Figure 3.

Alloy aged at 180°C for 120 h. The incident electron beam was parallel to

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/300/mathml/M11','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/300/mathml/M11">View MathML</a>

in (a-d) and

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/300/mathml/M12','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/300/mathml/M12">View MathML</a>

in (e), respectively. (a)

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/300/mathml/M13','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/300/mathml/M13">View MathML</a>

HAADF image, (b) Zr EDXS map, (c) Zn EDXS map, (d) a combined EDXS map of Zr and Zn and (e)

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/300/mathml/M14','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/300/mathml/M14">View MathML</a>

HAADF image.

Zhu et al. Nanoscale Research Letters 2012 7:300 doi:10.1186/1556-276X-7-300