In this paper, we describe a method of amorphous silicon carbide film formation for a solar cell passivation layer. The film was deposited on p-type silicon (100) and glass substrates by an RF magnetron co-sputtering system using a Si target and a C target at a room-temperature condition. Several different SiC [Si1-xCx] film compositions were achieved by controlling the Si target power with a fixed C target power at 150 W. Then, structural, optical, and electrical properties of the Si1-xCx films were studied. The structural properties were investigated by transmission electron microscopy and secondary ion mass spectrometry. The optical properties were achieved by UV-visible spectroscopy and ellipsometry. The performance of Si1-xCx passivation was explored by carrier lifetime measurement.
Keywords:a-Si1-xCx; passivation layer; RF magnetron co-sputtering system; carrier lifetime; solar cell
Semiconductor technology or microelectronics including solar cells has been adopted to form micro- or nano-sized state-of-the-art structures which can reduce system size, improve its performance, achieve lower system cost, and so on [1-3]. Generally, a semiconductor structure or system is manufactured by a combination of additive (film deposition) and subtractive (etching) processes. These days, many research have tried to utilize the microelectronic technology (especially in the deposition of thin film layers) to get more efficient and cost-effective solar cells [4,5].
Amorphous silicon-based thin film layers (SiO2, SiN, a-SiC:H, and so on) for antireflection coatings, diffusion barriers, passivation layers, and silicon bulk materials have been broadly researched in the solar cell industry. Among the film layers, SiO2 and SiN passivation layers have highly attracted to fabricate high-efficiency silicon solar cells. However, they have negative demerits such as the need for a high-temperature process, difficulty in the photolithography process, and poor thermal stability [6-8]. Hydrogenated amorphous silicon carbide [a-SiC:H] has been studied for solar cell passivation layers due to its wide bandgap, excellent coefficient of thermal expansion that matches with silicon wafers, relatively good thermal and mechanical stabilities, superior cost-of-ownership compared to other materials, and so on. The formation or deposition of the a-SiC:H film has mainly been done by plasma-enhanced chemical vapor deposition [9,10]. However, the thermal stability of the hydrogen-containing film is degraded during a post-high-temperature firing process. To avoid the hydrogen molecule's void generation, the authors have proposed an a-SiC deposition method by radio frequency [RF] sputtering which was performed by a single silicon-carbide composite target in an argon environment . In this paper, we introduce a deposition method of amorphous silicon carbide [a-Si1-xCx] which was done by RF magnetron co-sputtering. The method can utilize multiple targets (in this paper, Si and C) simultaneously in order to deposit complex compositional coatings. The compositional ratio can be controlled by the differences in sputtering yield, the relative ability of the materials to stick to the substrate, the deposition temperature, and the relevant percent of sputtered elements to reach the substrate without being scattered from the plasma. In this paper, we investigate several properties of the compositional films by controlling the Si target's RF power. Film thickness was measured using a field-emission scanning electron microscope [FE-SEM]. Reflective index of the film was obtained using an ellipsometer, and carrier lifetime of the film on the doped p-type silicon wafer was obtained by a silicon wafer lifetime tester.
The a-Si1-xCx passivation layer was deposited on 2 × 7-cm glass substrates and 4-inch p-type silicon (100) wafers using an RF magnetron co-sputtering system. Figure 1 shows the schematic diagram of our RF magnetron co-sputtering system. Before the RF plasma process, the substrates were cleaned in trichloroethylene, acetone, methanol, and distilled water for 10 min. For the silicon wafers, an acid treatment was added for 45 s. Pure (99.9%), 4-inch Si and C targets were installed to achieve a high-quality a-Si1-xCx passivation layer. The sputtering chamber was vacuumed up to the base pressure of 1 × 10-5 Torr using a turbomolecular pump. A highly pure (99.9999%) argon environment was established for the deposition with a flow of 40 sccm. Then, the Si and C targets were pre-sputtered to clean the target surface and the chamber for 10 min. The target-to-substrate distance and the substrate rotation speed were fixed for all depositions as 6 cm and 1, 700 rph, respectively. In this work, to check the effect of the Si-to-C ratio on the a-Si1-xCx passivation layers, the RF power of the C target was fixed at 150 W, and several different RF powers (100, 150, 175, and 200 W) of the Si target were applied to. However, the thicknesses of all a-Si1-xCx passivation layers were kept constant at 100 nm by controlling the deposition rate. The deposition rates with the different RF powers of the Si target were summarized in Figure 2, and the detailed experimental parameters were summarized in Table 1.
Figure 1. A schematic diagram of the RF magnetron co-sputtering system.
Figure 2. Deposition rate of a-Si1-xCx passivation layer as a function of the Si target's RF power.
Table 1. Deposition conditions of the a-Si1-xCx passivation layer
The deposited a-Si1-xCx passivation layer's thickness and crystal structure were measured using an FE-SEM (S-4800, Hitachi, Tokyo, Japan) and a transmission electron microscope [TEM] (JEM-2100F, JEOL, Seoul, South Korea), respectively. Optical properties of the transmittance and bandgap were measured by UV-visible spectroscopy (S-3100, Scinco, Seoul, South Korea), the refractive indexes were obtained using an ellipsometer (M2000D, Woollam, Uiwang-si, South Korea), and the electrical performance of the a-Si1-xCx passivation layer was analyzed by carrier lifetime measurement (WCT-120, Sinton Consulting Inc., Boulder, CO, USA).
Results and discussion
As mentioned in the 'Experimental details' section, the film thickness was fixed at 100 nm. The thickness was measured with three different apparatuses, such as FE-SEM, TEM, and secondary ion mass spectrometer [SIMS]. Figure 3 shows cross-sectional bright field TEM images with a variation on the RF power of the silicon target. As the RF power of the Si target goes higher, the color of the Si1-xCx film gets darker due to the Si-rich compositional ratio of the film. It may indicate that the compositional ratio of the SiC is changed by the RF target power of the element.
Figure 3. TEM images. At (a) 100-, (b) 150-, and (c) 200-W RF powers of the Si target.
SIMS is widely used in the profile distribution of compositional elements along the deposited film depth by detecting the ionized element's mass. Figure 4 shows the depth profiles of Si and C along the deposited film. By increasing the RF power of the Si target, the mass intensity of the silicon particle gets higher than that of carbon. When we applied the same RF power on both targets, the compositional ratio of the elements seems to be 50:50 in mass intensity. When it goes deeper near the p-type silicon surface region, the carbon intensity is decreased abruptly. The falling point of the carbon intensity indicated the thickness of the a-Si1-xCx film with a sharp boundary between the film and the substrate.
Figure 4. Depth profiles as functions of the Si target's RF powers. (a) 100, (b) 150, and (c) 200 W.
Figure 5a shows the refractive index spectra of the a-Si1-xCx passivation films measured using an ellipsometer as a function of the Si target's RF power. The refractive indexes in the wavelength range of 400 to 1, 000 nm are increased when a higher RF power of the Si target is applied. At a 200-W RF power of the Si target, the refractive index value is highest all over the wavelength range. Generally, the refractive index of Si is higher than that of C (Si ≈ 3.49, C ≈ 2.41 at 630 nm). Therefore, when the RF power of the Si target goes up, more Si ions are deposited on the film. This Si-rich film makes a higher refractive layer. Figure 5b describes one point of refractive index at 630 nm which is a standard wavelength for optical properties in the visible wavelength regime and is a red-light wavelength. We obtained a refractive index of 2.7 at the 100-W RF power of the Si target. Then, by increasing the RF power of the Si target, the refractive index goes up, and at the 200-W RF power, we achieved the highest refractive index of 3.7. This result has a very similar trend with our previous experiment which was done with a single SiC composite target . The previous result has a very narrow refractive index variation (3.2 to 3.4) with the change of a large RF power range (150 to 300 W), but co-sputtering method shows a relatively large refractive index variation (2.7 to 3.7). That is, we have more controllability of the refractive index selection for the passivation layer.
Figure 5. Refractive index of a-Si1-xCx passivation layer as a function of the Si target's RF power. (a) Refractive index, n. (b) One point of refractive index, n (630 nm).
The optical bandgaps were calculated from optical absorption measurement of the thin films which were deposited on the glass substrates. The optical absorptions were obtained from the intensity of the light measured by UV-visible spectroscopy . Then, the optical bandgaps of the films were determined by the Tauc plot method which was performed by extrapolating the linear part of the absorption vs. photon energy (αhν)1/2 curves [12,13]. Figure 6 shows the optical bandgap as a function of the RF power of the Si target. The absorption bandgaps are decreased from 1.4 to 0.9 eV as the RF power of the Si target is increasing. In general, the optical bandgap of carbon (≈5.5 eV at room temperature [RT]) has a much higher value than that of Si (≈1.11 eV at RT). When the Si target power is increasing, the film is changed to a Si-abundant layer. Therefore, it is reasonable that the higher RF power of the Si target brings a thin film with a lower optical bandgap.
Figure 6. Optical bandgap as a function of the Si target's RF power.
Figure 7 shows the carrier lifetime of the a-SiC passivation layer measured by a silicon wafer lifetime tester with the function of Si target power. The carrier lifetime of the passivation layer deposited with a 100-W Si target power was 8.9 μs. Samnanta et al. reported that impurity in the semiconductor can degrade the lifetime by the creation of an electrical defect center or crystal imperfection . Therefore, a carbon-rich thin layer can have more microdefects than a Si-rich film. In our study, the carrier lifetime was gradually decreased from 8.9 to 6.0 as the RF power of the Si target is increased from 100 to 200 W.
Figure 7. Carrier lifetime of a-Si1-xCx passivation layer as a function of the Si target's RF power.
We demonstrate a formation method of an a-Si1-xCx passivation layer for Si solar cells. The method was performed by RF magnetron co-sputtering with a Si target and a C target. The a-Si1-xCx passivation layer was deposited on p-type silicon (100) and glass substrates with the reaction of argon (Ar) gas. In this work, we have checked the effect of the Si-to-C ratio on the a-Si1-xCx passivation layers with variation on the RF powers of the Si target (100, 150, 175, and 200 W) and with fixation on the RF power of the C target (150 W). However, the thicknesses of all a-Si1-xCx passivation layers were kept constant at 100 nm. The SIMS profile showed that the film composition is changed with a variation on the RF power of the Si target. The refractive index analysis indicated that a Si-rich thin film has higher refractive index. We could obtain the highest refractive index of 3.7 with a 200-W RF power of the Si target. The optical bandgap analysis showed that the bandgap of the Tauc plot was observed to decrease gradually from 1.4 to 0.9 eV. The carrier lifetime analysis showed that the carrier lifetime of the a-Si1-xCx passivation layer was observed to decrease gradually from 8.9 to 6.0 μs as the carbon ratio in the film is decreased by changing the Si target power. Therefore, we could conclude that the RF magnetron co-sputtering method for SiC can deposit a thin film passivation layer for solar cells with various compositional ratios of Si and C.
The authors declare that they have no competing interests.
Y-HJ and WSC carried out the molecular genetic studies, participated in the sequence alignment, and drafted the manuscript. HIK and JHK carried out the immunoassay sample preparation. H-SL and JL participated in the sequence alignment. All authors read and approved the final manuscript.
This work was supported by the New IT Project for global competitiveness strengthening of the advanced mobile devices and equipments of the Chungcheong Leading Industry Office of the Korean Ministry of Knowledge Economy.
Song D, Cho EC, Conibeer G, Flynn C, Huang Y, Green MA: Structural, electrical and photovoltaic characterization of Si nanocrystals embedded SiC matrix and Si nanocrystals/c-Si heterojunction devices.
Sol Energ Mat Sol C 2008, 92:474-481. Publisher Full Text
Yunaz IA, Hashizume K, Miyajima S, Yamada A, Konagai M: Wide-gap a-SiC:H solar cells with graded absorption layer for triple cell applications. In Conference Record of the 33rd IEEE PVSC 2008: May 11-16 2008. San Diego, CA IEEE; 2008::1-5.
Schultz O, Rentsch J, Grohe A, Glunz S, Willeke G: Dielectric rear surface passivation for industrial multicrystalline silicon solar cells. In Conference Record of the 2006 IEEE 4th World Conference on Photovoltaic Energy Conversion: May 7-12 2006. Waikoloa, HI IEEE; 2006::885-889.
Thin Solid Films 2011, 519:6654-6657. Publisher Full Text
J Cryst Growth 2011, 326:183-185. Publisher Full Text
Appl Surf Sci 2010, 256:5744-5756. Publisher Full Text
Sol Energ Mat Sol C 2001, 65:437-443. Publisher Full Text
Sol Energ Mat Sol C 2001, 66:155-162. Publisher Full Text
Sol Energ Mat Sol C 2006, 90:3449-3455. Publisher Full Text
Philos Mag 1970, 22:903-922. Publisher Full Text
Appl Surf Sci 2003, 210:359-367. Publisher Full Text
Sol Energ Mat Sol C 2001, 68:307-312. Publisher Full Text
Solid-State Electonic 2003, 47:893-897. Publisher Full Text