TEM BFI, SAED, and lattice image of rice-like tenorite nanoclusters with tilt boundary and dislocation. TEM (a) BFI (left) coupled with SAED pattern (right) of the (Zn,H)-codoped tenorite nanocondensate clusters with slightly preferred orientation of (111) plane. (b) Lattice image of the individual tenorite nanocondensates ca. 5 nm in size which tended to coalesce over (111) to form (111) symmetrical tilt boundary with (<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/272/mathml/M3','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/272/mathml/M3">View MathML</a>) plane off by 20° as indicated by 2-D forward (c) and inverse Fourier transform (d) of the square region near the [101] zone axis. Note also dislocations (denoted as T) with (<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/272/mathml/M4','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/272/mathml/M4">View MathML</a>) half plane at the interface. The same sample as in Figure 6.

Lin et al. Nanoscale Research Letters 2012 7:272   doi:10.1186/1556-276X-7-272
Download authors' original image