Preparation of hollow porous Cu2O microspheres and photocatalytic activity under visible light irradiation

Yuan Yu1, Liying Zhang1*, Jian Wang1, Zhi Yang1, Mingce Long2, Nantao Hu1 and Yafei Zhang1*

Author Affiliations

1 Key Laboratory for Thin Film and Microfabrication of the Ministry of Education, Research Institute of Micro/Nano Science and Technology, Shanghai Jiao Tong University, Shanghai 200240, China

2 School of Environmental Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China

For all author emails, please log on.

Nanoscale Research Letters 2012, 7:347  doi:10.1186/1556-276X-7-347


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/7/1/347


Received:11 June 2012
Accepted:18 June 2012
Published:27 June 2012

© 2012 Yu et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Cu2O p-type semiconductor hollow porous microspheres have been prepared by using a simple soft-template method at room temperature. The morphology of as-synthesized samples is hollow spherical structures with the diameter ranging from 200 to 500 nm, and the surfaces of the spheres are rough, porous and with lots of channels and folds. The photocatalytic activity of degradation of methyl orange (MO) under visible light irradiation was investigated by UV-visible spectroscopy. The results show that the hollow porous Cu2O particles were uniform in diameters and have an excellent ability in visible light-induced degradation of MO. Meanwhile, the growth mechanism of the prepared Cu2O was also analyzed. We find that sodium dodecyl sulfate acted the role of soft templates in the synthesis process. The hollow porous structure was not only sensitive to the soft template but also to the amount of reagents.

Keywords:
Cu2O; Hollow porous microspheres; Photocatalytic; Visible light

Background

Much attention has been focused on fabricating high-efficiency photocatalytic materials, which is one of the most potential routes to mitigating environmental pollution [1]. Among them, metal oxide semiconductors, such as ZnO and TiO2, have attracted much attention owing to their high efficiency in the degradation of wide-ranged pollutants in which electron–hole pairs are generated under irradiation and degrade the pollutants absorbed on the surface of the photocatalytic materials [2-5]. Most of the metal oxide semiconductors have large band gaps, for example, 3.2 eV for ZnO [6] and 3.0 eV for TiO2[7], which are in the range of an UV spectrum. For this kind of materials, it is hard to generate electron–hole pairs under visible light irradiation because of the low photo energy, which therefore leads to lower photocatalytic efficiency and limits their large-scale applications. Therefore, in recent years, great efforts have been devoted to develop new photocatalytic materials with high efficiency under visible light irradiation.

As a typical p-type semiconducting material, cuprous oxide (Cu2O) possesses a stable, direct band gap of about 2.17 eV and a higher hall mobility up to 60 cm2/V·s [8], which has wide-scale applications in gas sensors, solar cells and lithium-ion batteries [7-9] owing to its unique optical and magnetic properties [9-15]. In 1998, Hara et al. [16] found that Cu2O can split water under visible light due to its low band gap. From then on, as a candidate of photocatalytic materials, Cu2O has attracted much research interests due to its important applications in degrading industrial dyeing wastewater, nitrogen-containing pesticides, etc. under visible light energy. Cu2O particles with different shapes, such as cube, octahedral, multipod, nanowire, hollow structure and porous spheres, have been synthesized [17-22]. It was found that the properties varied with the specific structure in different shapes [23]. Especially, hollow-structured particles with large specific areas have widespread potential applications in photocatalysts [24], drug delivery carriers, lightweight fillers and gas sensors [25,26]. Among lots of preparation approaches, the soft-template method is commonly used to synthesize Cu2O hollow-structured particles. So far, some polymer, such as EDTA-4Na [27], gelatin [28], PEG [29], PVP [30] and Oleic [31], were used as soft templates to fabricate hollow structures. Moreover, most reported photocatalytic studies related to Cu2O materials are mainly focused on UV-visible light irradiation [24,32,33]. In this paper, we used sodium dodecyl sulfate (SDS) as a soft template accompanied with gas bubble processes [34] to synthesize hollow porous Cu2O microspheres. The optical properties and photocatalytic activities under visible light irradiation were also investigated.

Methods

All of the chemical reagents used in the experiment were of analytical reagent grade and were directly used without further purification. To prepare the hollow porous Cu2O particles, CuSO4 was used as the Cu2+ source with SDS as the soft template. In a typical procedure, 180 mg SDS was dissolved into 45 ml deionized water under magnetic stirring for more than 20 min to form a stable micellar solution. Then, 1 ml (0.1 g/ml) CuSO4 solution, 0.04 ml (13 M) ammonia and 0.15 ml (5 M) NaOH solution were added in sequence to the above solution every 20 min. The color of the solution then turned to light turbid blue from clarification. After fully stirred, 0.18 ml (50 wt.%) N2H4·H2O solution was added dropwise as the reducing agent. As the reaction proceeded with constant stirring, the solution produced a lot of bubbles. The whole experiment process was under the condition of 20 °C for 40 min. When the reaction finished, the final products were separated by centrifugation and cleaned several times by filtration with plenty of deionized water and ethanol. Finally, the products were dried at 50 °C for 6 h in a vacuum oven.

The crystal structures of the as-prepared samples were identified by X-ray powder diffraction (XRD) using an advanced X-ray diffractometer (D8 ADVANCE, Bruker, Bremen, Germany) with a Cu-Kα rotating anode point source operating at 40 kV and 40 mA. The morphology and size were investigated by field emission scanning electron microscopy (SEM; Zeiss Ultra 55, Carl Zeiss Microscopy GmbH, Hamburg, Germany) at an accelerating voltage of 5 kV. The inner microstructure of the as-synthesized samples was studied by transmission electron microscopy (TEM; JEM-2100, JEOL, Tokyo, Japan). The optical absorption properties of the as-prepared Cu2O microspheres were characterized by UV-visible absorption spectroscopy with a He-Cd laser line of 325 nm as an excitation source (Lab-RAM HR 800 UV, HORIBA Jobin Yvon, Kyoto, Japan). The photocatalytic activity was analyzed by using methyl orange (MO) as a model pollutant molecule. The photocatalytic absorbance measurements were performed on a UNIC7000 spectrophotometer (Unic Company, USA) at 464 nm.

Results and discussion

The SEM and TEM images of the as-prepared Cu2O hollow microspheres are shown in Figure 1a,b. The morphology of the sample has been identified as hollow spherical structures, and the surfaces of the spheres are rough, porous and with lots of channels and folds. Most of them are uniform, and the diameter ranges from 200 to 500 nm. The TEM result and SEM images of several unclosed particles (inset in Figure 1a) confirm the hollow structure further.

thumbnailFigure 1. SEM (a) and TEM (b) images of the as-prepared Cu2O hollow porous microspheres. The inset in Figure 1a is an SEM image of several unclosed hollow spheres.

The typical XRD patterns of the as-synthesized hollow microspheres are shown in Figure 2. All the diffraction peaks of the samples are labeled and can be indexed very well according to the standard cubic phase Cu2O with a space group Pn3m (JCPDS file no. 05–0667). From the XRD patterns, no other characteristic diffraction peaks, such as CuO or Cu, can be detected, indicating that the pure Cu2O was obtained using this simple soft-template method at room temperature. The average crystalline grain size of the sample was calculated from the XRD patterns according to the Scherrer formula (Dhkl =  / βcosθ, where D is the average crystalline grain size, k is the Scherrer constant related to the shape and index (hkl) of the crystals, λ is the wavelength (0.154056 nm) of the X-ray, θ is the Blagg diffraction angle, and β is the full-width at half-maximum). The average crystalline grain size of the as-synthesized nanoparticle was estimated to be about 26 nm.

thumbnailFigure 2. XRD pattern of the Cu2O hollow porous microspheres.

Optical absorption behavior is one of the very important fundamental properties in revealing the energy structures and applications in photocatalysis. Figure 3 shows the UV-visible absorbance spectra of the as-prepared hollow porous Cu2O spheres by ultrasonically dispersing in absolute ethanol. Two strong absorption peaks in the UV region are observed at wavelengths of about 434 and 325 nm for the as-synthesized samples. The broader one around 434 nm should attribute to the intrinsic band gap absorption, and the sharp one at 325 nm may result from the residual SDS absorption peak. The direct optical band gap energy (Eg) of the Cu2O microspheres can be calculated from the 434-nm absorption peak. The inset in Figure 3 shows the curve of (αEphoton)2 versus the photon energy Ephoton, where α and Ephoton (hν) are respectively the absorption coefficient and the discrete photon energy. The Eg was determined by extrapolating the linear portion of the curve to zero, and the calculated value of Eg is 2.22 eV, which is a little larger than 2.17 eV for bulk materials. This may be attributed to the size effects since the microspheres are composed of nanoscaled particles, according to the SEM and TEM results.

thumbnailFigure 3. UV–vis absorbance spectra of as-prepared hollow porous Cu2O microspheres. The inset is the plot of (αEphoton)2 versus Ephoton to evaluate the band gap of Cu2O microspheres.

The photocatalytic activity of the Cu2O microspheres under visible light irradiations was also investigated. A cutoff filter was added under the Xe lamp to filter out the UV part (λ < 400 nm) to form a visible light source. The hollow porous Cu2O microspheres were dispersed in a MO aqueous solution and stirred for 10 min in the dark to establish absorption-desorption equilibrium. Then, the beaker containing this mixed solution was placed in the visible light source. An amount (3 ml) of the solution was removed from the beaker every 10 min to test the absorbance properties at 464 nm after filtrating the solid spheres. As shown in Figure 4, although the higher concentration initially degraded fast, two samples with different concentrations of 0.2 and 0.4 g/l were almost completely degraded in 1 h; especially for the sample with 0.2 g/l concentration, the degradation reached 80 % within 30 min. To confirm the results further, self-degradation experiment without hollow porous Cu2O microspheres was also performed, that is, only the MO solution was degraded under the same visible light source. Obviously, its degradation effect can be neglected. Compared with other reported results [35,36], hollow porous Cu2O microspheres possess higher degradation efficiency, that is, it has excellent visible light photocatalytic activity.

thumbnailFigure 4. Photocatalytic activity of the Cu2O microspheres under visible light irradiations in different concentrates.

This higher degradation efficiency of hollow porous Cu2O microspheres under visible light is mainly attributed to its peculiar structure with large specific areas as well as its outstanding visible light optical absorption characteristics. A hollow porous structure can provide more surface contact and space to absorb the pollutant molecule to make the excited electron arrive more easily at the surface [37]. As a comparison, the photocatalytic property of Cu2O particles with smooth octahedral surface (the SEM image is shown in Figure 5a) was also investigated. As shown in the result in Figure 4, its degradation efficiency is much less than those of the hollow porous samples, which indicates that the hollow porous structure played an important role for its higher degradation efficiency.

thumbnailFigure 5. SEM images. (a) Products without SDS, (b) with ammonia amount increased from 0.04 to 0.08 ml, and (c) with NaOH amount increased from 0.15 to 0.3 ml.

In order to confirm the above explanations, experiment without SDS was also performed. As shown in Figure 5a, some well-crystallized particles in octahedral shapes were formed instead of hollow porous microspheres, which indicate the soft-template role of SDS in the reaction.

The effects of ammonia and NaOH amount were also investigated. When the ammonia amount was increased from 0.04 to 0.08 ml (see Figure 5b) or the NaOH amount was increased from 0.15 to 0.3 ml (see Figure 5c), the morphology of the products changed a lot, and the hollow structure became imperfect. Especially, there formed many small nanoparticles and nanowires at the third condition (see Figure 5c). Summarily, SDS and the amount of reagents all played very important roles in the synthesis of novel hollow porous Cu2O microspheres.

thumbnailFigure 6. Growth schematic of hollow porous Cu2O microspheres.

The proposed growth process of hollow porous microspheres may be understood by the schematic shown in Figure 6. The anionic surfactant SDS acts the role of soft template and is a stable micelle in the solution. The inside lipophilic groups intertwined together in aqueous solution, whereas the outside hydrophilic groups containing sulfates attract Cu2+ to form the copper-rich zone. When ammonia and NaOH were added to the solution, Cu(OH)2 precursor formed firstly at the outside of the micelle and, finally, was reduced to Cu2O by hydrazine hydrate, which is a common reduction agent. At the same time, N2 was generated in the redox reaction process and produced lots of bubbles. Under the effects of SDS and bubbles, both of which acted as soft templates, the hollow porous Cu2O microspheres would be formed finally. The related chemical reactions should be as follows:

Cu 2 + +  2NH 3 H 2 O Cu OH 2 + 2 NH 4 + (1)

Cu 2 + +  2OH Cu OH 2 (2)

4 Cu OH 2 + N 2 H 4 2 Cu 2 O + 6 H 2 O + N 2 (3)

Conclusions

We have successfully synthesized hollow porous Cu2O microspheres with high purity by using a soft-template method at room temperature. This material has excellent photocatalytic activity under visible light irradiation in the degradation of MO owing to its unique optical properties and special morphology. The band gap was calculated to be 2.22 eV from its UV-visible absorbance spectrum. It was also found that the SDS acted as the soft template, and the amounts of ammonia and NaOH had important effects on the morphology of the products. These Cu2O microspheres with hollow porous structures may be a good candidate of photocatalytic materials under visible light irradiation.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

YY performed the experiment and measured the SEM and TEM data. LYZ designed the experiments and wrote the manuscript. ZY helped in the technical support for the experiments. JW and NTH participated in the measurements. MCL provided useful suggestions. YFZ supervised all of the study and provided financial support. All authors read and approved the final manuscript.

Acknowledgments

This work is supported by the National High-Tech R & D Program of China (863, no. 2011AA050504), National Natural Science Foundation of China (no. 61006002), the U-M/SJTU Collaborative Research Program and the Analytical and Testing Center of SJTU, Shanghai Pujiang Program (no. 11PJD011), Natural Science Foundation of Shanghai (no. 09ZR1414800), and the Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning.

References

  1. Hagfeldt A, Gratzel M: Light-induced redox reactions in nanocrystalline systems.

    Chem Rev 1995, 95:49-68. Publisher Full Text OpenURL

  2. Ma C, Zhou Z, Wei H, Yang Z, Wang Z, Zhang Y: Rapid large-scale preparation of ZnO nanowires for photocatalytic application.

    Nanoscale Res Lett 2011, 6:536. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  3. Hashimoto K, Irie H, Fujishima A: TiO2 photocatalysis: a historical overview and future prospects.

    Jpn J Appl Phys 2005, 44:8269-8285. Publisher Full Text OpenURL

  4. Wei H, Wang L, Li Z, Ni S, Zhao Q: Synthesis and photocatalytic activity of one-dimensional CdS@TiO2 core-shell heterostructures.

    Nano-Micro Lett 2011, 3:6-11. OpenURL

  5. Zhao W, Fu W, Yang H, Tian C, Li M, Ding J, Zhang W, Zhou X-A, Zhao H, Li Y: Synthesis and photocatalytic activity of Fe-doped TiO2 supported on hollow glass microbeads.

    Nano-Micro Lett 2011, 3:20-24. OpenURL

  6. Srikant V, Clarke DR: On the optical band gap of zinc oxide.

    J Appl Phys 1998, 83:5447-5451. Publisher Full Text OpenURL

  7. Lee H-S, Woo C-S, Youn B-K, Kim S-Y, Oh S-T, Sung Y-E, Lee H-I: Bandgap modulation of TiO2 and its effect on the activity in photocatalytic oxidation of 2-isopropyl-6-methyl-4-pyrimidinol.

    Top Catal 2005, 35:255-260. Publisher Full Text OpenURL

  8. Ishizuka S, Maruyama T, Akimoto K: Thin-film deposition of Cu2O by reactive radio-frequency magnetron sputtering.

    Jpn J Appl Phys 2000, 39:L786-L788. Publisher Full Text OpenURL

  9. Zhang J, Liu J, Peng Q, Wang X, Li Y: Nearly monodisperse Cu2O and CuO nanospheres: preparation and applications for sensitive gas sensors.

    Chem Mater 2006, 18:867-871. Publisher Full Text OpenURL

  10. Wanga R-C, Lin H-Y: Simple fabrication and improved photoresponse of ZnO–Cu2O core–shell heterojunction nanorod arrays.

    Sens Actuators B 2010, 149:94-97. Publisher Full Text OpenURL

  11. Liu W, Chen G, He G, Zhang W: Synthesis of starfish-like Cu2O nanocrystals through γ-irradiation and their application in lithium-ion batteries.

    J Nanopart Res 2011, 13:2705-2713. Publisher Full Text OpenURL

  12. Das K, De SK: Optical and photoconductivity studies of Cu2O nanowires synthesized by solvothermal method.

    J Lumin 2009, 129:1015-1022. Publisher Full Text OpenURL

  13. Hafez M, Al-Marzouki F, Mahmoud WE: Single crystalline quasi aligned one dimensional P-type Cu2O nanowire for improving Schottky barrier characteristics.

    Mater Lett 2011, 65:1868-1870. Publisher Full Text OpenURL

  14. Yue Y, Chen M, Yang J, Zhang L: Stress-induced growth of well-aligned Cu2O nanowire arrays and their photovoltaic effect.

    Scripta Mater 2012, 66:81-84. Publisher Full Text OpenURL

  15. Liu Y, Zhou H, Li J, Chen H, Li D, Zhou B, Cai W: Enhanced photoelectrochemical properties of Cu2O loaded short TiO2 nanotube array electrode prepared by sonoelectrochemical deposition.

    Nano-Micro Lett 2010, 2:277-284. OpenURL

  16. Hara M, Kondo T, Komoda M, Ikeda S, Shinohara K, Tanaka A, Kondoa JN, Domen K: Cu2O as a photocatalyst for overall water splitting under visible light irradiation.

    Chem Commun 1998, 3:357-358. OpenURL

  17. Jimenez-Cadena G, Comini E, Ferroni M, Sberveglieri G: Synthesis of Cu2O bi-pyramids by reduction of Cu(OH)2 in solution.

    Mater Lett 2010, 64:469-471. Publisher Full Text OpenURL

  18. Jiasheng X, Xue D: Five branching growth patterns in the cubic crystal system: A direct observation of cuprous oxide microcrystals.

    Acta Mater 2007, 55:2397-2406. Publisher Full Text OpenURL

  19. Chang Y, Zeng H: Manipulative synthesis of multipod framework for self-organization and self-amplification of Cu2O microcrystals.

    Cryst Growth Des 2004, 4:273-278. Publisher Full Text OpenURL

  20. Tan Y, Xue X, Peng Q, Zhao H, Wang T, Li Y: Controllable fabrication and electrical performance of single crystalline Cu2O nanowires with high aspect ratios.

    Nano Lett 2007, 7:3723-3728. Publisher Full Text OpenURL

  21. Liu X, Renzhi H, Xiong S, Liu Y, Chai L, Bao K, Qian Y: Well-aligned Cu2O nanowire arrays prepared by an ethylene glycol-reduced process.

    Mater Chem Phys 2009, 114:213-216. Publisher Full Text OpenURL

  22. Zhang L, Wang H: Cuprous oxide nanoshells with geometrically tunable optical properties.

    ACS Nano 2011, 5:3257-3267. PubMed Abstract | Publisher Full Text OpenURL

  23. Yang Z, Chiang C-K, Chang H-T: Synthesis of fluorescent and photovoltaic Cu2O nanocubes.

    Nanotechnology 2008, 19:025604. PubMed Abstract | Publisher Full Text OpenURL

  24. Shi J, Li J, Huang X, Tan Y: Synthesis and enhanced photocatalytic activity of regularly shaped Cu2O nanowire polyhedra.

    Nano Res 2011, 4:448-459. Publisher Full Text OpenURL

  25. Wang X, Liu Z, Qian Y: Synthesis, transformation to octahedron-like crystals, and gas-sensing property of six-horned nanospheres of Cu2O.

    Cryst Res Technol 2011, 46:967-972. OpenURL

  26. Conghua L, Qi L, Yang J, Wang X, Zhang D, Xie J, Ma J: One-pot synthesis of octahedral Cu2O nanocages via a catalytic solution route.

    Adv Mater 2005, 17:2562-2567. Publisher Full Text OpenURL

  27. Zhao X, Bao Z, Sun C, Xue D: Polymorphology formation of Cu2O: a microscopic understanding of single crystal growth from both thermodynamic and kinetic models.

    J Cryst Growth 2009, 311:711-715. Publisher Full Text OpenURL

  28. Xu L, Chen X, Wu Y, Chen C, Li W, Pan W, Wang Y: Solution-phase synthesis of single-crystal hollow Cu2O spheres with nanoholes.

    Nanotechnology 2006, 17:1501-1505. Publisher Full Text OpenURL

  29. Gou L, Murphy CJ: Controlling the size of Cu2O nanocubes from 200 to 25 nm.

    J Mater Chem 2004, 14:735-738. Publisher Full Text OpenURL

  30. Chen S, Chen X, Xue Z, Li L, You X: Solvothermal preparation of Cu2O crystalline particles.

    J Cryst Growth 2002, 246:169-175. Publisher Full Text OpenURL

  31. Liang X, Gao L, Yang S, Sun J: Facile synthesis and shape evolution of single-crystal cuprous oxide.

    Adv Mater 2009, 21:2068-2071. Publisher Full Text OpenURL

  32. Li J, Liu L, Ying Y, Tang Y, Li H, Feipeng D: Preparation of highly photocatalytic active nano-size TiO2–Cu2O particle composites with a novel electrochemical method.

    Electrochem Commun 2004, 6:940-943. Publisher Full Text OpenURL

  33. Haolan X, Wang W, Zhu W: Shape evolution and size-controllable synthesis of Cu2O octahedra and their morphology-dependent photocatalytic properties.

    J Phys Chem B 2006, 110:13829-13834. PubMed Abstract | Publisher Full Text OpenURL

  34. Peng Q, Dong Y, Li Y: ZnSe semiconductor hollow microspheres.

    Angew Chem Int Ed 2003, 42:3027-3030. Publisher Full Text OpenURL

  35. Zhang Y, Deng B, Zhang T, Gao D, Anwu X: Shape effects of Cu2O polyhedral microcrystals on photocatalytic activity.

    J Phys Chem C 2010, 114:5073-5079. Publisher Full Text OpenURL

  36. Ahmed A, Gajbhiyea NS, Joshi AG: Shape controlled synthesis and characterization of Cu2O nanostructures assisted by composite surfactants system.

    Mater Chem Phys 2011, 129:740-745. Publisher Full Text OpenURL

  37. Duan X, Gao R, Zhang Y, Jian Z: Synthesis of sea urchin-like cuprous oxide with hollow glass microspheres as cores and its preliminary application as a photocatalyst.

    Mater Lett 2011, 65:3625-3628. Publisher Full Text OpenURL