Synthesis and Characterization of ZnO Nanorods and Nanodisks from Zinc Chloride Aqueous Solution

Tengfa Long12, Shu Yin2*, Kouta Takabatake2, Peilin Zhnag2 and Tsugio Sato2

Author affiliations

1 Guangxi Normal University, Guilin, People’s Republic of China

2 IMRAM, Tohoku University, Sendai, Japan

For all author emails, please log on.

Citation and License

Nanoscale Research Letters 2008, 4:247-253  doi:10.1007/s11671-008-9233-2


The electronic version of this article is the complete one and can be found online at:


Received:12 November 2008
Accepted:2 December 2008
Published:16 December 2008

© 2008 to the authors

Abstract

ZnO nanorods and nanodisks were synthesized by solution process using zinc chloride as starting material. The morphology of ZnO crystal changed greatly depending on the concentrations of Zn2+ion and ethylene glycohol (EG) additive in the solution. The effect of thermal treatment on the morphology was investigated. Photocatalytic activities of plate-like Zn5(OH)8Cl2 · H2O and rod-like ZnO were characterized. About 18% of 1 ppm NO could be continuously removed by ZnO particles under UV light irradiation.

Keywords:
ZnO nanorod; ZnO nanodisk; Photocatalytic activity; Zinc chloride

Introduction

Zinc oxide with a hexagonal wurtzite crystal structure possesses unique optical and electronic properties, and wide applications on piezoelectric devices, transistors, photodiodes, photocatalysis [1-4], etc. In recent years, much attention has been paid to nanostructure ZnO materials, and various morphologies of ZnO such as nanowire, nanorod, nanotube, nanobelt, nanoring, nanoneedles, and hollow structures, etc. have been developed [5-14]. Many methods have been employed for the morphological control of ZnO crystal, such as pulsed laser deposition(PLD) [15], chemical vapor deposition [16], spray pyrolysis [17,18], thermal evaporation [19], wet-chemical route [20,21], etc., in which the wet chemical route has been becoming a charming method due to the mild reaction condition and simplicity of the synthesis process. It is important to prepare well-crystallized and orientated ZnO nanoparticles. In most solution processes for the synthesis of ZnO nanoparticles, zinc acetate, and zinc nitrate are used as starting materials [21-24], but using zinc chloride as a starting material was seldom reported. In the present study, ZnO with rod-like and plate-like structure were successfully synthesized from zinc chloride aqueous solution, and their photocatalytic properties were characterized.

Experimental

ZnCl2, hexamethylenetetramine (HMT, C6H12N4), ethylene glycol (EG), commercial ZnO powder, butyl acetate, ethyl acetate, and nitrocellulose were used as starting materials. All these chemicals were used as delivered without further purification. Firstly, the cleaned borosilicate glass substrate was coated with thin film of ZnO nanoparticles by a spin-coater (Mikasa 1H-D7). The coating liquid was prepared by uniformly mixing 1 g commercial ZnO nano particles (Sumitomo Osaka Cement ZnO-350) with 2 g of industrial grade nitrocellulose, 5 g of ethyl acetate and 5 g of butyl acetate together with 50 g zirconia balls of 2.7 mm diameter with ball milling using a plastic bottle for 40 h. Then, the prepared substrate was calcined at 400 °C for 1 h. For the second step, the equimolar of ZnCl2 and HMT were dissolved in water or 50 vol.% EG aqueous solution. The ZnO nanoparticles coated glass substrates obtained in the first step were dipped into 50 mL of as-prepared solution containing a desired concentration of ZnCl2–HMT mixture and the solution was kept at 95 °C for 12 h in a sealed silicate-glass bottle. Finally, the glass substrate was taken out and washed with distilled water and acetone, then vacuum dried at 80 °C for 1 h. The morphology of the crystals was observed by SEM (Hitachi S-4800) and TEM (JOEL JEM-2000EX). The crystalline phase of the products was determined by X-ray diffraction analysis (XD-01,SHIMADZU). The specific surface area (SSA) was evaluated by nitrogen adsorption–desorption isothermal measurement at 77 K (NOVA-4200e). FT–IR measurements were conducted using the FTS7000 series (DIGILIB). Thermal gravimetry and differential thermal analysis (TG–DTA) curves were traced on a Rigaku Thermoflex (TG8101D) at a heating rate of 10 °C/min in air. The diffuse reflectance spectra of the samples were measured using an UV–vis spectrophotometer (Shimadzu UV-2450). The photocatalytic activity was evaluated by the oxidative destruction of nitrogen monoxide under irradiation of high pressure mercury arc of various light wavelengths using a flow type reactor with a NOx analyzer (Yanaco, ECL-88A) [25].

Results and Discussion

Figure 1shows the morphologies of the samples prepared in aqueous solutions of equimolar of ZnCl2–HMT mixture with and without 50 vol.% EG additive. The initial concentrations of Zn2+were 0.01 M, 0.05 M, and 0.1 M, respectively. The morphology of the product changed greatly depending on EG additive and concentration of Zn2+. In the absence of EG, at such low initial ZnCl2–HMT concentration of 0.01 M, the product exhibited uniform spindle-like structure with the length of more than 20 μm (Fig. 1a). When ZnCl2–HMT concentration increased to 0.05 M, hexagonal plate-like morphology with diameter of about 50 μm was formed (Fig. 1b, c). In contrast, with 50 vol.% EG additive in the 0.01 M ZnCl2–HMT mixed aqueous solution, instead of spindle-like structure, ellipse-like head rod structure with smaller size (half length to that of spindle-like structure (Fig. 1a) was formed (Fig. 1d). When the initial concentration of ZnCl2–HMT reached 0.05 M, the morphology changed to a rod-like hexagonal structure (Fig. 1e). When ZnCl2–HMT concentration was 0.1 M, as shown in Fig. 1f, the product exhibited similar hexagonal plate-like morphology to that in the absence of EG, whereas the plate-like particle size decreased to about half to that prepared at the same zinc concentration in the absence of EG (Fig. 1c). These results indicated that zinc ion concentration and EG additive acted very important roles in the morphological control of particles during the solution synthesis process. The existence of EG made the crystals to grow homogeneously due to its good dispersibility and glutinosity. It was also found that in the absence of HMT in 0.1 M ZnCl2solution, only small amount of products with nonhomogeneous morphologies consisted of spherical and rod-like structure could be obtained, although the image was not shown here.

thumbnailFigure 1. SEM photographs of the crystals prepared at 95 °C for 12 h ina0.01 M,b0.05 M,c0.1 M ZnCl2–HMT mixed aqueous solution and ind0.01 M,e0.05 M,f0.1 M ZnCl2–HMT mixed 50 vol.% EG aqueous solution

Figure 2 shows the XRD patterns of the samples prepared in various concentrations of ZnCl2–HMT aqueous solutions with and without 50 vol.% EG additive. The spindle-like particles prepared in 0.01 M ZnCl2–HMT aqueous solution and ellipse-like head rod-like particles and rod-like particles prepared in 0.01 and 0.05 M ZnCl2–HMT–50vol.% EG aqueous solution possessed typical hexagonal wurtzite-type ZnO structure (ICSD No. 89-1397). The relative intensity of (100) and (101) peaks increased with increment of zinc ion concentration. On the other hand, the samples with hexagonal plate-like morphology prepared in 0.05 and 0.1 M ZnCl2–HMT aqueous solution and in 0.1 M ZnCl2–HMT–50% EG aqueous solution displayed quite different diffraction profiles consisting of the peaks at 2θ = 11.2°, 22.5°, 33.5°, 44.3°, 53.8° and 58.3°, which might be ascribed to simonkolleite structure Zn5(OH)8Cl2 · H2O (ICSD No. 77-2311). These phenomena were quite different with previous results, in which only wurtzite-type ZnO crystals formed using Zn(NO3)2 and Zn(CH3COO)2 as Zn2+ source. The plate-like structure strongly related to the formation of simonkolleite possessing layered structure [26]. It might be inferred that the high concentration of zinc ion and chloride ion preferred to form simonkolleite structure. Since the formations of ZnO and Zn5(OH)8Cl2 · H2O shown by Eqs. 13, might proceed competitively in the solution, the formation of Zn5(OH)8Cl2 · H2O became dominant at high chloride ion concentration.

(1)

(2)

(3)

The samples with various morphologies prepared in aqueous solution and 50% EG aqueous solution were characterized. Figure 3 shows the FT–IR spectra of the prepared rod-like ZnO and plate-like Zn5(OH)8Cl2 · H2O samples. It is accepted that zincite (ZnO) only has the bands in the 350–600 cm−1 region corresponds to the zinc–oxygen bond [27]. It was obvious that Fig. 3a , c showed the similar spectra with that of ZnO crystal. On the other hand, the samples b and d in Fig. 3 showed quite different spectra to those of Fig. 3a, c. A strong band due to deformation vibration of H2O molecules at 1,630 cm−1, an absorption band centered at 3,434 cm−1 represented the characteristic of an O–H stretching vibration, and intensive bands at 898 and 720 cm−1 due to stretching vibration modes of chloride ion [28-30] were observed. These results indicated that simonkolleite (Zn5(OH)8Cl2 · H2O) preferred to be formed at increased chloride ion concentration. These FT–IR data agreed with the XRD patterns shown in Fig. 2.

thumbnailFigure 2. XRD patterns of the products prepared at 95 °C for 12 h ina0.01 M,b0.05 M,c0.1 M ZnCl2–HMT mixed aqueous solution and ind0.01 M,e0.05 M,f0.1 M ZnCl2–HMT mixed 50 vol.% EG solution.b,c,f: simonkolleite: Zn5(OH)8Cl2 · H2O;a,d,e: wurtzite ZnO

thumbnailFigure 3. FT–IR spectra of samples prepared at 95 °C ina0.01 M,b0.05 M ZnCl2–HMT mixed aqueous solution; and those prepared inc0.05 M,d0.1 M ZnCl2–HMT mixed 50 vol.% EG aqueous solution

Figure 4 showed the TG–DTA curves of the hexagonal plate-like simonkolleite samples. The samples prepared in different zinc ion concentration showed similar TG–DTA curves. The weight loss until 100–120 °C was related to the adsorbed water molecules on the surface of the samples. Other two obvious weight loss accompanying with endothermic peak could be observed around 200 and 380 °C, respectively. These weight loss might be ascribed to the dehydration from OH groups and release of hydrogen chloride from the simonkolleite Zn5(OH)8Cl2 · H2O as shown by Eq. 4. [23]

(4)

At high temperature, Zn5(OH)8Cl2 · H2O decomposed completely to form ZnO. According to Eq. 4, the transformation of simonkolleite Zn5(OH)8Cl2 · H2O to ZnO results in the weight loss of 26.3 wt%. The weight losses above 120 °C shown in Fig. 4 were 26–28 wt% which agreed well to the calculated value.

thumbnailFigure 4. TG-DTA curves of the typical simonkolleite samples prepared in (a) 0.05 M ZnCl2–HMT mixed aqueous solution (b) 0.1 M ZnCl2–HMT mixed 50 vol.% EG aqueous solution

To confirm the morphological change and phase transformation behavior of the hexagonal plate-like simonkolleite, the sample was heat treated in air at 300, 600, and 1200 °C, and their XRD patterns and SEM photographs are shown in Figs. 5and6, respectively. As shown in Fig. 5, diffraction peaks of simonkolleite gradually disappeared with increment of treatment temperature. After heat treatment at 600 °C, only the characteristic peak of well crystallized ZnO could be observed. In additional, it might be observed that the (002) peak of the sample prepared by calcination showed higher intensity than those of (100) and (101) peaks, indicating the preferred orientation of ZnO particles, remember usually the ZnO possessed comparatively weak (002) peak intensity (ICSD No. 89-1397).

thumbnailFigure 5. XRD patterns of samples prepared in (a) 0.05 M ZnCl2–HMT mixed aqueous solution followed by calcination at (b) 300 °C, (c) 600 °C, (d) 1200 °C; and in (e) 0.5 M ZnCl2- HMT mixed 50 vol.% EG aqueous solution followed by calcination at (f) 300 °C, (g) 600 °C, (h) 1200 °C

thumbnailFigure 6. SEM images of samples prepared in (a) 0.05 M ZnCl2–HMT mixed aqueous solution followed by calcination at (b) 300 °C, (c) 600 °C, (d) 1200 °C; and in (e) 0.1 M ZnCl2–HMT mixed 50 vol.% EG aqueous solution followed by calcination at (f) 300 °C, (g) 600 °C, (h) 1200 °C

Figure 6indicated that the morphology also changed during the heat treatment process. After heat treatment at 300 °C, some weak trace of porous structure on the surface of the samples could be observed. With the increment of treatment temperature, the porosity on the sample surface increased. This behavior related to the decomposition of simonkolleite structure, i.e., the increment of porosity might be caused by the release of water and hydrogen chloride from Zn5(OH)8Cl2 · H2O at high temperature. Figure 7shows the TEM photographs of the plate-like Zn5(OH)8Cl2 · H2O and those after thermal treatment at different temperatures. It is obvious that plate-like Zn5(OH)8Cl2 · H2O possessed smooth surface and those after thermal treatment possessed porous structure, and the porosity increased with treatment temperature.

thumbnailFigure 7. TEM images of samples prepared in (a) 0.1 M ZnCl2–HMT mixed 50 vol.% EG aqueous solution followed by calcination at (b) 300 °C, (c) 600 °C, (d) 1200 °C

The SSA and deNOxphotocatalytic activities of the as-prepared samples with different morphologies were characterized. For comparison, a standard titania photocatalyst aeroxide®P25 was also characterized and the results are summarized in Table 1. The aeroxide®\P25 titania powder is usually used as a reference sample in photocatalytic research, because of its high photocatalytic activity. As shown in the Table 1, the Zn5(OH)8Cl2 · H2O with hexagonal plate-like structure prepared in both water or 50vol.% EG aqueous solution showed such high BET specific surface areas as 19.4 m2/g and 19.7 m2/g, respectively, while those of the as-prepared rod-like ZnO showed low values of 3–4 m2/g, however, ZnO samples showed higher deNOxactivity than those of Zn5(OH)8Cl2 · H2O. The high SSA of the simonkolleite might be related to its very thin plate-like structure. Although the prepared samples showed lower photocatalytic activity compared with commercial titania powders, it was notable that about 18% of 1 ppm NO was continuously removed under UV light irradiation.

Table 1. SSA and deNOxability of the samples prepared under different conditions, together with those of P25 titania

Figure 8shows the DRS spectra of the samples prepared at 95 °C in ZnCl2–HMT mixed aqueous solution and 50 vol.% EG aqueous solution together with that of commercial ZnO. The spindle-like ZnO showed similar DRS spectra with that of commercial ZnO powders, while that of plate-like simonkolleite showed quite different spectra, indicating very low absorption ability of UV light above 290 nm. This result agreed with those in Table 1, in which the ZnO samples showed higher photocatalytic deNOxability than those of plate-like simonkolleite samples although the SSA was smaller.

thumbnailFigure 8. DRS spectra of samples prepared at 95 °C in (a) 0.01 M ZnCl2–HMT mixed aqueous solution (spindle-like ZnO), (b) 0.1 M ZnCl2–HMT mixed 50 vol.% EG aqueous solution (plate-like simonkolleite). (c) commercial ZnO

Conclusions

Based on above results, the following conclusions might be drawn: The morphology and crystalline phase of the product by the heat treatment of ZnCl2–HMT aqueous solution with and without EG changed greatly depending on the concentrations of Zn2+ion and EG additive in the solution. Layered hexagonal plate-like Zn5(OH)8Cl2 · H2O were formed in 0.05 M and 0.1 M ZnCl2–HMT mixed aqueous solution and in 0.1 M ZnCl2–HMT mixed 50 vol.% EG aqueous solution. The existence of EG in the solution promote the homogeneous crystal growth, and also delay the formation of hexagonal plate-like structure. Hexagonal plate-like Zn5(OH)8Cl2 · H2O have comparatively higher SSA than that of rod-like ZnO crystal fabricated by the same method. Although the prepared ZnO samples showed lower photocatalytic activity compared with commercial titania powders, about 18% of 1 ppm NO was continuously removed.

Acknowledgments

This research was carried out as one of the projects under the Special Education and Research Expenses on “Post-Silicon Materials and Devices Research Alliance” and the JSPS Asian Core Program “Interdisciplinary Science of Nanomaterials”, JSPS Core University Program (CUP), supported by Nippon Sheet Glass Foundation for Materials Science and Engineering, Research for Promoting Technological Seeds, JST, and a Grant-in-Aid for Science Research (No.20360293).

References

  1. Zhu YW, Zhang HZ, Sun XC, Feng SQ, Xu J, Zhao Q, Xiang B, Wang RM:

    Appl. Phys. Lett.. 2003, 83:144-146.

    COI number [1:CAS:528:DC%2BD3sXltFKisLY%3D]; Bibcode number [2003ApPhL..83..144Z]

    Publisher Full Text OpenURL

  2. Keis K, Bauer C, Boschloo G, Hagfeldt A, Westermark K, Rensmo H, Siegbahn H:

    J. Photochem. Photobiol. A Chem.. 2002, 148:57-64.

    COI number [1:CAS:528:DC%2BD38Xktlaqtb0%3D]

    Publisher Full Text OpenURL

  3. Luo L, Zhang Y, Mao SS, Lin L:

    Sens. Actuators A Phys.. 2006, 127:201-206.

    COI number [1:CAS:528:DC%2BD28XisFOltb0%3D]

    Publisher Full Text OpenURL

  4. Zhang Y, Zhu F, Zhang J, Xia L:

    Nanoscale Res. Lett.. 2008, 3:201-204.

    COI number [1:CAS:528:DC%2BD1cXhsVyhtr%2FE]; Bibcode number [2008NRL.....3..201Z]

    Publisher Full Text OpenURL

  5. Wang ZL, Song J:

    Science. 2006, 312:242-246.

    COI number [1:CAS:528:DC%2BD28XjtlKqu7g%3D]; Bibcode number [2006Sci...312..242W]

    Publisher Full Text OpenURL

  6. Sun XM, Chen X, Deng ZX, Li YD:

    Mater. Chem. Phys.. 2003, 78:99-104.

    Bibcode number [2003CPL...379...99S]

    Publisher Full Text OpenURL

  7. Chen YX, Zhao XQ, Sha B, Chen JH:

    Mater. Lett.. 2008, 62:2369-2371.

    COI number [1:CAS:528:DC%2BD1cXktlGisL8%3D]

    Publisher Full Text OpenURL

  8. Pan ZW, Dai ZR, Wang ZL:

    Science. 2001, 291:1947-1949.

    COI number [1:CAS:528:DC%2BD3MXhvVSnu7s%3D]; Bibcode number [2001Sci...291.1947P]

    Publisher Full Text OpenURL

  9. Kong XY, Ding Y, Ying R, Wang ZL:

    Science. 2004, 303:1348-1351.

    COI number [1:CAS:528:DC%2BD2cXhsFyrtL0%3D]; Bibcode number [2004Sci...303.1348K]

    Publisher Full Text OpenURL

  10. Kim TY, Kim JY, Lee SH, Shim HW, Lee SH, Suh EK, Nahm KS:

    Synth. Met.. 2004, 144:61-68.

    COI number [1:CAS:528:DC%2BD2cXjsl2lsrw%3D]

    Publisher Full Text OpenURL

  11. Shen LM, Bao NZ, Yanagisawa K, Domen K, Grimes CA, Gupta A:

    J. Phys. Chem. C. 2007, 111:7280-7287.

    COI number [1:CAS:528:DC%2BD2sXksl2rtr4%3D]

    Publisher Full Text OpenURL

  12. Yan C, Xue D:

    Funct. Mater. Lett.. 2008, 1:37-42.

    COI number [1:CAS:528:DC%2BD1cXhtlClur%2FE]

    Publisher Full Text OpenURL

  13. Yan C, Xue D:

    J. Phys. Chem. B. 2006, 110:7102-7106.

    COI number [1:CAS:528:DC%2BD28XisFWitrg%3D]

    Publisher Full Text OpenURL

  14. Yan C, Liu J, Wu J, Gao K, Xue D:

    Nanoscale Res. Lett.. 2008, 3:473-480.

    COI number [1:CAS:528:DC%2BD1cXhsVyhtrjP]; Bibcode number [2008NRL.....3..473Y]

    Publisher Full Text OpenURL

  15. Subramanyam TK, Srinivasulu Naidu B, Uthanna S:

    Cryst. Res. Technol.. 2000, 35:1193-1202.

    COI number [1:CAS:528:DC%2BD3cXoslyktrk%3D]

    Publisher Full Text OpenURL

  16. Zhang X, Xie SY, Jiang ZY, Zhnag X, Tian ZQ, Xie ZX, Huang RB, Zheng LS:

    J. Phys. Chem. B. 2003, 107:10114-10118.

    COI number [1:CAS:528:DC%2BD3sXms1eqtLc%3D]

    Publisher Full Text OpenURL

  17. Wienke J, Booij AS:

    Thin Solid Films. 2008, 516:4508-4512.

    COI number [1:CAS:528:DC%2BD1cXls1Klsro%3D]; Bibcode number [2008TSF...516.4508W]

    Publisher Full Text OpenURL

  18. Dedova T, Volobujeva O, Klauson J, Mere A, Krunks M:

    Nanoscale Res. Lett.. 2007, 2:391-396.

    COI number [1:CAS:528:DC%2BD2sXhtFGnt7fN]; Bibcode number [2007NRL.....2..391D]

    Publisher Full Text OpenURL

  19. Umar A, Kim SH, Kim JH, Hahn YB:

    Mater. Lett.. 2008, 62:167-171.

    COI number [1:CAS:528:DC%2BD2sXhtlejsr3J]

    Publisher Full Text OpenURL

  20. Jiang P, Zhou JJ, Fang HF:

    Mater. Lett.. 2006, 60:2516-2521.

    COI number [1:CAS:528:DC%2BD28Xmtl2rsbc%3D]

    Publisher Full Text OpenURL

  21. Yin S, Sato T:

    J. Mater. Chem.. 2005, 15:4584-4587.

    COI number [1:CAS:528:DC%2BD2MXhtFKqt77E]

    Publisher Full Text OpenURL

  22. Yin S, LI R, SATO T:

    Adv. Sci. Technol.. 2006, 45:679.

    COI number [1:CAS:528:DC%2BD2sXjs1CjsLo%3D]

    Publisher Full Text OpenURL

  23. Bahadur H, Srivastava AK, Sharma RK, Chandra S:

    Nanoscale Res. Lett.. 2007, 2:469-475.

    COI number [1:CAS:528:DC%2BD2sXhtl2rtrrL]; Bibcode number [2007NRL.....2..469B]

    Publisher Full Text OpenURL

  24. Yin S, Hasegawa H, Maeda D, Ishitsuka M, Sato T:

    J. Photochem. Photobiol. A Chem.. 2004, 163:1-8.

    COI number [1:CAS:528:DC%2BD2cXhs1GjtL0%3D]

    Publisher Full Text OpenURL

  25. Zhang WX, Yanagisawa K:

    Chem. Mater.. 2007, 19:2329-2334.

    COI number [1:CAS:528:DC%2BD2sXjsFSks7w%3D]

    Publisher Full Text OpenURL

  26. Qu Q, Yan C, Wan Y, Cao C:

    Corros. Sci.. 2002, 44:2789-2803.

    COI number [1:CAS:528:DC%2BD38XlsVKitLs%3D]

    Publisher Full Text OpenURL

  27. Bhat NV, Nate MM, Kurup MB, Bambole VA:

    Nucl. Instrum. Methods Phys. Res. B. 2007, 262:39-45.

    COI number [1:CAS:528:DC%2BD2sXns1yks7w%3D]; Bibcode number [2007NIMPB.262...39B]

    Publisher Full Text OpenURL

  28. Ishikawa T, Matsumoto K, Kandori K, Nakayama T:

    Colloids Surf. A Physicochem. Eng. Asp.. 2007, 293:135-145.

    COI number [1:CAS:528:DC%2BD28XhtlGqtrzM]

    Publisher Full Text OpenURL

  29. Tanaka H, Fujioka A, Futoyu A, Kandori K, Ishikawa T:

    J. Solid State Chem.. 2007, 180:2061-2066.

    COI number [1:CAS:528:DC%2BD2sXnvFyltL4%3D]; Bibcode number [2007JSSCh.180.2061T]

    Publisher Full Text OpenURL