Open Access Nano Idea

Organic electrochemical transistors based on a dielectrophoretically aligned nanowire array

WooSeok Choi1, Taechang An1 and Geunbae Lim12*

Author Affiliations

1 Department of Mechanical Engineering, POSTECH, 790-784 Pohang, Republic of Korea

2 Division of Integrative Bioscience and Biotechnology, POSTECH, 790-784 Pohang, Republic of Korea

For all author emails, please log on.

Nanoscale Research Letters 2011, 6:339  doi:10.1186/1556-276X-6-339


The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/6/1/339


Received:5 November 2010
Accepted:14 April 2011
Published:14 April 2011

© 2011 Choi et al; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

In this study, we synthesized an organic electrochemical transistor (OECT) using dielectrophoresis of a carbon nanotube-Nafion (CNT-Nafion) suspension. Dielectrophoretically aligned nanowires formed a one-dimensional submicron bundle between triangular electrodes. The CNT-Nafion composite nanowire bundles showed p-type semiconductor characteristics. The drain-source current decreased with increasing gate voltage. The nanowire bundles showed potential as pH sensor because the drain-source current ratio varied linearly according to the gate voltage in pH buffers.

Background

Recently, there has been significant research in the area of organic thin-film transistors (OTFTs), because of the many benefits of organic semiconductors, such as structural flexibility, low temperature processing, and low cost [1-7]. Organic electrochemical transistors (OECTs), a subset of OTFTs, have been considered as sensors because of their ability to operate in aqueous environments with relatively low voltages and their integration with microfluidics. Furthermore, one can to get information on additional dimensions using gate-induced modulation, compared with two-terminal devices [5-12]. In particular, OECTs, formed using one-dimensional nanostructures, such as nanotubes and nanowires, are more attractive for use as chemical and biological sensors because of their large surface-to-volume ratio, light weight, and controllable transport properties [10-13].

Recently, we have developed a real-time, label-free, step-wise, and target-specific aptasensor for protein molecules using dielectrophoretically aligned single-walled carbon nanotube (SWNT) films between patterned cantilever electrodes. We used the SWNT film as a two-terminal resistive sensor and demonstrated its excellent performance for detecting thrombin and vascular endothelial growth factor (VEGF). We verified that the SWNT film had p-type semiconductor properties in a phosphate buffer solution at pH 5.6 using blank electrodes of the cantilever array as gate electrodes [14]. The structure of this device can be adapted for OECTs composed of semiconducting material between two electrodes and a remote gate electrode in the surrounding electrolyte solutions (Figure 1) [10-12]. This fabrication method is applicable to other materials under positive dielectrophoretic conditions. In addition, CNTs offer mechanical support to the organic materials, and their composites can improve electrical properties, such as conductivity, conductance, and electronic transport [15-20]. Our objective was to synthesize CNT composite nanowires aligned between electrodes using dielectrophoresis and to exploit them as OECTs for sensor applications.

thumbnailFigure 1. Schematic diagram of an organic electrochemical transistor based on a CNT-Nafion nanowire bundle.

In this article, we report the fabrication of CNT composite nanowires with Nafion, a well-known proton conductor [21,22] and the use of CNT-Nafion composite nanowires as electrochemical transistors in various pH buffers.

Results and discussion

Figure 2 shows the CNT-Nafion nanowire synthesis using dielectrophoresis. CNTs and Nafion molecules were gathered between the electrodes where the electric-field gradient was larger, because of their higher conductivity compared with the surrounding medium (Figure 2a). After the suspension was partially removed, the remaining suspension was compressed to form a concave meniscus with evaporation due to the surface tension between the electrodes and suspension (Figure 2b). As a result, the electric current was concentrated through the compressed CNTs and the surrounding Nafion, which bonded the CNT in the shape of the solution. A nanowire bundle with a submicron diameter was synthesized (Figure 2c).

thumbnailFigure 2. Microscope images of the CNT/Nafion nanowire fabrication process. (a) Attraction of the CNT and Nafion molecules between electrodes with an AC electric field; (b) compression of the CNT and Nafion by suspension evaporation; (c) A CNT-Nafion composite nanowire synthesized between electrodes.

Figure 3a, b shows a scanning electron microscope (SEM) image of a CNT bundle, and Figure 3c, d shows Nafion-coated CNT bundles. The Nafion wrapped the CNT bundle entirely, while CNT gathered individually. Figure 3e shows the energy dispersive X-ray spectroscopy (EDS) graph of CNT-Nafion nanowire bundles, which were 10% fluorine due to the Nafion composition. Immediately after synthesizing the nanowire bundles, the resistance of the CNT bundles was approximately 5 kΩ. In contrast, that of the CNT-Nafion bundles was found to be approximately 2 kΩ. Based on the SEM image, EDS graph, and electrical properties, the nanowire bundles synthesized were likely CNT-Nafion composites. As we reported previously [14], the SWNT-film was synthesized uniformly between flat cantilever electrodes; however, CNT-Nafion nanowires were synthesized between triangular electrodes. Because the electric field was concentrated at the end of the electrode, and a thin concave meniscus formed during evaporation, the nanowire bundles had submicron diameters, rather than a film structure. This fabrication technique is based on the bottum-up method; consequently, it is a simple method for fabricating CNT nanowire composites using dielectrophoresis.

thumbnailFigure 3. Difference of CNT and CNT-Nafion composite nanowire bundles. SEM image of (a, b) CNT nanowire bundles and (c, d) CNT-Nafion composite nanowire bundles. (e) EDS analysis of the CNT-Nafion nanowire bundles.

Figure 4a, b shows the characteristic drain current (IDS) versus drain voltage (VDS) curves at different gate voltages (VG) in 5 μL of a phosphate-buffered saline (PBS) droplet for CNT-Nafion nanowires and blank electrodes, respectively. Figure 4c plots the gate current (IG) versus VDS for CNT-Nafion nanowires under the same conditions. The maximum value of IDS for the nanowire transistor was approximately 700 μA at VG = 0.5 V. The leakage current, IDS at the blank electrodes and IG were at the most 0.2 μA. The leakage current through the electrolyte was negligible because the IDS value at the blank electrode and IG were approximately one thousand times smaller than the current through the CNT-Nafion nanowires. The value of IDS decreased with increasing electrolyte gate bias (Figure 4a), indicating that the holes were the primary charge-carriers in the CNT-Nafion composite nanowires. That is, they exhibited p-type characteristics in the buffer solutions [12,23]

thumbnailFigure 4. Verification of CNT-Nafion nanowire electrochemical transistors. Characteristic curves of IDS versus VDS for (a) electrochemical transistors based on dielectrophoretically-aligned CNT-Nafion nanowire bundles and (b) blank electrodes in 1 × PBS buffer (pH 7.2). (c) Characteristic curves of IG versus VDS for the electrochemical transistors under the same conditions.

To investigate the influence of protons on the characteristics of CNT-Nafion composites, we measured the drain current with increasing gate voltage from 0 to 0.2 V while VDS was fixed at 0.5 V in various pH buffers. Figure 5a shows the normalized IDS divided by the drain-source current when VG = 0 V versus gate voltage characteristic curves in different pH buffers. As expected, because holes were the primary charge-carriers, the normalized drain-current decreased steeperly with increasing gate voltage under high proton concentrations (lower pH). The normalized drain current to gate voltage ratio was linearly dependent on the buffer pH (Figure 5b).

thumbnailFigure 5. Characteristics of CNT-Nafion nanowire electrochemical transistors due to pH. (a) Normalized IDS versus VG characteristc curves in various pH buffers when VDS = 0.5 V. (b) Ratio of the normalized drain current to the gate voltage plotted against the pH of the CNT-Nafion nanowire electrochemical transistors.

Conclusions

We fabricated organic chemical transistors based on CNT-Nafion composite nanowires using dielectrophoresis. These composite nanowires had p-type semiconductor characteristics in aqueous media, and the drain-current to gate voltage ratio was proportional to the buffer pH. Because the synthesis of nanowire bundles occurred at electrodes with an applied electric field, and various organic materials have the potential to form composites with CNT, one can synthesize an individually addressable CNT composite nanowire array.

Methods

CNT-Nafion nanowires were synthesized between cantilever electrodes that were fabricated using a traditional MEMS technique. These electrodes were fabricated using a standard lift-off process. A gold layer (2000 Å) was deposited with a chrome layer (200 Å) as an adhesion layer using an e-beam evaporator on a silicon substrate covered with 1 μm of low-stress silicon nitride using low-pressure chemical vapor deposition (LPCVD). For the cantilever structure, the silicon nitride was etched using standard reactive ion etching (RIE), and the silicon was etched using isotropic wet etching using RSE-200 etchant. The SWNTs with 1.0-1.2 nm diameters and lengths of 5-20 μm were purchased from Ilgin Nanotech, and a SWNT-COOH suspension was prepared by oxidizing the CNTs in a strong acid with sonication [24]. Nafion was purchased from Aldrich and was used without purification. The CNT-Nafion solutions were prepared by combining 3 μL Nafion solution and 200 μL CNT-COOH suspension with sonication for 10 min.

The CNT-Nafion solution was placed on the cantilever electrodes, and an AC voltage of 1 MHz and 10 V peak-to-peak was applied. The SWNTs and monomers were aligned between the cantilever electrodes by the dielectrophoretic force. The SWNT-Nafion solution was removed partially while maintaining the AC electric field and the SWNT-Nafion nanowire bundles were synthesized as the remaining solution evaporated.

Figure 1 shows a schematic of the electrochemical transistors, which consisted of two Au electrodes connected by CNT-Nafion nanowires and a remote Ag/AgCl gate electrode immersed in an electrolyte droplet. The electrochemical transistors were characterized in pH buffers using Samchun Chemical at room temperature using a semiconductor analyzer (HP4156A, Hewlett-Packard).

Abbreviations

CNT-Nafion: carbon nanotube-Nafion; EDS: energy dispersive X-ray spectroscopy; LPCVD: low-pressure chemical vapor deposition; OECT: organic electrochemical transistor; OTFTs: organic thin film transistors; PBS: phosphate-buffered saline; RIE: reactive ion etching; SEM: scanning electron microscope; SWNT: single-walled carbon nanotube; VEGF: vascular endothelial growth factor.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

WSC and GL conceived of the study, and participated in its design and coordination. WSC and TA carried out the experiments. WSC drafted the manuscript. All authors read and approved the final manuscript.

Acknowledgements

This study was supported by the Mid-career Researcher program through NRF grant funded by the MEST (No. 2009-0085377), the World Class University program through the National Research Foundation of Korea funded by the Ministry of Education, Science and Technology (R31-2008-000-10105-0), and Development of Intelligent Robot Technology for Total Clinical System based (10024733) under the Industrial Source Technology Development Programs of the MKE of Korea.

References

  1. Katz HE: Organic molecular solids as thin film transistor semicoductors.

    J Mater Chem 1997, 7:369. Publisher Full Text OpenURL

  2. Sheraw CD, Zhou L, Huang JR, Gundlach DJ, Jackson TN: Organic thin-film transistor-driven polymer dispersed liquid crystal display on flexible polymeric substrates.

    Appl Phys Lett 2002, 80:1088. Publisher Full Text OpenURL

  3. Bartic C, Borghs G: Organic thin-film transistors as transducers for (bio)analytical applications.

    Anal Bioanal Chem 2006, 384:354. PubMed Abstract | Publisher Full Text OpenURL

  4. Stricker JT, Gudmundsdóttir AD, Smith AP, Taylor BE, Durstock MF: Fabrication of organic thin-film transistors using layer-by-layer assembly.

    J Phys Chem B 2007, 111:6322. PubMed Abstract | Publisher Full Text OpenURL

  5. Mabeck JT, Malliaras GG: Chemical and biological sensors based on organic thin-film transistors.

    Anal Bioanal Chem 2006, 384:343. PubMed Abstract | Publisher Full Text OpenURL

  6. Bernards DA, Malliaras GG: Steady-state and transient behavior of organic electrochemical transistors.

    Adv Funct Mater 2007, 17:3538. Publisher Full Text OpenURL

  7. Lin P, Yan F, Chan HLW: Ion-sensitive properties of organic electrochemical transistors.

    Appl Mater Interfaces 2010, 2:1637. Publisher Full Text OpenURL

  8. Jamalizadeh M, Shari F, Moaiyeri MH, Navi K, Hashemipour O: Five new MVL current mode differential absolute value circuits based on carbon nano-tube field effect transistors (CNTFETs).

    Nano-Micro Lett 2010, 2:227. OpenURL

  9. Roberts ME, Mannsfeld SCB, Queraltó N, Reese C, Locklin J, Knoll W, Bao Z: Water-stable organic transistors and their application in chemical and biological sensors.

    Proc Natl Acad Sci USA 2008, 105:12134. PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  10. Krüger M, Buitelaar MR, Nussbaumer T, Schönenberger C: Electrochemical carbon nanotube field effect transistor.

    Appl Phys Lett 2001, 78:1291. OpenURL

  11. Rosenblatt S, Yaish Y, Park J, Gore J, Sazonova V, McEuen P: High performance electrolyte gated carbon nanotube transistors.

    Nano Lett 2002, 2:869. Publisher Full Text OpenURL

  12. Alam MM, Wang J, Guo Y, Lee SP, Tseng HR: Electrolyte gated transistors based on conducting polymer nanowire junction arrays.

    J Phys Chem B 2005, 109:12777. PubMed Abstract | Publisher Full Text OpenURL

  13. Lee SY, Choi GR, Lim H, Lee KM, Lee SK: Electronic transport characteristics of electrolyte-gated conducting polyaniline nanowire field-effect transistors.

    Appl Phys Lett 2009, 95:013113. Publisher Full Text OpenURL

  14. An T, Kim K, Hahn SK, Lim G: Real-time, step-wise, electrical detection of protein molecules using dielectrophoretically aligned SWNT-film FET aptasensors.

    Lab Chip 2010, 10:2052. PubMed Abstract | Publisher Full Text OpenURL

  15. Huges M, Chen GZ, Shaffer MSP, Fray DJ, Windle AH: Electrochemical capacitance of a nanoporous composite of carbon nanotubes and polypyrrole.

    Chem Mater 2002, 14:1610. Publisher Full Text OpenURL

  16. An KH, Jeon KK, Heo JK, Lim SC, Bae DJ, Lee YH: High capacitance supercapacitor using nanocomposite electrode of SWNT and PPy.

    J Electrochem Soc 2002, 14:a1058. Publisher Full Text OpenURL

  17. Chen HW, Wu RJ, Chan KH, Sun YL, Su PG: The application of CNT/Nafion composite material to low humidity sensing measurement.

    Sens Actuators B 2005, 104:80. Publisher Full Text OpenURL

  18. Sivakkumar SR, Ko JM, Kim DY, Kim BC, Wallace GG: Performance evaluation of CNT/PPy/MnO2 composite electrodes for electrochemical capacitors.

    Electrochim Acta 2007, 52:7377. Publisher Full Text OpenURL

  19. Chen HZ, Bai R, Cao L, Xu HB, Xu WJ, Wang M: CNT-base organic-inorganic composite materials with optoelectronic functionality.

    Res Chem Intermed 2008, 34:115. Publisher Full Text OpenURL

  20. Baba A, Sato F, Fukuda N, Ushijima H, Yase K: Micro/nanopatterning of single-walled carbon nanotube-organic-organic semiconductor composites.

    Nanotechnology 2009, 20:085301. PubMed Abstract | Publisher Full Text OpenURL

  21. Opekar F, Štulík K: Electrochemical sensors with solid polymer electrolytes.

    Anal Chim Acta 1999, 385:151. Publisher Full Text OpenURL

  22. Nilssoon D, Krugler T, Svensson PO, Berggren M: An all-organic sensor-transistor based on a novel electrochemical transducer concept printed electrochemical sensors on paper.

    Sens Actuators B 2002, 86:193. Publisher Full Text OpenURL

  23. Snow ES, Novak JP, Lay MD, Perkins FK: 1/f noise in single-walled carbon nanotube devices.

    Appl Phys Lett 2004, 85:4172. Publisher Full Text OpenURL

  24. Chang-Rong JT, Pastorin G: The influence of carbon nanotubes on enzyme activity and structure: investigation of different immobilization procedures through enzyme kinetics and circular dichroism studies.

    Nanotechnology 2009, 20:255102. PubMed Abstract | Publisher Full Text OpenURL