Open Access Nano Express

Analytical model for the photocurrent-voltage characteristics of bilayer MEH-PPV/TiO2 photovoltaic devices

Chong Chen1, Fan Wu1, Hongwei Geng1, Wei Shen1 and Mingtai Wang12*

Author Affiliations

1 Institute of Plasma Physics, Chinese Academy of Sciences, Hefei 230031, PR China

2 School of Materials Science and Engineering, Anhui University of Architecture, Hefei 230022, PR China

For all author emails, please log on.

Nanoscale Research Letters 2011, 6:350  doi:10.1186/1556-276X-6-350


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/6/1/350


Received:28 January 2011
Accepted:19 April 2011
Published:19 April 2011

© 2011 Chen et al; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

The photocurrent in bilayer polymer photovoltaic cells is dominated by the exciton dissociation efficiency at donor/acceptor interface. An analytical model is developed for the photocurrent-voltage characteristics of the bilayer polymer/TiO2 photovoltaic cells. The model gives an analytical expression for the exciton dissociation efficiency at the interface, and explains the dependence of the photocurrent of the devices on the internal electric field, the polymer and TiO2 layer thicknesses. Bilayer polymer/TiO2 cells consisting of poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) and TiO2, with different thicknesses of the polymer and TiO2 films, were prepared for experimental purposes. The experimental results for the prepared bilayer MEH-PPV/TiO2 cells under different conditions are satisfactorily fitted to the model. Results show that increasing TiO2 or the polymer layer in thickness will reduce the exciton dissociation efficiency in the device and further the photocurrent. It is found that the photocurrent is determined by the competition between the exciton dissociation and charge recombination at the donor/acceptor interface, and the increase in photocurrent under a higher incident light intensity is due to the increased exciton density rather than the increase in the exciton dissociation efficiency.

Introduction

The polymer-based photovoltaic (PV) cells consisting of conjugated polymer as electron donor (D) and nanocrystals as electron acceptor (A) are of great interest due to their advantages over conventional Si-based cells, such as low cost, easy-processability, and capability to make flexible devices [1-3]. Generally, the p-type conducting polymer acts as both electron donor and hole conductor in the photovoltaic process of the device, while the n-type semiconductor serves as both electron acceptor and electron conductor. The electron donor and acceptor can be intermixed into bulk architecture or cast into a bilayer structure in the PV devices [4-13]. The latter architecture is attractive for efficient devices, because the photogenerated electrons and holes are, to a great extent, confined to acceptor and donor sides of the D/A interface, respectively, where the spatial separation of electrons and holes will minimize the interfacial charge recombination and facilitate the transport of charge carriers toward correct electrodes with greatly reduced energy loss at wrong electrodes [1-3].

The primary processes involved in the photocurrent generation in a polymer-based PV cells include the exciton generation in the polymer after absorption of light, exciton diffusion toward the D/A interface, exciton dissociation at the D/A interface via an ultrafast electron transfer. The kinetics of the charge-carrier separation and recombination at the D/A interface imposes a great effect on the cell efficiency, and modeling the kinetics of the interfacial charge separation and recombination will offer a good way to understand the efficiency-limiting factors in the devices and to inform experimental activities. For this purpose, several theoretical models dealing with the interfacial charge separation and recombination have been developed in the past years. However, most of them are based on either Monte Carlo (MC) simulation [14-21] or numerical calculations [22,23], and only a few models offer analytical expressions [5,24-26]. Furthermore, the previous studies mainly focused on understanding the influences of interfacial dipoles [14,20], energetic disorder [15,20], light intensity [17], interface morphologies [18-22], and electrostatic interactions [20], on the interfacial charge separation and recombination at the organic/organic interfaces. The quantitative analysis of the charge transfer mechanism at the organic/inorganic interfaces in the polymer-based PV cells has been scarcely explored so far. Commonly, the photoinduced interfacial charge transfer from the polymers to inorganic semiconductors is explained by the exciton dissociation at the D/A interface due to the favorable energy match between the D and A components, without considering the role of the interfacial electric field [16,27-31]. Breeze et al [5] proposed an analytical expression including the interfacial electric field for the exciton dissociation efficiency in bilayer MEH-PPV/TiO2 photovoltaic device, which only expresses the dependence of exciton dissociation efficiency on the polymer layer thickness, not on the TiO2 layer thickness. To understand the influence of TiO2 layer thickness on the exciton dissociation efficiency, one needs to consider the electrical properties of the system. In other words, more factors, such as voltage drop across the TiO2 layer, field-dependent mobility, field-dependent exciton dissociation, and charge recombination at the D/A interface, are necessarily to be incorporated into the model.

In this article, we propose a simple analytical model to describe the exciton dissociation and charge recombination rates at the D/A interface for the bilayer MEH-PPV/TiO2 cells by modeling the photocurrent-voltage characteristics of the devices. Not only this model is successful in describing the effect of the internal electric field at the D/A interface on exciton dissociation efficiency, but also describes the dependence of the exciton dissociation efficiency on the polymer and TiO2 layer thicknesses. We verify our model by fitting the measured experimental data on bilayer MEH-PPV/TiO2 devices under different conditions. The results obtained from the model show that the photocurrent of the devices is determined by the competition between the exciton dissociation and the charge recombination at the D/A interface; the exciton dissociation efficiency increases with either the increase in the forward electric field or the decrease in the thicknesses of polymer and/or TiO2 layers. In addition, it is found that a higher incident light intensity leads to a higher photocurrent density, but a lower exciton dissociation efficiency.

Experimental section

Poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) (Avg. Mn = 40000-70000) was purchased from Aldrich (product of USA). Titanium tetraisopropoxide [Ti(Oi-Pr)4] (Acros, 98+%) was used as TiO2 precursor. The bilayer PV devices with a structure of ITO/TiO2/MEH-PPV/Au, as shown in Figure 1, were constructed by spinning down first a nanostructured titanium dioxide (TiO2) layer and then a MEH-PPV layer over indium tin oxide (ITO, ≤15 Ω/∀, Wuhu Token Sci. Co., Ltd., Wuhu, China) sheet glass, as described elsewhere [11]. The current-voltage (J-V) characteristics were measured on a controlled intensity modulated photo spectroscopy (CIMPS) (Zahner Co., Kronach, Germany) in ambient conditions. The devices were illuminated through ITO glass side by a blue light-emitting diode (LED) as light source (BLL01, λmax = 470 nm, spectral half-width = 25 nm, Zahner Co., Kronach, Germany). A reverse voltage sweep from 1 to -1 V was applied and the current density under illumination (JL) was recorded at 300 K. In order to determine the photocurrent, the current density in the dark (JD) was also recorded, and the experimental photocurrent is given by Jph = JL - JD [24,26,32], as shown in Figure 2. From the resulting Jph-V characteristics the compensation voltage (V0) was determined as the bias voltage where Jph = 0 (inset to Figure 2). During all measurements, the gold and ITO contacts were taken as negative and positive electrodes, respectively, and the effective illumination area of the cells was 0.16 cm2.

thumbnailFigure 1. Geometry of the bilayer device under illumination.

thumbnailFigure 2. Current-voltage characteristics of ITO/TiO2/MEH-PPV/Au device. The solid line (JD) was recorded in the dark, and the dot line (JL) was measured under illumination at 470 nm with an intensity of 158.5 W/m2. The thickness of TiO2 layer was d = 65 nm, while that of the polymer layer was l = 220 nm. The inset shows the Jph as a function of bias, where the arrow indicates the compensation voltage (V0).

The model

Since the injected charge by the electrodes can be ignored and the charge density in the bulk is low when a small voltage is applied to the device, the electric fields in the polymer (Ep) and TiO2 (En) regions are regarded to be constant [33]. For the small applied voltage, the internal bias in the cell is V - V0 [34]. Therefore, the voltage drop across the device is simply given as Epl + End = V - V0. From the discontinuity of the electric field at the polymer/TiO2 interface, we have Epεp - Enεn = Q [33]. Thus, we obtain

(1)

(2)

where Ep (En) is the electric field in the polymer (TiO2 ) layer, εp (εn) is the polymer (TiO2) dielectric constant, l (d) is the polymer (TiO2) layer thickness, and Q is accumulated charge density at the polymer/TiO2 interface.

The excitons at the D/A interface may be quenched by two processes, namely, exciton dissociation into free charge carriers and the lost of energy by luminescence or due to other processes [35-37]. Here, we only consider the exciton quenching by dissociation. Therefore, the photocurrent can be described as [38]

(3)

where I is the incident photon flux, e the charge of an electron, and ηEQE(V) the voltage dependent the quantum efficiency. ηEQE(V) can be described as [18]

(4)

where ηA is the efficiency of photon absorption leading to the exciton generation, ηED the efficiency of excitons that diffuse to the D/A interface, ηCT the efficiency of exciton dissociation by charge transfer at the D/A interface, and ηCC the efficiency of charge collection at electrodes. Here, we suppose that ηED is constant, and ηCC = 1 since the recombination of charges in a D/A bilayer device mainly occurs at the D/A interface [39]. In addition, we neglect the fraction of incident light reflected by the sample, then ηA is taken as [40]

(5)

where α is the polymer absorption coefficient, and Lp the exciton diffusion length.

In a bilayer device, the electrons are injected into the acceptor layer and the holes remain in the donor layer after the interfacial exciton dissociation [39]. In other words, each charge carrier is in its respective phase. Therefore, in our case, the charge recombination in single polymer or TiO2 layer can be ignored. However, the recombination at the D/A interface must be considered. The presence of the internal electric field in the device may affect the charge-transport properties and also the charge recombination and exciton dissociation rates at the D/A interface. In our model, the exciton dissociation efficiency ηCT is expressed in terms of the ratio between exciton recombination and separation. As shown in Figure 3a, when applying a forward internal electric field (E > 0), the drift and diffusion currents of the electrons (holes) in the TiO2 (polymer) layer are in the same direction, the electric field contributes to suppress the recombination of injected electrons in TiO2 with holes in the highest-occupied molecular orbital (HOMO) of the polymer by accelerating their separation at the polymer/TiO2 interface.

thumbnailFigure 3. Schematic band diagram for a bilayer TiO2/MEH-PPV device under (a) E > 0 and (b) E < 0.

However, when applying a reverse internal electric field (E < 0) (Figure 3b), the drift current of the electrons (holes) in the TiO2 (polymer) layer is in a reverse direction, and the electric field prevents the photogenerated electrons (holes) from leaving the polymer/TiO2 interface, which raises the recombination of generated charge carries, i.e., reduces their separation probability at the interface. The exciton dissociation probability has a weaker dependence on the larger carrier mobility in bilayer photovoltaic devices [41]. In our case, the mobility of the electrons in the TiO2 layer is larger than that of the holes in the MEH-PPV layer. Therefore, the effect of the electron mobility in the TiO2 layer on the exciton dissociation probability is not considered in our model. Here, we define a forward hopping rate kf (Ep) and a backward hoping rate kb (Ep) for the holes, and the net hole hopping rate, k(Ep), is given by their difference [42],

(6)

It is known that the electric-field-dependent hole mobility has the Poole-Frenkel form [43],

(7)

Here, μ0 is the zero-field mobility of holes, γ the electric-field-dependent parameter [44] with a value of 5 × 10-3 (cm/V)1/2 [45]. Assuming that the zero-field hopping rate of holes, k0, in the polymer layer is proportional to the zero-field mobility μ0, then, we get the electric-field-dependent hole hopping rate k(E) with the same form,

(8)

In order to reflect the effect of an external electric field on hole transport in the polymer layer, we employ an activation energy [42]. Then, kf (Ep) and kb (Ep) can be expressed as, respectively

(9)

(10)

where l0 is the nearest neighbor hopping distance, kB the Boltzmann constant, T the absolute temperature, q the elementary charge, and Ea the thermal activation energy at zero field per molecule. In our calculations, we take Ea = 0.18 eV for MEH-PPV, which is comparable to the value of thermal activation energy 0.2 eV [45], and take l0 = 0.3 nm in the MEH-PPV molecules by referring to the typical distance of 0.6-1 nm between hopping sites in organic materials [46].

As Ep > 0 with E > 0 (i.e., V > V0), the net hole hopping rate is equal to the excitons separation rate at the D/A interface. The exciton separation rate ks(E) can be derived from Equation 6-9,

(11)

As mentioned above (Figure 3a), the forward electric field suppresses the recombination of the injected electrons in TiO2 with the holes in the polymer at the D/A interface. When the electrons transfer from TiO2 to the polymer layer, they have to overcome an energy barrier Δϕ at the D/A interface, in which the energy barrier is inevitably influenced by several factors, such as the applied bias, the electron-hole Coulomb interactions, and the temperature. Thus, the electron-hole recombination rate kr(E) (i.e., the electrons transfer rate from TiO2 to the polymer layer) at the D/A interface should be of an exponential dependence on the energy barrier. In addition, the recombination rate at the D/A interface should increase with temperature due to a thermally activated interfacial charge-transfer process [47]. Here, the bimolecular recombination of mobile charges and the space charge effect at the D/A interface are not considered for simplification. Furthermore, due to the large dielectric constant of TiO2 [47], the electron-hole Coulomb interactions can be ignored. Therefore, the energy barrier Δϕ should be dependent on the temperature T and the applied bias V. With the above considerations, we assumed a simple form for kr(E) [45],

(12)

When V = 0 V, kr(E) = v0. Thus, v0 is a zero-field recombination rate constant that depends on the used materials and the thickness of the polymer (TiO2) film in the devices, and the energy barrier Δϕ is the potential energy determined by the applied bias V. In order to get kr, it is assumed that Δϕ is in direct proportion to Vλ, i.e., Δϕ = βVλq, where β is a proportionality factor and λ is used to characterize the bias-dependent strength of Δϕ. Here, it should be noted that Δϕ in a specific device may not be in proportional to V (i.e., λ ≠ 1) because the bias-dependent strength of should be determined by experimental results. Moreover, Δϕ has the dimensions of energy, thus β is not a dimensionless factor. Finally, according to Equation 12 and the expression of kr can be expressed as,

(13)

Equation 13 shows that kr(E) decreases with increasing the forward applied bias. Hence, the exciton dissociation efficiency ηCT is [24,26,48],

(14)

The photocurrent Jph for V > V0 can be derived from Equations 3-5 and 14 as follows:

(15)

Results and discussion

In order to calculate the electric fields Ep and En, the accumulated charge density at the D/A interface is assumed to be a constant and Q=1.0 × 10-4 C/m2 [33]. We find that Q has a weak influence on the calculated results by our model, for which the reason may be that the internal electric field in the devices is only slightly modified due to the band bending created by the accumulation of the charge carriers at the D/A interface [24]. Therefore, it is reasonable that we simply assume Q is a constant. In spite of the parameters εp = 4ε0 which is comparable to εp = 3ε0 [45], εn = 55ε0 [49], αp(λ = 470 nm) = 105 cm-1, and Lp = 15 nm [12,13,50], there are still three parameters (i.e., λ, k0/v0, and β) needed to obtain Jph by Equation 15. Our calculated data revealed that the shape of Jph-V curve is strongly dependent on the values of λ, but less dependent on the values of k0/v0 and β. Therefore, the parameter λ can be first obtained by curve fitting taking the order of magnitude of 10-5 for k0/v0 and that of 10-3 for β; then, the values of k0/v0 and β can be obtained by the best fit. In our model, we take λ = 3 and β is a constant with a value of 5 × 10-3 V-2. Finally, the ratio k0/v0 is the only adjustable fit parameter in fitting the experimental photocurrent. Since k0 and v0 are zero-field recombination rate constants, the ratio k0/v0 is independent of the electric field. However, the ratio k0/v0 depends on the used materials or the geometry of the devices [48] such as the TiO2 (polymer) film thickness as shown in Figure 4.

thumbnailFigure 4. The measured and fitted photocurrent-voltage curves for ITO/TiO2/MEH-PPV/Au devices. (a-c) Panels are for the devices with different TiO2 and MEH-PPV layer thicknesses measured under the same illumination intensity; while (c, d) panels are used to show the influence of illumination intensity on the same device. The incident intensity was 15.85 mW/cm2 (a-c), 3.0 mW/cm2 (d) and 9.6 mW/cm2 (e). The k0/v0 values obtained by fitting the experimental data to Equation 15 are marked on the respective panels.

Note that, all the following theoretical curves were obtained by considering the experimentally determined compensation voltage V0. As shown by the solid lines in Figure 4, the excellent fits to the photocurrent-voltage characteristics of three types devices are obtained using the parameters described above. During the calculations, we use different k0/v0 values to fit the photocurrent-voltage characteristics of the differently structured devices (Figure 4a,b,c) and the same cell under the varied illumination intensities (Figure 4c,d,e). In Figure 4, it can be seen that the photocurrent increases as the applied voltage turns from reverse to forward direction, and subsequently tends to saturate at higher forward voltages. This phenomenon can be attributed to the dependence of the exciton dissociation efficiency ηCT on the internal electric field (Equation 14), since the efficiency ηED of exciton dissociation by charge transfer at the D/A interface is constant and the efficiency ηCC of charge collection at electrodes is equal to 1 (Equation 4) [39]. As suggested from Figure 3a, the exciton dissociation efficiency at the D/A interface increases with increasing the forward electric field strength (i.e., the forward applied voltage), and finally approach unit when the forward electric field strength is large enough. In order to examine the dependence of ηCT on the applied voltage V, the TiO2 and polymer film thicknesses and illumination intensity, we plot the expression ηCT from Equation 14 for all devices, as shown in Figure 5.

thumbnailFigure 5. The calculated ηCT as a function of applied voltage V with deferent l (a), d (b) and various illumination intensities (c).

Figure 5a shows that, for the devices with different TiO2 thicknesses (d), when V - V0 > 0, i.e., Ep(En) > 0, ηCT increases with the increasing forward applied voltage, indicating that the forward electric field is beneficial to the exciton dissociation efficiency as indicated in Figure 3a. When the forward electric field is large enough (V > -0.4 V here), ηCT for the device with d = 65 nm is larger than the calculated one for the device with d = 120 nm, which is in agreement with the result that a thicker TiO2 film leads to a higher series resistance and a lower photocurrent [11].

As for the devices with different polymer thicknesses (l) (Figure 5b), the similar dependence of the dissociation efficiency ηCT on the applied voltage is obtained, i.e., a higher the forward electric field results in a larger exciton dissociation efficiency ηCT. However, the thicker polymer film leads to a much smaller exciton dissociation efficiency in the whole applied voltage region. It is very likely due to the slower hole transfer rate in the polymer film as a result of the weakened internal electric field by the increased polymer film thickness, which leads to the smaller exciton dissociation rate at the D/A interface and further the lower exciton dissociation efficiency [5,51].

Figure 5c shows the influences of various incident intensities on the exciton dissociation efficiency ηCT. It is found that ηCT decreases with increasing the incident intensity at same applied voltage. The similar phenomenon that the efficiency of charge separation per incident photon decreases with increasing the incident light intensity has also been observed in bilayer TiO2/PdTPPC [16] and TiO2/P3HT [40] cells in the absence of internal electric field, and was attributed to the occurrence of exciton-exciton annihilation within the polymer layer. In our case, this phenomenon can be understood as follows. Although a higher incident intensity creates more excitons in the polymer layer and generates higher free electron and hole densities at the D/A interface, the higher densities of the charge carriers at the interface increases the charge recombination probability at the same time; moreover, as discussed above, the increasing forward applied voltage will enhance the exciton dissociation efficiency at the D/A interface. In other words, there is a competition between exciton dissociation and charge recombination at the D/A interface and the last result is that the exciton dissociation efficiency ηCT decreases as shown in Figure 5. This important result indicates that the increase in the photocurrent density under a higher incident light intensity is due to the increase in exciton density rather than the increase in the exciton dissociation efficiency, which is useful to optimize device performance.

Conclusions

An analytical model for the photocurrent-voltage (Jph-V) characteristics of the bilayer polymer/TiO2 photovoltaic cells is developed, where the generation of free charges takes place via dissociation of photogenerated excitons. The model describes the dependence of photocurrent generation on the device geometry and gives an analytical expression for the exciton dissociation efficiency. The experimental Jph-V data of the MEH-PPV/TiO2 devices are satisfactorily fitted to the model. Results show that increasing TiO2 or the polymer layer in thickness will reduce the exciton dissociation efficiency ηCT in the device and further the photocurrent. It is found that the photocurrent is determined by the competition between the exciton dissociation and charge recombination at the D/A interface, and the increase in photocurrent under a higher incident light intensity is due to the increased exciton density rather than the increase in the efficiency ηCT. Our results indicate that a thinner polymer layer combined with a thinner TiO2 layer favors the higher exciton dissociation efficiency in the bilayer devices. The model will provide information on optimization of device performance by investigating the effects of material parameters on device characteristics.

Abbreviations

A: acceptor; CIMPS: controlled intensity modulated photo spectroscopy; D: donor; HOMO: highest-occupied molecular orbital; ITO: indium tin oxide; LED: light-emitting diode; MC: Monte Carlo; PV: photovoltaic; TiO2: titanium dioxide.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

CC performed the experiments, developed the theory model, and drafted the manuscript. FW participated the theoretical analysis. HG and WS participated the device preparation. MW conceived of the study, and participated in its design and coordination. All authors read and approved the final manuscript.

Acknowledgements

This work was supported by the "100-talent Program" of Chinese Academy of Sciences, the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry, and the President Foundation of Hefei Institute of Physical Sciences.

References

  1. Coakley KM, McGehee MD: Conjugated polymer photovoltaic cells.

    Chem Mater 2004, 16:4533-4542. Publisher Full Text OpenURL

  2. Benanti TL, Venkataraman D: Organic solar cells: An overview focusing on active layer morphology.

    Photosynth Res 2006, 87:73-81. PubMed Abstract | Publisher Full Text OpenURL

  3. Günes S, Neugebauer H, Sariciftci NS: Conjugated polymer-based organic solar cells.

    Chem Rev 2007, 107:1324-1338. PubMed Abstract | Publisher Full Text OpenURL

  4. Kwong CY, Choy WCH, Djurisic AB, Chui PC, Cheng KW, Chan WK: Poly(3-hexylthiophene):TiO2 nanocomposites for solar cell applications.

    Nanotechnology 2004, 15:1156-1161. Publisher Full Text OpenURL

  5. Breeze AJ, Schlesinger Z, Carter SA, Brock PJ: Charge transport in TiO2/MEH-PPV polymer photovoltaics.

    Phys Rev B 2001, 64:125205. OpenURL

  6. Coakley KM, Liu YX, McGehee MD, Frindell KL, Stucky GD: Infiltrating semiconducting polymer into self-assembled mesoporous titania films for photovoltaic applications.

    Adv Funct Mater 2003, 13:301-306. Publisher Full Text OpenURL

  7. Beek WJE, Wienk MM, Janssen RAJ: Efficient hybrid solar cells from zinc oxide nanoparticles and conjugated polymer.

    Adv Mater 2004, 16:1009-1013. Publisher Full Text OpenURL

  8. Alem S, Bettignies RD, Nunzi JM: Efficient polymer-based interpenetrated network photovoltaic cells.

    Appl Phys Lett 2004, 84:2178-2180. Publisher Full Text OpenURL

  9. Beek WJE, Wienk MM, Kemerink M, Yang M, Janssen RAJ: Hybrid zinc oxide conjugated polymer bulk heterojunction solar cells.

    J Phys Chem B 2005, 109:9505-9516. PubMed Abstract | Publisher Full Text OpenURL

  10. Sun B, Snaith HJ, Dhoot AS, Westenhoff S, Greenham NC: Vertically segregated hybrid blends for photovoltaic devices with improved efficiency.

    J Appl Phys 2005, 97:014914. Publisher Full Text OpenURL

  11. Daoud WA, Turner ML: Evect of interfacial properties and Wlm thickness on device performance of bilayer TiO2-poly(1,4-phenylenevinylene) solar cells prepared by spin coating.

    React Funct Polym 2006, 66:13-20. Publisher Full Text OpenURL

  12. Savenije TJ, Warman JM, Goossens A: Visible light sensitisation of titanium dioxide using a phenylene vinylene polymer.

    Chem Phys Lett 1998, 287:148-153. Publisher Full Text OpenURL

  13. Arango AC, Carter SA, Brock PJ: Charge transfer in photovoltaics consisting of interpenetrating networks of conjugated polymer and TiO2 nanoparticles.

    Appl Phys Lett 1999, 74:1698-1700. Publisher Full Text OpenURL

  14. Koehler M, Santos MC, da Luz MGE: Positional disorder enhancement of exciton dissociation at donor/acceptor interface.

    J Appl Phys 2006, 99:053702. Publisher Full Text OpenURL

  15. Offermans T, Meskers SCJ, Janssen RAJ: Charge recombination in a poly(para-phenylene vinylene)-fullerenederivative composite film studied by transient, nonresonant, hole-burning spectroscopy.

    J Chem Phys 2003, 119:10924-10929. Publisher Full Text OpenURL

  16. Kroeze JE, Savenije TJ, Candeias LP, Warman JM, Siebbeles LDA: Triplet exciton diffusion and delayed interfacial charge separation in a TiO2/PdTPPC bilayer: Monte Carlo simulations.

    Sol Energy Mater Sol Cells 2005, 85:189-203. Publisher Full Text OpenURL

  17. Nelson J: Diffusion-limited recombination in polymer-fullerene blends and its influence on photocurrent collection.

    Phys Rev B 2003, 67:155209. OpenURL

  18. Peumans P, Forrest SR: Separation of geminate charge-pairs at donor-acceptor interfaces in disordered solids.

    Chem Phys Lett 2004, 398:27-31. Publisher Full Text OpenURL

  19. Watkins PK, Walker AB, Verschoor GLB: Dynamical monte carlo modelling of organic solar cells: The dependence of Internal quantum efficiency on morphology.

    Nano Lett 2005, 5:1814-1818. PubMed Abstract | Publisher Full Text OpenURL

  20. Marsh RA, Groves C, Greenham NC: A microscopic model for the behavior of nanostructured organic photovoltaic devices.

    J Appl Phys 2007, 101:083509. Publisher Full Text OpenURL

  21. Yang F, Forrest SR: Photocurrent generation in nanostructured organic solar cells.

    ACS Nano 2008, 2:1022-1032. PubMed Abstract | Publisher Full Text OpenURL

  22. Salafsky JS: Exciton dissociation, charge transport, and recombination in ultrathin, conjugated polymer-TiO2 nanocrystal intermixed composites.

    Phys Rev B 1999, 59:10885-10894. Publisher Full Text OpenURL

  23. Koster LJA, Smits ECP, Mihailetchi VD, Blom PWM: Device model for the operation of polymer/fullerene bulk heterojunction solar cells.

    Phys Rev B 2005, 72:085205. OpenURL

  24. Mihailetchi VD, Koster LJA, Hummelen JC, Blom PWM: Photocurrent generation in polymer-fullerene bulk heterojunctions.

    Phys Rev Lett 2004, 93:216601. PubMed Abstract | Publisher Full Text OpenURL

  25. Braker JA, Ramsdale CM, Greenham NC: Modeling the current-voltage characteristics of bilayer polymer photovoltaic devices.

    Phys Rev B 2003, 67:075205. OpenURL

  26. Marsh RA, Mcneill CR, Abrusci A, Campbell AR, Friend RH: A unified description of current-voltage characteristics in organic and hybrid photovoltaics under low light intensity.

    Nano Lett 2008, 8:1393-1398. PubMed Abstract | Publisher Full Text OpenURL

  27. Gowrishankar V, Scully SR, McGehee MD, Wang Q, Branz HM: Exciton splitting and carrier transport across the amorphous-silicon/polymer solar cell interface.

    Appl Phys Lett 2006, 89:252102. Publisher Full Text OpenURL

  28. Yang J, Shalish I, Shapira Y: Photoinduced charge carriers at surfaces and interfaces of poly [2-methoxy-5-(2'-ethyl-hexyloxy)-1,4-phenylene vinylene] with Au and GaAs.

    Phys Rev B 2001, 64:035325. OpenURL

  29. Greenham NC, Peng X, Alivisatos AP: Charge separation and transport in conjugated-polymer/semiconductor-nanocrystal composites studied by photoluminescence quenching and photoconductivity.

    Phys Rev B 1996, 54:17628-17637. Publisher Full Text OpenURL

  30. Ginger DS, Greenham NC: Photoinduced electron transfer from conjugated polymers to CdSe nanocrystals.

    Phys Rev B 1999, 59:10622-10629. Publisher Full Text OpenURL

  31. Kim SS, Jo J, Chun C, Hong JC, Kim DY: Hybrid solar cells with ordered TiO2 nanostructures and MEH-PPV.

    J Photochem Photobiol A Chem 2007, 188:364-370. Publisher Full Text OpenURL

  32. Blom PWM, Mihailetchi VD, Koster LJA, Markov DE: Device physics of polymer:fullerene bulk heterojunction solar cells.

    Adv Mater 2007, 19:1551-1566. Publisher Full Text OpenURL

  33. Koehler M, Roman LS, Inganäs O, da Luz MGE: Modeling bilayer polymer/fullerene photovoltaic devices.

    J Appl Phys 2004, 96:40-43. Publisher Full Text OpenURL

  34. Veldman D, Ipek Ö, Meskers SCJ, Sweelssen J, Koetse MM, Veenstra SC, Kroon JM, Bavel SSV, Loos J, Janssen RAJ: Compositional and Electric Field Dependence of the dissociation of charge transfer excitons in alternating polyfluorene copolymer/fullerene blends.

    J Am Chem Soc 2008, 130:7721-7735. PubMed Abstract | Publisher Full Text OpenURL

  35. Kalinowski J, Godlewski JS: spatial behaviour of the charge created at the illuminated interface molecular crystal/electrolyte.

    Chem Phys 1978, 32:201-213. Publisher Full Text OpenURL

  36. Kalinowski J, Godlewski J: Singlet exciton-charge carrier interaction in anthracene crystals.

    Phys Status Solidi (b) A 1974, 65:789-796. Publisher Full Text OpenURL

  37. Hieda H, Tanaka K, Naito K, Gemma N: Fluorescence quenching induced by injected carriers in organic thin films.

    Thin Solid Films 1998, 331:152-157. Publisher Full Text OpenURL

  38. Bulorić V, Forrest SR: Study of localized and extended excitons in 3,4,9,10-perylenetetra-carboxylic dianhydride (PTCDA) II. Photocurrent response at low electric fields.

    Chem Phys 1996, 210:13-25. Publisher Full Text OpenURL

  39. Gregg BA, Hanna MC: Comparing organic to inorganic photovoltaic cells: Theory, experiment, and simulation.

    J Appl Phys 2003, 93:3605-3614. Publisher Full Text OpenURL

  40. Kroeze JE, Savenije TJ, Vermeulen MJW, Warman JM: Contactless determination of the photoconductivity action spectrum, exciton diffusion length, and charge separation efficiency in polythiophene-sensitized TiO2 bilayers.

    J Phys Chem B 2003, 107:7696-7705. Publisher Full Text OpenURL

  41. Groves C, Marsh RA, Greenham NC: Electric-field dependent redox electron transfer in an organic solid: study of carrier photogeneration efficiency.

    J Chem Phys 2008, 129:114903. PubMed Abstract | Publisher Full Text OpenURL

  42. Umeda M, Nishizawa M, Itoh T, Selman JR, Uchida I: Enhanced electroluminescence of poly(2-methoxy-5-(2'-ethylhexyloxy)-1, 4-phenylene vinylene) films in the presence of TiO2 nanocrystals.

    Chem Phys Lett 2000, 326:219-224. Publisher Full Text OpenURL

  43. Weng CC, Chou CH, Wei KH, Huang JY: On pre-breakdown phenomena in insulators and electronic semi-conductors.

    J Polym Res 2006, 13:229-235. Publisher Full Text OpenURL

  44. Frenkel J: Temperature and electric-field dependences of hole mobility in light-emitting diodes based on poly [2-methoxy-5-(2-ethylhexoxy)-1,4-phenylene vinylene].

    Phys Rev 1938, 54:647-648. Publisher Full Text OpenURL

  45. Kumar A, Bhatnagar PK, Mathur PC, Husain M, Sengupta S, Kumar J: Charge carrier transport and recombination at the interface between disordered organic dielectrics.

    J Appl Phys 2005, 98:024502. Publisher Full Text OpenURL

  46. Arkhipov VI, Emelianova EV, Bässler H: Charge carrier generation and electron blocking at interlayers in polymer solar cells.

    J Appl Phys 2001, 90:2352-2357. Publisher Full Text OpenURL

  47. Petrozza A, Groves C, Snaith HJ: Electron transport and recombination in dye-Sensitized mesoporous TiO2 probed by photoinduced charge-conductivity modulation spectroscopy with monte carlo modeling.

    J Am Chem Soc 2008, 130:12912-12920. PubMed Abstract | Publisher Full Text OpenURL

  48. Yin C, Pieper B, Stiller B, Kietzke T, Neher D: Efficient solar cells from layered nanostructures of donor and acceptor conjugated polymers.

    Appl Phys Lett 2007, 90:133502. Publisher Full Text OpenURL

  49. van de Krol R, Goossens A, Schoonman J: Polymer-TiO2 solar cells: TiO2 interconnected network for improved cell performance.

    J Electrochem Soc 1997, 144:1723-1727. Publisher Full Text OpenURL

  50. Alam MM, Jenekhe SA: Efficient solar cells from layered nanostructures of donor and acceptor conjugated polymers.

    Chem Mater 2004, 16:4647-4656. Publisher Full Text OpenURL

  51. Oey CC, Djurišić AB, Wang H, Man KKY, Chan WK, Xie MH, Leung YH, Pandey A, Nunzi J-M, Chui PC: Polymer-TiO2 solar cells: TiO2 interconnected network for improved cell performance.

    Nanotechnology 2006, 17:706-713. Publisher Full Text OpenURL