Antibacterial activity of silver-doped hydroxyapatite nanoparticles against gram-positive and gram-negative bacteria

Carmen Steluta Ciobanu1, Simona Liliana Iconaru1, Phillippe Le Coustumer2, Liliana Violeta Constantin3 and Daniela Predoi1*

Author affiliations

1 National Institute of Materials Physics, 105 bis Atomistilor, P.O. Box MG 07, Magurele, Bucuresti, 077125, Romania

2 University of Bordeaux, EA 4592 Géoressources & Environnement, EGID, 1 allée F. Daguin 18, Pessac Cedex, 33607, France

3 Faculty of Physics, University of Bucharest, 405 Atomistilor, CP MG - 1, Magurele, Bucuresti, 077125, Romania

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2012, 7:324  doi:10.1186/1556-276X-7-324


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/7/1/324


Received:29 March 2012
Accepted:26 May 2012
Published:21 June 2012

© 2012 Ciobanu et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Ag-doped nanocrystalline hydroxyapatite nanoparticles (Ag:HAp-NPs) (Ca10-xAgx(PO4)6(OH)2, xAg = 0.05, 0.2, and 0.3) with antibacterial properties are of great interest in the development of new products. Coprecipitation method is a promising route for obtaining nanocrystalline Ag:HAp with antibacterial properties. X-ray diffraction identified HAp as an unique crystalline phase in each sample. The calculated lattice constants of a = b = 9.435 Å, c = 6.876 Å for xAg = 0.05, a = b = 9.443 Å, c = 6.875 Å for xAg = 0.2, and a = b = 9.445 Å, c = 6.877 Å for xAg = 0.3 are in good agreement with the standard of a = b = 9.418 Å, c = 6.884 Å (space group P63/m). The Fourier transform infrared and Raman spectra of the sintered HAp show the absorption bands characteristic to hydroxyapatite. The Ag:HAp nanoparticles are evaluated for their antibacterial activity against Staphylococcus aureus, Klebsiella pneumoniae, Providencia stuartii, Citrobacter freundii and Serratia marcescens. The results showed that the antibacterial activity of these materials, regardless of the sample types, was greatest against S. aureus, K. pneumoniae, P. stuartii, and C. freundii. The results of qualitative antibacterial tests revealed that the tested Ag:HAp-NPs had an important inhibitory activity on P. stuartii and C. freundii. The absorbance values measured at 490 nm of the P. stuartii and C. freundii in the presence of Ag:HAp-NPs decreased compared with those of organic solvent used (DMSO) for all the samples (xAg = 0.05, 0.2, and 0.3). Antibacterial activity increased with the increase of xAg in the samples. The Ag:HAp-NP concentration had little influence on the bacterial growth (P. stuartii).

Keywords:
silver; hydroxyapatite; gram-positive and gram-negative bacteria

Background

In the last years, nanocomposites have received considerable attention due to their unique chemical and physical properties such as nanometric sizes, high surface area, and high reactivity. Nanoparticles have been successfully used in fields like electronics, optics, biology, chemistry, environment, and medicine [1,2].

Pharmaceutical companies and research communities are searching for new antibacterial agents [3] due to the outbreak of infectious diseases caused by microorganisms and the lack of efficient antibiotics. It seems that the answer towards developing new antibacterial agents lies within the research area of nanoscale materials. The applications of nanoscale materials have increased considerably. Nanomaterials have also been used in nanochemistry to enhance the immobilization and activity of catalysts [4]; in medical and pharmaceutical nanoengineering, for delivery of therapeutic agents [5]; in chronic disease diagnostics, sensors, and the food industry, to limit bacterial growth [6-10]. The need for constantly developing new drugs and drug targets is due to the unique property of microorganisms to adapt to harsh conditions and, implicitly, to new drugs. In the last decade, the pharmaceutical companies have introduced only few new antibiotics, and none of them demonstrated improvements against multidrug-resistant bacteria [11]. As an alternative to classical antibiotics, nanoparticles with antibacterial properties are on the top of the scientific research current topics. One of the most known and used element for its antibacterial properties for thousands of years is silver [12,13]. Although the exact mechanism of silver is not known, it is currently used to control bacterial growth in various applications such as dentistry, burn wounds, and catheters [14,15]. The antimicrobial properties of silver depend on the cation, Ag+, which has the ability to form a strong bond with electron donor groups in biological molecules. The research interest in this area of materials science is to find an appropriate biomaterial and successfully embed silver ions [16]. For that purpose, during the past 30 years, there has been a major advance in the development of medical materials due to the innovation of ceramic materials.

One of the most representative biomaterial based on calcium phosphate is hydroxyapatite (HAp). Because of its similar molecular composition to human bone, HAp has been widely investigated for its bone regeneration and bone-engineering applications [17-21]. Microorganism adhesions on implant surfaces represent an initial crucial step in infections.

Previous studies have focused on preparation and characterization of silver nanoparticles (AgNPs) [22]. The exact antibacterial action of AgNPs is not completely understood [23]. On the other hand, in the literature, the studies on the preparation and characterization of the silver-doped HAp powders are almost absent. The most recent studies [24] present preliminary antimicrobial research on the Ag:HAp nanopowder.

In this paper, we report the synthesis method for obtaining silver-doped HAp with xAg = 0.05, 0.2, and 0.3. The structure, morphology, vibrational, and optical properties of the obtained samples were systematically characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) and FT-Raman spectroscopies. Staphylococcus aureus and Providencia stuartii bacterial strains are chosen to evaluate the in vitro antimicrobial activity of silver-doped HAp samples.

Methods

Sample preparation

All reagents for synthesis including ammonium dihydrogen phosphate [(NH4)2HPO4] (Alfa Aesar, Karlsruhe, Germany; 99.99% purity), calcium nitrate [Ca (NO3)2·4H2O] (Alfa Aesar, Karlsruhe, Germany; 99.99% purity), silver nitrate (AgNO3) (Alfa Aesar, Karlsruhe, Germany; 99.99% purity), and ammonium hydroxide (NH3) (25%, Alfa Aesar, Karlsruhe, Germany; 99.99% purity) were used for the synthesis of hydroxyapatite doped with silver.

Nanocrystalline hydroxyapatite doped with Ag (Ca10−xAgx(PO4)6(OH)2, from xAg = 0.05 to xAg = 0.3) was performed by setting the atomic ratio of Ag/[Ag + Ca] from 5% to 30% and [Ca + Ag]/P as 1.67. AgNO3 and Ca(NO3)2·4H2O were dissolved in deionized water to obtain 300-ml [Ca + Ag]-containing solution. On the other hand, (NH4)2HPO4 was dissolved in deionized water to make a 300-ml P-containing solution. The [Ca + Ag]-containing solution was put into a Berzelius and stirred at 100°C for 30 min. Meanwhile, the pH of the P-containing solution was adjusted to 10 with NH3 and stirred continuously for 30 min. The P-containing solution was added drop by drop into the [Ca + Ag]-containing solution and stirred for 2 h, and the pH was constantly adjusted and kept at 10 during the reaction. After the reaction, the deposited mixtures were washed several times with deionized water. The resulting material (Ag:HAp (xAg from 0.05 to 0.3)) was dried at 100°C for 72 h.

Sample characterization

The XRD measurements for the Ca10−xAgx(PO4)6(OH)2 samples were recorded using a Bruker D8 Advance diffractometer (BRUKER OPTIK GMBH, Karlsruhe, Germany), with nickel-filtered CuKα (λ = 1.5418 Å) radiation, and a high efficiency one-dimensional detector (Lynx Eye type) operated in integration mode. The diffraction patterns were collected in the 2θ range of 15° to 140°, with a step of 0.02° and a 34-s measuring time per step. TEM studies were carried out using a FEI Tecnai 12 (FEI Company, Hillsboro, OR, USA) equipped with a low-dose digital camera from Gatan Inc. (Pleasanton, CA, USA). The specimen for TEM imaging was prepared by ultramicrotomy to get a thin section of about 60 nm in thickness. The powder is embedded in an epoxy resin (polaron 612) before microtomy. The TEM modes used were bright field (BF) and selected area diffractions. The functional groups present in the prepared nanoparticles and thin films were identified by FT-IR using a Spectrum BX spectrometer (PerkinElmer Instruments, Branford, CT, USA). To obtain the nanoparticle spectra, 1% of nanopowder was mixed and ground with 99% KBr. Tablets of 10 mm in diameter were prepared by pressing the powder mixture at a load of 5 tons for 2 min. The spectrum was taken in the range of 500 to 4,000 cm−1 with a 4-cm−1 resolution. Micro-Raman spectra on HAp powders were performed in a backscattering geometry at room temperature and in ambient air, under a laser excitation wavelength of 514 nm, using a Jobin Yvon T64000 Raman spectrophotometer under a microscope.

The in vitro antibacterial activity

These nanoparticles were evaluated for their antibacterial activity against gram-positive (Staphylococcus aureus) and gram-negative (Providencia stuartii, Citrobacter freundii, Klebsiella pneumoniae and Serratia marcescens) bacteria.

The antimicrobial activities of the tested substances were determined against ATCC reference and clinical microbial strains, i.e., gram-positive (S. aureus ATCC 25293), gram-negative (P. stuartii 1116, C. freundii 1748, K. pneumoniae ESBL, S. marcescens 0804) bacterial strains.

The microbial strain identification was confirmed by aid of VITEK 2 (bioMérieux, Marcy l’Etoile, France). VITEK is an integrated system that automatically performs rapid identification using algorithms based on fluorescence and colorimetry and antimicrobial susceptibility testing based on kinetic analysis of growth data. VITEK cards for identification and susceptibility testing were inoculated and incubated according to the manufacturer’s recommendations. The results were interpreted using the software version AMS R09.1.

Microbial suspensions of 1.5 × 108 colony-forming unit (CFU)/ml corresponding to 0.5 McFarland density obtained from 15- to 18-h bacterial cultures developed on solid media were used in our experiments. The tested substances were solubilized in dimethyl sulfoxide (DMSO), and the starting stock solution was of 5,000 μg/ml concentration. The qualitative screening was performed by an adapted disk diffusion method [25-29].

The quantitative assay of the antimicrobial activity against planktonic microbial strains was performed using the liquid medium microdilution method, in 96-multiwell plates, in order to establish the minimal inhibitory concentration (MIC). For this purpose, two fold serial dilutions of the compounds ranging between 000 and 1.95 μg/ml were performed in a 200-μl volume of broth, and each well was seeded with 50 μl of microbial inoculum. Sterility control (wells containing only culture medium) and culture controls (wells containing culture medium seeded with the microbial inoculum) were used. The influence of the DMSO solvent was also quantified in a series of wells containing DMSO, diluted accordingly with the dilution scheme used for the complexes. The plates were incubated for 24 h at 37°C. The MIC values were considered as the lowest concentration of the tested compound that inhibited the visible growth of the microbial overnight cultures [25-29].

The assessment of the complexes influence on the microbial ability to colonize an inert substratum was performed using the microtiter method. For this purpose, the microbial strains have been grown in the presence of two fold serial dilutions of the tested compounds performed in liquid nutrient broth/YPG, distributed in 96-well plates and incubated for 24 h at 37°C for bacterial strains and for 48 h at 28°C for fungal strains. At the end of the incubation period, the plastic wells were emptied, washed three times with phosphate buffered saline, fixed with cold methanol, and stained with 1% violet crystal solution for 30 min. The biofilm that formed on plastic wells was resuspended in 30% acetic acid. The intensity of the colored suspensions was assessed by measuring the absorbance at 490 nm. The last concentration of the tested compound that inhibited the development of microbial biofilm on the plastic wells was considered the minimum inhibitory concentration of biofilm development and was also expressed in micrograms per milliliter [30-33].

Results and discussion

The XRD pattern of Ag:HAp (Ca10−xAgx(PO4)6(OH)2, with xAg = 0.05, 0.2, and 0.3) powders are shown in Figure 1. A typical XRD of HAp is demonstrated, which closely matches the one of Ca10(PO4)6(OH)2, according to the International Centre for Diffraction Data (ICDD), Powder Diffraction File (PDF) standard card number 9–432 represented at the bottom of the figure, as reference. No other crystalline phases were detected besides this phase (Figure 1). The XRD of Ag:HAp powders are similar to that of HAp, but the reduced intensity indicates that the crystallinity decreases gradually with xAg from 0.05 to 0.3. The XRD of Ag:HAp also demonstrates that powders obtained by coprecipitation exhibit the apatite characteristics with good crystal structure and no new phase or impurity. Insightful analyses of the doped HAp structures, carried out by Rietveld whole powder pattern fitting using the MAUD code [34], showed that Ag enters the HAp lattice by substituting Ca, with comparable probabilities for the two crystallographic sites of calcium in the HAp unit cell. The lattice parameters did not modify significantly after substitution. The XRD analysis using the anisotropic microstructure analysis implemented in MAUD as ‘Popa rules’ [35] show that the calculated lattice constants for Ag:HAp are in good agreement with the standard data PDF file number 9–432. The calculated lattice constants of a = b = 9.435 Å, c = 6.876 Å for xAg = 0.05, a = b = 9.443 Å, c = 6.875 Å for xAg = 0.2, and a = b = 9.445 Å, c = 6.877 Å for xAg = 0.3 are in good agreement with the standard of a = b = 9.418 Å, c = 6.884 Å (space group P63/m).

thumbnailFigure 1. Comparative representation of experimental XRD patterns and hydroxyapatite characteristic lines according to ICDD-PDF number 9–432.

The TEM micrographies give information on the texture (BF) and the structure (SAED) of the three samples (xAg = 0.05, 0.2, and 0.3). All the samples exhibit a uniform rod-like morphology with particles from 30 to 5 nm, as observed on the BF micrographies (Figure 2). These results revealed that the doping components have little influence on the surface morphology of the samples. The morphology identifications indicated that the nanoparticles with good crystal structure could be made using the coprecipitation method at low temperature. It can be seen from the high-resolution TEM (HRTEM) image of Ag:HAp-NPs with xAg = 0.3 (Figure 3) that the crystalline phase of hydroxyapatite with well-resolved lattice fringes can be observed. The distances (2.81 and 1.94 Å) between the adjacent lattice fringes agree well with the d211 and d222 spacing from the literature values (0.2814 and 0.194 nm; CJPDS no. 09–0432).

thumbnailFigure 2. TEM micrographies of the Ag:HAp samples synthesized withxAg= 0.05, 0.2, and 0.3.

thumbnailFigure 3. HRTEM image of Ag:HAp-NPs withxAg= 0.3.

FT-IR spectroscopy was performed in order to investigate the functional groups present in nano-hydroxyapatite, Ca10−xAgx(PO4)6(OH)2 (xAg = 0.05, 0.2, and 0.3), obtained at 100°C by coprecipitation method. Figure 4 shows the FT-IR results obtained from Ag:HAp-NPs when xAg increases from 0.05 to 0.3. These data clearly revealed the presence of various vibrational modes corresponding to phosphates and hydroxyl groups. For all samples, the presence of a strong OH vibration peak could be noticed. The broad bands in regions 1,600 to 1,700 cm−1 and 3,200 to 3,600 cm−1 correspond to H-O-H bands of water lattice [36-38].

thumbnailFigure 4. Transmittance infrared spectra of the Ag:HAp samples synthesized withxAg= 0.05, 0.2, and 0.3.

Band characteristics of the phosphate and hydrogen phosphate groups in apatitic environment were observed: 563, 634, 603, 960 cm−1, and 1,000 to 1,100 cm−1 for the PO43− groups [39,40] and at 875 cm−1 for the HPO42− ions [41]. Moreover, it should be noted that the HPO42− band was present in all the spectra, but for high values of xAg, the band diminished. A CO32− band occurred in the spectra at 1,384 cm−1[40].

Complementary information can be obtained from Raman spectroscopy (Figure 5). The internal modes of the PO43− tetrahedral ν1 frequency (960 cm−1) corresponds to the symmetric stretching of P-O bonds.

thumbnailFigure 5. Raman spectra of the Ag:HAp samples synthesized withxAg= 0.05, 0.2, and 0.3.

The vibrational bands at 429 (ν2) and 450 cm−1 (ν2) are attributed to the O-P-O bending modes. We assigned the bands present at 1,046 (ν3) and 1,074 cm−1 (ν3) to asymmetric ν3 (P-O) stretching. The values of ν4 (589 and 608 cm−1) can be addressed mainly to the O-P-O bending character [42]. However, intensity of the vibration peak decreases when xAg increases.

The qualitative screening of the antimicrobial activity of the tested compounds performed using stock solutions of 5 mg/ml obtained in DMSO allowed the selection of the active compounds, indicated by the occurrence of growth inhibition zones around the spotted compound, with higher diameters than those obtained for the DMSO solvent. The specific antimicrobial activity revealed by the qualitative assay is demonstrating that our compounds are interacting differently with the microbial targets, probably due to the differences in the microbial wall structures. For the quantitative assays, the active compounds have been tested only on the strains which proved to be sensitive in the qualitative assays. It is also to be mentioned that DMSO did not exhibit any traceable antimicrobial activity at the studied concentrations; thus, the solvent did not influence the biological activity of the tested substances. The inert substrate including the prosthetic medical devices represents risk factors for the occurrence of biofilm-associated infections.

These nanoparticles are evaluated for their antibacterial activity against gram-positive (S. aureus) and gram-negative (P. stuartii, C. freundii, K. pneumoniae, and S. marcescens) bacteria.

S. aureus is the most common organism associated with infections. The reason that S. aureus is a successful pathogen is because of a combination of bacterial immuno-evasive strategies. It is still one of the five most common causes of nosocomial infections and is often the cause of postsurgical wound infections [43]. S. aureus was inhibited for a Ag:HAp-NP concentration above 1.95 μg/ml for the samples with xAg = 0.2 and 0.3. For the samples with xAg = 0.05, no significant antibacterial activity was observed when the Ag:HAp-NP concentration was less than 250 μg/ml. For the samples with xAg = 0.2, the antibacterial activity increases to Ag:HAp-NP concentrations lower than 250 μg/ml. For Ag:HAp-NP concentrations greater than 250 μg/ml, we have a constant antibacterial activity. In the samples with xAg = 0.3, no significant bacterial growth was observed. The results of the antibacterial activity of different Ag:HAp-NPs are presented in Figure 6.

thumbnailFigure 6. Antibacterial activity of Ag:HAp-NPs (xAg= 0.05, 0.2, and 0.3) onS. aureus.

Both P. stuartii and C. freundii are commonly found in soil, water, and sewage [44]. P. stuartii[45] and C. freundii[46] are responsible for a number of significant opportunistic infections. Figures 7 and 8 show the results of antibacterial activity of different Ag:HAp-NPs exposed to P. stuartii and C. freundii, respectively.

thumbnailFigure 7. Antibacterial activity of Ag:HAp-NPs (xAg= 0.05, 0.2, and 0.3) onP. stuartii.

thumbnailFigure 8. Antibacterial activity of Ag:HAp-NPs (xAg= 0.05, 0.2, and 0.3) onC. freundii.

The results of qualitative antibacterial tests revealed that the tested Ag:HAp-NPs had an important inhibitory activity on P. stuartii and C. freundii. The absorbance values measured at 490 nm of P. stuartii and C. freundii in the presence of Ag:HAp-NPs decreased compared with that of the organic solvent used (DMSO) for all the samples (xAg = 0.05, 0.2, and 0.3). Antibacterial activity increased with the increase of xAg in the samples. The Ag:HAp-NP concentration had little influence on bacterial growth (P. stuartii).

In recent years, K. pneumoniae has become an important pathogen in nosocomial infections. It naturally occurs in the soil, and about 30% of strains can fix nitrogen in anaerobic conditions [47]. Figure 9 illustrated the antibacterial activity of different values of xAg on K. pneumoniae. It shows the inhibition of the bacteria based on the antimicrobial activity of the organic solvent used (DMSO). For samples with xAg = 0.2 and 0.3, the antibacterial activity did not depended on the Ag:HAp-NP concentration. For samples with xAg = 0.05, a slight antibacterial activity was observed up to 31.25 μg/ml Ag:HAp-NP concentration.

thumbnailFigure 9. Antibacterial activity of Ag:HAp-NPs (xAg= 0.05, 0.2, and 0.3) onK. pneumoniae.

S. marcescens is differentiated from other gram-negative bacteria by its ability to perform casein hydrolysis, which allows it to produce extracellular metalloproteinases which are believed to function in cell-to-extracellular matrix interactions [48]. The antibacterial activity of the Ag:HAp nanoparticles on S. marcescens can be seen in Figure 10. In the presence of Ag:Hap, the growth inhibitory effects on S. marcescens were not observed, even in high concentrations of Ag:Hap-NPs (500 and 1,000 μg/ml) for the samples with xAg = 0.2 and 0.3.

thumbnailFigure 10. Antibacterial activity of Ag:HAp-NPs (xAg= 0.05, 0.2 and 0.3) onS. marcescens.

Several studies demonstrated that silver nanoparticles show an efficient antibacterial activity against Escherichia coli and S. aureus[49-51]. Besides, a high concentration of silver nanoparticles may cause adverse health effects. For reducing the toxic effects of silver, several biodegradable polymers were used for coating the silver nanoparticles. Recent studies on Ag: Hap nanopowders [26] obtained by coprecipitation method demonstrated a good antibacterial activity. Novel nanopowders based on silver-doped hydroxyapatite will diminish the adverse effects of silver.

Based on the tests mentioned above, the results showed that the antimicrobial activity of the Ag:HAp-NPs depended strongly on xAg. The Ag:HAp-NP concentrations were high enough to obtain a good antibacterial activity. It was observed that the inhibition depends on the concentration of Ag:Hap-NPs in accord with the precedent studies on Ag nanoparticles [52]. Our study showed that Ag:HAp-NPs presents inhibitory effects on a large number of gram-positive and gram-negative bacteria.

Conclusions

In this study, our aim was to illustrate good antibacterial property of the silver-doped hydroxyapatite. Finally, it was demonstrated that Ag:HAp-NPs possess excellent antibacterial properties. Ag:HAp prepared by coprecipitation method at low temperature shows great promise as antibacterial agents against both gram-positive and gram-negative bacteria. The Ag:HAp nanoparticles show the efficient antibacterial activity against S. aureus, P. stuartii, C. freundii, and K. pneumoniae. Antibacterial activity increased with increasing xAg in the samples. Antibacterial activity is also related to the concentration of the Ag:HAp nanoparticles and the initial bacterial concentration. In the presence of Ag:Hap, the growth inhibitory effects on S. marcescens were not observed, even in high concentrations of Ag:Hap-NPs. Therefore, Ag: HAp-NPs may find various practical applications such as wound dressings or improving water quality.

Abbreviations

DMSO, dimethyl sulfoxide; FT-IR spectroscopy, Fourier transform infrared spectroscopy; ICDD, International Centre for Diffraction Data; PDF, Powder Diffraction File; TEM, transmission electron microscopy; XRD, X-ray diffraction.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

CSC and DP conceived the study. CSC, SLI, and LVC performed the synthesis of the powders. Characterization of materials was carried out by CSC and DP. TEM investigations were done by PLC. SLI performed the antibacterial investigations. DP directed the study and wrote the draft paper. All authors contributed to the interpretation of results and discussion, have corrected, read, and approved the final manuscript.

Acknowledgments

The authors would like to thank Florian Massuyeau (Institut des Matériaux-Jean Rouxel, Nantes) and Professor Carmen Mariana Chifiriuc (Microbiology Immunology Department, Faculty of Biology, University of Bucharest) for their kind help in using the Raman device and for assistance with the antimicrobial tests, as well as for their constructive discussions. This work was financially supported by IFA-CEA program under project no: C2-06.

References

  1. Morones JR, Elechiguerra JL, Camacho A, Ramirez JT: The bactericidal effect of silver nanoparticles.

    Nanotechnology 2005, 16:2346-2353. PubMed Abstract | Publisher Full Text OpenURL

  2. Kim JS, Kuk E, Yu KN, Kim JH, Park SJ, Lee HJ, Kim SH, Park YK, Park YH, Hwang CY, Kim YK, Lee YS, Jeong DH, Cho MH: Antimicrobial effects of silver nanoparticles.

    Nanomed Nanotechnol Biol Med 2007, 3:95-101. Publisher Full Text OpenURL

  3. Mahendra R, Alka Y, Aniket G: Silver nanoparticles as a new generation of antimicrobials.

    Biotechnol Adv 2009, 27:76-83. PubMed Abstract | Publisher Full Text OpenURL

  4. Wang P: Nanoscale biocatalyst systems.

    Curr Opinion Biotechnol 2006, 17:574-579. Publisher Full Text OpenURL

  5. Zhang L, Gu FX, Chan JM, Wang AZ, Langer RS, Farokhzad OC: Nanoparticles in medicine: therapeutic applications and developments.

    Clin Pharmacol Ther 2008, 83:761-769. PubMed Abstract | Publisher Full Text OpenURL

  6. Chau CF, Wu SH, Yen GC: The development of regulations for food nanotechnology.

    Trends Food Sci Technol 2007, 18:269-280. Publisher Full Text OpenURL

  7. Vigneshwaran N, Kathe AA, Varadarajan PV, Nachane RP, Balasubramanya RH: Functional finishing of cotton fabrics using silver nanoparticles.

    J Nanosci Nanotechnol 2007, 7:1893-1897. PubMed Abstract | Publisher Full Text OpenURL

  8. Jiang Wu, Lee S, Reddy VR, Manasreh MO, Weaver BD, Yakes MK, Kunets VasP, Benamara M, Salamo GJ: Photoluminescence plasmonic enhancement in In As quantum dots coupled to gold nanoparticles.

    Mater Lett 2011, 65:3605-3608. Publisher Full Text OpenURL

  9. Lee S, Cho K, Lim J, Kim W, Hwang S: Acclimation and activity of ammonia-oxidizing bacteria with respect to variations in zinc concentration, temperature, and microbial population.

    Bioresource Technol 2011, 12(5):4196-4203. OpenURL

  10. Shin SG, Lee S, Lee C, Hwang K, Hwang S: Qualitative and quantitative assessment of microbial community in batch anaerobic digestion of secondary sludge.

    Bioresource Technol 2010, 101(24):9461-9470. Publisher Full Text OpenURL

  11. Conlon JM, Kolodziejek J, Nowotny N: Antimicrobial peptides from ranid frogs: taxonomic and phylogenetic markers and a potential source of new therapeutic agents.

    Biochim Biophys Acta 2004, 1696:1-14. PubMed Abstract | Publisher Full Text OpenURL

  12. Goodman LS, Gilman A: The pharmacological basis of therapeutics. 5th edition. Macmillan Publishing Co., New York; 1975. OpenURL

  13. Silver S, Phung LT: Bacterial heavy metal resistance: new surprises.

    Annu Rev Microbiol 1996, 50:753-789. PubMed Abstract | Publisher Full Text OpenURL

  14. Catauro M, Raucci MG, De Gaetano FD, Marotta A: Antibacterial and bioactive silver containing Na2O CaO 2SiO2 glass prepared by sol–gel method.

    J Mater Sci Mater Med 2004, 15(7):831-837. PubMed Abstract | Publisher Full Text OpenURL

  15. Crabtree JH, Burchette RJ, Siddiqi RA, Huen IT, Handott LL, Fishman A: The efficacy of silver-ion implanted catheters in reducing peritoneal dialysis-related infections.

    Perit Dial Int 2003, 23(4):368-374. PubMed Abstract | Publisher Full Text OpenURL

  16. Wohrmann RM, Munstedt H: Zur bestimmung der freisetzung von silberionen aus silbergef ulltem polyurthan.

    Infection 1998, 26:49-52. OpenURL

  17. Xin R, Leng Y, Chen J, Zhang Q: A comparative study of calcium phosphate formation on bioceramics in vitro and in vivo.

    Biomaterials 2005, 26(33):6477-6486. PubMed Abstract | Publisher Full Text OpenURL

  18. Ramila A, Vallet-Regi M: Static and dynamic in vitro study of a sol–gel glass bioactivity.

    Biomaterials 2001, 22(16):2301-2306. PubMed Abstract | Publisher Full Text OpenURL

  19. Ragel CV, Vallet-Regi M, Rodriguez-Lorenzo LM: Preparation and in vitro bioactivity of hydroxyapatite/solgel glass biphasic material.

    Biomaterials 2002, 23(8):1865-1872. PubMed Abstract | Publisher Full Text OpenURL

  20. Fujibayashi S, Neo M, Kim HM, Kokubo T, Nakamura T: A comparative study between in vivo bones ingrowth and in vitro apatite formation on Na2O–CaO–SiO2 glasses.

    Biomaterials 2003, 24(8):1349-1356. PubMed Abstract | Publisher Full Text OpenURL

  21. Siriphannon P, Kameshima Y, Yasumori A, Okada K, Hayashi S: Comparative study of the formation of hydroxyapatite in simulated body fluid under static and flowing systems.

    J Biomed Mater Res 2002, 60(1):175-185. PubMed Abstract | Publisher Full Text OpenURL

  22. Sondi I, Salopek Sondi B: Silver nanoparticles as antimicrobial agent: a case study on E. coli as a model for gram–negative bacteria.

    J Colloid Interf Sci 2004, 275:177-182. Publisher Full Text OpenURL

  23. Li X, Li S, Zhang M, Zhang W, Li C: Evaluations of antibacterial activity and cytotoxicity on Ag nanoparticles.

    Rare Metal Mat Eng 2011, 40(2):0209-0214. Publisher Full Text OpenURL

  24. Ciobanu CS, Massuyeau F, Constantin LV, Predoi D: Structural and physical properties of antibacterial Ag doped nano-hydroxyapatite synthesized at 100°C.

    Nanoscale Res Lett 2011, 6:613. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  25. Limban C, Chifiriuc MC: Antibacterial activity of new dibenzoxepinone oximes with fluorine and trifluoromethyl group substituents.

    Int J Mol Sci 2011, 12(10):6432-6444. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  26. Limban C, Marutescu L, Chifiriuc MC: Synthesis, spectroscopic properties and antipathogenic activity of new thiourea derivatives.

    Molecules 2011, 16(9):7593-7607. PubMed Abstract | Publisher Full Text OpenURL

  27. Saviuc C, Grumezescu AM, Holban A, Bleotu C, Chifiriuc CM, Balaure P, Lazar V: Phenotypical studies of raw and nanosystem embedded Eugenia carryophyllata buds essential oil antibacterial activity on Pseudomonas aeruginosa and Staphylococcus aureus strains.

    Biointerface Res App Chem 2011, 1(3):111-118. OpenURL

  28. Chifiriuc MC, Palade R, Israil AM: Comparative analysis of disk diffusion and liquid medium microdillution methods for testing the antibiotic susceptibility patterns of anaerobic bacterial strains isolated from intrabdominal infections.

    Biointerface Res App Chem 2011, 1(6):209-220. OpenURL

  29. Marutescu L, Limban C, Chifiriuc MC, Missir AV, Chirita IC, Caproiu MT: Studies on the antimicrobial activity of new compounds containing thiourea function.

    Biointerface Res App Chem 2011, 1(6):236-241. OpenURL

  30. Grumezescu AM, Mihaiescu DE, Mogoşanu DE, Chifiriuc MC, Lazar V, Lazar V, Calugarescu I, Traistaru V: In vitro assay of the antimicrobial activity of Fe3O4 and CoFe2O4/oleic acid - core/shell on clinical isolates of bacterial and fungal strains.

    Optoelectron Adv Mat 2010, 4(11):1798-1801. OpenURL

  31. Chifiriuc C, Lazar V, Bleotu C, Calugarescu I, Grumezescu AM, Mihaiescu DE, Mogoşanu DE: Bacterial adherence to the cellular and inert substrate in the presence of CoFe2O4 and Fe3O4/oleic acid - core/shell.

    Dig J Nanomater Bios 2011, 6(1):37-42. OpenURL

  32. Saviuc C, Grumezescu AM, Oprea E, Radulescu V, Dascalu L, Chifiriuc MC, Bucur M, Banu O, Lazar V: Antifungal activity of some vegetal extracts on Candida biofilms developed on inert substratum.

    Biointerface Res App Chem 2011, 1(1):015-023. OpenURL

  33. Saviuc C, Grumezescu AM, Chifiriuc MC, Bleotu C, Stanciu G, Hristu R, Mihaiescu D, Lazar V: In vitro methods for the study of microbial biofilms.

    Biointerface Res App Chem 2011, 1(1):031-040. OpenURL

  34. Lutterotti L: Total pattern fitting for the combined size–strain–stress–texture determination in thin film diffraction.

    Nuclear Inst. and Methods in Physics Research B 2010, 268:334-340. Publisher Full Text OpenURL

  35. Popa NC: The (hkl) dependence of diffraction-line broadening caused by strain and size for all Laue groups in Rietveld refinement.

    J. Appl. Cryst. 1998, 31:176-180. Publisher Full Text OpenURL

  36. Predoi D, Ghita RV, Ungureanu F, Negrila CC, Vatasescu-Balcan RA, Costache M: Characteristics of hydroxyapatite thin films.

    J Optoelectron Adv Mater 2007, 9(12):3827-3831. OpenURL

  37. Predoi D, Barsan M, Andronescu E, Vatasescu-Balcan RA, Costache M: Hydroxyapatite - iron oxide bioceramic prepared using nano-size powders.

    J Optoelectron Adv Mater 2007, 9(11):3609-3613. OpenURL

  38. Costescu A, Pasuk I, Ungureanu F, Dinischiotu A, Costache M, Huneau F, Galaup S, Le Coustumer P, Predoi D: Physico-chemical properties of nano-sized hexagonal hydroxyapatite powder synthesized by sol–gel.

    Dig J Nanomater Bios 2010, 5:989-1000. OpenURL

  39. Ciobanu CS, Andronescu E, Vasile BS, Valsangiacom CM, Ghita RV, Predoi D: Looking for new synthesis of hydroxyapatite doped with europium.

    Optoelectron Adv Mat 2010, 4:1515-1519. OpenURL

  40. Bai X, More K, Rouleau CM, Rabiei A: Functionally graded hydroxyapatite coatings doped with antibacterial components.

    Acta Biomater 2010, 6:2264-2273. PubMed Abstract | Publisher Full Text OpenURL

  41. Doat A, Pelle F, Gardant N, Lebugle A: Synthesis of luminescent bioapatite nanoparticles for utilization as a biological probe.

    J Solid State Chem 2004, 177:1179-1187. Publisher Full Text OpenURL

  42. Elliot J: Structural and Chemistry of Apatites and other Calcium Ortophosphates. Elsevier, Amsterdam; 1994. OpenURL

  43. Ogston A: Classics in infectious diseases. “On abscesses”.

    Rev Infect Dis 1984, 6(1):122-128. PubMed Abstract | Publisher Full Text OpenURL

  44. Wang JT, Chang SC, Chen YC, Luh KT: Comparison of antimicrobial susceptibility of Citrobacter freundii isolates in two different time periods.

    J Microbiol, Immunol 2000, 33(4):258-262. OpenURL

  45. Lin CH, Huang HT, Chien CC, Tzeng DS, Lung FW: Purple urine bag syndrome in nursing homes: ten elderly case reports and a literature review.

    Clin Interv Aging 2008, 3(4):729-734. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  46. Whalen JG, Mully TW, English JC: Spontaneous Citrobacter freundii infection in an immunocompetent patient.

    Arch Dermatol 2007, 143(1):124-125. PubMed Abstract | Publisher Full Text OpenURL

  47. Podschun R, Ullman U: Klebsiella spp. as nosocomial pathogens: epidemiology, taxonomy, typing methods, and pathogenicity factors.

    Clin Microbiol Rev 1998, 11(4):589-603. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  48. Hejazi A, Falkiner FR: Serratia marcescens.

    J Med Microbiol 1997, 46(11):903-912. PubMed Abstract | Publisher Full Text OpenURL

  49. Shahverdi AR, Fakhimi A, Shahverdi HR, Minaian S: Synthesis and effect of silver nanoparticles on the antibacterial activity of different antibiotics against Staphylococcus aureus and Escherichia coli.

    Nanomed-Nanotechnol 2007, 3:168-171. Publisher Full Text OpenURL

  50. Guzman M, Dille J, Godet S: Synthesis and antibacterial activity of silver nanoparticles against gram-positive and gram-negative bacteria.

    Nanomedicine 2012, 8:37-45. PubMed Abstract | Publisher Full Text OpenURL

  51. Mirzajani F, Ghassempour A, Aliahmadi A, Ali Esmaeili M: Antibacterial effect of silver nanoparticles on Staphylococcus aureus.

    Res Microbiol 2011, 162:542-549. PubMed Abstract | Publisher Full Text OpenURL

  52. Brigita T, Barbara S, Boris O: Antimicrobial activity of AgCl embedded in a silica matrix on cotton fabric.

    Carbohyd Polym 2009, 75:618. Publisher Full Text OpenURL