Bending effects of ZnO nanorod metal–semiconductor–metal photodetectors on flexible polyimide substrate

Tse-Pu Chen1, Sheng-Joue Young2*, Shoou-Jinn Chang1*, Chih-Hung Hsiao1 and Yu-Jung Hsu3

Author affiliations

1 Institute of Microelectronics and Department of Electrical Engineering, Center for Micro/Nano Science and Technology, Advanced Optoelectronic Technology Center, National Cheng Kung University, Tainan, 701, Taiwan

2 Department of Electronic Engineering, National Formosa University, Yunlin, 632, Taiwan

3 Institute of Electro-Optical Science and Engineering, National Cheng Kung University, Tainan, 701, Taiwan

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2012, 7:214  doi:10.1186/1556-276X-7-214


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/7/1/214


Received:18 January 2012
Accepted:10 March 2012
Published:12 April 2012

© 2012 Chen et al.; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

The authors report the fabrication and I-V characteristics of ZnO nanorod metal–semiconductor–metal photodetectors on flexible polyimide substrate. From field-emission scanning electron microscopy and X-ray diffraction spectrum, ZnO nanorods had a (0002) crystal orientation and a wurtzite hexagonal structure. During the I-V and response measurement, the flexible substrates were measured with (i.e., the radius of curvatures was 0.2 cm) and without bending. From I-V results, the dark current decreased, and the UV-to-visible rejection ratio increased slightly in bending situation. The decreasing tendency of the dark current under bending condition may be attributed to the increase of the Schottky barrier height.

Keywords:
ZnO; Nanorod; MSM; Photodetector; Flexible

Background

Zinc oxide (ZnO), a nanostructured material that has been widely investigated, has a wide energy band gap of 3.37 eV at room temperature, high optical gain of 300/cm which is higher than that of GaN (100/cm) [1], and large exciton binding energy of 60 meV [2] which is higher than that of ZnSe (22 meV) and GaN (25 meV). The large exciton binding energy provides high-luminescence efficiency of light emission at or above room temperature. ZnO has slightly higher saturation velocity of 3.2 × 107 cm/s [3] than GaN, InGaN, and AlGaN [4,5], but the room temperature electron Hall mobility (205 cm2/V/s/) [6] is lower than that of GaN. ZnO has high mechanical and thermal stabilities, and radiation hardness for devices used in nuclear and space applications. ZnO also has lower growth temperature and material cost than III-nitride materials.

According to the researches, GaN and its alloys with AlN and InN cover the spectral range from red to vacuum UV (1.9 to 6.2 eV). Therefore, III-nitride materials have attracted a great deal of attention since the commercialization of light-emitting diodes. Not only GaN but also ZnO can tune the value of band gap by forming the ternary alloy of ZnMgO and ZnCdO with MgO and CdO [7], respectively.

Over the past decade, ZnO-based and III-nitride-based light-emitting diodes (LEDs) and laser diodes (LDs) have attracted much interest for display, illumination, and mobile phone backlights. Recently, Zhang et al. [8] studied on gain properties of high Al-content AlGaN-delta-GaN quantum wells (QWs) for mid- and deep-UV lasers. Zhao et al. [9] investigated the QW structures with large overlap design to enhance the internal quantum efficiency for InGaN QW-based LEDs. Shukla [10] studied a p-n junction LED employing ZnO/MgZnO QW active layer on a c-plane sapphire by the pulsed-laser deposition technique. Ahn et al. [11] showed p-n heterojunction LEDs that were formed from a p-Si thin film/nanostructured n-ZnO by a dielectrophoresis method. Except for the LEDs and LDs, ZnO makes it as a promising functional material for the electronic device manufacture such as field emission, photodetectors (PD), solar cells, waveguides, and chemical or biosensors.

To date, many groups have reported encouraging results for ZnO-based photodetectors. It is important that ZnO-based PDs be used in various military and commercial applications, like missile launching and flame detections, optical communications, and ozone layer monitoring. Indeed, ZnO-based PDs have various types, such as p-n junction PDs, p-i-n PDs, Schottky barrier PDs, and metal–semiconductor–metal (MSM) PDs [12-15]. Among the above structures, the MSM structure is a practical application due to its easy fabrication, low dark current and device noise values, high-response speed, and compatibility with integrated circuit technology. Recently, Yen et al. [16] obtained high photocurrent generation with ZnO/Si heterostructure MSM PDs by an avalanche multiplication in the ZnO layer. GaN-based MSM PDs also can detect the UV region, but a significant number of threading dislocations exit in GaN epilayers due to the large mismatches in lattice constant and thermal expansion coefficient between GaN and substrate, like sapphire and Si. Recently, Li et al. [17] found that dislocations had strong influence on the dark current and responsivity of the PDs. Consequently, ZnO-based materials have more advantages for PDs than GaN-based materials.

Recently, various one-dimensional (1-D) ZnO semiconducting nanostructures have been synthesized like nanorods, nanotubes, and nanobelts [18-20]. Most importantly, ZnO is well known as a piezoelectric material. Because of semiconductor properties and the coupling of piezoelectric of ZnO, many groups extensively investigated nanogenerators, piezoelectric field effect transistors, and piezoelectric strain and piezoelectric humidity/chemical sensors [21-24].

Today, many groups investigate the optoelectronic devices grown on flexible substrates, but the problem of these flexible substrates is that they must use low-temperature process. ZnO is one of the most suitable materials on flexible substrate because it can be prepared by low temperature processes, like sputter and aqueous method. Growth of 1-D ZnO semiconducting nanostructures on flexible substrates has been widely reported which are ideal candidates for LEDs, solar cell, file-effect transistors, personal health monitors, and field emission [22,25-27] due to cheap, lightweight, and portable characteristics. However, the mechanical bending characteristics of the ZnO nanorod MSM structures fabricated on flexible substrates have rarely been investigated.

In this letter, we fabricated MSM ultraviolet PDs with ZnO nanorods on flexible substrate by aqueous method. The advantages of aqueous method are low cost, simple process, low temperature, and high product yield. Further, the fabricated devices were measured with and without strong mechanical bending. The optical and electric properties and the working principle of the ZnO nanorod MSM PDs would be presented in detail.

Methods

The polyimide (PI) substrates were ultrasonically cleaned in methanol, isopropanol, and deionized water and dried with nitrogen. ZnO-seed layers with a thickness of about 130 nm were grown on polyimide substrates in a low-pressure RF sputter reactor. In our sputtering system, the background pressure in the sputtering chamber was evacuated to about 8 × 10−6 Torr with a turbo pump. The deposition processes were performed in Ar and O2 ambient at an applied RF power of 120 W. After deposition, the as-grown samples were annealed 40 min in oxygen flow at 300°C in a quartz tube. After annealing, the samples were cooled to room temperature naturally, and MSM PDs were subsequently fabricated on the annealed samples. The ZnO PDs were fabricated using interdigital MSM structures by standard lithography. Using e-beam evaporation, Ag/Au (40/50 nm) contact electrodes were deposited on the samples served as Schottky contacts. The metal contact did not anneal by furnace or RTA. Then, we used photoresist to protect the electrodes by standard lithography. ZnO nanorod arrays were grown using an aqueous solution containing zinc nitrate (Zn(NO3)2) and hexamethylenetetramine (HMTA) for 1 h at 90°C. During ZnO nanorod synthesis, Zn(NO3)2 and HMTA act as a Zn2+ source and a pH buffer, respectively, which keep the pH value at a constant [28]. After the process of the grown ZnO nanorods, the photoresist was lift-off, and there is no ZnO film or short nanorod formed on the metal electrode.

Figure 1 shows the schematic of the proposed ZnO nanorod MSM photodetector. The morphologies and size distribution of the ZnO nanorod PDs were characterized by field-emission scanning electron microscopy (JSM-7000 F, JEOL Ltd., Akishima, Tokyo, Japan) which was operated at 10 keV. X-ray diffraction (XRD) measurement was then utilized to characterize the optical and crystallographic properties of the as-grown ZnO nanorods. An HP-4156 C semiconductor parameter analyzer (Agilent Technologies Inc., Santa Clara, CA, USA) was then employed to measure current–voltage (I-V) characteristics of the proposed ZnO nanorod MSM photodetector. The photo-responsivity was obtained using the TRIAX 180 system (HORIBA Ltd., Minami-Ku, Kyoto, Japan) with a 300 W xenon arc lamp light source and standard synchronous detection scheme.

thumbnailFigure 1 . Schematic of the ZnO nanorod MSM PD prepared on flexible substrate.

Results and discussion

Figure 2a and its inset shows the top view and cross-sectional SEM images of the ZnO nanorods grown on the flexible substrate by aqueous method. From Figure 2a, a large of ZnO nanorod array grew uniformly on the flexible substrate with varying diameter of nanorods (80–100 nm). The shapes of the nanorods had wurtzite structure. The inset of the Figure 2a shows the cross-section of the nanorods. As seen, most of the nanorods were well aligned, perpendicular to the substrate which the length of the nanorods can reach up to approximately 1 μm. Figure 2b shows the top view of the ZnO MSM nanorod device. From the image, it can be seen that the ZnO nanorod arrays selectively distributed among the interdigitated electrodes of the device. It confirmed that the electrodes can effectively be protected by the photoresist, which avoid the nanorods growing onto the electrodes. Therefore, our method can fabricate MSM PDs with a large area aligned ZnO nanorods to enhance the performance.

thumbnailFigure 2 . SEM images. (a) Top view of the ZnO nanorods. Inset: the cross-sectional image of the nanorods. (b) Top view of the ZnO nanorods MSM photodetector.

Figure 3 shows the typical X-ray diffraction spectrum of the ZnO nanorods prepared on the ZnO/PI substrate. According to XRD result, it depicts the diffraction angles of 34.4° assigned as ZnO (0002) reflection. The strong (0002) reflection with narrow width indicates that the ZnO nanorods were crystallized in wurtzite structure and preferentially grown along the c-axis direction.

thumbnailFigure 3 . XRD spectrum measured from vertically aligned ZnO nanorods.

The ZnO nanorod MSM PDs were fabricated on flexible polyimide substrate, so the performance under bending conditions is of major importance. It is important to understand the characteristics of the flexible ZnO nanorod MSM PDs with bending and without bending for the future of plastic electronic productions. Stable performance at bending situation is a critical challenge. For this reason, we measured the electrical characteristics of the PDs with bending and without bending. Before the measurement, we prepared a holder with semicircular shape (the radius of the holder was 0.2 cm) and fixed the ZnO nanorod MSM PDs on it, which could make the device bending. For convenience of realization, Figure 4a shows a schematic drawing of the bending device, where r corresponds to the radius of the curvature of bending. A smaller radius of the curvature of bending means increased bending. Figure 4b shows the current–voltage characteristics of ZnO nanorod PDs under flat and 0.2-cm radius of bending curvature, respectively. From the result, it could be known that dark current decreased slightly under bending, but the shift was lesser than one order of magnitude. The I-V behavior of the device was modulated due to the change in Schottky barrier height (SBH) at the metal–semiconductor interface. It is well known that the lacking of center symmetry in ZnO lead ionic polarization can be induced by strain [29]. When the ZnO nanorod PDs are bent by an external force, the potential is induced by the piezoelectric effect which is created by the relative displacement of the Zn2+ with respect to the O2−, and these piezoelectric ionic charges cannot move freely until external force releases [21,30]. These piezoelectric ionic charges could affect the charge transport strongly. The changing of piezopotential would shift the local Fermi level and modify the local conduction band structure. Therefore, the PDs under tensile strain would increase the SBH and influence the charge transport property by the piezoelectric effect and the band structure.

thumbnailFigure 4 . Schematic drawing of the bending device, and the dark I-V characteristics and responsivity characteristics. (a) Schematic drawing of the bending device. (b) The I-V and (c) responsivity characteristics of the PD measured from flat and bending substrate in the dark.

In our experiment, the structure of our device is MSM structure which is like two back-to-back Schottky diodes, and our devices were measured at room temperature and the ZnO nanorods had low doping. Therefore, the current transport mechanism followed the thermionic emission-diffusion theory (for V > > 3 kT/q, approximately 77 mV) [31]. According to the literature [23], the thermionic emission-diffusion theory can be simplified by assuming some parameters are independent of strain, and then the change of SBH can be determined by the equation below [23]:

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/214/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/214/mathml/M1">View MathML</a>

(1)

where Izz) and I(0) are the current measured from the ZnO nanorod MSM PDs at a fixed bias with and without being strained, respectively. After calculation, the changes of SBH were 27 meV and 29 meV for two biases of 1 and 2 V, respectively. From the two values, it can be known that the change of the SBH is not very sensitive to the bias applied across the device.

Owing to the outward bending of the substrate, piezoelectric effects could be induced and it could be attributed to the tensile strain between n-ZnO lattices. As we know, strain can be used in many applications. In microelectronic industry, scaling of MOSFETs has attracted many people to study it for the improvement in integrated circuit density and performance. However, MOSFET size reduction has met technological challenges such as short-channel effect and high leakage current. Therefore, strain has been an increase in interest in semiconductor material since the 1950s. Using appropriate tensile and compressive strain components in the n- and p-MOSFET's channel region could enhance its performance [32-35].

Figure 4c shows the responsivity characteristics of the ZnO nanorod PDs under flat and bending curvature. In this figure, the responsivities in visible wavelengths decreased slightly under bending, and the cutoff wavelength was the same. The UV-to-visible rejection ratios, defined as the ratio of the responsivity at 370 nm and at 460 nm, are 174.6 and 503.2 for flat and 0.2-cm radius of curvature bending, respectively. The rejection ratio of the 0.2-cm radius of curvature bending had a larger value that could be attributed to the smaller dark current.

From the responsivity characteristics of the ZnO nanorod PDs, the PDs had high responsivities under UV-light illumination. In addition, the photoconductive gain is given by the following equation [36]:

<a onClick="popup('http://www.nanoscalereslett.com/content/7/1/214/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/7/1/214/mathml/M2">View MathML</a>

(2)

where G is the internal gain, R is the responsivity, h is the Plank's constant, v is the frequency of the light, q is the electronic charge, and η is the quantum efficiency. Assuming η is 1 for simplicity, the internal gains of the ZnO nanorod PDs measured at flat and 0.2-cm radius of curvature bending were 3.71 × 102 and 2.44 × 102, respectively. Both PDs had high responsivities due to ZnO nanorod large surface-to-volume ratio and the existence of the oxygen-related hole surface states on the ZnO nanorods surface. The oxygen molecules can adsorb on the ZnO nanorod surface by capturing free electrons and desorb from the surface by illustrating UV light which lead to an increase in the free carrier concentration, a decrease in the width of the depletion layer, and a reduction of the Schottky barrier height [37]. Recently, Soci et al. [37] published the ZnO nanowire PDs with high internal gain. They fabricated a ZnO photodetector with one ZnO nanowire. Their device has achieved an internal gain of approximately 108. Instead, our device has smaller internal gain than theirs. This could be attributed to the high density of nanorod array of our device and there were small gaps between the freestanding nanorods. When the nanorods were illustrated by the UV light, the oxygen molecules desorbed from the nanorods surface. However, the nanorods were too close that make the oxygen molecules quickly readsorb with the nanorod surface by capturing free electrons and decrease the photocurrent. Thus, the internal gain of our device was smaller than theirs.

Conclusions

In summary, we reported the fabrication and I-V characteristics of ZnO nanorod PDs on PI substrate. The crystal and optical properties of ZnO nanorods had been investigated by SEM and XRD. They showed the ZnO nanorods grown on the PI substrate had high density array, hexagonal wurtzite structure and well (0002) crystalline phase. From I-V curve, it was found that the dark current decreased slightly and the UV-to-visible rejection ratio increased slightly in bending situation. The decreasing tendency of dark current under bending may be attributed to the increase of the Schottky barrier height. Consequently, ZnO nanorods have great potential for high-performance UV photodetectors, and polyimide is a promising substrate for flexible PDs and devices.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

TPC, SJY, and SJC designed the whole experimental procedure and related analysis. CHH participated in data analysis. YJH did the nanowire growth and other experiments. All authors read and approved the final manuscript.

Acknowledgments

This work was supported by National Science Council of Taiwan under contract number NSC 100-2221-E-150-057. National Formosa University Research and Services Headquarters that provided the partial equipment for measurement is also acknowledged.

References

  1. Hvam JM: Direct recording of optical-gain spectra from Zno.

    J Appl Phys 1978, 49:3124-3126. Publisher Full Text OpenURL

  2. Look DC: Recent advances in ZnO materials and devices.

    Mater Sci Eng: B 2001, 80:383-387. Publisher Full Text OpenURL

  3. Solis-Pomar F, Martinez E, Melendrez MF, Perez-Tijerina E: Growth of vertically aligned ZnO nanorods using textured ZnO films.

    Nanoscale Res Lett 2011, 6:524. PubMed Abstract | BioMed Central Full Text | PubMed Central Full Text OpenURL

  4. Morkoc H, Strite S, Gao GB, Lin ME, Sverdlov B, Burns M: Large-band-gap sic, III-V nitride, and II-VI ZNSE-based semiconductor-device technologies.

    J Appl Phys 1994, 76:1363-1398. Publisher Full Text OpenURL

  5. Anwar AFM, Wu SL, Webster RT: Temperature dependent transport properties in GaN, A1(x)Ga(1-x)N, and InxGa1-xN semiconductors.

    IEEE T Electron Dev 2001, 48:567-572. Publisher Full Text OpenURL

  6. Look DC, Reynolds DC, Sizelove JR, Jones RL, Litton CW, Cantwell G, Harsch WC: Electrical properties of bulk ZnO.

    Solid State Commun 1998, 105:399-401. Publisher Full Text OpenURL

  7. Dietrich CP, Lange M, Stolzel M, Grundmann M: Microwire (Mg,Zn)O/ZnO and (Mg,Zn)O/(Cd,Zn)O non-polar quantum well heterostructures for cavity applications.

    Appl Phys Lett 2012, 100:031110-1-031110-4. OpenURL

  8. Zhang J, Zhao HP, Tansu N: Large optical gain AlGaN-delta-GaN quantum wells laser active regions in mid-and deep-ultraviolet spectral regimes.

    Appl Phys Lett 2011, 98:171111-1-171111-3. OpenURL

  9. Zhao HP, Liu GY, Zhang J, Poplawsky JD, Dierolf V, Tansu N: Approaches for high internal quantum efficiency green InGaN light-emitting diodes with large overlap quantum wells.

    Opt Express 2011, 19:A991-A1007. PubMed Abstract | Publisher Full Text OpenURL

  10. Shukla G: ZnO/MgZnO p-n junction light-emitting diodes fabricated on sapphire substrates by pulsed laser deposition technique.

    J Phys D: Appl Phys 2009, 42:075105. Publisher Full Text OpenURL

  11. Ahn J, Park H, Mastro MA, Hite JK, Eddy CR, Kim J: Nanostructured n-ZnO/thin film p-silicon heterojunction light-emitting diodes.

    Opt Express 2011, 19:26006-26010. PubMed Abstract | Publisher Full Text OpenURL

  12. Leung YH, He ZB, Luo LB, Tsang CHA, Wong NB, Zhang WJ, Lee ST: ZnO nanowires array p-n homojunction and its application as a visible-blind ultraviolet photodetector.

    Appl Phys Lett 2010, 96:053102. Publisher Full Text OpenURL

  13. Sun F, Shan C-X, Wang S-P, Li B-H, Zhang Z-Z, Yang C-L, Shen D-Z: Ultraviolet photodetectors fabricated from ZnO p-i-n homojunction structures.

    Mater Chem Phys 2011, 129:27-29. Publisher Full Text OpenURL

  14. Kim J, Yun J-H, Kim CH, Park YC, Woo JY, Park J, Lee J-H, Yi J, Han C-S: ZnO nanowire-embedded Schottky diode for effective UV detection by the barrier reduction effect.

    Nanotechnology 2010, 21:115205. PubMed Abstract | Publisher Full Text OpenURL

  15. Qin L, Shing C, Sawyer S: Metal–semiconductor–metal ultraviolet photodetectors based on zinc-oxide colloidal nanoparticles.

    IEEE Electron Device Lett 2011, 32:51-53. OpenURL

  16. Yen T, Yun J, Kim SJ, Cartwright A, Anderson WA: Photocurrent enhancement in nanocrystalline-ZnO/Si heterojunction metal–semiconductor–metal photodetectors.

    Electrochemical Solid-State Lett 2011, 14:H415-H418. Publisher Full Text OpenURL

  17. Li D, Sun X, Song H, Li Z, Chen Y, Miao G, Jiang H: Influence of threading dislocations on GaN-based metal–semiconductor–metal ultraviolet photodetectors.

    Appl Phys Lett 2011, 98:011108. Publisher Full Text OpenURL

  18. Yu J, Ippolito SJ, Wlodarski W, Strano M, Kalantar-Zadeh K: Nanorod based Schottky contact gas sensors in reversed bias condition.

    Nanotechnology 2010, 21:265502. PubMed Abstract | Publisher Full Text OpenURL

  19. Han JB, Fan FR, Xu C, Lin SS, Wei M, Duan X, Wang ZL: ZnO nanotube-based dye-sensitized solar cell and its application in self-powered devices.

    Nanotechnology 2010, 21:405203. PubMed Abstract | Publisher Full Text OpenURL

  20. Wang ZL: ZnO nanowire and nanobelt platform for nanotechnology.

    Mat Sci Eng R 2009, 64:33-71. Publisher Full Text OpenURL

  21. Wang ZL, Song JH: Piezoelectric nanogenerators based on zinc oxide nanowire arrays.

    Science 2006, 312:242-246. PubMed Abstract | Publisher Full Text OpenURL

  22. Kwon SS, Hong WK, Jo G, Maeng J, Kim TW, Song S, Lee T: Piezoelectric effect on the electronic transport characteristics of ZnO nanowire field-effect transistors on bent flexible substrates.

    Adv Mater 2008, 20:4557-4562. Publisher Full Text OpenURL

  23. Zhou J, Gu YD, Fei P, Mai WJ, Gao YF, Yang RS, Bao G, Wang ZL: Flexible piezotronic strain sensor.

    Nano Lett 2008, 8:3035-3040. PubMed Abstract | Publisher Full Text OpenURL

  24. Wang ZL, Lao CS, Kuang Q, Park MC, Deng YL: Polymer functionalized piezoelectric-FET as humidity/chemical nanosensors.

    Appl Phys Lett 2007, 90:262107. Publisher Full Text OpenURL

  25. Lee C-H, Kim Y-J, Hong YJ, Jeon S-R, Bae S, Hong BH, Yi G-C: Flexible inorganic nanostructure light-emitting diodes fabricated on graphene films.

    Adv Mater 2011, 23:4614-4619. PubMed Abstract | Publisher Full Text OpenURL

  26. Chu S, Li DD, Chang PC, Lu JG: Flexible dye-sensitized solar cell based on vertical ZnO nanowire arrays.

    Nanoscale Res Lett 2011, 6:38. OpenURL

  27. Hwang JO, Lee DH, Kim JY, Han TH, Kim BH, Park M, No K, Kim SO: Vertical ZnO nanowires/graphene hybrids for transparent and flexible field emission.

    J Mater Chem 2011, 21:3432-3437. Publisher Full Text OpenURL

  28. Ahsanulhaq Q, Umar A, Hahn YB: Growth of aligned ZnO nanorods and nanopencils on ZnO/Si in aqueous solution: growth mechanism and structural and optical properties.

    Nanotechnology 2007, 18:115603. Publisher Full Text OpenURL

  29. Wang ZL, Wu WZ: Piezotronic nanowire-based resistive switches as programmable electromechanical memories.

    Nano Lett 2011, 11:2779-2785. PubMed Abstract | Publisher Full Text OpenURL

  30. He JH, Hsin CL, Liu J, Chen LJ, Wang ZL: Piezoelectric gated diode of a single ZnO nanowire.

    Adv Mater 2007, 19:781-784. Publisher Full Text OpenURL

  31. Sze SM: Physics of Semiconductor Devices. 2nd edition. Wiley, New York; 1981. OpenURL

  32. Chu M, Sun Y, Aghoram U, Thompson SE: Strain: a solution for higher carrier mobility in nanoscale MOSFETs.

    AnnuRev Mater Res 2009, 39:203-229. Publisher Full Text OpenURL

  33. Lee MH, Chang ST, Wu TH, Tseng WN: Driving current enhancement of strained Ge (110) p-type tunnel FETs and anisotropic effect.

    Electron Device Lett, IEEE 2011, 32:1355-1357. OpenURL

  34. Yeo YC: Enhancing CMOS transistor performance using lattice-mismatched materials in source/drain regions.

    Semicond Sci Tech 2007, 22:S177-S182. Publisher Full Text OpenURL

  35. Ghani T, Armstrong M, Auth C, Bost M, Charvat P, Glass G, Hoffmann T, Johnson K, Kenyon C, Klaus J, McIntyre B, Mistry K, Murthy A, Sandford J, Silberstein M, Sivakumar S, Smith P, Zawadzki K, Thompson S, Bohr M: A 90 nm high volume manufacturing logic technology featuring novel 45 nm gate length strained silicon CMOS transistors. In Electron Devices Meeting Tech Dig 2003, 11.6.1–11.6.3.

  36. Bube RH: PhotoconductiVity of Solids. Wiley, New York; 1960:461. OpenURL

  37. Soci C, Zhang A, Xiang B, Dayeh SA, Aplin DPR, Park J, Bao XY, Lo YH, Wang D: ZnO nanowire UV photodetectors with high internal gain.

    Nano Lett 2007, 7:1003-1009. PubMed Abstract | Publisher Full Text OpenURL