Open Access Nano Express

Synthesis of YVO4:Eu3+/YBO3Heteronanostructures with Enhanced Photoluminescence Properties

Hongliang Zhu1*, Haihua Hu2, Zhengkai Wang1 and Diantai Zuo1

Author Affiliations

1 Center of Materials Engineering, Zhejiang Sci-Tech University, Xiasha University Town, 310018, Hangzhou, China

2 Zhejiang University City College, 310015, Hangzhou, China

For all author emails, please log on.

Nanoscale Research Letters 2009, 4:1009-1014  doi:10.1007/s11671-009-9349-z

The electronic version of this article is the complete one and can be found online at:

Received:6 January 2009
Accepted:14 May 2009
Published:29 May 2009

© 2009 to the authors


Novel YVO4:Eu3+/YBO3core/shell heteronanostructures with different shell ratios (SRs) were successfully prepared by a facile two-step method. X-ray diffraction, transmission electron microscopy and X-ray photoelectron spectroscopy were used to characterize the heteronanostructures. Photoluminescence (PL) study reveals that PL efficiency of the YVO4:Eu3+nanocrystals (cores) can be improved by the growth of YBO3nanocoatings onto the cores to form the YVO4:Eu3+/YBO3core/shell heteronanostructures. Furthermore, shell ratio plays a critical role in their PL efficiency. The heteronanostructures (SR = 1/7) exhibit the highest PL efficiency; its PL intensity of the5D07F2emission at 620 nm is 27% higher than that of the YVO4:Eu3+nanocrystals under the same conditions.

Core/shell heteronanostructures; Nanophosphors; Photoluminescence; Yttrium vanadate; Yttrium borate


Rare-earth (RE)-doped phosphors have a broad range of applications in cathode ray tubes (CRTs), plasma display panels (PDPs), field emission displays (FEDs), X-ray detectors, fluorescent lamps and so on [1-3]. In recent years, RE-doped nanophosphors have received a great deal of research attention due to the unique applications in higher-resolution displays, drug delivery system and biological fluorescence labeling [4-8]. Furthermore, fluorescent lamps made from small-sized phosphors always have high-packing density and low loading [9]. RE-doped nanophosphors are expected to have high brightness and luminescence quantum yield for practical applications. Unfortunately, high specific surface area and surface defects of the nanophosphors always result in serious surface recombination, which is a pathway for nonradiative relaxation [10]. Consequently, RE-doped nanophosphors have lower luminescence efficiency compared to their corresponding bulk powder phosphors [11,12]. More attention should be paid to improve the luminescence efficiency of RE-doped nanophosphors.

During the past decade, core/shell heteronanostructures have been widely investigated to obtain better properties [13,14]. Luminescence efficiency of RE-doped nanophosphors can be improved by forming core/shell heteronanostructures, because surface defects and surface recombination of the nanophosphors (cores) are greatly reduced by the nanocoatings (shells) [11,15]. Among RE-doped phosphors, europium ions–doped yttrium orthovanadate (YVO4:Eu3+) is an important red phosphor, which has been commercially used in CRTs, high-pressure mercury lamps and color television due to its excellent luminescence properties [2,3]. Many literatures have reported the preparation and luminescence properties of YVO4:Eu3+ nanophosphors [16-18], but few measures have been taken to improve their luminescence efficiency. In this paper, we propose novel YVO4:Eu3+/YBO3 core/shell heteronanostructures that exhibit enhanced photoluminescence efficiency. Compared to the reported heteronanostructures of YVO4:Eu3+ such as Y2O3:Eu3+@SiO2@YVO4:Eu3+, SiO2@YVO4:Eu3+ and YV0.7P0.3O4:Eu3+,Bi3+@SiO2[19-21], yttrium borate (YBO3), is used as shell material in this new heteronanostructures. YBO3 has excellent properties such as high VUV transparency, high stability, low synthesis temperature and exceptional optical damage threshold [22,23], so the new core/shell heteronanostructures proposed here may have promising applications in the fields of display, lighting and bio-nanotechnology.


The YVO4:Eu3+/YBO3 core/shell heteronanostructures were prepared by a facile two-step method. The YVO4:Eu3+ nanocrystals (cores) doped with 5 mol% europium were prepared by hydrothermal method. The YBO3 nanocoatings (shells) were grown onto the cores by the sol–gel method reported in our previous literature [22]. The shell ratio (SR) is molar percentage of the shell material (YBO3) in the core/shell heteronanostructures. In this study, different shell ratios such as 1/9, 1/8, 1/7, 1/5, 1/3, 1/2 and 2/3 were adopted, so a total of seven heteronanostructures were prepared.

Preparation of YVO4:Eu3+Nanocrystals

To 130 mL of deionized water, 30.4 mL of Y(NO3)3solution (0.15 mol/L), 1.6 mL of Eu(NO3)3solution (0.15 mol/L) and 0.758 g of NaVO3·2H2O were added under vigorous magnetic stirring for 30 min. The pH value of the solution was adjusted to 9.5 using ammonia under stirring. Then, the above solution was transferred into a Teflon-lined stainless steel autoclave (capacity 200 mL) and sealed. The autoclave was heated at 200 °C for 16 h and cooled naturally to room temperature. Finally, the YVO4:Eu3+nanocrystals were collected by centrifugation.

Preparation of Sol–Gel Solution

To 100 mL of water–ethanol solution (the volume ratio is 1:4) 3.83 g of Y(NO3)3·6H2O and 0.68 g of H3BO3(~10 mol% of excess) were added under stirring. To the above solution, 6.30 g of citric acid (CA) and 12.00 g of PEG 6000 (the molar ratio of Y(NO3), CA, and PEG was 5:15:1) were added. Herein, CA and PEG were used as the chelating and cross-linking reagents respectively. The above solution was stirred for 5 h and subsequently aged for 24 h. Finally, highly transparent sol–gel solution with yttrium concentration of 0.1 mol/L was obtained.

Preparation of YVO4:Eu3+/YBO3Heteronanostructures

Herein, we take the heteronanostructures (SR = 1/7) as an example to present their detailed procedures. The YVO4:Eu3+nanocrystals (4.56 mmol) obtained in the first step were heated to 120 °C in a petri dish. Then, 6.51 mL of the sol–gel solution was slowly dropped onto the heated YVO4:Eu3+nanocrystals. The obtained sample was annealed at 700 °C in air for 2 h with a heating rate of 1 °C/min. The furnace was cooled to room temperature naturally and the white YVO4:Eu3+/YBO3heteronanostructures (SR = 1/7) were obtained.

In this paper the YVO4:Eu3+(5 mol% Eu) nanocrystals obtained in the first step are called “the original sample”. To avoid the influence of annealing on the photoluminescence property, the original sample was also annealed at 700 °C for 2 h under the same conditions. The annealed original sample is denoted as “YVO4:Eu3+/YBO3core/shell heteronanostructures (SR = 0)”. In addition, YBO3powder was prepared by the above-mentioned sol–gel approach, for comparison.

Characterization and Photoluminescence Property

Phase identification of the products was carried out using a Thermo ARL X’TRA X-ray diffractometer (XRD) with Cu Kα radiation (λ = 1.54178 Å). Morphology observation of the original sample was observed using a JEOL JEM 200 CX transmission electron microscope (TEM). In addition, a Philips CM200 high-resolution transmission electron microscope (HRTEM) with an accelerating voltage of 200 kV was also employed to investigate the morphology and structure of the core/shell heteronanostructures (SR = 1/2). X-ray photoelectron spectroscopy (XPS) measurement was performed on a X-ray photoelectron spectrometer (Model Axis Ultra DLD, Kratos Corp., UK) with a standard MgKα (1,256.6 eV) X-ray source operating at 150 W. All binding energies were referenced to the C 1 s peak at 284.6 eV of the surface adventitious carbon. Photoluminescence (PL) excitation and emission spectra of all the powder products were obtained on a Hitachi fluorescence spectrophotometer (Model F-4600, Hitachi Corporation, Japan) under the same conditions.

Results and Discussion

All as-synthesized products were characterized by XRD, and their data were analyzed by a Thermo ARL WinXRD software package. Figure 1shows XRD patterns of the original sample (the YVO4nanocrystals obtained in the first step), typical core/shell heteronanostructures and YBO3powder. As shown in Fig. 1a, all XRD peaks are in good agreement with the values of YVO4(JCPDS no. 72–0274) confirming that the core material was YVO4:Eu3+. Likewise, the XRD pattern of the YBO3prepared by the sol–gel method is in good agreement with the standard card of YBO3(JCPDS no. 16-0277). Therefore, pure YBO3can be successfully obtained by the sol–gel approach. As shown in Fig. 1b–f, the YVO4:Eu3+/YBO3core/shell heteronanostructures exhibit two series of XRD patterns, namely, those of YVO4and YBO3. In addition, the intensities of the peaks of YBO3increase with the shell ratio. Figure 2shows enlarged XRD patterns of some typical products, which clearly demonstrate that the XRD peaks of both YVO4and YBO3could be found in the heteronanostructures. Therefore, the heteronanostructures are composed of the YVO4:Eu3+and YBO3.

thumbnailFigure 1. XRD patterns of the typical products.aThe YVO4:Eu3+nanocrystals.bfThe YVO4:Eu3+/YBO3heteronanostructures.gThe YBO3powder

thumbnailFigure 2. Enlarged XRD patterns in range of 20–40°.aThe YVO4:Eu3+nanocrystals.bThe YVO4:Eu3+/YBO3(SR = 1/3).cThe YVO4:Eu3+/YBO3(SR = 1/2).dThe YBO3powder

Transmission electron microscope images of the original sample (the YVO4:Eu3+nanocrystals obtained in the first step) and YVO4:Eu3+/YBO3core/shell heteronanostructures (SR = 1/2) are shown in Fig. 3. Figure 3a reveals that the original sample used as the core is nanocrystals. The inset of Fig. 3a clearly shows that the YVO4:Eu3+nanocrystals are around 20 nm in diameter. The core/shell heteronanostructures were obtained by sol–gel growth of YBO3nanocoatings onto the YVO4:Eu3+nanocrystals, so their particle sizes were larger than that of the YVO4:Eu3+nanocrystals. Figure 3b shows TEM image of the core/shell heteronanostructures (SR = 1/2). As shown in Fig. 3b, the heteronanostructures have a similar morphology to the original sample, while the average particle size of the heteronanostructures is approximately twice larger than the original YVO4:Eu3+nanocrystals. This phenomenon indirectly verifies that the YBO3nanocoatings have been grown onto the YVO4:Eu3+nanocrystals by the sol–gel process. Figure 3c is HRTEM image of a single particle of the heteronanostructures (SR = 1/2). Interestingly, two lattice fringes of different spacing appear in a single nanoparticle. The lattice fringes with a d-spacing of about 0.473 nm are found at the center of the particle, while the lattice fringe spacing is 0.308 nm in the peripheral zones of the particle. The two different types of the lattice fringes correspond well to the {101} planes of YVO4(JCPDS no. 72–0274) and the {101} planes of YBO3(JCPDS no. 16-0277), respectively. Therefore, YVO4:Eu3+/YBO3core/shell heteronanostructures were formed by the two-step process.

thumbnailFigure 3. TEM and HRTEM images of the typical products.aTEM image of the YVO4:Eu3+nanocrystals.bTEM image of the YVO4:Eu3+/YBO3(SR = 1/2).cHRTEM image of the YVO4:Eu3+/YBO3(SR = 1/2). The insets are their respective magnified images

X-ray photoelectron spectroscopy is the most commonly used technique for investigating the elemental composition of surface layers 1–5 nm in depth. Herein, XPS was used to further determine the formation of the YVO4:Eu3+/YBO3 core/shell heteronanostructures. If the YVO4:Eu3+ cores were effectively coated with the shell material (YBO3), the XPS peak intensities of the core material (YVO4:Eu3+) would be very low. In other words, whether or not the product was the YVO4:Eu3+/YBO3 core/shell heteronanostructures could be determined by the XPS bands of vanadium. Figure 4 shows XPS spectra of the YVO4:Eu3+/YBO3 heteronanostructures (SR = 1/2), YVO4:Eu3+ nanocrystals and YBO3 powder. XPS spectra in the range of 135–210 eV (Fig. 4a) reveals that B 1 s bands at 191.0 eV are clearly found in the YBO3 powder and the YVO4:Eu3+/YBO3 heteronanostructures [24], while not detected in the YVO4:Eu3+ nanocrystals. The strongest XPS band of vanadium is located at 515.6 eV, which is assigned to V 2p [25]. As shown in Fig. 4b, the V 2p band of the YVO4:Eu3+ nanocrystals is very strong, while that of the YVO4:Eu3+/YBO3 heteronanostructures (SR = 1/2) is much lower. This is because the YVO4:Eu3+ cores have been coated with YBO3 nanocoatings and no enough V 2p XPS signal from the cores was generated by X-ray source.

thumbnailFigure 4. XPS spectra of the YVO4:Eu3+/YBO3heteronanostructures (SR = 1/2) YVO4:Eu3+nanocrystals and YBO3powder in range ofa135–210 eV andb495–555 eV

High photoluminescence (PL) efficiency is important for practical applications of YVO4:Eu3+ nanophosphors. The YVO4:Eu3+/YBO3 core/shell heteronanostructures reported here are expected to exhibit enhanced PL efficiency under the same conditions. All PL excitation and emission spectra of the samples were measured in powder form using the same measurement parameters, so their respective PL emission intensity can relatively represent their PL efficiency. Figure 5a, b shows PL excitation and emission spectra of the YVO4:Eu3+/YBO3 core/shell heteronanostructures and original YVO4:Eu3+ nanocrystals and annealed YVO4:Eu3+ nanocrystals respectively. As shown in the excitation spectra (Fig. 5a), the heteronanostructures and YVO4:Eu3+ nanocrystals exhibit a similar broad excitation band in the range of 200–360 nm with a maximum value at 320 nm, which is ascribed to a charge transfer from the oxygen ligands to the central vanadium atom inside the VO43− ion [5,26]. As shown in Fig. 5b, both the YVO4:Eu3+ nanocrystals and the heteronanostructures show two well-known PL emission bands in the range of 550–650 nm. The two emission bands at 596 nm and 620 nm are assigned to the magnetic-dipole transition 5D07F1 of Eu3+ (596 nm) and the forced electric-dipole transition 5D07F2 of Eu3+ (620 nm), respectively [27]. Herein, the 5D07F2 emission at 620 nm (red emission) is selected as a criterion to determine their relative PL efficiency. The annealed YVO4:Eu3+ nanocrystals exhibit a little stronger PL emission than the original sample, because the crystallinity of the nanocrystals was improved by the annealing process. However, the influence of annealing on the photoluminescence properties can be avoided by comparison between the annealed sample and the heteronanostructures. Figure 5 reveals that all the heteronanostructures except for those with the shell ratios of 1/2 and 2/3 exhibit much stronger photoluminescence than the annealed YVO4:Eu3+ nanocrystals under the same conditions. Furthermore, the shell ratio plays a critical role in the PL efficiency of the heteronanostructures. When SR = 1/7, the heteronanostructures exhibit the highest PL efficiency, whose photoluminescence intensity of the 5D07F2 emission is 27% higher than that of the annealed YVO4:Eu3+ nanocrystals. Therefore, PL efficiency of YVO4:Eu3+ nanophosphor can be improved by forming YVO4:Eu3+/YBO3 core/shell heteronanostructures.

thumbnailFigure 5. Photoluminescence (a)excitation and (b) emission spectra of the YVO4:Eu3+/YBO3core/shell heteronanostructures

Nanostructured materials have a high surface area-to-volume ratio, and this characteristic inevitably results in high surface defects density and serious surface recombination. Therefore, RE-doped nanophosphors suffer more serious nonradiative relaxation than corresponding bulk power phosphors. Consequently, RE-doped nanophosphors always have lower luminescence efficiency. In this paper, the nonradiative decay of the YVO4:Eu3+ nanocrystals was greatly reduced by the YBO3 nanocoating on the YVO4:Eu3+ nanocrystals, so PL emission of the heteronanostructures was enhanced. YBO3 has excellent properties such as high VUV transparency, high stability, low synthesis temperature and exceptional optical damage threshold [22,23]; so, it is an ideal shell material for composite phosphors with core/shell heterostructures. The YBO3 shell ratio is a critical factor in photoluminescence enhancement of the heteronanostructures. Figure 6 shows the plot of change of PL intensity of the 5D07F2 emission at 620 with the shell ratio. The change exhibits a parabola-like curve that reaches the peak at SR = 1/7. When SR < 1/7, PL intensity increases with increasing SR. This is because the surface recombination, surface defects density and surface state density of YVO4:Eu3+ nanocrystals decrease with increasing the YBO3 coating. When SR = 1/7, the surface recombination, surface defects density and surface state density have been decreased to the maximum level, so the strongest PL emission was obtained. When SR > 1/7, PL intensity decreases with increasing molar percentage of the nonluminescent shell material (YBO3).

thumbnailFigure 6. Change of PL intensity of the5D07F2emission of the YVO4:Eu3+/YBO3core/shell heteronanostructures with shell ratio


YVO4:Eu3+/YBO3core/shell heteronanostructures with different shell ratios (SRs) were successfully prepared by sol–gel growth of YBO3nanocoating onto the YVO4:Eu3+nanocrystals. Characterizations by means of XRD, TEM and XPS confirmed the formation of the YVO4:Eu3+/YBO3core/shell heteronanostructures. The heteronanostructures exhibited much stronger photoluminescence (PL) than the YVO4:Eu3+nanocrystals under the same conditions. The shell ratio is a critical factor in PL enhancement of the heteronanostructures. When SR = 1/7, the heteronanostructures exhibited the highest PL efficiency, whose PL intensity (5D07F2emission) was 27% higher than that of the YVO4:Eu3+nanocrystals. YBO3is an ideal shell material for composite phosphors with core/shell heterostructures due to its high VUV transparency, high stability, low synthesis temperature and exceptional optical damage threshold.


This work was supported by the Teaching and Research Award Program for Outstanding Young Teachers in Higher Education Institutions of Zhejiang Province. Authors also thank financial supports from the Doctoral Science Foundation of Zhejiang Sci-Tech University (no. 0803611-Y).


  1. Feldmann C, Jüstel T, Ronda CR, Schmidt PJ:

    Adv. Funct. Mater.. 2003, 13:511.

    COI number [1:CAS:528:DC%2BD3sXls1Wqt7w%3D]

    Publisher Full Text OpenURL

  2. Jüstel T, Nikol H, Ronda C:

    Angew. Chem. Int. Ed.. 1998, 37:3084. Publisher Full Text OpenURL

  3. Blasse G, Grabmeier BC: Luminescent materials. Springer, Berlin; 1994. OpenURL

  4. Chander H:

    Mater. Sci. Eng. Rep.. 2005, 49:113. Publisher Full Text OpenURL

  5. Zhu H, Yang H, Jin D, Wang Z, Gu X, Yao X, Yao K:

    J. Nanopart. Res.. 2008, 10:1149.

    COI number [1:CAS:528:DC%2BD1cXovV2gtbc%3D]

    Publisher Full Text OpenURL

  6. Yang P, Quan Z, Lu L, Huang S, Lin J, Fu H:

    Nanotechnology. 2007, 18:235703.

    Bibcode number [2007Nanot..18w5703Y]

    Publisher Full Text OpenURL

  7. Giaume D, Poggi M, Casanova D, Mialon G, Lahlil K, Alexandrou A, Gacoin T, Boilot J-P:

    Langmuir. 2008, 24:11018.

    COI number [1:CAS:528:DC%2BD1cXhtVOmtrrO]

    Publisher Full Text OpenURL

  8. Ben-David Makhluf S, Arnon R, Patra CR, Mukhopadhyay D, Gedanken A, Mukherjee P, Breitbart H:

    J. Phys. Chem. C.. 2008, 112:12801. Publisher Full Text OpenURL

  9. Rao RP:

    J. Lumin.. 2005, 113:271.

    COI number [1:CAS:528:DC%2BD2MXkvFWqsbs%3D]

    Publisher Full Text OpenURL

  10. Abrams BL, Holloway PH:

    Chem. Rev.. 2004, 104:5783.

    COI number [1:CAS:528:DC%2BD2cXotFSqurY%3D]

    Publisher Full Text OpenURL

  11. Bu W, Hua Z, Chen H, Shi J:

    J. Phys. Chem. B.. 2005, 109:14461.

    COI number [1:CAS:528:DC%2BD2MXmtVChtrs%3D]

    Publisher Full Text OpenURL

  12. Lu S, Madhukar A:

    Nano. Lett.. 2007, 7:3443.

    COI number [1:CAS:528:DC%2BD2sXhtF2jtbzN]; Bibcode number [2007NanoL...7.3443L]

    Publisher Full Text OpenURL

  13. Luan W, Yang H, Fan N, Tu ST:

    Nanoscale. Res. Lett.. 2008, 3:134.

    Bibcode number [2008NRL.....3..134L]

    Publisher Full Text OpenURL

  14. Zhu CQ, Wang P, Wang X, Li Y:

    Nanoscale Res. Lett.. 2008, 3:213.

    COI number [1:CAS:528:DC%2BD1cXhsVyhtrzM]; Bibcode number [2008NRL.....3..213Z]

    Publisher Full Text OpenURL

  15. Louis C, Roux S, Ledoux G, Dujardin C, Tillement O, Cheng BL, Perriat P:

    Chem. Phys. Lett.. 2006, 429:157.

    COI number [1:CAS:528:DC%2BD28Xps1Cqsro%3D]; Bibcode number [2006CPL...429..157L]

    Publisher Full Text OpenURL

  16. Huignard A, Buissette V, Laurent G, Gacoin T, Boilot J-P:

    Chem. Mater.. 2002, 14:2264.

    COI number [1:CAS:528:DC%2BD38XisVarurY%3D]

    Publisher Full Text OpenURL

  17. Li G, Chao K, Peng H, Chen K:

    J. Phys. Chem. C.. 2008, 112:6228.

    COI number [1:CAS:528:DC%2BD1cXjvFeju70%3D]

    Publisher Full Text OpenURL

  18. Riwotzki K, Haase M:

    J. Phys. Chem. B.. 1998, 102:10129.

    COI number [1:CAS:528:DyaK1cXnt12itL0%3D]

    Publisher Full Text OpenURL

  19. Chang M, Tie S:

    Nanotechnology. 2008, 19:075711.

    Bibcode number [2008Nanot..19g5711C]

    Publisher Full Text OpenURL

  20. Darbandi M, Hoheisel W, Nann T:

    Nanotechnology. 2006, 17:4168.

    COI number [1:CAS:528:DC%2BD28XhtFChsLrJ]; Bibcode number [2006Nanot..17.4168D]

    Publisher Full Text OpenURL

  21. Yu M, Lin J, Fang J:

    Chem. Mater.. 2005, 17:1783.

    COI number [1:CAS:528:DC%2BD2MXitVShsrg%3D]

    Publisher Full Text OpenURL

  22. Zhu H, Zhang L, Zuo T, Gu X, Wang Z, Zhu L, Yao K:

    Appl. Surf. Sci.. 2008, 254:6362.

    COI number [1:CAS:528:DC%2BD1cXptVWhsL8%3D]; Bibcode number [2008ApSS..254.6362Z]

    Publisher Full Text OpenURL

  23. Tukia M, Hölsä J, Lastusaari M, Niittykoski J:

    Opt. Mater.. 2005, 27:1516.

    COI number [1:CAS:528:DC%2BD2MXkvFKmt7k%3D]; Bibcode number [2005OptMa..27.1516T]

    Publisher Full Text OpenURL

  24. Khattak GD, Salim MA, Wenger LE, Gilani AH:

    J. Non-Cryst. Solids. 1999, 244:128.

    COI number [1:CAS:528:DyaK1MXhs1aku74%3D]; Bibcode number [1999JNCS..244..128K]

    Publisher Full Text OpenURL

  25. Barreca D, Depero LE, Di Noto V, Rizzi GA, Sangaletti L, Tondello E:

    Chem. Mater.. 1999, 11:255.

    COI number [1:CAS:528:DyaK1MXlslCgtg%3D%3D]

    Publisher Full Text OpenURL

  26. Li Y, Hong G:

    J. Solid. State. Chem.. 2005, 178:645.

    COI number [1:CAS:528:DC%2BD2MXitlCnsr0%3D]

    Publisher Full Text OpenURL

  27. Zhu H, Yang D, Zhu L, Li D, Chen P, Yu G:

    J. Am. Ceram. Soc.. 2007, 90:3095.

    COI number [1:CAS:528:DC%2BD2sXhtFekt7zI]

    Publisher Full Text OpenURL