This article is part of the series IFFM&AFM2011 .

Open Access Nano Express

Electrochemical performance of Ni x Co1-x MoO4 (0 ≤ x ≤ 1) nanowire anodes for lithium-ion batteries

Kyung-Soo Park, Seung-Deok Seo, Hyun-Woo Shim and Dong-Wan Kim*

Author Affiliations

Department of Materials Science and Engineering, Ajou University, Suwon, 443-749, Republic of Korea

For all author emails, please log on.

Nanoscale Research Letters 2012, 7:35  doi:10.1186/1556-276X-7-35

The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/7/1/35


Received:2 September 2011
Accepted:5 January 2012
Published:5 January 2012

© 2012 Park et al; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

NixCo1-xMoO4 (0 ≤ x ≤ 1) nanowire electrodes for lithium-ion rechargeable batteries have been synthesized via a hydrothermal method, followed by thermal post-annealing at 500°C for 2 h. The chemical composition of the nanowires was varied, and their morphological features and crystalline structures were characterized using field-emission scanning electron microscopy and X-ray powder diffraction. The reversible capacity of NiMoO4 and Ni0.75Co0.25MoO4 nanowire electrodes was larger (≈520 mA h/g after 20 cycles at a rate of 196 mA/g) than that of the other nanowires. This enhanced electrochemical performance of NixCo1-xMoO4 nanowires with high Ni content was ascribed to their larger surface area and efficient electron transport path facilitated by their one-dimensional nanostructure.

Introduction

Among the types of anode materials available for rechargeable lithium-ion batteries, graphite has been commercialized. However, because of its drawbacks, such as capacity limitations (theoretical capacity of 372 mA h/g), initial loss of capacity, and structural deformation [1,2], one of the current areas of interest in lithium-ion battery research is the search for new anode candidates that have large reversible capacities. In the past decade, transition metal oxides (MxOy, M = Co, Ni, Cu, Fe) that can deliver a high reversible capacity by conversion reaction mechanisms (MxOy + ne- + nLi+ xM0 + LinOy) have been considered as an alternative to commercial graphite anodes for lithium-ion batteries [3-10].

Metal molybdates, AMoO4-type compounds (where A is a divalent metal ion), have attracted the interest of researchers because of their electronic and magnetic properties and their many applications, such as catalysis and photoluminescence [11-14]. Recently, CoMoO4 and NiMoO4, synthesized with nanowire morphology by a simple hydrothermal method, were exploited as materials for lithium-ion batteries but were only applied as cathodes [15,16].

In this paper, we report the fabrication of NixCo1-xMoO4 (0 ≤ x ≤ 1) nanowire electrodes by a hydrothermal method, followed by thermal post-annealing. We also demonstrate the superior electrochemical performance of NixCo1-xMoO4 nanowires for lithium-ion battery anodes.

Experimental details

NixCo1-xMoO4 (0 ≤ x ≤ 1) nanowires were synthesized by a simple hydrothermal method, in which high purity Ni(NO3)2·6H2O (99.999%; Sigma-Aldrich, Saint Louis, MO, USA), Co(NO3)2·6H2O (98%; Sigma-Aldrich, Saint Louis, MO, USA), and Na2MoO4·2H2O (99.5%; Sigma-Aldrich, Saint Louis, MO, USA) were used as source materials, followed by post-annealing at an elevated temperature. Initially, to prepare a clean solution (total cationic concentration of 0.1 M) with a molar fraction (x) of Ni (x = 0, 0.25, 0.5, 0.75, and 1), controlled amounts of Co- and Ni-containing reagents were dissolved in deionized water (80 mL) under constant magnetic stirring; then, the solution was added to an aqueous solution (80 mL) containing 0.1 M of Na2MoO4·2H2O. This resulting solution was transferred into a Teflon-lined stainless steel autoclave, sealed, and maintained at 180°C for 8 h. After the reaction was completed, the resulting solid products were harvested by centrifugation, washed with deionized water and acetone several times, and then dried at 60°C for 6 h in a vacuum oven. Finally, the as-prepared hydrate nanowire precursors were post-annealed at 500°C for 2 h to dehydrate them.

The morphologies and crystal structures of the prepared NixCo1-xMoO4·nH2O and NixCo1-xMoO4 (0 ≤ x ≤ 1) nanowires were investigated using field-emission scanning electron microscopy [FE-SEM] (10 kV; FEI NOVA, Tokyo, Japan) and X-ray powder diffraction [XRD] (λCuKa = 1.5405 Å; Miniflex II, Rigaku, Tokyo, Japan). The thermal behavior of the as-prepared hydrate samples was analyzed by thermogravimetric analysis [TGA] (DTG-60H, Shimadzu, Kyoto, Japan). For TGA, the samples were heated from room temperature up to 800°C at a heating rate of 10°C/min in air.

For the electrochemical evaluation of the NixCo1-xMoO4 (0 ≤ x ≤ 1) nanowires, positive electrode films were cast on a Cu foil by mixing each nanowire powder (1 to 2 mg) with Super P carbon black (MMM Carbon, Brussels, Belgium) and Kynar 2801 binder (PVdF-HFP, Arkema Inc., King of Prussia, PA, USA) in a mass ratio of 70:15:15. The assembled Swagelok-type cells composed of a positive electrode, negative electrode (lithium metal-foil), and separator film (Celgard 2400, Celgard LLC, Charlotte, NC, USA) saturated with a liquid electrolyte consisting of LiPF6 (1 M) dissolved in a solution of ethylene carbonate and dimethyl carbonate (1:1 v/v) were cycled at voltages between 0.01 and 3.0 V using an automatic battery cycler (WBCS 3000, WonaTech, Seoul, South Korea).

Results and discussion

Figures 1a to 1e show typical FE-SEM images of as-prepared NixCo1-xMoO4·nH2O precursors with various cationic compositions. All of the samples were of nanowire morphology regardless of their compositional differences. However, the diameters and lengths of the nanowires tended to decrease with increasing Ni concentration. As shown in Figure 1e, the NiMoO4·nH2O nanowires were agglomerated acutely and even formed clusters that were several microns in size. The agglomeration of the nanowires might be due to strong attractive forces between the small-sized nanowire particles. The crystalline structures of the as-prepared NixCo1-xMoO4·nH2O nanowires were confirmed from their XRD patterns, as seen in Figure 1f. The XRD patterns taken from all NixCo1-xMoO4·nH2O nanowires agreed well with previously reported patterns for CoMoO4·nH2O (JCPDS no.: 26-0477).

thumbnailFigure 1. Morphologies and crystal structures of NixCo1-xMoO4·nH2O nanowires. (a-e) Typical FE-SEM images of as-prepared NixCo1-xMoO4·nH2O nanowire precursors with various x values and (f) their corresponding X-ray diffraction patterns (by KS Park et al.).

The dehydration process was investigated using the thermogravimetric [TG] technique; the results of which are shown in Figure 2. The typical TG curves obtained from the NixCo1-xMoO4·nH2O nanowires in the temperature range from 30°C to 800°C showed net weight losses of 7% to 9% for each sample. This weight loss was mainly attributed to the evolution of species related to water molecules, such as reversibly bound water molecules (low temperature), water molecules forming an integral part of the crystal structure of NixCo1-xMoO4·nH2O (medium temperature), and water molecules reversibly bound to the hydrate crystal phase (high temperature) [14,15]. On the basis of the TG results, the post-annealing temperature for all the hydrate samples was 500°C, at which almost all water molecules were removed sufficiently to form NixCo1-xMoO4 nanowires.

thumbnailFigure 2. Thermal behavior of NixCo1-xMoO4·nH2O nanowires. TG curves for as-prepared NixCo1-xMoO4·nH2O nanowire precursors with various values of x, heating at a rate of 10°C/min in air (by KS Park et al.).

Figures 3a to 3e show FE-SEM images of NixCo1-xMoO4 (0 ≤ x ≤ 1) nanowires obtained by post-annealing the NixCo1-xMoO4·nH2O nanowire precursors at 500°C for 2 h. All post-annealed samples maintained their pristine nanowire morphologies. Although a marked change in the diameter or length of the nanowires after post-annealing was not observed, they seemed to be agglomerated slightly and were forming bundles, which could lead to a decrease in their surface area. In order to confirm the change in surface area that may have occurred during post-annealing of NixCo1-xMoO4·nH2O nanowire precursors, the Brunauer-Emmett-Teller [BET] (Belsorp-mini, BEL Japan Inc., Osaka, Japan) technique was carried out at liquid nitrogen temperature. From the results presented in Table 1 it can be confirmed that the surface areas of NixCo1-xMoO4 nanowires in all compositions were slightly decreased compared with those of the corresponding NixCo1-xMoO4·nH2O nanowires. This was ascribed to the aggregation and growth of the nanowires. Furthermore, it was found that the surface areas of the nanowires gradually increased with increasing Ni concentration because of the corresponding decrease in their diameter and length.

thumbnailFigure 3. Morphologies and crystal structures of NixCo1-xMoO4 nanowires. (a-e) FE-SEM images of NixCo1-xMoO4 nanowires with various x values and (f) their corresponding X-ray diffraction patterns. Filled circle, empty circle, filled inverted triangle, and empty inverted triangle correspond to α-CoMoO4, β-CoMoO4, α-NiMoO4, and β-NiMoO4, respectively (by KS Park et al.).

Table 1. Surface areas of prepared samples

To investigate the crystal structures of the NixCo1-xMoO4 nanowires, their XRD patterns were examined carefully. The XRD patterns obtained for the CoMoO4 and NiMoO4 nanowires in Figure 3f corresponded well with their bulk materials (JCPDS nos.: 25-1434, 21-0868, 33-0948, and 45-0142 for α-CoMoO4, β-CoMoO4, α-NiMoO4, and β-NiMoO4, respectively). However, as can be seen in Figure 3f, both end-members had α- and β-phases corresponding to each material together. It is known that single-phase β-CoMoO4 and α-NiMoO4 can be formed by fast cooling and by slow cooling, respectively, to room temperature after post-annealing of their hydrates [14,17,18]. Meanwhile, D. Vie et al. reported that the α-CoMoO4 phase became detectable as a minority phase after heat treatment of the amorphous solid precursor at a temperature above 700°C [17]. On the basis of these reports, we believe that the coexistence of α- and β-phases in CoMoO4 and NiMoO4 nanowires can be attributed to the medium cooling rate (≈10°C/min to 30°C/min) applied after post-annealing or to a change of phase transition temperature with the unique morphologies of the samples.

Among the NixCo1-xMoO4 nanowires with a medium composition, the XRD pattern of the Ni0.25Co0.75MoO4 nanowires agreed well with that of CoMoO4. However, in contrast with that observed for pure CoMoO4, the peaks corresponding to α-CoMoO4 became more dominant compared with those of β-CoMoO4, indicating that relative intensities of the diffraction peaks of the α-phase increase with Ni content [17]. In the case of the Ni0.5Co0.5MoO4 nanowires, it was found that the XRD pattern corresponded closer with pure NiMoO4 than with pure CoMoO4 (Figure 3f). This implies that the basic crystal structure of the nanowires was transformed from CoMoO4-related structures into NiMoO4-related structures. The XRD pattern of the Ni0.75Co0.25MoO4 nanowires also agreed with that of pure NiMoO4. It should be noted that no secondary phases, such as NiO and CoO, were detected in any of the XRD patterns, which indicated that CoMoO4 and NiMoO4 formed solid solutions perfectly.

In general, most reports on the lithium reactivity of molybdates have been focused on their application as anode materials for lithium-ion batteries because they could deliver high reversible capacity through a conversion reaction with lithium [19-21]. Moreover, NiO and CoO have also been known as anode materials, reacting with lithium by an equivalent mechanism with a molybdate [3]. On the basis of such knowledge, we expected the following electrochemical reaction mechanism of NixCo1-xMoO4 with lithium:

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/35/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/35/mathml/M1">View MathML</a>

(1)

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/35/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/35/mathml/M2">View MathML</a>

(2)

To evaluate the electrochemical performance of the NixCo1-xMoO4 nanowire electrodes, typical voltage-specific capacity curves were recorded at a current rate of C/5 (≈196 mA/g; note that 1 C ≈ 980 mA/g on the basis of the reaction in Equation 2) in a potential window between 0.01 and 3.0 V (Figure 4). In the first discharge reaction, samples containing nickel reacted with lithium at a lower potential region (≈0.4 V to 0.01 V) compared with the CoMoO4 nanowire electrode (≈0.3 V to 0.01 V). Notably, the first discharge capacities for Ni0.75Co0.25MoO4 and NiMoO4 were higher than their theoretical capacities; this might be ascribed to the formation of the solid electrolyte interface-like organic layer. Subsequent second discharge-charge reactions occurred reversibly on the basis of the reaction in Equation 2. These highly reversible capacities of NixCo1-xMoO4 nanowire electrodes could be an evidence for delivering capacity by conversion mechanism.

thumbnailFigure 4. Charging-discharging curves of NixCo1-xMoO4 nanowire electrodes. Charging-discharging curves of the NixCo1-xMoO4 nanowire electrodes with various x values at a rate of C/5 (by KS Park et al.).

Figure 5 shows the specific capacity of NixCo1-xMoO4 nanowire electrodes versus the cycle number at a current rate of C/5. When the values of x were 0, 0.25, and 0.5, the reversible capacities of NixCo1-xMoO4 nanowire electrodes faded rapidly even during the initial cycles, resulting in a poor reversible capacity of ≈290 mA h/g after 20 cycles. This result was attributed to the small surface areas of the nanowire electrodes. From the BET results summarized in Table 1 it was found that their surface areas were very small compared with those of the other nanowires, which led to a small electrode/electrolyte interface, resulting in a poor reversible capacity. Meanwhile, the reversible capacity of the NixCo1-xMoO4 nanowire electrodes with x values of 0.75 and 1 (≈520 mA h/g after 20 cycles) was larger than that of the previously mentioned three nanowire electrodes because of the increased electrode/electrolyte interface that resulted from the larger surface area of the nanowires (Table 1). In accordance with the BET results, the electrochemical performance of the NiMoO4 nanowire electrode was expected to be vastly superior compared with that of the Ni0.75Co0.25MoO4 nanowire electrode. However, the electrochemical performances of both electrodes were similar, as shown in Figure 5 due to the aggregation of the NiMoO4 nanowires. When we fabricated the positive electrode, the carbon black that is commonly used as a conducting additive was mechanically mixed with the nanowires as the active material. At that time, clusters formed by aggregation of the NiMoO4 nanowires could not be mixed efficiently with carbon black, which resulted in impairing their electrochemical performance by restriction of the electronic conduction paths from each nanowire to a current collector. In contrast, the Ni0.75Co0.25MoO4 nanowires did not form such clusters during the synthesis process. For this reason, the Ni0.75Co0.25MoO4 nanowire electrode could deliver a reversible capacity as high as the NiMoO4 nanowire electrode. Furthermore, the Ni0.75Co0.25MoO4 nanowire electrode exhibited a superior coulombic efficiency of ≈95% (Figure 5).

thumbnailFigure 5. Electrochemical properties of NixCo1-xMoO4 nanowire electrodes. Variation of the discharge (open circles)-charge (solid circles) specific capacity and coulombic efficiency (solid triangle) versus the cycle number at a rate of C/5 for the NixCo1-xMoO4 nanowire electrodes with various x values (by KS Park et al.).

Conclusion

In summary, we have successfully synthesized NixCo1-xMoO4 (0 ≤ x ≤ 1) nanowire electrodes by employing a hydrothermal method to prepare hydrate nanowires, followed by post-annealing of the as-prepared hydrate nanowires. Although α- and β-phases coexisted in all of the nanowire samples, no secondary phases were detected, indicating that CoMoO4 and NiMoO4 formed perfect solid solutions. Compared with the reversible capacity (≈290 mA h/g after 20 cycles) of the NixCo1-xMoO4 nanowire electrodes with x values of 0, 0.25, and 0.5, the reversible capacity of the nanowire electrodes containing a higher Ni content (x = 0.75 and 1) increased more (≈520 mA h/g after 20 cycles). Despite the difference in surface area between the NiMoO4 and Ni0.75Co0.25MoO4 nanowires, the reason for the observation of their similar reversible capacities was because of the agglomeration of NiMoO4 nanowires and the resulting restriction of the electronic conduction paths from each nanowire to a current collector. We anticipate that this approach will facilitate the tailoring of other electrodes based on solid solution materials, to provide electrodes with superior electrochemical performance.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

K-SP carried out the NixCo1-xMoO4 (0 ≤ x ≤ 1) nanowire sample preparation and drafted the manuscript. S-DS and H-WS participated in microstructural and electrochemical analyses. D-WK designed the study, led the discussion of the results, and participated in writing the manuscript. All authors read and approved the final manuscript.

Acknowledgements

This work was supported by the National Research Foundation of Korea (NRF) grant funded by the Korea government (MEST; nos. 2010-0029617 and 2011-0005776).

References

  1. Disma F, Aymard L, Dupont L, Tarascon JM: Effect of mechanical grinding on the lithium intercalation process in graphites and soft carbons.

    J Electrochem Soc 1996, 143:3959. Publisher Full Text OpenURL

  2. Disma F, Lenain C, Beaudoin B, Aymard L, Tarascon JM: Unique effect of mechanical milling on the lithium intercalation properties of different carbons.

    Solid State Ionics 1997, 98:145. Publisher Full Text OpenURL

  3. Poizot P, Laruelle S, Grugeon S, Dupont L, Tarascon JM: Nano-sized transition-metal oxides as negative-electrode materials for lithium-ion batteries.

    Nature 2000, 407:496. PubMed Abstract | Publisher Full Text OpenURL

  4. Taberna PL, Mitra S, Poizot P, Simon P, Tarascon JM: High rate capabilities Fe3O4-based Cu nano-architectured electrodes for lithium-ion battery applications.

    Nat Mater 2006, 5:567. PubMed Abstract | Publisher Full Text OpenURL

  5. Kim DW, Ko YD, Park JG, Kim BK: Formation of lithium-driven active/inactive nanocomposite electrodes based on Ca3Co4O9 nanoplates.

    Angew Chem Int Ed 2007, 46:6654. Publisher Full Text OpenURL

  6. Shim HW, Jin YH, Seo SD, Lee SH, Kim DW: Highly reversible lithium storage in Bacillus subtilis-directed porous Co3O4 nanostructures.

    ACS Nano 2011, 5:443. PubMed Abstract | Publisher Full Text OpenURL

  7. Li Y, Tan B, Wu Y: Mesoporous Co3O4 nanowire arrays for lithium ion batteries with high capacity and rate capability.

    Nano Lett 2008, 8:265. PubMed Abstract | Publisher Full Text OpenURL

  8. Shim HW, Cho IS, Hong KS, Cho WI, Kim DW: Li electroactivity of iron (II) tungstate nanorods.

    Nanotechnology 2010, 21:465602. PubMed Abstract | Publisher Full Text OpenURL

  9. Lee GH, Park JG, Sung YM, Chung KY, Cho WI, Kim DW: Enhanced cycling performance of Fe0/Fe3O4 nanocomposite electrode for lithium-ion batteries.

    Nanotechnology 2009, 20:295205. PubMed Abstract | Publisher Full Text OpenURL

  10. Ko YD, Kang JG, Choi KJ, Park JG, Ahn JP, Chung KY, Nam KW, Yoon WS, Kim DW: High rate capabilities induced by multi-phasic nanodomains in iron-substituted calcium cobaltite electrodes.

    J Mater Chem 2009, 19:1829. Publisher Full Text OpenURL

  11. Liu J, Huang X, Li Y, Li Z: A general route to thickness-tunable multilayered sheets of sheelite-type metal molybdate and their self-assembled films.

    J Mater Chem 2007, 17:2754. Publisher Full Text OpenURL

  12. Vilminot S, André G, Kurmoo M: Magnetic properties and magnetic structure of CuII3MoVI2O9.

    Inorg Chem 2009, 48:2687. PubMed Abstract | Publisher Full Text OpenURL

  13. Chu WG, Wang HF, Guo YJ, Zhang LN, Han ZH, Li QQ, Fan SS: Catalyst-free growth of quasi-aligned nanorods of single cryatal Cu3Mo2O9 and their catalytic properties.

    Inorg Chem 2009, 48:1243. PubMed Abstract | Publisher Full Text OpenURL

  14. Rodriguez JA, Chaturvedi S, Hanson JC, Albornoz A, Brito JL: Electronic properties and phase transformations in CoMoO4 and NiMoO4: XANES and time-resolved synchrotron XRD studies.

    J Phys Chem B 1998, 102:1347. Publisher Full Text OpenURL

  15. Xiao W, Chen JS, Li CM, Xu R, Lou XW: Synthesis, characterization, and lithium storage capability of AMoO4 (A = Ni, Co) nanorods.

    Chem Mater 2010, 22:746. Publisher Full Text OpenURL

  16. Ding Y, Wan Y, Min YL, Zhang W, Yu SH: General synthesis and phase control of metal molybdate hydrates MMoO4•nH2O (M = Co, Ni, Mn, n = 0, 3/4, 1) nano/microcrystals by a hydrothermal approach: magnetic, photocatalytic, and electrochemical properties.

    Inorg Chem 2008, 47:7813. PubMed Abstract | Publisher Full Text OpenURL

  17. Vie D, Martínez E, Sapiña F, Folgado JV, Beltrán A: Freeze-dried precursor-based synthesis of nanostructured cobalt-nickel molybdates Co1-xNixMoO4.

    Chem Mater 2004, 16:1697. Publisher Full Text OpenURL

  18. Rodriguez JA, Chaturvedi S, Hanson JC, Brito JL: Reaction of H2 and H2S with CoMoO4 and NiMoO4: TPR, XANES, time-resolved XRD, and molecular-orbital studies.

    J Phys Chem B 1999, 103:770. Publisher Full Text OpenURL

  19. Kim SS, Ogura S, Ikuta H, Uchimoto Y, Wakihara M: Reaction mechanisms of MnMoO4 for high capacity anode material of Li secondary battery.

    Solid State Ionics 2002, 146:249. Publisher Full Text OpenURL

  20. Leroux F, Goward GR, Power WP, Nazar LF: Understanding the nature of low-potential Li uptake into high volumetric capacity molybdenum oxides.

    Electrochem Solid-State Lett 1998, 1:255. OpenURL

  21. Sharma N, Shaju KM, Rao GVS, Chowdari BVR, Dong ZL, White TJ: Carbon-coated nanophase CaMoO4 as anode material for Li ion batteries.

    Chem Mater 2004, 16:504. Publisher Full Text OpenURL