Photoelectric Properties of Silicon Nanocrystals/P3HT Bulk-Heterojunction Ordered in Titanium Dioxide Nanotube Arrays

Vladimir Švrček*, Ivan Turkevych and Michio Kondo

Author Affiliations

Research Center for Photovoltaics, National Institute of Advanced Industrial Science and Technology (AIST), Central 2, Umezono 1-1-1, Tsukuba, 305-8568, Japan

For all author emails, please log on.

Nanoscale Research Letters 2009, 4:1389-1394  doi:10.1007/s11671-009-9410-y

The electronic version of this article is the complete one and can be found online at:


Received:24 June 2009
Accepted:5 August 2009
Published:18 August 2009

© 2009 to the authors

Abstract

A silicon nanocrystals (Si-ncs) conjugated-polymer-based bulk-heterojunction represents a promising approach for low-cost hybrid solar cells. In this contribution, the bulk-heterojunction is based on Si-ncs prepared by electrochemical etching and poly(3-hexylthiophene) (P3HT) polymer. Photoelectric properties in parallel and vertical device-like configuration were investigated. Electronic interaction between the polymer and surfactant-free Si-ncs is achieved. Temperature-dependent photoluminescence and transport properties were studied and the ratio between the photo- and dark-conductivity of 1.7 was achieved at ambient conditions. Furthermore the porous titanium dioxide (TiO2) nanotubes’ template was used for vertical order of photosensitive Si-ncs/P3HT-based blend. The anodization of titanium foil in ethylene glycol-based electrolyte containing fluoride ions and subsequent thermal annealing were used to prepare anatase TiO2nanotube arrays. The arrays with nanotube inner diameter of 90 and 50 nm were used for vertical ordering of the Si-ncs/P3HT bulk-heterojunction.

Keywords:
Silicon nanocrystals; Bulk heterojunction; Titanium dioxide nanotubes

Introduction

Most of the solar cells installed today are made of silicon. The vision is to produce solar cells from cheap materials in low-cost processes, thus resulting in lower cost electricity production. It is believed that bulk-heterojunction solar cells made of from conjugated polymer blends offer such a possibility [1,2]. Organic semiconductors propose simple device fabrication technologies (i.e., screen printing and spin casting) at low temperature and therefore are very attractive for photovoltaic industry [3]. The bulk-heterojunction concept for solar cells has a potential to be considerably improved [2-4]. One possible route is the introduction of organic electron acceptors into a conjugated polymer matrix. Silicon in the form of tiny Si-ncs, which exhibit quantum confinement effects, offers unique properties: i.e., the Si-ncs can serve as electron acceptors [5,6] and can produce multiple electrons per photon due to the carrier multiplication that can increase photocurrent generation [7]. The bulk-heterojunction based on Si-ncs can present new possibilities to design new types of absorber materials for low-cost hybrid solar cells [5-7].

The photovoltaic performance of Si-ncs/conductive polymer bulk-heterojunction relies on mesoscopic arrangement of both nanocrystals and polymer conjugation chains. The morphology of the bulk-heterojunction can be significantly affected by various fabrication parameters during the device formation [8]. Functional nanotubes fabrication and novel synthetic strategies for generating nanotubes from inorganic materials have been recently widely investigated and reported in literature [9]. An incorporation of novel 1D nanostructures into nano-porous templates and an enhancement of the solar cells performance based on 1D configurations have been recently demonstrated [10,11]. It is expected that a fiber- and/or vertical 1D-like order of photosensitive bulk-heterojunction gives considerable advantages over the thin film technology, because it provides larger interfacial area for efficient exciton dissociation and straight path for photogenerated carries. Furthermore, fiber arrays have much lower reflectance and enable fabrication of thicker devices with increased absorption compared with thin films. As a result, fibers help to avoid circuit shorts and interruption of percolation paths for carriers to their respective electrodes [8]. Till date several nanotubular architectures have been investigated for potential enhancement of electron percolation pathways in bulk-heterojunction [8,12]. One of such possibilities is vertically oriented titanium dioxide (TiO2) nanotube arrays. An efficient charge collection in photoelectrochemical devices after blend infiltration into transparent TiO2 nanotube films has been shown [13]. In addition, such architecture allows an improvement in light harvesting as thicker devices can be produced in order to increase the optical density [14]. A relatively easy fabrication technique of TiO2 nanotube arrays by anodization offers highly ordered nano-templates at low cost [15,16].

In this study, the bulk-heterojunction based on Si-ncs prepared by electrochemical etching and poly(3-hexylthiophene) (P3HT) polymer is investigated. Firstly, the photo-transport properties of the bulk-heterojunction fabricated in parallel configuration on interdigitated electrodes are studied. Next, a vertical 1D-like configuration of the bulk-heterojunction through infiltration into a nanotubular template of anodic TiO2is performed. Anodization of titanium foil followed by annealing has been used to fabricate the crystalline anatase nanotubular templates. The optoelectrical properties of photoconductive Si-ncs/P3HT bulk-heterojunction aligned in TiO2nanotubes with inner diameter of 90 and 50 nm are compared and discussed in details.

Experimental Details

Firstly, in order to infiltrate the bulk-heterojunction, the TiO2 nanotubes with two deferent inner diameters were prepared as follows. A 99.99% pure titanium foil was anodized in 0.3 wt% solution of NH4F in ethylene glycol in a two-electrode configuration under constant potentials of 40 and 20 V at room temperature, respectively [15]. The titanium foil served as anode and platinum mesh as the counter electrode. The transformation of amorphous as-grown anodic TiO2 into crystalline anatase was performed by annealing in air at 450 °C [16].

Secondly, following our previous work, the freestanding Si-ncs were prepared by electrochemical etching of silicon wafers [17]. Crystalline silicon boron-doped wafer with resistivity of 0.5–0.75 Ohm cm was used. The wafers were electrochemically etched in a mixture of hydrofluoric acid with pure ethanol and then the Si-ncs were harvested by mechanical scratching and sedimentation [5,17]. After dispersion in ethanol, we could observe bright room temperature photoluminescence (PL) in the colloid solution by naked eye. The typical emission of Si-ncs used in this study is shown in Fig. 1a. The strong orange PL can be observed at room temperature under the excitation by a He:Cd CW laser (325 nm). After evaporation of the ethanol, the freestanding Si-ncs showed broad PL spectra with a maximum typically located around ~600 nm [18].

thumbnailFigure 1. aPL emission from Si-ncs dispersed in ethanol at room temperature and under the excitation by a He:Cd CW laser (325 nm).bPL spectra measured for Si-ncs/P3HT blend film under excitation at 325 nm taken at 4 and 300 K

Then, the dried Si-ncs were used for bulk-heterojunction fabrication. Commercially available (ALDRICH, Nakayama, Tsukuba-branch, Japan) P3HT polymers were dissolved in chlorobenzene (14 mg/mL). An aliquot of 400 mg of the polymer solution and 2 mg of Si-ncs were mixed. The photoelectric properties of the blend were investigated in two configurations. For parallel photo-conductivity measurements, the Si-ncs/P3HT blend was coated on interdigitated platinum contact evaporated on glass [5]. For perpendicular measurements, the Si-ncs/P3HT blend was incorporated into the TiO2 nanotubes and covered on top by a transparent conductive oxide (TCO) electrode, which was spin-coated with poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS), to form TCO/PEDOT:PSS/(Si-ncs/P3HT)/TiO2-NTs device. Another device with only pure P3HT polymer was prepared for comparison. All samples were dried at 140 °C for 30 min in vacuum.

The temperature-dependent PL measurements were run from 4 to 300 K by placing the samples into a cryostat. The He:Cd CW laser (325 nm or 3.82 eV) has been used as an excitation source. The conductivity and photo-conductivity measurements were performed in ambient conditions. A constant potential from a regulated dc power supply was applied and the resulting current was measured with an ampere meter (Sub-Femtoamp, Keithley 6430). For the photo-conductivity measurements, a white light of 1.5 AM was used to irradiate the samples.

Results and Discussions

Bulk-Heterojunction in Parallel Configuration

Figure 1b shows PL spectra measured for Si-ncs/P3HT blend film under excitation at 325 nm taken at 4 and 300 K. The introduction of the Si-ncs into the conjugated polymer results in change of the PL characteristics [18]. Contrary to the pure polymer films, the red shift of the PL band as a function of temperature is recorded. A similar temperature dependence of the PL behavior was previously observed for Si-ncs with quantum confinement size effect, which was introduced into MEH-PPV polymer [18]. After exciton transfer from the polymer to the Si-ncs, the state filling effect is responsible for the shift of the PL band [19]. An increase in temperature decreases the emission intensity at higher emission energies and leads to a ~40-nm red-shift of PL spectrum maxima in temperature ranging from 4 to 300 K (Fig. 1b).

The parallel photo-conductivity is applied to check the bulk-heterojunction formation [5]. Figure 2a represents a schematic sketch of the experimental setup when the Si-ncs/P3HT bulk-heterojunction is spin-coated on interdigitated electrodes. It is believed that placing of both negative and positive contacts on the backside of the solar cell eliminates the front contact and provides a potential to improve short-circuit current [5]. Furthermore, this configuration could lead to an easier interconnection and a simpler way to module fabrication [20]. In our particular case, the introduction of the Si-ncs into the polymer increases the porosity of the blend and we can eliminate shunting of Si-ncs/P3HT bulk-heterojunction when we spin-coat a large surface area [5].

thumbnailFigure 2. aSchematic representation of the Si-ncs/P3HT bulk-heterojunction spin coated on interdigitated electrodes.bIVcurves for Si-ncs/P3HT blend. TheIVcharacteristics of P3HT polymer are only shown for comparison.Black linesrepresent the measurement indark and red linesunder AM1.5 illumination

Figure 2b displays the current–voltage (IV) curves for Si-ncs/P3HT blend in dark (black line) and under AM1.5 illumination (red line). An introduction of the Si-ncs into P3HT polymer increases the overall dark-conductivity (more than two times) through the polymer. Furthermore, under AM1.5 illumination, the photocurrent generation is observed. The ratio of the photo-conductivity to the dark-conductivity is about 1.7. We attribute the photocurrent generation to the formation of the bulk-heterojunction in the Si-ncs/P3HT blend. To form the bulk-heterojunction, the photosensitive material requires proper energy band alignment. Fortunately, the energy levels of Si-ncs match the energy levels of the conjugated P3HT polymer. The highest occupied molecular orbital for P3HT is −5 eV below the vacuum, whereas the lowest unoccupied molecular orbital is −3 eV. The band gap of Si-ncs is about (~2 eV) [5], which allows a proper adjustment of the bands for the eh separation [5]. The different electron affinities and ionization potentials provide a driving force for the eh dissociation when the excitons are generated under AM1.5 irradiation. We assume that a large fraction of the excitons dissociates at Si-ncs/polymer interface. Dissociated excitons leave the electrons in the nanocrystals and the holes in the polymer.

Alignment of Bulk-Heterojunction in TiO2Nanotubes

The morphology of the TiO2nanotube layer after thermal treatment is summarized in Fig. 3. Figure 3a, b shows scanning electron microscopy (SEM) images of TiO2nanotubes with average diameters of 50 and 90 nm, respectively, and with lengths of about 1 μm. In both cases, the transformation of amorphous TiO2into crystalline anatase was confirmed by XRD measurements. Figure 3cshows typical XRD spectra after the annealing process. Two most important TiO2anatase peaks corresponding to (101) and (200) orientations were clearly recorded.

thumbnailFigure 3. aSEM image of the nanotubular TiO2template used for vertical order of Si-ncs/P3HT bulk-heterojunction.bXRD spectra that reveals transformation of as-grown amorphous TiO2nanotubes into a single phase anatase after annealing at 450 °C

It is observed that infiltration of photosensitive Si-ncs/P3HT blend in the TiO2nanotubes results in increase in the photovoltage generation. The correspondingIVcharacteristics of Si-ncs/P3HT heterojunction in vertical configuration in the dark and under illumination at AM1.5 after annealing at 140 °C are compared in Fig. 4. TheIVcharacteristics of the blend sandwiched on solid nonporous substrate are presented in Fig. 4a. Similar to the parallel configuration (Fig. 3b), the introduction of Si-ncs in P3HT polymer increasesIVcurve bending and the photo-conductivity response. Both features are further enhanced when the bulk-heterojunction is introduced into the TiO2nanotubes. Figure 4b, c represents theIVcharacteristics of the blends infiltrated into TiO2nanotubes with diameters of 50 and 90 nm, respectively. TheIVcharacteristics for both the pure polymer and bulk-heterojunction show apinbehavior. However, superior open voltage and ratio between the photo- and dark-conductivity are observed in the case of infiltration of the blend into nanotubes with larger diameter (Fig. 4c, red line).

thumbnailFigure 4. IVcharacteristics of the sandwiched Si-ncs/P3HT bulk-heterojunction in the dark and under illumination at AM1.5 after annealing at 140 °C. TheIVcharacteristics were taken from the blend sandwiched on solid nonporous substrate (a) and within TiO2nanotube arrays with the diameters of 50 nm (b) and 90 nm (c), respectively. TheIVcharacteristics of pure polymer are shown for comparison

One can expected that the alignment of Si-ncs/P3HT bulk-heterojunction within TiO2 nanotubes, which are perpendicular to the contact, will facilitates charge transfer along the nanotubes [21]. Figure 5 displays a schematic sketch of the structure used in this study. At the same time, the alignment within the nanotubes can reduce losses incurred by charge hopping across the Si-ncs/P3HT blend. The typical range of exciton diffusion lengths in polymers is 5–20 nm. Therefore, one can expect that the nanotube size should be around this range in order to promote an efficient charge separation. However, the polymer chain packing inside small nanotubes can be fundamentally different from the chain packing in a bulk film [12]. In the bulk film, the high degree of π–π stacking between the polymer chains allows the delocalization of excitons over multiple chains. This can be eliminated in the case of confinement of the polymer in nanotubes. Similar to our architecture, it has been found [22] that the mobility of P3HT polymer infiltrated into an anodic alumina template with vertical channels was enhanced by as much as a factor of 20 due to alignment of the polymer chains in the pores in a direction perpendicular to the substrate. However, other group pointed out [23] that in small pores, the chains of the conjugated polymer were found to be isolated with little evidence of interchain contact. Similar to those reported effects, one could expect that infiltration of Si-ncs/P3HT polymer-based bulk-heterojunction into TiO2 nanotubes will result in alignment of the polymer chains. However, further studies should be performed in order to find an optimum diameter of nanotubes for a proper alignment of polymer, which contains Si-ncs.

thumbnailFigure 5. Schematic sketch of the structure for ordering of Si-ncs/P3HT bulk-heterojunction in TiO2nanotube arrays

The photovoltage generation in the bulk-heterojunction most likely results in increase in open circuit voltage. However, the voltage open-circuit values cannot be explained by the metal–insulator–metal model [24]. In this case, the polymer blend has a negligible amount of intrinsic charge carriers and is considered as an insulator. The upper limit of the open-circuit voltage can be estimated from the difference of the two electrodes work functions. Figure 6 shows corresponding energy level diagram of the blend sandwiched between PEDOT:PSS contact and TiO2 nanotubular template. On the other hand, small difference of the electrodes work functions results in a weak photocurrent generation. Even more, the presence of the Si-ncs in polymer makes the blend to be more semiconductor rather than an insulator; therefore, a high-voltage open-circuit can be partially explained by assuming a Schottky barrier at the Si-ncs/P3HT/PEDOT:PSS interface.

thumbnailFigure 6. Energy level diagram of Si-ncs conjugated P3HT polymer blends sandwiched between TCO and TiO2nanotube arrays

It is clear that the nanofiber morphology of the blend embedded into nanotubular templates can contribute to high open-circuit voltage as well. The bulk-heterojunction performance depends on mesoscopic arrangement of both nanocrystals and polymer chains. The fiber-like alignment provides larger interfacial area, which results in enhanced exciton dissociation. It has to be noted that compared to thin films, the fiber arrays configuration has lower reflectance. This is also most likely the reason in the case of TiO2nanotubes with larger diameter that allow infiltration of larger amount of bulk-heterojunction into nanotubes, and form thicker device. As a result, increased absorption and active surface area for exciton separation augment photovoltage generation. However, for a clear picture of the origin of an increase in the open-circuit voltage, further experiments have to be performed.

Summary

We have investigated photoelectric properties of the Si-ncs P3HT polymer-based bulk-heterojunction. The room temperature luminescent Si-ncs with large optical band gap (~2 eV) were prepared by electrochemical etching. The presence of the Si-ncs in the polymer increases the transport and assures an interaction between electronic states of the Si-ncs and P3HT polymer. As a result, the exciton transfer from the polymer and bulk-heterojunction formation were achieved. The exciton transfer and quantum confinement effect in Si-ncs lead to PL maxima shift around ~40 meV in the temperature region 4–300 K. The ratio between photo- and dark-conductivity around 1.7 in parallel configuration has been demonstrated. Furthermore, we showed that the titanium dioxide (TiO2) nanotube arrays with tunable nanotube diameter can be efficient for a vertical 1D-like order of Si-ncs/P3HT photosensitive blend. The arrangement of the Si-ncs/P3HT bulk-heterojunction within ordered TiO2nanotubes prepared perpendicular to the contact facilitates excitons separation and charge transfer along nanotubes. It is expected that the optimization of the morphology of the Si-ncs/P3HT blend infiltrated into TiO2nanotubes can lead to an improvement in the solar cell performance.

Acknowledgment

This study was supported by the New Energy Development Organization (NEDO) of Japan.

References

  1. Yu G, Heeger AJ: Charge separation and photovoltaic conversion in polymer composites with internal donor/acceptor heterojunctions.

    J. Appl. Phys. 1995, 78:4510.

    COI number [1:CAS:528:DyaK2MXot1alurc%3D]; Bibcode number [1995JAP....78.4510Y]

    Publisher Full Text OpenURL

  2. Halls JJM, Walsh CA, Greenham NC, Marseglia EA, Friend RH, Moratti SC, Holmes AB: Efficient photodiodes from interpenetrating polymer networks.

    Nature 1995, 376:498.

    COI number [1:CAS:528:DyaK2MXnsVCrs7c%3D]; Bibcode number [1995Natur.376..498H]

    Publisher Full Text OpenURL

  3. Shabeen SE, Ginley DS, Jabbour GE: Organic-based photovoltaics: toward low-cost power generation.

    MRS Bull. 2005, 30:10. OpenURL

  4. Yu G, Gao J, Hummelen JC, Wudl F, Heeger AJ: Polymer photovoltaic cells: enhanced efficiencies via a network of internal donor–acceptor heterojunctions.

    Science 1995, 270:1789.

    COI number [1:CAS:528:DyaK2MXhtVSiurjF]; Bibcode number [1995Sci...270.1789Y]

    Publisher Full Text OpenURL

  5. Švrček V, Fujiwara H, Kondo M: Improved transport and photo-stability of poly[methoxy-ethylexyloxy-phenylenevinilene] polymer thin films by boron doped freestanding silicon nanocrystals.

    Appl. Phys. Lett. 2008, 92:143301.

    Bibcode number [2008ApPhL..92n3301S]

    Publisher Full Text OpenURL

  6. Lui C, Holman Z, Kortshagen U: Hybrid solar cells from P3HT and silicon nanocrystals.

    Nano Lett. 2009, 9:449.

    Bibcode number [2009NanoL...9..449L]

    Publisher Full Text OpenURL

  7. Beard MC, Knutsen KK, Yu P, Luther J, Song Q, Ellingson RJ, Nozik AJ: Multiple exciton generation in colloidal silicon nanocrystals.

    Nano Lett. 2007, 7:2506.

    COI number [1:CAS:528:DC%2BD2sXotVShsbs%3D]; Bibcode number [2007NanoL...7.2506B]

    Publisher Full Text OpenURL

  8. Williams SS, Hampton MJ, Gowrishankar V, Ding I-K, Templeton JL, Samulski ET, DeSimone JM, McGehee MD: Nanostructured titania-polymer photovoltaic devices made using PFPE-based nanomolding techniques.

    Chem. Mater. 2008, 20:5229.

    COI number [1:CAS:528:DC%2BD1cXptVOmtbo%3D]

    Publisher Full Text OpenURL

  9. Yan C, Liu J, Liu F, Wu J, Gao K, Xue D: Tube formation in nanoscale materials.

    Nanoscale Res. Lett. 2008, 3:473.

    COI number [1:CAS:528:DC%2BD1cXhsVyhtrjP]; Bibcode number [2008NRL.....3..473Y]

    Publisher Full Text OpenURL

  10. Wang Z, Brust M: Fabrication of nanostructure via self-assembly of nanowires within the AAO template.

    Nanoscale Res. Lett. 2007, 2:34.

    COI number [1:CAS:528:DC%2BD2sXhsVSgtLk%3D]; Bibcode number [2007NRL.....2...34W]

    Publisher Full Text OpenURL

  11. Yu K, Chen J: Enhancing solar cell efficiencies through 1-D nanostructures.

    Nanoscale Res. Lett. 2009, 4:1.

    COI number [1:CAS:528:DC%2BD1MXht1Kgs7w%3D]; Bibcode number [2009NRL.....4....1Y]

    Publisher Full Text OpenURL

  12. Coakley KM, Liu YX, McGehee MD, Frindell KL, Stucky GD: Infiltrating semiconducting polymers into self-assembled mesoporous titania films for photovoltaic applications.

    Adv. Funct. Mater. 2003, 13:301.

    COI number [1:CAS:528:DC%2BD3sXjsVKitr8%3D]

    Publisher Full Text OpenURL

  13. Mor GK, Shankar K, Paulose M, Varghese OK, Grimes CA: High efficiency double heterojunction polymer photovoltaic cells using highly ordered TiO2 nanotube arrays.

    Appl. Phys. Lett. 2007, 91:152111.

    Bibcode number [2007ApPhL..91o2111M]

    Publisher Full Text OpenURL

  14. Law M, Greene LE, Johnson JC, Saykally R, Yang PD: Nanowire dye-sensitized solar cells.

    Nat. Mater. 2005, 4:455.

    COI number [1:CAS:528:DC%2BD2MXks1Cit7o%3D]; Bibcode number [2005NatMa...4..455L]

    Publisher Full Text OpenURL

  15. Prakasam HE, Shankar K, Paulose M, Varghese OK, Grimes CA: A new benchmark for TiO2 nanotube array growth by anodization.

    J. Phys. Chem. C 2007, 111:7235.

    COI number [1:CAS:528:DC%2BD2sXks1Sitrc%3D]

    Publisher Full Text OpenURL

  16. Macak JM, Aldabergerova S, Ghicov A, Schmuki P: Smooth anodic TiO2 nanotubes: annealing and structure.

    Phys. Status Solidi A 2006, 203:R67.

    COI number [1:CAS:528:DC%2BD28Xpt1Srtr0%3D]; Bibcode number [2006PSSAR.203...67M]

    Publisher Full Text OpenURL

  17. Švrček V, Slaoui A, Muller J-C: Ex-situ prepared Si nanocrystals: their elaboration and characterization in embedded silica glass.

    J. Appl. Phys. 2004, 95:3158.

    Bibcode number [2004JAP....95.3158S]

    Publisher Full Text OpenURL

  18. Švrcek V, Fujiwara H, Kondo M: Luminescent properties of doped freestanding silicon nanocrystals embedded in MEH-PPV.

    Sol. Energy Mater. Sol. Cells 2009, 93:774. Publisher Full Text OpenURL

  19. Brongersma ML, Polman A, Min KS, Boer E, Tambo T, Atwater HA: Tuning the emission wavelength of Si nanocrystals in SiO2 by oxidation.

    Appl. Phys. Lett. 1998, 72:2577.

    COI number [1:CAS:528:DyaK1cXislyqsrs%3D]; Bibcode number [1998ApPhL..72.2577B]

    Publisher Full Text OpenURL

  20. Tenne R, Rao CNR: Inorganic nanotubes.

    Philos. Trans. R. Soc. A 2004, 362:2099.

    COI number [1:CAS:528:DC%2BD2cXhtVOqt7rO]; Bibcode number [2004RSPTA.362.2099T]

    Publisher Full Text OpenURL

  21. Coakley KM, Srinivasan BS, Ziebarth JM, Goh C, Liu Y, McGehee MD: Enhanced hole mobility in regioregular polythiophene infiltrated in straight nanopores.

    Adv. Funct. Mater. 2005, 15:1927.

    COI number [1:CAS:528:DC%2BD2MXhtlers7fI]

    Publisher Full Text OpenURL

  22. Cadby AJ, Tolbert SH: Controlling optical properties and interchain interactions in semiconducting polymers by encapsulation in periodic nanoporous silicas with different pore sizes.

    J. Phys. Chem. B 2005, 109:17879.

    COI number [1:CAS:528:DC%2BD2MXpsFOqsrs%3D]

    Publisher Full Text OpenURL

  23. Parker ID: Carrier tunneling and device characteristics in polymer light-emitting diodes.

    J. Appl. Phys. 1994, 75:1656.

    COI number [1:CAS:528:DyaK2cXitlWhtbY%3D]; Bibcode number [1994JAP....75.1656P]

    Publisher Full Text OpenURL