Enhanced plasmonic behavior of bimetallic (Ag-Au) multilayered spheres

Ovidio Peña-Rodríguez1* and Umapada Pal2

Author Affiliations

1 Institut de Ciència de Materials de Barcelona (ICMAB-CSIC), Campus UAB, Bellaterra, Barcelona, 08193, Spain

2 Instituto de Física, Benemérita Universidad Autónoma de Puebla, Apartado Postal J-48, Puebla, Puebla 72570, México

For all author emails, please log on.

Nanoscale Research Letters 2011, 6:279  doi:10.1186/1556-276X-6-279

The electronic version of this article is the complete one and can be found online at: http://www.nanoscalereslett.com/content/6/1/279


Received:6 December 2010
Accepted:4 April 2011
Published:4 April 2011

© 2011 Peña-Rodríguez and Pal; licensee Springer.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

In this article we study the plasmonic behavior of some stable, highly biocompatible bimetallic metal-dielectric-metal (MDM) and double concentric nanoshell (DCN) structures. By simply switching the material of the inner structure from Au to Ag, the intensity of their surface plasmon resonance could be increased in the optical transparency region of the human tissues up to 20 and 60 percent for the MDM and DCN, respectively, while the biocompatibility is retained. The obtained results indicate that these novel structures could be highly suitable for surface enhanced Raman scattering and photothermal cancer therapy.

Background

Surface plasmon resonance (SPR), which comes from the collective oscillation of conduction electrons, dominates the optical spectra of metallic nanoparticles (NPs), making them attractive for many potential applications. For example, the dependence of their SPR frequency on the dielectric constant of embedding medium [1] can be used for cancer treatments [2,3], and biological or chemical sensing [4-6]. Moreover, the intense electromagnetic fields produced by the SPR in the surroundings of the nanoparticle are essential in surface-enhanced Raman scattering (SERS) [7], which in turn has important applications in areas such as medical diagnostics [8] and immunoassay [9,10].

Traditionally, gold and silver have been the preferred materials for the synthesis of nanoparticles [11-14], and both of them have some advantages and disadvantages. Gold NPs are easier to synthesize, have better biocompatibility and long-term stability but silver NPs have a more intense SPR, which is of great advantage for SERS and sensing applications. On the other hand, it can be attractive [15] to use bimetallic NPs, where the advantages of both materials can be combined to obtain structures with improved optical response. Nevertheless, while it has been demonstrated [15] that three-layered nanoshells of SiO2-Au-Ag can theoretically improve their optical response, those structures present some practical problems related to the difficulty of maintaining separate gold and silver layers, as they tend to form alloys [16-18].

Multilayered nanoshells or nanomatryushkas are a new kind of particles which have been synthesized recently [19-21], and studied theoretically [22-25]. In addition to their better SPR tunability, there appears no problem of alloying in such nanostructures as the metallic layers are separated by dielectric ones. In spite of this potential advantage, there exists no systematic study in literature on the advantages of replacing monometallic multilayered structures with bimetallic ones.

In this work, we have used classical Mie calculations [26-28] to study two different kinds of bimetallic multilayered nanoshells: metal-dielectric-metal (MDM) structures and double concentric nanoshells (DCNs). The bulk values of Ag and Au dielectric functions reported by Johnson and Christy [29] were used to calculate their optical responses after applying the usual size correction [30]. It has been observed that the configurations containing silver at the inner layer and gold at the outer are particularly advantageous as the SPR intensity can be increased without compromising biocompatibility and stability of the nanoparticles. Obtained results have been explained in terms of the theory of plasmon hybridization. These bimetallic structures could be used as excellent replacements for monometallic ones in most sensing and SERS-based applications.

Procedure

In the present article, we have studied bimetallic MDM structures and DCNs with geometries as shown in Figure 1a, where ri and ti (i = 0, ..., 3) are the radii and thicknesses of the ith layer (for the MDM structure r0 = t0 = 0). The extinction efficiencies for the different configurations were calculated by means of Scattnlay [28], a computer implementation of the algorithm developed by Yang [31] for the calculation of the scattering of EM radiation by a multilayered sphere. Moreover, in order to explain the observed shifts of the SPR, we have used a complementary, mainly qualitative method which has been developed recently: the theory of plasmon hybridization [20]. In this approach the characteristics of the SPR are explained in terms of the interactions between the plasmons of metallic nanostructures with simpler shapes. For instance, the SPR of metallic nanoshells can be understood from the coupling between the plasmons modes of a sphere (|ωs〉) and a cavity (|ωc〉), where two new plasmon oscillation modes are created: a higher energy (antibonding) mode (|ω+〉) and a lower energy (bonding) mode (|ω-〉), corresponding to the antisymmetric and symmetric interactions between the |ωs〉 and |ωc〉 modes, respectively.

thumbnailFigure 1. Schematic representation of the MDM and DCN structures. (a) Schematic representation of the studied MDM and DCN structures (for the MDM r0 = t0 = 0) and (b) their corresponding energy diagrams, representing plasmon hybridization.

The energy level diagram for plasmon hybridization in the studied MDM (red) and DCN (blue) structures is depicted in Figure 1b. The plasmon resonance in a MDM [DCN] structure can be viewed as the interaction between the plasmon responses of the inner sphere [nanoshell] (|ωs〉 [ and ]) and the outer ( and ) nanoshell. Three hybridized modes are obtained for the MDM, the energy mode corresponds to the antisymmetric coupling between the symmetric plasmon resonance modes of the outer () nanoshell and the sphere plasmon. The coupling between the higher-energy antibonding mode of the outer nanoshell and the nanosphere plasmon modes is very weak and only one hybridized mode is produced in this case (). In contrast, four hybridized modes are produced in the DCN structure because its inner nanoshell has two energy modes. The energy mode () corresponds to the antisymmetric (symmetric) coupling between the symmetric plasmon resonance modes of the inner () and outer () nanoshells. On the other hand, the energy mode () corresponds to the symmetric (antisymmetric) coupling between the antisymmetric plasmon resonance modes of the inner () and outer () nanoshells (Figure 1c). Although, in principle, there exists also a coupling between the antisymmetric and symmetric plasmons of the separate nanoshells, it has only a small influence on the hybridized modes, due to the large energy separation between those two modes [20].

The characteristics of the surface plasmon resonance obtained for the multilayer structures studied in this work primarily depend on the properties of the SPR of the two constituents metal layers (their composition and thickness) and the strength of the coupling between them (defined by the thickness of the dielectric layer that separates them). Since the dependence of the optical response in terms of geometrical parameters has been previously studied in detail for both structures [22,23], we focus only on the influence of the composition. For this, we have selected a configuration where both the dielectric layer thickness and the total size of the particles are constant, while the thickness of the metal layers is simultaneously varied (inversely), in order to obtain an opposite behavior between the inner and outer energy modes (one red-shifts when the other does the contrary). For this configuration, the optical response of the bimetallic nanostructures can be tuned to find an optimum relation between t1 and t3 yielding the maximum gain in intensity for a given red-shift. Moreover, the optical response can be analyzed across the full range where it can vary in a single simulation. Calculated values were compared with those obtained for the equivalent Au-only structures in both cases.

Results and discussion

The wavelength variations of extinction efficiency (Qext) for MDM and DCN structures of different compositions with a fixed thickness of 5 nm for all of its layers and embedded in water (n = 1.33) are shown in Figure 2. It can be seen that, with respect to the equivalent Au-only structures, the Au-Ag and Ag-only configurations have a more intense energy mode, but the mode is considerably less intense and blue-shifted. Additionally, the last two configurations are not advantageous for practical applications, due to the poor stability and biocompatibility of silver. On the other hand, the Ag-Au configuration with a more intense energy mode retains the advantages of Au structures, due to outer Au layer. The only drawback of the latter structures is a slight blue-shift of energy mode, which could easily be corrected by adjusting their geometrical parameters [22,23]. Considering these findings, we restrict our further studies only to the gains obtained by using the configurations containing Ag and Au at the inner and outer metallic shell, respectively, instead of their Au-only counterparts.

thumbnailFigure 2. Simulated extinction efficiency for MDM and DCN structures of various compositions. Simulated extinction efficiency as a function of the wavelength for (a) MDM and (b) DCN structures with a fixed thickness of 5 nm in all of its layers (for the MDM r0 = t0 = 0). Black, red, blue, and green lines correspond to the Au-Au, Ag-Au, Au-Ag, and Ag-Ag compositions, respectively.

The theoretical extinction efficiencies, calculated for fixed dielectric layers (5 nm) and the simultaneous inverse variations of t1 and t3 (t1 = 2, ..., 14 nm; t3 = 16 nm - t1) are shown in Figures 3 and 4 for the MDM and DCN structures, respectively. The spectra obtained as a function of t3 can be roughly divided into three regions. The first one corresponds to a very thin outer layer (below 5 nm); for which the and modes are widely separated. In this case, the position of the bonding (antibonding) mode of the composite structures is almost entirely controlled by the () mode. For this reason the bonding mode (the one we are interested in) is virtually identical for both compositions and the gain obtained in this case is quite small.

thumbnailFigure 3. Simulated extinction efficiency for Au-Au and Ag-Au MDM structures. Simulated extinction efficiency as a function of the wavelength for (a) Au-Au and (b) Ag-Au MDM structures, having t2 = 5 nm, while t1 and t3 are varied simultaneously (t1 = 2, ..., 14 nm; t3 = 16 nm - t1).

thumbnailFigure 4. Simulated extinction efficiency for Au-Au and Ag-Au DCN structures. Simulated extinction efficiency as a function of the wavelength for (a) Au-Au and (b) Ag-Au DCN structures, having t0 = t2 = 5 nm, while t1 and t3 are varied simultaneously (t1 = 2, ..., 14 nm; t3 = 16 nm - t1).

The intermediate region, which includes thicknesses of the outer layer ranging from 5 to 10 nm, is the most interesting because appreciable increases in the intensity of the mode are obtained for the bimetallic particles, at the expense of a small blue-shift. When both effects are weighted, a net gain of intensity is obtained, revealing the advantage of using bimetallic structures. The improvement in intensity can be explained by considering the characteristics of the geometry as well as the differences between the SPRs of silver and gold. Firstly, in this configuration the internal and external energy modes are closer to each other, resulting in a greater coupling between them, and consequently, both have some influence over the two hybridized modes. Moreover, the SPR of silver is considerably more intense than that of gold, and appears at higher energy (lower wavelength). Thus, the changes in the mode are driven by the increased influence of the inner metallic layer. Fortunately, the increase in intensity dominates over the red-shift, improving the optical response. On reducing the value of t3, the mode red-shifts, getting away from the mode and reducing their cross-influence over the hybridized modes, and then the differences in the mode between the Au-Au and Ag-Au configurations are erased (first region).

For the third region (t3 > 10 nm), again there are few differences between the two compositions; here the bonding hybridized mode keeps blue-shifting until it almost disappears, "absorbed" by the antibonding one. This effect is produced by the shielding caused by the thick outer layer, through which the light does not "see" the inner region and, therefore, the particle behaves almost like a single Au nanoshell.

Finally, in Figure 5, the variations of the extinction efficiency at the SPR maximum () as a function of its wavelength (λSPR), for the considered bimetallic structures are summarized. The region of transparency of the human tissues (700-1300 nm) is marked with vertical dashed lines. As can be seen, in spite of the differences in the intensity and red-shifts, the dependence of the energy mode on the geometrical parameters is essentially the same for both the MDM and DCN structures. Moreover, the intensity of their SPR bands is greater than the same for monometallic (Au-Au) structures in the 700-1300 nm spectral range. The gain in SPR intensity is particularly important in the region between 700 and 900 nm, which is up to 20 and 60 percent for the MDM and DCN, respectively. Therefore, these bimetallic nanoshell structures could be excellent replacements for the Au-only ones for bio-medical applications such as biosensors and cancer treatments [3].

thumbnailFigure 5. Summary of the variations of as a function of λSPR. Summary of the variations of the extinction efficiency at the SPR maximum () as a function of its wavelength (λSPR), for the studied MDM and DCN structures. The region of transparency of the human tissues (700-1300 nm) is marked with vertical dashed lines.

Conclusions

By manipulating structural parameters of bimetallic MDM (DCN) structures, a gain in intensity of mode up to 20 (60) percent can be achieved over their Au-only counterparts in the region of transparency of human tissues. The condition for such gains is that the outer metal layer has a thickness in the range of 5 to 10 nm; in this configuration the internal and external energy modes are closer, so that the interaction between them is greater and, consequently, both have some cross-influence over the hybridized modes. Thus, the energy mode "inherits" the spectral position of the energy mode of the outer metallic layer and the intensity of the inner one. Our designed bimetallic nanostructures could be more suitable than the conventional mono metallic nanoparticles and nanoshell structures for SERS and cancer therapy applications.

Abbreviations

DCN: double concentric nanoshell; MDM: metal-dielectric-metal; NPs: nanoparticles; SERS: surface enhanced Raman scattering; SPR: surface plasmon resonance.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

OPR conceived the study, performed the calculations and participated in the analysis of the results and writing the manuscript. UP supervised the study and participated in the analysis of the results and writing the manuscript. All authors read and approved the manuscript.

Acknowledgements

O. Peña-Rodríguez thanks DGAPA-UNAM and ICMAB-CSIC for extending a postdoctoral fellowship through the UNAM-CSIC agreement.

References

  1. Kelly KL, Coronado E, Zhao LL, Schatz GC: The optical properties of metal nanoparticles: the influence of size, shape, and dielectric environment.

    J Phys Chem B 2003, 107:668-677. OpenURL

  2. Hirsch LR, Stafford RJ, Bankson JA, Sershen SR, Rivera B, Price RE, Hazle JD, Halas NJ, West JL: Nanoshell-mediated near-infrared thermal therapy of tumors under magnetic resonance guidance.

    Proc Natl Acad Sci USA 2003, 100:13549-13554. OpenURL

  3. Zhang JZ: Biomedical applications of shape-controlled plasmonic nanostructures: a case study of hollow gold nanospheres for photothermal ablation therapy of cancer.

    J Phys Chem Lett 2010, 1:686-695. OpenURL

  4. Sun Y, Xia Y: Increased sensitivity of surface plasmon resonance of gold nanoshells compared to that of gold solid colloids in response to environmental changes.

    Anal Chem 2002, 74:5297-5305. OpenURL

  5. Cao M, Wang M, Gu N: Optimized surface plasmon resonance sensitivity of gold nanoboxes for sensing applications.

    J Phys Chem C 2009, 113:1217-1221. OpenURL

  6. Alivisatos P: The use of nanocrystals in biological detection.

    Nat Biotechnol 2004, 22:47-52. OpenURL

  7. Jackson JB, Halas NJ: Surface-enhanced Raman scattering on tunable plasmonic nanoparticle substrates.

    Proc Natl Acad Sci USA 2004, 101:17930-17935. OpenURL

  8. Allain LR, Vo-Dinh T: Surface-enhanced Raman scattering detection of the breast cancer susceptibility gene BRCA1 using a silver-coated microarray platform.

    Anal Chim Acta 2002, 469:149-154. OpenURL

  9. Hirsch LR, Jackson JB, Lee A, Halas NJ, West JL: A whole blood immunoassay using Gold nanoshells.

    Anal Chem 2003, 75:2377-2381. OpenURL

  10. Cui Y, Ren B, Yao J, Gu R, Tian Z: Synthesis of Agcore-Aushell bimetallic nanoparticles for immunoassay based on surface-enhanced Raman spectroscopy.

    J Phys Chem B 2006, 110:4002-4006. OpenURL

  11. Sönnichsen C, Alivisatos AP: Gold nanorods as novel nonbleaching plasmon-based orientation sensors for polarized single-particle microscopy.

    Nano Lett 2005, 5:301-304. OpenURL

  12. Raschke G, Brogl S, Susha AS, Rogach AL, Klar TA, Feldmann J, Fieres B, Petkov N, Bein T, Nichtl A, Kurzinger K: Gold nanoshells improve single nanoparticle molecular sensors.

    Nano Lett 2004, 4:1853-1857. OpenURL

  13. McFarland AD, Van Duyne RP: Single silver nanoparticles as real-time optical sensors with zeptomole sensitivity.

    Nano Lett 2003, 3:1057-1062. OpenURL

  14. Xu H, Käll M: Surface-plasmon-enhanced optical forces in Silver nanoaggregates.

    Phys Rev Lett 2002, 89:246802. OpenURL

  15. Wu D, Xu X, Liu X: Tunable near-infrared optical properties of three-layered metal nanoshells.

    J Chem Phys 2008, 129:074711. OpenURL

  16. Link S, Wang ZL, El-Sayed MA: Alloy formation of gold-silver nanoparticles and the dependence of the plasmon absorption on their composition.

    J Phys Chem B 1999, 103:3529-3533. OpenURL

  17. Moskovits M, Srnova-Sloufova I, Vlckova B: Bimetallic Ag-Au nanoparticles: extracting meaningful optical constants from the surface-plasmon extinction spectrum.

    J Chem Phys 2002, 116:10435-10446. OpenURL

  18. Fukutani H: Optical constants of silver-gold alloys.

    J Phys Soc Jpn 1971, 30:399-403. OpenURL

  19. Radloff C, Halas NJ: Plasmonic properties of concentric nanoshells.

    Nano Lett 2004, 4:1323-1327. OpenURL

  20. Prodan E, Radloff C, Halas NJ, Nordlander P: A hybridization model for the plasmon response of complex nanostructures.

    Science 2003, 302:419-422. OpenURL

  21. Xia X, Liu Y, Backman V, Ameer GA: Engineering sub-100 nm multi-layer nanoshells.

    Nanotechnology 2006, 17:5435-5440. OpenURL

  22. Wu D, Liu X: Tunable near-infrared optical properties of three-layered gold-silica-gold nanoparticles.

    Appl Phys B 2009, 97:193-197. OpenURL

  23. Peña-Rodríguez O, Pal U: Geometrical tunability of linear optical response of silica-gold double concentric nanoshells.

    J Phys Chem C 2010, 114:4414-4417. OpenURL

  24. Hasegawa K, Rohde C, Deutsch M: Enhanced surface-plasmon resonance absorption in metal-dielectric-metal layered microspheres.

    Opt Lett 2006, 31:1136-1138. OpenURL

  25. Khosravi H, Daneshfar N, Bahari A: Theoretical study of the light scattering from two alternating concentric double silica-gold nanoshell.

    Phys Plasmas 2010, 17:053302. OpenURL

  26. Mie G: Beiträge zur optik trüber medien, speziell kolloidaler metallösungen.

    Ann Phys 1908, 330:377-445. OpenURL

  27. Bohren CF, Huffman DR: Absorption and Scattering of Light by Small Particles. New York: Wiley-Interscience; 1998. OpenURL

  28. Peña O, Pal U: Scattering of electromagnetic radiation by a multilayered sphere.

    Comput Phys Commun 2009, 180:2348-2354. OpenURL

  29. Johnson PB, Christy RW: Optical constants of the noble metals.

    Phys Rev B 1972, 6:4370. OpenURL

  30. Peña O, Pal U, Rodríguez-Fernández L, Crespo-Sosa A: Linear optical response of metallic nanoshells in different dielectric media.

    J Opt Soc Am B 2008, 25:1371-1379. OpenURL

  31. Yang W: Improved recursive algorithm for light scattering by a multilayered sphere.

    Appl Opt 2003, 42:1710-1720. OpenURL