Organic–Inorganic Nanostructure Architecture via Directly Capping Fullerenes onto Quantum Dots

Jae Kwan Lee1, Jonggi Kim2 and Changduk Yang2*

Author affiliations

1 Research Center for Convergence Technology, Hoseo University, Chungnam 336-795, South Korea

2 Interdisciplinary School of Green Energy, Ulsan National Institute of Science and Technology (UNIST), Ulsan 689-798, South Korea

For all author emails, please log on.

Citation and License

Nanoscale Res Lett 2011, 6:23  doi:10.1007/s11671-010-9764-1

The electronic version of this article is the complete one and can be found online at:

Received:14 July 2010
Accepted:16 August 2010
Published:2 September 2010

© 2010 Lee et al.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.


A new form of fullerene-capped CdSe nanoparticles (PCBA-capped CdSe NPs), using carboxylate ligands with [60]fullerene capping groups that provides an effective synthetic methodology to attach fullerenes noncovalently to CdSe, is presented for usage in nanotechnology and photoelectric fields. Interestingly, either the internal charge transfer or the energy transfer in the hybrid material contributes to photoluminescence (PL) quenching of the CdSe moieties.

Quantum dots; Fullerene; Organic–inorganic nanostructure; Hybrid solar cell; Ligand exchange


Buckminsterfullerenes, beside their structural attraction, have been extensively researched in materials science due to their unique properties such as the excellent electron affinity as well as the interesting photophysical/photochemical nature [1-5]. A parallel and equally heady progress has also been made toward the development of semiconductor nanoparticles (e.g., CdSe) since the variation of their particle size and shape provides continuous and predictable changes in optical/electronic properties and chemical processability [6-8]. In addition, these nanocrystals behave essentially as a three-dimensional potential well for electrons (i.e., the quantum mechanical 'particle in a box'). It thus comes as no surprise that both the fullerenes and the nanocrystals have been actively investigated for various applications; however, their fields have been largely independent so far and have enjoyed their own remarkable developments in the past [9-11]. For instance, both fullerenes and semiconductor nanocrystals have been blended with conjugated polymers respectively, giving rise to photovoltaic cells with high-power conversion efficiencies [12-22]. Despite given the prominent features of fullerenes and semiconductor nanocrystals, fullerene-based mixed nanocomposites of well-defined composition and stoichiometry have not been adequately studied [23-26]. These points have attracted our attention to chemically combine the two in a single unit so that 'synergy' between the two can enhance and induce their outstanding properties.

To prepare the quantum dots (QDs)-based organic–inorganic hybrid nanomaterials, ligand exchange is a very useful method [27-29]. Even though thiol groups are the most used ligands for capping the QDs, they are unstable against photooxidation, which can lead to aggregation of the QDs [30-32]. Thus, we have turned to the carboxylic acid ligands for fullerene to CdSe nanocrystals. Recently, we reported the synthesis of the well-solubilized carboxylic acid fullerene (PCBA) (see below) for use as n-type materials in hybrid bulk-heterojunction solar cell [14].

In the current work, through the ligand-exchange reaction, we describe here a route to prepare readily soluble nanocomposite of PCBA-CdSe (Figure 1). The structural and spectroscopic properties of the resulting PCBA-capped CdSe nanoparticles (NPs) are of great interest since such rational design and synthesis can lead potentially to promising protocol for use in optical and photoelectric fields. Either the internal charge transfer or the energy transfer phenomenon between CdSe core and PCBA shell is clearly observed, resulting in the photoluminescence (PL) quenching of CdSe.

thumbnailFigure 1. Synthesis of PCBA-capped CdSe NPs.

Experimental Section


All solvents were purified and freshly distilled prior to use according to literature procedures. The synthesis of 4-(2-Ethylhexyloxy)-[6,6]-phenyl C61-butyric acid methyl ester (PCBA) [14], hexadecylamine-capped CdSe (HDA-capped CdSe) [18,33,34], and pyridine-capped CdSe (pyridine-capped CdSe) [34] was adapted from literature procedures. Commercially available materials were used as received unless noted.

Ligand Exchange to Prepare PCBA-capped CdSe NPs

To the pyridine-capped CdSe nanocrystals (17 mg) dried with N2 gas, PCBA (66.5 mg, 0.065 mmol) was added along with 10 mL anhydrous THF. The mixture was then sonicated at room temperature for an hour while the nanoparticles gradually became fully soluble in the THF to form an optically clear solution. The exchange procedure was monitored by FT-IR (diminution of the carboxylic acid band at 1705 cm-1), which showed nearly quantitative formation after 3 h. The solution was then dried by bubbling Ar and then stored in glove box.

Results and Discussion

(6,6)-Phenyl C61-butyric acid methyl ester (PCBM) is a soluble form of fullerenes as well as the most widely used organic n-type material. The PCBM can be hydrolyzed with a strong acid to the corresponding carboxylic acid PCMA which is a hardly soluble, not processable material. The introduction of a branched side chain as a solubilizer on the phenylene of PCBM (PCBA) [14] allows the excellent solubility, which enables to study the organic–inorganic hybrid material containing C60.

The hexadecylamine (HDA)-capped CdSe nanoparticles (CdSe NPs) were prepared using the reported procedures [18,33,34]. Then, HDA-capped CdSe NPs were successfully transformed to the corresponding pyridine-capped CdSe NPs by the treatment with pyridine under ultrasonication [34]. Subsequently, the ligand exchange with PCBA afforded the PCBA-capped CdSe NPs which is readily soluble in organic solvents (THF, chloroform, toluene, etc.) (Figure 1).

To ensure that the ligand exchanges had successfully gone to completion, the NPs were characterized by FT-IR (Figure 2). On a low-energy region (from 1,800 to 1,500 cm-1), the FT-IR spectrum of the pristine PCBA, displays a strong absorption band at 1,705 cm-1 assigned to the carboxylic acid, which is not present in the pyridine-capped CdSe NPs. In contrast, the PCBA-capped CdSe NPs reveal somewhat similar to the PCBA; however, it appears that the carboxylic acid band is diminished and shifted to lower energy at 1,730 cm-1 with a relatively decrease in intensity. The inspection of FT-IR of the PCBA-capped CdSe NPs such as the disappearance of the carboxylic acid band and new broad bands around 1,570 cm-1 is clearly suggestive that carboxylate binding are formed between PCBA and CdSe through the ligand exchange reaction.

thumbnailFigure 2. a FT-IR spectra on KBr for dropcast samples of PCBA (diamond), CdSe NPs (asterisk), PCBA-CdSe NPs (circle); b TEM of pyridine-capped CdSe NPs and c PCBA-CdSe NPs.

Figure 2b and 2c depict a transmission electron microscopy (TEM) micrograph of the NPs (pyridine-capped CdSe and PCBA-capped CdSe). The TEM image of the pyridine-capped CdSe is characteristic of uniformly shaped spheres, with a mean size of 5.0 ± 1 nm (see Figure 2b). In the case of analyzing the PCBA-capped CdSe, the monodispersed spheres are not easily seen in the resolution TEM; however, a nanometer-sized pattern of larger objects is observed. This can be attributed to the nanoagglomerated feature, which is resulted from the interaction between the PCBA attached to the CdSe. In addition, we cannot rule out that more than two CdSe units can be surrounded by PCBA moieties, which probably leads to the roughly spherical form.

The UV–Vis and photoluminescence (PL) properties of all the NPs (HDA-capped CdSe, pyridine-capped CdSe and PCBA-capped CdSe) were investigated in chloroform solution. As shown in Figure 3, the solution optical spectra of both HDA-capped CdSe and pyridine-capped CdSe exhibit broad absorption bands (410–460 nm), arising from exciton absorption peak in CdSe NPs. In the case of PCBA-capped CdSe, the distinguishable band at 330 nm corresponds to the characteristic of C60 not only exhibits but also the absorption feature is almost identical to that of the pristine PCBA. This implies that PCBA is completely binding along the CdSe unit.

thumbnailFigure 3. a UV–Vis absorption and b PL spectra of HDA-capped CdSe NPs (diamond), pyridine-capped CdSe NPs (asterisk), and PCBA-capped CdSe NPs (circle) in chloroform solution.

In PL spectrum of the pyridine-capped CdSe NPs, the bathochromic shift of the onset of the emission of ca. 60 nm is observed when compared to the HDA-capped CdSe NPs. This low-energy emission can be due to aggregated formation and increased intermolecular interaction in the NPs [35]. In the case of the PCBA-capped CdSe in solution, the PL quenching of the band at 512 nm corresponding to CdSe is clearly observed, and an emission peak centered at 795 nm which stems from the PCBA units becomes dominant. The decrease in PL intensity in CdSe NP is mostly likely caused by the quenching of photoexcited CdSe NP through charge transfer to the electron-accepting PCBA from CdSe NPs. However, we cannot rule out that, through utilization of the carboxylates as a linkage between CdSe with PCBA, it is possible to trigger the energy transfer in the hybrid material since the length scale of domain in PCBA-capped CdSe is smaller than typical values for Förster energy transfer (<10 nm) [36]. To confirm that the PCBA-capped CdSe of the intracomplex quenching is indeed charge injection of a conduction band electron of the photoexcited CdSe NPs to the surface-bound PCBA, we are complementing our studies by time-resolved transient absorption spectroscopic measurements with CdSe NPs and PCBA-capped CdSe.

Both PCBM and CdSe derivatives have been applied as the electron transport materials in the most widely used configuration of the photovoltaic cells [14,21,37-39]. Furthermore, the nearly complete quenching of emission from the higher energy CdSe NPs to PCBA may be a significant key in further improving the efficiency of an organic solar cell.

In addressing this fundamental question, we are currently studying the hybrid nanostructures fabricated with conjugated polymers, in that enables to create the positive aspect in the hybrid solar cells and other hybrid materials-based optical and electrooptical applications via the ligand exchange.


In summary, we have demonstrated the preparation of soluble nanoparticle of PCBA-CdSe by directly exchanging the ligands onto the surface of pyridine-capped CdSe, which is fully characterized by FT-IR, UV–Vis absorption, PL spectra, and TEM. The resulting PCBA-capped CdSe in solution shows a dominant emission peak centered at 795 nm, which is originated from the PCBA units. It clearly indicates that either the internal charge transfer or the energy transfer from the CdSe to PCBA moieties in solution occurs, so that the emission band (λmax = 512 nm) from the CdSe units is nearly quenched. We envision that a hybrid-polymeric nanoarchitecture can be utilized for constructing one layer of solar cell to explore the possible optoelectronic device application, which will open up new opportunities for the development of solar cells based on organic–inorganic nanocomposites. This work is currently under investigation.


This research was supported by Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (2010-0002494) and the National Research Foundation of Korea Grant funded by the Korean Government (MEST) (NRF-2009-C1AAA001-2009-0092950).


  1. Guldi DM, Martin N: Fullerenes: from Synthesis to Optoelectronic Properties. Kluwer Academic, Dordrecht; 2002:137-293.

  2. Shinar J, Vardeny ZV, Kafafí ZH: Optical and Electronic Properties of Fullerene-Based Material. Marcel Dekker, Inc., New York; 2000:21-292.

  3. Dagotto E:

    Science. 2001, 293:2410-2411. PubMed Abstract | Publisher Full Text OpenURL

  4. Makarova TL, Sundqvist B, Hohne R, Esquinazi P, Kopelevich Y, Scharff P, Davydov VA, Kashevarova LS, Rakhmanina AV:

    Nature. 2001, 413:716-718. PubMed Abstract | Publisher Full Text OpenURL

  5. Haddon RC, Perel AS, Morris RC, Palstra TTM, Hebard AF, Fleming RM:

    Appl Phys Lett. 1995, 67:121-123. Publisher Full Text OpenURL

  6. Peng XG, Manna L, Yang WD, Wickham J, Scher E, Kadavanich A, Alivisatos AP:

    Nature. 2000, 404:59-61. PubMed Abstract | Publisher Full Text OpenURL

  7. Heath JR:

    Acc Chem Res. 1999, 32:388. Publisher Full Text OpenURL

  8. Alivisatos AP:

    Science. 1996, 271:933-937. Publisher Full Text OpenURL

  9. Cravino A, Zerza G, Maggini M, Bucella S, Svensson M, Andersson MR, Neugebauer H, Sariciftci NS:

    Chem Commun. 2000, (24):2487-2488. Publisher Full Text OpenURL

  10. Scharber MC, Wuhlbacher D, Koppe M, Denk P, Waldauf C, Heeger AJ, Brabec CL:

    Adv Mater. 2006, 18:789-794. Publisher Full Text OpenURL

  11. Liang ZQ, Dzienis KL, Xu J, Wang Q:

    Adv Funct Mater. 2006, 16:542-548. Publisher Full Text OpenURL

  12. Yang C, Cho S, Heeger AJ, Wudl F:

    Angew Chem Int Ed. 2009, 48:1592-1595. Publisher Full Text OpenURL

  13. Park SH, Yang CD, Cowan S, Lee JK, Wudl F, Lee K, Heeger AJ:

    J Mater Chem. 2009, 19:5624-5628. Publisher Full Text OpenURL

  14. Yang C, Kim JY, Cho S, Lee JK, Heeger AJ, Wudl F:

    J Am Chem Soc. 2008, 130:6444-6450. PubMed Abstract | Publisher Full Text OpenURL

  15. Shiga T, Takechi K, Motohiro T:

    Sol Energ Mat Sol Cells. 2006, 90:1849-1858. Publisher Full Text OpenURL

  16. Landi BJ, Castro SL, Ruf HJ, Evans CM, Bailey SG, Raffaelle RP:

    Sol Energ Mat Sol Cells. 2005, 87:733-746. Publisher Full Text OpenURL

  17. Beek WJE, Wienk MM, Janssen RAJ:

    Adv Mater. 2004, 16:1009-1013. Publisher Full Text OpenURL

  18. Kumar S, Nann T:

    J Mater Res. 2004, 19:1990-1994. Publisher Full Text OpenURL

  19. Huynh WU, Dittmer JJ, Libby WC, Whiting GL, Alivisatos AP:

    Adv Funct Mater. 2003, 13:73-79. Publisher Full Text OpenURL

  20. Raffaelle RP, Castro SL, Hepp AF, Bailey SG:

    Prog Photovolt. 2002, 10:433-439. Publisher Full Text OpenURL

  21. Huynh WU, Dittmer JJ, Alivisatos AP:

    Science. 2002, 295:2425-2427. PubMed Abstract | Publisher Full Text OpenURL

  22. Guchhait A, Rath AK, Pal AJ:

    Chem Mater. 2009, 21:5292-5299. Publisher Full Text OpenURL

  23. Shon YS, Choo H:

    Chem Commun. 2002, (21):2560-2561. Publisher Full Text OpenURL

  24. Sudeep PK, Ipe BI, Thomas KG, George MV, Barazzouk S, Hotchandani S, Kamat PV:

    Nano Lett. 2002, 2:29-35. Publisher Full Text OpenURL

  25. Fujihara H, Nakai H:

    Langmuir. 2001, 17:6393-6395. Publisher Full Text OpenURL

  26. Xu CM, Xi B, Li YL, Wang C, Wang S, Shi ZQ, Fang HJ, Xiao SX, Zhu DB:

    New J Chem. 2001, 25:1191-1194. Publisher Full Text OpenURL

  27. Advincula RC:

    Dalton Trans. 2006, (23):2778-2784. PubMed Abstract | Publisher Full Text OpenURL

  28. Chen KB, Chen MH, Yang SH, Hsieh CH, Hsu CS, Chen CC, Chien HJ:

    J Polym Sci Part A Polym Chem. 2006, 44:5378-5390. Publisher Full Text OpenURL

  29. Landi BJ, Evans CM, Worman JJ, Castro SL, Bailey SG, Raffaelle RP:

    Mater Lett. 2006, 60:3502-3506. Publisher Full Text OpenURL

  30. Kloepfer JA, Bradforth SE, Nadeau JL:

    J Phys Chem B. 2005, 109:9996-10003. PubMed Abstract | Publisher Full Text OpenURL

  31. Potapova I, Mruk R, Prehl S, Zentel R, Basche T, Mews A:

    J Am Chem Soc. 2003, 125:320-321. PubMed Abstract | Publisher Full Text OpenURL

  32. Aldana J, Wang YA, Peng XG:

    J Am Chem Soc. 2001, 123:8844-8850. PubMed Abstract | Publisher Full Text OpenURL

  33. Qu LH, Peng XG:

    J Am Chem Soc. 2002, 124:2049-2055. PubMed Abstract | Publisher Full Text OpenURL

  34. Shallcross RC, D'Ambruoso GD, Korth BD, Hall HK, Zheng ZP, Pyun J, Armstrong NR:

    J Am Chem Soc. 2007, 129:11310-11311. PubMed Abstract | Publisher Full Text OpenURL

  35. Oh SW, Kang YS:

    Colloids Surf A Physicochem Eng Aspects. 2005, 257–258:415-418. Publisher Full Text OpenURL

  36. Förster T:

    Discuss Faraday Soc. 1959, 7-17. OpenURL

  37. Liu JS, Tanaka T, Sivula K, Alivisatos AP, Fréchet JMJ:

    J Am Chem Soc. 2004, 126:6550-6551. PubMed Abstract | Publisher Full Text OpenURL

  38. Janssen RAJ, Hummelen JC, Lee K, Pakbaz K, Sariciftci NS, Heeger AJ, Wudl F:

    J Chem Phys. 1995, 103:788-793. Publisher Full Text OpenURL

  39. Zheng LP, Zhou QM, Deng XY, Yuan M, Yu G, Cao Y:

    J Phys Chem B. 2004, 108:11921-11926. Publisher Full Text OpenURL