Open Access Nano Express

Suspended hybrid films assembled from thiol-capped gold nanoparticles

Yu Xin Zhang*, Ming Huang, Xiao Dong Hao, Meng Dong, Xin Lu Li and Jia Mu Huang

Author Affiliations

College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, People's Republic of China

For all author emails, please log on.

Nanoscale Research Letters 2012, 7:295  doi:10.1186/1556-276X-7-295


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/7/1/295


Received:11 May 2012
Accepted:6 June 2012
Published:6 June 2012

© 2012 Haltas et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

In this work, we explored the formation processes of suspended hybrid thin films of thiol-capped Au nanoparticles (AuNPs) inside metal oxide tubular structures. We found that a balance between in-film interactions of the AuNPs and boundary interactions with metal oxides is a key in making these special organic–inorganic thin films. The hybrid films process many processing advantages and flexibilities, such as controllable film thickness, interfacial shape and inter-AuNPs distance, tuning of particle sizes, thiol population, chain lengths, and other new properties by introducing functional groups to thiol chains. Among their many unique features, the assembly-disassembly property may be useful for future on-off or store-release applications.

Keywords:
Nanoparticles; interfaces; thin films; hybrid; self-assembly; disassembly

Background

Ligands (e.g., alkanethiolate, phosphines, amines, peptides, DNA, and polymers) assisted organization of Au nanoparticles (AuNPs) has received great research attention over the past two decades [1-13]. As starting building units, surface-passivated AuNPs have been synthesized into various shapes and sizes [1-16]. Because of the presence of surface ligands, these AuNPs can self-assemble into larger constructs via van der Waals interactions existing among the ligand molecules. For example, superlattices, supported films, supracrystals, and sponges have been constructed with thiol-capped AuNPs [1,2,7,12-15]. In their two-dimensional arrays/assemblies, in particular, monolayer or multilayers of AuNPs have been prepared on solid supports (e.g., typically on polymeric films of transmission electron microscopy (TEM) copper grids) [1,2,7,12,13]. Although a significant research progress has been made, to the best of our knowledge, suspended hybrid films organized from thiol-capped AuNPs have not been reported. In view of their hybrid nature (i.e., organic thiols plus inorganic AuNPs), which can be finely tuned by chemical methods, the self-assembled thin films may provide desirable functionality and porosity for future applications.

In this work, as part of our recent effort in this area, we have prepared suspended hybrid thin films composed of thiol-capped AuNPs. Our findings reveal that inter-particulate interaction among the thiol-stabilized AuNPs plays an important role in film formation, while a certain degree of interaction with boundary materials is also essential in making these organic–inorganic thin films.

Methods

In our synthesis, the AuNPs were synthesized according to a modified two-phase protocol [14-16], in which thiol molecules [1-dodecanethiol (DT) or 3-mercaptopropionic acid (MPA)] were used as surface capping agents for AuNPs (see supporting information (SI)-1 in 1). In a typical film preparation, anodic aluminum oxide (AAO) membrane templates were placed in a glass petri dish, and a drop of AuNP suspension (ca 0.02 mL; standard solution, see SI-1 in 1) was added onto each membrane, followed by a natural drying process. The same procedure was repeated several times in order to attain a desired film thickness. Afterwards, the AAO membranes were immersed in a plastic petri dish that contained an aqueous TiF4 solution (0.04 M) for a selected period of time (30 to 120 min). After the deposition of TiO2 nanotubes on their channels, the AAO membranes were washed with deionized water and air-dried at room temperature. The AAO templates were then removed by immersion in 1 M NaOH solution overnight. The solid products were collected and washed with deionized water and ethanol, followed by vacuum-drying. The product structure, morphology, and composition were investigated by TEM (JEM-2010, JEOL Ltd., Akishima, Tokyo, Japan), energy dispersive X-ray spectroscopy (EDX), and selected area electron diffraction.

Additional file 1:. The file shows eight supporting informations (SI) as follows: (1) synthetic conditions, (2) preparation details for Figure 2 of the main text, (3) DT-capped AuNP films formed inside TiO2 nanotubes (at large magnification), (4) cross-sectional top view on the DT/AuNP films inside TiO2 nanotubes, (5) EDX and results, (6) molecular structures of DT and MPA, (7) MPA-assisted agglomeration of DT-capped AuNPs, and (8) TEM images for representative AuNPs used in this work. (PDF 1207 kb)

Format: PDF Size: 1.2MB Download file

This file can be viewed with: Adobe Acrobat ReaderOpen Data

Results and discussion

Figure 1 depicts two formation routes using two different types of functionalized AuNPs (see SI-1 in 1). The DT-capped AuNPs tend to agglomerate together via van der Waals forces generated among their surface alkyl headgroups, and they have a relatively weak interaction with AAO channels. Upon drying, the DT-capped AuNPs always stay in liquid phase (a, b) and form suspended films inside the AAO channels when the solvent (toluene or cyclohexane) is evaporated (c). Intriguingly, TiO2 nanotubes are grown selectively on the walls of the AAO channels, pushing the AuNP phase upwards (d). Alternatively, the TiO2 nanotubes can be grown firstly onto the AAO channels, and then, the AuNP films are introduced. Other sequential combinations are also viable. All these observations indicate that there is a stronger interaction among the DT-capped AuNPs than that between AuNPs and AAO or TiO2 walls. Figure 2 displays some representative TEM images of our suspended hybrid films assembled from DT-capped AuNPs (see SI-2 in 1). The film thickness can be controlled by the concentration of AuNPs and number of times that the AuNP solution is applied to the AAO membranes. On the other hand, the wall thickness of TiO2 nanotubes can also be manipulated by the concentration of TiF4 and hydrolysis time. As can be seen (see SI-3 in 1), the DT-capped AuNPs are located exclusively in the interiors of TiO2 nanotubes, and the smooth film surface reveals a concave shape of air-liquid (containing AuNPs) interface during the drying. Due to the hydrophobicity of the alkyl capping on the AuNPs, the shape of this interface was essentially maintained upon the TiO2 growth, AAO dissolution, and washing treatment, where polar solvents (e.g., mostly water) were used; it is further affirmed that the assembled films are completely bounded with circumferences of TiO2 nanotubes (see SI-4 in 1). The composition of the prepared products was also investigated with EDX (see SI-5 in 1), which confirms the formation process illustrated in Figure 1 phases a to e.

thumbnailFigure 1. Schematic illustrations. (a to e) Formation of DT-capped AuNP hybrid films suspended inside TiO2 nanotubes and (f to g) formation of MPA-DT-capped AuNP-imbedded TiO2 nanotubes. Orange spheres represent AuNPs; black lines around AuNPs represent DT thiols; red lines around AuNPs represent MPA-DT thiols. Light blue backgrounds stand for a liquid phase (solvent: toluene or cyclohexane), grey vertical lines for AAO channels, and purple vertical lines for TiO2 nanotubes.

thumbnailFigure 2. TEM images. (a to p) Concave hybrid films made from DT-capped AuNPs. See Additional file 1 (SI-2) for more information on these samples.

When bifunctional thiol MPA is also introduced to the surface of AuNPs (see SI-1 in 1), the interaction between the AuNPs and AAO channel walls is significantly increased (Figure 1, phases f to i) since the carboxylate headgroups of MPA (see SI-6 in 1) are chemisorbed on Lewis acid sites of the AAO surface (Al3+ ions). In such a case, the MPA-DT-capped AuNPs can readily adsorb on the surface of AAO even when they are in a solution phase (Figure 1,phases f and g). During the growth of TiO2 nanotubes, the AuNPs are not relocated, and thus, they are incorporated (Figure 1, phases h to j) in the walls of TiO2 nanotubes, as seen in (Figure 3e,f). It is interesting to mention that these AuNPs aggregated into small islands (Figure 3; Figure 1, phases f and g) with a monolayer thickness, which indicates that there are weaker lateral interactions among the AuNPs through their long-chain DT molecules while MPA serves as a binder to the metal oxides [17]. Because they were immobile in the TiO2 matrix, the AuNPs did not grow much after the thermal treatment (Figure 3 g,h).

thumbnailFigure 3. TEM images. TiO2 nanotubes imbedded with MPA-DT-capped AuNPs: (a to d) thick-walled nanotubes; (e,f) thin-walled nanotubes; and (g,h) thin-walled nanotubes after being heated at 250°C for 30 min. The imbedded AuNPs can be seen with the guide of white arrows.

Apart from the concave interfaces (H-shape, Figure 2), convex interfaces can also be attained. We find that when MPA is added to the existing DT-capped AuNPs, spherical aggregation takes place (see SI-7 in 1). In this work, convex or flat interfaces have been prepared with addition of MPA, as shown in Figure 4. It is believed that in this case, MPA serves primarily as a surfactant on the surface of AuNP aggregates. Since carboxylate groups are hydrophilic (see SI-6 in 1), the AuNPs become less soluble in toluene or cyclohexane and tend to form convex or flat surfaces (Figure 4).

thumbnailFigure 4. TEM images. Convex or flat hybrid films made from DT-capped AuNPs (with aid of MPA): (a,b) a spherical type film at different magnifications, (c to f) flat films, and flat films after being heated (g) at 150°C for 120 min and (h) at 250°C for 120 min.

Concerning their applications, we note that this type of hybrid films (or hybrid membranes) possesses many structural advantages and processing flexibilities: (1) AuNPs (or other metallic NPs) can be tuned with different sizes (e.g., monodisperse AuNPs, 2.1 ± 0.3 nm and 6.2 ± 0.6 nm; see SI-8 in 1); (2) inter-AuNP distance depends on the thiol population and chain lengths (e.g., 3.8 ± 0.4 nm and 8.6 ± 0.5 nm; see SI-8 in 1); (3) film thickness and interfacial shape can be engineered; and (4) new properties can be obtained by introducing functional groups to thiol chains. All these control factors will determine the final porosity and functionality of the suspended hybrid films in future applications (e.g., gas separation). For instance, these films can be used as a catalyst or a sealant for the enclosure of nano test tubes [18-20]. At a relatively low temperature, the AuNPs in these films are readily fused into single metallic gold plugs at 150°C to 250°C, as reported in Figure 4 g,h. On the other hand, while they are very stable in aqueous solution, the suspended hybrid films of AuNPs are soluble (and thus removable) in common organic solvents such as toluene and cyclohexane. The assembly-disassembly property that these films possess may be useful for on-off or store-release operations.

Conclusions

In summary, we have explored the formation processes of suspended hybrid thin films of thiol-capped AuNPs inside metal oxide tubular structures. It has been found that a balance between the in-film interactions of the AuNPs and boundary interactions with metal oxides is a key in making these organic–inorganic thin films. Among many unique features, the assembly-disassembly property may be useful for on-off or store-release applications.

Abbreviations

AAO, Anodic aluminum oxide; AuNPs, Au nanoparticles; DT, 1-dodecanethiol; EDX, Energy dispersive X-ray spectroscopy; MPA, 3-mercaptopropionic acid; SI, Supporting information; TEM, Transmission electron microscopy.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

ZYX synthesized and characterized the hybrid films and wrote the manuscript. HM prepared the gold nanoparticles and TiO2 nanotubes. HXD and DM conceived and designed the experiments. LXL and HJM coordinated the study. All authors read and approved the final manuscript.

Acknowledgments

The authors gratefully acknowledge the financial support of the National Natural Science Foundation of China (Grant No. 51104194), Doctoral Fund of Ministry of Education of China (20110191120014), No.43 Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry, and Natural Science Foundation Project of CQ CSTC (CSTS2010BB4058). Dr. Zhang gratefully acknowledges Prof. Zeng Hua Chun for his kind discussions and the National University of Singapore for their technical supports.

References

  1. Kiely CJ, Fink J, Brust M, Bethell D, Schiffrin DJ: Spontaneous ordering of bimodal ensembles of nanoscopic gold clusters.

    Nature 1998, 396:444-446. Publisher Full Text OpenURL

  2. Fan HY, Yang K, Boye DM, Sigmon T, Malloy KJ, Xu HF, Lopez GP, Brinker CJ: Self-assembly of ordered, robust, three-dimensional gold nanocrystal/silica arrays.

    Science 2004, 304:567-571. PubMed Abstract | Publisher Full Text OpenURL

  3. Deng ZX, Tian Y, Lee SH, Ribbe AE, Mao CD: DNA-encoded self-assembly of gold nanoparticles into one-dimensional arrays.

    Angew Chem Int Ed 2005, 44:3582-3585. Publisher Full Text OpenURL

  4. Gao XY, Djalali R, Haboosheh A, Samson J, Nuraje N, Matsui H: Peptide nanotubes: Simple separation using size-exclusion columns and use as templates for fabricating one-dimensional single chains of an nanoparticles.

    Adv Mater 2005, 17:1753-1757. Publisher Full Text OpenURL

  5. Fresco ZM, Frechet JMJ: Selective surface activation of a functional monolayer for the fabrication of nanometer scale thiol patterns and directed self-assembly of gold nanoparticles.

    J Am Chem Soc 2005, 127:8302-8303. PubMed Abstract | Publisher Full Text OpenURL

  6. Lin S, Li M, Dujardin E, Girard C, Mann S: One-dimensional plasmon coupling by facile self-assembly of gold nanoparticles into branched chain networks.

    Adv Mater 2005, 17:2553-2559. Publisher Full Text OpenURL

  7. Fan HY, Leve E, Gabaldon J, Wright A, Haddad RE, Brinker CJ: Ordered two- and three-dimensional arrays self-assembled from water-soluble nanocrystal-micelles.

    Adv Mater 2005, 17:2587-2590. Publisher Full Text OpenURL

  8. Li CF, Li DX, Wan GQ, XuJie , Hou WG: Facile synthesis of concentrated gold nanoparticles with low size-distribution in water: temperature and pH controls.

    Nanoscale Res Lett 2011, 6:440. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  9. Gao J, Huang X, Liu H, Zan F, Ren J: Colloidal stability of gold nanoparticles modified with thiol compounds: bioconjugation and application in cancer cell imaging.

    Langmuir 2012, 28:4464-4471. PubMed Abstract | Publisher Full Text OpenURL

  10. Wang YQ, Liang WS, Geng CY: Coalescence behavior of gold nanoparticles.

    Nanoscale Res Lett 2009, 4:684. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  11. Biswas M, Dinda E, Rashid MH, Mandal TK: Correlation between catalytic activity and surface ligands of monolayer protected gold nanoparticles.

    J Colloid Interface Sci 2012, 368:77-85. PubMed Abstract | Publisher Full Text OpenURL

  12. Wang Y, Zeiri O, Neyman A, Stellacci F, Weinstock IA: Nucleation and island growth of alkanethiolate ligand domains on gold nanoparticles.

    ACS Nano 2012, 6:629-640. PubMed Abstract | Publisher Full Text OpenURL

  13. Tosoni S, Boese AD, Sauer J: Interaction between gold atoms and thio-aryl ligands on the Au(111) surface.

    J Phys Chem C 2011, 115:24871-24879. Publisher Full Text OpenURL

  14. Zhang YX, Zeng HC: Template-free parallel one-dimensional assembly of gold nanoparticles.

    J Phys Chem B 2006, 110:16812-16815. PubMed Abstract | Publisher Full Text OpenURL

  15. Zhang YX, Zeng HC: Surfactant-mediated self-assembly of Au nanoparticles and their related conversion to complex mesoporous structures.

    Langmuir 2008, 24:3740-3746. PubMed Abstract | Publisher Full Text OpenURL

  16. Manea F, Bindoli C, Polizzi S, Lay L, Scrimin P: Expeditious synthesis of water-soluble, monolayer-protected gold nanoparticles of controlled size and monolayer composition.

    Langmuir 2008, 24:4120-4124. PubMed Abstract | Publisher Full Text OpenURL

  17. Li J, Zeng HC: Preparation of monodisperse Au/TiO2 nanocatalysts via self-assembly.

    Chem Mater 2006, 18:4270-4277. Publisher Full Text OpenURL

  18. Li J, Zeng HC: Nanoreactors - size tuning, functionalization, and reactivation of Au in TiO2 nanoreactors.

    Angew Chem Int Ed 2005, 44:4342-4345. Publisher Full Text OpenURL

  19. Hillebrenner H, Buyukserin F, Kang M, Mota MO, Stewart JD, Martin CR: Corking nano test tubes by chemical self-assembly.

    J Am Chem Soc 2006, 128:4236-4237. PubMed Abstract | Publisher Full Text OpenURL

  20. Y-n Z, Zhao G, Lei Y, Wu Z, Jin Y, Li M: Novel construction of CdS-encapsulated TiO2 nano test tubes corked with ZnO nanorods.

    Mater Lett 2010, 64:2194-2196. Publisher Full Text OpenURL