Ultra-long Pt nanolawns supported on TiO2-coated carbon fibers as 3D hybrid catalyst for methanol oxidation

Yu-Lin Shen1, Shih-Yun Chen2, Jenn-Ming Song3* and In-Gann Chen4

Author Affiliations

1 Graduate Institute of Applied Science and Technology, National Taiwan University of Science and Technology, Taipei, 106, Taiwan

2 Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei, 106, Taiwan

3 Department of Materials Science and Engineering, National Chung Hsing University, Taichung, 402, Taiwan

4 Department of Materials Science and Engineering, National Cheng Kung University, Tainan, 701, Taiwan

For all author emails, please log on.

Nanoscale Research Letters 2012, 7:237  doi:10.1186/1556-276X-7-237


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/7/1/237


Received:14 January 2012
Accepted:30 April 2012
Published:26 June 2012

© 2012 Shen et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

In this study, TiO2 thin film photocatalyst on carbon fibers was used to synthesize ultra-long single crystalline Pt nanowires via a simple photoreduction route (thermally activated photoreduction). It also acted as a co-catalytic material with Pt. Taking advantage of the high-aspect ratio of the Pt nanostructure as well as the excellent catalytic activity of TiO2, this hybrid structure has the great potential as the active anode in direct methanol fuel cells. The electrochemical results indicate that TiO2 is capable of transforming CO-like poisoning species on the Pt surface during methanol oxidation and contributes to a high CO tolerance of this Pt nanowire/TiO2 hybrid structure.

Keywords:
Pt nanowires; Hybrid catalyst; Methanol oxidation; Thermally activated photoreduction

Background

In recent years, direct methanol fuel cell (DMFC) has attracted great attention as an alternative power source because of their many advantages, including light weight, high power density, portability, and storage of liquid fuel [1,2]. For most of the common DMFC devices, Pt-based catalysts have been used as an anode because of their outstanding performance in catalyzing the dehydrogenation of methanol. However, the commercialization of DMFC device still faces some problems, such as CO adsorption on Pt catalysts and thus poisoning [3,4]. Even a low concentration of CO will cause a remarkable decrease in catalytic activity of Pt-based electrodes. Therefore, the majority of the Pt-based electrocatalyst research has focused on this topic.

In addition to alloying [5,6], there are two other strategies for improving the Pt-based catalyst's performance. The first is to modify the morphology of Pt nanostructure, including the shape as well as the dimension. It has been demonstrated that changing the morphology of the Pt nanostructure from nanoparticle (NP) to nanowire (NW) can enhance the electrocatalytic activity of the catalysts, due to the large side surface which is able to provide additional catalytic active facets [7,8]. A great deal of effort has been devoted to the synthesis of one-dimensional Pt nanostructures; however, it still remains a huge challenge to synthesize long and oriented single-crystalline Pt NWs without temperates and surfactants. Lee et al. [9,10] have demonstrated the synthesis of single crystalline Pt NWs on polymeric, ceramic, or metallic substrate by a polyol process, combined with a trace addition of iron species (Fe2+ or Fe3+) and poly(vinylpyrrolidone) (PVP) as the surfactant. Cetyltrimethylammonium bromide (CTAB) has also been applied in the reduction of Pt ions to Pt NWs [7,11]. Moreover, without using templates and surfactants, HCOOH [12-15] and vitamin B2[16] have been suggested respectively to act as reductant agents in the chemical routes for the synthesis of Pt NWs. Through the above processes, the Pt NWs produced are extremely fine (mostly less than 10 nm in diameter) but exhibit a limit in length of about 200 nm so that their aspect ratios do not exceed 50.

The next tactic to enhance the catalyst activity and CO-tolerance is the development of new composites and catalytic supporting materials. In the last decade, the addition of oxides has been generally accepted as an efficient way to improve catalytic activity of platinum and its CO-tolerance for methanol electro-oxidation. For example, Cui et al. [17] found that the Pt-WO3/C composite catalysts exhibit excellent catalytic activity and stability for methanol electro-oxidation because WO3 is able to form the hydrogen-tungsten-bronze compound, which facilitates dehydrogenation during methanol oxidation reaction. RuO2, ZrO2, and MgO have also been studied and it was found that they can improve the catalytic performance of Pt [18-20]. A promising breakthrough is that the composites of Pt or Pt-Ru nanoparticles and semiconductor catalysts such as TiO2 and CeO2 have been developed as the anode for oxidation of methanol or ethanol [21-24]. It has been proposed that the Pt-CeO2 composite catalyst has a higher activity than Pt catalyst because CeO2 makes CO electro-oxidation easier. The redox reaction on the surface of CeO2 mixing with Pt particles causes the oxidation of CO to CO2 and thus gives rise to a better performance. Drew et al. [22] verified that TiO2 can enhance the current generation especially under ultraviolet (UV) light irradiation during the electrochemical testing and suggested that the holes formed upon UV illumination are consumed in methanol oxidation and bring about the additional current.

In view of the above description, this study aims to develop highly efficient three-dimensional composite electrode catalysts with Pt NWs grown on oxide-coated carbon fibers. A recently developed process, thermally assisted photoreduction (TAP) [25,26], was applied to prepare ultra-long metallic nanowires through the photocatalysis of TiO2. According to the Honda-Fujishima effect [27], electrons and holes on the surface of TiO2 films can be activated by UV light, which enables the reduction of metallic ions from the solution. The photoreduction process of metallic ions (M+) can be expressed briefly as follows,

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/237/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/237/mathml/M1">View MathML</a>

(1)

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/237/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/237/mathml/M2">View MathML</a>

(2)

Based on this, metallic nanowires can be formed on the surface of thin-film TiO2 via the photoreduction of metallic ions under certain irradiating and heating conditions. Instead of commonly used H2PtCl6, Na2Pt(OH)6 was selected as the precursor in this work.

Methods

The whole route for the synthesis of Pt NWs was illustrated in Figure 1. To make gel coating TiO2 films, the carbon fibers sheet in the size of 1 × 1 cm was dipped into the TiO2 solution. The carbon fiber sheets used were with a thickness of 360 μm and basis weight of 125 g/m2. After dipping, the weight gain per sample by absorption of TiO2 solution was 0.035 g. The dipped samples were then annealed at 500°C for 8 h in an oxygen atmosphere to obtain well crystallized anatase TiO2 (step 1 in Figure 1). The TiO2 solution used was prepared with isopropylalcohol (IPA)/titanium isopropoxide (TTIP)/hydrogen chloride (HCl) with the volume ratio 170:12:0.4 and stirred for 10 min at room temperature (20°C) before aging for 2 days. The weight of TiO2 on a 1 cm2 carbon fiber sample after annealing was measured to be 0.012 g (3.1 × 10−3 cm3 in volume). Fifteen microliters of 0.05 M Na2Pt(OH)6 aqueous salt solution was dropped on the TiO2 coated substrates (step 2). Afterward, the samples were isothermally heated at 300°C for 3 h in air by an infrared furnace, followed by a furnace-cooling to the ambient temperature (namely, the post thermal treatment, step 3 in Figure 1).

thumbnailFigure 1. Schematic illustration of the main steps for forming Pt nanowires by thermally assisted photoreduction.

It has been demonstrated that the extent of UV exposure on the TiO2 film affects the degree of excitation and thus strongly influences the shape and dimension of the reduced metallic structure [25]. In order to obtain reduced Pt with different morphologies and sizes, we varied the conditions of pre-UV exposure treatment performed on the annealed TiO2-coated carbon cloths before the growth of the nanowires (between the step 1 and step 2). The conditions included (1) no pre-UV light exposure, (2) pre-UV exposure on only one side of the carbon cloths for 48 h, and (3) pre-UV exposure on each side of carbon cloths for 12 h alternately to reach a total exposure time of 48 h. It is assumed that on the exposed side of the carbon cloth the TiO2 was excited. Therefore, the whole TiO2 film was presumed to be fully excited.

Electrochemical measurements of the hybrid electrocatalysts were performed in a three-electrode cell using an Autolab PG302N work station (Metrohm, Autolab BV, Utrecht, The Netherlands) at room temperature to evaluate their catalytic performance. Carbon cloths (0.25 cm2) with Pt-TiO2 catalysts were the working electrode. A Pt rod and Ag/AgCl were used as counter and reference electrodes, respectively. A solution of 1 M CH3OH and 0.5 M H2SO4 was used as the electrolyte. All the reagents used were of analytical grade. The cyclic voltammetry data for methanol electro-oxidation were recorded in the potential range of −0.2 to 1.0 V vs. Ag/AgCl with a scan rate of 20 mVs−1.

Results and discussion

After heating Na2Pt(OH)6 solution at 300°C for 3 h, the scanning electron microscopy image shown in Figure 2a illustrates that all the Pt salt was transformed into Pt NWs grown radially on both sides of the carbon cloths under no pre-UV exposure condition (condition 1), with an average diameter of about 40 nm and remarkable length of 1 to approximately 2 μm. Most of the NWs exhibit an aspect ratio ranging from 25 to 50. Of particular interest is, after long duration of pre-UV irradiation, microsized Pt nodules formed on the UV-exposed portion of the carbon cloths instead of nanowires. Figure 2b indicates that the samples under the condition 2 showed a Janus feature. That is, Pt microparticles (MP) grew on the exposed side (the upper side) of the carbon cloth, while the unexposed side (the underneath side) was with Pt nanowires. Furthermore, the surface of the two-side exposed carbon cloths in the condition 3 was completely covered with Pt microparticles (Figure 2c). Accordingly, these three structures are designated as NW/TiO2, NW + MP/TiO2, and MP/TiO2, respectively.

thumbnailFigure 2. Morphologies of the reduced Pt on TiO2coated carbon cloths with different UV exposure conditions. (a) no pre-UV-irradiated (b) one side-UV irradiated, (c) both side-UV irradiated.

The grazing angle X-ray diffraction (XRD) patterns, in Figure 3a, verify that those reduced structures on the TiO2 coating were all platinum. Figure 3b shows a high-resolution transmission electron microscopy (HR-TEM) image and energy dispersive spectrometer (EDS) spectrum of a Pt nanowire. The HR-TEM image shows the lattice spacing between the {111} planes to be 0.228 nm, which was in agreement with the value in the bulk Pt crystal, suggesting the Pt NWs grew along <111> axes, and the EDS spectrum demonstrates that the NWs thus produced were pure Pt without any detectable impurity. The inserted electron diffraction pattern constructed by the fast Fourier transform also verifies the preferred growth direction to be <111>. Similar results have been reported in our previous work [28].

thumbnailFigure 3. XRD patterns of Pt/TiO2hybrid structures, the HR-TEM image and EDS analytical results of a Pt nanowire. (a) XRD patterns of Pt/TiO2 hybrid structures shown in Figure 2, (b) the HR-TEM image and EDS analysis of a Pt nanowire (the Cu signal comes from the Cu grids).

Figure 4a illustrates the standard cyclic voltammogram curves (the 5th cycle) for methanol electro-oxidation on carbon fiber-supported Pt-TiO2 structures. For all the samples, a methanol oxidation peak appeared in the forward scan and a reoxidation peak was detected on the reverse sweep. Obtained from the cyclic voltammetry (CV) curves in Figure 4a, the maximum current density of the forward peak (If) and that of the backward peak (Ib), as well as their ratio, If/Ib, are given in Table 1, indicating the differences in electrochemical behavior. The forward and backward peak current densities (If and Ib) of the MP/TiO2 samples were greater than NW + MP/TiO2, which was in turn higher than NW/TiO2 samples. Also, the onset potential in the forward scan of the MP/TiO2 samples was 0.349, slightly lower than the others. Remarkably, the If/Ib value, which could be used to infer the CO tolerance of the catalysts, in a decreasing order was NW/TiO2 (2.00), NW + MP/TiO2 (1.52), and then MP/TiO2 (1.19). According to the results of Figure 4a, Figure 4b combines the data distribution of the forward peak current density and corresponding CO tolerance, indicating that NW/TiO2 catalysts exhibited higher CO tolerance but inferior current generation ability compared to MP/TiO2 mainly due to the limited amount of reduced Pt.

thumbnailFigure 4. Electrochemical performance of the Pt/TiO2hybrid structures with different morphologies. Electrochemical performance of the Pt/TiO2 hybrid structures with different morphologies in the solution of 1 M CH3OH and 0.5 M H2SO4 with a scan rate of 20 mVs−1: (a) cyclic voltammograms and (b) CO tolerance vs. forward peak current density.

Table 1. Electrochemical characteristics of the specimens during CV analysis (derived from the CV curves in Figure4a)

The excellent performance in CO tolerance of the NW/TiO2 samples can be explained that the high aspect ratio of the NWs leaving most of the TiO2 film uncovered and allowing for subsequent reactions [22], which were similar to those in the CeO2-Pt composites [29].

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/237/mathml/M3','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/237/mathml/M3">View MathML</a>

(3)

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/237/mathml/M4','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/237/mathml/M4">View MathML</a>

(4)

The OHads species (ads, adsorbed) on TiO2, obtained through the activation of water, can transform CO-like poisoning species (COads) on the Pt surface, produced by the methanol dehydrogenation, to CO2 and release active Pt for further catalysis.

The TAP process needs to be improved to obtain a higher population of Pt NWs and thus raises the catalytic activity for methanol oxidation. If this is done, it can be expected that the excellent performance in CO tolerance can be maintained because the high-aspect-ratio Pt NWs occupy only a small part of the fiber surface and leave most the TiO2 film free for oxidation of CO.

Conclusions

By means of templateless and surfactant-free method, TAP, this study successfully prepared carbon fibers supported Pt nanowires/TiO2 composite electrocatalysts, which show great potential for use as active anode in direct methanol fuel cells. Analytical results suggest that the Pt nanowires were single crystalline with a preferred <111> growth direction and exhibited an aspect ratio ranged between 25 and 50. This Pt nanowire/TiO2 hybrid structure possessed high CO tolerance because TiO2 enhances CO electro-oxidation and thus increases CO poisoning resistance. An optimal performance in catalytic activity for methanol oxidation and CO tolerance can be expected if the density of the Pt nanowires is increased further.

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

Y-LS carried out the main part of synthetic and analytical works, participated in the sequence alignment and drafted the manuscript. S-YC participated in the discussion of the growth mechanism. J-MS participated in the design of the study, draft preparation and coordination. I-GC conceived of the study and participated in its design. All authors read and approved the final manuscript.

Authors’ information

YLS is a PHD student at Graduate Institute of Applied Science and Technology, National Taiwan University of Science and Technology, Taipei 106, Taiwan. SYC is an associate professor in the Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei 106, Taiwan. JMS is an associate professor in the Department of Materials Science and Engineering, National Chung Hsing University, Taichung 402, Taiwan. IGC is a distinguished professor from the Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan.

Acknowledgments

We thank the National Science Council of Taiwan for funding NSC 100-2120-M-006-006 and National Cheng Kung University Project of Promoting Academic Excellence and Developing World Class Research Center: D98-R048 for support of this work.

References

  1. Hogarth MP, Hards GA: Direct methanol fuel cells.

    Platinum Metals Rev 1996, 40:150. OpenURL

  2. Casalegno A, Santoro C, Rinaldi F, Marchesi R: Low methanol crossover and high efficiency direct methanol fuel cell: the influence of diffusion layers.

    J Power Sources 2011, 196:2669. Publisher Full Text OpenURL

  3. Zhiani M, Rezaei B, Jalili J: Methanol electro-oxidation on Pt/C modified by polyaniline nanofibers for DMFC applications.

    Int J Hydrog Energy 2010, 35:9298. Publisher Full Text OpenURL

  4. Hamnett A: Mechanism and electrocatalysis in the direct methanol fuel cell.

    Catal Today 1997, 38:445. Publisher Full Text OpenURL

  5. Zhao HB, Yang J, Li L, Li H, Wang JL, Zhang YM: Effect of overoxidation treatment of Pt-Co/polypyrrole-carbon nanotube catalysts on methanol oxidation.

    Int J Hydrog Energy 2009, 34:3908. Publisher Full Text OpenURL

  6. Ross PN: Characterization of alloy electrocatalysts for direct oxidation of methanol: new methods.

    Electrochim Acta 2053, 1991:36. OpenURL

  7. Song Y, Garcia RM, Dorin RM, Wang H, Qiu Y, Coker EN, Steen WA, Miller JE, Shelnutt J: Synthesis of platinum nanowire networks using a soft template.

    Nano Lett 2007, 7:3650. PubMed Abstract | Publisher Full Text OpenURL

  8. Guo YG, Hu JS, Zhang HM, Liang HP, Wan LJ, Bai CL: Tin/platinum bimetallic nanotube array and its electrocatalytic activity for methanol oxidation.

    Adv Mater 2005, 17:746. Publisher Full Text OpenURL

  9. Lee EP, Chen J, Yin Y, Campbell CT, Xia Y: Pd-catalyzed growth of Pt nanoparticles or nanowires as dense coatings on polymeric and ceramic particulate supports.

    Adv Mater 2006, 18:3271. Publisher Full Text OpenURL

  10. Lee EP, Peng Z, Cate DM, Yang H, Campbell CT, Xia Y: Growing Pt nanowires as a densely packed array on metal gauze.

    J Am Chem Soc 2007, 129:10634. PubMed Abstract | Publisher Full Text OpenURL

  11. Krishnawamy R, Remita H, Imperor-Clerc M, Even C, Davidson P, Pansu B: Synthesis of single-crystalline platinum nanorods within a soft crystalline surfactant-PtII complex.

    Chem Phys Chem 2006, 7:1510. PubMed Abstract | Publisher Full Text OpenURL

  12. Sun S, Zang G, Geng D, Chen Y, Banis MN, Li R, Cai M, Sun X: Direct growth of single crystal Pt nanowires on Sn@CNT nanocable: 3D electrodes for highly active electrocatalysts.

    Chem Eur J 2010, 16:829. PubMed Abstract | Publisher Full Text OpenURL

  13. Sun S, Jaouen F, Dodelet J: Controlled growth of Pt nanowires on carbon nanospheres and their enhanced performance as electrocatalysts in PEM fuel cells.

    Adv Mater 2008, 20:3900. Publisher Full Text OpenURL

  14. Sun SH, Yang DQ, Villers D, Zhang GX, Sacher E, Dodelet JP: Template- and surfactant-free room temperature synthesis of self-assembled 3D Pt nanoflowers from single-crystal nanowires.

    Adv Mater 2008, 20:571. Publisher Full Text OpenURL

  15. Sun S, Yang D, Zhang G, Sacher E, Dodelet J: Synthesis and characterization of platinum nanowire-carbon nanotube heterostructures.

    Chem Mater 2007, 19:6376. Publisher Full Text OpenURL

  16. Nadagouda MN, Varma RS: Green and controlled synthesis of gold and platinum nanomaterials using vitamin B2: density-assisted self-assembly of nanospheres, wires and rods.

    Green Chem 2006, 8:516. Publisher Full Text OpenURL

  17. Cui Z, Feng L, Liu C, Xing W: Pt nanoparticles supported on WO3/C hybrid materials and their electrocatalytic activity for methanol electro-oxidation.

    J Power Sources 2011, 196:2621. Publisher Full Text OpenURL

  18. Peng F, Zhou C, Wang H, Yu H, Liang J, Yang J: The role of RuO2 in the electrocatalytic oxidation of methanol for direct methanol fuel cell.

    Catal Commun 2009, 10:533. Publisher Full Text OpenURL

  19. Silva VS, Schirmer J, Reissner R, Ruffmann B, Silva H: Proton electrolyte membrane properties and direct methanol fuel cell performance.

    J Power Sources 2005, 140:41. Publisher Full Text OpenURL

  20. Xu C, Shen P, Ji X, Zeng R, Liu Y: Enhanced activity for ethanol electrooxidation on Pt-MgO/C catalysts.

    Electrochem Commun 2005, 7:1305. Publisher Full Text OpenURL

  21. Zhang H, Zhou W, Du Y, Yang P, Wang C, Xu J: Enhanced electrocatalytic performance for methanol oxidation on Pt/TiO2/ITO electrode under UV illumination.

    Int J Hydrog Energy 2010, 35:13290. Publisher Full Text OpenURL

  22. Drew K, Girishkumar G, Vinodgopal K, Kamat PV: Boosting fuel cell performance with a semiconductor photocatalyst: TiO2/Pt-Ru hybrid catalyst for methanol oxidation.

    J Phys Chem B 2005, 109:11851. PubMed Abstract | Publisher Full Text OpenURL

  23. Mori T, Takahashi M, Suga T, Drennan J: Development of high quality Pt-CeO2 composite anode for direct methanol fuel cell applications. In In Proceeding of Polymers and Adhesives in Microelectronics and Photonics, 2007. Polytronic:Tokyo, Tokyo; 2007:51. OpenURL

  24. Wang XY, Jiang YS, Zhang HZ, JC: Development of high quality Pt-CeO2 composite anode for direct methanol fuel cell applications.

    Chem Res Chinese Universities 2011, 27:486. OpenURL

  25. Tung HT, Chen IG, Song JM, Yen CW: Thermal-assisted photoreduction of vertical silver nanowires.

    J Mater Chem 2009, 19:2386. Publisher Full Text OpenURL

  26. Tung HT, Song JM, Dong TY, Hwang WS, Chen IG: Synthesis of surfactant-free aligned single crystal copper nanowires by thermal-assisted photoreduction.

    Cryst Growth Des 2008, 8:3415. Publisher Full Text OpenURL

  27. Fujishima A, Honda K: Electrochemical photolysis of water at a semiconductor electrode.

    Nature 1972, 238:37. PubMed Abstract | Publisher Full Text OpenURL

  28. Shen YL, Chen SY, Song JM, Chin TK, Lin CH, Chen IG: Direct growth of ultra-long platinum nanolawns on a semiconductor photocatalyst.

    Nanoscale Res Lett 2011, 6:380. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  29. Scibioh MA, Kim SK, Cho EA, Lim TH, Hong SA, Ha HY: Pt-CeO2/C anode catalyst for direct methanol fuel cells.

    Appl Catal B 2008, 84:773. Publisher Full Text OpenURL