Photo-catalytic activity of Zn1-x Mn x S nanocrystals synthesized by wet chemical technique

Mansi Chitkara1, Karamjit Singh2*, Inderjeet Singh Sandhu1 and Harbhajan Singh Bhatti2

Author Affiliations

1 Nanomaterials Research Laboratory (NRL), Department of Applied Sciences, Chitkara University, Rajpura, Punjab 140 401, India

2 Department of Physics, Punjabi University, Patiala, Punjab 147 002, India

For all author emails, please log on.

Nanoscale Research Letters 2011, 6:438  doi:10.1186/1556-276X-6-438


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/6/1/438


Received:23 April 2010
Accepted:24 June 2011
Published:24 June 2011

© 2011 Chitkara et al; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Polyvinyl pyrrolidone capped Zn1-xMnxS (0 ≤ x ≤ 0.1) nanocrystals have been synthesized using wet chemical co-precipitation method. Crystallographic and morphological characterization of the synthesized materials have been done using X-ray diffraction and transmission electron microscope. Crystallographic studies show the zinc blende crystals having average crystallite size approx. 3 nm, which is almost similar to the average particle size calculated from electron micrographs. Atomic absorption spectrometer has been used for qualitative and quantitative analysis of synthesized nanomaterials. Photo-catalytic activity has been studied using methylene blue dye as a test contaminant. Energy resolved luminescence spectra have been recorded for the detailed description of radiative and non-radiative recombination mechanisms. Photo-catalytic activity dependence on dopant concentration and luminescence quantum yield has been studied in detail.

Introduction

Environmental pollution, toxic water pollutants, and industrialization on a global scale have drawn attention for sustained fundamental and applied research in the area of environmental remediation. The increased public concern with environmental pollutants has prompted the need to develop novel treatment methods [1] where photo-catalysis is gaining a lot of attention in the field of pollutant degradation. Semiconductor photo-catalysts offer the potential for complete elimination of toxic chemicals through their efficiency and potentially broad applicability [2,3]. Recently, semiconductor nanocrystals have attracted great attention due to their size tunable physical and chemical properties. Transition from bulk to nanoparticles lead to the display of quantum mechanical properties and an increased dominance of surface atoms, which give rise to unique photo-physical and photo-catalytic properties of nanomaterials, for example, with the decrease of particle size, extremely high surface to volume ratio is obtained leading to an increase in surface specific active sites for chemical reactions and photon absorption to enhance the reaction and absorption efficiency. The enhanced surface to volume ratio causes increase of surface states, which changes the activity of electrons and holes, affecting the chemical reaction dynamics. The size quantization increases the bandgap of photo-catalysts to enhance the redox potential of conduction band electrons and valence band holes [4].

Various new compounds and materials for photo-catalysis have been synthesized in the past few decades [5-13]. Semiconductor photo-catalysts, with a primary focus on TiO2 [14-17], have been applied to variety of problems of environmental interest in addition to water and air purification. The application of illuminated semiconductors for degrading undesirable organics dissolved in air or water is well documented and has been successful for a wide variety of compounds [2]. Transition-metal sulphides, in particular ZnS [18,19], have unique catalytic functions as a result of the rapid generation of electron-hole pairs by photo-excitation and the highly negative reduction potentials of excited electrons. Moreover, incorporation of metal ion dopants in these semiconductor nanoparticles can influence their photo-catalytic performance. Doping of Mn2+ ions in ZnS lengthens the lifetime of generated charge carriers, resulting in an enhancement in the photo-activity. Hence, ZnS:Mn2+ nanocrystals can be efficiently used for environmental cleaning, H2 production, and water purification. This article reports photo-catalytic activity of Zn1-xMnxS nanocrystals. Photo-catalytic activity has been well correlated with the luminescence quantum yield. Moreover, photo-catalytic and luminescence efficiency dependence on the Mn2+ concentration have been described in detail.

Experimental

Zn1-xMnxS (0 ≤ x ≤ 0.1) nanocrystals have been synthesized using wet chemical co-precipitation method already opted by Singh et al. [20] for the synthesis of Eu3+ doped Cd1-xZnxS quantum dots. All synthesis was carried out at room temperature under ambient conditions in aqueous media for its inherent advantages of being simple and environmental friendly. Analytical reagent grade chemicals: zinc acetate (C4H6O4Zn · 2H2O), manganese acetate (C4H6MnO4 · 4H2O), sodium sulphide (Na2S · H2O), and polyvinyl pyrrolidone (PVP) [(C6H9NO)n] were used without further purification. Solutions of 0.5 M zinc acetate, 0.5 M sodium sulphide, and 1 M manganese acetate were prepared in separate beakers. Then zinc and manganese precursor solutions were mixed in the stoichiometric proportion under vigorous stirring, 4 ml of 2% PVP solution was added to total 50 ml volume, before drop wise addition of sulfur precursor. PVP will act as the capping agent to avoid the agglomeration of nanocrystals. The resulting precipitates were centrifuged and dried in vacuum oven for 10 to 12 h continuously.

Panalytical's (Netherlands) X'Pert Pro Powder X-ray diffractometer with Cu Kα radiation (λ = 1.541 Å) was used to record diffraction patterns of the synthesized samples in the 2θ range 20 to 60°. Average crystallite size has been calculated from the line broadening of the X-ray diffraction (XRD) diffractogram using Scherrer formula [21]. Hitachi, [(H-7500), Japan] transmission electron microscope (TEM) was used to record micrographs for average particle size determination. For TEM studies, a drop of well ultrasonicated ethanol dispersed nanocrystals was placed on the carbon coated copper grid.

Atomic absorption spectrometer (Analytic Jena, Germany) has been used for qualitative and quantitative analysis of the synthesized nanomaterials. Sample preparation for the analysis involves dissolution of 0.01 mg of nanocrystals in 10 ml of 0.5% HNO3.

Energy resolved luminescence spectra were recorded using FlouroMax-3 (Jobin-Yvon, Edison, NJ, USA) spectrofluorometer equipped with photomultiplier tube and a xenon lamp.

The photo-catalytic activity of Zn1-xMnxS nanocrystals was studied by monitoring the degradation of methylene blue (MB) (C16H18ClN3S · 2H2O) dye in an aqueous suspension containing Zn1-xMnxS nanocrystals under the UV-radiation exposure with continuous magnetic stirring. A 350 ml of aqueous suspension was prepared by completely dissolving 1.1322 mg of the MB dye and then dispersing 140 mg of the Zn1-xMnxS nanocrystals in the de-ionized water. The resulting suspension was equilibrated by stirring in the dark for 1 h to stabilize the adsorption of MB dye on the surface of nanocrystals. The stable aqueous suspension was then exposed to the UV-radiation with continuous magnetic stirring, using the home made photoreactor containing two 18-W tubes as the UV-source (λ = 200 to 400 nm). Following the UV-radiation exposure, 10 ml sample of aqueous suspension was taken out after every 10-min interval for the total 80 min of the UV-radiation exposure. Suspension sample was centrifuged to filter out the Zn1-xMnxS nanocrystals, then nanocrystal free aqueous dye solution was examined using UV-vis absorption spectrophotometer (Systronics PC Based Double Beam Spectrophotometer:2202) to study the photo-degradation of the MB dye.

Results and discussion

Broad XRD patterns have been recorded for all the synthesized Zn1-xMnxS samples, Figure 1 shows one such X-ray diffractogram recorded for Zn0.9900Mn0.0100S. It is clear from the diffractogram that synthesized samples crystallize in zinc blende structure with the planes at {111}, {220}, and {311}, respectively. Recorded diffraction peaks are broadened due to the nanocrystalline nature of particles. Average crystallite size calculated from the recorded XRD patterns is approx. 3 nm.

thumbnailFigure 1. XRD pattern of Zn0.9900Mn0.0100S nanocrystals.

Figure 2 shows the TEM micrograph recorded for Zn1-xMnxS nanocrystals. Average particle size calculated from micrograph is approx. 3 to 4 nm, which is in proximity to the average crystallite size determined by XRD. So, all the synthesized particles are single nanocrystals.

thumbnailFigure 2. TEM image of Zn1-xMnxS nanocrystals.

Atomic absorption spectrometer (AAS) studies show that the actual concentration of manganese doping is approx. 24% of the initial manganese precursor concentration, which was added to the reaction media. So, the value of x in Zn1-xMnxS corresponds to initial atomic weight concentration of manganese with respect to zinc, which was calculated during stochiometric addition of precursors in the chemical co-precipitation reaction.

Figure 3 shows absorption spectra of synthesized nanocrystals, which lie in UV range. Energy resolved luminescence spectra shown in Figure 4 have been recorded at room temperature using 325-nm excitation. It is clear from the recorded spectrum that pure ZnS nanocrystals show only 425-nm emission peak, whereas dichromatic emission (λ1 = 425 nm and λ2 = 599 nm) has been observed in case of Mn2+-doped ZnS nanocrystals. Luminescence quantum yield of λ2 emission peak go on increasing with the increase of 'x' in Zn1-xMnxS nanocrystals, whereas λ1 emission intensity go on decreasing with increasing concentration of Mn2+ ions. More than six-fold increase and two-fold decrease has been observed in the emission intensities of λ2 and λ1 peaks, respectively, when the value of 'x' changes from 0.01 to 0.1 in Zn1-xMnxS nanocrystals. The Mn2+ ions substitute the Zn2+ ions in the ZnS nanocrystal acting as trap sites [22], where the electrons and holes can be trapped. Electrons after photo-excitation process in the host lattice subsequently decay via non-radiative process to the 4T1 localized state of manganese. The λ2 (599 nm) emission peak is attributed to the radiative decay between the 4T1 and 6A1 localized states of manganese inside the ZnS bandgap. The λ1 emission (425 nm) peak is assigned to the radiative transition of electrons from shallow trap states (ST) near the conduction band to sulfur vacancies (Vs) residing near the valence band. The increasing dopant concentration quenches the host related 425 nm emission. Detailed mechanism of various processes involved in Zn1-xMnxS nanocrystals upon excitation is shown in Figure 5. Photo-excited electrons from the conduction band transit spontaneously to the ST and 4T1 manganese trap sites via non-radiative processes. These ST electrons can recombine radiatively with Vs holes or further relaxed non-radiatively to the localized dopant trapping states. Radiative recombination of ST electrons and Vs holes is faster than the radiative transition between the 4T1 and 6A1 localized states [23].

thumbnailFigure 3. Absorption spectra of nanocrystals.

thumbnailFigure 4. Photoluminescence spectra of Zn1-xMnxS nanocrystals.

thumbnailFigure 5. Processes involved in Zn1-xMnxS nanocrystals upon excitation. CB, conduction band; ST, shallow trap; 4T1 and 6A1, manganese levels; VB, valence band; Vs, sulfur vacancy.

Figure 6 shows absorption spectra of pure MB dye with and without UV radiation exposure. It can be clearly seen from the recorded spectra that both the curves overlap on each other, which confirms that there is no photo-bleaching of pure MB dye.

thumbnailFigure 6. Absorption spectra of pure MB dye.

Figure 7 shows the Zn1-xMnxS (0 ≤ x ≤ 0.1) nanocrystals sensitized photo-degradation of MB dye under UV-radiation exposure. It can be clearly seen that MB dye is degraded to maximum extent in case of Zn0.9900Mn0.0100S nanocrystals, whereas it is degraded to minimum extent for Zn0.9000Mn0.1000S nanophoto-catalyst. Photoredox chemistry occurring at nanocrystal surface emanates from trapped charge carriers. Incorporation of Mn2+ in ZnS nanocrystal lattice significantly influences the photo-catalytic activity. Addition of Mn2+ ions lengthens the lifetime of excited charge carriers, which results the enhanced photo-catalytic activity. Various charge carrier recombination and charge carrier trapping processes are shown in Figure 5. The competition between the charge carrier recombination and charge carrier trapping followed by the competition between recombination of trapped carriers and interfacial charge transfer determine the overall quantum efficiency for interfacial charge transfer. Doping of Mn2+ up to optimal concentration increases the interfacial charge transfer probability, due to which photo-catalytic activity of ZnS nanocrystals is enhanced. As shown in Figure 7, photo-catalytic activity enhances with increasing value of 'x' only in the range x = 0 to x = 0.01, further increase of dopant concentration, i.e., x = 0.01 to x = 0.1 deteriorates photo-catalytic activity of Zn1-xMnxS nanocrystals. It is due to the fact that up to optimal Mn2+ concentration (x = 0.01), Mn2+ ions lengthens the charge carrier recombination, but at higher dopant concentrations although the possibility of charge carrier trapping is high, but the charge carriers may recombine through quantum tunneling. Moreover, increasing concentration of Mn2+ ions may cause the increased interaction between neighboring Zn2+ ions and the Mn2+ luminescence centre that enhances the spin-orbit coupling of Mn2+ ions, which leads to the relaxation of the spin selection rules [24]. This lowers the radiative recombination time for 4T1 6A1 transitions, so the recombination of trapped carriers dominates interfacial charge transfer at the higher dopant concentrations. Due to enhanced recombination rate luminescence quantum yield increases to large extent as shown in Figure 4. Figure 8 shows the absorption spectrum of MB dye solution for different durations of UV-radiation exposure in the presence of Zn0.9900Mn0.0100S nanocrystals (optimal dopant concentration). Zn0.9900Mn0.0100S nanocrystal photo-catalyst is efficiently degrading the dye, only negligible amount of dye is present in the solution after 80 min. There is a concentration dependent slight spectral shift in MB dye absorption spectra as the UV irradiation time changes from 0 to 80 min. Red shift in the absorption peak with increasing dye concentration has been observed due to augmented optical density. Moreover, at higher concentrations, aggregation can take place, which affects the optical behaviour. These non-toxic, stable, inexpensive nanocrystalline photo-catalyst having high-redox potentials can be efficiently used for environmental cleaning, water purification, and H2 production. Moreover, due to non-dissolving nature in aqueous media, these photo-catalysts can be easily recovered after use.

thumbnailFigure 7. Photodegradation of MB dye with time.

thumbnailFigure 8. Absorption spectrum of dye solution for different durations of UV-radiation exposure in the presence of Zn0.9900Mn0.0100S nanocrystals.

Conclusions

Zn1-xMnxS (0 ≤ x ≤ 0.1) nanocrystals have been successfully synthesized in aqueous media using a simple wet chemical precipitation technique. Crystallographic and morphological studies reveal the zinc blende nanostructures having average crystallite size approx. 3 nm. Energy resolved luminescence spectra report the quenching of host-related 425 nm emission and enhancement in luminescence quantum yield of dopant-related 599 nm emission, with the increasing concentration of Mn2+ ions. Photo-catalytic activity of nanocrystals studied using MB dye as a test contaminant enhances with the addition of Mn2+ ions in ZnS nanocrystals upto to optimal concentration (1 at. wt% of Zn2+), but the further increase of dopant concentration deteriorates photo-catalytic activity of Zn1-xMnxS nanocrystals as the recombination of trapped carriers dominates the interfacial charge transfer at the higher dopant concentrations. This mechanistic information of photo-catalytic activity dependence on dopant concentration and luminescence quantum yield will significantly contribute to enhance the understanding of photo-initiated processes in semiconductor nanocrystals.

Abbreviations

AAS: atomic absorption spectrometer; CB: conduction band; MB: methylene blue; PVP: polyvinyl pyrrolidone; ST: shallow trap; TEM: transmission electron microscope; VB: valence band; XRD: X-ray diffraction.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

MC: Performed experimental work. KS: Generated scientific idea, performed experimental work with first author and written the manuscript. ISS: Supported and participated in the technical work. HSB: Steer for generation of scientific idea and manuscript design.

Acknowledgements

Authors express their gratitude to Dr. Shyam Kumar, Chairman, Department of Physics, Kurukshetra University, Kurukshetra and Dr. Sanjiv Aggarwal, Reader, Department of Physics, Kurukshetra University, Kurukshetra for energy resolved spectroscopic studies. Regional Scientific Instruments Centre (RSIC), Punjab University, Chandigarh is gratefully acknowledged for crystallographic and morphological studies.

References

  1. Zeltner WA, Anderson MA: The use of nanoparticles in environmental applications. In Fine Particles Science and Technology. Edited by Pelizzetti E. Dordrecht: Kluwer Academic Publishers; 1996:643. OpenURL

  2. Hoffmann MR, Martin ST, Choi W, Bahnemann DW: Environmental applications of semiconductor photocatalysis.

    Chem Rev 1995, 95:69. Publisher Full Text OpenURL

  3. Anpo M, Takeuchi M: The design and development of highly reactive titanium oxide photocatalysts operating under visible light irradiation.

    J Catal 2003, 216:505. Publisher Full Text OpenURL

  4. Hoffmann AJ, Mills G, Yee H, Hoffmann MR: Q-sized cadmium sulphide: synthesis, characterization and efficiency of photoinitation of polymerization of several vinyl monomers.

    J Phys Chem 1992, 96:5546. Publisher Full Text OpenURL

  5. Anpo M, Shima T, Kodama S, Kubokawa Y: Photocatalytic hydrogenation of CH3CCH with H2O on small particle TiO2: Size quantization effects and reaction intermediates.

    J Phys Chem 1987, 91:4305. Publisher Full Text OpenURL

  6. Choi W, Termin A, Hoffmann MR: The role of metal ion dopants in quantum sized TiO2: correlation between photoreactivity and charge carrier recombination dynamics.

    J Phys Chem 1994, 98:13669. Publisher Full Text OpenURL

  7. Kanemoto M, Hosokawa H, Wada Y, Murakoshi K, Yanagida S, Sakata T, Mori H, Ishikawa M, Kobayashi H: Semiconductor photocatalysis. Part 20-Role of surface in the photoreduction of carbon dioxide catalysed by colloidal ZnS nanocrystallites in organic solvent.

    J Chem Soc Faraday Trans 1996, 92:2401. Publisher Full Text OpenURL

  8. Claudia L, Martinez T, Kho R, Mian OI, Mehra RK: Efficient photocatalytic degradation of environmental pollutants with mass-produed ZnS nanocrystals.

    J Colloid Interface Sci 2001, 240:525. PubMed Abstract | Publisher Full Text OpenURL

  9. Hu JS, Ren LL, Guo TG, Liang HP, Cao AM, Wan LJ, Bai CL: Mass production and high photocatalytic activity of ZnS nanoporous nanoparticles.

    Angew Chem Int Ed 2005, 44:1269. Publisher Full Text OpenURL

  10. Janet CM, Viswanath RP: Large scale synthesis of CdS nanorods and its utilization in photo-catalytic H2 production.

    Nanotechnology 2006, 17:5271. Publisher Full Text OpenURL

  11. Zheng Y, Chen C, Zhan Y, Lin X, Zheng Q, Wei K, Zhu J, Zhu Y: Luminescence and photocatalytic activity of ZnO nanocrystals: correlation between structure and property.

    Inorg Chem 2007, 46:6675. PubMed Abstract | Publisher Full Text OpenURL

  12. Bang JH, Helmich RJ, Suslick KS: Nanostructured ZnS:Ni2+ photocatalyst prepared by ultrasonic spray pyrolysis.

    Adv Mater 2008, 20:2599. Publisher Full Text OpenURL

  13. Ma LL, Sun HZ, Zhang YG, Lin YL, Li JL, Wang EK, Yu Y, Tan M, Wang JB: Preparation, characterization and photocatalytic properties of CdS nanoparticles dotted on the surface of carbon nanotubes.

    Nanotechnology 2008, 19:115709. PubMed Abstract | Publisher Full Text OpenURL

  14. Kormann C, Bahnemann DW, Hoffmann MR: Preparation and characterization of quantum-size titanium dioxide.

    J Phys Chem 1988, 92:5196. Publisher Full Text OpenURL

  15. Lepore GP, Langford CH, Vichova J, Vlcek A: Photochemistry and picosecond absorption spectra of aqueous suspensions of o polycrystalline titanium dioxide optically transparent in the visible spectrum.

    J Photochem Photobiol A Chem 1993, 75:67. Publisher Full Text OpenURL

  16. Wang CC, Zhang Z, Ying JY: Photocatalytic decomposition of halogenated organics over nanocrystalline titania.

    Nanostruct Mater 1997, 9:583. Publisher Full Text OpenURL

  17. Xiaodan Y, Qingyin W, Shicheng J, Yihang G: Nanoscale ZnS/TiO2 composites: Preparation, characterization and visible-light photocatalytic activity.

    Mater Charact 2006, 57:333. Publisher Full Text OpenURL

  18. Zhao Q, Xie Y, Zhang Z, Bai X: Size-selective synthesis of Zinc Sulfide hierarchical structures and their photocatalytic activity.

    Cryst Growth Des 2007, 7:153. Publisher Full Text OpenURL

  19. Stroyuk AL, Raevskaya AE, Korzhak AV, Kuchmii SY: Zinc sulfide nanoparticles: spectral properties and photocatalytic activity in metals reduction reactions.

    J Nanopart Res 2007, 9:1027. Publisher Full Text OpenURL

  20. Singh K, Kumar S, Verma NK, Bhatti HS: Photoluminescence properties of Eu3+ doped Cd1-xZnxS quantum dots.

    J Nanopart Res 2009, 11:1017. Publisher Full Text OpenURL

  21. Cullity BD: Elements of X-ray diffraction. Massachusetts: Addison-Wesley; 1978:102. OpenURL

  22. Kar S, Biswas S, Chaudhuri S, Nambissan PMG: Substitution-induced structural transformation in Mn-doped ZnS nanorods studied by positron annihilation spectroscopy.

    Nanotechnology 2007, 18:225606. Publisher Full Text OpenURL

  23. Bhatti HS, Sharma R, Verma NK, Kumar N, Vadera SR, Manzoor K: Lifetime shortening in doped ZnS nanophosphors.

    J Phys D Appl Phys 2006, 39:1754. Publisher Full Text OpenURL

  24. Bhatti HS, Singh K, Verma NK: Laser induced photoluminescence and morphological characterization of Cd(1-x)-yZnxMnyS nanocrystals.

    J Mater Sci Mater Electron 2009, 20:S255. Publisher Full Text OpenURL