Electro-synthesis of novel nanostructured PEDOT films and their application as catalyst support

Cuifeng Zhou1, Zongwen Liu1*, Yushan Yan2, Xusheng Du3*, Yiu-Wing Mai3 and Simon Ringer1

Author affiliations

1 Australian Centre for Microscopy and Microanalysis, University of Sydney, Sydney, NSW 2006, Australia

2 Department of Chemical & Environmental Engineering, University of California, 900 University Avenue, Riverside, CA, USA

3 School of Aerospace Mechanical & Mechatronic Engineering J07, University of Sydney, Sydney, NSW 2006, Australia

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2011, 6:364  doi:10.1186/1556-276X-6-364


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/6/1/364


Received:8 February 2011
Accepted:27 April 2011
Published:27 April 2011

© 2011 Zhou et al; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Poly(3,4-ethylenedioxythiophene) (PEDOT) films doped with nitric and chlorine ions have been electrochemically deposited simply by a one-step electrochemical method in an aqueous media in the absence of any surfactant. The fabricated PEDOT films were characterized by scanning electron microscopy, transmission electron microscopy, and Raman spectroscopy. The results indicate that the hierarchical structured PEDOT film doped with nitric ions displays a 'lunar craters' porous morphology consisting of PEDOT nano-sheets with a thickness of less than 2 nm. The effect of counter ions on the electro-polymerization, the electrochemistry, and the morphology of the polymer film was studied. Compared with PEDOT film doped with nitric acid, PEDOT film deposited in the presence of chlorine ions shows irregular morphology and less electrochemical activity. The specific nanostructure of the polymer was further studied as catalyst support for platinum nanoparticles to methanol electro-oxidation.

Introduction

Poly(3,4-ethylenedioxythiophene) (PEDOT) is an important π-conjugated conducting polymer, which is currently being investigated for use in many fields [1], such as antistatic and anticorrosion materials, artificial muscles, electrode materials in batteries, super-capacitors, display devices, and biosensors. Although various 1D or 2D PEDOT nanomaterials, such as nanofibers, nanospheres, nano-tubes, and nanorods [2-6], have been prepared and studied, there are few reports on the more complicated hierarchical structure of this functional polymer. PEDOT film is one of the main applied forms of this functional material. For example, PEDOT films are recently studied as catalyst support for Pt or Pd nanoparticles for either electro-oxidation of methanol or ethanol [7,8], which can be potentially used in direct methanol fuel cell (DMFC) or sensors to some chemicals, such as nitrite, bromate, oxygen, hydrogen peroxide [9]. As many applications of the PEDOT material are related to its microstructure and electrochemical activity, studies on the film surface control and physical chemical properties are very important.

Electrochemical polymerization is a convenient method to prepare PEDOT, and generally a film yields on the surface of the anode. The electro-synthesis can be done both in organic and aqueous solutions. Due to the low solubility of EDOT in water at room temperature, previous research on the electro-polymerization of PEDOT was usually done in an organic solution, such as acetonitrile and propylene carbonate [10,11]. Recently, there are growing interests in the study of electro-polymerization of PEDOT films in an aqueous solution [12-19]. It is known that the properties of conducting polymers are strongly dependent on their morphologies and their physical and chemical structures. Polypyrrole micro-containers have been synthesized electrochemically by direct oxidation of pyrrole monomer in an aqueous solution [20,21]. Surfactants were often used to control the morphology of the PEDOT film with electrochemical methods recently [12-17]. Sodium dodecylsulphate (SDS) has also been used in the electro-synthesis of PEDOT with different morphologies (globular and fibrous) [12]. PEDOT/PSS (poly(4-styrene sulfonate)) film with microstructures of micro-rings/arrows and bubbles has been prepared with the cyclic voltammetry method and the influences of applied potentials and surfactant (PSS) on the morphology of the resulted film were also investigated [13]. PEDOT micro-cups with diameters in the range of 1 to 4 mm were generated by direct oxidation of EDOT in the aqueous solution of LiClO4 and tri (ethylene glycol (EG)) on the ITO electrode with a PSS/PDDA multilayer coating [19].

The conductive polymers, such as PAni or PEDOT have been studied as catalyst or its support for hydrogen and methanol fuel cell applications [22-24]. Pt supported on PAni-based nano-tubes and nanofibers showed an excellent electrochemical activity for methanol oxidation, respectively [23,24]. In this work, a three-dimensional (3D) nanostructured PEDOT was fabricated through a simply one-step electrochemical route in an aqueous solution in the absence of any surfactant. Microscopic studies indicated that the films are comprised of fine electroactive polymer sheets with the edge thickness of less than 2 nm, which is only slightly larger than the well known graphene sheets. Moreover, a lunar crater porous morphology was observed on one surface of the films. To the best of our knowledge, this is the first report concerning the deposition of such nanostructured PEDOT films on Pt and its application as catalyst support for methanol oxidation.

Experimental

Electro-deposition of PEDOT

The electrochemical deposition of PEDOT was carried out on a CHI1202 Electrochemical Analyzer (CH Instruments). All solutions were prepared in distilled water and all potentials reported are referenced to saturated calomel electrode (SCE). An electrolyte of 0.1 M KNO3 (or 0.1 M KCl) + 0.01 M EDOT was used for the deposition of PEDOT doped with nitric ions (denoted as PEDOT-NO3) (or doped with chlorine ions (denoted as PEDOT-Cl)) on platinum electrode. A three-electrode electrochemical cell was used for the electrochemical measurements, where the counter electrode was a Pt foil and the reference electrode was a SCE. The charge consumed was monitored and was considered as a measure of the mass of the deposited PEDOT. The polymer was removed carefully from the electrode and dispersed in EG under ultrasonic irradiation to prepare the PEDOT suspensions.

Electrocatalyst fabrication and the methanol oxidation

Pt particles in EG were prepared in situ by a microwave assisted EG reduction method. 0.1 g H2PtCl6 and 0.1 g NaOH were dissolved in 5 mL EG. The glass bottle was placed in the center of a microwave oven and heated for 13 s to prepare the Pt nanoparticle containing solution. The fabricated black solution was very stable and was mix with the above PEDOT suspensions. Seventy microliters of the Pt containing solution was added dropwise to the above PEDOT suspension with strong ultrasonic irradiation to prepare the electrocatalyst composites. After centrifugation and washing with ethanol, the material was dispersed in 0.05 wt% Nafion solutions and sonicated for 20 min to prepare the catalyst ink. Eight microliters of such catalyst solution was added to the surface of the glass carbon (GC) electrode (Φ = 3 mm) and dried in air. Prior to the electrochemical measurement, the catalyst covered electrode was soaked in the electrolyte solution (1 M CH3OH + 0.5 M H2SO4) for 10 min.

Morphology and spectrum of the materials

Transmission electron microscopy (TEM) characterization was performed on a Philips CM12 operating at an accelerated voltage of 120 kV and scanning electron microscopy (SEM) analyses were performed on a Zeiss ULTRA plus. Raman spectroscopy of the products was performed on an Invia Renishaw Raman using a He-Ne laser at 633 nm wavelength.

Results and discussion

Electropolymerization of PEDOT

The conductive polymers are always prepared in their oxidation form with doping ions. The doping ions in the PEDOT have been reported to have great influence on the electrical properties of the film [12,13]. For example, the PEDOT films doped with Cl- have much less electrical conductivity than those doped with NO3- [12]. Here we studied the effect of the doping ions (Cl- and NO3-) on the electro-polymerization behavior, the morphology, and the electrochemical properties of the resulted PEDOT polymer film.

Figure 1 shows the cyclic voltammograms of the electrochemical oxidation of EDOT on the Pt electrode with Cl- and NO3- as doping ions, respectively. In the case of nitric ions (Figure 1a), two oxidation peaks appeared at about 1.15 and approx. 1.37 V. Similar to the previous report [18], the first peak can be attributed to the oxidation of the EDOT and the second peak may be related to the over-oxidation of the preformed PEDOT or its oligomers. However, in the case of chlorine ions (Figure 1b), only a poorly resolved current peak at 1.25 V appeared. The current is much less than the one with nitric ions, although the other parameters are the same. The electro-polymerization of the EDOT in the presence of chlorine ions is quite different from that previously reported in the presence of perchlorate ions [18] and dodecylsulphate anions [12]. Obviously the electrochemical process of the electro-deposition of PEDOT doped with chlorine ions needs further investigation.

thumbnailFigure 1. Cyclic voltammograms of Pt in 0.01 M EDOT + 0.1 M KNO3 and 0.01 M EDOT + 0.1 M KCl. Scan rate: 50 mV/s.

PEDOT films doped with chlorine and nitric ions were electro-synthesized with the chronocoulometry method, as shown in Figure 2. As the charges consumed implied the amount of the electrical conductive polymer on the electrode, the same charge was consumed to fabricate the same amount of polymer doped with different ions. The charges were consumed more quickly in the presence of nitric ions than those in the presence of chlorine ions, indicating the faster deposition of the PEDOT doped with nitric ions. With the electro-polymerization proceeding, a homogeneous deep blue polymer film doped with nitric ions was deposited on the Pt electrode surface. Different from the color of the PEDOT-NO3, PEDOT-Cl film is brown. The electrochemical behaviors of the PEDOT films with different doping ions were also investigated. As shown in Figure 3, the current of PEDOT-Cl is much less than that of PEDOT-NO3, indicating that the PEDOT doped with nitric ions is more electro-active than those doped with chlorine ions, which is in consistence with the above CV and chronocoulometry results.

thumbnailFigure 2. Chronocoulemetry of PEDOT deposition on Pt in 0.01 M EDOT + 0.1 M KNO3 and 0.01 M EDOT + 0.1 M KCl.

thumbnailFigure 3. Cyclic voltammograms in the phosphate buffer solution. Scan rate: 50 mV/s. (a)PEDOT-NO3 and (b)PEDOT-Cl.

Raman studies were carried out to further determine the vibration modes of the films in the wavenumber range of 400 to 2000 cm-1, as shown in Figure 4. The peaks at 1568 and 1500 cm-1 are originated from the asymmetrical stretching of Cα = Cβ, and the most intense peak at 1438 cm-1 can be attributed to the symmetrical stretching of Cα = Cβ (in the monomer EDOT, Cα is the carbon atoms connecting with the sulfur atom, while Cβ is the carbon atoms connecting with Cα). The peaks at 1366 cm-1 are assigned to the Cβ"-Cβ" inter-ring stretching, and the peaks at 1267 cm-1 are assigned to the C-C inter-ring stretching. The peaks at 1100 and 697 cm-1 are assigned to the C-O-C stretching and C-S-C bending, respectively. A peak from C-C anti-symmetrical stretching mode can be seen at 990 cm-1. The resulted spectrum is just similar to those of other results and the absence of any signal in the 650 to 680 cm-1 region of the spectrum could lead to similar conclusion that the electrodeposited PEDOT chains has a highly planar structure [11,16,25].

thumbnailFigure 4. Raman spectrum of PEDOT-NO3 film.

Based on the above results, the electroactive PEDOT film doped with nitric ions was selected as the catalyst support. The SEM images of the PEDOT film are presented in Figure 5a, b. The polymer film consists of flower-like particles, each comprising of many fine polymer sheets. In the cross-section image of the film (Figure 5c), the sheets seem to connect with each other, leaving countless irregular pores in the film. The thickness of the nanosheets is always less than 10 nm, which is also confirmed by TEM observation (Figure 5d), in which even approx. 2-nm sheet thickness can be identified from the folded edge of the polymer sheets. Due to their high aspect ratio, the nanosheets generally scrolled and bent to minimize the surface energy, similar to the behavior of the graphene nanosheets [26]. On the other side of the film facing to the Pt substrate (Figure 5e), many pores with nanoscale size can be found, which is just like the lunar craters. It should be noted that such nanostructure is not common in the electrodeposited PEDOT films, as no such sheet-like structure was found in electropolymerized PEDOT-Cl materials (Figure 5f).

thumbnailFigure 5. SEM and TEM images of the PEDOT-NO3 film. (a, b)up-surface; (c) the cross section and (d) the back-surface; (e) TEM image; (f) SEM images of PEDOT-Cl film.

Methanol oxidation on Pt-PEDOT catalyst

Figure 6 shows the morphology of the Pt-PEDOT materials. The white grains in the SEM micrographs (Figure 6a) are attributed to platinum nanoparticles. Due to high degree of porosity nanosheet structure of the PEDOT film, it favors for platinum particles to be uniformly dispersed over the film surface. The EDS results also prove the existence of Pt in the composite and the content of the platinum in the composite was 50 wt%. In the TEM image (Figure 6b), the Pt particles were uniformly dispersed on the surface and edge of the PEDOT sheets. Some aggregates with a diameter of about 20 to 60 nm can also be observed occasionally and they are composed of fine Pt particles (about 3 to 6 nm of size).

thumbnailFigure 6. Images of the Pt-PEDOT composites. (a)SEM and (b)TEM.

The cyclic voltammogram of a Pt-PEDOT/GC electrode in 0.5 M H2SO4 at a sweep rate of 100 mV/s is shown in curve b in Figure 7. The current peaks appearing between -0.2 and 0.0 V are due to adsorption and desorption of hydrogen atoms on the Pt surface. The CV is similar to those of Pt metal [7], suggesting that Pt-PEDOT film is electrochemically active. The curve a in Figure 7 illustrates the electrocatalytic activity of the Pt-PEDOT/GC electrode toward oxidation of methanol. Comparing with the curve b, two new peaks appeared above 0.15 V in curve a in Figure 7, in which the forward current peak is attributed to the oxidation of CH3OH molecule and the backward current peak to the oxidation of adsorbed intermediates. The current peaks related to hydrogen adsorption in curve a in Figure 7 are much less than the ones in curve b, indicating the adsorption of some reaction intermediates from the oxidation of methanol on the Pt nano-catalysts. Obviously, the methanol oxidation current on the Pt-PEDOT catalyst (curve b) has been enhanced by more than 70 times than that of Pt electrode (curve c), exhibiting the advantage of the application of nanostructured PEDOT catalyst support and Pt nanocatalyst. The higher current for the methanol oxidation on Pt-PEDOT catalyst indicates their higher electrocatalystic activity of the novel catalysts, which is believed to be related to their porous nanostructure and high electroactivity.

thumbnailFigure 7. Cyclic voltammograms of (a) Pt-PEDOT/GC and (c) Pt disk electrode in 1 M CH3OH + 0.5 M H2SO4, and (b) Pt-PEDOT/GC in 0.5 M H2SO4 . Scan rate: 100 mV/s.

Conclusion

PEDOT films with a flower-like nanostructure on Pt electrodes have been electrochemically generated simply by a one-step electrochemical method in an aqueous media in the absence of any surfactant. Inorganic counter ions have great effect on the electrochemistry and morphology of the electropolymerized PEDOT films. The morphology of the prepared PEDOT film doped with nitric ions shows porous hierarchical nanostructure based on fine nanosheets which develop large specific surface area with high electrochemical activity. Electrocatalysts comprised the PEDOT film and Pt nanoparticles showed high catalyst performance to methanol electro-oxidation.

Abbreviations

DMFC: direct methanol fuel cell; EG: ethylene glycol; GC: glass carbon; PEDOT: poly(3,4-ethylenedioxythiophene); PSS: poly(4-styrene sulfonate); SEM: scanning electron microscopy; SCE: saturated calomel electrode; SDS: sodium dodecylsulphate; TEM: transmission electron microscopy.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

CZ carried out the electrocatalyst study and morphology characterization, participated in the sequence data analysis and drafted the manuscript. ZL and YY conceived this study. ZL and SPR financial supported for the spectrum experiments and involved in revising the manuscript. XD conceived the study, carried out the electrodeposit of PEDOT, participated in the design of the study, performed the statistical analysis, drafted and involved in revising the manuscript critically for important intellectual content. YWM conceived this study and involved in revising the manuscript. All authors read and approved the final manuscript.

Acknowledgements

The authors are grateful for access to the characterization facilities in the Australian Microcopy & Microanalysis Research Facility at the Australian Key Centre for Microscopy and Microanalysis, University of Sydney. C.Z. acknowledges the award of an APA scholarship. Z.L. and X.D. would like to thank the Australian Research Council (ARC) for the financial supports (DP0773977 and DP0772551).

References

  1. Hohnholz D, Okuzaki H, MacDiarmid AG: Plastic electronic devices through line patterning of conducting polymers.

    Adv Funct Mater 2005, 15:51. Publisher Full Text OpenURL

  2. Jang J: Conducting polymer nanomaterials and their applications.

    Adv Polym Sci 2006, 199:189. Publisher Full Text OpenURL

  3. Martin CR: Membrane-based synthesis of nanomaterials.

    Chem Mater 1996, 8:1739. Publisher Full Text OpenURL

  4. Kim BH, Park DH, Joo J, Yu SG, Lee SH: Synthesis, characteristics, and field emission of doped and de-doped polypyrrole, polyaniline, poly (3,4-ethylenedioxythiophene) nanotubes and nanowires.

    Synth Met 2005, 150:279. Publisher Full Text OpenURL

  5. Wu J, Li Y, Feng W: A novel method to form hollow spheres of poly (3,4-ethylenedioxythiophene): Growth from a self-assemble membrane synthesized by aqueous chemical polymerization.

    Synth Met 2007, 157:1013. Publisher Full Text OpenURL

  6. Du XS, Zhou CF, Mai Y-W: Novel synthesis of poly(3,4-ethylenedioxythiophene) nanotubes and hollow micro-spheres.

    Mater Lett 2009, 63:1590. Publisher Full Text OpenURL

  7. Patra S, Munichandraiah N: Scanning electron microscopy studies of PEDOT prepared by various electrochemical routes.

    Langmuir 2009, 25:1732. PubMed Abstract | Publisher Full Text OpenURL

  8. Pandey RK, Lakshminarayanan V: Enhanced Electrocatalytic Activity of Pd-Dispersed 3,4-Polyethylenedioxythiophene Film in Hydrogen Evolution and Ethanol Electro-oxidation Reactions.

    J Phys Chem C 2010, 114:8507. Publisher Full Text OpenURL

  9. Karnicka K, Chojak M, Miecznikowski K, Skunik M, Baranowska B, Kolary A, Piranska A, Palys B, Adamczyk L, Kulesza PJ: Polyoxometallates as inorganic templates for electrocatalytic network films of ultra-thin conducting polymers and platinum nanoparticles.

    Bioelectrochemistry 2005, 66:79. PubMed Abstract | Publisher Full Text OpenURL

  10. Melato AI, Viana AS, Abrantes LM: Different steps in the electrosynthesis of poly(3,4-ethylenedioxythiophene) on platinum.

    Electrochim Acta 2008, 54:590. Publisher Full Text OpenURL

  11. Sakmeche N, Aeiyach S, Aaron JJ, Jouini M, Lacroix JC, Lacaze P-C: Improvement of the electrosynthesis and physicochemical properties of poly(3,4-ethylenedioxythiophene) using a sodium dodecyl sulfate micellar aqueous medium.

    Langmuir 1999, 15:2566. Publisher Full Text OpenURL

  12. Patra S, Barai K, Munichandraiah N: Scanning electron microscopy studies of PEDOT prepared by various electrochemical routes.

    Synth Met 2008, 158:430. Publisher Full Text OpenURL

  13. Han D, Yang G, Song J, Niu L, Ivaska A: Morphology of electrodeposited poly(3,4-ethylenedioxythiophene)/poly(4-styrene sulfonate) films.

    J Electroanal Chem 2007, 602:24. Publisher Full Text OpenURL

  14. Bhandari S, Deepa M, Singh S, Gupta G, Kant R: Redox behavior and optical response of nanostructured poly(3,4-ethylenedioxythiophene) films grown in a camphorsulfonic acid based micellar solution.

    Electrochim Acta 2008, 53:3189. Publisher Full Text OpenURL

  15. Wen Y, Xu J, He H, Lu B, Li Y, Dong B: Electrochemical polymerization of 3,4-ethylenedioxythiophene in aqueous micellar solution containing biocompatible amino acid-based surfactant.

    J Electroanal Chem 2009, 634:49. Publisher Full Text OpenURL

  16. Tamburri E, Orlanducci S, Toschi F, Terranova ML, Passeri D: Growth mechanisms, morphology, and electroactivity of PEDOT layers produced by electrochemical routes in aqueous medium.

    Synth Met 2009, 159:406. Publisher Full Text OpenURL

  17. Zhou CF, Liu ZW, Du XS, Ringer SP: Electrodeposited PEDOT films on ITO with a flower-like hierarchical structure.

    Synth Met 2010, 160:1636. Publisher Full Text OpenURL

  18. Du X, Wang Z: Effects of polymerization potential on the properties of electrosynthesized PEDOT films.

    Electrochim Acta 2003, 48:1713. Publisher Full Text OpenURL

  19. Gao Y, Zhao L, Li C, Shi G: Low-swelling proton-conducting copoly(aryl ether nitrile)s containing naphthalene structure with sulfonic acid groups meta to the ether linkage.

    Polymer 2006, 47:4953. Publisher Full Text OpenURL

  20. Qu LT, Shi GQ, Yuan JY, Han GY, Chen FE: Preparation of polypyrrole microstructures by direct electrochemical oxidation of pyrrole in an aqueous solution of camphorsulfonic acid.

    J Electroanal Chem 2004, 561:149. OpenURL

  21. Bajpai V, He P, Dai LM: Conducting-polymer microcontainers: Controlled syntheses and potential applications.

    Adv Funct Mater 2004, 14:145. Publisher Full Text OpenURL

  22. Drillet JF, Dittmeyer R, Jüttner K, Li L, Mangold K-M: New composite DMFC anode with PEDOT as a mixed conductor and catalyst support.

    Fuel Cells 2006, 6:432. Publisher Full Text OpenURL

  23. Rajesh B, Thampi KR, Bonard JM, Mathieu HJ, Xanthopoulos N, Viswanathan B: Nanostructured conducting polyaniline tubules as catalyst support for Pt particles for possible fuel cell applications.

    Electrochem Solid State 2004, 7:A404. Publisher Full Text OpenURL

  24. Chen Z, Xu L, Li W, Waje M, Yan Y: Polyaniline nanofibre supported platinum nanoelectrocatalysts for direct methanol fuel cells.

    Nanotechnology 2006, 17:5254. Publisher Full Text OpenURL

  25. Du XS, Yu ZZ, Dasari A, Ma J, Mo M, Meng Y, Mai YW: New method to prepare graphite nanocomposites.

    Chem Mater 2008, 20:2066. Publisher Full Text OpenURL

  26. Duvail JL, Rétho P, Garreau S, Louarn G, Godon C, Demoustier-Champagne S: Transport and vibrational properties of poly(3,4-ethylenedioxythiophene) nanofibers.

    Synth Met 2002, 131:123. Publisher Full Text OpenURL