBLC) model, the apparent dielectric constant (<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/68/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/68/mathml/M1">View MathML</a>) can be related to the microstructure parameters by the formula [23]:

thumbnailFigure 5. Temperature dependence of the dielectric dispersion at various frequencies. (a) CC3.1TO, (b) CC3.1TO with 0.5 vol.% Al2O3, (c) CC3.1TO with 1 vol.% Al2O3, and (d) CC3.1TO with 2 vol.% Al2O3.

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/68/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/68/mathml/M2">View MathML</a>

(1)

where d is the grain size, t is the thickness of the grain boundary (barrier width), and εgb is the internal dielectric constant of the barrier material. Since the grain size of the present samples decreased with the increasing additive, Equation 1 predicts that the higher dielectric constant for the 0.5 vol.% sample is not related to the grain size, but it may be connected to a change in the grain boundary characteristics such as εgb and t after adding the additive. The reason for the change of grain boundary characteristic is still unclear, but it is possible that the Al2O3 nanoparticles had a reaction with the matrix of the CC3.1TO, and as a result, the formation of Al-metal oxide phases at the grain boundary produced other products in small amounts which could not be detect by XRD [22]. However, the higher density for the 0.5 vol.% sample can be explained by the observed higher dielectric constant in the present work.

Conclusions

CC3.1TO-Al2O3 nanocomposites were fabricated for the first time. The samples were prepared using a solid-state reaction. The CC3.1TO ceramics showed a duplex microstructure, consisting of coarse and fine grains, while the nanocomposites showed mainly fine grains in their microstructure due to the fact that the additive inhibited grain growth. The additive also enhanced the hardness value especially for the 1 vol.% sample. However, the CC3.1TO and 0.5 vol.% Al2O3 showed a high dielectric constant with a strong dielectric frequency dispersion especially at low temperatures and also had a lowered loss tangent value, as compared with other samples. These results indicate that the addition of nanoparticles may be an alternative method to improve the dielectric behavior in some other giant dielectric materials.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

CP carried out the fabrication of CC3.1TO, XRD characterization, SEM characterization, density measurement, grain size measurement, dielectric properties measurement, and Knoop hardness measurement. GR designed the whole experimental procedure and related analyses. All authors read and approved the final manuscript.

Acknowledgements

This work was supported by The Thailand Research Fund (TRF), Thailand's Office of the Higher Education Commission (OHEC), and Faculty of Science and Graduate School, Chiang Mai University. The authors would like to thank Prof. Dr. Tawee Tunkasiri for his help in many facilities.

References

  1. Subramanian MA, Li D, Duran N, Reisner BA, Sleight AW: High dielectric constant in ACu3Ti4O12 and ACu3Ti3FeO12 phases.

    J Solid State Chem 2000, 151:323-325. Publisher Full Text OpenURL

  2. Ramirez AP, Subramanian MA, Gardel M, Blumberg G, Li D, Vogt T, Shapiro SM: Giant dielectric constant response in a copper-titanate.

    Solid State Commun 2000, 115:217-220. Publisher Full Text OpenURL

  3. Homes CC, Vogt T, Shapiro SM, Wakimoto S, Ramirez AP: Optical response of high-dielectric-constant perovskite-related oxide.

    Science 2001, 293:673-676. PubMed Abstract | Publisher Full Text OpenURL

  4. Leret P, Fernandez JF, de Frutos J, Fernandez-Hevia D: Nonlinear I-V electrical behaviour of doped CaCu3Ti4O12 ceramics.

    J Eur Ceram Soc 2007, 27:3901-3905. Publisher Full Text OpenURL

  5. Lunkenheimer P, Bobnar V, Pronin AV, Ritus AI, Volkov AA, Loidl A: Origin of apparent colossal dielectric constants.

    Phys Rev B 2002, 66:052105. OpenURL

  6. Sinclair DC, Adams TB, Morrison FD, West AR: CaCu3Ti4O12: one-step internal barrier layer capacitor.

    Appl Phys Lett 2002, 80:2153-2155. Publisher Full Text OpenURL

  7. Adams TB, Sinclair DC, West AR: Characterization of grain boundary impedances in fine- and coarse-grained CaCu3Ti4O12 ceramics.

    Adv Mater 2002, 14:1321-1323. Publisher Full Text OpenURL

  8. Chung SY, Lee SI, Choi JH, Choi SY: Initial cation stoichiometry and Q2 current-voltage behavior in Sc-doped calcium copper titanate.

    Appl Phys Lett 2006, 89:191907. Publisher Full Text OpenURL

  9. Kwon S, Huang CC, Patterson EA, Cann DP: The effect of Cr2O3, Nb2O5 and ZrO2 doping on the dielectric properties of CaCu3Ti4O12.

    Mater Lett 2008, 62:633-636. Publisher Full Text OpenURL

  10. Li T, Chen Z, Chang F, Hao J, Zhang J: The effect of Eu2O3 doping on CaCu3Ti4O12 varistor properties.

    J Alloy Compd 2009, 484:718-722. Publisher Full Text OpenURL

  11. Chiodelli G, Massarotti V, Capsoni D, Bini M, Azzoni CB, Mozzati MC, Lupotto P: Electric and dielectric properties of pure and doped CaCu3Ti4O12 perovskite materials.

    Solid State Commun 2004, 132:241-246. Publisher Full Text OpenURL

  12. Feng L, Tang X, Yan Y, Chen X, Jiao Z, Cao G: Decrease of dielectric loss in CaCu3Ti4O12 ceramics by La doping.

    Phys Status Solidi A 2006, 203:R22-R24. Publisher Full Text OpenURL

  13. Fang TT, Mei LT, Ho HF: Effects of Cu stoichiometry on the microstructures, barrier-layer structures, electrical conduction, dielectric responses, and stability of CaCu3Ti4O12.

    Acta Mater 2006, 54:2867-2875. Publisher Full Text OpenURL

  14. Kwon S, Huang CC, Subramanian MA, Cann DP: Effects of cation stoichiometry on the dielectric properties of CaCu3Ti4O12.

    J Alloy Compd 2009, 473:433-436. Publisher Full Text OpenURL

  15. Almeida AFL, Fechine PBA, Góes JC, Valente MA, Miranda MAR, Sombra ASB: Dielectric properties of BaTiO3 (BTO)-CaCu3Ti4O12 (CCTO) composite screen-printed thick films for high dielectric constant devices in the medium frequency (MF) range.

    Mater Sci Eng B 2004, 111:113-123. Publisher Full Text OpenURL

  16. Yu H, Liu H, Hao H, Luo D, Cao M: Dielectric properties of CaCu3Ti4O12 ceramics modified by SrTiO3.

    Mater Lett 2008, 62:1353-1355. Publisher Full Text OpenURL

  17. Du G, Li W, Fu Y, Chen N, Yin C, Yan M: An investigation on the solid-state reactions in CaCu3Ti4O12-ZnNb2O6 system.

    Mater Res Bull 2008, 43:2504-2508. Publisher Full Text OpenURL

  18. Ni L, Chen XM, Liu XQ, Hou RZ: Microstructure-dependent giant dielectric response in CaCu3Ti4O12 ceramics.

    Solid State Commun 2006, 139:45-50. Publisher Full Text OpenURL

  19. Kim KM, Lee JH, Lee KM, Kim DY, Riu DH, Lee SB: Microstructural evolution and dielectric properties of Cu-deficient and Cu-excess CaCu3Ti4O12 ceramics.

    Mater Res Bull 2008, 43:284-291. Publisher Full Text OpenURL

  20. Shao SF, Zhang JL, Zheng P, Wang CL: Effect of Cu-stoichiometry on the dielectric and electric properties in CaCu3Ti4O12 ceramics.

    Solid State Commun 2007, 142:281-286. Publisher Full Text OpenURL

  21. Puchmark C, Rujijanagul G, Jiansirisomboon S, Tunkasiri T, Vittayakorn N, Comyn TP, Milne SJ: Mechanical property evaluation of PZT/Al2O3 composites prepared by a solid state mixed oxide method.

    Curr Appl Phys 2006, 6:323-326. Publisher Full Text OpenURL

  22. Puchmark C, Jiansirisomboon S, Rujijanagul G, Comyn TP, He JY, Milne SJ: Properties of lead zirconate-alumina 'Nanocomposites'.

    Mater Res Bull 2007, 42:1269-1277. Publisher Full Text OpenURL

  23. Zuo R, Feng L, Yan Y, Chen B, Cao G: Observation of giant dielectric constant in CdCu3Ti4O12 ceramics.

    Solid State Commun 2006, 138:91-94. Publisher Full Text OpenURL