Open Access Highly Accessed Nano Idea

Solvothermal synthesis of uniform bismuth nanospheres using poly(N-vinyl-2-pyrrolidone) as a reducing agent

Jiliang Wu1, Fan Qin1, Zhong Lu1, Hai-Jian Yang2 and Rong Chen1*

Author affiliations

1 Key Laboratory for Green Chemical Process of Ministry of Education and School of Chemical Engineering & Pharmacy, Wuhan Institute of Technology, Wuhan, 430073, P. R. China

2 Key Laboratory of Catalysis and Materials Science of the State Ethnic Affairs Commission & Ministry of Education, College of Chemistry and Materials Science, South-Central University for Nationalities, Wuhan, 430074, P. R. China

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2011, 6:66  doi:10.1186/1556-276X-6-66

The electronic version of this article is the complete one and can be found online at:

Received:26 July 2010
Accepted:12 January 2011
Published:12 January 2011

© 2011 Wu et al; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.


Uniform bismuth nanospheres were successfully prepared from bismuth nitrate in the presence of poly(N-vinyl-2-pyrrolidone) (PVP) by solvothermal process. The product was characterized by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, selected area electron diffraction, and energy-dispersive X-ray. PVP plays a critical role both as a reducing agent and a capping agent in the formation of bismuth nanospheres. Shape and size of bismuth nanospheres could be tuned by changing the employed PVP/bismuth salt ratio. It was also found the solvent had an effect on the morphologies of bismuth nanomaterials. The possible formation and growth mechanism of bismuth nanospheres were also discussed and proposed to explain the reduction step.


Recently, metal nanostructures with functional properties have been extensively studied due to their wide applications. Among the various metal nanostructures, monodisperse metallic nanospheres have attracted considerable attention because of their unique optical, catalytic, as well as novel chemical and biological properties [1-8]. For example, the controlled silver nanospheres were applied for optical studies and antibacterial applications [9,10]. Thus, much effort has been devoted to the preparation of new metal nanospheres and their functional transformation [11-14]. As a semimetal, bismuth has unusual properties due to its highly anisotropic Fermi surface, low carrier densities, small carrier effective masses, and long carrier mean free path [15]. Bismuth nanostructures have received steadily growing interests, since they play important roles in many diverse applications [16,17]. Different bismuth nanomaterials, such as single-crystal bismuth thin film and nanowire, have been investigated for their large magnetoresistance, finite-size effects, and enhanced thermal conductivity [18-20]. It was also reported that spherical bismuth nanomaterials were a good catalyst for the growth of SnS2 nanotubes and germanium nanowires [21,22]. Up to now, a wide variety of bismuth nanostructures such as nanoparticles [23], nanowires [24], nanorods [25], nanotubes [26-28], triangular nanoplates [29], bunch-like nanostructures [17], nanocubes [30], as well as nanospheres (>100 nm) [31-34] have been prepared by using different methods. Among these methods, solvothermal synthesis has become an important and promising approach to prepare controlled inorganic nanocrystals [35-37].

In the reported literatures, the alcohol [normally ethylene glycol (EG)] was used as both solvent and reducing agent to generate bismuth nanospheres with a wide size distribution [31-34]. Wang and Xia [38] have developed the synthesis of uniform bismuth nanospheres by thermal decomposition bismuth acetate in EG under the protection of nitrogen. The use of protection of inactive gas and organic metal precursor, however, made it complicated and costly. Hence, a simple, low-cost approach for the preparation of uniform bismuth nanospheres is highly desired.

In this communication, we describe a solvothermal process for the synthesis of uniform bismuth nanospheres in the presence of poly(N-vinyl-2-pyrrolidone) (PVP). In most cases, PVP was used as a protecting agent to cap and stabilize the particles to avoid aggregation in the solution [39]. It was also reported that PVP was used as reducing agent in the preparation of noble metallic nanostructures [40,41]. In this synthesis, PVP acts as both reducing and capping agent. To the best of our knowledge, there are few publications relevant to the synthesis of bismuth nanomaterials using PVP as a reducing agent.



Bismuth nitrate pentahydrate (Bi(NO3)3·5H2O) was purchased from Fuchen Chemicals Reagent (China). N,N-dimethylformamide (DMF), ammonia, mannitol, and EG were purchased from Sinopharm Chemical Reagent (China); PVP (with average Mw of 10,000) was purchased from Sigma-Aldrich Inc. All the reagents were analytical grade and used directly without further purification.

Synthesis of uniform bismuth nanospheres

In a typical procedure, 0.5 mmol Bi(NO3)3·5H2O was dissolved in 12.5 mL of 0.1 mol/L mannitol solution, then 7.5 mL NH3·H2O (5 mol/L) was added to the solution slowly with vigorously stirring. After stirring for about 15 min, the white precipitation was collected and washed with deionized water by centrifugation for five times. Then the obtained white precipitation and 0.155 g of PVP were introduced into 35 mL EG. The mixture was stirred and sonicated until all the chemicals were well dispersed. Then it was transferred into a stainless steel autoclave with Teflon liner. The autoclave was sealed and maintained at 180°C for 12 h. After cooling to room temperature, the obtained black solution was centrifuged and the solid product was collected. The black solid product was then washed with absolute alcohol for five to seven times followed by centrifugation. Finally, the solid product was dried in a desiccator for a few days for further characterization (sample 1). Other samples of bismuth nanomaterials were also prepared with different amounts of PVP and different solvents using the same methods under identical conditions (Table 1).

Table 1. Experimental conditions for the synthesis of bimuth nanomaterials


The bismuth nanostructures were characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and energy-dispersive X-ray (EDX). The powder XRD pattern was recorded on Bruker AXS D8 Discover (Cu Kα radiation, λ = 1.5406 Å). The scanning rate is 1°/min in the 2θ range from 20 to 70°. The SEM images were taken on a Hitachi S4800 field emission scanning electron microscope operating at 3 or 5 kV (FESEM, Japan). TEM images and SAED pictures were recorded on a Philips Technai G2 20 electron microscope (Manufacturer: FEI Company), using an accelerating voltage of 200 kV. The EDX analysis was performed on an Oxford Instruments Inca with a scanning range from 0 to 20 keV. The samples for TEM observations were prepared by dispersing some of the solid products into absolute alcohol and then sonicated for several minutes. A few drops of the suspension were deposited on the copper grid, which was then put into the desiccator. The thermogravimetric and differential analysis was done by DIAMOND TG/DTA instrument (PerkinElmer Instruments, Waltham, CT, USA) with a heating rate of 10°C/min.

Results and discussion

Figure 1a shows the typical powder XRD pattern of the as-synthesized product (sample 1). All the diffraction peaks could be readily indexed to be rhombohedral phase of bismuth, which were consistent with the literature values (JCPDS No. 05-0519). No impurity was detected in this pattern, indicating the formation of pure bismuth products under current synthetic condition. The sharp and strong diffraction peaks also confirm the well crystallization of the products.

thumbnailFigure 1. XRD pattern (a) and SEM images of the as-synthesized product in EG at lower (b, c) and higher (d) magnifications (sample 1).

The morphologies and structures of the as-prepared bismuth nanospheres were investigated by SEM and TEM images. Figure 1b, c, d shows the representative SEM images of the as-prepared bismuth nanospheres with different magnifications. The low-magnification images (Figure 1b, c) indicate the large production of uniform bismuth nanospheres. No other bismuth morphologies could be found in the whole sample. The diameters of these nanospheres varied from 160 to 210 nm and most of them were about 180 nm. The high-magnification image shown in Figure 1d clearly reveals the detailed morphologies of the products, indicating the formation of uniform, regular nanospheres with smooth surfaces.

The low- (Figure 2a) and high-magnification (Figure 2b) TEM images further demonstrated the morphologies of these bismuth nanospheres clearly. It also reveals a well-defined spheric structure and smooth surface. The statistical analysis showed that bismuth nanospheres had a narrow size distribution and the average diameter was about 180 nm with a standard deviation of 10 nm (Figure 2c). SAED pattern taken from an individual bismuth particle showed clear diffraction spots, indicating a good single-crystal structure (Figure 2d). The elemental composition of the nanospheres was also analyzed by EDX, and characteristic bismuth absorption peaks were observed (Figure S1 in Additional File 1). The copper and carbon peaks are due to the carbon-coated copper grid.

thumbnailFigure 2. Typical (a) low- and (b) high-magnification TEM images of as-prepared bismuth nanospheres (sample 1). (c) The histogram of size distribution of the bismuth nanospheres prepared from "a". (d) The SAED pattern of a single bismuth nanosphere.

Additional file 1. Figure S1. EDX spectrum of bismuth nanospheres prepared in EG.

Format: DOCX Size: 49KB Download fileOpen Data

To investigate the composition of the white precipitate obtained in the synthetic procedure, thermogravimetric and differential thermal analysis (TG/DTA) and EDX measurements were carried out. Figure 3a shows the results of the thermal analysis of the white precipitate at a heating rate of 10°C/min in the nitrogen atmosphere. It indicates a two-step weight loss in the temperature range from 25 to 200 and 200 to 300°C. The first weight loss in the TG trace could be attributed to the desorption of physically adsorbed water, and the second one could be recognized in according with the exothermal reaction in DTA trace (Figure 3a). The exothermal reaction thermal was found to arise from the decomposition of the white precipitate. The white precipitate was further investigated by EDX spectrum. As shown in Figure 3b, the white precipitate was composed of Bi, O, and C and no other additional elements were detected. The Si signal is attributed to the silicon wafers. When the white precipitate was calcined at 350°C for 90 min, the XRD pattern of the calcined product was very close to the standard data (Bi2O3, JCPDS No. 71-2274) (Figure S2 in Additional File 2). Hence, it was proposed that the possible component of the white precipitate was bismuth complexes (BiIII-mannitol), which were formed in ammonia solution.

thumbnailFigure 3. Thermogravimetric and differential thermal analysis (TG/DTA) and EDX Analysis (a) TG/DTA curves of thermal decomposition of the white precipitation at a heating rate of 10°C/min in the N2 atmosphere; (b) EDX pattern of the white precipitation.

Additional file 2. Figure S2. XRD pattern of the white precipitation was calcined at 350°C for 90 min.

Format: DOCX Size: 46KB Download fileOpen Data

In this study, it was found that there was no black product precipitated from the solution in the absence of PVP under identical experiment condition. The XRD pattern of the obtained white product could not be assigned in the XRD standard data base (Figure S3 in Additional File 3). It is obvious that PVP plays a key role in the formation of bismuth nanospheres. It was proposed that PVP reduced Bi3+ ions to give metallic bismuth. The reduction process could be probably understood considering two main reactions: (1) direct abstraction of hydrogen atoms from the polymer by the Bi3+ ions; (2) reduction of the Bi3+ ions by the organic radicals formed in (1) or during the bismuth-accelerated degradation of PVP, which is similar to the reported literatures [40,42]. It was reported that the capping organic molecules in the reaction system could determine the subsequent morphology of the product because of their special chemical properties and self-assembling functions [43-45]. Recently, it was also found that EG molecules could adsorb onto the surface of bismuth crystals through O-Bi bonding which could significantly decrease their growth rates and lead to highly anisotropic growth [33,46]. Thus, when the molar ratio of repeating units of PVP to Bi3+ is about 3, that is, there is no excess PVP in the solution, these uniform bismuth nanospheres can be obtained under the only effect of EG.

Additional file 3. Figure S3. XRD pattern of the white product obtained in EG in the absence of PVP.

Format: DOCX Size: 121KB Download fileOpen Data



When the amount of PVP was increased to 0.310 g (the molar ratio of repeating units of PVP to Bi3+ is about 6), bismuth nanospheres and nanowires were formed, as shown in Figure 4a. The diameters of obtained bismuth nanospheres were in the range from 250 to 500 nm, and the length of the nanowires varies from 0.5 to more than 6 μm. When the molar ratio of repeating units of PVP to Bi3+ was further increased to about 9 (the amount of PVP is 0.465 g), a mass of bismuth nanowires were obtained and few bismuth nanospheres remained, as shown in Figure 4b. The length of bismuth nanowires is up to 10 μm and the diameters of nanospheres are in range from 200 to 500 nm. The elemental composition of these nanowires and few nanospheres was also analyzed by EDX, and characteristic bismuth absorption peaks were observed (Figure 4e). Thus, PVP is considered to act both as reducing agent and capping agent in this synthesis. It was believed that the formation of bismuth nanowires was based on the Ostwald ripening process [47,48]. At first, bismuth nanoparticles were formed in the solution according to eqs 1 or 2 with PVP as reducing or nucleating agent. Then, the excess PVP molecules could cap onto the surface of bismuth particles [33], and bismuth nanowires were produced through this polyol process. In this process, bismuth particles can continuously grow into nanospheres, nanorods, or nanowires. The co-effect of PVP and EG resulted in a wide size distribution of the diameter of bismuth nanospheres in this experiment and literatures [31-33].

thumbnailFigure 4. SEM (a) image of bismuth nanomaterials were obtained when the amount of PVP was 0.310 g (sample 3). SEM image (b) and EDX pattern (e) of bismuth nanomaterials were obtained when the amount of PVP was 0.465 g (sample 4). Typical low- (c), high-magnification (d) TEM images, and EDX spectrum (f) of the bismuth nanostructures using DMF instead of EG as solvent (sample 5).

Interestingly, when DMF was instead of EG, bismuth nanoparticles and nanotubes arrays were formed under identical experimental conditions (Figure 4c, d). The average diameter of bismuth nanoparticles is about 50 nm, and the diameters of the bismuth nanotubes are in a narrow range from about 3.2 to 5.2 nm, with an average diameter of 4.3 nm. EDX was used to further analyze the elemental compositions of these nanotubes lying on the hole of the copper grid. It reveals the elemental Bi signals and confirmed the purity of this bismuth nanotube (Figure 4f). The copper and carbon peaks are due to the carbon-coated copper grid. Here, DMF plays an important role in the fabrication of bismuth nanotubes. In this synthesis, the starting materials can dissolve in DMF and DMF can partially decompose into dimethylamine, which is a good coordination ligand with N-chelation. The diffusion of Bi3+ ions in DMF-dimethylamine will be faster due to its lower viscosity, which is beneficial for the formation of nanotube products [49]. The formation mechanism is still limited and further study in progress.


In summary, uniform bismuth nanospheres were successfully synthesized via a facile solvothermal process by reduction of EG solution of bismuth salt, using PVP both as a reducing agent and a capping agent. The shapes and sizes of the bismuth nanostructures varied with the changing of the PVP/bismuth salt molar ratio. Uniform bismuth nanospheres with an average diameter of 180 nm could be routinely synthesized through this solvothermal approach by controlling the PVP/bismuth salt ratio. The solvent EG also played an important role in the formation of uniform bismuth nanospheres. Bismuth nanoparticles and nanotubes were formed when DMF was used as a solvent instead of EG. The possible formation mechanism of the bismuth nanotubes was also discussed and further study was in progress.


DMF: N,N-dimethylformamide; EDX: energy-dispersive X-ray; EG: ethylene glycol; PVP: poly(N-vinyl-2-pyrrolidone); SAED: selected area electron diffraction; SEM: scanning electron microscopy; TEM: transmission electron microscopy; XRD: X-ray diffraction.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

JW participated in the acquisition of data and drafted the manuscript. FQ carried out the SEM characterization and participated the analysis and interpretation of data. ZL and HJY helped to draft and revise the manuscript. RC made contributions to conception and design of the study, revised the manuscript critically for important intellectual content, and has given final approval of the version to be published.


This study was supported by National Natural Science Foundation of China (Grant 20801043), the Program for New Century Excellent Talents in University (NCET-09-0136), and the Outstanding Youth Scientific Foundation of Hubei Province (2009CDA075).


  1. Bigall NC, Härtling T, Klose M, Simon P, Eng LM, Eychmüller A: Monodisperse platinum nanospheres with adjustable diameters from 10 to 100 nm: Synthesis and distinct optical properties.

    Nano Lett 2008, 8:4588. PubMed Abstract | Publisher Full Text OpenURL

  2. Schwartzberg AM, Olson TY, Talley CE, Zhang JZ: Synthesis, characterization, and tunable optical properties of hollow gold nanospheres.

    J Phys Chem B 2006, 110:19935. PubMed Abstract | Publisher Full Text OpenURL

  3. Semagina N, Kiwi-Minsker L: Palladium nanohexagons and nanospheres in selective alkyne hydrogenation.

    Catal Lett 2009, 127:334. Publisher Full Text OpenURL

  4. Lee S, Chon H, Lee M, Choo J, Shin SY, Lee YH, Rhyu IJ, Son SW, Oh CH: Surface-enhanced raman scattering imaging of HER2 cancer markers overexpressed in single MCF7 cells using antibody conjugated hollow gold nanospheres.

    Biosens Bioelectron 2009, 24:2260. PubMed Abstract | Publisher Full Text OpenURL

  5. Nitin N, Javier DJ, Roblyer DM, Richards-Kortum R: Widefield and high-resolution reflectance imaging of gold and silver nanospheres.

    J Biomed Opt 2007, 12:051505. PubMed Abstract | Publisher Full Text OpenURL

  6. Skala MC, Crow MJ, Wax A, Izatt JA: Photothermal optical coherence tomography of epidermal growth factor receptor in live cells using immunotargeted gold nanospheres.

    Nano Lett 2008, 8:3461. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  7. Li W, Camargo PHC, Lu X, Xia Y: Dimers of silver nanospheres: Facile synthesis and their use as hot spots for surface-enhanced raman scattering.

    Nano Lett 2008, 9:485. Publisher Full Text OpenURL

  8. Chon H, Lee S, Son SW, Oh CH, Choo J: Highly sensitive immunoassay of lung cancer marker carcinoembryonic antigen using surface-enhanced raman scattering of hollow gold nanospheres.

    Anal Chem 2009, 81:3029. PubMed Abstract | Publisher Full Text OpenURL

  9. Cobley CM, Rycenga M, Zhou F, Li ZY, Xia Y: Controlled etching as a route to high quality silver nanospheres for optical studies.

    J Phys Chem C 2009, 113:16975. Publisher Full Text OpenURL

  10. Lok C-N, Ho C-M, Chen R, He Q-Y, Yu W-Y, Sun H, Tam PK-H, Chiu J-F, Che C-M: Proteomic analysis of the mode of antibacterial action of silver nanoparticles.

    J Proteome Res 2006, 5:916. PubMed Abstract | Publisher Full Text OpenURL

  11. Jia FL, Zhang LZ, Shang XY, Yang Y: Non-aqueous sol-gel approach towards the controllable synthesis of nickel nanospheres, nanowires, and nanoflowers.

    Adv Mater 2008, 20:1050. Publisher Full Text OpenURL

  12. Goy-López S, Castro E, Taboada P, Mosquera Vc: Block copolymer-mediated synthesis of size-tunable gold nanospheres and nanoplates.

    Langmuir 2008, 24:13186. PubMed Abstract | Publisher Full Text OpenURL

  13. Xiao C-W, Shen C-M, Xu Z-C, Yang T-Z, Gao H-J: Anomalous aggregation growth of palladium nanosphere with spr band in visible range.

    Chin Phys B 2008, 17:2066. Publisher Full Text OpenURL

  14. Lee C-L, Kuo L-C, Huang Y-C, Yen Y-W: Mesoporous, self-assembled palladium nanospheres: High efficiency activator for electroless nickel deposition.

    Electrochem Commun 2006, 8:697. Publisher Full Text OpenURL

  15. Yang FY, Liu K, Chien CL, Searson PC: Large magnetoresistance and finite-size effects in electrodeposited single-crystal Bi thin films.

    Phys Rev Lett 1999, 82:3328. Publisher Full Text OpenURL

  16. Carotenuto G, Hison C, Capezzuto F, Palomba M, Perlo P, Conte P: Synthesis and thermoelectric characterisation of bismuth nanoparticles.

    J Nanoparticle Res 2009, 11:1729. Publisher Full Text OpenURL

  17. Zhang Z, Yu K, Bai D, Zhu Z: Synthesis and electrochemical sensing toward heavy metals of bunch-like bismuth nanostructures.

    Nanoscale Res Lett 2010, 5:398. Publisher Full Text OpenURL

  18. Boukai A, Xu K, Heath JR: Size-dependent transport and thermoelectric properties of individual polycrystalline bismuth nanowires.

    Adv Mater 2006, 18:864. Publisher Full Text OpenURL

  19. Huber TE, Nikolaeva A, Gitsu D, Konopko L, Graf MJ: Role of boundary roughness in the electronic transport of Bi nanowires.

    J Appl Phys 2008, 104:123704. Publisher Full Text OpenURL

  20. Moore AL, Pettes MT, Zhou F, Shi L: Thermal conductivity suppression in bismuth nanowires.

    J Appl Phys 2009, 106:034310. Publisher Full Text OpenURL

  21. Yella A, Mugnaioli E, Panthöfer M, Therese HA, Kolb U, Tremel W: Bismuth-catalyzed growth of SnS2 nanotubes and their stability.

    Angew Chem Int Ed 2009, 48:6426. Publisher Full Text OpenURL

  22. Xiang Y, Cao L, Arbiol J, Brongersma ML, Fontcuberta i Morral A: Synthesis parameter space of bismuth catalyzed germanium nanowires.

    Appl Phys Lett 2009, 94:163101. Publisher Full Text OpenURL

  23. Wang F, Tang R, Yu H, Gibbons PC, Buhro WE: Size- and shape-controlled synthesis of bismuth nanoparticles.

    Chem Mater 2008, 20:3656. Publisher Full Text OpenURL

  24. Xu Y, Ren Z, Ren W, Cao G, Deng K, Zhong Y: Magnetic-field-assisted solvothermal growth of single-crystalline bismuth nanowires.

    Nanotechnology 2008, 19:115602. Publisher Full Text OpenURL

  25. Cao S, Guo C, Wang Y, Miao J, Zhang Z, Liu Q: Template-catalyst-free growth of single crystalline bismuth nanorods by RF magnetron sputtering method.

    Solid State Commun 2009, 149:87. Publisher Full Text OpenURL

  26. Yang D, Meng G, Xu Q, Han F, Kong M, Zhang L: Electronic transport behavior of bismuth nanotubes with a predesigned wall thickness.

    J Phys Chem C 2008, 112:8614. Publisher Full Text OpenURL

  27. Derrouiche S, Zoican Loebick C, Wang C, Pfefferle L: Energy-induced morphology changes in bismuth nanotubes.

    J Phys Chem C 2010, 114:4336. Publisher Full Text OpenURL

  28. Boldt R, Kaiser M, Köhler D, Krumeich F, Ruck M: High-yield synthesis and structure of double-walled bismuth-nanotubes.

    Nano Lett 2010, 10:208. PubMed Abstract | Publisher Full Text OpenURL

  29. Fu R, Xu S, Lu Y-N, Zhu JJ: Synthesis and characterization of triangular bismuth nanoplates.

    Cryst Growth Des 2005, 5:1379. Publisher Full Text OpenURL

  30. Wang WZ, Poudel B, Ma Y, Ren ZF: Shape control of single crystalline bismuth nanostructures.

    J Phys Chem B 2006, 110:25702. PubMed Abstract | Publisher Full Text OpenURL

  31. Cheng G, Wu J, Xiao F, Yu H, Lu Z, Yu X, Chen R: Synthesis of bismuth micro- and nanospheres by a simple refluxing method.

    Mater Lett 2009, 63:2239. Publisher Full Text OpenURL

  32. Li J, Fan H, Chen J, Liu L: Synthesis and characterization of poly(vinyl pyrrolidone)-capped bismuth nanospheres.

    Colloids Surf A 2009, 340:66. Publisher Full Text OpenURL

  33. Wang J, Wang X, Peng Q, Li Y: Synthesis and characterization of bismuth single-crystalline nanowires and nanospheres.

    Inorg Chem 2004, 43:7552. PubMed Abstract | Publisher Full Text OpenURL

  34. Wu J, Yang H, Li H, Lu Z, Yu X, Chen R: Microwave synthesis of bismuth nanospheres using bismuth citrate as a precursor.

    J Alloys Compd 2010, 498:L8. Publisher Full Text OpenURL

  35. Wang X, Zhuang J, Peng Q, Li Y: A general strategy for nanocrystal synthesis.

    Nature 2005, 437:121. PubMed Abstract | Publisher Full Text OpenURL

  36. Nikolopoulou A, Papoulis D, Komarneni S, Tsolis-Katagas P, Panagiotaras D, Kacandes GH, Zhang P, Yin S, Sato T: Solvothermal preparation of TiO2/saponite nanocomposites and photocatalytic activity.

    Appl Clay Sci 2009, 46:363. Publisher Full Text OpenURL

  37. Gao F, Lu Q, Komarneni S: Interface reaction for the self-assembly of silver nanocrystals under microwave-assisted solvothermal conditions.

    Chem Mater 2005, 17:856. Publisher Full Text OpenURL

  38. Wang Y, Xia Y: Bottom-up and top-down approaches to the synthesis of monodispersed spherical colloids of low melting-point metals.

    Nano Lett 2004, 4:2047. Publisher Full Text OpenURL

  39. Komarneni S, Li D, Newalkar B, Katsuki H, Bhalla AS: Microwave-polyol process for Pt and Ag nanoparticles.

    Langmuir 2002, 18:5959. Publisher Full Text OpenURL

  40. Hoppe CE, Lazzari M, Pardinas-Blanco I, Lopez-Quintela MA: One-step synthesis of gold and silver hydrosols using poly(N-vinyl-2-pyrrolidone) as a reducing agent.

    Langmuir 2006, 22:7027. PubMed Abstract | Publisher Full Text OpenURL

  41. Chen J, Lim B, Lee EP, Xia Y: Shape-controlled synthesis of platinum nanocrystals for catalytic and electrocatalytic applications.

    Nano Today 2009, 4:81. Publisher Full Text OpenURL

  42. Kaczmarek H, Kamińska A, Światek M, Rabek JF: Photo-oxidative degradation of some water-soluble polymers in the presence of accelerating agents.

    Die Angew Makromol Chem 1998, 261-262:109. Publisher Full Text OpenURL

  43. Bombicz P, Mutikainen I, Krunks M, Leskelä T, Madarász J, Niinistö L: Synthesis, vibrational spectra and X-ray structures of copper(I) thiourea complexes.

    Inorg Chim Acta 2004, 357:513. Publisher Full Text OpenURL

  44. Peng X, Manna L, Yang W, Wickham J, Scher E, Kadavanich A, Alivisatos AP: Shape control of CdSe nanocrystals.

    Nature 2000, 404:59. PubMed Abstract | Publisher Full Text OpenURL

  45. Lee S-M, Cho S-N, Cheon J: Anisotropic shape control of colloidal inorganic nanocrystals.

    Adv Mater 2003, 15:441. Publisher Full Text OpenURL

  46. Wang YW, Hong BH, Kim KS: Size control of semimetal bismuth nanoparticles and the UV-visible and IR absorption spectra.

    J Phys Chem B 2005, 109:7067. PubMed Abstract | Publisher Full Text OpenURL

  47. Yin Y, Alivisatos AP: Colloidal nanocrystal synthesis and the organic-inorganic interface.

    Nature 2005, 437:664. PubMed Abstract | Publisher Full Text OpenURL

  48. Alivisatos AP: Semiconductor clusters, nanocrystals, and quantum dots.

    Science 1996, 271:933. Publisher Full Text OpenURL

  49. Wei G, Deng Y, Lin Y-H, Nan C-W: Solvothermal synthesis of porous tellurium nanotubes.

    Chem Phys Lett 2003, 372:590. Publisher Full Text OpenURL