Table 2
EIS parameters in equivalent circuit for the bare and coated 316 L systems
Samples	Rs(Ω)	Q2		R2(Ω)	Q1		R1(Ω)
		Y0	n		Y0	n
Bare 316 L	31.22	―	―	―	9.984 × 10−6	0.8635	1.803 × 105
TiO2	29.85	1.632 × 10−5	0.7882	8.797 × 102	5.368 × 10−5	0.8053	3.177 × 105
0.2%Ce-TiO2	30.63	1.738 × 10−7	0.7969	6.736 × 103	7.309 × 10−7	0.8541	3.905 × 106
1.2%Ce-TiO2	31.08	1.412 × 10−8	0.8376	4.853 × 104	1.952 × 10−7	0.8835	4.581 × 107
2.2%Ce-TiO2	29.92	1.979 × 10−5	0.7213	6.447 × 102	1.355 × 10−5	0.8223	1.495 × 106

Li et al. Nanoscale Research Letters 2012 7:227   doi:10.1186/1556-276X-7-227