Open Access Nano Express

Dielectric Relaxation of La-Doped Zirconia Caused by Annealing Ambient

C Z Zhao12*, M Werner23, S Taylor2, P R Chalker3, A C Jones4 and Chun Zhao12

Author Affiliations

1 Department of Electrical and Electronic Engineering, Xi'an Jiaotong, Liverpool University, 215123, Suzhou, Jiangsu, China

2 Department of Electrical Engineering and Electronics, University of Liverpool, Liverpool, L69 3GJ, UK

3 Department of Engineering, Materials Science and Engineering, University of Liverpool, Liverpool, L69 3GH, UK

4 Department of Chemistry, University of Liverpool, Liverpool, L69 3ZD, UK

For all author emails, please log on.

Nanoscale Res Lett 2011, 6:48  doi:10.1007/s11671-010-9782-z


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/6/1/48


Received:13 April 2010
Accepted:9 September 2010
Published:30 September 2010

© 2010 Zhao et al.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

La-doped zirconia films, deposited by ALD at 300°C, were found to be amorphous with dielectric constants (k-values) up to 19. A tetragonal or cubic phase was induced by post-deposition annealing (PDA) at 900°C in both nitrogen and air. Higher k-values (~32) were measured following PDA in air, but not after PDA in nitrogen. However, a significant dielectric relaxation was observed in the air-annealed film, and this is attributed to the formation of nano-crystallites. The relaxation behavior was modeled using the Curie–von Schweidler (CS) and Havriliak–Negami (HN) relationships. The k-value of the as-deposited films clearly shows a mixed CS and HN dependence on frequency. The CS dependence vanished after annealing in air, while the HN dependence disappeared after annealing in nitrogen.

Keywords:
La; ZrO2; La0.35Zr0.65O2

Introduction

Amorphous ZrO2 is one of the most promising dielectrics (dielectric constant k-value ~20) to replace SiO2 in MOSFETs at the 45-nm node CMOS technologies. Due to the aggressive down-scaling of MOSFET, higher dielectric constant materials and higher mobility semiconductors other than silicon are introduced [1-11]. Germanium is considered to be a good candidate to replace silicon in the channel of next-generation high-performance CMOS devices, while rare earth oxides belonging to another class of materials offer good passivation of germanium to reduce the density of interface states, as it has recently been suggested [5,7,10]. On the other hand, theoretical studies have reported that the metastable tetragonal and cubic phases (t- and c-phases) of ZrO2 have higher k-values [12,13]. The addition of rare earth elements, such as La, Gd, Dy, or Er, is reported to stabilize these phases and k-values of up to 40 have been obtained [7-11,14].

In order to induce the t- and c-phases in the La-doped ZrO2, dielectric post-deposition annealing (PDA) is needed, otherwise the layers grown by atomic layer deposition (ALD) at relatively low temperatures (<450°C) have an amorphous microstructure [15,16]. However, the transformation from amorphous to t- and c-phases can cause both dielectric relaxation and an adverse increase in the leakage current [14,17]. Leakage, which is the quantity defined in the ITRS Roadmap, depends on the combination of k-value and energy offset values between the energy bands of the high-k material and the silicon crystal. For example, 1 × 10-8 A/cm2 is a value required for DRAM capacitors [18] (much higher values are accepted for gate oxides in CMOS). Since the purpose to introduce high-k dielectrics is to reduce the leakage current of gate oxides, a lot of investigations on the leakage current of high-k dielectrics have been carried out [19-23].

However, there is little information about dielectric relaxation of La-doped ZrO2 dielectrics. Since loss due to the dielectric relaxation can cause MOSFET deterioration, the aim in this study was therefore to investigate the effect of PDA on the relaxation behavior of La-doped ZrO2. In this paper, we report the influence of the annealing ambient on the dielectric relaxation processes, which can be described by both the Havriliak–Negami (HN) and Curie–von Schweidler (CS) relationships [24-27] in the frequency range of 10 MHz.

Experimental

La-doped ZrO2 films, with a thickness of 35 nm, were deposited on n-type Si(100) substrates by liquid injection ALD at 300°C, using a modified Aixtron AIX 200FE AVD reactor configured for liquid injection [28]. Both Zr and La sources are Cp-based precursors ([(MeCp)2ZrMe(OMe)] and [(iPrCp)3La]) [15,16]. The composition of the La-doped ZrO2 films was estimated to be La0.35Zr0.65O2 from Auger electron spectroscopy (AES). Selected films were annealed at 700°C or 900°C for 15 min, in an N2 or air ambient.

The effects of PDA on the physical and electrical properties of the La0.35Zr0.65O2 films have been investigated using cross-section transmission electron microscopy (XTEM), X-ray diffraction (XRD), high–low frequency capacitance–voltage (C–V), capacitance–frequency (C–f), and current–voltage (I–V) measurements, respectively.

In order to perform the C–V, C–f and I–V measurements, metal (Au) gate electrodes were evaporated to form metal–oxide–semiconductor capacitors (Au/La0.35Zr0.65O2/IL/n-Si, where IL stands for interfacial layer) with an effective contact area of 4.9 × 10-4 cm2. The backside of the Si wafer was cleaned with a buffered HF solution, and subsequently a 200-nm-thick film of Al was deposited to form an ohmic back contact. A thermal SiO2 sample was grown using dry oxidation at 1100°C to provide a comparison with the high-k stacks. Its back-side contact was prepared in exactly the same way as for all other La0.35Zr0.65O2 samples: depositing Al after HF treatment.

Results and Discussion

XRD was carried out using a Rikagu Miniflex X-ray diffractometer with nickel-filtered Cu Kα radiation (λ = 1.5405 Å) and a 2θ increment of 0.2° per minute, and the results are shown in Figure 1. Results from the as-deposited samples and samples annealed at 700°C showed that the films were amorphous. XRD spectra from both samples annealed at 900°C show two clear diffraction peaks at 29.3° and 33.9°, suggesting that crystallization starts between 700 and 900°C. These peaks correspond to the t- or c- phases, but it is difficult to distinguish between them. Selected area diffraction results (not shown) obtained using a TEM would suggest that the cubic phase is the most likely.

thumbnailFigure 1. X-ray diffraction data for La0.35Zr0.65O2 films deposited by ALD and then annealed in air or N2 for 15 min at different temperatures.

XTEM was carried out on both the 900°C PDA samples using a JEOL 2000FX operated at 200 kV. XTEM images in Figure 2 show that equiaxed nano-crystallites of ~4 nm diameter were formed in the air-annealed sample, in comparison with larger ~15-nm crystals for the N2-annealed sample. The thickness of the La0.35Zr0.65O2 layers and the IL was also obtained by XTEM. The 35-nm-thick La0.35Zr0.65O2 layers retained their thickness after PDA, but the IL increased from 1.5 nm on the as-deposited samples to 4.5 nm and 6 nm after PDA at 900°C in N2 and in air, respectively, which is attributed to either an internal or external oxidation mechanism. Previous medium energy ion scattering (MEIS) results [16] showed the incorporation of some La in the IL, which is reported to increase the k-value of the IL from 3.9 (pure SiO2) to ~10 [29].

thumbnailFigure 2. XTEM images from La0.35Zr0.65O2 samples, which were annealed in air and N2 at 900°C for 15 min, respectively.

C–V and C–f measurements were carried out using a HP4192 impedance analyzer and an Agilent E4980A LCR meter at various frequencies (20 Hz–13 MHz) in parallel mode. C–f measurements were performed at a strong accumulation region (Vg = + 3 V). C–V measurements were carried out from strong inversion toward strong accumulation and vice versa. Three typical sets of C–V curves of the as-deposited and PDA samples were shown in Figure 3. PDA was found to significantly reduce the hysteresis to ~10 mV (counterclockwise), independent of the annealing ambient. PDA in air caused a negative shift of the C–V curves due to positive charge generation and also caused an enhanced accumulation capacitance, which originated from a k-value increase in the La0.35Zr0.65O2 layer. Positive charge generation will be discussed first, and then the k-value increase.

thumbnailFigure 3. C–V measurements were carried out at frequency = 1 kHz for as-deposited and PDA samples.

From the early days of silicon technology, thermal oxidation of Si has been known to introduce fixed positive charge at the Si/SiO2 interface [30]. Positive charge generation during high-temperature processing is not new to thin film SiO2 physics; its presence has been detected ever since the pioneering era of Si oxidation in the form of fixed oxide charge that often develops during the oxidation process [31]. The presence of positively charged, over-coordinated oxygen centers in SiO2 has been suggested previously in the work of Snyder and Fowler [32]. They showed that the positive charge involved with the E' oxygen-vacancy center is in fact associated with over-coordination of an O. Warren et al. suggested that the formation of positively charged over-coordinated O defects is near the Si/SiO2 interface [33,34]. The effect of post-deposition oxidation of SiOx/ZrO2 gate dielectric stacks at different temperatures (500–700°C) on the density of fixed charge was proposed by Houssa et al. [35]. They indicated that increasing oxidation temperature, the density of negative fixed charge is reduced. The net positive charge observed after oxidation at >500°C resembles the charge generated at the Si/SiO2 interface by hydrogen in the same temperatures range. They proposed that the observed oxidation-induced positive charge in the SiOx/ZrO2 gate stack may be related to over-coordinated oxygen centers induced by hydrogen. This also matches our previous observations at the Si/SiO2 and Si/SiO2/HfO2 structures [36,37].

Before discussing the k-value increase, the causes of frequency dispersion must be totally understood. Figure 4 (a) indicates that a large frequency dispersion was observed during C–V measurements in the air-annealed sample. There are five reasons that may cause the frequency dispersion observed: (1) series resistances, (2) parasitic effects (including back contact imperfection and cables and connections), (3) leakage currents, (4) the interlayer between La0.35Zr0.65O2 layer and semiconductor silicon substrate, or (5) a k-value dependence on frequency of the La0.35Zr0.65O2 dielectric. To obtain the genuine intrinsic properties and permittivity of the La0.35Zr0.65O2 dielectric from the CV measurements, the first four effects must be eliminated.

thumbnailFigure 4. (a) C–V results at different frequencies from the air-annealed sample. Significant frequency dispersion was observed. (b) No frequency dispersion in C–V measurements was observed in the thermal oxide (SiO2) sample with the back-side contact prepared in the same way as for the LaZrO sample shown in (a).

The effects of series resistances and parasitic effects were reported in our previous work [38]. To minimize the effects of series resistances and back contact imperfections (including contact resistance R, contact capacitance C, or parasitic R–C coupled in series, etc.), aluminum back contacts were deposited over a large area of the substrate wafer that was cleaned with a buffered HF solution before aluminum contacts were formed. The same procedure was carried out for all as-deposited, N2-annealed, and air-annealed samples. All samples tested had the same or very similar substrate area (~ 2 × 2 cm2) to ensure that the effects of series resistance and back contact imperfections were the same for all samples. Furthermore, measurement cables and connections were kept short to further minimize parasitic capacitance effects and were the same for all samples. To provide a comparison with Figure 4a, a C–V measurement on a thermal SiO2 sample with the same HF treatment and Al deposition on its back was carried out from the same test system; the results are shown in Figure 4b. It is clear that no frequency dispersion was observed on the thermal SiO2 sample. Therefore, the effects of series resistances and parasitic effects are negligible.

The leakage current characteristics of the La-doped films were evaluated from the I–V measurements, as shown in Figure 5. At low oxide fields (Eox at 0 to +2MV/cm), the leakage current density is improved under positive gate biases after annealing, which is attributed to the thicker IL. However, PDA also causes crystallization that introduces leakage current paths and reduces the break-down voltage. The leakage current densities at +2MV/cm are 1.6 × 10-5 Acm-2 for as-deposited samples, but below 5 × 10-8 Acm-2 after the 900°C PDA either in N2 or in air. This suggests that the effect of leakage currents on frequency dispersion is negligible during C–V measurements.

thumbnailFigure 5. The relationship between leakage current density (Jg) and electric field (Eox) applied across the La0.35Zr0.65O2/IL (IL stands for interfacial layer) stacks for as-deposited and PDA samples. Break-down voltages (VBD) were indicated.

Before k-value of the La0.35Zr0.65O2 dielectric is extracted from the strong accumulation capacitance at +3 V (<+1MV/cm), the effect of the presence of the lossy interlayer must be taken into account. The effect was also reported in our previous work [38].

The relationship between the extracted k-value and test frequency shown in Figure 6 indicates that significant dielectric relaxation only occurs in the air-annealed sample. Parasitic effects could not be the cause of the frequency dispersion observed because of the sample preparation and measurement procedures described earlier. Significant frequency dispersion was not seen in other MOSCs fabricated using the same substrates prepared and measured in exactly the same way. We conclude therefore that the frequency dispersion observed in the La0.35Zr0.65O2 film annealed in air is a real material property of this dielectric. There are two important observations in Figure 6: (1) PDA in air increases the k-value of the La0.35Zr0.65O2 dielectric significantly (k-value reaches 32 at 1 kHz), along with a significant dielectric relaxation. (2) There is less of an effect on the k-value for the film annealed in N2, with a small increase in k-value at some frequencies and a flatter frequency response compared to the as-deposited sample. Both effects of temperature/ambient and causes of dielectric relaxation are discussed later.

thumbnailFigure 6. Frequency dependence of k-value of La0.35Zr0.65O2 dielectric for as-deposited and PDA samples. Significant dielectric relaxation was observed in the air-annealed sample. Solid lines are the fitting results using equations (1) and (2).

Annealing at a high temperature is employed to induce the t- and c-phases in the La-doped ZrO2 dielectric from the amorphous samples [15,16]. The addition of La is to stabilize these phases, and the stabilized tetragonal/cubic ZrO2 phase gives a higher k-value [7-14]. Annealing temperature was reported to range from 400 to 1,050°C, depending on the deposition conditions and substrates of high-k dielectrics that determine the microstructure of the as-deposited samples. It was reported that the germanium substrate requires lower annealing temperatures ranging from 400 to 600°C [7-11]. If the microstructure of the as-deposited LaZrO2 samples had already been tetragonal/cubic, annealing at high temperatures would not be necessary [9].

It has been shown previously that dielectric relaxation in the time domain can be described by a power-law time dependence, t-n [26,27], or a stretched exponential time dependence, exp[-(t/t0)m] [39,40], where n and m are parameters ranging between 0 and 1, and t0 is a characteristic relaxation time.

In the frequency domain, after a Fourier transform, the corresponding dielectric response of t-n dependence is well described in terms of Curie–von Schweidler (CS) behavior [24,26,27], while the Fourier transform of exp[-(t/t0)m] function into frequency domain can be approximated by a Havriliak–Negami (HN) relationship [25], after a great deal of work [41-43]. The CS law and HN relationship can be, respectively, expressed as

<a onClick="popup('http://www.nanoscalereslett.com/content/6/1/48/mathml/M1','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/6/1/48/mathml/M1">View MathML</a>

(1)

<a onClick="popup('http://www.nanoscalereslett.com/content/6/1/48/mathml/M2','MathML',630,470);return false;" target="_blank" href="http://www.nanoscalereslett.com/content/6/1/48/mathml/M2">View MathML</a>

(2)

where εs and ε, are the static and high-frequency limit permittivities, respectively; τ is the HN relaxation time; ω = 2πf is the angular frequency; and n, α, and β are the relaxation parameters.

A theoretical description of the slow relaxation in complex condensed systems is still a topic of active research despite the great effort made in recent years. There exist two alternative approaches to the interpretation of dielectric relaxation: the parallel and series models [44]. The parallel model represents the classical relaxation of a large assembly of individual relaxing entities such as dipoles, each of which relaxes with an exponential probability in time but has a different relaxation time tk. The total relaxation process corresponds to a summation over the available modes k, given a frequency domain response function, which can be approximated by the HN relationship.

The alternative approach is the series model, which can be used to describe briefly the origins of the CS law (the t-n behavior). Consider a system divided into two interacting sub-systems [45]. The first of these responds rapidly to a stimulus generating a change in the interaction which, in turn, causes a much slower response of the second sub-system. The state of the total system then corresponds to the excited first system together with the unresponded second system and can be considered as a transient or metastable state, which slowly decays as the second system responds.

In some complex condensed systems, neither the pure parallel nor the pure series approach is accepted and instead interpolates smoothly between these extremes [46]. The CS behavior has to be faster than the HN function at short times and slower than the HN function at long times.

Based on the discussion above, the dielectric relaxation results (shown in Figure 6) have been modeled with the CS and/or HN relationships (see solid lines in Figure 6). The relaxation of the as-deposited film obeyed a mixed CS and HN relationships. After the 900°C PDA, the relaxation behavior of the N2-annealed film was dominated by the CS law, whereas the air-annealed film was predominantly modeled by the HN relationship that was accompanied by a sharp drop in the k-value.

Although the exact microstructural cause of these relaxation processes is not clearly known, several mechanisms for the dielectric relaxation have been proposed, including distribution of relaxation time [47], distribution of hopping probabilities [48], space charge trapping [49], self-similar multi-well potential for ionic configurations [45], or double potential well occupied by one electron [50]. However, it has been reported that a decrease in crystal grain size can cause an increase in the dielectric relaxation in ferroelectric relaxor ceramics [51,52]. This relaxation effect has been attributed to higher stresses in the smaller grains [51]. A similar effect appears to have occurred with these La-doped dielectric films, with the 900°C air anneal producing 4-nm diameter equiaxed nano-crystallites within the film, and suffering from a severe dielectric relaxation. The 900°C N2-annealed film contains much larger ~15-nm crystals and does not suffer from severe dielectric relaxation. Therefore, the physical processes behind the relaxation are probably related to the size of the crystal grains formed during annealing.

Conclusions

PDA at 900°C either in N2 or in air causes crystallization (t- or c-phases) of the La0.35Zr0.65O2 dielectric. Larger crystal grain sizes were observed in the N2-annealed sample than in the air-annealed sample. Following PDA in N2, the k-value was maintained and the dielectric relaxation was reduced. However, PDA in air causes a significant increase in k-value (32 at 1 kHz) and a significant dielectric relaxation, probably associated with smaller crystal grain sizes. The relaxation behavior of the as-deposited sample can be modeled using the mixed CS and HN relationships. PDA in N2 suppressed the HN law, while the CS law was removed following PDA in air.

Acknowledgements

This research was funded in part from the Engineering and Physical Science Research Council of UK under the grant EP/D068606/1, the National Natural and Science Foundation of China under the grant no. 60976075, and the Suzhou Science and Technology Bureau of China under the grant SYG201007.

References

  1. Boscke TS, Govindarajan S, Fachmann C, Heitmann J, Avellan A, Schroder U, Kirsch PD, Krug C, Hung PY, Song SC, Ju BS, Price J, Pant G, Gnade BE, Krautschneider W, Lee B-H, Jammy R:

    Tech Dig Int Electron Devices Meet. 2006, 255. OpenURL

  2. Lu N, Li H-J, Peterson JJ, Kwong DL:

    Appl Phys Lett. 2007, 90:082911. Publisher Full Text OpenURL

  3. Darmawan P, Lee PS, Setiawan Y, Ma J, Oscipowicz T:

    Appl Phys Lett. 2007, 91:092903. Publisher Full Text OpenURL

  4. Lopes JMJ, Littmark U, Roeckerath M, St Lenk , Schubert J, Mantl S, Besmehn A:

    J Appl Phys. 2007, 101:104109. Publisher Full Text OpenURL

  5. Mavrou G, Galata S, Tsipas P, Sotiropoulos A, Panayiotatos Y, Dimoulas A, Evangelou EK, Seo JW, Dieker Ch:

    J Appl Phys. 2008, 103:014506. Publisher Full Text OpenURL

  6. Abermann S, Bethge O, Henkel C, Bertagnolli E:

    Appl Phys Lett. 2009, 94:262904. Publisher Full Text OpenURL

  7. Abermann S, Henkel C, Bethge O, Pozzovivo G, Klang P, Bertagnolli E:

    Applied Surface Science. 2010, 256:5031. Publisher Full Text OpenURL

  8. Mavrou G, Tsipas P, Sotiropoulos A, Galata S, Panayiotatos Y, Dimoulas A, Marchiori C, Fompeyrine J:

    Appl Phys Lett. 2008, 93:212904. Publisher Full Text OpenURL

  9. Tsoutsou D, Apostolopoulos G, Galata S, Tsipas P, Sotiropoulos A, Mavrou G, Panayiotatos Y, Dimoulas A:

    Microelectron Eng. 2009, 86:1626. Publisher Full Text OpenURL

  10. Tsoutsou D, Lamagna L, Volkos SN, Molle A, Baldovino S, Schamm S, Coulon PE, Fanciulli M:

    Appl Phys Lett. 2009, 94:053504. Publisher Full Text OpenURL

  11. Lamagna L, Wiemer C, Baldovino S, Molle A, Perego M, Schamm-Chardon S, Coulon PE, Fanciulli M:

    Appl Phys Lett. 2009, 95:122902. Publisher Full Text OpenURL

  12. Vanderbilt D, Zhao X, Ceresoli D:

    Thin Solid Films. 2005, 486:125. Publisher Full Text OpenURL

  13. Zhao X, Vanderbilt D:

    Phys Rev B. 2002, 65:233106. Publisher Full Text OpenURL

  14. Govindarajan S, Boscke TS, Sivasubramani P, Kirsch PD, Lee BH, Tseng H-H, Jammy R, Schroder U, Ramanathan S, Gnade BE:

    Appl Phys Lett. 2007, 91:062906. Publisher Full Text OpenURL

  15. Gaskell JM, Jones AC, Aspinall HC, Taylor S, Taechakumput P, Chalker PR, Heys PN, Odedra R:

    Appl Phys Lett. 2007, 91:112912. Publisher Full Text OpenURL

  16. Gaskell JM, Jones AC, Chalker PR, Werner M, Aspinall HC, Taylor S, Taechakumput P, Heys PN:

    Chem Vap Deposition. 2007, 13:684. Publisher Full Text OpenURL

  17. Boscke TS, Govindarajan S, Kirsch PD, Hung PY, Krug C, Lee BH, Heitmann J, Schroder U, Pant G, Gnade BE, Krautschneider WH:

    Appl Phys Lett. 2007, 91:072902. Publisher Full Text OpenURL

  18. Mueller W, Aichmayr G, Bergner W, Erben E, Hecht T, Kapteyn C, Kersch A, Kudelka S, Lau F, Luetzen J, Orth A, Nuetzel J, Schloesser T, Scholz A, Schroeder U, Sieck A, Spitzer A, Strasser M, Wang PF, Wege S, Weis R:

    Tech Dig –Int Electron Devices Meet. 2005, 34. OpenURL

  19. Fu Chung-Hao, Chang-Liao Kuei-Shu, Wang Tien-Ko, Tsai WF, Ai CF:

    Microelectronic Engineering. 2010, 87:2014. Publisher Full Text OpenURL

  20. Xiong Yuhua, Tu Hailing, Du Jun, Ji Mei, Zhang Xinqiang, Wang Lei:

    Appl Phys Lett. 2010, 97:012901. Publisher Full Text OpenURL

  21. Southwick RichardG, Reed Justin, Buu Christopher, Butler Ross, Bersuker Gennadi, Knowlton WilliamB:

    IEEE Tran Device and Materials Reliability. 2010, 10:201. Publisher Full Text OpenURL

  22. Kim Joo-Hyung, Ignatova VelislavaA, Kücher Peter, Weisheit Martin, Zschech Ehrenfried:

    Current Applied Physics. 2009, 9:e104. Publisher Full Text OpenURL

  23. Martin Dominik, Grube Matthias, Weber WalterM, Rüstig Jürgen, Bierwagen Oliver, Geelhaar Lutz, Riechert Henning:

    Appl Phys Lett. 2009, 95:142906. Publisher Full Text OpenURL

  24. Jonscher AK: Dielectric Relaxation in Solids. Chelsea Dielectric Press, London; 1983. OpenURL

  25. Havriliak S, Negami S:

    Polymer. 1967, 8:161. Publisher Full Text OpenURL

  26. Curie J:

    Ann Chim Phys. 1889, 18:203. OpenURL

  27. von Schweidler E:

    Ann Phys. 1907, 24:711. Publisher Full Text OpenURL

  28. Potter RJ, Chalker PR, Manning TD, Aspinall HC, Loo YF, Jones AC, Smith LM, Critchlow GW, Schumacher M:

    Chem Vap Deposition. 2005, 11:159. Publisher Full Text OpenURL

  29. Watanabe H, Ikarashi N, Ito F:

    Appl Phys Lett. 2003, 83:3546. Publisher Full Text OpenURL

  30. Cheng YC:

    Prog Surf Sci. 1977, 8:181.

    and references therein

    Publisher Full Text OpenURL

  31. Deal BE, Sklar M, Grove AS, Snow EH:

    J Electrochem Soc. 1967, 114:266. Publisher Full Text OpenURL

  32. Synder KC, Fowler WB:

    Phys Rev B. 1993, 48:13238. Publisher Full Text OpenURL

  33. Warren WL, Vanheusden K, Schwank JR, Fleetwood DM, Winokur PS, Devine RAB:

    Appl Phys Lett. 1996, 68:2993. Publisher Full Text OpenURL

  34. Warren WL, Vanheusden K, Fleetwood DM, Schwank JR, Shaneyfelt MR, Winokur PS, Devine RAB:

    IEEE Tran Nuclear Science. 1996, 43:2617. Publisher Full Text OpenURL

  35. Houssa M, Afanas'ev VV, Stesmans A, Heyns MM:

    Appl Phys Lett. 2000, 77:1885. Publisher Full Text OpenURL

  36. Zhang JF, Zhao CZ, Groeseneken G, Degraeve R, Ellis JN, Beech CD:

    J Appl Phys. 2001, 90:1911. Publisher Full Text OpenURL

  37. Zhao CZ, Zhang JF, Chang MH, Peaker AR, Hall S, Groeseneken G, Pantisano L, De Gendt S, Heyns M:

    J Appl Phys. 2008, 103:014507. Publisher Full Text OpenURL

  38. Taechakumput P, Zhao CZ, Taylor S, Werner M, Chalker PR, Gaskell JM, Jones AC, Drobnis M:

    In "Origin of Frequency Dispersion in High-k Dielectrics", Semiconductor Technology Conference (ISTC2008), Proceeding of the 7th International Conference on Semiconductor Technology. Edited by Ming Yang. 2008, 20-26.

    ISBN 978-988-17408-1-6

    OpenURL

  39. Kohlrausch F:

    Pogg Ann Phys. 1863, 119:352. OpenURL

  40. Williams G, Watts DC:

    Trans Faraday Soc. 1970, 66:80. Publisher Full Text OpenURL

  41. Alvarez F, Alegria A, Colmenero J:

    Phys Rev B. 1991, 44:7306. Publisher Full Text OpenURL

  42. Bello A, Laredo E, Grimau M:

    Phys Rev B. 1999, 60:12764. Publisher Full Text OpenURL

  43. Bokov AA, Mahesh Kumar M, Xu Z, Ye Z-G:

    Phys Rev B. 2001, 64:224101. Publisher Full Text OpenURL

  44. Jonscher AK: Universal Relaxation Law–A sequel to Dielectric Relaxation in Solids. Chelsea Dielectrics Press, London; 1996. OpenURL

  45. Dissado LA, Hill RM:

    Nature. 1979, 279:685. Publisher Full Text OpenURL

  46. Hunt A:

    J Non-Crystalline Solids. 1995, 183:109. Publisher Full Text OpenURL

  47. Waser R, Klee M:

    Inter Ferro. 1992, 2:257. OpenURL

  48. Scher H, Montroll EW:

    Phys Rev B. 1975, 12:2455. Publisher Full Text OpenURL

  49. Wolters SR, Van Der Schoot JJ:

    J Appl Phys. 1985, 58:831. Publisher Full Text OpenURL

  50. Reisinger H, Steinlesberger G, Jakschik S, Gutsche M, Hecht T, Leonhard M, Schroder U, Seidl H, Schumann D:

    Tech Dig –Int Electron Devices Meet. 2001, 267. OpenURL

  51. Yu H, Liu H, Hao H, Guo L, Jin C, Yu Z, Cao M:

    Appl Phys Lett. 2007, 91:222911. Publisher Full Text OpenURL

  52. Sivakumar N, Narayanasamy A, Chinnasamy CN, Jeyadevan B:

    J Phys: Condens Matter. 2007, 19:386201. Publisher Full Text OpenURL