Abstract
Nonlinear charge transport parallel to the layers of pmodulationdoped GaInNAs/GaAs quantum wells (QWs) is studied both theoretically and experimentally. Experimental results show that at low temperature, T = 13 K, the presence of an applied electric field of about 6 kV/cm leads to the heating of the high mobility holes in the GaInNAs QWs, and their realspace transfer (RST) into the lowmobility GaAs barriers. This results in a negative differential mobility and selfgenerated oscillatory instabilities in the RST regime. We developed an analytical model based upon the coupled nonlinear dynamics of the realspace hole transfer and of the interface potential barrier controlled by spacecharge in the doped GaAs layer. Our simulation results predict dc biasdependent selfgenerated current oscillations with frequencies in the high microwave range.
Introduction
During the past decade, dilute nitrides, particularly the quaternary material system of GaInNAs/GaAs, have attracted a great deal of attention, both because of unusual physical properties and potential applications for a variety of optoelectronic devices. The addition of a small amount of nitrogen induces a strong perturbation in the conduction band of matrix semiconductors, while having a negligible effect on the valence band. As a result, the electron mobility is greatly lowered and the hole mobility can become higher than the electron mobility, in materials with relatively high nitrogen content. High hole mobility coupled with the low hole confinement energy (110 meV in our calculation for the samples investigated in this study) [1] in the GaInNAs/GaAs quantum well (QW) structure makes it possible for holes in the well to gain enough energy to overcome the small band discontinuity under an electric field applied parallel to the layer interface, and to transfer into the lowmobility pdoped GaAs layer. This leads to a negative differential mobility (NDM) caused by realspace hot hole transfer, as we previously observed [1]. Therefore, under dc conditions, a selfgenerated current oscillation in the realspace regime, as proposed by Schöll and coauthors [25], is expected in pmodulationdoped GaInNAs/GaAs heterostructures.
In this work, we study the nonlinear charge transport in a modulationdoped GaInNAs/GaAs semiconductor heterostructure where the GaAs barrier layer is intentionally pdoped. The charge transport processes perpendicular and parallel to the layers far from thermodynamic equilibrium are modeled by several coupled nonlinear dynamics equations. In this model, selfgenerated current oscillations can be described in the following way. Realspace transfer (RST) of holes out of the GaInNAs well layer leads to an increase of the hole density in the GaAs barrier, which diminishes the negative space charge that controls the band bending (Figure 1). Consequently, the potential barrier Φ_{B }decreases, with some delay due to the finite dielectric relaxation time. This leads to an increased thermionic emission backward current J_{bw }into the GaInNAs well, which decreases the hole density in the GaAs barrier. As a result, the space charge and Φ_{B }are increased in the GaAs. This, in turn, decreases the thermionic emission backward current from the well into the barrier [6].
Figure 1. Schematic energyband profile of a GaInNAs/GaAs heterostructure.
Negative differential resistance instabilities in pmodulationdoped GaInNAs/GaAs QWs
The layer structure of the sample used in this study is given in Table 1. The sample, which was grown by molecular beam epitaxy (MBE) on semiinsulating GaAs substrate, consists of three 7 nm thick GaInNAs QWs, separated by 20 nm thick Bedoped GaAs barriers. These ptypedoped barriers are separated from the QWs by 5 nm undoped spacer layers to reduce the remote impurity scattering. The mole fraction of indium and nitrogen in the Ga_{1x}In_{x}N_{y}As_{1y }QWs is x = 0.3 and y = 0.015, respectively. The sample was fabricated in the shape of a simple bar for IV measurement. Fabrication details are given somewhere else [1].
The nonlinear transport processes depicted in Figure 1 are modeled by a set of dynamic equations relevant to current instabilities in semiconductors. We derive a set of nonlinear partial differential equations for the hole density in the wells (p_{w}), and in the barriers (p_{b}), the potential barrier in each of GaAs layers (Φ_{B}), and the dielectric relaxation of the applied parallel field (ξ_{II}).
The dynamics of the carrier density in the well and in the barrier are given by [5]
where J_{wb }and J_{bw }are the thermionic currents flowing from the GaInNAs well layers to the GaAs barrier and from the barrier into the well, respectively, q is the positive electron charge, and L_{w }and L_{b }are the width of the GaInNAs QW and the GaAs barrier, respectively. The electric field parallel to the layer interface ξ_{II }can be derived from Poisson's equation and is given by
where ε_{0 }and ε_{s }are the absolute and relative permittivity, respectively. Using Equations (1)(3), the dielectric relaxation of the applied parallel field ξ_{II }as a function of the current flow (ydirection), the transverse space coordinator (xdirection), and the time t can be written as
Where ξ_{0 }= U_{0}/d is the applied field and U_{0 }is the applied voltage, σ_{L }= d/⌊h(L_{w}+L_{b})qμ_{w}R_{L}N_{A}⌋ is connected to the load resistance R_{L}, d is the sample length, h is the width of the sample, μ_{w }and μ_{b }are the hole mobility in the QW and the GaAs barrier, respectively. By integrating both sides of Equation (5), we finally have the dielectric relation of the parallel electric field
where J_{II }is the external current density flowing through the external circuit at applied bias voltage U_{0}.
Here, we define the current density flowing through the sample as a function of applied parallel field, using
The timedependent potential barrier in the GaAs layer is given by
Equations (1) and (2) represent particle continuity, where the thermionic current densities J_{bw }and J_{wb }can be calculated using Bethe's theory, by assuming that the width of the space charge is comparable to the mean free path L_{m }of the holes [4,5]
where
Since the number of holes in the well and the barrier are related to each other, their total number is conserved [1]:
where p_{0 }is the 3 D hole density in the well at low field.
Numerical results
The steadystate can be evaluated by setting Equations (1), (2), (6), and (8) to zero, and using the parameters listed in Table 2. The resulting static current density characteristic as a function of the static electric field is shown in Figure 2. The measured IV curve obtained with the same sample in our previous study is placed in the figure inset for comparison [1]. Simulation results predict that the RST of hot holes leads to an Nshaped characteristic with a regime of negative differential resistance [4,7,8]. The critical field for the onset of NDM is the order of 6 kV/cm, which agrees well with our experimental results.
Table 2. Numerical parameters used in the simulation for the GaInNAs/GaAs sample [1]
Figure 2. Static current densityfield characteristic as a function of the static electric field
The timedependent nonlinear Equations (1), (2), (6), and (8) have been numerically
resolved using Euler's methods. The simulation reveals that the instability of the
dynamic system is strongly dependent on the applied dc bias field, ξ_{0 }= U_{0}/d. We found that selfgenerated nonlinear oscillation appears in a range of applied
dc electric fields where the load line lies in the NDM regime, as shown in Figure
3a. Figure 3b shows the corresponding currentdensity oscillations with frequency of 44 GHz, for
Figure 3. (a) Static current density versus electric field
It is interesting to find that the oscillation frequency is strongly dependent on
the dopant concentration in the barrier and the barrier thickness, as shown in Figure
4. The oscillation frequency increases from 29 to 50 GHz as the dopant concentration
in the barrier increases from 1.9 × 10^{16 }cm^{3 }to 2.4 × 10^{16 }cm^{3}, accompanied by gradually reduced oscillation amplitude. Finally, the periodic oscillation
damps out when the dopant concentration is above 2.4 × 10^{16 }cm^{3}, as shown in Figure 5. The oscillation shows similar behavior as the barrier thickness increases. The fact
that the selfgenerated oscillation frequency can be tuned by the doping concentration
and the layer width can be explained by the nonlinear combination of the effective
thermionic emission time,
Conclusion
In this work, we studied the transport processes parallel and perpendicular to the layers of ptype modulationdoped GaInNAs/GaAs multiQW structures far from the thermodynamic equilibrium. The simulation results of the steadystate predict an NDM induced by RST of hot holes in the QWs and the critical electric field of the onset of NDM to be the order of 6 kV/cm. This value agrees well with our previous experimental results. The numerically timedependent simulations indicate that the selfgenerated oscillation caused by RST with the frequency in the range 2050 GHz appears under the right applied electric field. The frequency of selfgenerated oscillation can be flexibly optimized to the range of considerable interest for applications as a simple way of generating highfrequency microwave power based on GaInNAs material system. According to our simulation, the predicted selfgenerated oscillation can be observed if the GaInNAs QW structure is optimized around 25 nm barrier and less than 2.4 × 10^{16 }cm^{3 }doping concentration. The current oscillation measurements will be performed using optimized structures fabricated into two terminal devices, and shunted with a 50 Ω resistor and highspeed circuit (highspeed oscilloscope and pulse generator). The experiment results are expected to be published in the near future.
Abbreviations
NDM: negative differential mobility; QWs: quantum wells; RST: realspace transfer.
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
HMK: carried out the theoretical calculations, in collaboration with AA. MS grew the sample according to the specifications. YS fabricated the devices, carried out the experiments. HMK and YS wrote up the article. NB, is the supervisor of the project. All authors read and approved the final manuscript.
Acknowledgements
We acknowledge the collaboration within the COST Action MP0805 entitled "Novel Gain Materials and Devices Based on IIIVN Compounds".
References

Sun Y, Balkan N: Energy and momentum relaxation dynamics of hot holes in modulation doped GaInNAs/GaAs quantum wells.
J Appl Phys 2009, 106:073704. Publisher Full Text

Schöll E, Aoki K: Novel mechanism of a realspace transfer oscillator.

Döttling R, Schöll E: Oscillatory bistability of real space transfer in semiconductor heterostructures.

Döttling R, Schöll E, Pyragas K, Cooper D: Tuning of Semiconductor Oscillators by Chaos Control.

Döttling R, Rudzick O, Schöll E, Straw A, Vickers AJ, Balkan N, Da Cunha A: Selfgenerated nonlinear oscillations in multilayer semiconductor heterostructures.

1988, 37:319.

Sun Y, Balkan N, Alsan M, Lisesivdin SB, Carrere H, Arikan MC, Marie X: Electronic transport in n and ptype modulation doped GaxIn1xNyAs1y/GaAs quantum wells.
J Phys Condens Matter 2009, 21:174210. Publisher Full Text

Balkan N, Ridley BK, Vickers A: Negative Differential Resistance and Instabilities in 2D Semiconductors. New York: Plenum Press; 1993.

Döttling R, Schöll E: Front and domain propagation in semiconductor heterostructures.