Open Access Nano Express

LiMn2O4–y Br y Nanoparticles Synthesized by a Room Temperature Solid-State Coordination Method

Yudai Huang12, Rongrong Jiang1, Shu-Juan Bao1, Yali Cao12 and Dianzeng Jia12*

Author Affiliations

1 Institute of Applied Chemistry, Xinjiang University, Urumqi, 830046, People’s Republic of China

2 School of Science, Xi’an Jiaotong University, Xi’an, 710049, People’s Republic of China

For all author emails, please log on.

Nanoscale Research Letters 2009, 4:353-358  doi:10.1007/s11671-009-9252-7


The electronic version of this article is the complete one and can be found online at:


Received:22 July 2008
Accepted:8 January 2009
Published:22 January 2009

© 2009 to the authors

Abstract

LiMn2O4–yBrynanoparticles were synthesized successfully for the first time by a room temperature solid-state coordination method. X-ray diffractometry patterns indicated that the LiMn2O4–yBrypowders were well-crystallized pure spinel phase. Transmission electron microscopy images showed that the LiMn2O4–yBrypowders consisted of small and uniform nanosized particles. Synthesis conditions such as the calcination temperature and the content of Brwere investigated to optimize the ideal condition for preparing LiMn2O4–yBrywith the best electrochemical performances. The optimized synthesis condition was found in this work; the calcination temperature is 800 °C and the content of Bris 0.05. The initial discharge capacity of LiMn2O3.95Br0.05obtained from the optimized synthesis condition was 134 mAh/g, which is far higher than that of pure LiMn2O4, indicating introduction of Brin LiMn2O4is quite effective in improving the initial discharge capacity.

Keywords:
LiMn2O4–yBry; Nanoparticles; Room temperature solid-state coordination method; Lithium–ion battery

Introduction

Development of the cathode materials for lithium–ion battery is vital to meet the demands of portable devices, power tools, e-bikes, future usages of electric vehicles, and so on [1]. Among three promising candidates for cathode materials (LiCoO2, LiNiO2, and LiMn2O4), lithium manganese oxides (LiMn2O4) [2] are inexpensive cathode materials with a high energy density, environmental acceptability, and are more abundant in nature. In spite of these advantages, LiMn2O4 has the problem of severe capacity fading during charge and discharge cycles [3,4], which makes it unsuitable for commercial application. Intensive research has particularly focused on the mechanism of capacity fading and has suggested numerous solutions.

Among these projects, doping [5,6] is considered to be an effective path to improve the electrochemical performance of spinel LiMn2O4, so several attempts have been made for improving the lithium manganese spinels by doping various metals ions [7-10]. Although such substitutions often result in enhancing the stability of spinel, the first discharge capacity of them is considerably lower than that of the parent compound. The reduction in the first discharge capacity is mainly due to the fact that the substituent ions do not contribute to the discharge capacity. In 1999, Amatucci et al. [11] and Palacin et al. [12] reported that the introduction of the anion in spinel structure can reduce the Mn oxidation state and then increase the first discharge capacity. These interesting results derived from the anion doping stimulated our research interest to investigate the effect of other anions doping. To the best of our knowledge, up to now, no Br-doped cathode materials (LiMn2O4–yBry) have been reported.

It is believed that single-phase, homogeneity, uniform particle morphology with nanometer size distribution is the desired feature for achieving a higher electrode activity [13]. Nanometer-scale structured electrode materials are of great interest as potential building blocks for future generation electronic devices with greatly reduced size [14], because they show higher capacity and better cycling performance than conventional electrodes composed of this kind of materials [15]. There have been increased interests in synthesizing nanostructures and their derivative compounds for their diverse physicochemical properties and potential applications as cathode materials for lithium–ion batteries [16]. Moreover, it is well known that the preparation methods and post-treatment techniques could influence the structure and electrochemical performance of materials significantly [17-19]. Further, the subtle variation of chemical composition [20,21] will bring great changes in the electrochemical performance of products. Room temperature solid-state coordination method [22,23] possesses the advantages of simple manipulation and better prospects for commercialization as compared to the conventional solid-state method [24]. More meaningfully, it achieves homogeneous mixture of the starting components, a low synthesis temperature and small grain size of the powders. Besides this, several nanomaterials have been synthesized using this method [25-27]. In this study, LiMn2O4–yBry nanoparticles were synthesized successfully for the first time by a room temperature solid-state coordination method. The structures, morphologies, and electrochemical properties of these materials were also investigated.

Experimental

Stoichiometric lithium acetate, manganese acetate, lithium bromide, and citric acid (worked as chelating reagent, molar ratio of citric acid to the total metal ions is 1:1), which were ground into powders separately, were mixed with polyethylene glycol (PEG) 400 (worked as dispersants) in an agate mortar and ground with a pestle for 1.5 h in order to make them react to reach the best possible homogeneity. Then the mixtures were dried at 120 °C for 8 h to form precursors. The obtained precursors were annealed at 500 °C for 1 h, after ground, held at 600–800 °C for 10 h in air in a muffle furnace to obtain final LiMn2O4–yBrypowders. Figure 1shows the flowchart.

thumbnailFigure 1. Flowchart showing the synthesis of LiMn2O4–yBrysamples by room temperature solid-state coordination method

An X-ray diffractometer (XRD) (MXP18AHF, Mac, Japan) with Cu Kα radiation (λ = 1.54056 Å) was used for the identification of the crystalline phases of the powders. The morphological characteristics of the products were investigated using transmission electron microscope (TEM, H-600, Hitachi, Japan).

The cells consisted of a LiMn2O4-based composite as the positive electrode, a Li disk as the negative electrode, and an electrolyte of 1 M LiPF6in a 1:1 (volume ratio) mixture of ethylene carbonate (EC)/dimethyl carbonate (DMC). The cathode was formed by mixing the active material with acetylene black and PVDF binder in 85:10:5 ratio inN-methyl-pyrrolidone (NMP). NMP acts as the solvent for the binder. The paste was applied to an aluminum foil current collector using a blade. The film was dried at 60 °C in air for 1 h and then was vacuum dried at 120 °C for 4 h. Celgard 2300 membrane was used as the separator. The cells were assembled in an argon-filled glove box. All the electrochemical tests were carried out at room temperature. Cyclic voltammetry (CV) (CHI660B Electrochemical Workstation Chenhua Co. of Shanghai, China) experiments were conducted from 3.2 to 4.35 V at a scan rate of 0.1 mV/s, and a Li metal disk served as both counter and reference electrode. Charge/discharge tests were performed at a constant current density of 0.30 mA/cm2within the potential range of 3.0 and 4.35 V.

Results and Discussion

The XRD patterns of LiMn2O4–yBry powders calcinated at 600–800 °C for 10 h are shown in Fig. 2. The XRD of the powders calcinated at 600 °C shows the impurity peaks of Mn2O3 (marked by ▼). The formation of impurity phase Mn2O3 indicates that the temperature is not high enough to reach full crystallization and containing some vacancies in LiMn2O4 structure during combustion. When the calcination temperature increases to 700 °C, the impurity peaks of Mn2O3 disappear and the pure spinel LiMn2O4 structure forms, which indicates that pure spinel LiMn2O4 can be produced by heat treatment at relatively higher temperatures. Moreover, when the temperature increases, the intensity of peaks grows correspondingly, which indicates better crystallization is obtained. The diffraction peaks of LiMn2O3.95Br0.05 and LiMn2O3.90Br0.10 synthesized at 700 and 800 °C corresponded to pure phase spinel structure. The results indicate that the structure of the ternary spinel remains when some of the O2− in the spinel phase are replaced by Br. Doping do not seem to change the spinel structure of the samples because no other impurity peaks are observed in the XRD patterns. The lattice constants of all the samples, which are calculated from the XRD spectra, are summarized in Table 1. The samples with the same chemical compositions calcined at different temperatures have little difference in lattice constants. However, the products doped with Br have larger lattice constants, which is ascribed to the substitution of O2− by Br. The Br has larger ion (1.96 Å) radius than that of O2− (1.4 Å) and Br substitution leads to reduction of Mn4+ to the larger Mn3+ cations, which results in improving capacity as reported by Amatucci et al. [21]. Because the powders calcinated at 600 °C show the impurity peaks of Mn2O3, we did not do the electrochemistry test of them.

thumbnailFigure 2. XRD patterns of LiMn2O4–yBry: (A) LiMn2O4calcinated at 600 °C; (B) LiMn2O4calcinated at 700 °C; (C) LiMn2O4calcinated at 800 °C; (D) LiMn2O3.95Br0.05calcinated at 600 °C; (E) LiMn2O3.95Br0.05calcinated at 700 °C; (F) LiMn2O3.95Br0.05calcinated at 800 °C; (G) LiMn2O3.90Br0.10calcinated at 600 °C; (H) LiMn2O3.90Br0.10calcinated at 700 °C; (I) LiMn2O3.90Br0.10calcinated at 800 °C

Table 1. Lattice constants calculated from the XRD spectra

The trend of morphology variation of different LiMn2O4–yBry with temperature is similar, so the TEM of LiMn2O3.95Br0.05 powders calcinated at 600–800 °C for 10 h are given as examples in Fig. 3. The sample calcined at 600 °C agglomerates severely and its size is about 200 nm. This maybe due to some Mn2O3 impurity existing in the sample. As the temperature increases to 700 °C, the distribution of the particle size becomes narrow and the average particle size is about 100 nm. The decrease of particle size is due to the breaking of agglomerated powders as the calcination temperature increases, but agglomeration still exists. As the temperature increases further, it presents the spherical particle morphology, homogenous particle composition and narrow distribution of particle size. The extent of agglomeration of particles in the sample is meliorated. The particle size of the sample calcined at 600 °C is larger than that of the sample calcined at 700 and 800 °C, which indicates the calcination temperature has significant effect on the crystallization and morphology of the samples. This agreed well with the result of XRD. Products with nanosized particles would facilitate reducing the diffusion length of the lithium ions during intercalation and deintercalation processes, which would improve the electrochemical performance of the samples [28].

thumbnailFigure 3. TEM photographs of LiMn2O3.95Br0.05: (a) calcinated at 600 °C, (b) 700 °C, and (c) 800 °C

Cyclic voltammograms of the Li/LiMn2O4–yBrycells between 3.2 and 4.35 V at a scan rate of 0.1 mV/s for the first cycle are shown in Fig. 4. The cyclic voltammograms reveal that there are two pairs of redox peaks on each cycle voltammograms. The two pairs of redox peaks correspond to two-step reversible intercalation/deintercalation reaction. The samples synthesized at 800 °C present higher current peaks than the ones prepared at 700 °C. The LiMn2O3.95Br0.05samples synthesized at 800 °C possess the highest current peaks, which indicates that the product calcined at 800 °C might have better electrochemical activity.

thumbnailFigure 4. Cyclic voltammogram of Li/LiMn2O4–yBrycells between 3.2 and 4.35 V at scan rate of 0.1 mV/s: (A) LiMn2O4calcinated at 700 °C; (B) LiMn2O4calcinated at 800 °C; (C) LiMn2O3.95Br0.05calcinated at 700 °C; (D) LiMn2O3.95Br0.05calcinated at 800 °C; (E) LiMn2O3.90Br0.10calcinated at 700 °C; (F) LiMn2O3.90Br0.10calcinated at 800 °C

Figure 5 displays voltage versus discharge capacity curves for LiMn2O4–yBry between 3 and 4.35 V versus Li/LiMn2O4–yBry by applying 0.3 mA/cm2 at room temperature. For LiMn2O4–yBry sample prepared at 700 °C, the initial discharge capacity of pure spinel is 106 mAh/g. It increases to 127 mAh/g as y = 0.05 and decreases to 118 mAh/g as y = 0.10. It is clear that the increase of initial discharge capacity results from Br doping. This may be explained by the following reasons. The substitution of monovalent Br for divalent O2− results in the increasing of Mn3+ content in spinel which contributes to charge/discharge capacity during intercalation/deintercalation of Li+ in LiMn2O4. Moreover, Br doping brings in larger lattice constants of samples, thus Li+ can move more freely in the sample and this might help increase the capacity [21]. When the calcination temperature increases to 800 °C, LiMn2O4–yBry samples deliver initial discharge capacity of 109, 134, and 121 mAh/g as y = 0, 0.05, and 0.10, respectively. Samples calcined at relatively higher temperature have higher initial discharge capacity. The LiMn2O3.95Br0.05 synthesized at 800 °C possess the highest initial discharge capacity. However, with the increase of Br content in spinel (from 0.05 to 0.10), the initial discharge capacity decreases, which maybe due to Br doping that can improve the initial discharge capacity, but the Br content has an optimal value. In this work, the optimal value is 0.05.

thumbnailFigure 5. Voltage versus discharge capacity curves of LiMn2O4–yBry: (A) LiMn2O4calcinated at 700 °C; (B) LiMn2O4calcinated at 800 °C; (C) LiMn2O3.95Br0.05calcinated at 800 °C; (D) LiMn2O3.95Br0.05calcinated at 700 °C; (E) LiMn2O3.90Br0.10calcinated at 700 °C; (F) LiMn2O3.90Br0.10calcinated at 800 °C

The above-mentioned results show that effective anion doping can result in improvement of initial discharge capacity. Figure 6 displays the variations of discharge capacity versus cycle number curves of LiMn2O4–yBry between 3 and 4.35 V versus Li/LiMn2O4–yBry by applying 0.3 mA/cm2 at room temperature. As can be seen from Fig. 6, the samples doped by Br have larger initial discharge capacity than the pure spinels. However, Br-doped samples present appreciably high capacity loss than the parent compound. For LiMn2O4–yBry sample prepared at 700 °C, the capacity retention rate of pure spinel is 86%. It decreases to 79% as y = 0.05 and 82% as y = 0.10. For LiMn2O4–yBry sample prepared at 800 °C, the capacity retention rate of pure spinel is 83%. It decreases to 82% as y = 0.05 and 79% as y = 0.10. The LiMn2O4–yBry (y = 0.05, 0.10) samples have higher initial discharge capacity but lower cycle life than that of the parent compound. This is due to the increase of Mn3+ content by monovalent Br substitution for divalent O2−. The high-spin Mn3+ ions give rise to the Jahn-Teller distortion which is the origin of the capacity loss. In a word, the increase of Mn3+ causes two effects: (1) the increase of initial discharge capacity and (2) the decrease of the capacity retention. As reported by many literatures, surface modification and cation codoping can overcome Jahn-Teller distortion [29]. Sun et al. [30,31] reported that LiAl0.34Mn1.76O3.98S0.02 and Li1.03Al0.2Mn1.8O3.96S0.04 materials prepared via a sol–gel method showed excellent cyclability in both 4 and 3 V regions. In our lab, the research work of Br and Al3+ codoping for improvement of the electrochemical performance of spinel LiMn2O4 is undergoing.

thumbnailFigure 6. Discharge capacity versus cycle number curves of LiMn2O4−yBry: (A) LiMn2O4calcinated at 700 °C; (B) LiMn2O4calcinated at 800 °C; (C) LiMn2O3.95Br0.05calcinated at 700 °C; (D) LiMn2O3.95Br0.05calcinated at 800 °C; (E) LiMn2O3.90Br0.10calcinated at 700 °C; (F) LiMn2O3.90Br0.10calcinated at 800 °C

Conclusion

In this work, LiMn2O4–yBrynanoparticles were synthesized by a room temperature solid-state coordination method for the first time. The powders have homogeneous morphology, small particles, and high crystallinity. The CV and charge/discharge test revealed that Brdoping improves the initial discharge capacity of the samples. The LiMn2O3.95Br0.05calcined at 800 °C has an initial discharge capacity of 134 mAh/g.

Acknowledgments

This work was partially supported by the Nature Science Foundation of Xinjiang Province (grant nos. 200821121 and 200721102) and the National Nature Science Foundation of China (grant nos. 20666005 and 20661003).

References

  1. Tarascon JM, Armand M:

    Nature. 2001, 414:35. Publisher Full Text OpenURL

  2. Tarascon JM, Wang E, Shokoohi FK, McKinnon WR, Colson S:

    J. Electrochem. Soc.. 1991, 138:2859.

    COI number [1:CAS:528:DyaK38XntVehuw%3D%3D]

    Publisher Full Text OpenURL

  3. Gummow RJ, de Kock A, Thackeray MM:

    Solid State Ionics. 1994, 69:59.

    COI number [1:CAS:528:DyaK2cXltFehtLo%3D]

    Publisher Full Text OpenURL

  4. Xia Y, Zhou Y, Yoshio M:

    J. Electrochem. Soc.. 1997, 144:2593.

    COI number [1:CAS:528:DyaK2sXlvFOhsLk%3D]

    Publisher Full Text OpenURL

  5. Wu YP, Rahm E, Holze R:

    Electrochim. Acta. 2002, 47:3491.

    COI number [1:CAS:528:DC%2BD38Xmt1yhsLo%3D]

    Publisher Full Text OpenURL

  6. Amatucci G, Pasquier AD, Blyr A, Zheng T, Tarascon JM:

    Electrochim. Acta. 1999, 45:255.

    COI number [1:CAS:528:DyaK1MXntlymtrs%3D]

    Publisher Full Text OpenURL

  7. Komaba S, Oikawa K, Myung ST, Kumagai N, Kamiyama T:

    Solid State Ionics. 2002, 149:47.

    COI number [1:CAS:528:DC%2BD38XktFKit7o%3D]

    Publisher Full Text OpenURL

  8. Huang YD, Li J, Jia DZ:

    J. Colloid Interface Sci.. 2005, 286:263.

    COI number [1:CAS:528:DC%2BD2MXjsFamsrs%3D]

    Publisher Full Text OpenURL

  9. Yoshio M, Xia Y, Kumada N, Ma S:

    J. Power Sources. 2001, 101:79.

    COI number [1:CAS:528:DC%2BD3MXmsV2js7g%3D]

    Publisher Full Text OpenURL

  10. Lee JH, Hong JK, Jang DH, Sun YK, Oh SM:

    J. Power Sources. 2000, 89:7.

    COI number [1:CAS:528:DC%2BD3cXjslKjurY%3D]

    Publisher Full Text OpenURL

  11. Amatucci GG, Pereira N, Zhang T, Plitz I, Tarascon JM:

    J. Power Sources. 1999, 81–82:39. Publisher Full Text OpenURL

  12. Palacin MR, Cras FL, Seguin L, Anne M, Chabre Y, Tarascon JM, Amatucci G, Vaughan G, Strobel P:

    J. Solid State Chem.. 1999, 144:361.

    COI number [1:CAS:528:DyaK1MXivFOqsLw%3D]

    Publisher Full Text OpenURL

  13. Lu CZ, Fey GTK:

    J. Phys. Chem. Solids. 2006, 67:756.

    COI number [1:CAS:528:DC%2BD28Xis1ektrk%3D]; Bibcode number [2006JPCS...67..756L]

    Publisher Full Text OpenURL

  14. Dai H, Wong EW, Libeber CM:

    Science. 1996, 272:523.

    COI number [1:CAS:528:DyaK28XisFOmsbo%3D]; Bibcode number [1996Sci...272..523D]

    Publisher Full Text OpenURL

  15. Zhou YK, Shen CM, Li HL:

    Solid State Ionics. 2002, 146:81.

    COI number [1:CAS:528:DC%2BD38XksFag]

    Publisher Full Text OpenURL

  16. Dobley A, Ngala K, Yang S, Zavalij PY, Whittingham MS:

    Chem. Mater.. 2001, 13:4382.

    COI number [1:CAS:528:DC%2BD3MXnsVCrtLw%3D]

    Publisher Full Text OpenURL

  17. Sun YK, Yoon CS, Kim CK, Youn SG, Lee YS, Yoshio M, Oh IH:

    J. Mater. Chem.. 2001, 11:2519.

    COI number [1:CAS:528:DC%2BD3MXntFCls7s%3D]

    Publisher Full Text OpenURL

  18. Barboux P, Tarascon JM, Shokoohi FK:

    J. Solid State Chem.. 1991, 94:185.

    COI number [1:CAS:528:DyaK3MXmsVKnu7g%3D]; Bibcode number [1991JSSCh..94..185B]

    Publisher Full Text OpenURL

  19. Wang GX, Bradhurst DH, Liu HK, Dou SX:

    Solid State Ionics. 1999, 120:95.

    COI number [1:CAS:528:DyaK1MXisV2ltrw%3D]

    Publisher Full Text OpenURL

  20. Endres P, Fuchs B, Kemmler-Sack S, Brandt K, Faust-Becker G, Praas H-W:

    Solid State Ionics. 1996, 89:221.

    COI number [1:CAS:528:DyaK28Xms1eqs7w%3D]

    Publisher Full Text OpenURL

  21. Amatucci G, Tarascon JM:

    J. Electrochem. Soc.. 2002, 149:K31.

    COI number [1:CAS:528:DC%2BD38XovVWisbo%3D]

    Publisher Full Text OpenURL

  22. Ye XR, Jia DZ, Yu JQ, Xin XQ, Xue ZL:

    Adv. Mater.. 1999, 11:941.

    COI number [1:CAS:528:DyaK1MXlt12msbY%3D]

    Publisher Full Text OpenURL

  23. Wang RY, Jia DZ, Zhang L, Liu L, Guo ZP, Li BQ, Wang JX:

    Adv. Funct. Mater.. 2006, 16:687.

    COI number [1:CAS:528:DC%2BD28XjsVKjsbo%3D]

    Publisher Full Text OpenURL

  24. Wu HM, Tu JP, Yuan YF, Li Y, Zhao XB, Gao GS:

    Mater. Chem. Phys.. 2005, 93:461.

    COI number [1:CAS:528:DC%2BD2MXls1Omu70%3D]

    Publisher Full Text OpenURL

  25. Jia DZ, Yu JQ, Xia X:

    Chin. Sci. Bull.. 1998, 43:571.

    COI number [1:CAS:528:DyaK1cXjsFOltb4%3D]

    Publisher Full Text OpenURL

  26. Zhou TY, Xin XQ:

    Nanotechnology. 2004, 15:534.

    COI number [1:CAS:528:DC%2BD2cXlt1ersrw%3D]; Bibcode number [2004Nanot..15..534Z]

    Publisher Full Text OpenURL

  27. Sun ZP, Liu L, Zhang L, Jia DZ:

    Nanotechnology. 2006, 17:2266.

    COI number [1:CAS:528:DC%2BD28Xmtl2nur0%3D]; Bibcode number [2006Nanot..17.2266S]

    Publisher Full Text OpenURL

  28. Zhou YK, Li HL:

    J. Mater. Chem.. 2002, 12:681.

    COI number [1:CAS:528:DC%2BD38XhsVCnsrg%3D]

    Publisher Full Text OpenURL

  29. Capsoni D, Bini M, Chiodelli G, Mustarelli P, Massarotti V, Azzoni CB, Mozzati MC, Linati L:

    J. Phys. Chem. B. 2002, 106:7432.

    COI number [1:CAS:528:DC%2BD38XkvF2qtLs%3D]

    Publisher Full Text OpenURL

  30. Sun YK, Jeon YS:

    J. Mater. Chem.. 1999, 9:3147.

    COI number [1:CAS:528:DyaK1MXnsF2nu7w%3D]

    Publisher Full Text OpenURL

  31. Sun YK:

    Electrochem. Commun.. 2000, 2:6.

    COI number [1:CAS:528:DC%2BD3cXhsVKnurc%3D]

    Publisher Full Text OpenURL