Friction and Shear Strength at the Nanowire–Substrate Interfaces

Yong Zhu1*, Qingquan Qin1, Yi Gu2 and ZhongLin Wang3

Author Affiliations

1 Department of Mechanical and Aerospace Engineering, North Carolina State University, Raleigh, NC, 27695, USA

2 Department of Physics, Washington State University, Pullman, WA, 99164, USA

3 School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA, 30332, USA

For all author emails, please log on.

Nanoscale Research Letters 2009, 5:291-295  doi:10.1007/s11671-009-9478-4


The electronic version of this article is the complete one and can be found online at:


Received:6 September 2009
Accepted:28 October 2009
Published:28 November 2009

© 2009 to the authors

Abstract

The friction and shear strength of nanowire (NW)–substrate interfaces critically influences the electrical/mechanical performance and life time of NW-based nanodevices. Yet, very few reports on this subject are available in the literature because of the experimental challenges involved and, more specifically no studies have been reported to investigate the configuration of individual NW tip in contact with a substrate. In this letter, using a new experimental method, we report the friction measurement between a NW tip and a substrate for the first time. The measurement was based on NW buckling in situ inside a scanning electron microscope. The coefficients of friction between silver NW and gold substrate and between ZnO NW and gold substrate were found to be 0.09–0.12 and 0.10–0.15, respectively. The adhesion between a NW and the substrate modified the true contact area, which affected the interfacial shear strength. Continuum mechanics calculation found that interfacial shear strengths between silver NW and gold substrate and between ZnO NW and gold substrate were 134–139 MPa and 78.9–95.3 MPa, respectively. This method can be applied to measure friction parameters of other NW–substrate systems. Our results on interfacial friction and shear strength could have implication on the AFM three-point bending tests used for nanomechanical characterisation.

Keywords:
Nanowire; Interface; Friction; Shear strength; Nanomechanics

Introduction

In nanodevices, nanowires (NWs) are typically integrated to larger structures. The NW–substrate interfaces therefore play a critical role in both mechanical reliability and electrical performance of these nanodevices, especially when the size of the NW is small [1,2]. Such interfaces include two configurations, NW length or NW tip in contact with the substrate, and both configurations have a wide range of applications. For example, the tip-substrate contacts are present in nanogenerators [3], nanostructured solar cells [4], atomic force microscopy (AFM) with carbon nanotube (CNT) tips [5], CNT tapes [6] and many other nanodevices. Indeed, as recently outlined by Wang [7], one critical future direction for nanogenerator research is study of the NW–metal interface to build a robust, low wearing structure for improving the device lifetime.

Experimental work on NW interfacial mechanics has been limited so far due to experimental challenges at the nanoscale [8] and the fact that many existing tribology tools such as AFM, surface force apparatus (SFA), quartz microbalance and microfabricated devices cannot be readily applied [9,10]. Static friction force between NWs (including CNTs) and substrates was estimated from the highly deformed shapes of NWs [11]. Recently CNTs were found to slip on silicon oxide surface at a lateral force of 8 nN [12], and ZnO NWs to slip on silicon surface at a few μN [13]. However, the above studies on friction are only limited to the configuration of NW length in contact with a substrate. To the best of our knowledge, no experiments have been reported to investigate the configuration of individual NW tip in contact with a substrate.

Here we report the first experimental study on the friction between NW tips (ends) and a substrate. Silver and ZnO NWs in contact with a gold-coated substrate were studied as model systems in view that silver and ZnO NWs have very different tip shapes. Silver NW is an important class of metallic NWs because of its potential use as interconnects in view that bulk silver exhibit very high electric and thermal conductivity [14]. ZnO is one of the most important semiconductor NWs with a broad range of applications including nanogenerators, biosensors, nanolasers and nanoelectromechanical systems (NEMS) [15]. The friction measurements reported in the present article were enabled by an innovative experimental method based on column buckling theory. The experiments were conducted in situ inside a scanning electron microscope (SEM) using a nanomanipulator as the actuator and an AFM cantilever as the force sensor.

Experimental

The silver NWs were synthesised using a seed-assisted, solution-phase method with a fivefold twin structure [16]. Figure 1a is a transmission electron microscopy (TEM) image showing the NW tip. Figure 1b and 1c are high-resolution TEM images showing a layer of silver oxide with varying thickness on the NW surface. The ZnO NWs were synthesised using the vapour–liquid–solid (VLS) method with a wurtzite structure and growth direction of [0001] [17]. Figure 1d is a SEM image showing the tip of a ZnO NW, which appears to be flat.

thumbnailFigure 1. ac TEM images of a silver NW; b, c show an oxide layer on the surface of the silver NW; d SEM image of a ZnO NW

In situ SEM buckling tests of NWs were conducted as shown in Fig. 2. A nanomanipulator (Klocke Nanotechnik, Germany) that possesses 1 nm resolution in three orthogonal directions was used to pick up individual NWs [18,19]. A NW was clamped onto the tungsten tip on the nanomanipulator using electron beam-induced deposition (EBID) of carbon. Then the NW was approached to make contact with an AFM cantilever (OBL-10, Veeco). Carbon deposition was not used at the NW–cantilever interface. Compressive force was applied to the NW by the nanomanipulator movement, which led to buckling of the NW. In this case, the boundary condition was fixed-pinned. Continued loading further changed the postbuckling shape of the NW until sliding occurred at the NW–cantilever interface.

thumbnailFigure 2. Buckling process of an individual NW; a is before buckling and b is after buckling and just prior to sliding on the right end

After buckling of the NW, there exist two forces at the NW–substrate interface, a compressive (normal) force and a frictional (lateral) force. The compressive force on the NW can be easily measured from the deflection of the AFM cantilever; however, it is not trivial to measure the friction force. Below we describe a method to measure friction force based on the buckling theory. Free-body diagram of a buckled member under fixed-pinned boundary condition is shown in Fig. 3a, with the left end fixed and the right end pinned. A small lateral deflection gives rise to a moment M at the fixed end and shear force (friction force)F at each end of the member. From the moment balance, it can be easily obtained that, where L is the length of the member. The governing equation at a section with a distance x from the right end is given by

where,E is the Young’s modulus and I is the moment of inertia. The solution to Eq. 1is

thumbnailFigure 3. a Free-body diagram of a buckled column with fixed-pinned boundary condition. Right end is the NW-substrate interface. b Nonlinear least squares fitting of Eq. 3to digitized shape of a NW prior to sliding

Taking into account the fixed-pinned boundary condition, we obtain

Equation 3describes the shape of the member in the postbuckling stage. Details on the equation derivation can be found elsewhere [20]. Eq. 3 provides the theoretical basis of our method to measure the friction force. By fitting the observed shape of the NW just prior to sliding to Eq. 3 using the nonlinear least squares method, M can be determined since P is measured from the deflection of the AFM cantilever. Then F can be obtained using F = M/L. Figure 3b shows the fitting of a deformed NW to Eq. 3. Clearly the agreement is very good.

Results and Discussion

Following the method described above, three silver NWs and three ZnO NWs were tested for friction measurements. The Amonton–Coulomb friction law is written as F = μP, where μ is the so-called coefficient of friction. The normal force, friction force and coefficient of friction for all six NWs are listed in Table 1. Note that these NWs did not break in the buckling experiments so that each NW was tested multiple times with very good repeatability. However, the Amonton–Coulomb law was obtained from empirical observations with many counterexamples; for instance, geckos are able to move on walls and ceilings when P ≤ 0. A more fundamental friction law that links friction and adhesion was proposed by Bowden and Tabor [21],

where τ is the interfacial shear strength and A is the true contact area. This law has been supported by numerous SFA and AFM experiments [10]. The two theories were reconciled by considering the multiple asperities among the contacting surfaces [22]; as a result the true contact area is typically proportional to the normal force.

Table 1. Normal force, friction force and coefficient of friction in each experiment

The NW–substrate contact is treated as the single-asperity contact because the NW diameters are smaller than the wavelength of the substrate topography. In order to evaluate interfacial shear strength using Eq. 4, the true contact area must be determined. In our experiments as well as AFM experiments, the true contact area is calculated using continuum mechanics models. The well-known Hertzian model does not take into account attractive adhesion forces between the contacting surfaces. Other widely accepted models that take adhesion force into account are due to Johnson, Kendall, and Roberts (JKR) [23], Derjaguin, Mutter, Toporov (DMT) [24] and Maugis [25], respectively.

For simplicity, the continuum models typically assume the contact between a sphere and a flat surface. It is known that the JKR and DMT theories are two extremes of a spectrum of elastic solutions determined by the Tabor parameter [26], which is given by

where R is the radius of the sphere, K is the reduced modulus of two materials with E1 and E2 the respective Young’s moduli, and ν1 and ν2 the respective Poisson’s ratios, z0 is the interatomic equilibrium distance (=0.2 nm), γ is the interfacial energy per unit area (work of adhesion). Each NW tip was fitted with a sphere. When μ > 5, the JKR model is valid; when μ < 0.1, the DMT model should be applied; in the intermediate range, the Maugis model becomes appropriate. In all our experiments 2.05 < μ < 2.39 (see Table 2), so the Maugis model should be used. However, the Maugis model does not have an explicit expression for contact radius. For the Tabor parameter in this range, the JKR model was found to approximate the Maugis solution very closely [27], therefore the JKR model was used in our calculation due to its explicitness.

Table 2. Contact pressure and interfacial shear strength using the Hertz and JKR models

Following the Hertz and JKR models, the contact radius a as a function of the externally applied load P is given by

respectively, wherewith γ1 and γ2 the respective surface energy and γ12 the interface energy. γ1 = 1.37 J/m2 for gold, γ2 = 0.8 J/m2 for silver oxide [28] and γ2 = 1.74 J/m2 for ZnO with {0001} surface [29]. Therefore, γ = 2.09 J/m2 and γ = 3.09 J/m2 for the contacts between gold and silver oxide and between gold and ZnO, respectively. In addition, Egold = 78 GPa, Esilver = 84 GPa, EZnO = 140 GPa, [30]. The contact radius, contact pressure and interfacial shear strength calculated using the two models are listed in Table 2. It can be seen that the interfacial shear strengths between silver NW and gold substrate and between ZnO NW and gold substrate are 134–139 MPa and 78.9–95.3 MPa, respectively, according to the JKR model. These values are in good agreement with those obtained from AFM and mesoscale friction tester in similar environment (vacuum or dry) [31].

Several issues related to the experiments and data analyses are discussed. First of all, our measurements showed that no metallic bonding formed between silver NWs and the gold substrate as the strength of metallic bonding is typically on the order of GPa [32]. This is due to the presence of a thin layer of silver oxide, as shown in the high-resolution TEM images (Figure 1). Second, it is not appropriate to treat the ZnO NWs as the molecular junctions where the contact areas remain constant (in our case the NW cross-sections) [33], otherwise the interfacial shear strength would be too small. This is reasonable because it is very likely that the NW is not perfectly perpendicular to the substrate. Edge of the NW tip could be in contact with the substrate, and the contact area can then be approximately fitted with a sphere. Third, previous experiments showed that electron beam increases adhesion force between semiconductors and metals [34,35]. For contacts between ZnO NW tips and a gold substrate, we found the adhesion force did not show noticeable change when the contact area was exposed to electron beam only for a short time (e.g., less than 10 s) [36]. Last, although our experimental method gave rise to the first measurement of the friction data between NW tips and a substrate, we are aware that it cannot measure the friction as a function of the progressively applied normal force. MEMS devices with simultaneous normal and lateral force measurement capability are under development to address this issue.

Our results on interfacial friction and shear strength could have direct implication on the AFM three-point bending tests that are widely used in extracting mechanical properties of one-dimensional nanostructures including CNTs and NWs [37,38]. Often the adhesion between the NWs and the substrate is assumed to be strong enough to provide a fixed–fixed boundary condition for the three-point bending tests. The assumption is valid for NWs with small diameters; but for those with large diameters, it could lead to large data scatter as typically observed in experiments. Our results could be incorporated into data reduction in the three-point bending experiments to quantify the influence of adhesion and friction on the measured mechanical properties. Other methods that could also be used to eliminate the ambiguity caused by the NW–substrate friction in the three-point bending tests include EBID of platinum or carbon to reinforce the clamps [39].

Conclusions

In summary, a new experimental method to measure the friction between a NW tip and a substrate has been developed. Silver and ZnO NWs were tested with a gold-coated surface as the substrate. The coefficients of friction between silver NW and gold substrate and between ZnO NW and gold substrate were found to range from 0.09 to 0.12 and from 0.10 to 0.15, respectively. The adhesion between NWs and the substrate substantially modified the true contact area, which in turn affected the interfacial shear strength significantly. According to the calculated Tabor parameter, the JKR model was selected to approximately calculate the contact area and the interfacial shear strength. The interfacial shear strengths between silver NW and gold substrate and between ZnO NW and gold substrate ranged from 134 to 139 MPa and from 78.9 to 95.3 MPa, respectively. These values are in good agreement with previous results obtained in similar environment (vacuum or dry) [31].

Acknowledgement

This work was supported by the National Science Foundation under Award No. CMMI-0826341 and the Faculty Research and Professional Development Fund from North Carolina State University. We thank to Fengru Fan and Afsoon Soudi for kindly providing the NW samples.

References

  1. Lu W, Lieber CM: Semiconductor nanowires.

    J. Phys. D Appl. Phys. 2006, 39(21):R387-R406.

    COI number [1:CAS:528:DC%2BD28Xht1GrtrrO]; Bibcode number [2006JPhD...39R.387L]

    Publisher Full Text OpenURL

  2. Patolsky F, Lieber CM: Nanowires nanosensors.

    Mater. Today 2005, 8:20-28.

    COI number [1:CAS:528:DC%2BD2MXjs1KqtLw%3D]

    Publisher Full Text OpenURL

  3. Wang ZL, Song JH: Piezoelectric nanogenerators based on zinc oxide nanowire arrays.

    Science 2006, 312(5771):242-246.

    COI number [1:CAS:528:DC%2BD28XjtlKqu7g%3D]; Bibcode number [2006Sci...312..242W]

    PubMed Abstract | Publisher Full Text OpenURL

  4. Law M, Greene LE, Johnson JC, Saykally R, Yang PD: Nanowire dye-sensitized solar cells.

    Nat Mater 2005, 4(6):455-459.

    COI number [1:CAS:528:DC%2BD2MXks1Cit7o%3D]; Bibcode number [2005NatMa...4..455L]

    PubMed Abstract | Publisher Full Text OpenURL

  5. Dai HJ, Hafner JH, Rinzler AG, Colbert DT, Smalley RE: Nanotubes as nanoprobes in scanning probe microscopy.

    Nature 1996, 384(6605):147-150.

    COI number [1:CAS:528:DyaK28XmvFGhs7s%3D]; Bibcode number [1996Natur.384..147D]

    Publisher Full Text OpenURL

  6. Ge L, Sethi S, Ci L, Ajayan PM, Dhinojwala A: Carbon nanotube-based synthetic gecko tapes.

    Proc. Natl Acad. Sci. USA 2007, 104(26):10792-10795.

    COI number [1:CAS:528:DC%2BD2sXnsV2ltbw%3D]; Bibcode number [2007PNAS..10410792G]

    PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  7. Wang ZL: Towards self-powered nanosystems: from nanogenerators to nanopiezotronics.

    Adv. Funct. Mater. 2008, 18(22):3553-3567.

    COI number [1:CAS:528:DC%2BD1cXhsVyqu77M]

    Publisher Full Text OpenURL

  8. Falvo MR, Superfine R: Mechanics and friction at the nanometer scale.

    J. Nanopart. Res. 2000, 2:237-248. Publisher Full Text OpenURL

  9. Corwin AD, de Boer MP: Effect of adhesion on dynamic and static friction in surface micromachining.

    Appl. Phys. Lett. 2004, 84(13):2451-2453.

    COI number [1:CAS:528:DC%2BD2cXis1Wmu7Y%3D]; Bibcode number [2004ApPhL..84.2451C]

    Publisher Full Text OpenURL

  10. Carpick RW, Salmeron M: Scratching the surface: Fundamental investigations of tribology with atomic force microscopy.

    Chem. Rev. 1997, 97(4):1163-1194.

    COI number [1:CAS:528:DyaK2sXjsFWis7w%3D]

    PubMed Abstract | Publisher Full Text OpenURL

  11. Conache G, Gray SM, Ribayrol A, Froberg LE, Samuelson L, Pettersson H, Montelius L: Friction measurements of InAs nanowires on silicon nitride by AFM manipulation.

    Small 2009, 5(2):203-207.

    COI number [1:CAS:528:DC%2BD1MXhvVWls7k%3D]

    PubMed Abstract | Publisher Full Text OpenURL

  12. Whittaker JD, Minot ED, Tanenbaum DM, McEuen PL, Davis RC: Measurement of the adhesion force between carbon nanotubes and a silicon dioxide substrate.

    Nano Lett. 2006, 6(5):953-957.

    COI number [1:CAS:528:DC%2BD28XjsFWmtbs%3D]; Bibcode number [2006NanoL...6..953W]

    PubMed Abstract | Publisher Full Text OpenURL

  13. Manoharan MP, Haque MA:

    Role of adhesion in shear strength of nanowire-substrate interfaces. J. Phys. D Appl. Phys. 2009, 42(9):095304. OpenURL

  14. Sun YG, Mayers B, Herricks T, Xia YN: Polyol synthesis of uniform silver nanowires: a plausible growth mechanism and the supporting evidence.

    Nano Lett. 2003, 3(7):955-960.

    COI number [1:CAS:528:DC%2BD3sXksVSjtrc%3D]; Bibcode number [2003NanoL...3..955S]

    Publisher Full Text OpenURL

  15. Wang ZL: Zinc oxide nanostructures: growth, properties and applications.

    J. Phys. Condens. Matter 2004, 16(25):R829-R858.

    COI number [1:CAS:528:DC%2BD2cXmtVyhtLY%3D]; Bibcode number [2004JPCM...16R.829W]

    Publisher Full Text OpenURL

  16. Fan FR, Ding Y, Liu DY, Tian ZQ, Wang ZL: Facet-selective epitaxial growth of heterogeneous nanostructures of semiconductor and metal: ZnO nanorods on Ag nanocrystals.

    J. Am. Chem. Soc 2009, 131(34):12036-12037. PubMed Abstract | Publisher Full Text OpenURL

  17. Soudi A, Khan EH, Dickinson JT, Gu Y: Observation of unintentionally incorporated nitrogen-related complexes in ZnO and GaN nanowires.

    Nano Lett 2009, 9(5):1844-1849. PubMed Abstract | Publisher Full Text OpenURL

  18. Zhu Y, Espinosa HD: An electromechanical material testing system for in situ electron microscopy and applications.

    Proc. Natl Acad. Sci. USA 2005, 102(41):14503-14508.

    COI number [1:CAS:528:DC%2BD2MXhtFKjsLnK]; Bibcode number [2005PNAS..10214503Z]

    PubMed Abstract | Publisher Full Text | PubMed Central Full Text OpenURL

  19. Zhu Y, Xu F, Qin QQ, Fung WY, Lu W: Mechanical properties of vapor-liquid-solid synthesized silicon nanowires.

    Nano Lett. ASAP 2009, 9(11):3934-3939. Publisher Full Text OpenURL

  20. Chajes A: Principles of Structural Stability Theory. Prentice-Hall, Englewood Cliffs, NJ; 1974. OpenURL

  21. Bowden FP, Tabor D: The Friction and Lubrication of Solids. Oxford University Press, Oxford, UK; 1954. OpenURL

  22. Greenwood JA, Williams JBP: Contact of nominally flat surfaces.

    Proc. R. Soc. Lond. A Math. Phys. Sci. 1966, 295(1442):300.

    COI number [1:CAS:528:DyaF2sXht1ChsA%3D%3D]; Bibcode number [1966RSPSA.295..300G]

    Publisher Full Text OpenURL

  23. Johnson KL, Kendall K, Roberts AD: Surface energy and contact of elastic solids.

    Proc. R. Soc. Lond. A Math. Phys. Sci. 1971, 324(1558):301.

    COI number [1:CAS:528:DyaE3MXkvFWmtrY%3D]; Bibcode number [1971RSPSA.324..301J]

    Publisher Full Text OpenURL

  24. Derjaguin BV, Muller VM, Toporov YP: Effect of contact deformations on adhesion of particles.

    J. Colloid Interface Sci. 1975, 53(2):314-326.

    COI number [1:CAS:528:DC%2BD1MXhtlGhtLrE]

    Publisher Full Text OpenURL

  25. Maugis D: Adhesion of spheres—the JKR-DMT transition using a Dugdale model.

    J. Colloid Interface Sci. 1992, 150(1):243-269.

    COI number [1:CAS:528:DyaK38XhvVaiu7s%3D]

    Publisher Full Text OpenURL

  26. Tabor D: Surface forces and surface interactions.

    J. Colloid Interface Sci. 1977, 58(1):2-13.

    COI number [1:CAS:528:DyaE1MXht1Onsw%3D%3D]

    Publisher Full Text OpenURL

  27. Carpick RW, Ogletree DF, Salmeron M: A general equation for fitting contact area and friction vs load measurements.

    J. Colloid Interface Sci. 1999, 211(2):395-400.

    COI number [1:CAS:528:DyaK1MXhtlCis78%3D]

    PubMed Abstract | Publisher Full Text OpenURL

  28. Israelachvili JN: Intermolecular and Surface Forces. Academic Press, Amsterdam; 1991. OpenURL

  29. Kim M, Hong YJ, Yoo J, Yi GC, Park GS, Kong KJ, Chang H: Surface morphology and growth mechanism of catalyst-free ZnO and MgxZn1−xO nanorods.

    Phys. Status Solidi-Rapid Res. Lett. 2008, 2(5):197-199.

    COI number [1:CAS:528:DC%2BD1cXhsVSnu7nL]

    Publisher Full Text OpenURL

  30. Lucas M, Mai W, Yang R, Wang ZL, Riedo E: Aspect ratio dependence of the elastic properties of ZnO nanobelts.

    Nano Lett. 2007, 7(5):1314-1317.

    COI number [1:CAS:528:DC%2BD2sXktlChsLc%3D]; Bibcode number [2007NanoL...7.1314L]

    PubMed Abstract | Publisher Full Text OpenURL

  31. Xu DW, Ravi-Chandar K, Liechti KA: On scale dependence in friction: transition from intimate to monolayer-lubricated contact.

    J. Colloid Interface Sci. 2008, 318(2):507-519.

    COI number [1:CAS:528:DC%2BD1cXhtFalug%3D%3D]

    PubMed Abstract | Publisher Full Text OpenURL

  32. Bhushan B: Nanotribology and Nanomechanics: An Introduction. Heidelberg, Springer; 2008. OpenURL

  33. Li QY, Kim KS: Micromechanics of friction: effects of nanometre-scale roughness.

    Proc. R. Soc. Lond. A Math. Phys. Sci. 2008, 464(2093):1319-1343.

    Bibcode number [2008RSPSA.464.1319L]

    Publisher Full Text OpenURL

  34. Miyazaki HT, Tomizawa Y, Saito S, Sato T, Shinya N: Adhesion of micrometer-sized polymer particles under a scanning electron microscope.

    J. Appl. Phys. 2000, 88(6):3330-3340.

    COI number [1:CAS:528:DC%2BD3cXmt1aqsb8%3D]; Bibcode number [2000JAP....88.3330M]

    Publisher Full Text OpenURL

  35. Ding WQ: Micro/nano-particle manipulation and adhesion studies.

    J. Adhesion Sci. Technol. 2008, 22(5–6):457-480.

    COI number [1:CAS:528:DC%2BD1cXps1OjtLk%3D]

    Publisher Full Text OpenURL

  36. Qin QQ, Xu F, Zhu Y: Adhesion between zinc oxide nanowires and gold coated surfaces.

    J. Appl. Phys 2009.

    submitted

    OpenURL

  37. Salvetat JP, Briggs GAD, Bonard JM, Bacsa RR, Kulik AJ, Stockli T, Burnham NA, Forro L: Elastic and shear moduli of single-walled carbon nanotube ropes.

    Phys. Rev. Lett. 1999, 82(5):944-947.

    COI number [1:CAS:528:DyaK1MXotV2itw%3D%3D]; Bibcode number [1999PhRvL..82..944S]

    Publisher Full Text OpenURL

  38. Ni H, Li XD, Gao HS: Elastic modulus of amorphous SiO2 nanowires.

    Appl. Phys. Lett. 2006, 88:043108. Publisher Full Text OpenURL

  39. Zhu Y, Ke C, Espinosa HD: Experimental techniques for the mechanical characterization of one-dimensional nanostructures.

    Exp. Mech. 2007, 47(1):7-24. Publisher Full Text OpenURL