Open Access Nano Express

Confident methods for the evaluation of the hydrogen content in nanoporous carbon microfibers

Mario Culebras1*, Antonio Madroñero2, Andres Cantarero1, José Maria Amo2, Concepción Domingo3 and Antonio López4

Author Affiliations

1 Materials Science Institute, University of Valencia, 46071 Valencia, PO Box 22085, Spain

2 CENIM, , Av. Gregorio del Amo 8, 28040 Madrid, Spain

3 Instituto de Estructura de la Materia (CSIC), , C/ Serrano 121, 28006 Madrid, Spain

4 CIEMAT, , 04200 Tabernas, Almeria, Spain

For all author emails, please log on.

Nanoscale Research Letters 2012, 7:588  doi:10.1186/1556-276X-7-588


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content


Received:25 August 2012
Accepted:5 September 2012
Published:24 October 2012

© 2012 Culebras et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Nanoporous carbon microfibers were grown by chemical vapor deposition in the vapor-liquid solid mode using different fluid hydrocarbons as precursors in different proportions. The as-grown samples were further treated in argon and hydrogen atmospheres at different pressure conditions and annealed at several temperatures in order to deduce the best conditions for the incorporation and re-incorporation of hydrogen into the microfibers through the nanopores. Since there are some discrepancies in the results on the hydrogen content obtained under vacuum conditions, in this work, we have measured the hydrogen content in the microfibers using several analytical methods in ambient conditions: surface tension, mass density, and Raman measurements. A discussion on the validity of the results obtained through the correlation between them is the purpose of the present work.

Keywords:
Raman dispersion; Chemical vapor deposition; Nanoporous materials

Background

Hydrogen is known to be the most common element in the Milky Way, and it represents 74% in content, followed by helium (24%), oxygen (1%), and carbon (0.4%) [1]. It is found in a large amount of chemical compounds, particularly in carbon-rich and organic materials. Atomic hydrogen is unstable, and it is usually found in combination with other elements (hydrocarbons, polymers, water, etc.) or as a diatomic molecule. Hydrogen is used, as least in prototypes, in fuel cells, which is a very important issue in energy storage [2]. Another interesting application is thermoelectricity; the electrical conductivity and the Seebeck coefficient can be engineered by changing the hydrogen content [3].

On average, the storage capacity of hydrogen in carbon nanostructures is of the order of 1.5 wt.%, although the storage capacity can significantly change with the desorption temperature [4] or hydrostatic pressure [5]. For instance, single-walled carbon nanotubes (CNTs) show a hydrogen uptake of 5 to 10 wt.% at 133 K and 40 kPa [6]. It has also been shown that single- or multi-walled CNTs adsorbed a hydrogen amount of 3 to 4 wt.% at room temperature but at 10 MPa [7,8].

An important problem in this research field is to have a confident measurement of the hydrogen content. This is not an easy matter because of the depletion of hydrogen when the fibers are in a vacuum environment [9], and many of the used techniques need vacuum conditions. Techniques such as elastic recoil detection analysis show unsatisfactory sensitivity since it works with the samples placed into a high vacuum chamber [10]. It was also difficult to obtain confident results in the measurement of the hydrogen content by reflection electron energy loss spectroscopy; the measurement error was not lower than 20% [11].

In this work, we study carbon fibers grown by chemical vapor deposition, a method which allows obtaining a good-quality material under a reasonable cost. The vapor growth produces filaments of some centimeters of length and microfibers with a length smaller than 100 μm. The manufacturing process of vapor-grown carbon fibers (VGCFs) has been previously described in the literature [12]. They have been prepared incorporating metallic particles of group VII to the gas flow entering into the reactor. Although VGCFs synthesized with a metallic catalyst have received special attention in many fields because of their controllable structure and attractive mechanical and electrical properties [7,13], one of the most important applications of VGCFs in the near future will be as hydrogen storage materials, mainly in the form of nanowires because of its large surface for hydrogen incorporation. In this work, we have studied the hydrogen content in VGCFs, both filaments and microfibers, restricting the analysis to techniques which do not need vacuum, and try to select the more confident technique for measuring the hydrogen content in porous materials, particularly in carbonaceous specimens.

Methods

Crystal growth and sample preparation

The precursors for the growth of samples A to C, and D and E are basically hydrogen, methane, ethane, and benzene. They have been grown in vapor-liquid-solid mode in a furnace at 1,323 K within a quartz ampule. The microfibers were prepared using small iron particles as catalyst. These particles came from minute drops of ferrocene solved in alcohol. Once evaporated, they were placed in a hot hydrogen environment. In this way, they have been turned into minute chips of active metallic iron. The growth temperature of our furnace was 1,323 K in all cases. As a result, minute fiber-type flying seeds (FS) are created. If the catalyst particles are deliberately placed on a substrate, carbonaceous microfilaments or filaments grown on a substrate (FGS) of some centimeters of length are created on the substrate. The description of the raw atmosphere for the sample preparation is given in Table 1. The five samples (A to E) have received further treatments to analyze the incorporation and refilling of hydrogen (producing samples F to I). The raw atmosphere, temperature, and pressure conditions for the fabrication of samples F to I are shown in Table 2.

Table 1. Set of samples grown as explained in the text

Table 2. Samples obtained after further treatment on samples A and B (FGS)

Thermogravimetric measurements

In order to carry out a rough comparison between the samples, thermogravimetric measurements (TGA) were performed using a TGA system. The samples were kept in Ar atmosphere, and the heating velocity was 2 K/min between 323 and 473 K and 20 K/min between 473 and 1,023 K.

Surface energy measurements

In the present study, we used the contact angle measured in a sessile drop test as the way to evaluate the surface area. Following Fowkes [14], the following relationship exists between the contact angle θ and the surface energies γL and γS of the liquid and solid, respectively:

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M1">View MathML</a>

(1)

where the upper index p and d are used to distinguish the polar and dispersive components ( <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M2">View MathML</a>; <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M3','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M3">View MathML</a>) of the surface energy. By using two liquids, a polar liquid (for instance, glycerol: <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M4','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M4">View MathML</a> mN/m and <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M5','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M5">View MathML</a> mN/m) and a non-polar liquid (as vaseline oil: <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M6','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M6">View MathML</a> mN/m), we were able to obtain <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M7','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M7">View MathML</a> and <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M8','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M8">View MathML</a> from the measurements of the contact angles with the VGCFs.

Density measurements

In the work of Madroñero et al. [15], it was shown that the external part of the VGCFs is composed of two phases: an amorphous matrix and graphitic platelets. The hydrogen adsorption takes place basically in the amorphous phase because the accumulation of hydrogen is more intensive in defects [16]. According to that, it is reasonable to assume that the relationship between the amount of stored hydrogen and the density should not be very different from the established relation for amorphous hydrogenated films [17]. It can be accepted that the relation between density and hydrogen content follows the Gaussian expression [18]:

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M9','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M9">View MathML</a>

(2)

where ρ is the density in g/cm3 and x is the hydrogen content in wt.%. As the first step, the mass of each sample was determined. Then, the volume was established using a gas pycnometer with helium. The hydrogen content of each sample has been calculated from Equation 2.

Raman measurements

A Raman confocal microscope (Renishaw 2000, Renishaw, Gloucestershire, UK) has been used in the analysis. It was provided with a Leica microscope (Leica, Solms, Germany), a nitrogen-cooled charge couple device, and an air-cooled Ar ion laser (514.5 nm) as excitation source. A ×50 objective has been utilized. The spectra of all the samples have been evaluated by the own software of the system.

Results and discussion

Figure 1A,B shows two images obtained by scanning electron microscopy (SEM). The fibers observed in these images were fabricated from methane and hydrogen (samples A and D following Table 1): the first image shows a FGS fiber, while the second, a FS fiber.

thumbnailFigure 1. SEM images of a filament grown on a substrate (A) and a microfiber-type flying seed (B).

Thermogravimetric tests correspond to three representative samples, one as grown (A), a second sample overcharged (J(A)), and a third one recharged after clearing (H(G)). The objective of these tests was to check if some irregularities in the curve of weight loss may suggest complexity in the outgassing mechanism. Figure 2 shows the thermograms of samples A, J(A), and H(G). As can be observed, there is no preferential temperature for the hydrogen taking off in the outgassing process. This fact may suggest a simple process of outgassing without a hydrogen diffusion mechanism [19], which has been widely described in the scientific literature.

thumbnailFigure 2. Thermogravimetric records. Samples A (solid black line), H(G) (dashed red line), and J(A) (dotted blue line).

The Raman spectra of carbonaceous materials consist of two main broad peaks known as <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M10','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M10">View MathML</a>-band ( <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M11','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M11">View MathML</a>stands for ‘graphite’) and <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M12','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M12">View MathML</a>-band (proportional to the level of ‘disorder’ or defects) [20]. The <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M13','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M13">View MathML</a>-band is located around 1,575/cm, and it is assigned to a doubly degenerated deformation vibration of the hexagonal ring corresponding to the E2g mode of graphite with <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M14','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M14">View MathML</a> crystal symmetry. The <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M15','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M15">View MathML</a>-band is located around 1,355/cm, and it is an indication of the crystal size [21]. The existence of the <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M16','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M16">View MathML</a>-band points out the existence of disorder-induced scattering. During the process of carbonization of polymers through thermal treatment at increasing temperatures, the intensity of the <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M17','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M17">View MathML</a>-band decreases (indicating recrystallization). When the <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M18','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M18">View MathML</a>-band disappears completely, the material has turned into a well-ordered graphite [22] material with no defects (obviously, a neglected defect concentration).

Therefore, we may suggest that the variation of the ratio between the intensity of the <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M19','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M19">View MathML</a> and <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M20','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M20">View MathML</a>peaks indicates an alteration in the graphitic character of the material [23]. For this reason, the relationship between the intensity of the peaks <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M21','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M21">View MathML</a>has been generally used to predict the elastic modulus of carbon thin films [24] and CNTs [25]. This relationship points out the alteration of crystalline perfection.

We have correlated the surface energy and density measurements with that of the Raman ratio of the <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M22','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M22">View MathML</a>intensities. Figure 3 shows the correlation between the surface energy measure with the sessile drop method as indicated in the previous section with that of the Raman ratio <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M23','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M23">View MathML</a>. Although the line is a linear square fit, there is no evidence of a linear correlation, but we can roughly observe an increase of the surface tension when the quantity of defects (the decrease of the <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M24','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M24">View MathML</a> intensity in the Raman spectra) is decreased. A first point to be noticed in the figure is that the FGS samples have a smaller surface tension (27−35mN/m) than that of the FS samples (57 to 62 mN/m), nearly one half, and a smaller defect concentration. By looking at Table 2, we can realize that the increase in the annealing temperature and the outgassing time on sample A (F(A) and G(A)) increases enormously the surface tension and probably the recrystallization. Annealing sample A (J(A)) in a hydrogen atmosphere and high pressure increases the number of defects and the surface tension. In sample B, however, the annealing with hydrogen at high pressure (K(B)) produces nearly no effect in the surface tension or recrystallization. The same happens for samples H(G) (refilling) and I(H) (annealed in vacuum in a residual hydrogen atmosphere); the surface tension and number of defects is very close to sample G(A).

thumbnailFigure 3. Correlation between surface tension and the Raman ratio<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M26','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M26">View MathML</a>.

In Figure 4, the change of <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M27','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M27">View MathML</a>as a function of the hydrogen content derived from the density measurements using Equation 2 is shown. Given the good linear correlation between the ratio <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M28','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M28">View MathML</a>and the hydrogen content, we have made a linear fit. Although it crosses zero because we left only the slope as fitting parameter in the linear fit, it may not necessarily cross zero. There is probably, at some point, a saturation effect given a finite value of the Raman ratio for zero hydrogen content since a sample without hydrogen is not necessarily perfect. From the comparison of the results for samples A, B, and C shown in Figure 4, it is observed that the feedstock atmosphere composition have an observable but not very remarkable influence on the hydrogen content in the case of FGS; to a methane atmosphere precursor corresponds a hydrogen content of 0.19%, to a benzene precursor corresponds a hydrogen content of 0.22%, and to methane-ethylene, 0.15% of hydrogen. In FS fiber samples (D and E), the hydrogen content is smaller than in the FGS. In the case of sample G(A), the desorption is more pronounced because besides the temperature, the vacuum per se produces an outtake of hydrogen in this type of fibers [26]. The small difference between the hydrogen content of samples A and J(A) suggests that the refilling from a high-pressure atmosphere of hydrogen is not effective, and the sample to be recharged was not activated for hydrogen adsorption [7]. The same conclusion is valid for the comparison between K(B) and B. The more unexpected change is that observed in the variation from G(A) to H(G). The question is that G(A) was submitted to an annealing with a temperature higher than 500°C. It is well established that spangles of graphene after an annealing around 500°C releases all the fluctuant hydrogen, and the C-H bonds resting in the final material are very stable because they are sp3 bonds [27].

thumbnailFigure 4. Correlation between<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M30','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M30">View MathML</a>and the hydrogen content derived from density measurements. The line is a linear fit, keeping only the slope as a parameter. Actually, it does not necessarily cross zero (perfect sample with no defects).

Conclusions

From the analysis and comparison of the different techniques used to measure the hydrogen content in the carbonaceous materials, we can conclude that the density and Raman measurements are the most confident techniques since there is a clear linear correlation between the hydrogen content extracted from the density measurements and the <a onClick="popup('http://www.nanoscalereslett.com/content/7/1/588/mathml/M31','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/588/mathml/M31">View MathML</a>ratio of the Raman peaks. In any of these techniques, vacuum is needed for the measurements, and we can ignore the discussion or the evaluation on the effect of the vacuum conditions on the final results. From the results, we can also conclude that the samples with more hydrogen content are those grown bubbling hydrogen in benzene: B compared with C and A (FGS), and E compared to D (FS).

Competing interests

The authors declare that they have no competing interest.

Authors’ contributions

AM grew the carbon fibers. MC did the thermal treatments. JMA carried out the density and surface tension measurements. CD performed the Raman measurements. AL performed the TGA measurements. Finally, AC made the Raman analysis and curve fits. All authors read and approved the final manuscript.

Acknowledgements

We thank the financial support given by the project CSD2010-0044, which belongs to the ‘Consolider Ingenio’ Programme of the Ministry of Finances and Competitiveness.

References

  1. Croswell K: Alchemy of the Heavens. New York: Anchor; 1996. OpenURL

  2. Biĉáková O, Straka P: Production of hydrogen from renewable resources and its effectiveness.

    Int J Hydrogen Energy 2012, 37:11563. Publisher Full Text OpenURL

  3. Madroñero A, Robla J, García-Hierro J, Martín-Gonzalez MS, Díaz P, López A: Variation of the Seebeck coefficient with hydrogen content in carbon microfilaments.

    J Mat Sci: Mat Electron 1470, 23:2012. OpenURL

  4. Yoo E, Habe T, Nakamura J: Possibilities of atomic hydrogen storage by carbon nanotubes or graphite materials.

    Sci and Tech Adv Mater 2005, 6:615. Publisher Full Text OpenURL

  5. Yang RT: Hydrogen storage by alkali-doped carbon nanotubes - revisited.

    Carbon 2000, 38:623. Publisher Full Text OpenURL

  6. Dillon C, Jones KM, Bekkedahl TA, Kiang CH, Bethune DS, Heben MJ: Storage of hydrogen in single-walled carbon nanotubes.

    Nature 1997, 386:377. Publisher Full Text OpenURL

  7. Liu C, Ran YY, Liu M, Cong HT, Cheng HM, Dresselhaus MS: Hydrogen storage in single-walled carbon nanotubes at room temperature.

    Science 1999, 286:1127. PubMed Abstract | Publisher Full Text OpenURL

  8. Zhu H, Cao A, Li X, Xu C, Mao Z, Ruan D, Liang D, Wu D: Hydrogen adsorption in bundles of well-aligned carbon nanotubes at room temperature.

    Appl Surf Sci 2001, 178:50. Publisher Full Text OpenURL

  9. Camargo Jr SS, Santos RA, Beyer W: Characterization of DLC:Si films by the gas effusion technique.

    Diamond Relat Mater 2000, 9:658. Publisher Full Text OpenURL

  10. Tanga XM, Weber J, Mikhailov SN, Müller C, Hänni W, Hintermann HE: Structure stability of hydrogenated amorphous carbon film during thermal annealing.

    J Non-Cryst Solids 1995, 185:145. Publisher Full Text OpenURL

  11. Rico VJ, Yubero F, Espinós JP, Cetrino J, Gonzalez-Felipe AR, Garg D, Henry S: Determination of the hydrogen content in diamond-like carbon and polymeric thin films by reflection electron energy loss spectroscopy.

    Diamond Relat Mater 2007, 16:107. Publisher Full Text OpenURL

  12. Tibbetts GG: Vapor-grown carbon fibers: status and prospects.

    Carbon 1989, 27:745. Publisher Full Text OpenURL

  13. Chen P, Wu X, Lin J, Tan KL: High H2 uptake by alkali-doped carbon nanotubes under ambient pressure and moderate temperatures.

    Science 1999, 285:91. PubMed Abstract | Publisher Full Text OpenURL

  14. Fowkes FM: Attractive forces at interfaces.

    Ind Eng Chem 1964, 56:40. OpenURL

  15. Madroñero A, Ariza E, Verdu M, Brandl W, Barba C: Some microstructural aspects of vapor-grown carbon fibers to disclose their failure mechanisms.

    J Mater Sci 1996, 31:6189. Publisher Full Text OpenURL

  16. Lueking AD, Burgess Clifford CE, Narayanan DL: Induced defects in carbonaceous materials for hydrogen storage.

    ACS Div Fuel Chem Preprints 2004, 49:843. OpenURL

  17. Neyts E, Bogaerts A, Van de Sanden MCM: Effect of hydrogen on the growth of thin hydrogenated amorphous carbon films from thermal energy radicals.

    Appl Phys Lett 2006, 88:141922. Publisher Full Text OpenURL

  18. Madroñero A, Asenjo A, Gil C, Jaafar M, López A: Reconnaissance of the specific surface of vapour grown carbon micro and nanofibres as a main controller of the sorption of hydrogen.

    Appl Surf Science 2010, 256:5797. Publisher Full Text OpenURL

  19. Warrier M, Schneider R, Salonen E, Nordlund K: Effect of the porous structure of graphite on atomic hydrogen diffusion and inventory.

    Nucl Fusion 2007, 47:1656. Publisher Full Text OpenURL

  20. Heise HM, Kuckuk R, Ojha AK, Srivastava A, Srivastava V, Asthana BP: Characterisation of carbonaceous materials using Raman spectroscopy: a comparison of carbon nanotube filters, single- and multi-walled nanotubes, graphitised porous carbon and graphite.

    J Raman Spectrosc 2009, 40:344. Publisher Full Text OpenURL

  21. Tuinstra F, Koenig JL: Raman spectrum of graphite.

    J Chem Phys 1970, 53:1126. Publisher Full Text OpenURL

  22. Kim C, Hakamada K, Endo M: Raman spectroscopy of Kapton-derived carbon film.

    Carbon 1998, 36:1401. Publisher Full Text OpenURL

  23. Katagiri K, Ishida H, Ishitani A: Raman spectra of graphite edge planes.

    Carbon 1998, 26:565. OpenURL

  24. Fang TH, Chang WJ: Nanomechanical characterization of amorphous hydrogenated carbon thin films.

    Appl Surf Sci 2006, 252:6243. Publisher Full Text OpenURL

  25. Enomoto K, Kitakata S, Yasuhara T, Ohtake N, Kuzumaki T, Mitsuda Y: Measurement of Young’s modulus of carbon nanotubes by nanoprobe manipulation in a transmission electron microscope.

    Appl Phys Lett 2006, 88:153115. Publisher Full Text OpenURL

  26. Madroñero A, Aguado J, Blanco JM, López A: Uptake of hydrogen from some carbon fibres examined by Secondary Ion Mass Spectrometry.

    Appl Surf Scien 2011, 257:1881. Publisher Full Text OpenURL

  27. Subrahmanyam KS, Kumar P, Maitra U, Govindara A, Hembram KPSS, Waghmare UV, Rao CNR: PNAS.

    Proc Nat Acad Sci USA 2011, 108:2467. OpenURL