This article is part of the series Porous Semiconductors - Science and Technology 2012.

Open Access Nano Express

Effect of etching time on morphological, optical, and electronic properties of silicon nanowires

Nesma Nafie, Manel Abouda Lachiheb and Mongi Bouaicha*

Author affiliations

Laboratoire de Photovoltaique, Centre de Recherches et des Technologies de l’Energie, Technopole de Borj-Cedria, BP 95, Hammam-Lif, Tunis, 2050, Tunisia

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2012, 7:393  doi:10.1186/1556-276X-7-393

The electronic version of this article is the complete one and can be found online at:

Received:27 April 2012
Accepted:8 June 2012
Published:16 July 2012

© 2012 Nafie et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.


Owing to their interesting electronic, mechanical, optical, and transport properties, silicon nanowires (SiNWs) have attracted much attention, giving opportunities to several potential applications in nanoscale electronic, optoelectronic devices, and silicon solar cells. For photovoltaic application, a superficial film of SiNWs could be used as an efficient antireflection coating. In this work we investigate the morphological, optical, and electronic properties of SiNWs fabricated at different etching times. Characterizations of the formed SiNWs films were performed using a scanning electron microscope, ultraviolet–visible-near-infrared spectroscopy, and light-beam-induced-current technique. The latter technique was used to determine the effective diffusion length in SiNWs films. From these investigations, we deduce that the homogeneity of the SiNWs film plays a key role on the electronic properties.

Silicon nanowires; Reflectivity; Light-beam-induced-current; Diffusion length


Silicon nanowires (SiNWs) have attracted much attention in the recent years due to their importance in the field of electronic devices and photovoltaic [1-4]. Hence, SiNWs could be used as an antireflection coating due to the reduction of optical loss which is an important factor to obtain efficient Si solar cells. However, when SiNWs are used as an antireflection coating, a great care should be taken to avoid degradation of the electronic properties, which in turn can increase the serial resistance of the solar cell. Different methods have been employed to fabricate SiNWs, such as chemical physical deposition [5], laser ablation [6,7], thermal evaporation [8,9], and etching. In this paper, we used the silver-assisted chemical etching technique [10-15]. We fabricate SiNWs at different durations, ranging from 10 to 90 min.


Substrates used in this study are P+ silicon wafers, boron-doped and (100) oriented, with thickness of 500 μm and resistivity of 0.01 to 0.02 Ωcm. After cleaning, silicon samples were immersed into the etching solution containing 0.05 M AgNO3, 40% HF, and H2O2 at room temperature for different etching times; 10, 20, 30, 40, 50, 60, 70, 80, and 90 min. After etching, samples were rinsed with deionized water to remove residual HF and immersed in a H2O-HNO3 (2 and 1 V) solution during several seconds to remove the silver film.

The morphology of samples was analyzed using a scanning electron microscope (SEM). We performed top and cross-section SEM images of the samples. The cross-section SEM images were used to evaluate the length of SiNWs. We measured the surface reflectivity in the 250 to 1,250 nm spectral range by a UV–vis-NIR spectrophotometer. To study the electronic properties of the formed films, we evaluate the effective diffusion lengths (L) of minority carriers in the SiNWs films. Values of L were carried out from the light-beam-induced-current (LBIC) profiles measured on metal/SiO2/SiNWs/c-Si/metal diode.

Results and discussion

In Figure 1 we give the top SEM views of one sample, before (Figure 1a) and after (Figure 1b) removing the silver film. One can see in Figure 1a, the silver dendrites formed during the etching process. In Figure 1b, we give a tilted SEM view of the SiNWs after removing the Ag film. In Figure 2, we give cross-sectional SEM images of SiNWs films prepared at 10, 20, 30, 40, 50, 60, 70, 80, and 90 min etching times. As reported in Figure 3, the mean length of the film varies from 21 to 38 μm. From Figure 3, we notice that the etching velocity is similar for 10, 20, and 30 min. However, it is more important for 40 and 50 min, where the maximum length is reached. When the sample is etched at greater durations, the length decreases by 10 μm from its maximum value and seems to be stabilized at values around 28 μm. This was attributed to the fact that when the etching process started, the HF solution etches the silicon substrate leading to an increase of the SiNWs’ length. After reaching the maximum length at 50 min, SiNWs themselves are etching by the HF solution as observed in the SEM image corresponding to 60 min.

thumbnailFigure 1. Top SEM views of one sample. (a) Before, and (b) after removing the silver film.

thumbnailFigure 2. Cross-section SEM images of formed SiNWs at different durations.

thumbnailFigure 3. Variation of the length of SiNWs films vs. etching time.

The total reflectivity in the 250 to 1,250 nm spectral range of formed films has very low values, less than 1% in the UV domain and a maximum of 8% in the visible and near-infrared regions (Figure 4). Generally, radiations with small wavelengths (UV domain) are absorbed at small depth and this absorption depends on the surface morphology. In the case of the non-treated sample, the reflectivity in the UV region is greater than 50% as shown in the inset of Figure 4. However, values of the reflectivity of SiNWs films in the UV domain are in the 0.5% to 1.5% range, which is unusual in silicon, even with texturized morphology and/or porous silicon. This was attributed to the important internal surface area of SiNWs. From curves in Figure 4, we remark that in the fully used spectral range, the SiNWs film elaborated at 50 min has the minimum value of the total reflectivity. The small values of reflectivity are attributed to the multiple reflections of incident photons which are important when the length of SiNWs film is important (38 μm during 50 min).

thumbnailFigure 4. Total reflectivity spectra of all SiNWs films in the 250 to 1,250 nm wavelength range. The inset is the total reflectivity of untreated silicon surface.

For the electronic characterization, we use the LBIC technique at the He-Ne wavelength. A schematic illustration of the LBIC technique is given in Figure 5. LBIC measurements were performed on metal-insulator-semiconductor structures formed on SiNWs films. Typical LBIC profiles are given in Figure 6. We notice that we obtained the same shape of LBIC profiles for samples etched during 30, 50, 60, 70, 80, and 90 min. However, for samples etched during 10, 20, and 40 min, the LBIC profiles have approximately the same shape of that one performed on the MIS diode without SiNWs (0 min). Using the LBIC measurements (ILBIC), we determine the effective values of L. To carry out L values, we fit the LBIC theoretical expression given in Equation 1 [16] to the measured LBIC profiles.

<a onClick="popup('','MathML',630,470);return false;" target="_blank" href="">View MathML</a>


Obtained values of the effective diffusion length are plot in Figure 7. We remark that the obtained L values can be divided into two domains: red and green regions in Figure 7. The red region corresponds to the L values obtained for samples prepared during 0, 10, 20, and 40 min. The green region corresponds to samples prepared at 30, 50, 60, 70, 80, and 90 min.

thumbnailFigure 5. Schematic illustration of the LBIC technique.

thumbnailFigure 6. Typical normalized LBIC profiles. Vertical dash line corresponds to the metal position on the top of the MIS structure.

thumbnailFigure 7. Obtained values of the diffusion length vs. etching time.

To understand why L values change from a sample to another, we use the cross-section SEM images of Figure 2 and the total reflectivity of films given in Figure 4. In Figure 2, we remark that durations 10, 20, and 40 min lead to inhomogeneous SiNWs films. However, the cross-section SEM images of samples prepared during 30, 50, 60, 70, 80, and 90 min show homogeneous films. In addition, taken into account that at the used wavelength in the LBIC investigations (He-Ne: 633 nm), the corresponding values of the total reflectivity (Figure 4) cannot explain, for example, why the L value of the sample prepared at 90 min is greater than that one prepared at 30 min. Consequently, we attribute these variations not to the total reflectivity, but to the carriers’ trapping at surface defects. For this purpose, we consider the schemes given in Figure 8. Thus, when the MIS diode contains homogeneous SiNWs, a great amount of photo-generated electrons by the laser beam can reach the top metal contact. However, when SiNWs are not homogeneous, surface recombination at small wires reduces the LBIC current value, leading to a decrease in the effective diffusion length.

thumbnailFigure 8. Schematic illustration of the MIS diode when the SiNWs film is homogeneous and not.


In this study, we present a morphological, optical, and electronic study of SiNWs films elaborated at different durations; 10, 20, 30, 40, 50, 60, 70, 80, and 90 min. At some etching durations, a regular structure of formed SiNWs was observed. The SiNWs lengths vary from 21 to 38 μm. We notice a spectacular very low value of the total reflectivity reaching a minimum less than 1% in the 250 to 400 nm and a minimum of 1.5% in the visible domain. From LBIC investigations, we deduce that the homogeneity of the SiNWs film plays a key role on the electronic properties. Hence, we carried out that when the SiNWs film is inhomogeneous, surface recombination of photo-generated carriers can decrease the effective diffusion length.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

NN prepared samples, MIS diodes, and performed SEM images. She also achieved the reflectivity and LBIC measurements. MAL helped on the preparation of samples, SEM investigations, carrying out the length of SiNWs, and the interpretation of LBIC profiles. Finally, MB supervised the work, did the interpretations, and wrote the text with NN and MAL. All authors read and approved the final manuscript.


  1. Zhao XY, Wei CM, Yang L, Chou MY: Quantum confinement and electronic properties of SiNWs.

    Phys Rev Lett 2004, 92:236805. PubMed Abstract | Publisher Full Text OpenURL

  2. Ma DDD, Lee CS, Au FCK, Tong SY, Lee ST: Small diameter SiNWs.

    Science 1874, 2003:299. OpenURL

  3. Li DY, Wu YY, Kim P, Shi L, Yang PD: Thermal conductivity of individual SiNWs.

    Appl Phys Lett 2003, 83:2934. Publisher Full Text OpenURL

  4. Cui Y, Lieber CM: Functional nanoscale electronic devices assembled using SiNWs building blocks.

    Science 2001, 291:851. PubMed Abstract | Publisher Full Text OpenURL

  5. Westwater J, Gosain DP, Tomiya S, Usui S, Ruda H: Growth of silicon nanowires via gold/silane vapor–liquid–solid reaction.

    J Vac Sci Technol B 1997, 15:554. Publisher Full Text OpenURL

  6. Morales AM, Lieber CM: A laser ablation method for the synthesis of crystalline semiconductor nanowires.

    Science 1998, 279:208. PubMed Abstract | Publisher Full Text OpenURL

  7. Wang N, Zhang YF, Tang YH, Lee CS, Lee ST: SiO2-enhanced synthesis of Si nanowires by laser ablation.

    Appl Phys Lett 1998, 73:3902. Publisher Full Text OpenURL

  8. Yu DP, Bai ZG, Ding Y, Hang QL, Zhang HZ, Wang JJ, Zou YH, Qian W, Xiong GC, Zhou HT, Feng SQ: Nanoscale silicon wires synthesized using simple physical evaporation.

    Appl Phys Lett 1998, 72:3458. Publisher Full Text OpenURL

  9. Zhang YF, Tang YH, Lam C, Wang N, Lee CS, Bello I, Lee ST: Bulk quantity Si nanowires synthesized by SiO sublimation.

    J Cryst Growth 2000, 212:115. Publisher Full Text OpenURL

  10. Peng KQ, Yang YJ, Gao SP, Zhu J: Synthesis of large-area silicon nanowires arrays via self-assembling nanoelectrochemistry.

    Adv Mater 2002, 14:1164. Publisher Full Text OpenURL

  11. Peng K, Yung Y, Gao S, Zhu J: Dendrites-assisted growth of silicon nanowires in electroless metal deposition.

    Adv Funct Mater 2002, 13:127. OpenURL

  12. Peng K, Fung H, Hu J, Wu Y, Zhu J, Yun Y, Lee ST: Metal-particle-induced, highly localized site-specific etching of Si and formation of single-crystalline Si nanowires in aqueous fluoride solution.

    Chem Eur 2006, 12:7942. Publisher Full Text OpenURL

  13. Srivastava SK, Kumar D, Singh PK, Kar M, Kumar V, Husain M: Excellent antireflection properties of vertical silicon nanowire arrays.

    Sol Energ Mater Sol Cells 2010, 94:1506. Publisher Full Text OpenURL

  14. Peng KQ, Xu Y, Wu Y, Yan Y, Lee ST, Zhu J: Aligned single-crystalline Si nanowires arrays for photovoltaic applications.

    Small 2005, 11:1062. OpenURL

  15. Peng KQ, Wu Y, Fang H, Zhong XY, Xu Y, Zhu J: Uniform, axial-orientation alignment of one-dimensional single-crystal silicon nanostructure arrays.

    Angew Chem Int Ed 2005, 44:2737. Publisher Full Text OpenURL

  16. Ioannou DE, Dimitriadis CA: A SEM-EBIC minority-carrier diffusion-length measurement technique.

    IEEE Trans Electron Dev 1982, ED-29(3):445-450. OpenURL