Tunable Visible Emission of Ag-Doped CdZnS Alloy Quantum Dots

Ruchi Sethi, Lokendra Kumar*, Prashant K Sharma and AC Pandey

Author affiliations

Nanophosphor Application Centre, Physics Department, University of Allahabad, Allahabad, 211 002, India

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2009, 5:96-102  doi:10.1007/s11671-009-9449-9

Published: 13 October 2009

Abstract

Highly luminescent Ag-ion-doped Cd1−xZnxS (0 ≤ x ≤ 1) alloy nanocrystals were successfully synthesized by a novel wet chemical precipitation method. Influence of dopant concentration and the Zn/Cd stoichiometric variations in doped alloy nanocrystals have been investigated. The samples were characterized by X-ray diffraction (XRD) and high resolution transmission electron microscope (HRTEM) to investigate the size and structure of the as prepared nanocrystals. A shift in LO phonon modes from micro-Raman investigations and the elemental analysis from the energy dispersive X-ray analysis (EDAX) confirms the stoichiometry of the final product. The average crystallite size was found increasing from 1.0 to 1.4 nm with gradual increase in Ag doping. It was observed that photoluminescence (PL) intensity corresponding to Ag impurity (570 nm), relative to the other two bands 480 and 520 nm that originates due to native defects, enhanced and showed slight red shift with increasing silver doping. In addition, decrease in the band gap energy of the doped nanocrystals indicates that the introduction of dopant ion in the host material influence the particle size of the nanocrystals. The composition dependent bandgap engineering in CdZnS:Ag was achieved to attain the deliberate color tunability and demonstrated successfully, which are potentially important for white light generation.

Keywords:
Alloy; Nanocrystals; Photoluminescence; Raman spectroscopy