Open Access Nano Express

Anodic Aluminum Oxide Membrane-Assisted Fabrication of β-In2S3Nanowires

Jen-Bin Shi1, Chih-Jung Chen2, Ya-Ting Lin2*, Wen-Chia Hsu1, Yu-Cheng Chen2 and Po-Feng Wu2

Author Affiliations

1 Department of Electronic Engineering, Feng Chia University, Taichung, 40724, Taiwan

2 The Graduate Institute of Electrical and Communications Engineering, Feng Chia University, 100, Wen-Hwa Rd, Seatwen, Taichung, 40724, Taiwan

For all author emails, please log on.

Nanoscale Research Letters 2009, 4:1059-1063  doi:10.1007/s11671-009-9357-z


The electronic version of this article is the complete one and can be found online at:


Received:9 March 2009
Accepted:24 May 2009
Published:6 June 2009

© 2009 to the authors

Abstract

In this study, β-In2S3nanowires were first synthesized by sulfurizing the pure Indium (In) nanowires in an AAO membrane. As FE-SEM results, β-In2S3nanowires are highly ordered, arranged tightly corresponding to the high porosity of the AAO membrane used. The diameter of the β-In2S3nanowires is about 60 nm with the length of about 6–8 μm. Moreover, the aspect ratio of β-In2S3nanowires is up to 117. An EDS analysis revealed the β-In2S3nanowires with an atomic ratio of nearly S/In = 1.5. X-ray diffraction and corresponding selected area electron diffraction patterns demonstrated that the β-In2S3nanowire is tetragonal polycrystalline. The direct band gap energy (Eg) is 2.40 eV from the optical measurement, and it is reasonable with literature.

Keywords:
Nanomaterials; In2S3; Nanowire; AAO

Introduction

Nowadays, one-dimensional (1-D) nanomaterials (nanorods, nanowires, nanobelts and nanotubes) have been attractive due to their physical and chemical properties. These nanostructures in particular show results in electronics [1], magnetic [2], optics, etc., that have great potential applications in the next generation of nanodevices [3]. Various methods such as chemical vapor deposition (CVD), laser ablation, thermal evaporation, hydrothermal process, and anodic aluminum oxide (AAO) membrane-assisted synthesis method have been employed to prepare 1-D nanomaterials. AAO membrane-based assembling has been widely applied in recent years to produce nanowires with extremely long length and high aspect ratios, and it also provides a simple, rapid and cheap way for fabricating nanowires as aligned arrays [4,5].

Indium sulphide (In2S3) is an III-VI compound material, and it exists in three phases at normal pressure: α (cubic), β (tetragonal) and γ (trigonal) [6]. β-In2S3, an ordered-defect superstructure of the defect-spinel α-In2S3, is stable below 420 °C [6], whereas γ-In2S3 is only stable above 754 °C, unless by adding As or Sb [7]. β-In2S3 crystal is known an n-type semiconductor with the band gap energy of 2.0 eV [6]. Furthermore, its photoconductive properties make it a promising candidate for photovoltaic applications such as solar cells [8]. Solar cell devices prepared by using β-In2S3 as a buffer layer show 16.4% conversion efficiency, which is very close to that of the standard CdS buffer layer [9].

A variety of methods have been developed into synthesized In2S3 powder, thin films, and nanofibers. Powder of β-In2S3 was synthesized using indium chloride (InCl3) and thioacetamide (CH3CSNH2) as precursors via the sonochemical route [10]. β-In2S3 thin films were prepared using the CSP technique, and the spray solutions were mixtures of indium chloride (InCl3) and thiourea (CS(NH2)2) [11]. In addition, β-In2S3 nanofibers were prepared using indium chloride and thiourea as source precursors by hydrothermal method with AAO membrane at 150 °C for 15 h. [12]. However, β-In2S3 nanowires were fabricated within AAO template synthesis, using the electrodeposition and sulfurizing methods that are not yet reported.

To fabricate the β-In2S3nanowires, an effective and economical technique-anodic alumina oxide (AAO) membrane-assisted method was utilized in this study. The microstructure and optical properties of β-In2S3nanowires are discussed.

Experimental

Porous anodic aluminum oxide (AAO) membrane with average channel diameter of 60 nm and thickness of 25 μm was fabricated by two-step anodization process as described previously [4,5]. First, high purity aluminum sheet (99.9995%) was anodized in the oxalic acid solution under constant voltage 40 V for several hours. Subsequently, the anodized Al sheet was put into H3PO4 solution to completely remove the alumina layer. The AAO membrane can be fabricated by repeating the anodization process under the same conditions of the first step anodization. After the anodization, the AAO membrane was obtained by etching away the underlying aluminum substrates with HgCl2 solution. The transparent AAO membrane was immersed in H3PO4 solution to widen the nanochannels. Finally, the diameter of the nanochannel was about 60 nm.

In order to prepare for pure Indium (In) nanowires, a layer of Pt was sputtered onto one side of the membrane acting as the working electrode in a standard two-electrode electrochemical cell. Pure Indium (In) was electrodeposited inside the nanochannels of the AAO membrane under constant voltage, using an electrolyte containing In(SO4)3, H3BO3,and distilled water. The AAO membrane with pure Indium (In) nanowires was washed with distilled water and air dried, put into a glass tube and together with sulfur powder (99.99%). The glass tube was evacuated by using a pump, and it was placed into the furnace. The samples were then heated from room temperature (heating rate: 5 °C/min) to 500 °C and held at this temperature for 10 h to completely sulfurize the pure Indium (In) nanowires. It is expected that S atoms would react with the In to form β-In2S3.

The morphologies of the as-prepared AAO membrane and the β-In2S3nanowires were analyzed by field emission scanning electron microscopy/energy dispersive spectrometer (FE-SEM/EDS, HITACHI S-4800). The crystal structure of the nanowires was examined by X-ray diffraction (XRD, SHIMADZU XRD-6000) utilizing Cu Kα radiation. More details about the microstructure of the β-In2S3nanowires were investigated by the high-resolution transmission electron microscopy/corresponding selected area electron diffraction (HR-TEM/SAED, JEOL JEM-2010). For HR-TEM and SAED analysis, the β-In2S3nanowires were dispersed in ethanol and vibrated for few minutes. Then, a few drops of the resulting suspension were dripped onto a copper grid. For optical analysis, the AAO membrane was dissolved by NaOH solution at room temperature and washed with distilled water to expose freely nanowires of β-In2S3. After the β-In2S3nanowires are absolutely dispersed in distilled water using a supersonic disperser, the absorption spectra of the β-In2S3nanowires were measured on an UV/Visible/NIR spectrophotometer (HITACHI U-3501).

Results and Discussion

According to the FE-SEM images of Fig. 1a, it can be seen the surface of AAO membrane was still kept clean after pure Indium (In) nanowires were sulfurized at 500 °C for 10 h. Figure 1b shows a typical FE-SEM image for the cross-section image of β-In2S3nanowires. It can be clearly seen that the β-In2S3nanowires were wellfilled in nanochannels of the AAO membrane. The length of the β-In2S3nanowires was in the average range 6–8 μm with the aspect ratio around 117. Figure 1c reveals the high-magnification FE-SEM image, it can be observed that the β-In2S3nanowires were independent and parallel to each other with the diameter, which is about 60 nm. The EDS spectrum of the β-In2S3nanowires is not shown. The result of EDS measurement reveals the atomic ratio of In and S with 41.79:58.21 and is very close to 1:1.5, which is in good agreement with the XRD result. After dissolving the AAO membrane by thorough chemical etching and followed by rinsing with distilled water, the β-In2S3nanowires are still on the conducting substrate surface (Pt). Figure 1d reveals the β-In2S3nanowires without AAO membrane. When the AAO membrane was dissolved away, the individual β-In2S3nanowires were observed almost the same with the diameter of the channels of the AAO membrane. Thus, it can be seen the dimension of the β-In2S3nanowires was controlled by AAO membrane.

thumbnailFigure 1. FE-SEM images ofaplane-view,bcross-section view of β-In2S3nanowires arrays with the pore diameter of about 60 nm in the AAO membrane,ccross-section view at high magnification of β-In2S3nanowires arrays in the AAO membrane, anddthe AAO membrane was absolutely dissolved in NaOH solution

Figure 2 shows the X-ray powder diffraction (XRD) spectra of the as-prepared β-In2S3 nanowires without AAO membrane, which makes the crystal structure of the β-In2S3 nanowires convenient for characterization. All the peaks were indexed as the reported data for β-In2S3 (JCPDS Card no. 32-0456). After the pure Indium (In) nanowires were completely sulfurized, no diffraction peaks of In and S or other impurities have been found. Furthermore, the In peaks totally disappear and the β-In2S3 peaks appear after sulfurize the pure Indium (In) nanowires. Metal oxides such as In2O3 nanowires have been prepared by oxidation of pure Indium (In) nanowires [13], and it is generally accepted that the chemical reaction of oxidation and sulfurization are similar to each other. Hence, the technique used here for formation of β-In2S3 is understandable. The reaction equation of β-In2S3 nanowires can be expressed as follows:

(1)

thumbnailFigure 2. X-ray diffraction patterns of β-In2S3nanowires without AAO membrane

In which the S atoms would react with In atoms at high temperatures to form β-In2S3nanowires. The completeness of reaction is mainly dominated by time and temperature, long periods and high temperatures of the sulfurization process were needed to prepare the fine crystalline β-In2S3nanowires. We observed that the β-In2S3nanowires were completely formed when the sulfurization time reached to 10 h and the temperatures up to 500 °C.

Detailed information on the microstructure of as-prepared β-In2S3nanowires was obtained by HR-TEM. Low-magnification HR-TEM image (Fig. 3a) illustrates the numerous β-In2S3nanowires. Figure 3b reveals the HR-TEM image of an individual β-In2S3nanowire. The diameter of the nanowire is about 60 nm. In Fig. 3c, the corresponding SAED pattern of an individual nanowire exhibits a polycrystalline. Moreover, the concentric diffraction rings could be indexed outwards as (2 2 12), (1 0 9), (0 0 12) and (1 0 3) lattice planes of tetragonal β-In2S3. The HR-TEM image of the nanowires (Fig. 3d) shows the parallel fringes with a spacing of 0.1913 nm, which can be assigned to the (2 2 12) plane of β-In2S3.

thumbnailFigure 3. aThe low-magnification HR-TEM image of β-In2S3nanowires,bthe high-magnification HR-TEM image of an individual β-In2S3nanowire,cSAED pattern of an individual β-In2S3nanowire, anddHR-TEM image of a single β-In2S3nanowire with lattice fringes

Figure 4 shows the UV/Visible/NIR absorption spectra of the as-grown β-In2S3 nanowires, recorded in the wavelength range 200–900 nm, which obviously reveals a broad absorption peak around 350 nm. Recently, Shen et al. reported that the bulk of In2S3 was prepared by In(NO3)3·4.5H2O with H2S at 300 °C for 3 h in the muffle oven [14]. They observed an absorption onset of bulk In2S3 at 650 nm. In addition, In2S3 colloidal thin films were synthesized by the spin-coating method [15]. They prepared a yellow colloid suspension by adding H2S gas into an InCl3 solution, containing a small amount of acetic acid as a stabilizer. The thin film was heated at 400 °C for 30 min under a N2 atmosphere. In2S3 colloidal thin films have an absorption edge at about 550 nm. Furthermore, flowerlike β-In2S3 assembled with nanoflakes were synthesized by the hydrothermal method using InCl3·4H2O and L-cysteine [16]. The absorption peak of In2S3 flowerlike is located at 395 nm. In addition, In2S3 hollow spheres were prepared by dodecanethiol-assisted hydrothermal process at 180 °C for 12 h, employing InCl3·4H2O and L-cysteine as precursors [17]. They observed an absorption peak of In2S3 hollow spheres located at 251 nm. However, our value of absorption peak is between the largest value of bulk (650 nm) and the smallest value of hollow spheres (251 nm). Our value of absorption peak is reasonable with literature [14-17].

thumbnailFigure 4. UV/Visible/NIR absorption spectra with β-In2S3nanowires and (αhν)2versusplot (inset)

In order to determine the band gap energy (Eg) of the β-In2S3 nanowires, the optical absorption coefficient (α) at the absorption edge may be expressed as [18]:

(2)

where hv is the photon energy, A is the optical transition dependent constant, Eg is the optical band gap, and m is a constant that depends on the types of transitions involved. The values of m = 1/2, 3/2, 2, and 3 are for direct allowed, direct forbidden, indirect allowed, and indirect forbidden transitions, respectively. This equation gives band gap (Eg), when straight portion of (αhν)1/m against plot is extrapolated to the point α = 0. The analysis of the absorption spectra obtained for our samples shows that the spectral variation of the absorption coefficient, within the fundamental absorption region can be fitted by Eq. 2. However, m = 3/2, 2, and 3, the band gap energies were found to be a negative number, which is not reasonable in physics. The inset in Fig. 4 shows the (αhν)2 against plot. Relationship fitting to the absorption spectra of β-In2S3 as m = 1/2, which is the allowed direct transition for these nanowires. In this inset figure, we observed that the curve has a very good straight line fit from 2.7 to 2.9 eV. This result indicates that the optical energy gap is direct transition. We also observed that the curve has been breakaway this line range when the photon energy is above 2.9 eV. The band gap energy (Eg) of β-In2S3 nanowires with diameter of about 60 nm is estimated to be 2.40 eV as m = 1/2 for extrapolation. In literature [19], powder of β-In2S3 was synthesized using InCl3 and CH3CSNH2 as precursors followed by annealing in Ar atmosphere in the temperature range 573–1,123 K. The grain size of powder varied in the range 0.40–1.48 μm for different annealing temperatures. The band gap energy of β-In2S3 powder for various grain sizes was between 2.12 and 2.14 eV. Moreover, thin films of In2S3 were prepared from In2S3 powder using vacuum evaporation with resistively heated graphite crucible [20]. The average grain sizes of In2S3 thin film were around 0.22 μm. The optical band gaps of In2S3 thin film for different annealing temperatures and times were between 1.75 and 2.19 eV. β-In2S3 films were prepared by rapid heating of metallic Indium (In) films in H2S atmosphere [21]. The grain sizes of the β-In2S3 films were in the range 22–30 nm. The films exhibit the higher band gap of 2.58 eV. Consequently, our band gap energy of β-In2S3 nanowires with 60 nm is between the largest band gap energy with grain sizes of 22–30 nm (2.58 eV) and the smallest band gap energy with grain sizes around 0.22 μm (1.75 eV). Our band gap energy of β-In2S3 nanowires with 60 nm is acceptable with literature [19-21].

Conclusions

In summary, we have presented a simple, inexpensive, and reasonable method to fabricate β-In2S3nanowires. The β-In2S3nanowires were first fabricated by sulfurizing the pure Indium (In) nanowires at 500 °C for 10 h, which is embedded in an AAO membrane. β-In2S3nanowires have high wire packing densities with uniform wire diameters and lengths of about 60 nm and 6–8 μm, respectively. The analysis of the HR-TEM/SAED revealed that the β-In2S3nanowire is polycrystalline. The β-In2S3nanowires exhibited a linear relationship at 2.7–2.9 eV asm = 1/2, indicating that the direct band gap energy is 2.40 eV.

Acknowledgments

The research was supported by the National Science Council of R.O·C. under grant No. NSC-96-2122-M-035-003-MY2.

References

  1. Yi G, Schwarzacher W:

    Appl. Phys. Lett.. 1999, 74:1746.

    COI number [1:CAS:528:DyaK1MXhvV2ntbY%3D]; Bibcode number [1999ApPhL..74.1746Y]

    Publisher Full Text OpenURL

  2. Ross CA, Hwang M, Shima M, Smith HI, Farhoud M, Savas TA, et al.:

    J. Magn. Magn. Mater.. 2002, 249:200.

    COI number [1:CAS:528:DC%2BD38XotFOitb8%3D]; Bibcode number [2002JMMM..249..200R]

    Publisher Full Text OpenURL

  3. Zach MP, Ng KH, Penner RM:

    Science. 2000, 290:2120.

    COI number [1:CAS:528:DC%2BD3cXptVyis78%3D]; Bibcode number [2000Sci...290.2120Z]

    Publisher Full Text OpenURL

  4. Shi JB, Chen YJ, Lin YT, Wu C, Chen CJ, Lin JY:

    Jpn. J. Appl. Phys.. 2006, 45:9075.

    COI number [1:CAS:528:DC%2BD2sXhs1eltw%3D%3D]; Bibcode number [2006JaJAP..45.9075S]

    Publisher Full Text OpenURL

  5. Shi JB, Chen YC, Lee CW, Lin YT, Wu C, Chen CJ:

    Mater. Lett.. 2008, 62:15.

    COI number [1:CAS:528:DC%2BD2sXhtlejsrzP]

    Publisher Full Text OpenURL

  6. Diehl R, Nitsche R:

    J. Cryst. Growth. 1975, 28:306.

    COI number [1:CAS:528:DyaE2MXktlGrtbw%3D]; Bibcode number [1975JCrGr..28..306D]

    Publisher Full Text OpenURL

  7. Diehl R, Carpentier CD, Nitsche R:

    Acta Crystallogr. B. 1976, 32:1257. Publisher Full Text OpenURL

  8. Bube RH, McCaroll WH:

    J. Phys. Chem. Solids. 1959, 10:333.

    COI number [1:CAS:528:DyaF3cXjt1Ohuw%3D%3D]; Bibcode number [1959JPCS...10..333B]

    Publisher Full Text OpenURL

  9. Barreau N, Marsillac S, Albertini D, Bernede JC:

    Thin Solid Films. 2002, 403–404:331. Publisher Full Text OpenURL

  10. Gorai S, Chaudhuri S:

    Mater. Chem. Phys.. 2005, 89:332.

    COI number [1:CAS:528:DC%2BD2cXhtVamtLbL]

    Publisher Full Text OpenURL

  11. John TT, Kartha CS, Vijayakumar KP, Abe T, Kashiwaba Y:

    Vacuum. 2006, 80:870.

    COI number [1:CAS:528:DC%2BD28XltVektbc%3D]

    Publisher Full Text OpenURL

  12. Zhu X, Ma J, Wang Y, Tao J, Zhou J, Zhao Z, Xie L, Tian H:

    Mater. Res. Bull.. 2006, 41:1584.

    COI number [1:CAS:528:DC%2BD28XmvVakur8%3D]

    Publisher Full Text OpenURL

  13. Zheng MJ, Zhang LD, Li GH, Zhang XY, Wang XF:

    Appl. Phys. Lett.. 2001, 79:839.

    COI number [1:CAS:528:DC%2BD3MXls1Ortbg%3D]; Bibcode number [2001ApPhL..79..839Z]

    Publisher Full Text OpenURL

  14. Shen S, Guo L:

    J. Solid State Chem.. 2006, 179:2629.

    COI number [1:CAS:528:DC%2BD28Xns1Srtbo%3D]; Bibcode number [2006JSSCh.179.2629S]

    Publisher Full Text OpenURL

  15. Yasaki Y, Sonoyama N, Sakata T:

    J. Electroanal. Chem.. 1999, 469:116.

    COI number [1:CAS:528:DyaK1MXksV2rt7g%3D]

    Publisher Full Text OpenURL

  16. Chen LY, Zhang ZD, Wang WZ:

    J. Phys. Chem. C. 2008, 112:4117.

    COI number [1:CAS:528:DC%2BD1cXisVCnu7Y%3D]

    Publisher Full Text OpenURL

  17. Zhao P, Huang T, Huang K:

    J. Phys. Chem. C. 2007, 111:12890.

    COI number [1:CAS:528:DC%2BD2sXptVWlu7s%3D]

    Publisher Full Text OpenURL

  18. Burns G: Solid State Physics. Academic Press, Orlando; 1985. OpenURL

  19. Gorai S, Guha P, Ganguli D, Chaudhuri S:

    Mater. Chem. Phys.. 2003, 82:974.

    COI number [1:CAS:528:DC%2BD3sXpt1GgtrY%3D]

    Publisher Full Text OpenURL

  20. Timoumi A, Bouzouita H, Brini R, Kanzari M, Rezig B:

    Appl. Surf. Sci.. 2006, 253:306.

    COI number [1:CAS:528:DC%2BD28XhtFKksL%2FJ]; Bibcode number [2006ApSS..253..306T]

    Publisher Full Text OpenURL

  21. Yoosuf R, Jayaraj MK:

    Sol. Energy Mater. Sol. Cells. 2005, 89:85.

    COI number [1:CAS:528:DC%2BD2MXmsVWnu74%3D]

    Publisher Full Text OpenURL