This article is part of the series International Conference on Superlattices, Nanostructures, and Nanodevices (ICSNN 2012).

Open Access Nano Express

Initial stage growth of GexSi1−x layers and Ge quantum dot formation on GexSi1−x surface by MBE

Aleksandr I Nikiforov*, Vyacheslav A Timofeev, Serge A Teys, Anton K Gutakovsky and Oleg P Pchelyakov

Author affiliations

Rzhanov Institute of Semiconductor Physics, Siberian Branch of the Russian Academy of Science, Lavrentjeva 13, Novosibirsk, 630090, Russia

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2012, 7:561  doi:10.1186/1556-276X-7-561


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/7/1/561


Received:16 July 2012
Accepted:29 September 2012
Published:9 October 2012

© 2012 Nikiforov et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License ( http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Critical thicknesses of two-dimensional to three-dimensional growth in GexSi1−x layers were measured as a function of composition for different growth temperatures. In addition to the (2 × 1) superstructure for a Ge film grown on Si(100), the GexSi1−x layers are characterized by the formation of (2 × n) reconstruction. We measured n for all layers of Ge/GexSi1−x/Ge heterosystem using our software with respect to the video recording of reflection high-energy electron diffraction (RHEED) pattern during growth. The n reaches a minimum value of about 8 for clear Ge layer, whereas for GexSi1−x films, n is increased from 8 to 14. The presence of a thin strained film of the GexSi1−x caused not only the changes in critical thicknesses of the transitions, but also affected the properties of the germanium nanocluster array for the top Ge layer. Based on the RHEED data, the hut-like island form, which has not been previously observed by us between the hut and dome islands, has been detected. Data on the growth of Ge/GexSi1−x/Ge heterostructures with the uniform array of islands in the second layer of the Ge film have been received.

Keywords:
Silicon; Germany; Epitaxy; RHEED; Growth mode; Quantum dots

Background

The Ge/GexSi1−x/Ge heterosystems with alternating layers of quantum dots and quantum wells are of great practical interest for the fabrication of mid-infrared photodetectors based on intraband transitions [1]. The energy diagram is modified due to changes both in the composition and in the thickness of the GexSi1−x film, as well as in the growth temperature. Potentialities of engineering the quantum dot electron structure are expanded when quantum dots are arranged in close proximity to the two-dimensional (2D) potential well. Such a potential well is a thin continuous layer of GexSi1−x solid solution; variations in the composition and thickness of the layer allow the energy structure of the system ‘quantum dot-solid solution layer’ to be controlled [2]. There arise additional intraband transitions of charge carriers from quantum dot levels to 2D sub-bands of the solid solution in the system. In such heterostructures, optical transitions between the bound states in a quantum dot and delocalized states in the plane of the 2D sub-bands of the solid solution film have been realized. By varying the width and the germanium content in the quantum well, the necessary energy of the optical transition can be achieved. Since the initial state of the hole is a bound state in a quantum dot thereby removing the ban on the optical transitions at normal incidence of the light, thus, it is possible to produce the mid-IR photodetectors operating at normal light incidence with high detectivity [3].

Numerous discussions on regularities of the formation of Ge and GeSi islands on the Si(100) surface are available in the literature. The system under study is considered as a model for understanding the processes of island formation and evolution during the Stranski-Krastanov growth mode [4]. A specific feature of the Ge growth on the Si(100) surface is the existence of two types of islands: these are the so-called hut clusters and three-dimensional (3D) islands facetted by {113} planes. Hut clusters are faceted by {105} planes; they are dozens of nanometers in size depending on the growth conditions. Three-dimensional islands are formed on depositing Ge in a larger quantity, and they are larger in size. Theoretical calculations on critical thicknesses of the morphological transitions are reported in [5-7] and experimental data in [8-10]; numerous data were summarized in review papers [11-13]. However, only scarce data are available in the literature concerning the studies of Ge/SiGe/Si(100) structures. The surface morphology of the 15-nm strained buffer layer of Si0.7Ge0.3 solid solution was studied using the atomic force microscopy technique [14] before and after growth of Ge islands. After six monolayers of Ge has been deposited at 600°C, islands of two types are formed: small hut islands (edge length 20 to 45 nm, height ca. 2.1 nm) faceted by {105} planes and large dome islands (diameter ca. 50 nm, height ca. 8.7 nm). Densities of the hut and dome islands are 1 × 1011 and 1 × 109 cm−2, respectively. The critical thickness of the Ge film at transition to the 3D growth mechanism was studied [15] depending on the composition of the GeSi solid solution at high deposition temperature (700°C). The islands were shown [16] to increase both in size and in density as the Ge content was increased in the pre-deposited Si1−xGex solid solution. The authors of a study [16] assume that the increased island density is caused by an increased surface roughness after the SiGe deposition, while the islands increased in size due to increasing Si content that resulted from mixing at high growth temperature and from a decrease of the wetting layer in thickness. The latter is accounted for by the accumulation of elastic strain energy in the SiGe layer. Ge islands grown on the buffer layer of the solid GeSi solution produced a more intense photoluminescence signal at room temperature than the signal of Ge islands grown on Si(100). This result was obtained due to a higher quantum dot density which provides more effective capturing of charge carriers.

The effect on the surface morphology produced by the epitaxial growth of Ge on Si(001) is a rapid change of the surface reconstruction. In addition to the (2 × 1) superstructure for a Ge film grown on Si(001), the quasi-equilibrium is characterized by the formation of (2 × n) reconstruction [17]. The (2 × n) reconstruction begins to appear to release the accumulated misfit strain [18]. Since strain increases with increasing film thickness, other modes of strain relaxation become significant. The 2D to 3D transition starts to be observed at the Ge thickness greater than or equal to three monolayers.

Methods

A molecular beam epitaxy (MBE) installation Katun-C equipped with two electron beam evaporators for Si and Ge was used for synthesis; dopants (Sb and B) were evaporated from the usual and high temperature effusion cells. Analytical equipment of the chamber included a mass spectrometer, a quartz thickness monitor, and a high-energy electron (20 kV) diffractometer. Diffraction patterns were monitored during the growth using a CCD camera that is online with a PC. The software allowed us to monitor both the whole images and chosen fragments of the diffraction patterns at the rate of ten frames per second. Ge and GeSi layers grew at the rate of ten monolayers per minute. The Ge and Si growth rates were controlled using quartz thickness monitors. Silicon 4-in diameter (100) p-type plates misoriented by less than 0.5° were used as substrates.

After chemical pretreatment, substrates were mounted in a growth chamber where they were cleaned in a low silicon flow at 800°C for 5 min. The cleaning process was controlled using reflection high-energy electron diffraction (RHEED) patterns where the appearance of proper Si(100)-(2 × 1) superstructure was identified.

RHEED was the main method used for surface analysis, and it is the most practiced technique in MBE. This technique enabled oscillations of the in-plane lattice constant to be detected for the Ge film growing according to the 2D mechanism on the silicon surface [19]. Ex situ scanning tunnel microscopy (STM) with an ultrahigh vacuum instrument Omicron-Riber (Omicron Nanotechnology GmbH, Taunusstein, Germany; Riber, Paris, France) was used for the characterization of the surface morphology.

Results and discussion

As the deposited layer increases in thickness, elastic strains induced by mismatching of the Si and Ge lattice constants also increase. Starting with some critical thickness, transitions from 2D to 3D growth mechanism are observed, with some strains being relaxed, which is energetically favorable due to a decrease in the free energy of the system. Thus, identifying the moments of 2D to 3D transitions at various thicknesses of the GexSi1−x layer allowed the 2D to 3D transition thickness of the Ge film to be determined as a function of the GexSi1−x thickness for different Ge content in GexSi1−x layers and growth temperature (see Figure 1). The obtained dependence differs from the calculated data [5,6]. The reason is that the said experimental dependence indicates the thicknesses of the strained pseudomorphous solid solution when the 3D islands emerge, while the calculated dependences [5,6] relate to the solid solution thickness when the plastic relaxation occurs and mismatch dislocation are introduced into the interface.

thumbnailFigure 1. 2D to 3D transition thickness of GexSi1−x layers for different Ge content and growth temperature.

The surface morphology of the germanium island film on the surface of GexSi1−x solid solution changes essentially if germanium islands are formed as hut clusters before growing the GexSi1−x layer. The morphology of the GexSi1−x layer located above the hut islands depends on the Ge content in the GexSi1x layer. The GexSi1−x film is a combination of (2 × 1) and (2 × n) reconstructions for x < 0.25. On the GexSi1−x surface with concentrations x > 0.25, both the above-mentioned reconstructions and the relief of underlying islands are observed. We measured n of (2 × n) reconstruction using our software with respect to the video recording of the RHEED pattern during growth (Figure 2). The n reaches a minimum value of about 8 for clear Ge layer, whereas for GexSi1−x films, n increases from 8 to 14 (Figure 3). The further deposition of the Ge film on the solid solution layer leads to a series of structural transitions on the surface.

thumbnailFigure 2. The horizontal profile of the RHEED pattern for GexSi1−x layer (x= 0.2).

thumbnailFigure 3. Horizontal intensity profile of the RHEED pattern.

From the kinetic diagram describing the 2D to 3D transition of GexSi1−x films, the values located below the 2D to 3D transition revealed the GexSi1−x thickness region, such that GexSi1−x layers were obtained the 2D dislocation-free pseudomorphic films. The presence of a thin strained GexSi1−x film caused not only changes in critical thicknesses of the transitions, but also affected the properties of the germanium nanocluster array for the top Ge layer. Based on the RHEED data, the shape of the hut-like islands, which were not observed before between the hut and dome islands, was detected. Thus, shaped islands appear on the phase diagram in the range of x = 0.25 to x = 0.5 (Figure 4). Data were obtained on the growth of Ge/GexSi1−x/Ge heterostructures with the uniform array of islands (standard deviation is approximately 10%) in the second layer of the Ge film.

thumbnailFigure 4. The phase diagram of the growth for Ge/GexSi1−x/Ge heterostructure.

The faceting by {105} planes changes upon deposition of several solid solution monolayers. Figure 5 shows an STM image of Ge islands (dGe = 0.3 nm) on Ge0.3Si0.7 (dGeSi = 10 nm)/Ge hut-cluster layers (dGe = 0.6 nm) at 500°C. Germanium islands are formed as square-based pyramids on the solid solution surface similar to those reported in [20]. Their density is lower than the density of underlying initial hut clusters (9 × 1010 cm−2). Furthermore, bases of the pyramidal islands differ from those of the initial hut clusters; they are 20 nm in characteristic size. However, the size distribution of the pyramidal islands is much more uniform (approximately by a factor of 2) than that of the germanium hut clusters. The underlying germanium layer causes variations in not only parameters of the island array, but also in their faceting. The RHEED data indicate the presence of facets at a greater angle than plane {105}. While the base edges keep their orientations, these are, supposedly, planes {104} or {103}; their accurate identification needs further studies. The presence of intermediate hut-like shape of the islands is of interest both for structural and topological properties of the surface that affect the optical and electronic properties of the system as a whole.

thumbnailFigure 5. STM images of Ge islands.

The crystal structure of Ge/GexSi1−x/Si heterolayers with quantum dots was analyzed using cross-sectional high-resolution transmission electron microscopy (TEM). Figure 6 shows a typical TEM image of such kind of heterostructures. Layers of germanium, solid solution, and silicon are rather different in contrast to allow them to be inspected individually. Neither of the layers contains any defects. Hence, the structure is elastically strained; plastic relaxation does not occur, and the germanium islands are of the characteristic hut cluster shape.

thumbnailFigure 6. High-resolution TEM image of Ge quantum dots (dGe= 0.3 nm) on 5-nm-thick Ge0.4Si0.6 at 500°C.

Conclusions

The critical thickness of 2D to 3D transition was determined as a function of composition for different growth temperatures during the growth of solid solution GexSi1−x. Non-relaxed atomically smooth GeSi layers were used as an initial surface to fabricate Ge nanoislands. The results obtained make it possible to produce dislocation-free strained heterostructures GexSi1−x, where germanium quantum dots reside in quantum wells formed by layers of GeSi solid solution. It is shown that regular pyramidal germanium islands with different faceting and array properties are formed on the surface of the solid solution coverage over germanium hut clusters. The n of (2 × n) reconstruction was determined as a function of composition during the growth of solid solution GexSi1−x in the Ge/GexSi1−x/Ge heterostructure. An increase in n from 8 to 14 was believed to take place at the enhancement of the Ge content in the GexSi1−x film.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

AIN conceived the study, performed data analysis, and took part in discussions and interpretation of results; he also supervised and coordinated the research projects. VAT participated in the design of the study, carried out the experiments, performed data analysis, and took part in discussions and interpretation of results. SAT investigated the surface morphology by STM and took part in discussions and interpretation of results. AKG performed the HRTEM studies and took part in discussions and interpretation of results. OPP participated in the design of the study, took part in discussions and interpretation of results, and supervised the research project. All authors read and approved the final manuscript.

Acknowledgments

The work is supported by the Russian Foundation for Basic Research (project no. 12-02-00427, 12-02-31051).

References

  1. Masini G, Colace L, Assanto G: Germanium-on-silicon infrared detectors.

    Encyclopedia of Nanoscience and Nanotechnology 2004, 3:829. OpenURL

  2. Tao Z, Zhan N, Yang H, Ling Y, Zhong Z, Fang L: The studies of Ge quantum dots on strained Si0.7Ge0.3 layer by photoluminescence and deep level transient spectroscopy.

    Appl Surf Sci 2009, 255:3548. Publisher Full Text OpenURL

  3. Yakimov AI, Nikiforov AI, Timofeev VA, Bloshkin AA, Kirienko VV, Dvurechenskii AV: Midinfrared photoresponse of Ge quantum dots on a strained Si0.65Ge0.35 layer.

    Semicond Sci Technol 2011, 26:085018. Publisher Full Text OpenURL

  4. Liu F, Fang W, Lagally MG: Effect of strain on structure and morphology of ultrathin Ge films on Si(001).

    Chem Rev 1997, 97:1045-1061. PubMed Abstract | Publisher Full Text OpenURL

  5. Matthews JW, Blakeslee AE: Defects in epitaxial multilayers: III. Preparation of almost perfect multilayers.

    J Cryst Growth 1976, 32:265. Publisher Full Text OpenURL

  6. Dodson BW, Tsao JY: Relaxation of strained‐layer semiconductor structures via plastic flow.

    Appl Phys Lett 1987, 51:1325-1327. Publisher Full Text OpenURL

  7. Yurasov DV, Drozdov YN: The critical thickness of Stranski-Krastanov transition with accounted segregation effect.

    Semiconductors 2008, 42:563. Publisher Full Text OpenURL

  8. Volpi F, Portavoce A, Ronda A, Shi Y, Gay JM, Berbezier I: Nucleation and evolution of Si1−xGex islands on Si(001).

    Thin Solid Films 2000, 380:46. Publisher Full Text OpenURL

  9. Nikiforov AI, Cherepanov VA, Pchelyakov OP, Dvurechenskii AV, Yakimov AI: In situ RHEED control of self-organized Ge quantum dots.

    Thin Solid Films 2000, 380:158. Publisher Full Text OpenURL

  10. Berbezier I, Ronda A, Volpi F, Portavoce A: Morphological evolution of SiGe layers.

    Surf Sci 2003, 531:231-243. Publisher Full Text OpenURL

  11. Baribeau J-M, Wu X, Rowell NL, Lockwood DJ: Ge dots and nanostructures grown epitaxially on Si.

    J Phys Condens Matter 2006, 18:R139. Publisher Full Text OpenURL

  12. Brunner K: Si/Ge nanostructures.

    Rep Prog Phys 2002, 65:27. Publisher Full Text OpenURL

  13. Pchelyakov OP, Yu B, Bolkhovityanov AVD, Nikiforov AI, Yakimov AI, Voigtlander B: Molecular beam epitaxy of silicon-germanium nanostructures.

    Thin Solid Films 2000, 367:75. Publisher Full Text OpenURL

  14. Yang H, Tao Z, Lin J, Fang L, Zuimin J, Zhenyang Z: Systematic studies of the photoluminescence of Ge quantum dots grown on strained Si0.7Ge0.3 buffer layer.

    Appl Phys Lett 2008, 9(2):111907. OpenURL

  15. Vostokov NV, Yu N, Drozdov ZFK’n, Lobanov DN, Novikov AV, Yablonski AN, Stoffel M, Denker U, Schmidt OG, Gorbenko OM, Soshnikov IP: Influence of a predeposited Si1–xGex layer on the growth of self-assembled SiGe/Si(001) islands.

    Phys Solid State 2005, 47:26. Publisher Full Text OpenURL

  16. Lobanov DN, Novikov AV, Vostokov NV, Drozdov YN, Yablonskiy AN, Krasilnik ZF, Stoffel M, Denker U, Schmidt OG: Growth and photoluminescence of self-assembled islands obtained during the deposition of Ge on a strained SiGe layer.

    Opt Mater 2005, 27:818. Publisher Full Text OpenURL

  17. Tersoff J, Tromp RM: Shape transition in growth of strained islands: spontaneous formation of quantum wires.

    Phys Rev Lett 1993, 70:2782. PubMed Abstract | Publisher Full Text OpenURL

  18. Guo LW, Huang Q, Li YK, Ma SL, Peng CS, Zhou JM: Critical Ge concentration for 2 × n reconstruction appearing on GeSi covered Si(100).

    Surf Sci 1998, 406:L592-L596. Publisher Full Text OpenURL

  19. Nikiforov AI, Cherepanov VA, Pchelyakov OP: Oscillation of in-plane lattices constant of Ge islands during molecular beam epitaxy growth on Si.

    Mater Sci Eng B 2002, 89:180. Publisher Full Text OpenURL

  20. Arapkina LV, Yuryev VA: Atomic structure of Ge quantum dots on the Si(001) surface.

    JETP Lett 2010, 91:281. Publisher Full Text OpenURL