Open Access Nano Express

Intense Red Catho- and Photoluminescence from 200 nm Thick Samarium Doped Amorphous AlN Thin Films

Muhammad Maqbool1* and Tariq Ali2

Author Affiliations

1 Department of Physics and Astronomy, Ball State University, Muncie, IN, 47306, USA

2 Department of Physics, State University of New York at Buffalo, Buffalo, NY, 14260, USA

For all author emails, please log on.

Nanoscale Research Letters 2009, 4:748-752  doi:10.1007/s11671-009-9309-7


The electronic version of this article is the complete one and can be found online at:


Received:21 January 2009
Accepted:2 April 2009
Published:25 April 2009

© 2009 to the authors

Abstract

Samarium (Sm) doped aluminum nitride (AlN) thin films are deposited on silicon (100) substrates at 77 K by rf magnetron sputtering method. Thick films of 200 nm are grown at 100–200 watts RF power and 5–8 m Torr nitrogen, using a metal target of Al with Sm. X-ray diffraction results show that films are amorphous. Cathodoluminescence (CL) studies are performed and four peaks are observed in Sm at 564, 600, 648, and 707 nm as a result of4G5/26H5/2,4G5/26H7/2,4G5/26H9/2, and4G5/26H11/2transitions. Photoluminescence (PL) provides dominant peaks at 600 and 707 nm while CL gives the intense peaks at 600 nm and 648 nm, respectively. Films are thermally activated at 1,200 K for half an hour in a nitrogen atmosphere. Thermal activation enhances the intensity of luminescence.

Keywords:
Cathodoluminescence; Photoluminescence; Thermal activation; XRD; Samarium; AlN

Introduction

Rear-earth doped nitride semiconductors thin films are attracting increasing attention as phosphor materials, and are used for optical displays [1-5]. Sputter deposited AlN has been shown to be a viable host for luminescent rare earth (RE) ions due to its transparency over a wide range, including the UV, IR, and entire visible range [6-17]. Recent progress toward nitride-based light-emitting diode and electroluminescent devices (ELDs) has been made using crystalline and amorphous AlN doped with a variety of rare-earth elements [1-9]. The electronic structure of the RE ions differ from the other elements and are characterized by an incompletely filled 4fn shell. The 4f electrons lay inside the ion and are shielded from the surroundings by the filled 5s2 and 5p6 electron orbital [17]. When these materials are excited by various means, intense sharp-line emission is observed due to intra-4fn-shells transitions of the rare-earth ion core [18-21]. The amorphous III-nitride semiconductors have the advantage over their crystalline counterpart because the amorphous material can be grown at room temperature with little stress due to lattice mismatch [22]. They may also be more suitable for waveguides and cylindrical and spherical laser cavities because of the elimination of grain boundaries at low-temperature growth [5].

High thermal conductivity, stability, and chemical inertness of AlN also make it very useful for its electrical and thermal applications.

In the present work, luminescence properties of Samarium (Sm) are studied when deposited in AlN host. The spectra obtained provide data in a broad range from 300 to 800 nm. Thus luminescence from the films in UV, visible, and IR are obtained and studied simultaneously. The effect of thermal activation is also studied by activating these materials in a tube furnace up to 1,200 K.

Experimental Details

Thin films of amorphous AlN:Sm were prepared at 77 K by rf magnetron sputtering of an aluminum target of 99.999% purity in a pure nitrogen atmosphere. Doping of thin films with Sm was accomplished by drilling a small hole (0.5 cm diameter) in the aluminum target (4.2 cm diameter) and placing a slug of Sm in the hole. Sm was then co-sputtered with the aluminum. The rf power was varied between 100 and 200 watts. All films were deposited onto 2 cm × 2 cm, or less, p-silicon (100) substrates. The background pressure in the chamber was <3 × 10−5 Torr. Liquid nitrogen was used to keep the temperature of the film at 77 K. The metallic substrate holder was designed such that it had a half inch diameter cylindrical hole from the top. The substrate was pasted on the metal base of the holder below the liquid nitrogen. Liquid nitrogen was constantly poured in the holder to provide a constant low-temperature to the substrate during film growth.

The as-deposited films were characterized for their characteristic emissions. The thickness of the films was 200 nm, measured with a quartz crystal thickness monitor in the growth chamber. X-rays diffraction (XRD) was used to determine the structure of the films. No diffraction peaks were observed, indicating that the as-deposited films were amorphous.

Cathodoluminescence (CL) studies of the films were performed at room temperature in a vacuum chamber at a pressure of about 3 × 10−6 Torr, which was maintained with an Alcatel CFF 450 turbo pump. Films were excited with electron beam energy of 2.85 kV and beam current of 100 μA. The films were placed an angle of 45° to the incident electron beam coming out of electron gun. The detector was placed at an angle of 45° to the film such that lines joining electron gun, the film and detector were making and angle of 90°. Luminescence from the films was focused onto the entrance slit of a SPEX Industries double monochromator with gratings blazed at 500 nm and detected at a Thorn EMI fast high gain photomultiplier tube with a range of 200–900 nm. The resolution of the spectra was 1 nm.

A 488 nm line of Argon laser was used to obtain the photoluminescence spectra, analyzed by a spectrometer equipped with a cooled photomultiplier tube. The power of the laser beam was 9.3 mW.

Thermal activation was accomplished by placing the flat films in a tube furnace at 1,200 K in a nitrogen atmosphere for half an hour.

Results and Discussion

Figure 1shows the photoluminescence (PL) spectrum of AlN:Sm when excited with a 488 nm Argon laser. A strong emission occurred at 598 nm (near 600 nm) which is indicated by a sharp peak in the figure. This peak corresponds to4G5/26H9/2transition. The intensity of the emission is very strong and hence it serves as a potential candidate for a red laser production at 598 nm. Further the PL is showing that the material can emit light under photon excitation and can be optically pumped for a laser construction. This work is still in progress and will be reported once laser achievement is successful.

thumbnailFigure 1. PL spectrum of amorphous AlN:Sm with excitation at 488 nm and emission at 598 nm

Figure 2shows the PL spectrum of AlN:Sm when excited with the same 488 nm Argon laser. A very strong emission occurred at 707 nm (near 710 nm) which is indicated by a sharp peak in the figure. This peak corresponds to4G5/26H11/2transition. The intensity of the emission is very strong and hence it also serves as a potential candidate for an orange-red laser production at 707 nm. The intensity of this peak is almost double than the intensity of the peak at 598 nm with the same power of excitation sourcing. Thus the4G5/26H11/2transition has a strong potential to produce a red-near IR laser under optimum conditions.

thumbnailFigure 2. PL spectrum of amorphous AlN:Sm with excitation at 488 nm and emission at 707 nm

Figure 3 provides CL spectrum of AlN:Sm in 300–850 nm range at room temperature. It is observed that Sm3+ give four transitions under electron excitation. Three of these transitions are in the visible range of the spectrum at 564, 600, and 648 nm as a result from 4G5/26H5/24G5/26H7/2 and 4G5/26H9/2 transitions, respectively [7,20]. The fourth peak falls in the infrared region at 707 nm due to 4G5/26H11/2. The peak at 600 nm is the strongest while the peak at 707 nm is the weakest amongst all. The 4G5/26H5/2 transition at 564 nm falls in yellow region of the spectrum. The dominant transition 4G5/26H7/2 at 600 nm and the 4G5/26H9/2 transitions occur in red region of the visible spectrum. Because of the combination of these colors and dominancy of orange-red peak, the direct observation of AlN:Sm films exposed to electron beam in CL gives orange-red light to naked eye. All these transitions and their relative intensities are tabulated in Table 1.

thumbnailFigure 3. CL spectrum of amorphous AlN:Sm films

Table 1. Summary of Sm3+ions emissions from AlN:Sm

Figure 4gives a combined spectra of AlN:Sm before and after thermal activation. It is clear from the figure that thermal annealing enhances the luminescence from Sm. It is observed that thermal annealing doubles the luminescence intensity from the dominant transition4G5/26H7/2at 600 nm. The4G5/26H5/2transition at 564 nm has got maximum enhancement when annealed thermally at 1,200 K for half an hour. The intensity of luminescence of this transition increases by a factor of 2.5 after thermal annealing. The other two transitions are also enhanced significantly by thermal annealing.

thumbnailFigure 4. CL spectra of thermally activated and inactivated amorphous AlN:Sm films

Figure 5shows the XRD analysis of the AlN:Sm films deposited on Si(100) substrate. Only one peak can be observed in the film at 69.1° that corresponds to Si(100). No other peak is present in the figure, indicating that the deposited films are amorphous. Thermal activation of the films at 1,200 K has not changed the structure of the films.

thumbnailFigure 5. XRD analysis of the AlN:Sm films deposited on Si(100) substrates

Table 1 provides detail of all transitions from Sm3+. Column 2 and 3 give all transitions and the corresponding wavelengths of emission. The relative intensities of non-annealed and annealed samples are given in column 4 and 5, respectively. These relative intensities are determined by comparing the intensity of every peak to the intensity brightest peak (567 nm) in the non-annealed samples. Column 4 gives the ratio by which the intensity of luminescence is enhanced by thermal annealing. Careful consideration of these ratios tells that enhancement is higher for lower wavelengths and it goes down when one moves from ultraviolet to infrared region of the spectrum. The reason being, with increasing temperature the probability of populating higher energy levels increases and hence higher energy levels are thermally more populated as compared to lower energy levels at high-temperature [21]. These thermally populated higher energy levels give rise to enhanced emission.

Both PL peaks indicate very strong emission from AlN:Sm when excited with 488 nm laser. Such a strong intensity clearly indicates that this material is a potential candidate for laser production. We are in the process of providing optimum conditions and laser power to achieve laser in AlN:Sm. Polarization study is also in progress and will be published soon once it is complete.

This significant increase in the intensities of luminescence from Sm3+ ions by thermal annealing has got a good explanation. Luminescence occurs from Sm3+ ions and not from Sm2+ or Sm1+. During the film deposition, it is most likely that some of Al3+ of AlN may be replaced by Sm3+ but there are also chances for imperfections and defects giving rise to Sm2+ or Sm1+ during film growth. These ions do not contribute to luminescence. Smaller the number of these ions, more will be Sm3+ ions and hence luminescence will be higher. When these films are activated thermally at a higher temperature then most of Sm2+ or Sm1+ impurities ionize and converts to Sm3+ ions giving path to enhanced luminescence [22-24]. Moreover when the films are transferred to the furnace and thermally activated after removed from the deposition chamber, they are exposed to air. Thus oxidation of the surface of the film cannot be ignored. Oxygen enhances the luminescence of rare-earth ions giving rise to the enhanced luminescence after thermal activation of the films [13].

The results show that amorphous AlN:Sm is a promising candidate for its use in nanoscale optical devices and communication tools. The strong red emission makes this material a potential candidate for making quantum dots.

Conclusion

Thin films of amorphous AlN:Sm are deposited by rf magnetron sputtering. Films were characterized for their surface morphology and luminescence properties by XRD, PL, and CL. Samarium ion emits mainly in visible region with the most intense transition in the orange-red portion of the spectrum. Thermal activation enhances the luminescence of films. PL provides very sharp emission in red making it a useful material for nanoscale optical devices applications.

References

  1. Maqbool M, Ahmad I, Richardson HH, Kordesch ME:

    Appl. Phys. Lett.. 2007, 91(19):193511.

    Bibcode number [2007ApPhL..91s3511M]

    Publisher Full Text OpenURL

  2. Maqbool M, Richardson HH, Kordesch ME:

    J. Mater. Sci.. 2007, 42(14):5657-5660.

    COI number [1:CAS:528:DC%2BD2sXnslynsL0%3D]; Bibcode number [2007JMatS..42.5657M]

    Publisher Full Text OpenURL

  3. Maqbool M, Ahmad I:

    Curr. Appl. Phys.. 2008, 9:234-237.

    Bibcode number [2009CAP.....9..234M]

    Publisher Full Text OpenURL

  4. Chen H, Gurumurugan K, Kordesch ME, Jadwisienczak WM, Lozykowski HJ:

    MRS Internet J. Nitride Semicond. Res.. 2000, 5:U130. OpenURL

  5. Caldwell M, Richardson HH, Kordesch ME:

    MRS Internet J. Nitride Semicond. Res.. 2000, 5:U142. OpenURL

  6. Jadwisienczak WM, Lozykowski HJ, Perjeru F, Chen H, Kordesch M, Brown I:

    Appl. Phys. Lett.. 2000, 76:3376.

    COI number [1:CAS:528:DC%2BD3cXjs1SntLo%3D]; Bibcode number [2000ApPhL..76.3376J]

    Publisher Full Text OpenURL

  7. Dimitrova V, Van Patten PG, Richardson HH, Kordesch ME:

    Appl. Phys. Lett.. 2000, 77:478.

    COI number [1:CAS:528:DC%2BD3cXltVWjtro%3D]; Bibcode number [2000ApPhL..77..478D]

    Publisher Full Text OpenURL

  8. Dimitrova V, Van Patten PG, Richardson H, Kordesch ME:

    Appl. Surf. Sci.. 2001, 175–176:481. OpenURL

  9. Caldwell ML, Martin AL, Spalding CM, Dimitrova VI, Van Patten PG, Kordesch ME, Richardson HH:

    J. Vac. Sci. Technol. A. 2001, 19:1894.

    Bibcode number [2001JVST...19.1894M]

    OpenURL

  10. Caldwell ML, Martin AL, Dimitrova VI, Van Patten PG, Kordesch ME, Richardson HH:

    Appl. Phys. Lett.. 2001, 78:1246.

    COI number [1:CAS:528:DC%2BD3MXhtl2gu70%3D]; Bibcode number [2001ApPhL..78.1246C]

    Publisher Full Text OpenURL

  11. Caldwell ML, Van Patten PG, Kordesch ME, Richardson HH:

    MRS Internet J. Nitride Semicond. Res.. 2001, 6:13. OpenURL

  12. Richardson HH, van Patten PG, Richardson DR, Kordesch ME:

    Appl. Phys. Lett.. 2002, 80:2207.

    COI number [1:CAS:528:DC%2BD38Xit1Ons7k%3D]; Bibcode number [2002ApPhL..80.2207R]

    Publisher Full Text OpenURL

  13. Chen H, Chen K, Drabold DA, Kordesch ME:

    Appl. Phys. Lett.. 2000, 77:1117.

    COI number [1:CAS:528:DC%2BD3cXlslGgtrg%3D]; Bibcode number [2000ApPhL..77.1117C]

    Publisher Full Text OpenURL

  14. Little ME, Kordesch ME:

    Appl. Phys. Lett.. 2001, 78:2891.

    COI number [1:CAS:528:DC%2BD3MXjt1ejsL0%3D]; Bibcode number [2001ApPhL..78.2891L]

    Publisher Full Text OpenURL

  15. Suyver JF, Kik PG, Kimura T, Polman A, Franzo G, Coffa S:

    Nucl. Instr. Meth. Phys. Res. B. 1999, 148:497-501.

    COI number [1:CAS:528:DyaK1MXhsVCgsw%3D%3D]; Bibcode number [1999NIMPB.148..497S]

    Publisher Full Text OpenURL

  16. Gruber JB, Zandi B, Lozykowski HJ, Jadwisienczak WM:

    J. Appl. Phys.. 2002, 91(5):2929-2935.

    COI number [1:CAS:528:DC%2BD38Xhs1ahtrg%3D]; Bibcode number [2002JAP....91.2929G]

    Publisher Full Text OpenURL

  17. Lozykowski HJ:

    Phys. Rev. B. 1993, 48:17758.

    COI number [1:CAS:528:DyaK2cXhslKrtr0%3D]; Bibcode number [1993PhRvB..4817758L]

    Publisher Full Text OpenURL

  18. Steckl AJ, Birkhahn R:

    Appl. Phys. Lett.. 1998, 73:1700.

    COI number [1:CAS:528:DyaK1cXmtValtrc%3D]; Bibcode number [1998ApPhL..73.1700S]

    Publisher Full Text OpenURL

  19. Bell MJV, Nunes LAO, Zanatta AR:

    J. Appl. Phys.. 1999, 86(1):338-341.

    COI number [1:CAS:528:DyaK1MXjvV2kurw%3D]; Bibcode number [1999JAP....86..338B]

    Publisher Full Text OpenURL

  20. Overberg M, Abernathy CR, MacKenzie JD, Pearton SJ, Wilson RG, Zavada JM:

    Mater. Sci. Eng. B. 2001, 81:121-126. Publisher Full Text OpenURL

  21. MacKenzie JD, Abernathy CR, Pearton SJ, Hommerich U, Seo JT, Wilson RG, Zavada JM:

    Appl. Phys. Lett.. 1998, 72(21):2710-2712.

    COI number [1:CAS:528:DyaK1cXjtV2qsrw%3D]; Bibcode number [1998ApPhL..72.2710M]

    Publisher Full Text OpenURL

  22. Wang SZ, Yoon SF, He L, Shen XC:

    J. Appl. Phys.. 2001, 90(5):2314-2320.

    COI number [1:CAS:528:DC%2BD3MXmt1Wktrk%3D]; Bibcode number [2001JAP....90.2314W]

    Publisher Full Text OpenURL