Open Access Nano Express

Mesoporous nitrogen-doped TiO2 sphere applied for quasi-solid-state dye-sensitized solar cell

Peng Xiang, Xiong Li, Heng Wang, Guanghui Liu, Ting Shu, Ziming Zhou, Zhiliang Ku, Yaoguang Rong, Mi Xu, Linfeng Liu, Min Hu, Ying Yang, Wei Chen, Tongfa Liu, Meili Zhang and Hongwei Han*

Author Affiliations

Michael Grätzel Center for Mesoscopic Solar Cells, Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, 430074, Hubei, People's Republic of China

For all author emails, please log on.

Nanoscale Research Letters 2011, 6:606  doi:10.1186/1556-276X-6-606


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/6/1/606


Received:27 September 2011
Accepted:24 November 2011
Published:24 November 2011

© 2011 Xiang et al; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

A mesoscopic nitrogen-doped TiO2 sphere has been developed for a quasi-solid-state dye-sensitized solar cell [DSSC]. Compared with the undoped TiO2 sphere, the quasi-solid-state DSSC based on the nitrogen-doped TiO2 sphere shows more excellent photovoltaic performance. The photoelectrochemistry of electrodes based on nitrogen-doped and undoped TiO2 spheres was characterized with Mott-Schottky analysis, intensity modulated photocurrent spectroscopy, and electrochemical impedance spectroscopy, which indicated that both the quasi-Fermi level and the charge transport of the photoelectrode were improved after being doped with nitrogen. As a result, a photoelectric conversion efficiency of 6.01% was obtained for the quasi-solid-state DSSC.

Introduction

Since a mesoscopic TiO2-based dye-sensitized solar cell [DSSC] was reported by O' Regan and Grätzel in 1991 [1], DSSC has emerged as a promising candidate for the practical photovoltaic application due to its low manufacturing cost and high energy conversion efficiency. Even though DSSC is now commercially available, market expansion is still limited because of the use of a liquid electrolyte, which always signifies instability due to the leakage of the solvent and the erosion of the electrode. It seems a good way to replace the liquid electrolyte by a solid-state or quasi-solid-state medium [2,3]. Unfortunately, compared with liquid electrolyte, solid-state or quasi-solid-state DSSC still presents lower energy conversion efficiency. Therefore, how to improve the performance of DSSC composing of solid-state or quasi-solid-state medium is still a big issue.

As one of the key components, mesoscopic TiO2 film plays an important role in determining the performance of DSSC, which assumes both the task of dye anchorage and charge carrier transport. Over the past decade, substantial efforts have been made to improve the performance of DSSC through the reformation of the TiO2 film. The first strategy is to increase the light absorption efficiency of the photoanode by increasing the surface area of the TiO2 film, which provides sufficient room for dye loading. Another strategy is to improve the electron injection efficiency by adjusting the conduction band edge to match the LUMO of the dye [4]. The last strategy is to increase the charge collection efficiency through the improvement of the electron transport or lifetime [5].

For an effective DSSC, the key parameters of the mesoscopic TiO2 film such as porosity, pore size distribution, light scattering, electron percolation, and conduction band edge should be coordinated to the characterization of the dye and electrolyte medium, which could be controlled by precursor chemistry, hydrothermal growth temperature, binder addition, doping materials, and sintering conditions [6]. Recently, Chen et al. [7] reported a mesoporous anatase TiO2 bead with high surface area and controllable pore size for DSSC, which indicated that the DSSC employing mesoporous TiO2 sphere has demonstrated longer electron diffusion lengths and extended electron lifetimes over Degussa P25 titania electrodes due to the favorable interconnected, densely packed nanocrystalline TiO2 particles inside the spheres, resulting in the improvement of the parameters. In 2005, Ma et al. [8] reported nitrogen-doped TiO2 particles for DSSC that enhanced the incident photon-to-current conversion efficiency within the spectrum of 380 to 520 nm and 550 to 750 nm; as a result, the short-circuit photocurrent density was pronouncedly improved. After that, Tian et al. [9] found that the position of the flatband potential edge was shifted to negative when doping nitrogen into the TiO2 film, which is attributed to the formation of an O-Ti-N bond and results in the improvement of the open-circuit voltage in DSSC.

Therefore, it could be expected to promote the performance of DSSC from the improvement of both the short-circuit photocurrent density and the open-circuit voltage with the nitrogen-doped TiO2 sphere. Herein, we attempted to synthesize a crystalline nitrogen-doped TiO2 sphere under the hydrothermal condition and apply it in quasi-solid-state DSSC. The results indicated that with the nitrogen-doped TiO2 sphere, the parameters of quasi-solid-state DSSC were improved in both the short-circuit photocurrent density and the open-circuit voltage. As a result, a power conversion efficiency up to 6.01% of quasi-solid-state DSSC was obtained under air mass [AM] 1.5 sunlight at 100 mW/cm2.

Experimental details

Mesoporous TiO2 spheres were synthesized with the hydrothermal method as follows: 8 g dodecylamine and 8 g titanium isopropoxide [TIP] were mixed with 360 mL ethanol. The urea solution was added into the dodecylamine-TIP mixture solution under vigorous stirring at ambient temperature. The molar ratio of the urea to TIP was adjusted to 0, 4, 8, and 16. Twelve hours later, the white TiO2 suspension was transferred into a Teflon-lined autoclave and then heated at 210°C. After 12 h, the nitrogen-doped TiO2 spheres were obtained and marked as TN0, TN1, TN2, and TN3, respectively.

Mesoscopic nitrogen-doped or undoped TiO2 sphere pastes for screen print were prepared as reported [10]. Hydroxypropyl cellulose was dissolved in ethanol to form 10 wt.% ethanolic mixture. Two grams of mesoscopic nitrogen-doped TiO2 sphere, 5 g 10 wt.% ethanolic mixture, 8.1 g terpineol, and 10 mL ethanol were mixed by ball milling for 12 h. Then, the slurry was sonicated for 30 min and concentrated to a paste with 20 wt.% TiO2.

The mesoscopic nitrogen-doped or undoped TiO2 sphere-based photoelectrode was coated on a fluorine-doped tin oxide [FTO] glass (TEC15; Pilkington TEC Glass™, IL, USA) by using a doctor blade and then sintered at 450°C for 30 min. The thickness of nitrogen-doped or undoped TiO2 sphere film was controlled by the thickness of scotch tape. The photoelectrode with a 2-μm TiO2 sphere layer was used for Mott-Schottky [MS] analysis. The electrode with a 12-μm TiO2 sphere film was dyed with N719 ethanolic solution. A sandwich structure quasi-solid-state DSSC containing the mesoscopic TiO2 sphere-based electrode, platinized counter electrode, and quasi-solid-state electrolyte was performed for photocurrent-voltage testing, which was sandwiched with a 100-μm film of Surlyn (DuPont Surlyn, Wilmington, DE, USA) and then heated at 100°C for sealing.

The surface appearance of their films on FTO glass was performed using a Sirion 200 field emission scanning electron microscopy [FE-SEM] (FEI Company, Eindhoven, the Netherlands). Veeco Dektak 150 (Veeco Instruments Inc., NY, USA) was used to detect the thickness of the TiO2 film. MS analysis was performed in a three-electrode cell under a dark condition, where the TN0- and TN2-based electrodes without dye (ca. 2 μm) were used as the work electrode, a saturated calomel electrode [SCE] served as the reference electrode, a platinum wire was used as the counter electrode, and the active area was 0.36 cm2. The ethylene carbonate and propylene carbonate (1:1 volume ratio) solution containing 0.01 M iodine [I2] and 0.1 M potassium iodide was used as an electrolyte for MS analysis. Intensity modulated photocurrent spectroscopy [IMPS] was characterized within TN0- and TN2-based DSSC and performed with a green light emitting diode (λmax = 535 nm) driven by Zahner Zenium. The photocurrent density-voltage curves of the quasi-solid-state DSSC were perfomed with a Keithley 2400 SourceMeter (Keithley Instruments, Inc., Ohio, USA) under illumination with an Oriel solar simulator (Newport Corporation, CA, USA) composed of a 1, 000-W xenon arc lamp and AM 1.5 G filters. Light intensity was calibrated with a normative silicon cell. The electrochemical impedance spectroscopy [EIS] of the quasi-solid-state DSSC was characterized by a potentiostat (M2273; EG&G Inc., MD, USA) with a frequency range from 100 mHz to 1 MHz.

Results and discussion

Figure 1 shows the SEM images of the TiO2 films using TN0, TN1, TN2, and TN3 powders. It could be found that films using TN0, TN1, and TN2 are composed of the interconnected mesoscopic spheres with the size around 550 nm, but the film using TN3 is composed of a three-dimensional network of interconnected nanoparticles. The TiO2 film composing of large mesoscopic spheres with considerable quantities and small nanocrystalline particles presents the ability to scatter light and also provides sufficient surface area for the dye loading. However, urea and dodecylamine are used as the nitrogen source and dispersant, forming mesoporous TiO2 spheres during the thermal treatment, respectively. Too much urea could destroy the accompaniment of the TiO2 sphere. Therefore, the mesoporous spheres are dispersed into small particles with the increase of urea content in the precursor solution as shown in the film using TN3.

thumbnailFigure 1. SEM images of nitrogen-undoped and doped TiO2 spheres based films.

Figure 2 presents the photocurrent density-voltage curves of the DSSC using TN0, TN1, TN2, and TN3 as photoelectrodes. Here the electrolyte is 10 wt.% Poly(ethylene oxide) (Mw = 2 × 106 g·mol-1), 0.1 M I2, 0.1 M lithium iodide, 0.6 M 1, 2-dimethyl-3-propyl imidazolium iodide, and 0.45 M N-methyl-benzimidazole 3-methoxypropionitrile solution [11]. An inverted vessel containing this electrolyte is shown in the inserted picture of Figure 2 and exhibits the characterization of the quasi-solid-state DSSC. The parameters of DSSCs are summarized in the inserted table, which demonstrates that compared with the undoped-nitrogen TiO2 sphere-based quasi-solid-state DSSC, all the performance of doped-nitrogen TiO2 sphere-based quasi-solid-state DSSC was improved. With the increase of nitrogen content within the TiO2 spheres, the short-circuit photocurrent density [Jsc] is increased from 8.57 mA·cm-2 of the undoped TiO2 sphere-based quasi-solid-state DSSC (TN0) to 10.09 mA·cm-2 of the TN1 and then reached to a maximum value of 12.82 mA·cm-2 of the TN2. However, when the nitrogen content within the sphere is increased further, the Jsc is decreased to 11.43 mA·cm-2 of the TN3. Compared with Jsc, the open-circuit voltage [Voc] is increased within a small amplitude with the increase of nitrogen content within the TiO2 spheres, which exhibits 590.6 mV for TN0, 596.3 mV for TN1, 607.0 mV for TN2, and 605.3 mV for TN3, and the fill factor is almost at a constant value of around 0.78, which is presented as follows: 0.79 for TN0, 0.78 for TN1, 0.77 for TN2, and 0.78 for TN3. As a result, the highest energy conversion efficiency [η] of 6.01% was obtained for TN2-based quasi-solid-state DSSC, which is 49% higher than that of TN0 (η = 4.04%), 27% higher than that of TN1 (η = 4.72%), and 11% higher than that of the TN3-based device (η = 5.41%).

thumbnailFigure 2. Current-voltage curves of quasi-solid-state DSSCs with nitrogen-doped and undoped TiO2 sphere-based electrodes.

In order to ascertain the role of doping nitrogen, two typical mesoscopic TiO2 sphere photoeletrodes with (TN2) and without doping nitrogen (TN0) were investigated by MS analysis, EIS, and IMPS. Normally, the Voc of DSSC could be improved by retarding interfacial recombination, shifting the conduction band of TiO2 to more negative potentials, and engineering a more favorable equilibrium Fermi-level position [12]. The flat band potential [Efb] is a very useful quantity in photoelectrochemistry as it facilitates location of the energetic position of the valence and conduction band edge of a given semiconductor material [13], which could be detected by MS analysis [9-12]. Figure 3 presents the MS plots of TN0- and TN2-based electrodes. Efb could be calculated by the following equation [14].

thumbnailFigure 3. Mott-Schottky plots of an electrode using TN0 and TN2.

C sc - 2 =  2  E - E fb - k T e   N D ε ε 0 e A 2

where Csc is the space charge capacity, ND is the electron density, ε is the dielectric constant, ε0 is the permittivity of vacuum, and A is the active surface area. Efb is the intercept extrapolating a straight line from the plot of the square of the space charge capacity against the applied voltage, which found that the Efb of the electrode using TN0 and TN2 are about -0.55 V and -0.68 V (vs. SCE), respectively. Compared with the undoped TiO2 sphere-based electrode, the Efb of the nitrogen-doped TiO2 sphere-based electrode is shifted to about 0.13 V negatively, which suggests that a higher quasi-Fermi level could be obtained by doping nitrogen, resulting in the enhancement of Voc of the mesoscopic nitrogen-doped TiO2 sphere-based DSSC.

The charge transport within the nanocrystalline semiconductor of the photoelectrode could be detected by IMPS, and Figure 4 presents the IMPS of the photoelectrode using TN0 and TN2. The transport time [τd] of the injected electrons through the TiO2 film can be calculated from the equation τd = 1/(2πfd, min) [15], where fd, min is the characteristic frequency at the minimum of the IMPS imaginary component. The simulation results show that τd values are estimated to be 1.72 and 1.18 ms in the films using TN0 and TN2, respectively. In addition, the electron diffusion coefficient [Dn] could be calculated from the equation Dn = d2/(2.35τd) [15], where d is the thickness of the photoeletrode. Therefore, the Dn in the films using TN0 and TN2 are calculated to be 9.9 × 10-6 and 1.44 × 10-5 cm2·s-1, respectively. It is clear that the charge transport within the TN2 film is faster than that of the TN0 film, which suggests that the charge collection efficiency and Jsc of DSSC could be improved by nitrogen doping.

thumbnailFigure 4. IMPS plots of TN0- and TN2-based quasi-solid-state DSSCs.

EIS was carred out in the dark condition to investigate the discrepancy of the interfacial recombination between the electrodes using TN0 and TN2. Figure 5 presents the typical Nyquist plots of the TN0- and TN2-based cells. The interfacial impedance related to the electron transfer from the conduction band of TiO2 to the electrolyte can be described by the semicircle of the middle frequency region in the Nyquist plot. Their charge transfer resistance [Rct] values are evaluated by fitting the spectra with the equivalent circuit shown in the inset, which shows 281 Ω of TN0- and 362 Ω of TN2-based cells. Compared with the pure TiO2 sphere-based cell, the Rct of the mesoscopic nitrogen-doped TiO2 sphere-based cell is increased to 29%, suggesting that the interface resistance between the TiO2 sphere electrode and electrolyte is increased by introducing nitrogen. Therefore, the interface recombination between photoelectrode and electrolyte within DSSC would be retarded with this nitrogen-doped TiO2 sphere, resulting in the decrease of dark current and the improvement of Jsc and Voc.

thumbnailFigure 5. Nyquist plots of TN0- and TN2-based quasi-solid-state DSSCs.

Conclusions

A series of mesoscopic nitrogen-doped and undoped TiO2 spheres for quasi-solid-state DSSC have been prepared by the hydrothermal method. The effects of nitrogen within TiO2 spheres on the photovoltaic performance have been investigated, which show that the introduction of nitrogen increases Jsc, Voc, and efficiency. The photoelectrochemistry of nitrogen-doped and undoped TiO2 sphere-based electrodes was performed with MS, IMPS, and EIS. The results indicated that the quasi-Fermi level and the charge transport of the photoelectrode were improved, and the interfacial recombination was retarded after being doped with nitrogen within a mesoscopic sphere-based electrode. As a result, a DSSC with a power conversion efficiency of 6.01% under AM 1.5 sunlight at 100 mW/cm2 has been obtained with N719 dye in combination with a quasi-solid state electrolyte. Higher parameter DSSC could be expected with this mesoscopic nitrogen-doped TiO2 sphere.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

PX carried out the DSSC studies, participated in the sequence alignment and drafted the manuscript. XL, HW, GL, TS, ZZ, and WC participated in the design of the study and performed the statistical analysis. ZK, YR, MX, LL, MH, YY, TL, and MZ carried out material synthesis. HH conceived of the study and participated in its design and coordination. All authors read and approved the final manuscript.

Acknowledgements

The authors acknowledge the financial support by the National Natural Science Foundation of China (Grant No. 61106056), the Nature Science Foundation of Hubei Province (2008CDA042), and the Fundamental Research Funds for the Central Universities (Hust, 2011TS020). We also thank the Analytical and Testing Center of Huazhong University of Science and Technology [HUST] for field emission scanning electron microscopy [FE-SEM] testing.

References

  1. O'Regan B, Gratzel M: A low-cost, high-efficiency solar cell based on dye-sensitized collidal TiO2 films.

    Nature 1991, 353:737-740. Publisher Full Text OpenURL

  2. Bach U, Lupo D, Comte P, Moser JE, Weissortel F, Salbeck J, Spreitzer H, Gratzel M: Solid-state dye-sensitized mesoporous TiO2 solar cells with high photon-to-electron conversion efficiencies.

    Nature 1998, 395:583-585. Publisher Full Text OpenURL

  3. Wang H, Liu GH, Li X, Xiang P, Ku ZL, Rong YG, Xu M, Liu LF, Hu M, Yang Y, Han HW: Highly efficient poly(3-hexylthiophene) based monolithic dye-sensitized solar cells with carbon counter electrode.

    Energ Environ Sci 2011, 4:2025-2029. Publisher Full Text OpenURL

  4. Jose R, Thavasi V, Ramakrishna S: Metal oxides for dye-sensitized solar cells.

    J Am Ceram Soc 2009, 92:289-301. Publisher Full Text OpenURL

  5. DiCarmine PM, Semenikhin OA: Intensity modulated photocurrent spectroscopy (IMPS) of solid-state polybithiophene-based solar cells.

    Electrochim Acta 2008, 53:3744-3754. Publisher Full Text OpenURL

  6. Kalyanasundaram K, Gratzel M: Applications of functionalized transition metal complexes in photonic and optoelectronic devices.

    Coord Chem Rev 1998, 177:347-414. Publisher Full Text OpenURL

  7. Chen DH, Huang FZ, Cheng YB, Caruso RA: Mesoporous anatase TiO2 beads with high surface areas and controllable pore sizes A superior candidate for high-performance dye-sensitized solar cells.

    Adv Mater 2009, 21:2206-2210. Publisher Full Text OpenURL

  8. Ma TL, Akiyama M, Abe E, Imai I: High-efficiency dye-sensitized solar cell based on a nitrogen-doped nanostructured titania electrode.

    Nano Lett 2005, 5:2543-2547. PubMed Abstract | Publisher Full Text OpenURL

  9. Tian HJ, Hu LH, Zhang CN, Liu WQ, Huang Y, Mo L, Guo L, Sheng J, Dai SY: Retarded charge recombination in dye-sensitized nitrogen-doped TiO2 solar cells.

    J Phys Chem C 2010, 114:1627-1632. Publisher Full Text OpenURL

  10. Ito S, Murakami TN, Comte P, Liska P, Gratzel C, Nazeeruddin MK, Gratzel M: Fabrication of thin film dye sensitized solar cells with solar to electric power conversion efficiency over 10%.

    Thin Solid Films 2008, 516:4613-4619. Publisher Full Text OpenURL

  11. Shi YT, Zhan C, Wang LD, Ma BB, Gao R, Zhu YF, Qiu Y: The electrically conductive function of high-molecular weight poly(ethylene oxide) in polymer gel electrolytes used for dye-sensitized solar cells.

    Phys Chem Chem Phys 2009, 11:4230-4235. PubMed Abstract | Publisher Full Text OpenURL

  12. Feng X, Shankar K, Paulose M, Grimes CA: High open-circuit voltage-tantalum-doped TiO2nanowire arrays.

    Angew Chem 2009, 48:8095-8098. Publisher Full Text OpenURL

  13. Gratzel M: Photoelectrochemical cells.

    Nature 2001, 414:338-344. PubMed Abstract | Publisher Full Text OpenURL

  14. Van de Krol R, Goossens A, Schoonman J: Mott-Schottky analysis of nanometer-scale thin-film anatase TiO2.

    J Electrochem Soc 1997, 144:1723-1727. Publisher Full Text OpenURL

  15. Zhang W, Zhu R, Ke L, Liu X, Liu B, Ramakrishna S: Anatase mesoporous TiO2 nanofibers with high surface area for solid-state dye-sensitized solar cells.

    Small 2010, 6:2176-2182. PubMed Abstract | Publisher Full Text OpenURL