Band alignment and enhanced breakdown field of simultaneously oxidized and nitrided Zr film on Si

Yew Hoong Wong and Kuan Yew Cheong*

Author Affiliations

Energy Efficient and Sustainable Semiconductor Research Group, School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, Engineering Campus, 14300 Nibong Tebal, Seberang Perai Selatan, Penang, Malaysia

For all author emails, please log on.

Nanoscale Research Letters 2011, 6:489  doi:10.1186/1556-276X-6-489


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/6/1/489


Received:11 April 2011
Accepted:10 August 2011
Published:10 August 2011

© 2011 Wong and Cheong; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

The band alignment of ZrO2/interfacial layer/Si structure fabricated by simultaneous oxidation and nitridation of sputtered Zr on Si in N2O at 700°C for different durations has been established by using X-ray photoelectron spectroscopy. Valence band offset of ZrO2/Si was found to be 4.75 eV, while the highest corresponding conduction offset of ZrO2/interfacial layer was found to be 3.40 eV; owing to the combination of relatively larger bandgaps, it enhanced electrical breakdown field to 13.6 MV/cm at 10-6 A/cm2.

Keywords:
oxidation; sputtered-Zr; nitrous oxide; band alignment; electrical breakdown field

Background

Application of high dielectric constant (κ) materials as future gate dielectrics on Si-based metal oxide semiconductor (MOS) devices has driven a tremendous research to realize an ultra-large-scale integrated circuitry with high performance and low power consumption [1-3]. Of various investigated high κ materials, ZrO2 is being considered as a potential gate dielectric for the near future generation technology nodes. It has been reported that excellent electrical properties of MOS capacitors that incorporated ZrO2 thin film as gate dielectric [4,5]. Putkonen et al. [5] and Niinisto et al. [4] have obtained the breakdown fields of ZrO2 at 6.0 and 9.5 MV/cm, respectively, at leakage current density of 10-2 A/cm2. In order to attain excellent electrical properties of a device, interface properties of dielectric/Si play an indispensable role [6,7]. The leakage characteristic and electrical breakdown field of gate dielectric are basically dependent on the bandgap of the dielectric and on the band alignment with Si [8,9]. Hence, to use ZrO2 as gate dielectric in MOS capacitors, it should have sufficiently high band offsets with Si (> 1.00 eV) for both holes (valence band offset) and electrons (conduction band offset), so that an ultralow leakage current can be acquired [2,3]. Therefore, it is crucial to quantify these energy band offsets. Additionally, it is necessary to consider an interfacial layer (IL) that is inevitably formed in between ZrO2 and Si in the evaluation of band alignment. Works along this direction were reported by a number of researchers (Table 1). It is summarized that band alignment of the ZrO2/IL/Si system can be categorized into two types, depending on the oxide deposition techniques rather than the types (n or p) of semiconductor: type (i), alignment of ZrO2 bandgap in between the IL bandgap [10-13] and type (ii), alignment of ZrO2 conduction band outside the IL bandgap [14]. In this work, using simultaneous oxidation and nitridation of sputtered Zr on n-type Si in N2O, alignment of ZrO2 valence band outside the IL bandgap has been revealed [type (iii) in Table 1] (Figure 1). Owing to this type of alignment, dielectric electric breakdown field at low leakage current density has been enhanced.

Table 1. Comparison of the obtained values of Eg(ZrO2), Eg(IL), ΔEv, and ΔEc

thumbnailFigure 1. Band alignment of ZrO2/IL/Si system. Eg(ZrO2) = bandgap of ZrO2, Eg(IL) = bandgap of IL, Eg(Si) = bandgap of Si, ΔEv(ZrO2/Si) = valence band offsets of ZrO2 to Si, ΔEv(IL/Si) = valence band offsets of IL to Si, ΔEc(ZrO2/Si) = conduction band offset of ZrO2 to Si, ΔEc(IL/Si) = conduction band offset of IL to Si, ΔEc(ZrO2/IL) = conduction band offset of ZrO2 to IL.

Results and discussion

Figure 2a shows typical X-ray photoelectron spectroscopy (XPS) valence band spectra of ZrO2 and IL for all investigated samples. The valence band edges (Ev) of ZrO2 and IL were estimated by an intercept of linear extrapolation of a maximum negative slope near the edge to the minimum horizontal baseline [10]. As a result, valence band offsets (ΔEv) of ZrO2 and IL with respect to Si substrate were 4.75 ± 0.05 eV and 3.75 ± 0.05 eV, respectively, for all investigated samples. To determine conduction band offset (ΔEc) of ZrO2/IL/Si system, the bandgaps (Eg) of ZrO2 and IL were first deduced from O 1s plasmon loss spectra [15,16] of ZrO2 and IL, respectively. Figure 2b representatively demonstrates the XPS O 1s plasmon loss spectra of ZrO2 and IL for a 15-min sample. Whilst for other samples, the Eg values of ZrO2 and IL extracted from their respective O 1s plasmon loss spectra are shown in Figure 3. As explained earlier, values of Eg were also approximated by an intercept of linear extrapolation. The extracted Eg values of ZrO2 and IL were 6.20 to 6.50 eV and 8.20 to 8.80 eV, respectively, with tolerance of 0.05 eV, dependent on the oxidation time (Figure 3). Ultimately, conduction band offset of ZrO2 to IL, ΔEc(ZrO2/IL) for the ZrO2/IL/Si system can be eventually derived [17]:

thumbnailFigure 2. XPS valence band spectra of ZrO2 and IL for all investigated samples. (a) XPS valence band spectra of ZrO2 and IL for all investigated samples. (b) XPS O 1s plasmon loss spectra of ZrO2 and IL for 15-min sample.

thumbnailFigure 3. Eg values of ZrO2 and IL extracted from their respective O 1s plasmon loss spectra. The calculated values of Eg(ZrO2), Eg(IL), ΔEc(ZrO2/Si), ΔEc(IL/Si), and ΔEc(ZrO2/IL) in the band alignment of ZrO2/IL/Si system.

(1)

where, Eg(ZrO2) and Eg(IL) are the bandgaps of ZrO2 and IL, respectively. ΔEv(ZrO2/Si) and ΔEv(IL/Si) are the valence band offsets of ZrO2 and IL, respectively, with respect to Si substrate. The calculated values of Eg(ZrO2), Eg(IL), ΔEc(ZrO2/Si), ΔEc(IL/Si), and ΔEc(ZrO2/IL) are presented in Figure 3. The highest value of ΔEc(ZrO2/IL), i.e., 3.40 eV, was attained by sample oxidized/nitrided for 15 min (Figure 3) when compared to other samples. A schematic of the band alignment of the ZrO2/IL/Si system is illustrated in Figure 1. The Eg value of Si substrate is obtained from literature [3,18]. It is found that values of Eg(ZrO2), Eg(IL), ΔEc, and ΔEv obtained in this study are higher than the values reported in literatures (Table 1).

Figure 4 shows typical leakage current density electric field (J-E) characteristics of the investigated samples. The J-E plot was transformed from current-voltage (I-V) measurement. The E value was estimated by first determining the flatband voltage (VFB) shift from the applied gate voltage (Vg) and then dividing the total thicknesses of ZrO2 and IL (tox) measured by energy filtered transmission electron microscopy (EFTEM) (images are not shown here). The acquired J value in this study is ~10-8A/cm2 at E = 2.0 MV/cm, which is lower than the other studies [4,5,14].

thumbnailFigure 4. J-E characteristics of the investigated Al/ZrO2/IL/Si MOS capacitors. Inset shows the average breakdown fields (BK-1 and BK-2) for the investigated samples.

A two-step oxide breakdown (BK-1 and BK-2) is being recorded in the J-E plot for all investigated samples (inset of Figure 4). The existence of interfacial and ZrO2 layers in the sample is the main cause of this two-step breakdown [19]. The breakdowns can be explained as follows. One of the layers may experience an electrical breakdown at a lower field, which is labeled as BK-1. Subsequently, another layer would block the carriers. Due to the increment of the electric field, the concentration of the carrier increases until the layer is electrically broken down at a higher electric field at BK-2. The instantaneous increment of leakage current density at BK-1 is relatively small when compared with others, and it is defined as soft breakdown. The magnitude of BK-1 increases gradually as the oxidation time is increased (inset of Figure 4). In contrast, the instantaneous increment of current density at BK-2 is large, and this is considered as hard breakdown. The highest dielectric breakdown field, which is referred to as hard breakdown, is attained by sample oxidized/nitride for 15 min (13.6 MV/cm at 10-6 A/cm2). The lowest one is recorded by sample oxidized/nitride for 10 min (4.8 MV/cm at 10-6 A/cm2). In comparison, dielectric breakdown field recorded in this work is higher than the previous reported works [4,5,14].

Conclusions

In summary, the band alignment of ZrO2/IL/Si structure produced by simultaneous oxidation and nitridation of sputtered Zr thin film on Si in N2O has been established. Via this method, higher ΔEc and ΔEv values have been attained. Hence, a higher electrical breakdown field at low leakage current density has been achieved.

Methods

The n-type Si(100) substrate with a resistivity of 1 to 10 Ω cm was used in this study. After undergoing a standard wafers cleaning process, a 5-nm thick Zr film was sputtered on the cleaned Si substrates by an RF sputtering system. Following that, samples were loaded into a horizontal tube furnace and were heated up from room temperature to 700°C in an Ar flow ambient, and the heating rate was fixed at 10°C/min. Once the set temperature was achieved, N2O gas was introduced with a flow rate of 150 mL/min for a set of durations (5, 10, 15, and 20 min). After the furnace was cooled down to room temperature in an Ar ambient, the samples were withdrawn from the furnace. To experimentally determine band alignment of the dielectric/semiconductor structure, XPS measurements were conducted using Kratos Axis Ultra DLD (Kratos Analytical, Chestnut Ridge, NY, USA). with a monochromatic Al-Kα X-ray source (hν = 1,486.69 eV) performed at the Research Center for Surface and Materials Science, The Auckland University, New Zealand. The spectra of survey or wide scan (binding energy of -5 to 25 eV) were collected at a take off angle of 0° with respect to surface normal, with low pass energy of 20 eV and small step size of 0.1 eV. Due to the onset of single particle excitation and band-to-band transition, the energy loss spectrum of O 1s photoelectron provides further insight on the bandgaps of ZrO2 and IL [20]. Subsequently, a detail scan of O 1s was carried out using the same pass energy and step size of 1.0 eV. Ar ion gun (5 keV) was employed to etch the sample in order to perform chemical depth profiling (results are not shown here), in order for the boundary of ZrO2 and IL to be identified. A Shirley background function, which is proportional to the integrated photoelectron peak area, was subtracted from all of the XPS spectra to correct for the inelastic photoelectron scattering effect [21]. Band alignment extraction was based on Kraut method [15,16]. As to characterize the leakage characteristic and electrical breakdown field of the film, MOS capacitor test structure was formed by thermally evaporated a 100-nm thick aluminum (Al) film, acting as a gate electrode, on top of the films. The area of a capacitor was photolithographically defined at 9 × 10-4 cm2. In order to obtain an Ohmic back contact, a 100-nm thick Al film was thermally evaporated on the backside of the Si substrate after removal of native oxide. I-V measurements were performed by a computer-controlled Agilent HP4155-6C semiconductor parameter analyzer (Agilent Technologies, Santa Clara, CA, USA).

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

YHW has been involved in the experimental design, data acquisition, data interpretation and analysis, and drafting and revision of the manuscript. KYC has been involved in revising the manuscript critically for important intellectual content and has given final approval to the version to be submitted for publication.

Acknowledgements

The authors would like to acknowledge the support provided by USM fellowship, USM-RU-PRGS (8032051), and The Academy of Sciences for the Developing World (TWAS) through the TWAS-COMSTECH research grant (09-105 RG/ENG/AS_C) during the study.

References

  1. Robertson J: High dielectric constant oxides.

    Eur Phys J Appl Phys 2004, 28:265-291. Publisher Full Text OpenURL

  2. Wilk GD, Wallace RM, Anthony JM: High-k gate dielectrics: current status and materials properties considerations.

    J Appl Phys 2001, 89:5243-5275. Publisher Full Text OpenURL

  3. Wong YH, Cheong KY: ZrO2 thin films on Si substrate.

    J Mater Sci: Mater Electron 2010, 21:980-993. Publisher Full Text OpenURL

  4. Niinisto J, Putkonen M, Niinisto L, Kukli K, Ritala M, Leskela M: Structural and dielectric properties of thin ZrO2 films on silicon grown by atomic layer deposition from cyclopentadienyl precursor.

    J Appl Phys 2004, 95:84-91. Publisher Full Text OpenURL

  5. Putkonen M, Niinistö J, Kukli K, Sajavaara T, Karppinen M, Yamauchi H, Niinistö L: ZrO2 thin films grown on silicon substrates by atomic layer deposition with Cp2Zr(CH3)2 and water as precursors.

    Chem Vap Dep 2003, 9:207-212. Publisher Full Text OpenURL

  6. Aygun G, Yildiz I: Interfacial and structural properties of sputtered HfO2 layers.

    J Appl Phys 2009, 106:014312-014317. Publisher Full Text OpenURL

  7. Weinreich W, Ignatova VA, Wilde L, Teichert S, Lemberger M, Bauer AJ, Reiche R, Erben E, Heitmann J, Oberbeck L, Schroder U: Influence of N2 and NH3 annealing on the nitrogen incorporation and k-value of thin ZrO2 layers.

    J Appl Phys 2009, 106:034107-034107. Publisher Full Text OpenURL

  8. Chen Q, Feng YP, Chai JW, Zhang Z, Pan JS, Wang SJ: Band alignment and thermal stability of HfO2 gate dielectric on SiC.

    Appl Phys Lett 2008, 93:052104-052103. Publisher Full Text OpenURL

  9. Yim CJ, Ko DH, Jang MH, Chung KB, Cho MH, Jeon HT: Change in band alignment of HfO2 films with annealing treatments.

    Appl Phys Lett 2008, 92:012922-012923. Publisher Full Text OpenURL

  10. Miyazaki S: Characterization of high-k gate dielectric/silicon interfaces.

    Appl Surf Sci 2002, 190:66-74. Publisher Full Text OpenURL

  11. Houssa M, Tuominen M, Naili M, Afanas'ev V, Stesmans A, Haukka S, Heyns MM: Trap-assisted tunneling in high permittivity gate dielectric stacks.

    J Appl Phys 2000, 87:8615-8620. Publisher Full Text OpenURL

  12. Afanas'ev VV, Houssa M, Stesmans A, Heyns MM: Band alignments in metal-oxide-silicon structures with atomic-layer deposited Al2O3 and ZrO2.

    J Appl Phys 2002, 91:3079-3084. Publisher Full Text OpenURL

  13. Fulton CC, Cook JTE, Lucovsky G, Nemanich RJ: Interface instabilities and electronic properties of ZrO2 on silicon (100).

    J Appl Phys 2004, 96:2665-2673. Publisher Full Text OpenURL

  14. Yamaguchi T, Satake H, Fukushima N: Band diagram and carrier conduction mechanisms in ZrO2 MIS structures.

    IEEE Trans on Electron Devices 2004, 51:774-779. Publisher Full Text OpenURL

  15. Kraut EA, Grant RW, Waldrop JR, Kowalczyk SP: Precise determination of the valence band edge in x-ray photoemission spectra: application to measurement of semiconductor interface potentials.

    Phys Rev Lett 1980, 44:1620. Publisher Full Text OpenURL

  16. Kraut EA, Grant RW, Waldrop JR, Kowalczyk SP: Semiconductor core-level to valence band maximum binding-energy differences: precise determination by x-ray photoelectron spectroscopy.

    Phys Rev B 1983, 28:1965. Publisher Full Text OpenURL

  17. Zhu LQ, Zhang LD, Li GH, He G, Liu M, Fang Q: Thermal stability and energy-band alignment of nitrogen-incorporated ZrO2 films on Si(100).

    Appl Phys Lett 2006, 88:232901-232903. Publisher Full Text OpenURL

  18. Muller RS, Kamins TI:

    Device Electronics for Integrated Circuits. 2nd edition. 1986, 54. OpenURL

  19. Xiaolong Y, Qianghua X, Tao M: Electrical breakdown in a two-layer dielectric in the MOS structure.

    Mat Res Soc Symp Proc 2004, 811:D2.8.1. OpenURL

  20. Miyazaki S, Nishimura H, Fukuda M, Ley L, Ristein J: Structure and electronic states of ultrathin SiO2 thermally grown on Si(100) and Si(111) surfaces.

    Appl Surf Sci 1997, 113-114:585-589. OpenURL

  21. Shirley DA: High-resolution x-ray photoemission spectrum of the valence bands of gold.

    Phys Rev B 1972, 5:4709. Publisher Full Text OpenURL